Effect of Sr substitution on photoluminescent properties of BaAl2O4:Eu, Dy

Phosphor material BaAl₂O₄:Eu²⁺, Dy³⁺ with varying compositions of Sr substitution were prepared by the solid-state synthesis method. The phosphor compositions were characterized for their phase and crystallinity by XRD, SEM and TEM. Photoluminescence (PL) properties were investigated measuring PL and decay time for varying Ba/Sr compositions. The PL results show the blue shift in the luminescence properties in Sr substituted BaAl₂O₄:Eu²⁺, Dy³⁺ compared to parent BaAl₂O₄:Eu²⁺, Dy³⁺. It is probably due to the influence of 5d electron states of Eu²⁺ in the crystal field because of atomic size variation causing crystal defects. Dy³⁺ ion doping in the phosphor generates deep traps, which results in long afterglow phosphorescence.     

Sr和Ba替代对Eu掺杂Ca2.955Si2O7的结构和发光特性的影响研究

利用固相反应法制备了Sr和Ba替代的Ca_2.955-xM_xSi₂O₇: 0.045Eu²⁺ (M= Sr, Ba, x= 0.1-0.5)系列荧光粉, 利用较大离子半径的Sr和Ba元素替代Eu掺杂Ca_2.955-xM_xSi₂O₇ 中的Ca元素,研究Sr和Ba替代对样品结构和发光特性的影响. X射线衍射测试结果表明,少量Sr和Ba替代不会改变基质的晶体结构, 样品仍然为单斜晶系.未替代前, Ca_2.955Si₂O₇: 0.045Eu²⁺ 样品的发射峰在574 nm左右,随着Sr含量的增加,样品的发射峰发生蓝移; 而Ba含量在x= 0.1-0.4时不会引起发射峰位置的移动, 但x= 0.5样品的发射峰发生蓝移.同等含量的Sr和Ba部分替代样品中的Ca元素, Ba替代样品的光谱强度较强.     

Effects of non-stoichiometry on crystallinity, photoluminescence and afterglow properties of Sr2MgSi2O7:Eu, Dy phosphors

Eu²⁺, Dy³⁺ co-doped Sr₂MgSi₂O₇ phosphors with deficient, stoichiometric or excess amounts of silicon are prepared by solid-state reaction. XRD and SEM results indicate that all the samples studied are found to be free from impurities and samples with SiO₂ excess possess better crystallinity and larger grain size. Photoluminescence reveals that the position of Eu²⁺ emission is not changed with various compositions. However, both photoluminescence intensity and afterglow properties are increased by an incorporation of excess SiO₂ and are decreased by SiO₂ deficiency. The thermoluminescence results show that the corresponding increase or decrease in afterglow is associated with trap density, but no change in trap depth. The underlying reason of photoluminescence and afterglow enhancement is discussed.     

Synthesis and characterization of structural and luminescence properties of blue — green BaAlxOy:Eu2+ phosphor by solution — combustion method

Europium-doped barium aluminate (BaAl _x O _y :Eu²⁺) phosphors were obtained at low temperatures (500°C) using the solution — combustion of corresponding metal nitrate-urea solution mixtures. The particle size and morphology and the structural and luminescent properties of the synthesized phosphors were examined by means of scanning electron microscopy (SEM), X-ray diffraction (XRD), Electron diffraction spectroscopy (EDS) and photoluminescence (PL). It was found that the change in Ba: Al molar ratios showed greatly influence not only on the particle size and morphology, but also on their PL spectra and crystalline structure. The structure of BaAl _x O _y nanophosphors changes from a hexagonal Ba₂Al₁₀O₁₇ phase for samples with 6:100 molar ratios to a hexagonal BaAl₂O₄ one with an increase in Ba content. The peak of the emission band occurs at a longer wavelength (around 615 nm) with a decrease in Ba concentration but displays a broad blue-green emission band composed from two emissions with the maximum at 495 and 530nm coming from Eu²⁺ in two sites for increasing Ba content. The blue-green emission is probably due to the influence of 5d electron states of Eu²⁺ in the crystal field because of atomic size variation causing crystal defects while the red emission is due to f - f transitions. These findings clearly demonstrate the possibility of fine tuning the colour emission.     

发光二极管用红色荧光粉Sr0.8-xBaxEu0.2WO4的制备和性质研究

采用化学共沉淀法制备了不同Ba²⁺掺杂浓度、 不同煅烧温度的Sr_0.8-xBa_xEu_0.2WO₄红色荧光粉. 研究了样品的晶体取向和晶格 畸变对发光性质的影响, 实验结果表明: 合成的Sr_0.8-xBa_xEu_0.2WO₄红色荧光粉为四方相, 样品中Eu³⁺的⁵D₀–⁷F₂跃迁的红光能被近紫外光和蓝光有效激发. 适量的Ba²⁺离子取代部分的Sr²⁺提高了Sr_0.8Eu_0.2WO₄荧光粉的发光强度, Ba²⁺掺杂浓度的改变对基质的晶格参数、晶体对称性和发光性能影响较大, Ba²⁺的最佳掺杂量为30%.     

Thermoluminescence of rare earth activated CdSO4, SrSO4 and BaSO4

The thermoluminescence (TL) of rare earth (RE) activated sulfates of Cd, Sr and Ba was studied above room temperature. Many of the phosphors prepared exhibit an extremely bright TL following X-irradiation (most notably with Sm, Eu, Tb, Dy and Tm dopants), having an efficiency comparable to that of the highest sensitivity phosphors available for TL dosimetry, and exhibiting activator-induced glow peaks between 405 and 480°K. In a given lattice, the RE³⁺ ions produce a characteristic glow peak at the same temperature (independent of the particular RE ion), whereas Eu²⁺ produces a single glow peak at a different temperature. A decrease in glow peak temperature with increasing interatomic spacing was observed in the homologous SrSO₄-BaSO₄ system - this shift being most pronounced in the Eu²⁺ -doped materials. TL emission spectra were obtained for trivalent Sm, Tb, Dy and Tm and for divalent Eu in these sulfates (and also in CaSO₄).     

Line emission of SrBe2Si2O7:Eu2+ and BaBe2Si2O7:Eu2+

The compounds SrBe₂Si₂O₇ and BaBe₂Si₂O₇ both have the barylite structure. With 254 nm excitation, the Eu²⁺-activated compounds give UV emission peaking at 360 nm (Sr) and at 375 nm (Ba). Maximum quantum efficiencies of 40% (Sr) and 65% (Ba) were measured. The emission consists of a 5d-4f band emission as well as 4f-4f line emission, in contrast to many other Eu²⁺-activated oxides which generally show only 5d-4f band emission. At 77°K, both compounds show only the 4f-4f line emission peaking at 360 nm. At higher temperatures, 5d-4f band emission shows up at the cost of the line emission. A thermal equilibrium is assumed between the lowest excited 5d and 4f levels. The energy difference between these levels, calculated from the variation in the line-band intensity ratio with temperature, was computed to be 0.15 eV (Sr) and 0.09 eV (Ba). The occurrence of the line emission in the barylites is correlated with the weakness of the crystal field at the Eu²⁺ ions and with the high quenching temperature of the 5d-4f band emission.     

Eu2+, Cr3+共掺杂的MAl12O19 (M=Ca, Sr, Ba) 的发光性质及能量传递

三基色荧光粉中, 红色荧光粉性能较差, 为获得性能优良的红色荧光粉, 本文采用高温固相法合成了Eu²⁺, Cr³⁺单掺杂及共掺杂的碱土金属多铝酸盐MAl₁₂O₁₉ (M =Ca, Sr, Ba) 发光体. 实验表明, 在以上三种基质中均存在Eu²⁺→Cr³⁺的能量传递, 利用能量传递可以有效将Eu²⁺的蓝光或绿光转换为红光. 三种碱土金属多铝酸盐基质的晶体结构相似,但Eu²⁺, Cr³⁺发光受晶体场影响,导致在不同的基质中Eu²⁺, Cr³⁺间能量传递效率不同.通过光谱分析及能量传递效率计算发现, 相同掺杂浓度下,CaAl₁₂O₁₉中Eu²⁺→Cr³⁺的能量传递效率最高,SrAl₁₂O₁₉次之, BaAl₁₂O₁₉最低.红光转换率在CaAl₁₂O₁₉中最高.     

The structure of mixed fluorides Ca1?xSrxF2 and Sr1?xBaxF2 and the luminescence of Eu2+ in these crystals

The structure of the mixed fluorites Ca_1−x Sr_xF₂ and Sr_1−x Ba_xF₂, as well as the structure of the Eu²⁺ impurity center in these crystals, is calculated within the framework of the virtual-crystal method realized in the shell model and pair-potential approximation. The phenomenological dependence of the position of the lower level of the 4f ⁶5d configuration of the Eu²⁺ ion on distance to the Eu²⁺-ligand is derived. The dependences of the Stokes shift and the Huang-Rhys factor on x are calculated for the yellow luminescence in Sr_1−x Ba_xF₂:Eu²⁺. The value of x at which the lower level of the 4f ⁶5d configuration of the Eu²⁺ ion in Sr_1−x Ba_xF₂:Eu²⁺ falls within the conduction band is found. __________ Translated from Fizika Tverdogo Tela, Vol. 45, No. 5, 2003, pp. 823–826. Original Russian Text Copyright ? 2003 by Nikiforov, Zakharov, Chernyshev, Ugryumov, Kotomanov.     

Photoluminescence properties of Sr1-xSi2O2N2: Eux as green to yellow-emitting phosphor for blue pumped white LEDs

This study evaluated potential applications of green to yellow-emitting phosphors (Sr_1−xSi₂O₂N₂: Eu²⁺_x) in blue pumped white light emitting diodes. Sr_1-xSi₂O₂N₂: Eu²⁺_x was synthesized at different Eu²⁺ doping concentrations at 1450 °C for 5 h under a reducing nitrogen atmosphere containing 5% H₂ using a conventional solid reaction method. The X-ray diffraction patterns of the prepared phosphor (Sr_1-xSi₂O₂N₂: Eu²⁺_x) were indexed to the SrSi₂O₂N₂ phase and an unknown intermediate phase. The photoluminescence properties of these phosphors (Sr_1−xSi₂O₂N₂: Eu²⁺_x) showed that the samples were excited from the UV to visible region due to the strong crystal field splitting of the Eu²⁺ ion. The emission spectra under excitation of 450 nm showed a bright color at 545-561 nm. The emission intensity increased gradually with increasing Eu²⁺ doping concentration ratio from 0.05 to 0.15. However, the emission intensity decreased suddenly when the Eu²⁺ concentration ratio was >0.2. As the doping concentration of Eu²⁺ was increased, there was a red shift in the continuous emission peak. These results suggest that Sr_1-xSi₂O₂N₂: Eu₂⁺_x phosphor can be used in blue-pumped white light emitting diodes.     

White light emitting from single phased K2Ca1−x−yP2O7: xEu, yMn phosphors under UV excitation

A single phased white light emitting phosphors K₂Ca_1−x−yP₂O₇: xEu²⁺, yMn²⁺ were synthesized by solid state reaction method. The Effective energy transfer occurs in this phosphor due to the large spectral overlap between the emission of Eu²⁺ and the excitation of Mn²⁺. The emission hue of K₂Ca_1−x−yP₂O₇: xEu²⁺, yMn²⁺ from blue to white light can be obtained by tuning the Eu²⁺/Mn²⁺ content ratio. The energy transfer mechanism from Eu²⁺ to Mn²⁺ in this phosphor was carefully investigated and demonstrated to be via the dipole–quadrupole interaction.     

Luminescence properties of Tm co-doped Sr2Si5N8:Eu red phosphor

The Sr₂Si₅N₈:Eu²⁺ phosphors, both undoped and doped with Tm³⁺, were synthesized by high temperature solid-state method. The XRD pattern shows that only Sr₂Si₅N₈ phase is formed whatever Tm³⁺ was doped or not. The peak positions of both phosphors are centered at 612 nm which is assigned to the 4f⁶5d→4f⁷ transition of Eu²⁺. It implies that the crystal field, which affects the 5d electron states of Eu²⁺, is not changed dramatically after the phosphor is doped with Tm³⁺. The afterglow time is about 10 min after Tm³⁺ ion is introduced into the phosphor. The concentration of Tm³⁺ has little influence on the afterglow time of the phosphor. The depths of trap energy level of the two phosphors were calculated based on the TL spectra. The depths of Sr₂Si₅N₈:Eu²⁺ and Sr₂Si₅N₈:Eu²⁺, Tm³⁺ are 1.75 and 1.01 eV, respectively.     

Luminescence properties of Eu2+ in M2MgSi2O7 (M=Ca, Sr, and Ba) phosphors

The photoluminescence properties of alkali-earth magnesium silicates (M₂MgSi₂O₇, M=Ca, Sr, and Ba) doped with Eu²⁺ were investigated. Solid solutions of Ba _x Sr_2−x Si₂O₇, Ca₂MgSi₂O₇, and Sr₂MgSi₂O₇ were prepared. Ba _x Sr_2−x Si₂O₇ retained a tetragonal crystal structure similar to the structure of the other compounds up to a stoichiometry of x=1.6, which enabled a systematic study of the common structure. Monoclinic Ba₂MgSi₂O₇ was prepared, and the luminescence properties were compared with those of other samples. The emission and excitation spectra of tetragonal M₂MgSi₂O₇ (M=Ca, Sr, and Ba) changed as a function of the covalency, site symmetry, and crystal field strength. The luminescence properties showed excellent agreement with theoretical predictions based on these factors. The Stokes shift differentiated the emission behaviors of the tetragonal and monoclinic structures.     

Emission color variation of M2SiO4:Eu (M=Ba, Sr, Ca) phosphors for light-emitting diode

The luminescent properties of alkaline earth orthosilicates M₂SiO₄ (M=Ba, Sr, Ca) doped with Eu²⁺ ions are investigated. Two emission bands are assigned to the f-d transitions of Eu²⁺ ions doped into two different cation sites in host lattices confirmed by electron paramagnetic resonance signal. Two emission bands show the different emission color variation with substituting M²⁺ cations with smaller cations. This behavior is discussed in terms of two competing factors of the crystal field strength and covalence. Also the decay times are in order of 600-1000 ns. These phosphors with maximum excitation of around 370 nm can be applied as a color-tunable phosphor for light-emitting diode based on ultraviolet chip/phosphor technology.     

Photoluminescence of Eu single doped and Eu/Dy codoped Sr2Al2SiO7 phosphors with long persistence

This paper reports the preparation of long persistent Sr₂Al₂SiO₇:Eu²⁺ and Sr₂Al₂SiO₇:Eu²⁺, Dy³⁺ phosphors and the comparison of their photoluminescent properties. The silicate phosphors prepared by solid-state reaction routine showed a broad blue emission peaking at 484 nm when activated by UV illumination. Such a bluish-green emission can be attributed to the intrinsic 4f-5d transitions of Eu²⁺. After the UV source was switched off, long persistent phosphorescence could be observed by naked eyes for both samples in darkness. Afterglow measurements revealed that Eu/Dy codoped phosphor possesses better afterglow properties than the Eu single doped one, since the maximum lifetime (τ_max=99 s) of the photons calculated from the decay profile is much larger than that of the Eu single doped phosphor (τ_max=82 s). TSL results suggested that the difference in afterglow properties was caused by the difference in the electron traps within the crystal lattice. For Eu/Dy codoped phosphor, the doping of Dy ions produced electron traps with trap depth of 0.52 eV, which is suitable and therefore leads to good persistence. However, in the case of Eu single doped phosphor, the trap depth is 0.88 eV, which is really too deep an energy barrier to overcome, and therefore a poor persistence was observed in the experiment.     

Photoluminescent properties of Eu 3 +(Dy 3 +)-activated YNb x Ta 1 - x O 4 and REVTa 2 O 9 (RE?=?Y, La, Gd) phosphors from the hybrid precursors

In the context, Eu³⁺ (Dy³⁺)-doped YNb_xTa_1-xO₄ and REVTa₂O₉ (RE=Y, La, Gd) phosphors have been synthesized from the hybrid precursors. Both XRD and SEM indicated the particles present good crystalline state, whose crystalline grain sizes were in the range of 0.5 to 1 μm. Besides, XRD patterns of YNb_xTa_1-xO₄ (x=0.1, 0.2, 0.3, 0.5, 0.9) have shown that the phase has been changed from M^′-type YTaO₄ to M-type YNbO₄ with increasing niobium content. Furthermore, from the luminescent spectra of Eu³⁺-doped YNb_xTa_1-xO₄, it was observed that the ⁵ D ₀–⁷ F ₂ transition of Eu³⁺ was predominated and its intensity increases with increasing niobium content, as well as the intensity ratio of ⁵ D ₀–⁷ F ₂ transition to ⁵ D ₀–⁷ F ₁ transition for Eu³⁺. The optimum concentrations of Eu³⁺ and Dy³⁺ in YNb_0.5Ta_0.5O₄ have been found to be 6 and 5 mol %, respectively. At the same time, the luminescent properties of Eu³⁺ and Dy³⁺ in REVTa₂O₉ (RE=Y, La, Gd) have also been investigated that GdVTa₂O₉:Eu³⁺ (Dy³⁺) presents high luminescence, while LaVTa₂O₉:Eu³⁺ (Dy³⁺) shows weak luminescence. PACS 78.20.-e; 78.55.-m; 61.72.Ss; 32.50.+d; 81.40 Tv     

Effects of non-stoichiometry and substitution on photoluminescence and afterglow luminescence of Sr4Al14O25:Eu, Dy phosphor

The effects of nonstoichiometry and cationic substitution on photoluminescence and afterglow characteristics of strontium aluminate phosphor (Sr₄Al₁₄O₂₅:Eu²⁺, Dy³⁺) were investigated. Photoluminescence intensity of both the strontium-deficit and -rich phosphors was enhanced, but no definite correlation was observed between the afterglow intensity and non-stoichiometry. The photoluminescence emission maxima were either blue or green shifted in case of non-stoichiometric phosphors, whereas the afterglow emission maxima were not affected by the non-stoichiometry. Substitution of strontium by calcium resulted in white afterglow emission at higher calcium concentration. The emission centers in case of photoluminescence and afterglow emission appear to be different. Addition of silver significantly enhanced the afterglow intensity due to increased trap density.     

Enhanced luminescence from spontaneously ordered Gd2O3:Eu based nanostructures

Nanostructured Gd₂O₃:Eu³⁺ and Li⁺ doped Gd₂O₃:Eu³⁺ thin films were prepared by pulsed laser ablation technique. The effects of annealing and Li⁺ doping on the structural, morphological, optical and luminescent properties are discussed. X-ray diffraction and Micro-Raman investigations indicate a phase transformation from amorphous to nanocrystalline phase and an early crystallization was observed in Li⁺ doped Gd₂O₃:Eu³⁺ thin films on annealing. AFM images of Li⁺ doped Gd₂O₃:Eu³⁺ films annealed at different temperatures especially at 973 K show a spontaneous ordering of the nanocrystals distributed uniformly all over the surface, with a hillocks (or tips) like self-assembly of nanoparticles driven by thermodynamic and kinetic considerations. Enhanced photoemission from locations corresponding to the tips suggest their use in high resolution display devices. An investigation on the photoluminescence of Gd_2−xEu_xO₃ (x=0.10) and Gd_2−x−yEu_xLi_yO₃ (x=0.10, y=0.08) thin films annealed at 973 K reveals that the enhancement in luminescence intensity of about 3.04 times on Li⁺ doping is solely due to the increase in oxygen vacancies and the flux effect of Li⁺ ions. The observed decrease in the values of asymmetric ratio from the luminescence spectra of Li⁺ doped Gd₂O₃:Eu³⁺ films at high temperature region is discussed in terms of increased EuO bond length as a result of Li⁺ doping.     

Luminescence and energy transfer in Eu, Mn co-doped Li4SrCa(SiO4)2 for white light-emitting-diodes

Li₄(Sr_0.96Eu_0.04)(Ca_1 − xMn_x)(SiO₄)₂ phosphors were synthesized by solid-state reactions and photoluminescence (PL) properties were investigated. These phosphors have intense absorption in n-UV region, which is suitable for excitation of UV LEDs. The orange-reddish emission of Mn²⁺ can be adjusted by changing the Mn²⁺/Eu²⁺ ratio. Energy transfer from Eu²⁺ to Mn²⁺ is observed. Li₄(Sr_0.96Eu_0.04)(Ca_1 − xMn_x)(SiO₄)₂ phosphors could be used in white LEDs.     

Photoluminescence and thermoluminescence of Ce and Eu in Ca2Al2SiO7 matrix

The Ca₂Al₂SiO₇ samples doped with Ce³⁺ and Eu²⁺ are synthesized via a high temperature solid-state reaction. Ca₂Al₂SiO₇: Ce³⁺ emits a strong UV-violet emission while Ca₂Al₂SiO₇: Eu²⁺ emits a blue-green emission. The Stokes shift of the latter is greater due to a stronger crystal repulsion from ligands to Eu²⁺ ions. Ca₂Al₂SiO₇: Ce³⁺ exhibits a stronger initial intensity and longer duration of afterglow due to the higher liberated probability of the trapped carriers. The thermoluminescence curves reveal that at least three traps exist in the phosphors. Ca²⁺ vacancies may enhance the electron trapping and then lead to a stronger afterglow. A possible explanation will be provided.