Electron transport in high quality undoped ZnO film grown by plasma-assisted molecular beam epitaxy

High quality ZnO films were grown on c-plane sapphire substrate using low temperature ZnO buffer layer by plasma-assisted molecular beam epitaxy. The film deposited at 720 °C showed the lowest value of full-width at half maximum for the symmetric (0002) diffraction peak of about 86 arcsec. The highest electron mobility in the films was about 103-105 cm²/V s. From temperature-dependent Hall effect measurements, the mobility strongly depends on the dislocation density at low temperature region and the polar optical phonon scattering at high temperature, respectively. Moreover, by obtaining the activation energy of the shallow donors, it was supposed that hydrogen was source of n-type conductivity in as-grown ZnO films.     

Epitaxial ZnO films grown on ZnO-buffered c-plane sapphire substrates by hydrothermal method

ZnO films are hydrothermally grown on ZnO-buffered c-plane sapphire substrates at a low temperature of 70 °C. A radio-frequency (RF) reactive magnetron sputtering has been used to grow the ZnO buffer layers. X-ray diffraction, scanning electron microscopy, and room temperature photoluminescence are carried out to characterize the structure, morphology and optical property of the films. It is found that the films are stress-free. The epitaxial relationship between the ZnO film and the c-plane sapphire substrate is found to be ZnO (0 0 0 1)||Al₂O₃ (0 0 0 1) in the surface normal and in plane. Sapphire treatment, as such acid etching, nitridation, and oxidation are found to influence the nucleation of the film growth, and the buffer layers determine the crystalline quality of the ZnO films. The maximum PL quantum efficiency of ZnO films grown with hydrothermal method is found to be about 80% of single-crystal ZnO.     

Low-temperature MOVPE growth of ZnO thin films by using a buffer layer

ZnO thin films have been grown on a-plane (1,1,−2,0) sapphire substrates by metalorganic vapor phase epitaxy (MOVPE) at low substrate temperature of 350 °C. It is showed that the crystal and electrical quality of the thin films was improved by using a ZnO buffer layer. The photoluminescence (PL) measurements indicate that the ZnO thin films grown at such a low substrate temperature have a strong UV emission.     

The role of a ZnO buffer layer in the growth of ZnO thin film on Al2O3 substrate

A ZnO buffer layer and ZnO thin film have been deposited by the pulsed laser deposition technique at the temperatures of 200 C and 400 C, respectively. Structural, electrical and optical properties of ZnO thin films grown on sapphire (Al₂O₃) substrate with 1, 5, and 9 nm thick ZnO buffer layers were investigated. A minute shift of the (101) peak was observed which indicates that the lattice parameter was changed by varying the thickness of the buffer layer. High resolution transmission electron microscopy (TEM) was used to investigate the thickness of the ZnO buffer layer and the interface involving a thin ZnO buffer between the film and substrate. Selected area electron diffraction (SAED) patterns show high quality hexagonal ZnO thin film with 30 in-plane rotation with respect to the sapphire substrate. The use of the buffer can reduce the lattice mismatch between the ZnO thin film and sapphire substrate; therefore, the lattice constant of ZnO thin film grown on sapphire substrate became similar to that of bulk ZnO with increasing thickness of the buffer layer.     

Engineering of nearly strain-free ZnO films on Si(1 1 1) by tuning AlN buffer thickness

ZnO properties were investigated as a function of AlN buffer layer thickness (0–100 nm) in ZnO/AlN/Si(1 1 1) structures grown by metal organic vapor phase epitaxy. A significant improvement of ZnO film crystallinity by tuning AlN buffer thickness was confirmed by x-ray diffraction, topography and photoluminescence measurements. An optimal AlN buffer layer thickness of 50 nm is defined, which allows for growth of nearly strain-free ZnO films. The presence of free excitons at 10 K suggests high crystal quality for all ZnO samples grown on AlN/Si(1 1 1) templates. The intensities of neutral and ionized donor bound exciton lines are found to correlate with the in-plane and out-of-plane strain in the films, respectively.     

Effect of microstructure of MgO buffer layer on BaTiO3 grown on silicon substrates

MgO ultrathin films were grown on Si(1 0 0) substrates as buffer layers for the growth of ferroelectric BaTiO₃ thin films by laser molecular beam epitaxy (L-MBE). The deposition process of MgO buffer layers grown on silicon was in situ monitored by reflection high-energy electron diffraction (RHEED). The structure of BaTiO₃ films fabricated on MgO buffers was investigated by X-ray diffraction. Biaxially textured MgO was obtained at high laser energy density, but when the laser energy was lowered, MgO buffer was transformed to the form of texture with angular dispersion with the increase of the film thickness. BaTiO₃ films grown on the former buffer were completely (0 0 1) textured, while those on the latter were (0 0 1) preferred orientated. Furthermore, the fabricated MgO buffers and BaTiO₃ films had atomically smooth surface and interface. All these can reveal that the quality of textured MgO buffer is a key factor for the growth of BaTiO₃ films on silicon.     

Effect of MgO buffer layer thickness on the electrical properties of MgZnO thin film transistors fabricated by plasma assisted molecular beam epitaxy

We report the fabrication and electrical characteristics of thin film transistors based on MgZnO thin films with different thicknesses of MgO buffer layer. The MgZnO thin films with MgO buffer layers were grown on SiO₂/p-Si substrates by plasma assisted molecular beam epitaxy. The effects of the buffer layer thickness on the structural properties of MgZnO films are investigated by X-ray diffraction, and the results show that the crystal quality of the MgZnO film is enhanced with 4 nm MgO buffer layer. The MgZnO TFT with 4 nm MgO buffer layer exhibits an n-type enhancement mode characteristics with a field effect mobility of 1.85 cm²/V s, a threshold voltage of 27.6 V and an on/off ratio of above 10⁶.     

Effects of sic buffer layer on the optical properties of ZnO films grown on Si (1 1 1) substrates

ZnO films have been grown by a sol-gel process on Si (1 1 1) substrates with and without SiC buffer layers. The influence of SiC buffer layer on the optical properties of ZnO films grown on Si (1 1 1) substrates was investigated. The intensity of the E₂ (high) phonon peak in the micro-Raman spectrum of ZnO film with the SiC buffer layer is stronger than that of the sample without the SiC buffer layer, and the breadth of E₂ (high) phonon peak of ZnO film with the SiC buffer layer is narrower than that of the sample without the SiC buffer layer. These results indicated that the crystalline quality of the sample with the SiC buffer layer is better than that of the sample without the SiC buffer layer. In photoluminescence spectra, the intensity of free exciton emission from ZnO films with the SiC buffer was much stronger than that from ZnO film without the SiC buffer layer, while the intensity of deep level emission from sample with the SiC buffer layer was about half of that of sample without the SiC buffer layer. The results indicate the SiC buffer layer improves optical qualities of ZnO films on Si (1 1 1) substrates.     

Magnetic anisotropy of epitaxial iron films on single-crystal MgO(001) and Al_2 O_3 (11\bar 20) substrates

The ferromagnetic resonance and magnetization of single-crystal thin (27–100 Å films grown in the (110) direction are measured in the temperature range 20–400 K. The films are prepared by molecular-beam epitaxy on single-crystal sapphire substrates with a Nb(110)buffer layer. The angular dependence of the parameters of the ferromagnetic resonance spectrum is observed to have a 180° character when the static magnetic field is rotated in the plane of the sample. It is established that this angular dependence can be described on the assumption that the lattice distortions are essentially trigonal. A comparative analysis of previous data for Fe(001) films with the data for Fe(110) films shows that the source of the corrections to the cubic anisotropy constant is the characteristic distribution of the strains along the thickness of the film. Zh. éksp. Teor. Fiz. 115, 689–703 (February 1999)     

Polarized neutron reflectometry of the influence of Fe/Si,Fe/FeSi2 and Au/Fe interfaces on the magnetic properties of epitaxial Fe films

The magnetic and structural properties of epitaxial Fe films grown on Si(1 1 1) are investigated by polarized neutron reflectometry (PNR) at room temperature. The influence of different types of interfaces, Fe/Si, Fe/FeSi₂ and Au/Fe on the magnetic properties of Fe films deposited by molecular beam epitaxy onto Si(1 1 1) are characterized. We observe a drastic reduction of the magnetic moment in the entire Fe film deposited directly on the silicon substrate essentially due to strong Si interdiffusion throughout the whole Fe layer thickness. The use of a silicide FeSi₂ template layer stops the interdiffusion and the value of the magnetic moment of the deposited Fe layer is close to its bulk value. We also evidence the asymmetric nature of the interfaces, Si/Fe and Fe/Si interfaces are magnetically very different. Finally, we show that the use of Au leads to an enhancement of the magnetization at the interface.     

Layer by layer growth of ZnO on (0001) sapphire substrates by radical-source molecular beam epitaxy

Layer by layer growth of ZnO epilayers on (0001) Al₂O₃ substrates is achieved by radical-source molecular beam epitaxy. A thin MgO buffer, followed by a low-temperature ZnO buffer was used in order to accommodate the lattice mismatch between ZnO and sapphire. Reflection high-energy electron diffraction intensity was employed for the optimization of the ZnO growth. The surface morphology of the samples was studied with atomic force microscopy. Investigation of the nature of the influence of the MgO buffer layer on the formation of ZnO on sapphire substrate was carried out using Transmission Electron Microscopy. For the first time it was shown that a thin spinel (magnesium aluminum oxide) layer is formed on the interface of the sapphire substrate and MgO buffer layer leading to the crystalline quality improvement of the ZnO main layer. X-Ray diffractometry measurements of the obtained ZnO layers show excellent quality of the single crystalline ZnO heteroepitaxially grown on sapphire. The crystalline quality of the ZnO layers is even better than that of our previously reported layers grown employing hydrogen peroxide as an oxidant. The full width at half maximum of the XRD (0002) rocking curve is as low as 25 arc s. The influence of growth parameters (Zn/O flux ratio, temperature, etc.) on the structural properties as well as on the surface morphology of the zinc oxide layers on sapphire is investigated and discussed.     

Characteristics of Ni films deposited on SiO2/Si(1 0 0) and MgO(0 0 1) by direct current magnetron sputtering system with the oblique target

280 nm-thick Ni films were deposited on SiO₂/Si(1 0 0) and MgO(0 0 1) substrates at 300 K, 513 K and 663 K by a direct current magnetron sputtering system with the oblique target. The films deposited at 300 K mainly have a [1 1 0] crystalline orientation in the film growth direction. The [1 1 0]-orientation weakens and the [1 1 1]- and [1 0 0]-orientations enhance with increasing deposition temperature. The lattice constant of the Ni films is smaller than that of the Ni bulk, except for the film grown on MgO(0 0 1) at 663 K. Furthermore, as the deposition temperature increases, the lattice constant of the films grown on the SiO₂/Si(1 0 0) decreases whereas that of the films grown on the MgO(0 0 1) increases. The films deposited at 300 K and 513 K grow with columnar grains perpendicular to the substrate. For the films deposited at 663 K, however, the columnar grain structure is destroyed, i.e., an about 50 nm-thick layer consisting of granular grains is formed at the interface between the film and the substrate and then large grains grow on the layer. The Ni films deposited at 300 K consist of thin columnar grains and have many voids at the grain boundaries. The grains become thick and the voids decrease with increasing deposition temperature. The resistivity of the film decreases and the saturation magnetization increases with increasing deposition temperature.     

Effect of electrically degenerated layer on the carrier transport property of ZnO epitaxial thin films

ZnO films were prepared on (1 1 1) YSZ and (0 0 0 1) sapphire by pulsed laser deposition method. Effect of lattice mismatch on the carrier transport properties of ZnO epitaxial thin films was investigated. The carrier mobility of the ZnO films on YSZ was larger than that of ZnO/sapphire due to smaller lattice mismatch when the thickness was below 150 nm. The effect of electrically degenerated layer on the carrier transport property increased with decreasing the film thickness of ZnO film. The carrier density and electron mobility of 20 nm-thick-ZnO film on either substrate were regardless of the temperature. We concluded that the dominant carrier scattering mechanism in ZnO ultra thin films is double Schottky barriers at the grain boundary and that their height depends on the carrier concentration.     

Epitaxial growth of Al on Si(1 1 1) with Cu buffer layers

The structure of thin Al films grown on Si(1 1 1) with thin Cu buffer layers has been investigated using synchrotron radiation photoemission spectroscopy. A thin Cu(1 1 1) layer between the Si(1 1 1) substrate and an Al film may enhance quantum well effects in the Al film significantly. The strength of quantum well effects has been investigated qualitatively with respect to the thickness of the Cu buffer layer and to the Al film thickness. Deposition of Cu on Si(1 1 1)7 × 7 leads to formation of a disordered silicide layer in an initial regime before a well-ordered Cu(1 1 1) film is formed after deposition of the equivalent of 6 layers of Cu. In the regime below 6 layers of Cu the disorder is transferred to Al layers subsequently grown on top. The initial growth of up to 8 layers of Al on a well-ordered Si/Cu(1 1 1) layer leads to a disordered film due to the lattice mismatch between the two metals. When the Cu buffer layer and the Al over-layer are above 6 and 8 layers, respectively the Al film shows sharp low energy electron diffraction patterns and very sharp quantum well peaks in the valence band spectra signalling good epitaxial growth.     

Nonpolar a-plane GaN grown on r-plane sapphire using multilayer AlN buffer by metalorganic chemical vapor deposition

Mirror-like and pit-free non-polar a-plane (1 1 −2 0) GaN films are grown on r-plane (1 −1 0 2) sapphire substrates using metalorganic chemical vapor deposition (MOCVD) with multilayer high-low-high temperature AlN buffer layers. The buffer layer structure and film quality are essential to the growth of a flat, crack-free and pit-free a-plane GaN film. The multilayer AlN buffer structure includes a thin low-temperature-deposited AlN (LT-AlN) layer inserted into the high-temperature-deposited AlN (HT-AlN) layer. The results demonstrate that the multilayer AlN buffer structure can improve the surface morphology of the upper a-plane GaN film. The grown multilayer AlN buffer structure reduced the tensile stress on the AlN buffer layers and increased the compressive stress on the a-plane GaN film. The multilayer AlN buffer structure markedly improves the surface morphology of the a-plane GaN film, as revealed by scanning electron microscopy. The effects of various growth V/III ratios was investigated to obtain a-plane GaN films with better surface morphology. The mean roughness of the surface was 1.02 nm, as revealed by atomic force microscopy. Accordingly, the multilayer AlN buffer structure improves the surface morphology and facilitates the complete coalescence of the a-plane GaN layer.     

Thickness dependence on thermal stability of sputtered Ag nanolayer on Ti/Si(1 0 0)

Thermal stability of Ag layer on Ti coated Si substrate for different thicknesses of the Ag layer have been studied. To do this, after sputter-deposition of a 10 nm Ti buffer layer on the Si(1 0 0) substrate, an Ag layer with different thicknesses (150-5 nm) was sputtered on the buffer layer. Post annealing process of the samples was performed in an N₂ ambient at a flow rate of 200 ml/min in a temperature range from 500 to 700 °C for 30 min. The electrical property of the heat-treated multilayer with the different thicknesses of Ag layer was examined by four-point-probe sheet resistance measurement at the room temperature. Phase formation and crystallographic orientation of the silver layers were studied by θ-2θ X-ray diffraction analysis. The surface topography and morphology of the heat-treated films were determined by atomic force microscopy, and also, scanning electron microscopy. Four-point- probe electrical measurement showed no considerable variation of sheet resistance by reducing the thickness of the annealed Ag films down to 25 nm. Surface roughness of the Ag films with (1 1 1) preferred crystallographic orientation was much smaller than the film thickness, which is a necessary condition for nanometric contact layers. Therefore, we have shown that the Ag layers with suitable nano-thicknesses sputtered on 10 nm Ti buffer layer were thermally stable up to 700 °C.     

Effect of substrate temperature on structural, optical and electrical properties of pulsed laser ablated nanostructured indium oxide films

Nanocrystalline indium oxide (INO) films are deposited in a back ground oxygen pressure at 0.02 mbar on quartz substrates at different substrate temperatures (T_s) ranging from 300 to 573 K using pulsed laser deposition technique. The films are characterized using GIXRD, XPS, AFM and UV-visible spectroscopy to study the effect of substrate temperature on the structural and optical properties of films. The XRD patterns suggest that the films deposited at room temperature are amorphous in nature and the crystalline nature of the films increases with increase in substrate temperature. Films prepared at T_s ≥ 473 K are polycrystalline in nature (cubic phase). Crystalline grain size calculation based on Debye Scherrer formula indicates that the particle size enhances with the increase in substrate temperature. Lattice constant of the films are calculated from the XRD data. XPS studies suggest that all the INO films consist of both crystalline and amorphous phases. XPS results show an increase in oxygen content with increase in substrate temperature and reveals that the films deposited at higher substrate temperatures exhibit better stoichiometry. The thickness measurements using interferometric techniques show that the film thickness decreases with increase in substrate temperature. Analysis of the optical transmittance data of the films shows a blue shift in the values of optical band gap energy for the films compared to that of the bulk material owing to the quantum confinement effect due to the presence of quantum dots in the films. Refractive index and porosity of the films are also investigated. Room temperature DC electrical measurements shows that the INO films investigated are having relatively high electrical resistivity in the range of 0.80-1.90 Ωm. Low temperature electrical conductivity measurements in the temperature range of 50-300 K for the film deposited at 300 K give a linear Arrhenius plot suggesting thermally activated conduction. Surface morphology studies of the films using AFM reveal the formation of nanostructured indium oxide thin films.     

ZnO:Ag film growth on Si substrate with ZnO buffer layer by rf sputtering

ZnO buffer layers were deposited on n-Si (1 0 0) substrate by rf magnetron sputtering at a lower power of 40 W. Then Ag-doped ZnO (SZO) films were deposited on buffered and non-buffered Si at a higher sputtering power of 100 W. The effects of buffer layer on the structural, electrical and optical properties of SZO films were investigated. The three-dimensional island growth process of ZnO buffer layer was discussed. The energy band diagram of p-SZO/n-Si heterojunction was constructed based on Anderson's model. Results show the ZnO buffer layer leads to better properties of SZO film, including larger grain size, smoother surface, higher carrier mobility, better rectifying behavior, lower interface state density, and weaker deep-level emission. It is because the ZnO buffer layer effectively relaxes the partial stress induced by the large lattice mismatch between SZO and Si.     

Observation of ultra-broadband terahertz emission from ZnTe films grown by metaloganic vapor epitaxy

ZnTe films were grown on (0001) sapphire substrates by the metalorganic vapor phase epitaxy (MOVPE) method. Single crystalline (111) ZnTe epitaxial layers were confirmed by x-ray diffraction, reflection high-energy electron diffraction, and cathodoluminescence measurements. Emission of THz radiation with a spectral distribution up to 40 THz was clearly observed from the ZnTe film with a thickness of 10 μm. The results show that MOVPE is a promising growth method for obtaining high-quality ZnTe epitaxial films on sapphire substrates, which paves the way for obtaining thinner ZnTe films to provide a flatter frequency response in THz device applications.     

Effects of crystalline quality on the ultraviolet emission and electrical properties of the ZnO films deposited by magnetron sputtering

The ZnO films were deposited on c-plane sapphire, Si (0 0 1) and MgAl₂O₄ (1 1 1) substrates in pure Ar ambient at different substrate temperatures ranging from 400 to 750 °C by radio frequency magnetron sputtering. X-ray diffraction, photoluminescence and Hall measurements were used to evaluate the growth temperature and the substrate effects on the properties of ZnO films. The results show that the crystalline quality of the ZnO films improves with increasing the temperature up to 600 °C, the crystallinity of the films is degraded as the growth temperature increasing further, and the ZnO film with the best crystalline quality is obtained on sapphire at 600 °C. The intensity of the photoluminescence and the electrical properties strongly depend on the crystalline quality of the ZnO films. The ZnO films with the better crystallinity have the stronger ultraviolet emission, the higher mobility and the lower residual carrier concentration. The effects of crystallinity on light emission and electrical properties, and the possible origin of the n-type conductivity of the undoped ZnO films are also discussed.