An in situ GISAXS study of selective solvent vapor annealing in thin block copolymer films: Symmetry breaking of in-plane sphere order upon deswelling

Thin films of asymmetric poly(styrene-b-4-vinylpyridine) (PS-b-P4VP) block copolymers are studied by means of in situ grazing-incidence small-angle X-ray scattering (GISAXS) during solvent vapor annealing in tetrahydrofuran, a solvent selective for the PS majority block of the copolymer. Upon swelling, PS-b-P4VP block copolymers form hexagonal arrays of spherical P4VP microdomains in a PS matrix in films 7–9 layers thick. Deswelling the films induces a transition from hexagonal to face-centered orthorhombic (fco) symmetry, which is stable only at ∼7 layers of spherical microdomains. Dry films show co-existing hexagonal and orthorhombic symmetries when the solvent is removed slowly, whereas instantaneous solvent removal suppresses the fco structure, resulting in films with only hexagonal structure. The in-plane order of microdomains is significantly deteriorated in dry films independent of the solvent removal rate.Spherical block copolymer microdomains are known to undergo a transition from hexagonal to orthorhombic packing in isothermally annealed thin films when the number of sphere layers is increased from 4 to 5. In this paper, in situ GISAXS experiments reveal that a similar transition occurs during solvent vapor annealing in a selective solvent. Interestingly, the transition from hexagonal to orthorhombic packing of spheres occurs as solvent is removed from a thin block copolymer film. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2016, 54, 331–338     

Morphology Evolution of Block Copolymer Blend Thin Films Induced by Solvent Vapor Annealing

ABSTRACT

Self-assembly of binary block copolymer blends in thin film induced by solvent vapor annealing has been systematically studied. The diblock copolymers polystyrene-b-poly(2-vinylpyridine) with different molecular weights and volume fractions were blended with different molar ratios to cast thin films on silica substrate by spin coating. The films were annealed separately in the vapor of ethanol or toluene over time to induce morphology transformations from spheres, gyroids, and bicontinuous nanostructures, depending on the blending ratio, solvent selectivity, and annealing time, as investigated by atomic force microscopy and X-ray photoelectron spectroscopy. The formation and transformation mechanism of the self-assembly structure are discussed in the context of solvent-copolymer interactions. This study provides new insights into the simple manipulation of self-assembled nanostructures of block copolymer thin films.     

Ordering evolution of block copolymer thin films upon solvent-annealing process

Morphologies of polystyrene-block-poly(2-vinylpyridine) copolymer (S2VP) thin films, which are forming poly(2-vinylpyridine) cylinders in bulk phase, were investigated by atomic force microscopy (AFM) and transmission electron microscopy (TEM) to account for their ordering behavior induced by solvent annealing. Initially, when the copolymer was dissolved in toluene, which is selective solvent for majority polystyrene (PS) blocks, and was spin-coated on Si substrates, dimple-type micellar structures of S2VP were formed. After the film was placed in a solvent-annealing chamber covered with a lid under the existence of chloroform, surface morphologies of S2VP were measured as a function of annealing time. In this study, it was found that the morphologies of S2VP thin film repeated the cycle of the creation and extinction of various morphologies on ordering process. Namely, S2VP exhibited the various transformations between different morphologies, including highly disordered state, cylinders normal to the plane, and cylinders parallel to the plane. Each of the morphologies observed here was employed as a template to synthesize gold (Au) nanoparticles or nanowires. The arrays of Au nano-objects were used to tune a surface plasmon resonance.     

PI-b-PMMA diblock copolymers: nanostructure development in thin films and nanostructuring of thermosetting epoxy systems

Poly(isoprene-block-methyl methacrylate) (PI-b-PMMA) block copolymers with different block ratios have been used to generate nanostructures both in thin films and by nanostructuring a thermosetting epoxy system. Obtained morphologies have been analyzed in terms of atomic force microscopy. The nanostructuring of thin films was carried out by thermal and solvent vapor annealing, in which the copolymer films were exposed to acetone vapors, selective solvent for methyl methacrylate (PMMA) block. By solvent vapor annealing thin films of both copolymers self-assembled into a hexagonally packed cylindrical morphology. Thermal annealing was carried out above the glass transition temperature of both blocks, obtaining worm-like and lamellar morphologies, depending on the block ratio. One of the copolymers has also been used for nanostructuring an epoxy thermosetting system. Morphologies consisting of spherical-shaped PI domains dispersed in a continuous epoxy matrix in which PMMA remained miscible were obtained, independently of the copolymer amount.     

Nanoparticle arrangements in block copolymer particles with microphase‐separated structures

In this study, metal‐polymer particles with microphase‐separated structures were prepared by self‐organized precipitation, where a good solvent is evaporated from a solution that also contains block copolymer, Au NPs, and a poor solvent. Control of the microphase‐separated structure in composite particles consisting of Au NPs and block copolymer was accomplished by changing the Au NP size, the mix ratio, and the copolymerization ratio of the block copolymer. The morphology of the inner structures was changed from a lamellar phase to a spherical phase by increasing the Au NP concentration. © 2011 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2011     

One-step route to the fabrication of highly porous polyaniline nanofiber films by using PS-b-PVP diblock copolymers as templates

We report a new method to control both the nucleation and growth of highly porous polyaniline (PANI) nanofiber films using porous poly(styrene-block-2-vinylpyridine) diblock copolymer (PS-b-P2VP) films as templates. A micellar thin film composed of P2VP spheres within a PS matrix is prepared by spin coating a PS-b-P2VP micellar solution onto substrates. The P2VP domains are swollen in a selective solvent of acetic acid, which results in the formation of pores in the block copolymer film. PANI is then deposited onto the substrates modified with such a porous film using electrochemical methods. During the deposition, the nucleation and growth of PANI occur only at the pores of the block copolymer film. After the continued growth of PANI by the electrochemical deposition, a porous PANI nanofiber film is obtained.     

Aerosol assisted chemical vapor deposition using nanoparticle precursors: a route to nanocomposite thin films

Gold nanoparticle and gold/semiconductor nanocomposite thin films have been deposited using aerosol assisted chemical vapor deposition (CVD). A preformed gold colloid in toluene was used as a precursor to deposit gold films onto silica glass. These nanoparticle films showed the characteristic plasmon absorption of Au nanoparticles at 537 nm, and scanning electron microscopic (SEM) imaging confirmed the presence of individual gold particles. Nanocomposite films were deposited from the colloid concurrently with conventional CVD precursors. A film of gold particles in a host tungsten oxide matrix resulted from co-deposition with [W(OPh)(6)], while gold particles in a host titania matrix resulted from co-deposition with [Ti(O(i)Pr)(4)]. The density of Au nanoparticles within the film could be varied by changing the Au colloid concentration in the original precursor solution. Titania/gold composite films were intensely colored and showed dichromism: blue in transmitted light and red in reflected light. They showed metal-like reflection spectra and plasmon absorption. X-ray photoelectron spectroscopy and energy-dispersive X-ray analysis confirmed the presence of metallic gold, and SEM imaging showed individual Au nanoparticles embedded in the films. X-ray diffraction detected crystalline gold in the composite films. This CVD technique can be readily extended to produce other nanocomposite films by varying the colloids and precursors used, and it offers a rapid, convenient route to nanoparticle and nanocomposite thin films.     

Supramolecular Complex of Poly(styrene)-b-Poly(4-vinylpyridine) and 1-Pyrenebutyric Acid in Thin Film

Summary: Here, we have described a novel supramolecular complex (SMC) between poly(styrene)-b-poly(4-vinylpyridine) (PS-b-P4VP) and 1-pyrenebutyric acid (PBA) and studied of its self assembly in thin film. PBA will make supramolecular complex with the P4VP block due to strong hydrogen bonding between the carboxylic group of 1-pyrenebutyric acid and pyridine ring of P4VP. The formation of supramolecular complex between PS-P4VP and PBA through hydrogen bonding is investigated through FTIR study. The supramolecular complex of PS-b-P4VP and 1-pyrenebutyric acid changed the block copolymer morphology from cylindrical to lamella in thin film due to the increase of the volume fraction of P4VP (PBA). In both cases (parent block copolymer and SMC), the microdomains are oriented normal to the substrate after annealing in a selective solvent. Pure block copolymer shows cylindrical morphology with a periodicity of ∼26 nm, whereas the SMC shows lamellar morphology with a periodicity of ∼ 29 nm. After fabricating the thin film from SMC, 1-pyrenebutyric acid can be easily removed by dissolving the thin film in ethanol to transform the block copolymer thin film into nanotemplate or membrane.     

Fabrication of an open Au/nanoporous film by water-in-oil emulsion-induced block copolymer micelles

Water-in-oil (W/O) emulsion-induced micelles with narrow size distributions of approximately 140 nm were prepared by sonicating the polystyrene-b-poly(2-vinylpyridine) (PS-b-P2VP) block copolymer in the toluene/water (50:1 vol %). The ordered nanoporous block copolymer films with the hydrophilic P2VP interior and the PS matrix were distinctly fabricated by casting the resultant solution on substrates, followed by evaporating the organic solvent and water. The porous diameter was estimated to be about 70 nm. Here, we successfully prepared the open nanoporous nanocomposites, the P2VP domain decorated by Au (5+/-0.4 nm) nanoparticles based on the methodology mentioned. We anticipate that this novelty enhances the specific function of nanoporous films.     

Polymer/metal segmental Janus nanoparticles

Polymer/metal composite segmental Janus nanoparticles(NPs) are synthesized by sequential growth againstpoly(4-vinylpyridine)(P4VP) crosslinked cP4VP-PS Janus NPs. A Janus cluster of poly(4-vinylpyridine)-block-polystyrene(P4VPb-PS) diblock copolymer is self-organized after absorption onto a silica patchy sphere via hydrogen bonding. Selective crosslinking of P4VP leads to the formation of robust cP4VP-PS Janus NPs. Within the cP4VP domain, functional species such as metals are preferentially grown by in situ reduction. Other thiol-capped polymers, for example, thiol-cappedpoly(Nisopropylacrylamide)(PNIPAM-SH), can be conjugated onto the opposite side to form polymer/metal triple segmental Janus NPs. The hyperthermia effect of Au NP of PNIPAM-Au@cP4VP-PS by near infrared(NIR) irradiation can trigger a fast transition from amphiphilic to hydrophobic of the Janus NPs at low surrounding temperature. De-stabilization ofthe emulsion is NIR triggered although the system temperature is below LCST(~32 °C).     

Solvent vapor annealing of block copolymer thin films: removal of processing history

The ordering processes of PS-b-P2VP block copolymer thin films with different processing histories were studied during solvent vapor annealing by in situ grazing incidence small-angle X-ray scattering (GISAXS). We compared cylinder-forming PS-b-P2VP thin films with 34 kg/mol molecular weight that were prepared in three different ways: spin coating, spin coating and subsequent solvent vapor annealing where the solvent vapor was removed instantaneously, and spin coating and subsequent solvent vapor annealing where the solvent vapor was removed slowly. Block copolymer thin films retained the morphology resulting from the different “processing histories” at smaller swelling ratios. This processing history was erased when the samples reached a higher swelling ratio (~1.4). After the solvent was slowly removed from the swollen film, the surface morphology was characterized by ex situ AFM. All samples showed the same morphology after solvent annealing regardless of the initial morphology, indicating the morphology of solvent annealed samples is determined by the polymer concentration in the swollen film and the solvent vapor removal rate, but not the processing history.     

Solvent-induced novel morphologies in diblock copolymer blend thin films

We report the morphology and phase behaviors of blend thin films containing two polystyrene-b-poly(methyl methacrylate) (PS-b-PMMA) diblock copolymers with different blending compositions induced by a selective solvent for the PMMA block, which were studied by transmission electron microscopy (TEM). The neat asymmetric PS-b-PMMA diblock copolymers employed in this study, respectively coded as a1 and a2, have similar molecular weights but different volume fractions of PS block (fPS=0.273 and 0.722). Another symmetric PS-b-PMMA diblock copolymer, coded as s, which has a PS block length similar to that of a1, was also used. For the asymmetric a1/a2 blend thin films, circular multilayered structures were formed. For the asymmetric a1/symmetric s blend thin films, inverted phases with PMMA as the dispersed domains were observed, when the weight fraction of s was less than 50%. The origins of the morphology formation in the blend thin films via solvent treatment are discussed. Combined with the theoretical prediction by Birshtein et al. (Polymer 1992, 33, 2750), we interpret the formation of these special microstructures as due to the packing frustration induced by the difference in block lengths and the preferential interactions between the solvent and PMMA block. Results obtained here suggest that diblock copolymer blend thin films treated with a selective solvent offer an alternative and attractive approach to control the self-organization of polymers.     

A Novel Route for Fabricating Metal‐Polymer Composite Nanoparticles with Phase‐Separated Structures

Au nanoparticles (NPs) and polymer composite particles with phase‐separation structures were prepared based on phase separation structures. Au NPs were successfully synthesized in amphiphilic block‐copolymer micelles, and then composite particles were formed by a simple solvent evaporation process from Au NPs and polymer solution. The phase separated structures (Janus and Core‐shell) were controlled by changing the combination of polymers having differing hydrophobicity.

     

Nanoscale patterning of two metals on silicon surfaces using an ABC triblock copolymer template

Patterning technologically important semiconductor interfaces with nanoscale metal films is important for applications such as metallic interconnects and sensing applications. Self-assembling block copolymer templates are utilized to pattern an aqueous metal reduction reaction, galvanic displacement, on silicon surfaces. Utilization of a triblock copolymer monolayer film, polystyrene-block-poly(2-vinylpyridine)-block-poly(ethylene oxide) (PS-b-P2VP-b-PEO), with two blocks capable of selective transport of different metal complexes to the surface (PEO and P2VP), allows for chemical discrimination and nanoscale patterning. Different regions of the self-assembled structure discriminate between metal complexes at the silicon surface, at which time they undergo the spontaneous reaction at the interface. Gold deposition from gold(III) compounds such as HAuCl4(aq) in the presence of hydrofluoric acid mirrors the parent block copolymer core structure, whereas silver deposition from Ag(I) salts such as AgNO3(aq) does the opposite, localizing exclusively under the corona. By carrying out gold deposition first and silver second, sub-100-nm gold features surrounded by silver films can be produced. The chemical selectivity was extended to other metals, including copper, palladium, and platinum. The interfaces were characterized by a variety of methods, including scanning electron microscopy, scanning Auger microscopy, X-ray photoelectron spectroscopy, and atomic force microscopy.     

Amphiphilic gold nanoparticles with V-shaped arms

Here we describe a very efficient method to produce well-defined amphiphilic gold nanoparticles (Au NPs) with an equal number of hydrophobic and hydrophilic arms which are distributed along the surface of a 2-nm gold core in an alternating fashion. The strategy involves direct coupling of V-shaped block copolymer amphiphile 2 with a carboxylic group at its junction point to mercaptophenol-terminated Au NPs. The reaction proceeds under mild esterification conditions and yields the product with a molecular weight of 40 kDa, high grafting density (2.9 chains/nm2), and extremely low polydispersity (1.07). The big advantage of this approach is the opportunity to avoid the use of expensive and often inaccessible polymeric thiols. The method described here is applicable to any carboxyl-terminated molecules and can be used for the preparation of complex, yet well-defined, macromolecular hybrid structures such as 1 (Au(PB-PEG)n). The new product, which was characterized by a combination of SEC, NMR, UV-vis, DLS, and TEM, represents a unique example of gold nanoparticles soluble in any conventional solvent.     

Creating surfactant nanoparticles for block copolymer composites through surface chemistry

A simple strategy to tailor the surface of nanoparticles for their specific adsorption to and localization at block copolymer interfaces was explored. Gold nanoparticles coated by a mixture of low molecular weight thiol end-functional polystyrene (PS-SH) (Mn = 1.5 and 3.4 kg/mol) and poly(2-vinylpyridine) homopolymers (P2VP-SH) (Mn = 1.5 and 3.0 kg/mol) were incorporated into a lamellar poly(styrene-b-2-vinylpyridine) diblock copolymer (PS-b-P2VP) (Mn = 196 kg/mol). A library of nanoparticles with varying PS and P2VP surface compositions (FPS) and high polymer ligand areal chain densities was synthesized. The location of the nanoparticles in the PS-b-P2VP block copolymer was determined by transmission electron microscopy. Sharp transitions in particle location from the PS domain to the PS/P2VP interface, and subsequently to the P2VP domain, were observed at FPS = 0.9 and 0.1, respectively. This extremely wide window of FPS values where the polymer-coated gold nanoparticles adsorb to the interface suggests a redistribution of PS and P2VP polymers on the Au surface, inducing the formation of amphiphilic nanoparticles at the PS/P2VP interface. In a second and synthetically more challenging approach, gold nanoparticles were covered with a thiol terminated random copolymer of styrene and 2-vinylpyridine synthesized by RAFT polymerization. Two different random copolymers were considered, where the molecular weight was fixed at 3.5 kg/mol and the relative incorporation of styrene and 2-vinylpyridine repeat units varied (FPS = 0.52 and 0.40). The areal chain density of these random copolymers on Au is unfortunately not high enough to preclude any contact between the P2VP block of the block copolymer and the Au surface. Interestingly, gold nanoparticles coated by the random copolymer with FPS = 0.4 were dispersed in the P2VP domain, while those with FPS = 0.52 were located at the interface. A simple calculation for the adsorption energy to the interface of the nanoparticles with different surface arrangements of PS and P2VP ligands supports evidence for the rearrangement of thiol terminated homopolymers. An upper limit estimate of the adsorption energy of nanoparticles uniformly coated with a random arrangement of PS and P2VP ligands where a 10% surface area was occupied by P2VP -mers or chains was approximately 1 kBT, which indicates that such nanoparticles are unlikely to be segregated along the interface, in contrast to the experimental results for nanoparticles with mixed ligand-coated surfaces.     

Mineralization of gold in block copolymer micelles

Ultrasmall gold particles have been prepared inside the micelles of polystyrene-block-poly(ethylene oxide) and polystyrene-block-poly(2-vinylpyridine) in toluene. Starting point was the formation of a thermodynamically stable dispersion of HAuCl₄ or LiAuCl₄ in the inverse micelles of the block copolymer which were treated with hydrazine or pyrrole. Analysis of the effect of the reduction agent on the stability of the micelles yielded a simple model for the transformation process involving coagulation of the swelling micelles. Kinetic control of the different steps, i.e., reduction, mineralization, coagulation, film formation, allowed to prepare thin films in which highly uniform gold particles were arranged in yet unknown order. When pyrrole was employed for the reduction, the gold monocrystals got embedded in a shell of polypyrrole.     

Multiscale dewetting of triblock copolymer thin film induced by solvent vapor

Multiscale dewetting of poly(styrene‐b‐ethylene/butylenes‐b‐styrene) (SEBS) triblock copolymer thin films induced by volatile solvent vapor treatment were observed in this study. Film rupture occurred at first and produced macroscopic holes. Near‐regular droplets (which represented a compromise between complete disorder and perfect order) could be formed at the last stage. The mechanism of solvent‐driven dewetting was discussed by comparing with that of thermal‐induced dewetting. Similar to thermal‐induced dewetting, the block copolymer thin films initially break up through the nucleation of holes that perforated the films. The rapid growing holes became unstable and formed nonequilibrium fingering patterns. The films exhibit autophobic or autodewetting phenomena. The velocity of the holes growth was nearly a constant (3.3 μm/min). The stages of the dewetting were quite similar to that found for homopolymer and block copolymer thin films dewetting on solid or liquid substrates under thermal treatment. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 2874–2884, 2005     

Synthesis of gold nanoparticles stabilized with poly(N-isopropylacrylamide)-co-poly(4-vinyl pyridine) colloid and their application in responsive catalysis

The copolymer of poly(N-isopropylacrylamide)-co-poly(4-vinylpyridine) was synthesized by free radical copolymerization of 4-vinylpyridine and N-isopropylacrylamide. The copolymer synthesized with the feed monomer ratio of 4-vinylpyridine/N-isopropylacrylamide equal to 1/3 was associated to form thermoresponsive colloid in neutral water at room temperature, the average size and the cloud-point temperature of which were 40 nm and 32 °C, respectively. The thermoresponsive colloid was used as scaffold to load 2-nm Au nanoparticles to form the responsive catalyst of colloid-stabilizing gold nanoparticles. The catalysis in the model reduction of 4-nitrophenol with NaBH₄ suggested that the catalytic reduction could be modulated due to the thermoresponsive phase-transition of the colloid-stabilizing gold nanoparticles. That was, the catalytic reduction firstly accelerated with the increase in temperature below the cloud-point temperature and then decelerated with the increase in temperature above the cloud-point temperature of the thermoresponsive colloid-stabilizing Au nanoparticles.     

Micellar structures of poly(styrene-b-4-vinylpyridine)s in THF/toluene mixtures and their functionalization with gold

The effects of the block copolymer composition and the solvent selectivity on the micellar morphologies of poly(styrene- b-4-vinylpyridine)s (PS- b-P4VPs) and their functionalizations with gold were studied in 10 mg/mL solutions using small-angle X-ray scattering and transmission electron microscopy (TEM). The solvent selectivity for the PS block was controlled by toluene/tetrahydrofuran (THF) mixtures in which toluene and THF are selective for PS and nonselective, respectively. The micellar structure was strongly dependent on phi (wt % toluene in toluene/THF mixture) and the composition of the block copolymers. PS(12K)- b-P4VP(11.8K) (symmetric) showed spherical micelles in the entire range of phi except phi = 0 (THF, nonselective solvent). PS(3.3K)- b-P4VP(18.7K) (asymmetric, longer P4VP) showed multiple morphologies with transitions from spheres to cylinders and finally to vesicles with an increase in phi. PS(19.6K)- b-P4VP(5.1K) (asymmetric, longer PS) showed spherical micelles only at the narrow ranges of 90 wt % 相似文献