Structure and magnetic properties of Ca1−x−yMgxCu2+yO3 influenced by isoelectronic substitution x

Phases of the composition Ca_1−x−yMg_xCu_2+yO₃ have been prepared for the first time. The compounds are isostructural with the known end-members CaCu₂O₃ and MgCu₂O₃ showing a two-leg spin-ladder-like connection of copper and oxygen atoms within the Cu₂O₃-layer. Opposite the spin ladders this layer is folded, which results in a long-range antiferromagnetic ordering of these phases. The Néel temperature can be adapted by variation of x in Ca_1−x−yMg_xCu_2+yO₃ between 24 and 80 K. Several structural features, which influence the magnetic ordering, are discussed.     

Magnetic properties and magnetic structures of Sr3−xCaxRu2O7

We have measured magnetization curves and powder neutron diffraction of double-layered Ruddlesden-Popper type ruthenate Sr_3−xCa_xRu₂O₇ (x=1.5, 2.0 and 3.0). The field dependence of the magnetization revealed that the transition field of metamagnetic transition along the b-axis shifted to lower fields and that the transition became broad with increasing Sr content. The slope of the magnetization curve also increased with increasing Sr content below the metamagnetic transition. These results indicate that an itinerant component is partly introduced by the Sr substitution. From the magnetic reflection, on cooling below T_N, an additional reflection was observed at (0 0 1) for each x, and the amplitude increased with decreasing temperature. The observed diffraction patterns are very similar to those of Ca₃Ru₂O₇. We conclude that the magnetic structure of the antiferromagnetic ordered phase is basically the same structure with that of Ca₃Ru₂O₇.     

Magnetic and transport properties of SmCoAsO1−xFx

A series of SmCoAsO_1−xF_x (with x=0, 0.05, 0.1, and 0.2) samples have been prepared by solid state reactions. X-ray powder diffraction proved that all samples can be indexed as a tetragonal ZrCuSiAs-type structure. A clear shrinkage of the lattice constants a and c with increasing F content indicated that F has been doped into the lattice. The magnetic and transport properties of the samples have been investigated. Parent SmCoAsO compound exhibited complicated magnetism including antiferromagnetism, ferromagnetism, and ferrimagnetism. For the fluorine doped samples, the antiferromagnetic Néel temperatures were almost independent of the F content and metamagnetic transitions were observed below antiferromagnetic Néel temperatures. With increasing F content, high temperature (below 142 K) ferrimagnetic state gradually changed to ferromagnetic state. In the resistivity result, metallic conduction in the region of 2-300 K and Fermi liquid behavior at low temperatures were shown in all samples. Transport properties at applied magnetic fields showed anomalies at low temperatures.     

High sensitivity of magnetism of the “114” ferrimagnet CaBaCo4O7 to stoichiometry deviation

The effect of oxygen/cobalt off-stoichiometry upon magnetism in CaBaCo₄O₇ has been investigated. It is shown that the oxides CaBaCo₄O_7+δ and CaBaCo_4−xO_7−δ (0≤x≤0.20) synthesized below 1100 °C in air exhibit phase separation, where ferrimagnetic regions with T_C~56 K to 64 K coexist with regions of magnetic clusters. The latter are detected from ac-susceptibility measurements, which show various frequency dependent peaks at ~14–20 K, 37 K, and 45 K, depending on the stoichiometry. The origin of this phenomenon is attributed to the great sensitivity of the material to oxidation as the synthesis of temperature is lowered, leading to the introduction of additional Co³⁺ cations, with respect to the ideal formula CaBaCo₂²⁺Co₂³⁺O_7. This excess Co³⁺ tends to destroy the ferromagnetic zig-zag chains of the ferrimagnetic structure and creates various cobalt spin clusters, leading to the inherent phase separation in the samples.     

EPR investigations of oxidation effects in (V1−xMox)2−δO3

Electron paramagnetic resonance (EPR) investigations has been carried out on the new family of molybdenum doped vanadium sesquioxides (V_1−xMo_x)_2−δO₃. The oxidation effects were monitored from the rate of paramagnetic V⁴⁺ created when the sample is exposed to the air. The effects of the oxidation time, sample temperature, and annealing at 1000 °C under a diluted hydrogen atmosphere on the EPR signal features are analyzed. The V⁴⁺ concentration in the oxidized samples is determined and the relaxation effects driven by the conduction electrons are pointed out from the thermal behaviour of the EPR line features. EPR spectra of all the oxidized samples also reveal a small ferromagnetic contribution strongly correlated with the V⁴⁺ content.     

Magnetic properties of the ferrimagnetic cobaltite CaBaCo4O7

The magnetic properties of the ferrimagnetic cobaltite CaBaCo₄O₇ are systematically investigated. We find that the susceptibility exhibits a downward deviation below ∼360 K, suggesting the occurrence of short-range magnetic correlations at a temperature well above T_C. The effective moment is determined to be ., which is consistent with that expected for the Co²⁺/Co³⁺ high spin species. Using a criterion given by Banerjee [Phys. Lett. 12 (1964) 16], we demonstrate that the paramagnetic to ferrimagnetic transition in CaBaCo₄O₇ has a first order character.     

Magnetic and related properties of the solid solution CeCuxGa4−x

Physical properties of polycrystalline samples of CeCu_xGa_4−x (x = 0.2–1.4), crystallizing in the tetragonal BaAl₄-type structure (space group I 4/mmm), were studied by means of X-ray powder diffraction, magnetization, specific heat, electrical resistivity and magnetoresistivity measurements in wide temperature and magnetic fields ranges. The unit-cell volume of the system was found to decrease with increasing x (in total by about 4%) but the magnetic moments of Ce³⁺ ions remain localized in the whole x-range studied. The alloys exhibit ferromagnetic order at low temperatures, which manifests itself as distinct and relatively sharp anomalies in all the temperature characteristics measured. The ordering temperature decreases with increasing the Cu content from 5.5(1) K for x = 0.2 down to 1.35(5) K for x = 1.4, and the electrical transport properties of the system show some features characteristic of Kondo lattices.     

Low field AC susceptibility study of intergranular critical current density in Mg-substituted CuBa2Ca3Cu4O12−y high temperature superconductors

Measurements of the a.c.susceptibility (χ=χ′+iχ″) have been made on the Mg substituted high T_C superconducting system, CuBa₂(Mg_xCa_1−x)₃Cu₄O_12−y (Cu-1234) with x=0, 0.10 & 0.20, at different values of the a.c.field amplitude. Estimates of the intergranular critical current density(J_C) made from the field dependent χ″-T curves show an improvement in the Mg-substituted Cu-1234 system. Results have been analysed in the light of the crystal structure and the superconducting anisotropy factor (γ=ξ_ab/ξ_c) of the Cu-1234 system. Lower superconducting anisotropy emanating from Mg substitution has been found to be significant, resulting in better superconducting properties.     

Kondo behaviour of the solid solution (Ce1−xLax)PtGa

The solid solution (Ce_1−xLa_x)PtGa has been studied through X-ray diffraction, magnetization (σ(B)), magnetic susceptibility (χ(T)), electrical resistivity (ρ(T)), magnetoresistivity (MR) and heat capacity (C_P(T)) measurements. The Néel temperature (T_N=3.3 K) for CePtGa is lowered upon La substitution as observed from χ(T) and ρ(T) measurements. The Kondo temperature T_K as calculated from MR measurements is comparable to T_N and also decreases with La substitution. The volume dependence of T_K is in accordance with the compressible Kondo lattice model and a Doniach diagram of the results is presented. C_P(T) measurements are presented for CePtGa, Ce_0.2La_0.8PtGa and LaPtGa and the results are discussed in terms of the electronic and magnetic properties. Other features of interest are anomalies in ρ(T) and C_P(T) due to crystalline electric field effects and metamagnetism as observed in σ(B) studies for samples with 0≤x≤ 0.3.     

Electroresistance effect in La1−xCaxMnO3 (0<x<1) ceramics

Electroresistance (ER) effects were investigated for a full series of manganite ceramics La_1−xCa_xMnO₃ (0<x<1), synthesized by solid state reaction. The results indicate that while the ER effects are large only in the presence of electrically active, high E-field boundaries, the equilibrium or metastable electronic-magnetic states in the adjoining domains are also significant, as a large ER occurs only at x=0.51 and x=0.17; those compositions are both near a two-phase coexistence region, i.e. close to a compositional regime where equilibrium insulating/metallic phase domains and interfaces would occur spontaneously.     

Magnetic properties of prussian blue modified Fe3O4 nanocubes

Size controlled cubic Fe₃O₄ nanoparticles in the size range 90–10 nm were synthesized by varying the ferric ion concentration using the oxidation method. A bimodal size distribution was found without ferric ion concentration and the monodispersity increased with higher concentration. The saturation magnetization decreased from 90 to 62 emu/g when the particle size is reduced to 10 nm. The Fe₃O₄ nanoparticles with average particle sizes 10 and 90 nm were surface modified with prussian blue. The attachment of prussian blue with Fe₃O₄ was found to depend on the concentration of HCl and the particle size. The saturation magnetization of prussian blue modified Fe₃O₄ varied from 10 to 80 emu/g depending on the particle size. The increased tendency for the attachment of prussian blue with smaller particle size was explained based on the surface charge. The prussian blue modified magnetite nanoparticles could be used as a radiotoxin remover in detoxification applications.     

Structure and magnetic properties of perovskite Sr2CuNbO6−δ

Single phase perovskite Sr₂CuNbO_6−δ with a high proportion of Cu¹⁺ ions and oxygen vacancies was synthesized by solid-state reaction. The structure was determined by Rietveld method with space group Pm3m. Isotropic g value was evaluated from electron spin resonance (ESR) measurements. The ESR result is consistent with that of magnetic susceptibility.     

Magnetoelectric characterization of xNi0.75Co0.25Fe2O4-(1−x)BiFeO3 nanocomposites

Magnetoelectric (ME) nanocomposites containing Ni_0.75Co_0.25Fe₂O₄-BiFeO₃ phases were prepared by citrate sol-gel process. X-ray diffraction (XRD) analysis showed phase formation of xNi_0.75Co_0.25Fe₂O₄-(1−x)BiFeO₃ (x=0.1, 0.2, 0.3 and 0.4) composites on heating at 700 °C. Transmission electron microscopy revealed the formation of powders of nano order size and the crystal size was found to vary from 30 to 85 nm. Dispersion in dielectric constant (ε) and dielectric loss (tan δ) in the low-frequency range have been observed. It is seen that nanocomposites exhibit strong magnetic properties and a large ME effect. On increasing Ni_0.75Co_0.25Fe₂O₄ contents in the nanocomposites, the saturation magnetization (M_S) and coercivity (H_C) increased after annealing at 700 °C. The large ME output in the nanocomposites exhibits strong dependence on magnetic bias and magnetic field frequency. The large value of ME output can be attributed to small grain size of ferrite phase of nanocomposite being prepared by citrate precursor process.     

Electrical and electrochemical properties of molten salt-synthesized Li4Ti5−xSnxO12 (x=0.0, 0.05 and 0.1) as anodes for Li-ion batteries

Submicron-sized polyhedral Li₄Ti_5−xSn_xO₁₂ (x=0.0, 0.05, and 0.1) materials were successfully prepared by a single-step molten salt method. The structural, morphological, transport and electrochemical properties of the Li₄Ti_5−xSn_xO₁₂ were studied. X-ray diffraction patterns showed the formation of a cubic structure with a lattice constant of 8.31 Å, and the addition of dopants follows Vegard's law. Furthermore, FT-IR spectra revealed symmetric stretching vibrations of octahedral groups of MO₆ lattice in Li₄Ti₅O₁₂. The formation of polyhedral submicron Li₄Ti_5−xSn_xO₁₂ particles was inferred from FE-SEM images, and a particle size reduction was observed for Sn-doped Li₄Ti₅O₁₂. The chemical composition of Ti, O and Sn was verified by EDAX. The DC electrical conductivity was found to increase with increasing temperature, and a maximum conductivity of 8.96×10⁻⁶ S cm⁻¹ was observed at 200 °C for Li₄Ti₅O₁₂. The galvanostatic charge–discharge behavior indicates that the Sn-doped Li₄Ti₅O₁₂ could be used as an anode for Li-ion batteries due to its enhanced electrochemical properties.     

Structural,thermal and electrical properties of the semiconductor system Ag(1−x)CuxInSe2

This paper presents a study of bulk samples synthesized of the Ag_1−xCu_xInSe₂ semiconductor system. Structural, thermal and electrical properties, as a function of the nominal composition (Cu content) x=0.0, 0.2, 0.4, 0.6, 0.8, and 1.0 were studied. The influence of x on parameters such as melting temperature, solid phase transition temperature, lattice parameters, bond lengths, crystallite size t (coherent domain), electrical resistivity, electrical mobility and majority carrier concentration was analyzed. The electrical parameters are analyzed at room temperature. In general, it is observed that the properties of the Ag_1−xCu_xInSe₂ system for x≤0.4 are dominated by n-AgInSe₂, while for x>0.4, these are in the domain of p-CuInSe₂. The crystallite size t in the whole composition range (x) is of the order of the nanoparticles. Secondary phases (CuSe, Ag₂Se and InSe) in small proportion were identified by XRD and DTA.     

Simulation of Al/Fe disorder in Ca2FexAl2−xO5

A method is described which is capable of simulating disorder across a range of composition. It is used to study the disorder of iron and aluminium on the octahedral and tetrahedral cation sites in the Brownmillerite phase Ca₂Fe_xAl_2−xO₅. The arrangements with the lowest lattice energies are those that maximize the number of Fe³⁺ on octahedral sites throughout the composition range. An exchange of one Fe³⁺ with one Al³⁺, which results in a decrease in the number of iron ions on octahedral sites, increases the lattice energy by an amount that is dependent on x but is independent of the number of exchanges. The exchange of trivalent cations also results in an expansion in the b lattice direction, accompanied by a decrease in the a and c directions across the full range of composition.     

Chemical pressure effect in CeFeAs1−xPxO0.95F0.05

We investigate the chemical pressure effect due to P doping in the CeFeAs_1−xP_xO_0.95F_0.05(0≤x≤0.4) system. The compound CeFeAsO_0.95F_0.05 without P doping is on the boundary between antiferromagnet (AFM) and superconductor. The AFM order of Ce³⁺ local moments causes a significant reentrance behavior in both resistivity and magnetic susceptibility. Upon P doping, T_c increases and reaches a maximum of 21.3 K at x=0.15, and then it is suppressed to lower temperatures. Meanwhile, the AFM order of Ce³⁺ ions remains nearly the same in the whole doping range (0≤x≤0.4). Our experimental results suggest a competition between superconductivity and Kondo effect in the Ce 1111 system.     

Specific heat and magnetic susceptibility of single-crystalline ZnCr2−xAlxSe4 (x=0.15, 0.23)

A correlation between the second critical field H_c2 of the helix to paramagnetic transition and the magnetic specific heat C-peak was found in ZnCr_2−xAl_xSe₄ spinel single crystals with x=0.15, 0.23. The specific heat peak is anomalously sharp for all finite magnetic fields used here and this points to a first order magneto-structural transition (from cubic to tetragonal symmetry). The C(T)-peak is increasingly suppressed as the external field increases. Approaching the Neel temperature T_N, a broad ac-magnetic susceptibility peak is observed for zero dc-magnetic field. That peak does not show an energy loss and thus points towards a return to a second order type of transition. The magnetic contribution to the specific heat displays a sharp peak at T_N and is maximal at the spin fluctuation temperature T_sf=34 K. T_sf is related to the maximum of the magnetic susceptibility at T_m=40 K (at 50 kOe) in the spin fluctuation region, as evidenced by the entropy exceeding 90% of the entropy calculated classically for the complete alignment of the Cr spins, (2−x)R ln(2S+1). The X-ray photoelectron spectroscopy (XPS) data indicate that Al-substitution does not affect Cr³⁺ 3d³ electronic configuration.     

Immiscibility in the Fe3O4-FeCr2O4 spinel binary

A recent thermodynamic model of mixing in spinel binaries, based on changes in cation disordering (x) between tetrahedral and octahedral sites [Am. Mineral. 68 (1983) 18, 69 (1984) 733], is investigated for applicability to the Fe₃O₄-FeCr₂O₄ system under conditions where incomplete mixing occurs. Poor agreement with measured consolute solution temperature and solvus [N. Jb. Miner. Abh. 111 (1969) 184] is attributed to neglect of: (1) ordering of magnetic moments of cations in the tetrahedral sublattice antiparallel to the moments of those in the octahedral sublattice and (2) pair-wise electron hopping between octahedral site Fe³⁺ and Fe²⁺ ions. Disordering free energies (ΔG_D), from which free energies of mixing are calculated, are modeled by

     

Highly cation-deficient manganese perovskite, La1−xMn1−yO3 with x=y

Oxidative (δ>0) nonstoichiometry in the perovskite ‘LaMnO_3+δ’ has been known to be manifested not with O interstitials but rather with cation vacancies of equal amounts at the two cation sites, La and Mn, i.e. La_1−xMn_1−yO₃ with x=y. Here, we report the fabrication of samples with record-high cation-vacancy concentrations (x>0.12 or δ>0.4) by means of a variety of high-pressure oxygenation techniques. Linear (negative) dependence of the cell volume on x was observed within the whole x range investigated, down to 56.9 Å³ (per formula unit) for a sample oxygenated at 5 GPa and 1100 °C using Ag₂O₂ as an excess oxygen source. With increasing degree of cation deficiency in La_1−xMn_1−xO₃, the ferromagnetic transition temperature was found to follow a bell shape with respect to x exhibiting a maximum of ∼250 K about x≈0.1. For moderately oxygenated samples large magnetoresistance effect was evidenced.