Preparation of TiO<Subscript>2</Subscript>-coated LiCo<Subscript>1/3</Subscript>Ni<Subscript>1/3</Subscript>Mn<Subscript>1/3</Subscript>O<Subscript>2</Subscript> by electrostatic self-assembly method and its properties

A precursor of TiO₂–LiCo_1/3Ni_1/3Mn_1/3O₂ was prepared by electrostatic self-assembly method. The final product was obtained by heating the precursor at 400–450 °C for 4–6 h in air. X-ray diffraction (XRD), scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS), and electrochemical tests were used to examine the structural, morphology, elementary valence, and electrochemical characteristics. XRD indicated that the TiO₂-coated material can be indexed by α-NaFeO₂ layered structure, which belongs to hexagonal-type space group R3m. XPS results confirmed the existence of TiO₂ compound on the surface of the coated sample. The SEM image showed that the material had spherically porous morphology with the uniform size about 6 μm. The initial charge–discharge capacity of the TiO₂-coated LiCo_1/3Ni_1/3Mn_1/3O₂ material was 168.8/160.0 mAh/g. After 60 cycles, the discharge capacity of the TiO₂-coated LiCo_1/3Ni_1/3Mn_1/3O₂ sample was 147.0 mAh/g, and the coulombic efficiency was 94.0%. Compared with the uncoated sample, the electrochemical performance of TiO₂-coated LiCo_1/3Ni_1/3Mn_1/3O₂ was improved.     

n/p-Type changeable semiconductor TiO<Subscript>2</Subscript> prepared from NTA

A novel kind of nano-sized TiO₂ (anatase) was obtained by high-temperature (400–700°C) dehydration of nanotube titanic acid (H₂Ti₂O₄(OH)₂, NTA). The high-temperature (400–700°C) dehydrated nanotube titanic acids (HD-NTAs) with a unique defect structure exhibited a p-type semiconductor behavior under visible-light irradiation ( nm, E _photon=2.95 eV), whereas exhibited an n-type semiconductor behavior irradiated with UV light ( nm, E _photon=3.40 eV).     

First-principles calculations on implanted TiO<Subscript>2</Subscript> by 3d transition metal ions

3d transition metal (V, Cr and Fe) ions are implanted into TiO₂ by the method of metal ion implantation. The electronic band structures of TiO₂ films doped 3d transition metal ions have been analyzed by ab initio band calculations based on a self-consistent full-potential linearized augmented plane-wave method within the first-principle formalism. Influence of implantation on TiO₂ films is examined by the method of UV-visible spectrometry. The results of experiment and calculation show that the optical band gap of TiO₂ films is narrowed by ion implantation. The calculation shows that the 3d state of V, Cr and Fe ions plays a significant role in red shift of UV-Vis absorbance spectrum.     

Low-frequency Raman characterization of size-controlled anatase TiO<Subscript>2</Subscript> nanopowders prepared by continuous hydrothermal syntheses

The advantages of a recently presented continuous hydrothermal elaboration route for size-controlled anatase TiO₂ nanoparticles are investigated. Nanopowders prepared by this route and using a soft chemistry route are characterized using X-ray diffraction, surface area measurements, high-resolution electron microscopy and Raman spectroscopy with an emphasis on the determination of the size distribution with low-frequency Raman measurements. The continuous hydrothermal route is shown to be more suitable for producing narrower size distributions.     

Absorption by CS<Subscript>2</Subscript> molecules on “hot” band emission lines from a TEA CO<Subscript>2</Subscript> laser

We have measured absorption of emission from a TEA CO₂ laser, lasing on hot band lines, in pure CS₂ and a mixture of CS₂ with air, and we have determined the optimal lines for optical excitation. Numerical modeling has shown that as the peak intensity of the pump radiation is increased, we observe absorption saturation, the extent of which decreases as the pressure increases. The major factor responsible for absorption saturation is the “rotational bottleneck” effect. Depending on the peak intensity of the radiation, addition of a buffer gas can lead to an increase or decrease in the absorption. __________ Translated from Zhurnal Prikladnoi Spektroskopii, Vol. 74, No. 1, pp. 61–66, January–February, 2007.     

Anomalous absorption in H<Subscript>2</Subscript>CN and CH<Subscript>2</Subscript>CN molecules

Structures of H₂CN and CH₂CN molecules are similar to that of H₂CO molecule. The H₂CO has shown anomalous absorption for its transition 1₁₁–1₁₀ at 4.8 GHz in a number of cool molecular clouds. Though the molecules H₂CN and CH₂CN have been identified in TMC-1 and Sgr B2 through some transitions in ortho as well as in para species, here we have investigated the condition under which transitions 1₁₁–1₁₀ and 2₁₂–2₁₁ of these molecules may show anomalous absorption. For the present investigation, we have calculated energy levels and radiative transition probabilities. However, we have used scaled values for collisional rate coefficients. We found that relative values of collisional rate coefficients can produce the required anom-alous absorption in 1₁₁–1₁₀ and 2₁₂–2₁₁ transitions in the molecules.      

Influence of the sample orientation in Sn<Subscript>2</Subscript>P<Subscript>2</Subscript>S<Subscript>6</Subscript> crystals on the hydrostatic piezoelectric coefficients

The influence of the sample orientation on the effective value of the hydrostatic piezoelectric coefficients d _h ⁽ⁱ⁾ of Sn₂P₂S₆ crystals has been studied. The hydrostatic piezoelectric coefficients d _h ⁽¹⁾ and d′ _h ⁽³⁾ , were measured, d _h ⁽¹⁾ =(244±3) pC/N and d′ _h ⁽³⁾ =(92±1) pC/N. The hydrostatic piezoelectric coefficient d _h ⁽³⁾ for orthogonal axis system was calculated to be d _h ⁽³⁾ =(87±2) pC/N. The, optimal orientation of the sample has been found as (Xy l)−20°-cut. Maximal value of the effective hydrostatic piezoelectric coefficient d _h ⁽¹⁾ equals 260 pC/N. Double rotated samples were also studied. The orientation of the samples insensitive to the pressure has been found. The theoretical mean value of hydrostatic piezoelectric coefficient (d _h ) _mean corresponding to randomly oriented Sn₂P₂S₆ grains in a poled composite has been calculated to be (d _h ) _mean =136 pC/N.     

Synthesis of ZnAl<Subscript>2</Subscript>O<Subscript>4</Subscript>/α-Al<Subscript>2</Subscript>O<Subscript>3</Subscript> complex substrates and growth of GaN films

With the solid phase reaction between pulsed-laser-deposited (PLD) ZnO film and α-Al₂O₃ substrate, ZnAl₂O₄/α-Al₂O₃ complex substrates were synthesized. X-ray diffraction (XRD) spectra show that as the reaction proceeds, ZnAl₂O₄ changes from the initial (111)-oriented single crystal to poly-crystal, and then to inadequate (111) orientation. Corresponding scanning electron microscope (SEM) images indicate that the surface morphology of ZnAl₂O₄ transforms from uniform islands to stick structures, and then to bulgy-line structures. In addition, XRD spectra present that ZnAl₂O₄ prepared at low temperature is unstable at the environment of higher temperature. On the as-obtained ZnAl₂O₄/α-Al₂O₃ substrates, GaN films were grown without any nitride buffer using light-radiation heating low-pressure MOCVD (LRH-LP-MOCVD). XRD spectra indicate that GaN film on this kind of complex substrate changes fromc-axis single crystal to poly-crystal as ZnAl₂O₄ layer is thickened. For the single crystal GaN, its full width at half maximum (FWHM) of X-ray rocking curve is 0.4°. Results indicate that islands on thin ZnAl₂O₄ layer can promote nucleation at initial stage of GaN growth, which leads to the (0001)-oriented GaN film.     

Controlling the orientation of ZnO nanorod arrays using TiO<Subscript>2</Subscript> thin film templates dip-coated by sol–gel

The oriented ZnO nanorod arrays have been synthesized on a silicon wafer that coated with TiO₂ films by aqueous chemical method. The morphologies, phase structure and the photoluminescence (PL) properties of the as-obtained product were investigated by field-emission scanning electron microscopy (FE-SEM), X-ray diffractometer (XRD), transmission electron microscope (TEM) and PL spectrum. The nanorods were about 100 nm in diameter and more than 1 μm in length, which possessed wurtzite structure with a c axis growth direction. The room-temperature PL measurement of the nanorod arrays showed strong ultraviolet emission. The effect of the crystal structure and the thickness of TiO₂ films on the morphologies of ZnO nanostructures were investigated. It was found that the rutile TiO₂ films were appropriate to the oriented growth of ZnO nanorod arrays in comparison with anatase TiO₂ films. Moreover, flakelike ZnO nanostructures were obtained with increasing the thickness of anatase TiO₂ films.     

Inelastic neutron scattering and lattice dynamics of NaNbO<Subscript>3</Subscript> and Sr<Subscript>0.70</Subscript>Ca<Subscript>0.30</Subscript>TiO<Subscript>3</Subscript>

NaNbO₃ and (Sr,Ca)TiO₃ exhibit an unusual complex sequence of temperature- and pressure-driven structural phase transitions. We have carried out lattice dynamical studies to understand the phonon modes responsible for these phase transitions. Inelastic neutron scattering measurements using powder samples were carried out at the Dhruva reactor, which provide the phonon density of states. Lattice dynamical models have been developed for SrTiO₃ and CaTiO₃ which have been fruitfully employed to study the phonon spectra and vibrational properties of the solid solution (Sr,Ca)TiO₃.      

Preparation of nanosized Bi<Subscript>2</Subscript>WO<Subscript>6</Subscript> using different content of starting materials and their photoactivities

A series of nanosized Bi₂WO₆ catalysts was synthesized using various starting materials, and they were characterized by X-ray diffractometry, transmission electron microscopy, and diffuse reflectance spectroscopy. Rhodamine-B (RhB) photodegradation in aqueous medium was employed as a probe reaction to test the photoactivity of the as-prepared samples. Dependence of the photocatalytic activities on different contents of the starting materials was examined under visible irradiation (λ > 400 nm). The sample prepared in the following conditions: reaction time 24 h, the pH of the solution 7, the Bi³⁺ amount in the start precipitates 5 mmol — exhibited the highest photochemical activity when the hydrothermal temperature was settled at 180°C. Published in Zhurnal Prikladnoi Spektroskopii, Vol. 76, No. 2, pp. 243–249, Martch–April, 2009.     

Characterization of Y<Subscript>2</Subscript>BaCuO<Subscript>5</Subscript> nanoparticles synthesized by nano-emulsion method

Nanoscale yttrium–barium–copper oxide (Y₂BaCuO₅, Y211) particles were synthesized using the emulsion method and the solution method. The basic water-in-oil (w/o) emulsion system consisted of n-octane (continuous oil phase), cetyltrimethylammonium bromide (cationic surfactant), butanol (cosurfactant) and water. The composition of the emulsion system was varied and characterized by measuring the conductivity of the solutions and droplet size. The droplet size of emulsion was determined by using the dynamic light scattering method. The water content, cosurfactant content, and surfactant/n-octane ratio affected the droplet size which was in the range of 3–8 nm, and hence the w/o emulsion system was referred to as a nano-emulsion system. A model was used to verify the droplet size. The influence of salt (Y₂(NO₃)₃) content on the droplet size was investigated and the addition of salt reduced the droplet size. The effects of reaction time and temperature on the Y211 particle sizes were also investigated. The particles were characterized using the TEM, SEM, and XRD. Nanoparticles produced by the nano-emulsion method were calcined at 850°C to form the Y211 phase as compared to solid state processing temperature of 1050°C. Based on the TEM analysis, the average diameter of the Y211 particles produced using the nano-emulsion method was in the range of 30–100 nm. The effect of adding 15% Y211 nanoparticles to the superconductor YBCO-123 as flux pinning centers, was investigated, and the transition temperature was reduced by 3 K.     

Investigation on structural characteristics of PVDF–AgCF<Subscript>3</Subscript>SO<Subscript>3</Subscript>–Al<Subscript>2</Subscript>O<Subscript>3</Subscript> nanocomposite solid polymer electrolyte system

There has been an increasing interest towards the incorporation of nanosize ceramic fillers in polymer electrolytes. Solid polymer electrolytes based on polyvinylidene fluoride (PVDF), silver triflate (AgCF₃SO₃), and x wt% of aluminum oxide (Al₂O₃) nanopowders (where x = 1, 3, 5, and 10, respectively) have been prepared using solution casting technique. The structural characteristics of these thin film specimens were studied using Fourier transform infrared (FTIR) and X-ray diffraction (XRD) patterns at room temperature. The appearance of new absorption bands and gradual shifts observed in some characteristic peaks confirmed the complex formation between polyvinylidene fluoride and silver triflate. Furthermore, the addition of nanosized filler Al₂O₃ has also indicated the interaction of the filler with the polymer salt complex. The XRD patterns obtained for all these samples in the 2θ range 10° to 70° showed the amorphous nature of these samples. Paper presented at the Third International Conference on Ionic Devices (ICID 2006), Chennai, Tamilnadu, India, December 7–9, 2006.     

VUV luminescence of Er<Superscript>3+</Superscript> ions in LiYF<Subscript>4</Subscript> and BaY<Subscript>2</Subscript>F<Subscript>8</Subscript> crystals

Vacuum ultraviolet luminescence of Er³⁺ ions in LiYF4 and BaY₂F₈ crystals has been investigated. It is revealed that under excitation by 193 nm radiation from an ArF excimer laser the interconfigurational 5d–4f radiative transitions in Er³⁺ ions are observed. It is shown that from the LiYF₄:Er crystal only the spin-forbidden luminescence (λ = 165 nm) is detected, whereas both the spin-forbidden (λ = 169 nm) and spin-allowed (λ = 160.5 nm) components are observed from the BaY₂F₈:Er crystal.     

Surface morphology of PrBa<Subscript>2</Subscript>Cu<Subscript>3</Subscript>O<Subscript>7-δ</Subscript> single crystals after the long-lasting high-temperature reduction

The results of the detailed scanning electron microscopy study of PrBa₂Cu₃O_7-δ single crystals after the long-lasting high-temperature post-growth treatment are reported. The presence of the unstable decomposition products on the crystal surface indicates that the onset of superconductivity must be related to the structural transformations in the bulk (approximately 20% of the total volume of the examined crystals). The time-dependent character of the superconductivity in the Pr-123 crystals could be attributed to the migration of defects in the Pr−Ba sublattice from the bulk toward the surface.     

One-step synthesis of colloidal Mn<Subscript>3</Subscript>O<Subscript>4</Subscript> and γ-Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> nanoparticles at room temperature

A facile room-temperature synthesis has been developed to prepare colloidal Mn₃O₄ and γ-Fe₂O₃ nanoparticles (5 to 25 nm) by an ultrasonic-assisted method in the absence of any additional nucleation and surfactant. The morphology of the as-prepared samples was observed by transmission electron microscopy. High-resolution transmission electron microscopy observations revealed that the as-synthesized nanoparticles were single crystals. The magnetic properties of the samples were investigated with a superconducting quantum interference device magnetometer. The possible formation process has been proposed.     

Study of structural phase transitions in YBa<Subscript>2</Subscript>Cu<Subscript>3</Subscript>O<Subscript>6+δ</Subscript> by x-ray photoelectron spectroscopy

We have used x-ray photoelectron spectroscopy to investigate the charge state of oxygen found in the basal structural plane of YBa₂Cu₃O₆+γ.. We have observed a change in this state after thermal treatment, with a transition to the adjacent structural phase region. We have shown that changes in the charge state of oxygen can be used as an indicator of structural changes occurring in YBa₂Cu₃O₆+δ.. We have found that the rate of structural relaxation yttrium barium cuprate depends on the amount of structural water it contains. __________ Translated from Zhurnal Prikladnoi Spektroskopii, Vol. 74, No. 2, pp. 195–198, March–April, 2007.     

Structural relaxation of Zr<Subscript>41</Subscript>Ti<Subscript>14</Subscript>Cu<Subscript>12.5</Subscript>Ni<Subscript>10</Subscript>Be<Subscript>22.5</Subscript> bulk metallic glass under high pressure

Zr₄₁Ti₁₄Cu_12.5Ni₁₀Be_22.5 bulk metallic glass (BMG) is annealed at 573 K under 3 GPa and its structural relaxation is investigated by X-ray diffraction, ultrasonic study, compression as well as sliding wear measurements. It is found that after the ZrTiCuNiBe BMG sample was annealed under high pressure, the mechanical properties were improved. Moreover, theBMG with relaxed structure exhibits markedly different acoustic properties. These results are attributed to the fact that relaxation under high-pressure results in a microstructural transformation in the BMG.     

Accuracy in determination of the temperature and partial pressure of CO<Subscript>2</Subscript> in CO<Subscript>2</Subscript>:N<Subscript>2</Subscript>:H<Subscript>2</Subscript>O:NO<Subscript>2</Subscript> mixtures by multiple-frequency laser probing

We present the results of analysis of the errors introduced by hot-band transitions 11¹0-01¹1, 03¹0-01¹1, 12⁰0-12⁰1 of the CO₂ molecule and the absorption lines of the H₂O and NO₂ molecules in determination of the temperature and partial pressure of CO₂, included in the gas mixture CO₂: N₂:H₂O: NO₂ at atmospheric pressure, by multiple-frequency laser probing using a CO₂ laser tunable over the lines of the 00⁰1-[10⁰0,02⁰0]_I,II ground-state laser transitions. __________ Translated from Zhurnal Prikladnoi Spektroskopii, Vol. 74, No. 6, pp. 810–815, November–December, 2007.     

Synthesis of transparent BaTiO<Subscript>3</Subscript> nanoparticle/polymer hybrid

Transparent BaTiO₃ nanoparticle/polymer hybrid was synthesized by polymerization and hydrolysis of barium titanium alkoxide modified with 2-vinyloxyethoxy ligand. Barium alkoxide, titanium alkoxide and 2-vinyloxyethanol were reacted affording a BaTiO₃ precursor, which was then hydrolyzed and polymerized to form BaTiO₃ particle/polymer hybrids below 100°C. BaTiO₃ particles increased in crystallinity with increasing water amount for hydrolysis. The absorption edge of the hybrid film on silica plates shifted to shorter wavelength with decreasing crystallite size. Nano-sized BaTiO₃ particle/polymer hybrid polymerized with methyl methacrylate (MMA) was shaped into a transparent and self-standing film with a refractive index of 1.595 at 589 nm.