Influence of deposition conditions on the optical properties of erbium-doped yttrium oxide films grown by aerosol-UV assisted MOCVD

Erbium-doped Y₂O₃ films were prepared by aerosol-UV assisted metal-organic chemical vapour deposition (MOCVD) at 410 °C. The effects of humidity of carrier gas and UV-assistance on their structure and optical properties were investigated on the as-deposited and thermal annealed films using infrared spectroscopy, X-ray diffraction and transmission electron microscopy. It was found that the as-deposited Er:Y₂O₃ films crystallise in the Y₂O₃ cubic structure and present a very low organic contamination when the deposition takes place under high air humidity and, even better, with UV-assistance. After annealing, two different structural phases are observed corresponding to the cubic and the monoclinic structures of Y₂O₃. The Er³⁺ luminescence analysed in the visible and IR regions, shows the classical green transitions. The best optical properties were obtained with as-deposited and annealed Er:Y₂O₃ films grown under high air humidity with UV-assistance. Under such deposition conditions, ⁴I_13/2 lifetimes was found to be 3.07 and 6.1 ms for films annealed at 800 and 1000 °C, respectively, and up-conversion phenomena were underlined. This indicates that the deposition conditions, in particular air humidity, play an important role in the luminescent properties even after annealing.     

Effects of deposition temperature on the structural and morphological properties of SnO2 films fabricated by pulsed laser deposition

Tin oxide (SnO₂) thin films were grown on Si (1 0 0) substrates using pulsed laser deposition (PLD) in O₂ gas ambient (10 Pa) and at different substrate temperatures (RT, 150, 300 and 400 °C). The influence of the substrate temperature on the structural and morphological properties of the films was investigated using X-ray diffraction (XRD), atomic force microscopy (AFM) and scanning electron microscopy (SEM). XRD measurements showed that the almost amorphous microstructure transformed into a polycrystalline SnO₂ phase. The film deposited at 400 °C has the best crystalline properties, i.e. optimum growth conditions. However, the film grown at 300 °C has minimum average root mean square (RMS) roughness of 3.1 nm with average grain size of 6.958 nm. The thickness of the thin films determined by the ellipsometer data is also presented and discussed.     

Optical properties of ITO/TiO2 single and double layer thin films deposited by RPLAD

Indium tin oxide (ITO) and titanium dioxide (TiO₂) single layer and double layer ITO/TiO₂ films were prepared using reactive pulsed laser ablation deposition (RPLAD) with an ArF excimer laser for applications in dye-sensitized solar cells (DSSCs). The films were deposited on SiO₂ substrates either at room temperatures (RT) or heated to 200-400 °C. Under optimized conditions, transmission of ITO films in the visible (vis) range was above 89% for films produced at RT and 93% for the ones deposited at higher temperatures. Increasing the substrate temperature from RT to 400 °C enhances the transmission of TiO₂ films in the vis-NIR from about 70% to 92%. High transmission (≈90%) was observed for the double layer ITO/TiO₂ with a transmission cut-off above 900 nm. From the transmission data, the energies gaps (E_g), as well as the refractive indexes (n) for the films were estimated. n ≈ 2.03 and 2.04, respectively for ITO films and TiO₂ film deposited at 400 °C in the visible region. Post-annealing of the TiO₂ films for 3 h at 300 and 500 °C was performed to enhance n. The refractive index of the TiO₂ films increases with the post-annealing temperature. The direct band gap is 3.6, 3.74 and 3.82 eV for ITO films deposited at RT, 200, and 400 °C, respectively. The TiO₂ films present a direct band gap of 3.51 and 3.37 eV for as deposited TiO₂ films and when annealed at 400 °C, respectively. There is a shift of about 0.1 eV between ITO and ITO/TiO₂ films deposited at 200 °C. The shift decreases by half when the TiO₂ film was deposited at 400 °C. Post-annealing was also performed on double layer ITO/TiO₂.     

Spray pyrolytic synthesis of large area NiOx thin films from aqueous nickel acetate solutions

Non-stoichiometric nickel oxide thin films were prepared by pyrolytic decomposition of aerosol droplets of aqueous nickel acetate solution. Conventional un-nebulized spray pyrolysis system was used for the synthesis of thin films. The fine droplets were atomized by employing compressed air as carrier gas and allowed to decompose onto pre-heated Sn doped In₂O₃ (ITO) coated glass. The preparative parameters such as substrate temperature, solution concentration, distance from spray-nozzle to substrate, pressure of carrier air, etc., were optimized to obtain large area, uniform, thin films. The appropriate substrate temperature was selected after thermo-gravimetric analysis of nickel acetate. The temperature range of 330-420 °C was investigated for pyrolysis. Structural studies using X-ray diffraction (XRD) show the formation of cubic NiO. Morphological aspects of the films as-prepared and air annealed films have been studied by employing scanning electron microscopy. The optical absorption studies give direct band gap equal to 3.61 eV. The compositional analysis was carried out from the elemental depth profiles employing Auger electron spectroscopy. These indicate the formation of non-stoichiometric nickel oxide thin films. By studying I-V characteristics in alkaline electrolyte, electrocatalytic activity is tested.     

Characteristics of electron beam evaporated nanocrystalline SnO2 thin films annealed in air

Tin oxide (SnO₂) thin films (about 200 nm thick) have been deposited by electron beam evaporation followed by annealing in air at 350-550 °C for two hours. Optical, electrical and structural properties were studied as a function of annealing temperature. The as-deposited film is amorphous, while all other annealed films are crystalline (having tetragonal structure). XRD suggest that the films are composed of nanoparticles of 5-10 nm. Raman analysis and optical measurements suggest quantum confinement effects that are enhanced with annealing temperature. For instance, Raman peaks of the as-deposited films are blue-shifted as compared to those for bulk SnO₂. Blue shift becomes more pronounced with annealing temperature. Optical band gap energy of amorphous SnO₂ film is 3.61 eV, which increases to about 4.22 eV after crystallization. Two orders of magnitude decrease in resistivity is observed after annealing at 350-400 °C due to structural ordering and crystallization. The resistivity, however, increases slightly with annealing temperature above 400 °C, possibly due to improvement in stoichiometry and associated decrease in charge carrier density.     

Influence of deposition temperature on the structural and morphological properties of Be3N2 thin films grown by reactive laser ablation

Be₃N₂ thin films have been grown on Si(1 1 1) substrates using the pulsed laser deposition method at different substrate temperatures: room temperature (RT), 200 °C, 400 °C, 600 °C and 700 °C. Additionally, two samples were deposited at RT and were annealed after deposition in situ at 600 °C and 700 °C. In order to obtain the stoichiometry of the samples, they have been characterized in situ by X-ray photoelectron (XPS) and reflection electron energy loss spectroscopy (REELS). The influence of the substrate temperature on the morphological and structural properties of the films was investigated using scanning electron microscopy (SEM), atomic force microscopy (AFM) and X-ray diffraction (XRD). The results show that all prepared films presented the Be₃N₂ stoichiometry. Formation of whiskers with diameters of 100-200 nm appears at the surface of the films prepared with a substrate temperature of 600 °C or 700 °C. However, the samples grown at RT and annealed at 600 °C or 700 °C do not show whiskers on the surface. The average root mean square (RMS) roughness and the average grain size of the samples grown with respect the substrate temperature is presented. The films grown with a substrate temperature between the room temperature to 400 °C, and the sample annealed in situ at 600 °C were amorphous; while the αBe₃N₂ phase was presented on the samples with a substrate temperature of 600 °C, 700 °C and that deposited with the substrate at RT and annealed in situ at 700 °C.     

Pulsed laser deposited iron fluoride thin films for lithium-ion batteries

Iron fluoride thin films were successfully grown by Pulsed Laser Deposition (PLD), and their physico-chemical properties and electrochemical behaviours were examined by adjusting the deposition conditions, such as the target nature (FeF₂ or FeF₃), the substrate temperature (T_s ≤ 600 °C), the gas pressure (under vacuum or in oxygen atmosphere) and the repetition rates (2 and 10 Hz). Irrespective of the FeF₂ or FeF₃ target nature, iron fluoride thin films, deposited at 600 °C under vacuum, showed X-ray diffraction (XRD) patterns corresponding to the FeF₂ phase. On the other hand, iron fluoride thin films deposited at room temperature (RT) from FeF₂ target were amorphous, whereas the thin films deposited from FeF₃ target consisted of a two-phase mixture of FeF₃ and FeF₂ showing sharp and broad diffraction peaks by XRD, respectively. Their electrochemical behaviour in rechargeable lithium cells was investigated in the 0.05-3.60 V voltage window. Despite a large irreversible capacity on the first discharge, good cycling life was observed up to 30 cycles. Finally, their electrochemical properties were compared to the ones of iron oxide thin films.     

KrF pulsed laser deposition of La5Ca9Cu24O41 thin films on various substrates

Recent studies on single crystals of cuprate oxides containing spin chains and ladders have reported large anisotropic magnon-mediated thermal conductivity. A potential use of thin films of such materials could be in the thermal management of electronic devices for the guiding of unwanted heat to a heat sink. In this article, the pulsed laser deposition and characterization of La₅Ca₉Cu₂₄O₄₁ thin films on SrLaAlO₄, SrTiO₃, MgO, and Si substrates are reported for the first time. The films were grown using a pulsed UV laser (KrF, 248 nm) and various substrate temperatures up to 650 °C. The XRD spectra revealed successful target-film stoichiometric transfer and high texturing of the thin films with (0 k 0) preferred orientation.     

Nanostructure of photocatalytic TiO2 films sputtered at temperatures below 200 °C

The article reports on correlations between the process parameters of reactive pulsed dc magnetron sputtering, physical properties and the photocatalytic activity (PCA) of TiO₂ films sputtered at substrate surface temperature T_surf ≤ 180 °C. Films were deposited using a dual magnetron system equipped with Ti (Ø50 mm) targets in Ar + O₂ atmosphere in oxide mode of sputtering. The TiO₂ films with highly photoactive anatase phase were prepared without a post-deposition thermal annealing. The decomposition rate of the acid orange 7 (AO7) solution during the photoactivation of the TiO₂ film with UV light was used for characterization of the film PCA. It was found that (i) the partial pressure of oxygen pO₂ and the total sputtering gas pressure p_T are the key deposition parameters influencing the TiO₂ film phase composition that directly affects its PCA, (ii) the structure of sputtered TiO₂ films varies along the growth direction from the film/substrate interface to the film surface, (iii) ∼500 nm thick anatase TiO₂ films with high PCA were prepared and (iv) the structure of sputtered TiO₂ films is not affected by the substrate surface temperature T_surf when T_surf < 180 °C. The interruption of the sputtering process and deposition in long (tens of minutes) pulses alternating with cooling pauses has no effect on the structure and the PCA of TiO₂ films and results in a decrease of maximum value of T_surf necessary for the creation of nanocrystalline nc-TiO₂ film. It was demonstrated that crystalline TiO₂ films with high PCA can be sputtered at T_surf ≤ 130 °C. Based on obtained results a phase zone model of TiO₂ films was developed.     

Effect of UV lamp irradiation during oxidation of Zr/Pt/Si structure on electrical properties of Pt/ZrO2/Pt/Si structure

Metal-insulator-metal (MIM) capacitors were fabricated using ZrO₂ films and the effects of structural and native defects of the ZrO₂ films on the electrical and dielectric properties were investigated. For preparing ZrO₂ films, Zr films were deposited on Pt/Si substrates by ion beam deposition (IBD) system with/without substrate bias voltages and oxidized at 200 °C for 60 min under 0.1 MPa O₂ atmosphere with/without UV light irradiation (λ = 193 nm, Deep UV lamp). The ZrO₂(∼12 nm) films on Pt(∼100 nm)/Si were characterized by X-ray diffraction pattern (XRD), field emission scanning electron microscopy (FE-SEM) and high-resolution transmission electron microscopy (HRTEM), capacitance-voltage (C-V) and current-voltage (I-V) measurements were carried out on MIM structures. ZrO₂ films, fabricated by oxidizing the Zr film deposited with substrate bias voltage under UV light irradiation, show the highest capacitance (784 pF) and the lowest leakage current density. The active oxygen species formed by UV irradiation are considered to play an important role in the reduction of the leakage current density, because they can reduce the density of oxygen vacancies.     

Spray pyrolytic deposition of transparent aluminum oxide (Al2O3) films

Optically transparent Al₂O₃ films has been synthesized, on quartz substrates at 500, 600 and 700 °C, from 0.02 M aluminum acetyl acetonate (Al(acac)₃) in ethanol, by using ultrasonic spray pyrolysis technique. The films synthesized at 500, 600 and 700 °C are amorphous having average particle sizes 27 ± 6, 18 ± 3 and 14 ± 3, respectively. The films are found to be 95% optically transparent in the visible region. The optical transparency of the films in the ultraviolet region is found to increase with increase in deposition temperature. The observed increase in optical band gap and decrease in refractive index is attributed to the decrease in particle size with increase in deposition temperature. The stoichiometry and chemical bonding of the amorphous film studied using XPS and FTIR spectroscopy revealed the presence chemisorbed oxygen.     

Influence of substrate temperature on structures and dielectric properties of pyrochlore Bi1.5Zn1.0Nb1.5O7 thin films prepared by pulsed laser deposition

The influence of substrate temperature on structural and dielectric properties of cubic pyrochlore Bi_1.5Zn_1.0Nb_1.5O₇ (BZN) thin films prepared by pulsed laser deposition process has been investigated. BZN thin films were deposited on Pt/Ti/SiO₂/Si(1 0 0) substrate and in situ annealed at 700 °C. The results indicate that the substrate temperature has a significant effect on the structural and dielectric properties of BZN thin films. The films exhibit a cubic pyrochlore structure in the substrate temperature range from 550 °C to 700 °C and at the annealing temperature of 700 °C. With further increase of substrate temperature to 750 °C, the phases of Bi₂O₃, BiNbO₄ and Bi₅Nb₃O₁₅ can be detected in the XRD pattern due to the Zn loss. The dielectric constant and loss tangent of the films deposited at 650 °C are 192 and 6 × 10⁻⁴ at 10 kHz, respectively. The tunability is 10% at a dc bias field of 0.9 MV/cm.     

Characterization of single-crystalline In2O3 films deposited on Y-stabilized ZrO2 (1 0 0) substrates by MOCVD

Epitaxial In₂O₃ films have been deposited on Y-stabilized ZrO₂ (YSZ) (1 0 0) substrates by metalorganic chemical vapor deposition (MOCVD). The films were deposited at different substrate temperatures (450-750 °C). The film deposited at 650 °C has the best crystalline quality, and observation of the interface area shows a clear cube-on-cube epitaxial relationship of In₂O₃(1 0 0)||YSZ(1 0 0) with In₂O₃[0 0 1]||YSZ[0 0 1]. The Hall mobility of the single-crystalline In₂O₃ film deposited at 650 °C is as high as 66.5 cm² V⁻¹ s⁻¹ with carrier concentration of 1.5 × 10¹⁹ cm⁻³ and resistivity of 6.3 × 10⁻³ Ω cm. The absolute average transmittance of the obtained films in the visible range exceeds 95%.     

Optimization of annealing conditions of In2S3 thin films deposited by vacuum thermal evaporation

In₂S₃ thin films were grown on glass substrates by means of the vacuum thermal evaporation technique and subsequently thermally annealed in nitrogen and free air atmosphere from 250 to 350 °C for different durations. Experimental parameters have been adjusted in order to optimize the annealing conditions, and to obtain high band gap energy at low deposition temperature, as required for photovoltaic applications. In order to improve our understanding of the influence of the deposition and annealing parameters on device performance, we have investigated our indium sulfide material by X-ray diffraction, energy dispersive X-ray analysis (EDAX), atomic force microscopy (AFM) and spectrophotometry. The optical and structural properties of the films were studied as a function of the annealing temperature and durations. X-ray diffraction analysis shows the initial amorphous nature of deposited In-S thin films and the phase transition into crystalline In₂S₃ upon thermal annealing. Films show a good homogeneity and optical direct band gap energy about 2.2 eV. An annealing temperature of 350 °C during 60 min in air atmosphere were the optimal conditions.     

The electrochemical preparation and microwave absorption properties of magnetic carbon fibers coated with Fe3O4 films

Electrodeposition was employed to fabricate magnetite (Fe₃O₄) coated carbon fibers (MCCFs). Temperature and fiber surface pretreatment had a significant influence on the composition and morphology of Fe₃O₄ films. Uniform and compact Fe₃O₄ films were fabricated at 75 °C on both nitric acid treated and untreated carbon fibers, while the films prepared at 60 °C were continuous and rough. Microwave measurements of MCCF/paraffin composites (50 wt.% of MCCFs, pretreated carbon fibers as deposition substrates) were carried out in the 2-18 GHz frequency range. MCCFs prepared at 60 °C obtained a much higher loss factor than that prepared at 75 °C. However, the calculation results of reflection loss were very abnormal that MCCFs prepared at 60 °C almost had no absorption property. While MCCFs prepared at 75 °C exhibited a good absorption property and obtained −10 dB and −20 dB refection loss in wide matching thickness ranges (1.0-6.0 mm and 1.7-6.0 mm range, respectively). A secondary attenuation peak could also be observed when the thickness of MCCF/paraffin composite exceeded 4.0 mm. The minimum reflection loss was lower.     

High-throughput characterization of BixY3−xFe5O12 combinatorial thin films by magneto-optical imaging technique

Bi_xY_3−xFe₅O₁₂ thin films have been grown on GGG (Gd₃Ga₅O₁₂) (1 1 1) substrates by the combinatorial composition-spread techniques under substrate temperature (T_sub) ranging from 410 to 700 °C and O₂ pressure of 200 mTorr. In order to study the effect of substrates on the deposition of Bi_xY_3−xFe₅O₁₂ thin films, garnet substrates annealed at 1300 °C for 3 h were also used. Magneto-optical properties were characterized by our home-designed magneto-optical imaging system. From the maps of Faraday rotation angle θ_F, it was evident that the Faraday effect appears only when T_sub = 430-630 °C. θ_F reaches to the maximum value (∼6°/μm, λ = 632 nm) at 500 °C, and is proportional to the Bi contents. XRD and EPMA analyses showed that Bi ions are easier to substitute for Y sites and better crystallinity is obtained for annealed substrates than for commercial ones.     

Structural and optical properties of SrCu2O2 films deposited on sapphire substrates by pulsed laser deposition

We deposited SrCu₂O₂ (SCO) films on sapphire (Al₂O₃) (0 0 0 1) substrates by pulsed laser deposition. The crystallographic orientation of the SCO thin film showed clear dependence on the growth temperature. X-ray diffraction (XRD) and transmission electron microscopy (TEM) analysis showed that the film deposited at 400 °C was mainly oriented in the SCO [2 0 0] direction, whereas when the growth temperature was increased to 600 °C, the SCO film showed a dominant orientation of SCO [1 1 2]. The SCO film deposited at 500 °C was obvious polycrystalline, showing multi peaks from (2 0 0), (1 1 2), and (2 1 1) diffraction in the XRD spectrum. The SCO film deposited at 600 °C showed a band gap energy of 3.3 eV and transparency up to 80% around 500 nm. The photoluminescence (PL) spectra of the SCO films grown at 500 °C and 600 °C mainly showed blue-green emission, which was attributed to the intra-band transition of the isolated Cu⁺ and Cu⁺–Cu⁺ pairs according to the temperature dependent-PL analysis.     

Structure and photoluminescence properties of epitaxial SnO2 films grown on α-Al2O3 (0 1 2) by MOCVD

SnO₂ thin films have been successfully deposited on α-Al₂O₃ (0 1 2) substrates by metalorganic chemical vapor deposition (MOCVD) in the temperature range 500-700 °C. The films were epitaxially grown in the tetragonal SnO₂ phase and were (1 0 1) oriented. In-plane orientation relationship [0 1 0]SnO₂||[1 0 0]Al₂O₃ and [1 0 1?]SnO₂||[1? 2? 1]Al₂O₃ was determined between the film and substrate. Photoluminescence (PL) spectra measured at room temperature revealed that the film grown at 700 °C showed an intense ultra-violet (UV) PL peak at 333 nm, which was a band-edge emission peak in SnO₂ films. At a temperature of 13 K, a new broad PL band centered at about 480 nm was observed. The corresponding PL mechanisms are discussed in detail.     

Spray pyrolysis deposition of YSZ and YSZ-Pt composite films

In the present paper procedures are described for spray pyrolysis deposition of YSZ films (0.1-30 μm in thickness) with 8 or 15 mole % of YO_1.5 on different substrates. Aqueous or ethylene glycol solutions of Y-Zr-citrates were used as starting material and O₂ as carrier gas. The crystal structure and the morphology of the films were studied.The optimal deposition and post-deposition annealing conditions were defined, taking into account the desired film thickness and characteristics. Substrate temperatures of 250 °C during the deposition followed by heating for 10 min to 400 °C after every spraying and to 590 °C after every three sprayings with final annealing at 590 °C for 2 h in static air atmosphere were found to be suitable for the production of dense, uniform and cracks-free films.     

Photocatalytic behavior of heavy La-doped TiO2 films deposited by pulsed laser deposition using non-sintered target

We have investigated the control of photocatalytic behavior under deposited conditions of non-sintered target of different molar ratios with TiO₂ and La₂O₃ from 1:0 to 1:2 for heavily La doping, and post-annealing temperature from 600 °C to 1000 °C for crystallizing by pulsed laser deposition. We have successfully crystallized heavily La-doped TiO₂ films with post-annealing temperature over 800 °C and with molar ratio of TiO₂:La₂O₃ over 1:1 on a quartz substrate. Heavily La-doped TiO₂ films are observed the decomposition of methylene blue and a water-splitting reaction in photocatalytic behavior under Xe light irradiation. When stoichiometric La-doped TiO₂ (TiO₂:La₂O₃ = 1: 1) is synthesized with heat-treatment at 900 °C, the best results are obtained under photocatalytic behavior and pure La₂Ti₂O₇ crystalline were obtained.