La2O2S∶Mn2+荧光粉的微波合成及其荧光特性

Using La₂(SO₄)3 and the active carbon powder as reactants, La₂O₂S∶Mn²⁺ red phosphor was synthesized by microwave radiation method. The phosphor was characterized by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), laser-diffraction size analyzer and fluorospectrophotometer. The XRD analysis showed that the phosphor was pure phase La₂O₂S. The phosphor of La₂O₂S∶Mn²⁺ showed hexagonal crystal structure with diverse shapes, such as spherical and rod, with average particle size of 10.22 μm. The emission and excitation spectra of the phosphor were determined by fluorospectrophotometer and the results showed that the excitation spectrum of the phosphor under 600 nm emission wavelength was excitation bands between 250 nm and 350 nm with a peak value of 303 nm. Then ,when exicited under UV 303 nm, the phosphor showed broad band emission of 550~700 nm with a peak at 607 nm. In addition, the optimal effects were obtained for the phosphor preparation when the concentration of the activator Mn²⁺ was x_Mn=0.01, the ratio of C and O (n_C / n_O) in the reactants was 0.6∶1, and the time of reaction was about 1 h. La₂O₂S∶Mn²⁺ has strong absorption of UV spectrum and can emit bright red light.     

水溶性荧光CdSe量子点的合成及其在指纹显现中的应用

Water-soluble fluorescent CdSe quantum dots(QDs) were synthesized by using Se、Na₂SO₃ and CdCl₂ as precursors and mercaptoacetic acid(TGA) as modifier. The effects of refluxing time and initial pH values of the reaction on the particle size and fluorescence intensity of CdSe QDs were studied. The XRD、HRTEM and fluorescent spectroscopy were employed to characterize these samples. It is found that CdSe QDs with crystalline size of 2～3 nm are homogeneously distributed in the organic matrix. The maximum fluorescence absorption and emission peak of CdSe QDs solution are at 450 nm and 562 nm, respectively. The fingerprint details on the surface of smooth objects were clearly developed with CdSe QDs solution under irradiation of UV lights.     

球形Gd2O3∶Eu纳米发光材料的制备

Spherical nanometer Gd₂O₃∶Eu luminescent materials were prepared by homogeneous precipitation method, and the properties were studied also. TG, FTIR and XRD analysis showed that the precursor was carbonate, the cubic Gd₂O₃was obtained after calcination. TEM photographs indicated that the samples were spherical and well dispersed with nanometer and submicrometer size of 200～300 nm which is the nanoparticles’ aggregate. The mechanics of agglomerating growth is also discussed. ED photograph showed that the particle was crystalline. The PL analysis exhibited that CTB band of nanometer Gd₂O₃∶Eu was of 17 nm red shift to bulk materials, and the emission peak was broadened due to the surface and interface effect of nanocrystals.     

二硫代乙二酰胺合镍在硫化镉纳米晶表面的逐层配位组装

CdS nanocrystals, which were surface modified by poly (nickel dithioxamide) [Ni(DTO)]_n, were prepared and characterized. TEM image showed that the shape and the outward aspect of the modified CdS sample were essentially the same as those of the original material and no impurities were found. The characteristic IR peaks at 1 513cm^-1 and 870 cm^-1 confirmed the success in assembling [Ni(DTO)]_n on the surface of CdS. For XPS spectra, the characteristic bands of Ni2p3/2 and Ni2p1/2 appeared at 856 eV and 877 eV indicating the nickel in Ni(Ⅱ) oxidation state. The solid state electronic spectra showed the improvement in surface energy gap, which was changed from 2.38 eV to below 1.91 eV.     

自激活白光发射Ba2TiP2O9发光材料的发光特性

The Ba₂TiP₂O₉ phosphor was synthesized via the conventional high-temperature solid-state method. The Ba₂TiP₂O₉ phosphor showed high luminance white-light emitting when excited under 254 nm radiation. Furthermore, obvious long-lasting phosphorescence could be observed when the UV excitation source had been removed. XRD and photoluminescence (PL) spectra as well as the luminance decay were used to characterize the synthesized phosphor. The results of XRD indicated that the products obtained under 1 100 ℃ for 3 h had a good crystallization. Both the PL spectra and luminance decay measurement revealed that this kind of phosphors was a new kind of white-light-emitting phosphor. The thermoluminescence properties have also been investigated. The energy level of the 352 K and 493 K TL peaks have also been calculated and found that their energy level values were 0.35 eV and 1.08 eV, respectively. The 352 K TL peak is responsible for the origin of the long-lasting phosphorescence.     

球形La2O3∶Eu纳米晶的制备及其发光特性

The spheric La₂O₃∶Eu nanocrystals were prepared using NH₃·H₂O-NH₄HCO₃ mixture as precipitant. The material was characterized by FTIR, XRD and TEM techniques. The luminescence properties of Eu³⁺ in spheric La₂O₃ were measured by three dimension spectra, emission and excitation spectra. The results indicate that the La₂O₃∶Eu nanocrystals are in hexagonal phase by annealing at 800 ℃, the crystal size is about 30 nm. The maximum emission and excitation wavelength were determined by three dimensional spectroscopy to be at 591 nm and 394 nm, respectively. In emission spectrum the band at 591 nm and 612 nm are corresponding to ⁵D₀-⁷F₁ and ⁵D₀-⁷F₂ transition of Eu³⁺ ions. With increasing in annealing temperature the differences of intensity of the two transitions are increased. This phenomenon shows that the luminescence intensity of La₂O₃∶Eu nanocrystals can be tuned by changing annealing temperature.     

发光材料BaAl2Si2O8∶Eu2+的物相结构与发光性能

A phosphor, Ba_0.97Al₂Si₂O₈∶Eu²⁺, was synthesized by high temperature solid-phase method at different temperatures. The samples were characterized by TG/DTA, XRD and fluorescence spectroscopy. The results show that the main phase for host of these luminescence materials is barium feldspar BaAl₂Si₂O₈∶Eu²⁺ and there is a transition from hexagonal crystal system to monoclinic crystal system in the process of the sintering of barium feldspar. The luminescent phenomen of barium feldspar with hexagonal structure can not be observed under the excitation of ultraviolet lamp of 365 nm while the barium feldspar with monoclinic structure has excellent luminescence properties. The excitation spectra of all these samples show broad band spectra ranging from 250～390 nm with peak at λ_ex of 357 nm,which indicates that these samples can be effectively excited by near ultraviolet ; the emission spectra range from 380～600 nm with peak at λ_em of 433 nm. The luminescent intensity increases then decreases with the concentration of doping Eu²⁺ ions. When the concentration of dopants is 2.5mol%, the luminescent intensity reaches the maximum value. When the concentration of Eu²⁺ ions changes from 0.5mol% to 2.5mol%, the emission peak has a red shift from 427 nm to 440 nm.     

高岭石结构缺陷的 1H MAS NMR和Raman研究

The structure default of kaolinites was characterized with ¹H MAS NMR and Raman spectra. Although the HI indexes of Suzhou and Maoming kaolinite are similar, their ¹H MAS NMR and Raman spectra are very different. ¹H MAS NMR showed that the hydroxyl proton chemical shifts of Suzhou kaolinite are in the higher field and with larger different between the inner surface hydroxyls protons and inner hydroxyls proton chemical shifts than Maoming kaolinite. Raman spectra showed that the surface hydroxyls stretching vibration bands of Suzhou kaolinite are in the high frequency region, and the half height widths of the bands are 7.0～14 cm^-1. The area ratio S_z/(S_z+S_A), where S_Z and S_A are the areas of bands 3685 cm^-1 and 3695 cm^-1 respectively, is 0.23. But the surface hydroxyls stretching vibration bands of Maoming kaolinite are in the low frequency region, and the half height widths of the bands are 8.9～15.1 cm^-1. The area ratio S_z/(S_z+S_A) is 0.77. Those data proved that Suzhou kaolinite has lower structure default than Maoming kaolinite and ¹H MAS NMR and Raman spectra are effective method for study of kaolinite structure default.     

TiO2纳米管负载Ag、Au、Pt纳米粒子的微波合成与表征(英)

TiO₂ nanotubes were prepared under normal pressure at a temperature of 120 ℃. Ag, Au, Pt nanoparticles supported on TiO₂ nanotubes were prepared by microwave assisted heating polyol process. TEM images showed that microwave prepared Ag, Au, Pt nanoparticles supported on TiO₂ nanotubes were small and well dispersed on the surface of the TiO₂ nanotubes. UV-Vis absorption spectra showed that the absorbance of Ag/TiO₂ nanotubes and Au/TiO₂ nanotubes in the visible light range increased greatly compared to the single titania nanotubes.     

N 掺杂TiO2光催化剂的制备及其可见光活性研究

A visible-light-active photocatalyst was prepared by calcination of the hydrolysis product of tetrabutyl titanate with ammonia as precipitant. The photocatalyst was characterized by X-ray diffraction (XRD), UV-Vis diffuse reflection spectra (DRS), thermal gravimetric-differential thermal analysis (TG-DTA), X-ray photoelectron spectroscopy (XPS), scanning electron microscope (SEM). The color of the photocatalyst was yellow and could absorb light wavelength under 550 nm as measured by DRS. The catalyst calcined at higher temperature will give lower absorbance for visible light. Structures of the sample were characterized mainly to be anatase by XRD except for the sample calcined at 700 ℃ which gave mixtures of anatase and rutile. TG-DTA results showed that temperature for anatase formation was 415 ℃. XPS results showed that doped-nitrogen was presented in the sample, they are important to show visible-light absorbency. The photocatalytic activities were evaluated using methyl orange and phenol as model pollutants, the results showed that over 90% of phenol could be degraded under visible light using N/TiO₂ as the catalyst after 4 hours reaction. Almost the same activity was found for the TiO₂ photocatalyst calcined at different temperature under sunlight but activities were different when the treatment was under UV light.     

二氧化碳和丙烯直接合成甲基丙烯酸的NiPMo/TiO2催化剂的研究

用溶胶-凝胶法以磷钼酸(MPA)的镍盐溶液水解钛酸四丁酯制备了NiPMo/TiO2催化剂.使用ICP、 XRD、 TG-DTA、 IR、 TPD-MS和微反应技术研究了催化剂的化学组成、热稳定性、化学吸附性质和催化反应性能.杂多钼酸盐与TiO2通过O2-在TiO2表面发生了键合.在623 K下,杂多阴离子仍保持原有的Keggin结构.CO2在Lewis酸位Ni(Ⅱ)和Lewis碱位Ni-O-Mo的桥氧协同作用下生成CO2卧式吸附态Ni(Ⅱ)←O-(CO)←(O--Ni).丙烯有多种吸附态在催化剂上吸附.在563 K、 1 MPa和空速1500 h-1的反应条件下,丙烯的摩尔转化率为3.2%,产物MAA选择性为95%.     

Toward new camptothecins. Part 6: Synthesis of crucial ketones and their use in Friedländer reaction

In the context of the preparation of camptothecin and luotonin A analogs, the synthesis of some key keto-precursors and their use in Friedländer condensation are described. This paper also focuses on the stability of these keto intermediates and emphasizes the major differences between indolizinones and pyrroloquinazolinones series. Noteworthy is also the report of some original structures isolated as by-products of some experiments.     

CoFe2O4自形成磁性液体场致结构化对磁化的影响

The Langevin paramagnetic theory can’t describe the relation between magnetization of ferrofluids and applied magnetic field. The structuralization of ferrofluids, which is considered the main influence factor of the magnetization, is regarded. The part of magnetization works is deposited when the structure is forming. This action influences the magnetization of ferrofluids directly or indirectly. On the base of the “compressing” model, the Langevin function that usually describes the magnetization of ferrofluid is modified, and a well-fitted curve is obtained. An equation of the relation between the equivalent volume fraction after being “compressed” and the intensity of magnetic field is discovered, which approximately describes the process of magnetization. The relation between the approximate initial susceptibility and the volume fraction can be obtained from modified formula.     

Highly regioselective Buchwald–Hartwig amination at C-2 of 2,4-dichloropyridine enabling a novel approach to 2,4-bisanilinopyridine (BAPyd) libraries

The highly regioselective Buchwald–Hartwig amination at C-2 of the cheap and readily accessible reagent, 2,4-dichloropyridine with a range of anilines and heterocyclic amines is described. This new methodology is robust and provides a facile access to 4-chloro-N-phenylpyridin-2-amines on 0.25 mol scale. These intermediates undergo a further Buchwald–Hartwig amination at higher temperature to enable rapid exploration of the chemical space at C-4 and to provide a library of 2,4-bisaminopyridines.     

KMnO4-mediated oxidative CN bond cleavage of tertiary amines: Synthesis of amides and sulfonamides

KMnO₄-mediated oxidative CN bond cleavage of tertiary amines producing secondary amine was introduced, which was trapped by electrophiles (acyl chloride and sulfonyl chloride) to form amides and sulfonamides. The reaction could take place at mild condition, tolerating a wide range of function groups and affording products in moderate to excellent yields.     

Chemistry of heterocyclic compounds at the A. E. Favorsky Irkutsk Institute of Chemistry, Siberian Branch of the Russian Academy of Sciences, over 50 years (Review)

The review contains a concise historical account and information on the most significant researches undertaken by the staff at the A. E. Favorsky Irkutsk Institute of Chemistry, Siberian Branch of the Russian Academy of Sciences on the Chemistry of Heterocyclic Compounds. Dedicated to Academician of the Russian Academy of Sciences B. A. Trofimov on his 70th jubilee. Translated from Khimiya Geterotsiklicheskikh Soedinenii, No. 10, pp. 1443–1502, October, 2008.     

Sulfur-directed metal-free and regiospecific methyl C(sp3)–H imidation of thioanisoles

Regiospecific and direct imidation of the methyl C(sp³)–H bond of thioanisoles is realized under mild and metal-free conditions with N-fluorobis(benzenesulfonyl)imide as an oxidant and nitrogen source. Proposed mechanism suggests that thionium ion intermediates and a Pummerer-type reaction are involved. The imidation has advantages such as high step-economy, excellent functionality tolerance, and regiospecificity, giving structurally diverse imidation products.     

Selective syntheses of 2H-1,3-oxazines and 1H-pyrrol-3(2H)-ones via temperature-dependent Rh(II)-carbenoid-mediated 2H-azirine-ring expansion

The Rh(II)-catalyzed reaction of 2-carbonyl-substituted 2H-azirines with ethyl 2-cyano-2-diazoacetate or 2-diazo-3,3,3-trifluoropropionate provides an easy access to 2H-1,3-oxazines and 1H-pyrrol-3(2H)-ones. These compounds can be selectively prepared from the same starting material using temperature as the only varied parameter. The 2-azabuta-1,3-diene intermediate, a common precursor for both heterocyclic products, isomerizes into 2H-1,3-oxazine under kinetic control, while 1H-pyrrol-3(2H)-one is the sole product of the reaction at elevated temperatures. According to DFT-calculations a one-atom oxazine ring contraction involving ring-opening to a 2-azabuta-1,3-diene intermediate, followed by a 1,5- and 1,2-prototropic shift leads to the consecutive formation of imidoylketene and azomethine ylide, which then further undergo cyclization to the pyrrole derivative.     

Synthesis of 1-benzyloxypyrazin-2(1H)-one derivatives

Different approaches for the synthesis of 1-benzyloxypyrazin-2(1H)-one derivatives from simple amino acids have been investigated. A library of 33 precursors for the preparation of N-hydroxy pyrazinones was obtained in moderate to good yields.