STM spectroscopy on superconducting FeSe1−xTex single crystals at 300 mK

We report cryogenic scanning tunneling spectroscopy measurements on single crystals of superconducting FeSe_1−xTe_x, at doping levels of x=0.5 and 0.7, with critical temperatures . Atomically resolved topographic images were obtained, showing large-scale density-of-state clustering which appears to have no periodicity and to vary with the doping. Conductance spectra taken at 300 mK showed a generally asymmetric V-shaped background, along with a sharp dip structure within . These spectra appeared to vary over ∼nm length scale, and not correlated with the topography. The overall spectral evolution versus temperature is consistent with the dip structure arising from a superconducting energy gap which closes above T_c, and with the spectral background having a non-superconducting origin. The persistence of finite zero-bias conductance down to 300 mK, well below T_c, indicates the presence of low-energy quasiparticles on parts of the Fermi surface. We discuss our data in light of some other recent spectroscopic measurements of FeSe_1−xTe_x, and in terms of its characteristic band structure.     

Low-temperature measurements of magnetic susceptibility and specific heat of Eu2Ti2O7—An XY pyrochlore

Magnetic susceptibility obtained from magnetization measurement (for fields H=0.1 and 1.0 T) of polycrystalline Eu₂Ti₂O₇ shows two distinct features. Firstly, increases on cooling below 300 K and attains a temperature-independent constant value at 68 K (T_max). Secondly, shows an antiferromagnetic increase below 4.9±0.1 K. The former behavior is explained by crystal field (CF) theory. CF levels and wave functions of ground and excited states are determined accurately from analyses of and earlier reported Mössbauer and optical spectra. Analysis of vs. 1/T curve at low temperatures gives the classical nearest-neighbor exchange interaction J^cl=−0.76 K and a weak dipolar interaction D_nn=0.0056 K. C_P of polycrystalline sample of Eu₂Ti₂O₇ and Y₂Ti₂O₇ are measured between 1.8-35 and 1.8-120 K respectively and θ_D vs. T (K) curves are calculated. At 4 K, θ_D of Eu₂Ti₂O₇ shows a kink and dC_P/dT curve show a maximum. Optical results show energy exchange between Eu³⁺ ions at intrinsic and extrinsic (defect) sites via super-exchange interaction at low temperature which may account for the observed anomalous behavior of and C_P.     

Effect of Mn-doping on the electrical properties of Cu2GeSe3

In this work we report the temperature dependence of the resistivity ρ of p-Cu₂GeSe₃ and manganese-doped p-Cu₂GeSe₃ at low temperature. It was found that for a intrinsic sample ρ obeys the Shklovskii-Efros-type variable-range hopping resistivity law in the temperature range from 4 to 63 K. This behaviour is governed by generation of a Coulomb gap Δ=78 meV in the density of localized states. We find a low activation term T₀=0.24 K, which is an indication of a large localization length ξ. For Mn-doped sample a metal-insulator transition (MIT) is observed at T=65 K. On the basis of the Mott criterion for metal-insulator transition, the critical carrier density n_c is determined. From the analysis of resistivity data it is concluded that Mn acts as acceptor impurity.     

Temperature dependence of electrical resistivity for Ca-doped perovskite-type Y1−xCaxCoO3 prepared by sol-gel process

The temperature dependences of DC electrical resistivity for perovskite-type oxides Y_1−xCa_xCoO₃ (0?x?0.1), prepared by sol-gel process, were investigated in the temperature range from 20 K up to 305 K. The results indicated that with increase of doping content of Ca the resistivity of Y_1−xCa_xCoO₃ decreased remarkably, which was found to be caused mainly by increase of carrier (hole) concentration. In the whole temperature range investigated the temperature dependence of resistivity ρ(T) for the un-doped (x=0) sample decreased exponentially with decreasing temperature (i.e. ln ρ∝1/T), with a conduction activation energy ; the resisitivity of lightly doped oxide (x=0.01) possessed a similar temperature behavior but has a reduced E_a (0.155 eV). Moreover, experiments showed that the relationship ln ρ∝1/T existed only in high-temperature regime for the heavily doped samples (T?82 and ∼89 K for x=0.05 and 0.1, respectively); at low temperatures Mott's ln ρ∝T^−1/4 law was observed, indicating that heavy doping produced strong random potential, which led to formation of considerable localized states. By fitting of the experimental data to Mott's T^−1/4 law, we estimated the density of localized states N(E_F) at the Fermi level, which was found to increase with increasing doping content.     

Quadratic temperature dependence of electron-phonon scattering in disordered V1−xPdx alloys

We report the results of a comprehensive study of weak localization and electron-electron interaction effects in disordered V_1−xPd_x alloys whose compositions are close to the (low T_c) A15 V₃Pd compound. Magnetoresistivity and zero field resistivity have been measured within the temperature range 1.5≤T≤300 K. The low-temperature resistivity obeys a law, which is explained by electron-electron interaction. We have determined the electron-phonon scattering time (τ_e-ph) for V_1−xPd_x alloys. Our results indicate an anomalous electron-phonon scattering rate obeying quadratic temperature dependence. This observation is interpreted by the existing theories of electron-phonon interactions.     

Magnetocaloric properties of DyCo2−xGax alloys

The influence of the substitution of Ga atoms for Co atoms in DyCo₂ compounds on magnetocaloric properties has been investigated. A series of DyCo_2−xGa_x alloys with x=0, 0.03, 0.06, 0.1, 0.15, and 0.2 was prepared by the arc-melting method for this investigation. Experimental results revealed that the Ga substitution for Co in DyCo₂ can form a single phase with the cubic Laves phase structure up to x=0.2. As the Ga content x increases, the lattice parameter and the Curie temperature T_c increases from 143 to 196 K linearly. The maximum magnetic entropy changes in a low field change of 0-1.5 T, increasing from 8.24 to 10.61 J/K kg when the Ga content x increases from 0 to 0.03, but decreasing gradually to 3.51 J/K kg as the Ga content further increases to x=0.2. All the samples show a relatively large magnetic entropy change with very small hysteresis loss.     

Surface defect states of CdTexS1 − x quantum dots

Properties of surface defect states of CdTe_xS_1 − x quantum dots with an average diameter of 7 nm are investigated experimentally. The stoichiometric ratio is found to be for by use of the energy dispersive analysis of x-ray. The photoluminescence spectrum, the photoluminescence excitation spectrum, and the surface passivation are adopted to characterize the properties of surface defect states. The energy levels of surface defect states of CdTe_xS_1 − x quantum dots are also determined.     

Ac magnetotransport in La0.7Sr0.3Mn0.95Fe0.05O3 at low dc magnetic fields

We report the ac electrical response of La_0.7Sr_0.3Mn_1−xFe_xO₃(x=0.05) as a function of temperature, magnetic field (H) and frequency of radio frequency (rf) current (). The ac impedance (Z) was measured while rf current directly passes through the sample as well as in a coil surrounding the sample. It is found that with increasing frequency of the rf current, Z(T) shows an abrupt increase accompanied by a peak at the ferromagnetic Curie temperature. The peak decreases in magnitude and shifts down with increasing value of H. We find a magnetoimpedance of for at around room temperature when the rf current flows directly through the sample and when the rf current flows through a coil surrounding the sample. It is suggested that the magnetoimpedance observed is a consequence of suppression of transverse permeability which enhances skin depth for current flow. Our results indicate that the magnetic field control of high frequency impedance of manganites is more useful than direct current magnetoresistance for low-field applications.     

Specific heat anomalies in the quasi two-dimensional monophosphate tungsten bronzes KxP4W8O32

The monophosphate tungsten bronzes K_xP₄W₈O₃₂ (0.75<x<2) are quasi-two-dimensional conductors which show electronic transitions at a critical temperature T_c depending on the concentration of the alkali metal. The phase diagram shows a maximum at for x=1.30. We report specific heat measurements in the range 120-190 K. The thermal anomalies found at the transition temperature are larger than in conventional charge density wave materials. This corroborates that the transition is not a ‘pure’ charge density wave transition and that a structural transition dominates the instability.     

Electrical behavior of nano-polycrystalline (La1−yKy)0.7Ba0.3MnO3 manganites

We present a study of the structural and electrical behavior of nano-polycrystalline mixed barium and alkali substituted lanthanum-based manganite, (La_1−yK_y)_0.7Ba_0.3MnO₃ with y=0.0-0.3. The samples were synthesized by the polymerization complex sol-gel method. The powder X-ray diffraction (XRD) data of the samples show a single-phase character with space group. The magnetic and electrical transport properties of the nano-polycrystalline samples have been investigated in the temperature range 50-300 K and a magnetic field up to 10 kOe. The metal-insulator transition temperature T_p of all the samples decreased with potassium doping, and also, it increased slightly with the application of magnetic field. The low field magnetoresistance, which is absent in the single-crystalline perovskite, was observed and increased with decreasing temperature. Comparing the experimental resistivity data with the theoretical models shows that the high temperature electrical behavior of these samples is in accordance with the adiabatic small polaron-hopping model. In the metal-ferromagnetic region the resistivity is found to be quite well described by ρ=ρ₀+ρ₂T²+ρ_4.5T^4.5.     

Thermal annealing effects on the magnetic behavior of Ce2NiSi3

We have investigated the crystallographic, magnetic and thermodynamic properties of the as-cast and annealed Ce₂NiSi₃ alloys, crystallizing in the AlB₂-type hexagonal structure. The DC-magnetic susceptibility data show that the as-cast sample exhibits an antiferromagnetic (AFM) ordering below T_N= 3.8 K, whereas the annealed sample shows, at 4.2 K, a magnetic transition of AFM nature and, around 2.5 K, an additional anomaly. The specific heat shows a peak with at 3.8 K for the as cast sample, which shifts to lower temperatures when the magnetic field increases, consistent with the antiferromagnetic nature of the transition. On the other hand, in the annealed alloy, the maximum of the specific heat peak reaches at 4.2 K, and no additional anomalies were observed. The different magnetic behavior between the as-cast and annealed samples is attributed to thermal effects on the structural disorder of nickel and silicon atoms, as already observed in other isotypic R₂TSi₃ alloys, where R=U or Ce, and T= transition metal.     

Effect of cation size and disorder on the power loss of La0.7(Ba1−xSrx)0.3MnO3

The power loss P_L of La_0.7(Ba_1-xSr_x)_0.3MnO₃ (0≤x≤1) as a function of temperature, frequency (f) and amplitude of flux density (B_p), has been studied to analyze the effect of A-site cation mean radius <r_A> and size-disorders σ². It is found that as f is lower than 1 MHz, P_L is proportional to in the low induction region, and in the high induction region, indicating that P_L is dominated by hysteresis losses. For f approaches 1 MHz, P_L of the majority of samples obeys a law, which may be attributed to eddy current loss. The temperature dependence of P_L displays a peak around the transition from ferromagnetic-metal to paramagnetic-insulator, resembling the feature of the Rayleigh constant η. This case further demonstrates that in the low frequency region, P_L predominantly originates from hysteresis loss. A decrease in σ² with increasing x, will relieve local strain, raising η, thus give rise to an increase in P_L.