Lead-free ferroelectric BaTiO3 doped-(Na0.5Bi0.5)TiO3 thin films processed by pulsed laser deposition technique

The difficulties in synthesizing phase pure BaTiO₃ doped-(Na_0.5Bi_0.5)TiO₃ are known. In this work, we reporting the optimized pulsed laser deposition (PLD) conditions for obtaining pure phase 0.92(Na_0.5Bi_0.5)TiO₃-0.08BaTiO₃, (BNT-BT_0.08), thin films. Dielectric, ferroelectric and piezoelectric properties of BNT-BT_0.08, thin films deposited by PLD on Pt/TiO₂/SiO₂/Si substrates are investigated in this paper. Perovskite structure of BNT-BT_0.08 thin films with random orientation of nanocrystallites has been obtained by deposition at 600 °C. The relative dielectric constant and loss tangent at 100 kHz, of BNT-BT_0.08 thin film with 530 nm thickness, were 820 and 0.13, respectively. Ferroelectric hysteresis measurements indicated a remnant polarization value of 22 μC/cm² and a coercive field of 120 kV/cm. The piezoresponse force microscopy (PFM) data showed that most of the grains seem to be constituted of single ferroelectric domain. The as-deposited BNT-BT_0.08 thin film is ferroelectric at the nanoscale level and piezoelectric.     

Growth and structure of Bi0.5(Na0.7K0.2Li0.1)0.5TiO3 thin films prepared by pulsed laser deposition technique

Bi_0.5(Na_0.7K_0.2Li_0.1)_0.5TiO₃ (BNKLT) thin films were prepared on Pt/Ti/SiO₂/Si substrates by pulsed laser deposition (PLD) technique. The films prepared were examined by using X-ray diffraction (XRD), scanning electron microscopy (SEM) and atomic force microscopy (AFM). The effects of the processing parameters, such as oxygen pressure, substrate temperature and laser power, on the crystal structure, surface morphology, roughness and deposition rates of the thin films were investigated. It was found that the substrate temperature of 600 °C and oxygen pressure of 30 Pa are the optimized technical parameters for the growth of textured film, and all the thin films prepared have granular structure, homogeneous grain size and smooth surfaces.     

Electrical properties of La2O3 thin films grown on TiN/Si substrates via atomic layer deposition

The electrical as well as the structural properties of La₂O₃ thin films on TiN substrates were investigated. Amorphous stoichiometric La₂O₃ thin films were grown at 300 °C via atomic layer deposition technique by using lanthanum 2,2,6,6-tetramethyl-3,5-heptanedione [La(TMHD)₃] and H₂O as precursors. Post-annealing of the grown film induced dramatic changes in structural and the electrical properties. Crystalline phases of the La₂O₃ film emerged with the increase of the post-annealing temperature. Metal-insulator-metal (MIM) capacitor was fabricated to measure the electrical properties of the grown film. The dielectric constant of the La₂O₃ thin films increased with annealing temperature to reach the value of 17.3 at 500 °C. The leakage current density of the film post-annealed at 400 °C was estimated to be 2.78 × 10⁻¹⁰ and 2.1 × 10⁻⁸ A/cm² at ±1 V, respectively.     

Annealing effects on structural, optical and electrical properties of e-beam evaporated CuIn0.5Ga0.5Te2 thin films

CuIn_0.5Ga_0.5Te₂ (CIGT) thin films have been prepared by e-beam evaporation from a single crystal powder synthesized by direct reaction of constituent elements in a stoichiometric proportion. Post-depositional annealing has been carried out at 300 and 350 °C. The compositions of the films were determined by energy dispersive X-ray analysis (EDXA) and it was found that there was a remarkable fluctuation in atomic percentage of the constituent elements following to the post-depositional annealing. X-ray diffraction analysis (XRD) has shown that as-grown films were amorphous in nature and turned into polycrystalline structure following to the annealing at 300 °C. The main peaks of CuIn_0.5Ga_0.5Te₂ and some minor peaks belonged to a binary phase Cu₂Te appeared after annealing at 300 °C, whereas for the films annealed at 350 °C single phase of the CuIn_0.5Ga_0.5Te₂ chalcopyrite structure was observed with the preferred orientation along the (1 1 2) plane. The effect of annealing on and near surface regions has been studied using X-ray photoelectron spectroscopy (XPS). The results indicated that there was a considerable variation in surface composition following to the annealing process. The transmission and reflection measurements have been carried out in the wavelength range of 200-1100 nm. The absorption coefficients of the films were found to be in the order of 10⁴ cm⁻¹ and optical band gaps were determined as 1.39, 1.43 and 1.47 eV for as-grown and films annealed at 300 and 350 °C, respectively. The temperature dependent conductivity and photoconductivity measurements have been performed in the temperature range of −73 to 157 °C and the room temperature resistivities were found to be around 3.4 × 10⁷ and 9.6 × 10⁶ (Ω cm) for the as-grown and annealed films at 350 °C, respectively.     

Preparation of transparent conductive TiO2:Nb thin films by pulsed laser deposition

This study investigated the optical and electrical properties of Nb-doped TiO₂ thin films prepared by pulsed laser deposition (PLD). The PLD conditions were optimized to fabricate Nb-doped TiO₂ thin films with an improved electrical conductivity and crystalline structure. XRD analyses revealed that the deposition at room temperature in 0.92 Pa O₂ was suitable to produce anatase-type TiO₂. A Nb-doped TiO₂ thin film attained a resistivity as low as 6.7 × 10⁻⁴ Ω cm after annealing at 350 °C in vacuum (<10⁻⁵ Pa), thereby maintaining the transmittance as high as 60% in the UV-vis region.     

Influence of substrate temperature on structures and dielectric properties of pyrochlore Bi1.5Zn1.0Nb1.5O7 thin films prepared by pulsed laser deposition

The influence of substrate temperature on structural and dielectric properties of cubic pyrochlore Bi_1.5Zn_1.0Nb_1.5O₇ (BZN) thin films prepared by pulsed laser deposition process has been investigated. BZN thin films were deposited on Pt/Ti/SiO₂/Si(1 0 0) substrate and in situ annealed at 700 °C. The results indicate that the substrate temperature has a significant effect on the structural and dielectric properties of BZN thin films. The films exhibit a cubic pyrochlore structure in the substrate temperature range from 550 °C to 700 °C and at the annealing temperature of 700 °C. With further increase of substrate temperature to 750 °C, the phases of Bi₂O₃, BiNbO₄ and Bi₅Nb₃O₁₅ can be detected in the XRD pattern due to the Zn loss. The dielectric constant and loss tangent of the films deposited at 650 °C are 192 and 6 × 10⁻⁴ at 10 kHz, respectively. The tunability is 10% at a dc bias field of 0.9 MV/cm.     

Annealing temperature influence on electrical properties of ion beam sputtered Bi2Te3 thin films

Ion beam sputtering process was used to deposit n-type fine-grained Bi₂Te₃ thin films on BK7 glass substrates at room temperature. In order to enhance the thermoelectric properties, thin films are annealed at the temperatures ranging from 100 to 400 °C. X-ray diffraction (XRD) shows that the films have preferred orientations in the c-axis direction. It is confirmed that grain growth and crystallization along the c-axis are enhanced as the annealing temperature increased. However, broad impurity peaks related to some oxygen traces increase when the annealing temperature reached 400 °C. Thermoelectric properties of Bi₂Te₃ thin films were investigated at room temperature. The Bi₂Te₃ thin films, including as-deposited, exhibit the Seebeck coefficients of −90 to −168 μV K⁻¹ and the electrical conductivities of 3.92×10²-7.20×10² S cm⁻¹ after annealing. The Bi₂Te₃ film with a maximum power factor of 1.10×10⁻³ Wm⁻¹ K⁻² is achieved when annealed at 300 °C. As a result, both structural and transport properties have been found to be strongly affected by annealing treatment. It was considered that the annealing conditions reduce the number of potential scattering sites at grain boundaries and defects, thus improving the thermoelectric properties.     

Fabrication and vacuum annealing of transparent conductive Ga-doped Zn0.9Mg0.1O thin films prepared by pulsed laser deposition technique

In this study, highly transparent conductive Ga-doped Zn_0.9Mg_0.1O (ZMO:Ga) thin films have been deposited on glass substrates by pulsed laser deposition (PLD) technique. The effects of substrate temperature and post-deposition vacuum annealing on structural, electrical and optical properties of ZMO:Ga thin films were investigated. The properties of the films have been characterized through Hall effect, double beam spectrophotometer and X-ray diffraction. The experimental results show that the electrical resistivity of film deposited at 200 °C is 8.12 × 10⁻⁴ Ω cm, and can be further decreased to 4.74 × 10⁻⁴ Ω cm with post-deposition annealing at 400 °C for 2 h under 3 × 10⁻³ Pa. In the meantime, its band gap energy can be increased to 3.90 eV from 3.83 eV. The annealing process leads to improvement of (0 0 2) orientation, wider band gap, increased carrier concentration and blue-shift of absorption edge in the transmission spectra of ZMO:Ga thin films.     

Optical and electrical properties of SnO2:Sb thin films deposited by oblique angle deposition

The antimony doped tin oxide (SnO₂:Sb) (ATO) thin films were prepared by oblique angle electron beam evaporation technique. X-ray diffraction, field emission scanning electron microscopy, UV-vis-NIR spectrophotometer and four-point probe resistor were employed to characterize the structure, morphology, optical and electrical properties. The results show that oblique angle deposition ATO thin films with tilted columns structure are anisotropic. The in-plane birefringence of optical anisotropy is up to 0.035 at α = 70°, which means that it is suitable as wave plate and polarizer. The electrical anisotropy of sheet resistance shows that the sheet resistance parallel to the deposition plane is larger than that perpendicular to the deposition plane and it can be changed from 900 Ω/□ to 3500 Ω/□ for deposition angle from 40° to 85°, which means that the sheet resistance can be effectively tuned by changing the deposition angle. Additionally, the sandwich structure of SiO₂ buffer layer plus normal ATO films and oblique angle deposition ATO films can reduce the resistance, which can balance the optical and electrical anisotropy. It is suggested that oblique angle deposition ATO thin films can be used as transparent conductive thin films in solar cell, anti-foggy windows and multifunctional carrier in liquid crystal display.     

Effects of the substrate temperature on the properties of CuIn5S8 thin films

Structural, optical and electrical properties of CuIn₅S₈ thin films grown by thermal evaporation have been studied relating the effects of substrate heating conditions of these properties. The CuIn₅S₈ thin films were carried out at substrate temperatures in the temperature range 100-300 °C. The effects of heated substrate on their physico-chemical properties were investigated using X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDX), optical transmission and hot probe method. X-ray diffraction revealed that the films are strong preferred orientation along the (3 1 1) plane upon substrate temperature 200 °C and amorphous for the substrate temperatures below 200 °C. No secondary phases are observed for all the films. The composition is greatly affected by heated substrate. From the optical transmission and reflection, an important absorption coefficient exceeds 10⁵ cm⁻¹ at 800 nm was found. As increasing the substrate temperature, the optical energy band gap decreases from 1.70 eV for the unheated films to 1.25 eV for the deposited films at 300 °C. It was found that CuIn₅S₈ thin film is an n-type semiconductor at 250° C.     

Effects of co-substitution on the electrical properties of BiFeO3 thin films prepared by chemical solution deposition

Ferroelectric BiFeO₃ thin films with Nd-Cr (or Sm-Cr) co-substitution (denoted by BNdFCr and BSmFCr, respectively) were deposited on the Pt(2 0 0)/TiO₂/SiO₂/Si(1 0 0) substrates by a chemical solution deposition method. X-ray diffraction patterns revealed the formation of BNdFCr and BSmFCr thin films without any secondary phases. The co-substituted BNdFCr (or BSmFCr) thin films, which were annealed at 550 °C for 30 min in N₂ atmosphere, exhibited enhanced electrical properties compared to BFO thin films with the remanent polarization (2P_r) and coercive electric field (2E_c) of 196, 188 μC/cm² and 600, 570 kV/cm with the electric field of 800 kV/cm, respectively. The leakage current densities of BNdFCr and BSmFCr thin films measured at room temperature were approximately three orders of magnitude lower than that of BFO thin film, and the leakage current at room temperature of the thin films exhibited three distinctive conduction behaviors. Furthermore, the values of pulse polarizations [i.e., +(P*-P^{^}) or −(P*-P^{^})] of BNdFCr and BSmFCr thin films were reasonably unchanged up to 1.4 × 10¹⁰ switching cycles.     

Optical and gas sensing properties of thick TiO2 films grown by laser deposition

In this work the optical and the gas sensing properties of thick TiO₂ waveguide films, produced by pulsed laser deposition, were investigated by m-line spectroscopy. The films were deposited on (0 0 1) SiO₂ substrates at temperature of 100 °C. The thickness of the films was measured to be in the range from 650 to 1900 nm and the roughness increases from 5 to 14.6 nm. High quality mode spectra, consisted of thin and bright TE and TM modes, were observed in the films with thickness up to 1200 nm. All the films revealed anisotropic optical properties. Gas sensitivity of the films to CO₂ was examined at room temperature on the basis of the variations of the refractive index. CO₂ concentration of 3 × 10⁴ ppm was detected, which corresponds to a refractive index variation of about 1 × 10⁻⁴. The crystal structure and the optical transmittance of the films were also presented and discussed.     

Growth of superconducting FeSe0.5Te0.5 thin films by pulsed-laser deposition

FeSe_0.5Te_0.5 thin films with PbO-type structure are successfully grown on MgO(1 0 0) and LaSrAlO₄(0 0 1) substrates from FeSe_0.5Te_0.5 or FeSe_0.5Te_0.75 polycrystalline targets by pulsed-laser deposition. The film deposited on the MgO substrate (film thickness ∼ 55 nm) shows superconductivity at 10.6 K (onset) and 9.2 K (zero resistivity). On the other hand, the film deposited on the LaSrAlO₄ substrate (film thickness ∼ 250 nm) exhibits superconductivity at 5.4 K (onset) and 2.7 K (zero resistivity). This suggests the strong influence of substrate materials and/or the c-axis length to superconducting properties of FeSe_0.5Te_0.5 thin films.     

Investigation on upconversion photoluminescence of Bi3TiNbO9:Er:Yb thin films

Bi₃TiNbO₉:Er³⁺:Yb³⁺ (BTNEY) thin films were fabricated on fused silica by pulsed laser deposition. It was demonstrated that different laser fluence and substrate temperature during growth of BTNEY upconversion photoluminescence (UC-PL) samples control the film’s grain size and hence influences the UC-PL properties. The average grain size of BTNEY thin films deposited on fused silica substrates with laser fluence 4, 5, 6, and 7 J/cm² are 30.8, 35.9, 40.6, and 43.4 nm, respectively. The 525 nm emission intensities increase with the deposition laser fluence and the emission intensities of BTNEY thin film deposited under 700 and 600 °C are almost 24 and 4 times, respectively, as strong as those of samples under 500 °C. The grain size of BTNEY thin film increases with the increasing temperature. UC-PL of BTNEY films is enhanced by increasing grain size of the films.     

Surface morphology and luminescence characterization of β-FeSi2 thin films prepared by pulsed laser deposition

β-FeSi₂ thin films were prepared on Si (1 1 1) substrates by pulsed laser deposition (PLD) with a sintering FeSi₂ target and an electrolytic Fe target. The thin films without micron-size droplets were prepared using the electrolytic Fe target; however, the surface without droplets was remarkably rougher using the Fe target than using the FeSi₂ target. After deposition at 600 °C and then annealing at 900 °C for 20 h, XRD indicated that the thin film prepared using the Fe target had a poly-axis-orientation, but that prepared using the FeSi₂ target had a one-axis-orientation. The PL spectra of the thin films prepared using the FeSi₂ and Fe targets at a growth temperature of 600 °C and subsequently annealed at 900 °C for 20 h had A-, B- and C-bands. Moreover, it was found that the main peak at 0.808 eV (A-band) in the PL spectrum of the thin films prepared using the FeSi₂ target was the intrinsic luminescence of β-FeSi₂ from the dependence of PL peak energy on temperature and excitation power density.     

Epitaxial thin films of (Bi0.9La0.1)2NiMnO6 obtained by pulsed laser deposition

Bulk Bi₂NiMnO₆ has been shown to be ferromagnetic and ferroelectric. Here, we report a systematic study of the influence of the deposition conditions on the growth of (Bi_0.9La_0.1)₂NiMnO₆ thin films onto (0 0 1) SrTiO₃ substrates by pulsed laser deposition. Oxygen pressure and substrate temperature have been varied from 0.3 to 0.6 mbar and 600 to 660 °C, respectively. Whereas it is found that single-phase and epitaxial films can be obtained in a relatively broad oxygen pressure range, the temperature window, centred on 620 °C, is extremely narrow. Films of low roughness, about 1 unit cell, have been obtained. It is found that the magnetisation of the films, which are ferromagnetic with Curie temperatures about 100 K, is lower than the expected theoretical value, which might be attributed to an incomplete Ni-O-Mn long-range ordering.     

Fabrication and characterization of La-doped HfO2 gate dielectrics by metal-organic chemical vapor deposition

La-doped HfO₂ gate dielectric thin films have been deposited on Si substrates using La(acac)₃ and Hf(acac)₄ (acac = 2,4-pentanedionate) mixing sources by low-pressure metal-organic chemical vapor deposition (MOCVD). The structure, thermal stability, and electrical properties of La-doped HfO₂ films have been investigated. Inductive coupled plasma analyses confirm that the La content ranging from 1 to 5 mol% is involved in the films. The films show smaller roughness of ∼0.5 nm and improved thermal stability up to 750 °C. The La-doped HfO₂ films on Pt-coated Si and fused quartz substrates have an intrinsic dielectric constant of ∼28 at 1 MHz and a band gap of 5.6 eV, respectively. X-ray photoelectron spectroscopy analyses reveal that the interfacial layer is Hf-based silicate. The reliable value of equivalent oxide thickness (EOT) around 1.2 nm has been obtained, but with a large leakage current density of 3 A/cm² at V_g = 1V + V_fb. MOCVD-derived La-doped HfO₂ is demonstrated to be a potential high-k gate dielectric film for next generation metal oxide semiconductor field effect transistor applications.     

Synthesis and materials properties of transparent conducting In2O3 films prepared by sol-gel-spin coating technique

Transparent conducting indium oxide (In₂O₃) thin films have been prepared on glass substrates by the simple sol-gel-spin coating technique. These films have been characterized by X-ray diffraction, resistivity and Hall effect measurements, optical transmission, scanning electron microscopy and atomic force microscopy for their structural, electrical, optical and morphological properties. The influence of spin parameters, number of coating, process temperature on the quality of In₂O₃ films are studied. In the operating range of deposition, 400-475 °C, all the films showed predominant (2 2 2) orientation. Films deposited at optimum process conditions exhibited a resistivity of 2×10⁻² Ω cm along with the average transmittance of about 80% in the visible spectral range (400-700 nm).     

Influence of deposition temperature on the structural and morphological properties of Be3N2 thin films grown by reactive laser ablation

Be₃N₂ thin films have been grown on Si(1 1 1) substrates using the pulsed laser deposition method at different substrate temperatures: room temperature (RT), 200 °C, 400 °C, 600 °C and 700 °C. Additionally, two samples were deposited at RT and were annealed after deposition in situ at 600 °C and 700 °C. In order to obtain the stoichiometry of the samples, they have been characterized in situ by X-ray photoelectron (XPS) and reflection electron energy loss spectroscopy (REELS). The influence of the substrate temperature on the morphological and structural properties of the films was investigated using scanning electron microscopy (SEM), atomic force microscopy (AFM) and X-ray diffraction (XRD). The results show that all prepared films presented the Be₃N₂ stoichiometry. Formation of whiskers with diameters of 100-200 nm appears at the surface of the films prepared with a substrate temperature of 600 °C or 700 °C. However, the samples grown at RT and annealed at 600 °C or 700 °C do not show whiskers on the surface. The average root mean square (RMS) roughness and the average grain size of the samples grown with respect the substrate temperature is presented. The films grown with a substrate temperature between the room temperature to 400 °C, and the sample annealed in situ at 600 °C were amorphous; while the αBe₃N₂ phase was presented on the samples with a substrate temperature of 600 °C, 700 °C and that deposited with the substrate at RT and annealed in situ at 700 °C.     

Properties of K0.5Bi0.5TiO3 thin films deposited on different substrates

K_0.5Bi_0.5TiO₃ thin films were deposited on fused quartz, n-type Si(100) and Pt/TiO₂/SiO₂/Si substrates by repeated coating/dying cycles. X-ray diffraction analysis shows that the films annealed at 700 °C for 10 min present perovskite phase. Atomic force microscopy reveals that the surface morphology is smooth, the grain sizes of the films on Si(100) are quite larger than on fused quartz. The capacitance-voltage hysteresis loops at various sweeping speed are collected as are polarization types. The films in the ON and OFF states are relatively stable. The films also exhibit a hysteresis loop at an applied voltage of 4 V, with a remanent polarization of 9.3 μC/cm² and a coercive voltage of 2 V. The insulating property of negative bias voltage is better than that of positive bias voltage. The transmittance of the films is between 74 and 82% in the wavelength range of 200-2000 nm.