管线钢LF脱氧脱硫热力学及实验分析

通过对LF冶炼高级别管线钢的脱氧热力学分析和脱硫影响的研究,确定了合理的脱氧剂量.为对比改进效果进行了工业实验,同时分析了渣中各氧化物和造渣工艺对脱硫效率的影响,给出了首钢迁钢要达到高脱硫效率所需的最佳渣系和各指标值,并指出进站20min内是脱硫最关键的时段.改进后的工艺可以使LF冶炼周期缩短约8min.     

钢水定氧半电池电极粉的预处理工艺研究

炼钢过程中钢水氧含量的准确测量关键在于定氧半电池,其参比电极粉以Cr2O3和Cr粉末为主要原料。研究Cr2O3和Cr粉末的混合比例,并进行相应的装配前预处理,以制备适用于低氧端测试的半电池参比电极粉。结果表明,为保证参比气氛氧分压的稳定,参比电极粉中Cr必须过量;采用球磨混合方式,通过预烧结处理的参比电极粉,可有效防止高温烧结团聚现象,提高定氧电信号的测量速度和准确性。     

RH真空处理GCr15轴承钢中全氧及显微夹杂物的行为研究

针对RH工艺生产轴承钢,通过现场试验研究了RH真空处理时间对钢中全氧和显微夹杂物的影响.试验结果表明,延长RH真空时间可以进一步降低钢中全氧和显微夹杂物的数量,RH脱氧主要是通过显微夹杂物的去除,全氧与显微夹杂物随时间的变化关系基本一致;真空处理25min可使钢液中全氧和显微夹杂降低约60%,比14min时多降低约13%,并得出邢钢轴承钢生产条件下,RH精炼过程钢液的表观脱氧速度系数为-0.036min-1;工艺优化后147炉轴承钢产品的平均全氧为6.7×10-6.     

RH处理超低碳铝镇静钢的总氧预测模型及应用

根据300t钢包RH真空处理超低碳铝镇静钢的实验数据,建立了RH处理过程钢中总氧含量的预测模型,得到了钢中氧含量的预测公式.模型综合考虑了处理时间、真空室吹氩流量、钢水环流量、浸渍管直径和钢包渣中(FeO+MnO)含量等因素对总氧含量的影响,并对改进RH处理工艺进行了讨论.模型分析表明,促进夹杂物上浮的手段有增大吹氩流量、增加浸渍管直径,但都有一个合适的范围.     

无取向电工钢脱碳组织的动力学分析

无取向电工钢两相区脱碳退火获得柱状铁素体晶粒可有效改善材料组织的均匀性.本文从动力学角度分析柱状晶的生长过程.柱状晶的形成分为“形核”和定向生长两个阶段,其中定向生长过程本质上是反应扩散和再结晶长大共同引起的界面迁移,且在动力学上符合抛物线规律,但其生长速率与退火温度之间并非呈单调的变化关系,而是在900℃时呈极大值.最后结合柱状晶生长速率的导出公式得到柱状晶“晶核”的尺寸约束条件,这对实际生产过程中无取向电工钢脱碳工艺的设计有一定的指导意义.     

CAS-OB钢水同时降低[Al]_s,[O]和T.O的实验研究

为防止常规ＣＡＳ－ＯＢ铝热法精炼钢水时［Ａｌ］ｓ和Ｔ［Ａｌ］过高而导致连铸时中间包水口 堵塞,对用Ａｌ－ＣａＯ处理钢水进行了实验结果表明：用Ａｌ－ＣａＯ脱氧能够同时降低钢中溶解氧、 总氧（１０×１０－６～３０×１０－６）和酸溶铝量（７×１０－６～１２×１０－６）,并能控制钢中夹杂物的形态、数量和分布．     

钢液精炼和连铸过程中物理去除夹杂物现状及展望

夹杂物去除是钢液精炼的重要任务之一。目前与去除夹杂物相关的工艺方法主要有:钢包-电磁搅拌和钢包底吹氩;RH及RH侧底复吹;中间包-控流装置、气幕挡墙和通道电磁感应加热;结晶器电磁搅拌与电磁制动和水口吹氩。本文总结了钢水精炼中各个反应器去除夹杂物的方法和机理,并分析了影响夹杂物去除效率的主要因素,为钢水二次精炼的夹杂物去除工艺优化提供理论依据和参考。     

Mechanism and simulation of droplet coalescence in molten steel

Droplet coalescence in liquid steel was carefully investigated through observations of the distribution pattern of inclusions in solidified steel samples. The process of droplet coalescence was slow, and the critical Weber number (We) was used to evaluate the coalescence or separation of droplets. The relationship between the collision parameter and the critical We indicated whether slow coalescence or bouncing of droplets occurred. The critical We was 5.5, which means that the droplets gradually coalesce when We ≤ 5.5, whereas they bounce when We > 5.5. For the carbonate wire feeding into liquid steel, a mathematical model implementing a combined computational fluid dynamics (CFD)-discrete element method (DEM) approach was developed to simulate the movement and coalescence of variably sized droplets in a bottom-argon-blowing ladle. In the CFD model, the flow field was solved on the premise that the fluid was a continuous medium. Meanwhile, the droplets were dispersed in the DEM model, and the coalescence criterion of the particles was added to simulate the collision-coalescence process of the particles. The numerical simulation results and observations of inclusion coalescence in steel samples are consistent.     

CSP结晶器内钢液流动及凝固的数值模拟

应用数值模拟方法,建立CSP漏斗型结晶器内钢液流动及凝固传热耦合模型。针对结晶器内铸坯角部受到强冷的特点,对结晶器内热流密度采用修正方程进行计算,分析热流密度修正系数对铸坯凝固坯壳表面温度计算精度的影响。通过比较不同拉坯速率下结晶器内钢液凝固的特点,研究凝固坯壳对结晶器内钢液流动行为的影响。结果表明,采用热流密度修正系数后,铸坯凝固坯壳角部温度的计算值与实际情况更相符;提高拉坯速率可使铸坯凝固坯壳厚度减小;拉坯速率较大时凝固坯壳厚度随铸坯距弯月面距离的增大基本呈线性增长,拉坯速率为3m/min时,凝固坯壳在生长过程中厚度的增长有短暂的停滞现象;凝固坯壳对钢液流动的影响较大,主要是由钢液有效流动区域减少及两相区额外动量阻损造成的。     

全浮动芯棒钢管连轧金属流动的有限元分析

结合生产实际,采用ABAQUS显式动力仿真平台,对宝钢140mm全浮动芯棒钢管连轧过程中金属的变形及流动规律进行了仿真分析.分析结果表明:金属的横向流动主要表现为从孔顶区域流向侧壁区域;金属的纵向延伸主要发生在孔顶区域,且钢管外壁金属相对内壁金属向前滑移.孔型侧壁区域金属的横向堆积及纵向延展不充分是导致荒管壁厚不均的主要原因.