熔片X射线荧光光谱法测定锡矿石中八种重金属元素

建立了X射线荧光光谱法测定锡矿石中8种重金属元素Fe,Cu,Zn,As,Sn,Sb,Pb,Bi的分析方法。通过固体纯物质机械混合研磨配制了校准曲线所用的标准样品。采用混合熔剂(Li2B4O7:Li BO2:Li F=10:2.5:1,质量比)加氧化剂Li NO3熔融制备了X射线荧光法所用玻璃片样品(混合熔剂:Li NO3:试样=20:3:1质量比)。在高温熔融过程中,易挥发元素As,Pb一直存在于熔体中,未随熔融时间的增加而出现挥发损失。使用外加内标元素法(In和Co)对元素Sn,Sb,Fe的吸收增强效应进行校正,其它元素使用Compton散射线内标法进行校正。采用干扰曲线法校正Pb Lα对As Kα以及Sn Lβ1背景峰对Sb Lα的谱线重叠干扰。各元素检出限分别为Fe 0.0074%,Cu 0.0043%,Zn 0.0025%,As 0.0036%,Sn 0.019%,Sb 0.010%,Pb 0.0039%,Bi 0.0026%。对国家一级标准物质锡精矿GBW07232和锡矿石GBW07281分别进行10次制样测量,各元素精密度(RSD)在0.11%~18%之间。     

碳酸氢钠-氧化镁半熔-碘电极法测定磷矿中碘

建立了NaHCO_3-MgO半熔-I电极法测定磷矿中微量碘的分析方法。研究了半熔剂、程序控温半熔方式、酸度等因素对测定结果的影响,通过优化实验条件,选择NaHCO_3-MgO(3:2)为半熔剂,采用由室温升至500℃熔融30min,再升到750℃熔融30min的程序控温方式熔融分解,离心去除干扰离子,在pH5的C_6H_8O_7·H_2O-Na_3C_6H_5O_7·2H_2O缓冲溶液中测定磷矿中I,其检出限为0.006μg/mL,加标回收率在99.0%~102.0%之间,相对标准偏差(RSD)≤6.0%。同时测定了国家标准物质磷矿,结果与参考值一致。     

X射线荧光光谱法测定金红石中主次组分

采用Li2B4O7和LiBO2的混合熔剂(67∶33)熔融制样,波长色散X射线荧光光谱法测定金红石中TiO2,TFe,P,SiO2,Al2O3,MnO,CaO,Cr2O3,MgO,ZrO2,HfO2等组分。实验中样品和熔剂的质量比为1∶14,以溴化锂(LiBr)作脱模剂,采用高频熔炉在1 150℃熔融90s进行制样,所得熔片均匀、强度高、成型良好。方法用于金红石实际样品的测定,结果同参考值或化学分析方法的结果相吻合,相对标准偏差(RSD,n=10)P为3.8%、Al2O3为2.8%,其它均小于2%,能够满足实际测定工作的需要。     

X射线荧光光谱法测定金红石中主次组分

采用Li2B4O7和LiBO2的混合熔剂(67∶33)熔融制样,波长色散X射线荧光光谱法测定金红石中TiO2,TFe,P,SiO2,Al2O3,MnO,CaO,Cr2O3,MgO,ZrO2,HfO2等组分。实验中样品和熔剂的质量比为1∶14,以溴化锂(LiBr)作脱模剂,采用高频熔炉在1 150℃熔融90s进行制样,所得熔片均匀、强度高、成型良好。方法用于金红石实际样品的测定,结果同参考值或化学分析方法的结果相吻合,相对标准偏差(RSD,n=10)P为3.8%、Al2O3为2.8%,其它均小于2%,能够满足实际测定工作的需要。     

X射线荧光光谱法测定钠冰晶石的主要化学成分

选用国家标准样品和高纯物质配制实验用标准样品,采用混合熔剂(67%Li2B4O7+33%LiBO2)熔融制样,使用X射线荧光光谱法测定钠冰晶石中SiO2、Fe2O3、MgO、CaO、K2O、TiO2、P2O5、Na、F、Al各组分的含量,实验结果表明,各组分的相对标准偏差(RSD)在0.57%~6.5%,与第三方实验室对比测定结果表明,方法可以满足工厂检测要求。     

磷酸硼中三氧化二硼的测定方法研究

研究了以KOH为熔剂,高温熔融样品,Pb(NO3)2分离磷酸根,甘露醇作H3BO3强化剂,电位差滴定测定磷酸硼中三氧化二硼的分析方法.该方法的回收率为98%～99%,RSD 0.3%～0.4%,能满足科研和生产的分析需要.     

X射线荧光光谱法测定硅石中主次量元素组分

以Li_2B_4O_7、LiBO_2和LiF(质量比为45∶10∶5)为混合熔剂,NH_4NO_3为氧化剂,LiBr为脱模剂,熔融制作样片,采用硅质砂岩、石英岩标准样品和配制标准样品作为校准样品,建立了熔融制样-X射线荧光光谱法(XRF)测定硅石中主次量成分(SiO_2、Al_2O_3、TFe_2O_3、MgO、CaO、K_2O、MnO、TiO_2、P_2O_5)的快速分析方法。对样品制备以及分析测试过程中的条件进行了优化,在最优条件下,对标准样品(GBW03112、GBW07835)进行重复测定,相对标准偏差RSD2%。同时对3个混合配制的硅石标准样品进行分析,结果与参考值无显著性差异。     

熔融制样X射线荧光光谱法测定水泥及水泥熟料中成分

采用波长色散X射线荧光光谱仪测定水泥和水泥熟料中的Na2O、MgO、A12O3、SiO2、P2Os、SO3、K2O、CaO、TiO2、MnO、Fe2O3等成分。采用熔融玻璃片方法制样,采用Li2B4O7为熔剂,较混合熔剂的制样效果好;硫在1050℃熔融制样过程中的挥发较慢,对测定结果无明显影响。方法测定准确度、精密度较好,所得结果与湿法化学分析结果相符。     

熔融制样-X射线荧光测定锰矿中10种主次成分的条件优化

选用Li_2B_4O_7、LiBO_2和LiF(质量比为45∶10∶5)为混合熔剂,NH_4NO_3为氧化剂,LiBr为脱模剂,熔融制作样片,利用岛津1800型X射线荧光光谱分析仪对GBW07261~GBW07266等锰矿标准物质拟合校准曲线,建立了X射线荧光同时测定锰矿中10种主次量组分(SiO_2、Al_2O_3、Fe、MgO、CaO、K_2O、Mn、TiO_2、P、Zn)的快速分析方法.对样品制备以及分析测试过程中的条件(熔剂稀释比例、熔融温度及时间、测定电压电流以及PHA等)进行了优化,在优化条件下,对GBW07263、GBW07265进行重复测定,相对标准偏差(RSD,n=12)低于2%.同时对锰矿标准样品及合成锰矿样品进行分析,结果与参考值一致.     

火焰原子吸收法测定铬质引流砂中铁镁含量

建立了火焰原子吸收光谱法连续测定铬质引流砂中铁、镁含量的分析方法。试样以碳酸钠-硼酸混合熔剂熔融,以盐酸浸取,在校准溶液中加入重铬酸钾和二氧化硅进行基体匹配,抵消基体影响。对熔剂、熔融温度等进行讨论,确立了最佳分析条件,对样品多次测定,其测定结果与国家标准测定方法测定的结果基本一致,相对标准偏差(RSD,n=11)小于0.3%,加标回收率在98.7%~101%。方法具有操作简便、准确性好、速度快、成本低等特点。     

络合滴定法快速测定重晶石中的钡

采用沉淀、给 合滴定法，间接快速地测定了重晶石中钡的含量。对重晶石熔样方式、络合反应条件及共存干扰离子的消除方法进行了研究。该方法快速、准确，加收率为98.5%-100.7%，RSD小于2.48%。     

巯基棉分离富集-ICP-AES测定高盐体系中痕量的铅、镉

采用巯基棉富集分离,电感耦合等离子体原子发射光谱法（ICP-AES）测定了高盐水样中痕量的铅、镉。研究表明,pH值为7时,巯基棉同时富集铅、镉的效果最好,可成功分离基体元素,以盐酸（1.5mol/L）溶液洗脱,铅、镉的加标回收率在95.0%~105.0%,相对标准偏差RSD为3.8%~9.7%。     

熔融法制样-X射线荧光光谱法测定锌精矿中主、次组分含量

应用X射线荧光光谱法测定了锌精矿中主次量组分(包括锌、硫、铁、硅、铅、铜、砷、银、镉、锡及锑)。锌精矿样品(0.6g)与6.3g四硼酸锂和3.2g硝酸锂置于铂-金坩埚中拌匀,先在500℃随即升至700℃灼烧10min,使样品中的硫离子预氧化为硫酸盐。硝酸锂与四硼酸锂生成四硼酸锂和偏硼酸锂混合物熔剂,在1 030℃熔融样品10min,将熔化的样品倒入样模中,冷却后脱模所得熔块用于X射线荧光光谱分析。对在预氧化及熔融过程中由于样品组成变化及质量的增加所造成的基体干扰,采用基于Sherman方程的可变理论α影响系数法进行校正。在所测定的元素中,锌和硫的校准曲线范围依次为27%～62%和10%～35%,两者的标准偏差均小于0.2%。应用所提出的方法分析了2个CRM(GBW 07168和SRM 113b),所得测定值与认定值一致。     

Determination of carbonate content in barite ore by headspace gas chromatography

This paper reports a method for determining the carbonate content in barite ore using headspace gas chromatography. Based on the acidification reaction, the carbonate in the barite ore was converted to CO₂ in a closed headspace vial. When the carbonate content was significant, the pressure caused changes in the CO₂ and O₂ signals and affected the measurement accuracy. It was found that carbonate content is proportional to the intensity ratio of the CO₂ to O₂ signals. Thus, the carbonate content in barite ore can be measured indirectly using a theoretical model. The results showed that the carbonate in 3 g of barite ore sample with a particle size of 74 μm could react completely with a hydrochloric acid solution (2 mol/L) at 65°C for 5 min. The method described herein had good precision (relative standard deviation < 4.14%) and accuracy (relative differences < 6.12%). Further, the limit of quantification was 0.07 mol/L. Owing to its simplicity and speed, this method can be used for the batch determination of carbonate content in barite ore.     

高频燃烧红外吸收光谱法测定碳酸钴中的硫

采用高频燃烧红外吸收光谱法测定碳酸钴中的硫,在测定过程中先将样品进行灼烧处理,并选用纯铁和钨助熔剂熔样,解决了水分干扰和样品熔解不完全的问题。方法可以准确测定碳酸钴中质量分数为0.001%~0.01%的硫,加标回收率为98.4%~101.4%,相对标准偏差RSD为2.8%~6.3%。     

硅胶管采样—液相色谱法测定空气中的氯氰菊酯

本文报道空气中氯氰菊酯的高效液相色谱测定方法，空气样品用硅胶管采样，经甲醇洗脱后用ＨｙｐｏｒｓｉｌＯＤＳ柱分离，紫外检测器检测，在本法的测定条件下，最低检测浓度为０．０４ｍｇ／ｍ＾３，当氯氰菊酯浓度范围为０～２５．０ｍｇ／Ｌ时，呈线性响应关系，相对标准偏差为２．４％～８．４％，本法的解吸效率为９６．８％～１００．３％，采样效率为１００％，氯氰菊酯在硅胶管中可稳定７ｄ。     

X射线荧光光谱法测定萤石中的氟,钙及二氧化硅

提出艇偏硼酸锂和四硼酸锂混合熔剂熔融制样，以Ｘ－射线荧光光谱法定量测定萤石中ＣａＦ２、总钙和二氧化硅。经实际试样和标准试样检测，本法可用实际试样分析，在ＣａＦ２含量为７７－９８％时，其最大误差为０．６０％。     

海水中铜锌铅镉的萃取-反萃取法同时提取-原子吸收光谱法测定

采用萃取-反萃取法同时提取出海水中Cu、Zn、Pb、Cd,Cu、Pb、Cd石墨炉法测定,Zn用火焰法测定.对样品的前处理方法和最佳仪器条件进行了研究,并通过加标实验验证了方法的可靠性.结果表明:萃取-反萃取法能完全满足海水中Cu、Zn、Pb、Cd的前处理要求,可节省一半前处理时间,有溶液稳定、环保、节省试剂等优点.     

A multi-scale assessment of Pb(II) sorption on dolomite

Macroscopic sorption studies indicated that Pb sorption capacity was independent of pH over the pH range 5-7, while sorption as a function of reaction time up to two weeks for systems with no bulk precipitate phases showed continuous Pb uptake on dolomite. This could be due to diffusion of Pb into the micropores of dolomite as well as an increase in surface sites caused by particle size reduction during suspension mixing. Normalized XANES spectra for systems undersaturated with respect to Pb carbonate precipitates resembled the spectrum of Pb4(OH)4(4+), suggesting that Pb is mainly coordinated to dolomite as an inner-sphere surface complex. On the other hand, the XANES spectrum for 10(-3) M Pb at 1 atm CO2(g) in a 2 M Mg(NO3)2 background electrolyte solution resembled that of cerussite, while a sample at 5 x 10(-4) M Pb in equilibrium with air and 2 M Mg(NO3)2 resembled that of hydrocerussite. EXAFS analyses of sorption samples in chloride solutions showed that there were only first-shell contributions under 1 atm CO2(g), while higher shell contributions from Ca/Mg were seen at 10(-3.42) atm CO2(g). On the other hand, EXAFS samples prepared in nitrate solutions showed noticeable differences in speciation under different reaction conditions-from outer-sphere surface complexes at low Pb concentrations and pH, to inner-sphere surface complexes at moderate Pb concentrations and neutral pH, to the formation of Pb carbonate precipitates at the highest Pb loadings.     

脉冲熔融-飞行时间质谱法测定Ti-Al合金中氩

以标准气体参考物质为依据绘制氩校准工作曲线,利用脉冲熔融-飞行时间质谱法建立了准确测定钛铝合金中氩的分析方法。通过程序升温法确定钛铝合金中氩可以在分析功率为2800W时完全释放。并对比了助熔剂和称样量等分析条件对实验结果的影响,结果表明,采用高纯镍篮,钛铝合金中氩释放完全。脉冲熔融-飞行时间质谱法测定的结果与传统脉冲熔融-热导法测定结果基本一致。