Self-bonding in an amorphous polymer below the glass transition: A T-peel test investigation

Films of amorphous polystyrene (PS) with a weight-average molecular weight (M_w) of 225 × 10³ g/mol were bonded in a T-peel test geometry, and the fracture energy (G) of a PS/PS interface was measured at the ambient temperature as a function of the healing time (t_h) and healing temperature (T_h). G was found to develop with (t_h)^1/2 at T_h = T_g-bulk − 33 °C (where T_g-bulk is the glass-transition temperature of the bulk sample), and log G was found to develop with 1/T_h at T_g-bulk − 43 °C ≤ T_h ≤ T_g-bulk − 23 °C. The smallest measured value of G = 1.4 J/m² was at least one order of magnitude larger than the work of adhesion required to reversibly separate the PS surfaces. These three observations indicated that the development of G at the PS/PS interface in the temperature range investigated (<T_g-bulk) was controlled by the diffusion of chain segments feasible above the glass-transition temperature of the interfacial layer, in agreement with our previous findings for fracture stress development at several polymer/polymer interfaces well below T_g-bulk. Close values of G = 8–9 J/m² were measured for the symmetric interfaces of polydisperse PS [M_w = 225 × 10³, weight-average molecular weight/number-average molecular weight (M_w/M_n) = 3] and monodisperse PS (M_w = 200 × 10³, M_w/M_n = 1.04) after healing at T_h = T_g-bulk − 33 °C for 24 h. This implies that the self-bonding of high-molecular-weight PS at such relatively low temperatures is not governed by polydispersity. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1861–1867, 2004     

Molecular relaxation in the blends of polystyrene/poly(2,6-dimethyl-1,4-phenylene oxide) at low temperature

Molecular relaxation behavior in terms of the α, β, and γ transitions of miscible PS/PPO blends has been studied by means of DMTA and preliminary work has been carried out using DSC. From DSC and DMTA (by tan δ), the observed α relaxation (T_α or T_g) of PS, PPO, and the blends, which are intermediate between the constituents, are in good agreement with earlier reports by others. In addition, the β transition (T_β) of PS at 0.03 Hz and 1 Hz is observed at −30 and 20°C, respectively, while the γ relaxation (T_γ) is not observed at either frequency. The T_β of PPO is 30°C at 0.03 Hz and is not observed at 1 Hz, while the T_γ is −85°C at 0.03 Hz and −70°C at 1 Hz. On the other hand, blend composition-independent β or γ relaxation observed in the blends may be a consequence of the absence of intra- or intermolecular interaction between the constituents at low temperature. Thus it is suggested that at low temperature, the β relaxation of PS be influenced solely by the local motion of the phenylene ring, and that the β or γ relaxation of PPO be predominated by the local cooperative motions of several monomer units or the rotational motion of the methyl group in PPO. © 1998 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 36: 1981–1986, 1998     

Synthesis and characterization of polyesteramides derived from an oxazoline-functional alcohol and dicarboxylic acid anhydrides

Novel polyesteramides were synthesized by copolymerization in bulk of 5-(4,5-dihydro-1,3-oxazol-2-yl)-1-pentanol and various cyclic dicarboxylic acid anhydrides at temperatures varying between 120 and 200°C. The polymers resulting from polycondensation were characterized by means of ¹H–NMR, FTIR, MALDI–TOF–MS, SEC, and DSC. The glass transition temperatures, T_g, of the copolymers were varied between −28 and +31°C as a function of the anhydride type. Molecular weights, M_w, were dependent on reaction temperature, reaction time, and anhydride type. Spectroscopic investigation of reaction products and esteramide model compounds provided evidence for imide by-product formation, which accounts for the low degree of polymerization. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 3367–3376, 1999     

SURFACE RHEOLOGY OF POLYMERIC SOLIDS

Surface molecular motions of amorphous polymeric solids have been directly measured on the basis of scanningviscoelasticity microscopic (SVM) and lateral force microscopic (LFM) measurements. SVM and LFM measurements werecarried out for films of conventional monodisperse polystyrene (PS) with sec-butyl and proton-terminated end groups atroom temperature. In the case of the number-average molecular weight, M_n, less than ca. 4.0×10~4, the surface was in a glass-rubber transition state even though the bulk glass transition temperature, T_g was far above room temperature, meaning thatthe surface molecular motion was fairly active compared with that in the bulk. LFM measurements of the, monodisperse PSfilms at various scanning rates and temperatures revealed that the time-temperature superposition was applicable to thesurface mechanical relaxation behavior and also that the surface glass transition temperature, T_g~σ, was depressed incomparison with the bulk one even though the magnitude of M_n was fairly high at 1.40×10~5. The surface molecular motionof monodisperse PS with various chain end groups was investigated on the basis of temperature-dependent scanningviscoelasticity microscopy (TDSVM). The T_g~σs for the PS films with M_n of 4.9×10~6 to 1.45×10~6 measured by TDSVMwere smaller than those for the bulk one, with corresponding M_ns, and the T_g~σs for M_ns smaller than ca. 4.0×10~4 were lowerthan room temperature (293 K). The active thermal molecular motion at the polymeric solid surface can be interpreted interms of an excess free volume near the surface region induced by the surface localization of chain end groups. In the case ofM_n=ca. 5.0×10~4, the T_g~σs for the α, ω-diamino-terminated PS (α,ω-PS(NH_2)_2) and α, ω-dicarboxy-terminated PS (α, ω-PS(COOH)_2) films were higher than that of the PS film. The change of T_g~σ for the PS film with various chain end groups canbe explained in terms of the depth distribution of chain end groups at the surface region depending on the relativehydrophobicity.     

Orientation and relaxation study of polystyrene: Polystyrene/poly(phenylene oxide) blends

Polarization modulation infrared linear dichroism has been used to study the molecular orientation and relaxation of polystyrene/poly(2,6‐dimethyl 1,4‐phenylene oxide) (PS/PPO) miscible blends, containing up to 20% PPO, during and after a rapid uniaxial deformation above T_g. In general, it is found that both the PS and PPO chain orientation functions increase with stretching rate and PPO content, and decrease with temperature. For all blends investigated, between T_g + 5 and T_g + 13 °C, the relaxation occurs at the same rate for PS and PPO and, therefore, the relaxation times calculated are similar indicating, under those conditions, a strong relaxation coupling between the two polymers at both short and long times. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 1405–1415, 2000     

Effect of nanoscale confinement on the glass transition temperature of free-standing polymer films: Novel,self-referencing fluorescence method

The effect of nanoscale confinement on the glass transition temperature, T_g, of freely standing polystyrene (PS) films was determined using the temperature dependence of a fluorescence intensity ratio associated with pyrene dye labeled to the polymer. The ratio of the intensity of the third fluorescence peak to that of the first fluorescence peak in 1-pyrenylmethyl methacrylate-labeled PS (MApyrene-labeled PS) decreased with decreasing temperature, and the intersection of the linear temperature dependences in the rubbery and glassy states yielded the measurement of T_g. The sensitivity of this method to T_g was also shown in bulk, supported PS and poly(isobutyl methacrylate) films. With free-standing PS films, a strong effect of confinement on T_g was evident at thicknesses less than 80–90 nm. For MApyrene-labeled PS with M_n = 701 kg mol⁻¹, a 41-nm-thick film exhibited a 47 K reduction in T_g relative to bulk PS. A strong molecular weight dependence of the T_g-confinement effect was also observed, with a 65-nm-thick free-standing film exhibiting a reduction in T_g relative to bulk PS of 19 K with M_n = 701 kg mol⁻¹ and 31 K with M_n = 1460 kg mol⁻¹. The data are in reasonable agreement with results of Forrest, Dalnoki-Veress, and Dutcher who performed the seminal studies on T_g-confinement effects in free-standing PS films. The utility of self-referencing fluorescence for novel studies of confinement effects in free-standing films is discussed. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 2754–2764, 2008     

The physical and NMR characterizations of allyl‐ and crotylcelluloses

Tri‐O‐allylcellulose (degree of polymerization, DP ∼112) was prepared in ∼91% yield, and tri‐O‐crotylcellulose (DP ∼138) was prepared in ∼56% yield from microcrystalline cellulose (DP ∼172, and polydispersity index, PDI ∼1.95) using modified literature methods. Number‐average molecular weight (M_n = 31,600), weight‐average molecular weight (M_w = 191,800), and PDI = 6.07 data suggested that tri‐O‐allylcellulose may be crosslinking in air to generate branched chains. The polymer was stabilized with 100 ppm butylated hydroxy toluene (BHT). The material without BHT experienced glass transition (T_g, differential‐scanning calorimetry, DSC) between −2 and +3 °C, crosslinked beyond 100 °C, and degraded at 298.6 °C (by thermogravimetric analysis, TGA). M_n (45,100), M_w (118,200), PDI (2.62), and thermal data (T_g − 5 to +3 °C, melting point 185.8 °C, recrystallization 168.9 °C, and degradation 343.6 °C) on tri‐O‐crotylcellulose suggested that the polymer was formed with about the same polydispersity as the starting material and is heat stable. While allylcellulose generated continuous flexible yellow films by solution casting, crotylcellulose precipitated from solution as brittle white flakes. Dynamic mechanical analysis (DMA) data on allylcellulose films (T_g − 29.1 °C, Young's modulus 5.81 × 10⁸ Pa) suggest that the material is tough and flexible at room temperature. All ¹H and ¹³C resonances in the NMR spectra were identified and assigned using the following methods: Double‐quantum filter correlation spectroscopy (DQF COSY) was used to assign the network of seven protons in the anhydroglucose portion of the repeat unit. The proton assignments were verified and confirmed by total correlation spectroscopy (TOCSY). A combination of heteronuclear single‐quantum coherence (HSQC) and ¹³C spectroscopies were used to identify all bonded carbon–hydrogen pairs in the anhydroglucose portion of the repeat unit, and assign the carbon nuclei chemical shift values. Heteronuclear multiple bond correlation (HMBC) spectroscopy was used to connect the resonances of methines and methylenes at positions 2, 3, and 6 to the methylene resonances of the allyl ethers. TOCSY was used again to identify the fifteen ¹H resonances in the three pendant allyl groups. Finally, a combination of HSQC, HMBC, and ¹³C spectroscopies were used to identify each carbon in the allyl pendants at 2, 3, and 6. Because of line broadening and signal overlap, we were unable to identify the conformational arrangement about the C5 and C6 bond in tri‐O‐allyl‐ and tri‐O‐crotylcelluloses. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1889–1902, 2000     

Surface mechanical properties of low‐molecular‐weight polystyrene below its glass‐transition temperatures

Lap shear and friction force measurements were carried out on a series of monodisperse polystyrene (PS) films below the corresponding glass‐transition temperatures. It showed that adhesion between the PS/PS interface was possible at the temperature below the bulk T_g, and the lower the molecular weight of PS, the lower the temperature at which the interfacial strength was detectable. The examination of a series of molecular weights indicated both the surface molecular motion and the magnitude of the interfacial strength were dependent on molecular weight and its distribution. And a steep increase of the friction force with increasing the test temperature was observed around 0 ∼ 30 °C. The contact angle of water versus molecular weight measurements also showed a transition at room temperature. The behavior observed in this study was supposed to be due to the increased molecular mobility, and was in good agreement with the measured surface transition temperatures by DSC. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 654–658, 2000     

Glass transition of polymer/single-walled carbon nanotube composite films

The glass-transition temperatures (T_g's) of nanocomposites of polystyrene (PS) and single-walled carbon nanotubes were measured in the bulk and in thin films with differential scanning calorimetry and spectroscopic ellipsometry, respectively. The bulk T_g of the nanocomposites increased by approximately 3 °C and became much broader than that of PS. For the nanocomposite films thinner than 45 nm, T_g decreased with decreasing film thickness [i.e., ΔT_g(nano) < 0]. This phenomenon also occurred in thin PS films, the magnitude of the depression in PS [ΔT_g(PS)] being somewhat larger. The film thickness dependence and the differences in the magnitude of ΔT_g in the two systems were examined in light of current theory, and a quantitative comparison was made. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 3339–3345, 2003     

Impact of chain architecture (branching) on the thermal and mechanical behavior of polystyrene thin films

The modulus and glass transition temperature (T_g) of ultrathin films of polystyrene (PS) with different branching architectures are examined via surface wrinkling and the discontinuity in the thermal expansion as determined from spectroscopic ellipsometry, respectively. Branching of the PS is systematically varied using multifunctional monomers to create comb, centipede, and star architectures with similar molecular masses. The bulk‐like (thick film) T_g for these polymers is 103 ± 2 °C and independent of branching and all films thinner than 40 nm exhibit reductions in T_g. There are subtle differences between the architectures with reductions in T_g for linear (25 °C), centipede (40 °C), comb (9 °C), and 4 armed star (9 °C) PS for ≈ 5 nm films. Interestingly, the room temperature modulus of the thick films is dependent upon the chain architecture with the star and comb polymers being the most compliant (≈2 GPa) whereas the centipede PS is most rigid (≈4 GPa). The comb PS exhibits no thickness dependence in moduli, whereas all other PS architectures examined show a decrease in modulus as the film thickness is decreased below ～40 nm. We hypothesize that the chain conformation leads to the apparent susceptibility of the polymer to reductions in moduli in thin films. These results provide insight into potential origins for thickness dependent properties of polymer thin films. © 2011 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2012     

Analysis of polystyrene surface properties on thin film bonding under carbon dioxide pressure using nanoparticle embedding technique

A gold nanoparticle embedding technique is used to determine how vacuum and pressured carbon dioxide (CO₂) affect polystyrene (PS) thin film properties. The pressured CO₂ greatly increased the gold nanoparticle embedding depth, possibly due to a low cohesive energy density near the film surface. For the monodisperse PS used in this study (M_n = 214,000), two spin‐coated thin films with intimate contact can be bonded below the bulk glass transition temperature (T_g) under CO₂ pressure when the embedded depth is larger than half of the gyration radius of PS molecules. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 1535–1542, 2009     

Polyurethane elastomers based on amphiphilic poly(caprolactone)‐b‐poly(butadiene)‐b‐poly(caprolactone) triblockcopolyols

Hydroxyl‐terminated poly(butadiene) (HTPB; M_n = 2100 g mol⁻¹) was capped with 30 and 60 wt % of ɛ‐caprolactone to reach amphiphilic triblock copolymers in form of capped poly(butadiene) CPB. The former (CPB30; M_n = 3300 g/mol) is amorphous with a glass temperature of −56 °C. CPB60 (M_n = 4000 g mol⁻¹) is semi‐crystalline with a melting point of 50 °C and a glass transition at −47 °C. The CPBs, HTPB and polycaprolactone diol (M_n = 2000 g mol⁻¹) were used as soft segment components in the preparation of polyurethane elastomers (PUE), using a 1/1 mixture of an MDI prepolymer and uretonimine modified MDI, and hard phase components in form of 1,3‐propane diol, 1,4‐butane diol, and 1,5‐pentane diol. CPB‐based elastomers with 1,4 butane diol (8 wt %) show hard domains as fringed aggregates with a better connection to the continuous phase than the HTPB‐based PUE. The soft segment glass transition temperature (T_g) is at −28 °C for HTPB‐based PUE and at −43 °C for those of CPB. The tensile strength of the CPB30&60‐based PUE is found between 20 and 30 MPa at an elongation at break of 400% and 550%, respectively. © 2018 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2018 , 56, 1162–1172     

Effects of POSS nanoparticles on glass transition temperatures of ultrathin poly(t‐butyl acrylate) films and bulk blends

As a model system, thin films of trisilanolphenyl‐POSS (TPP) and two different number average molar mass (5 and 23 kg mol^?1) poly(t‐butyl acrylate) (PtBA) were prepared as blends by Langmuir–Blodgett film deposition. Films were characterized by ellipsometry. For comparison, bulk blends are prepared by solution casting and the samples are characterized via differential scanning calorimetry. The increase in T_g as a function of TPP content for bulk high and low molar mass samples are in the order of ～10 °C. Whereas bulk T_g shows comparable increases for both molar masses (～10 °C), the increase in surface T_g for higher molar mass PtBA is greater than for low molar mass (～22 °C vs. ～10 °C). Nonetheless, the total enhancement of T_g is complete by the time 20 wt % TPP is added without further benefit at higher nanofiller loads. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 175–182     

Polymer diffusion in latex films at ambient temperature

Polymer diffusion across interfaces at room temperature (21°C) was analyzed by direct nonradiative energy transfer (DET) in labeled latex films. Two modellatex polymers were examined: poly(butyl methacrylate) [PBMA, M_w = 3.5 × 10⁴, T_g (dry) = 21°C] and a copolymer of 2-ethylhexyl methacrylate with 10 wt % (acetoacetoxy)-ethyl methacrylate [P(EHMA-co-AAEM), M_w = 4.8 × 10⁴, T_g (dry) = −7°C]. Little energy transfer due to polymer diffusion was detected for the P(EHMA-co-AAEM) latex samples in the dispersed state or dried to solids content below ca. 90%, but above 90% solids, diffusion occurs among particles. For PBMA, diffusion occurs only after the film is dried (>97% solids) and aged. In the dry PBMA films, it requires 4–5 days at 21°C to reach a significant extent of mixing (f_m = 0.3–0.4). This corresponds to an estimated penetration depth d_app of 30–40 nm and a mean apparent diffusion coefficient (D_app) of 5 × 10⁻⁴ nm²/s. The corresponding D_app value for the dry P(EHMA-co-AAEM) sample is 5 × 10⁻² nm²/s, and it takes about 25–40 min for this polymer to reach f_m of 0.3–0.4 with d_app of 20–30 nm. © 1998 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 36: 1129–1139, 1998     

Rubbing‐induced molecular alignment and its relaxation in polystyrene thin films

Rubbing‐induced molecular alignment and its relaxation in polystyrene (PS) thin films are studied with optical birefringence. A novel relaxation of the alignment is observed that is distinctly different from the known relaxation processes of PS. First, it is not the Kohlrausch–Williams–Watts type but instead is characterized by two single exponentials plus a temperature‐dependent constant. At temperatures several degrees or more below the glass‐transition temperature (T_g), the relaxation time falls between that of the α and β relaxations. Second, the decay time constants are the same within 40% for PS with weight‐average molecular weights (M_w's) of 13,700–550,000 Da at temperatures well below the sample T_g's, indicating that the molecular relaxations involved are mostly local within the entanglement distance. Nonetheless, the temperature at which the rubbing‐induced molecular alignment disappears (T₀) exhibits a strong M_w dependence and closely approximates the T_g of the sample. Furthermore, T₀ depends notably on the thickness of the polymer in much the same way as previously found for the T_g of supported PS films. This suggests that the α process becomes dominant near T_g. Preliminary spectroscopic studies in the mid‐infrared range show a significant degree of bending of the phenyl ring toward the sample surface, with the C? C bond connecting the phenyl ring and the main chain tends to lie along the rubbing direction, which indicates that the relaxation is connected with the reorientation of this C? C bond. We exclude the observed relaxation, as predominantly a near‐surface one, because detailed studies on the effects of rubbing conditions on the degree of molecular alignment indicate that the alignment is not local to the polymer–air surface. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2906–2914, 2001     

Novel,biodegradable, functional poly(ester‐carbonate)s by copolymerization of trans‐4‐hydroxy‐L‐proline with cyclic carbonate bearing a pendent carboxylic group

Water‐soluble poly(ester‐carbonate) having pendent amino and carboxylic groups on the main‐chain carbon is reported for the first time. This article describes the melt ring‐opening/condensation reaction of trans‐4‐hydroxy‐N‐benzyloxycarbonyl‐L ‐proline (N‐CBz‐Hpr) with 5‐methyl‐5‐benzyloxycarbonyl‐1,3‐dioxan‐2‐one (MBC) at a wide range of molar fractions. The influence of reaction conditions such as catalyst concentration, polymerization time, and temperature on the number average molecular weight (M_n) and molecular weight distribution (M_w/M_n) of the copolymers was investigated. The polymerizations were carried out in bulk at 110 °C with 3 wt % stannous octoate as a catalyst for 16 h. The poly(ester‐carbonate)s obtained were characterized by Fourier transform infrared spectroscopy, ¹H NMR, differential scanning calorimetry, and gel permeation chromatography. The copolymers synthesized exhibited moderate molecular weights (M_n = 6000–14,700 g mol^?1) with reasonable molecular weight distributions (M_w/M_n = 1.11–2.23). The values of the glass‐transition temperature (T_g) of the copolymers depended on the molar fractions of cyclic carbonate. When the MBC content decreased from 76 to 12 mol %, the T_g increased from 16 to 48 °C. The relationship between the poly(N‐CBz‐Hpr‐co‐MBC) T_g and the compositions was in approximation with the Fox equation. In vitro degradation of these poly(N‐CBz‐Hpr‐co‐MBC)s was evaluated from weight‐loss measurements and the change of M_n and M_w/M_n. Debenzylation of 3 by catalytic hydrogenation led to the corresponding linear poly(ester‐carbonate), 4 , with pendent amino and carboxylic groups. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2303–2312, 2004     

Eight-arm star polystyrene in methylcyclohexane: Cloud-point curves,critical lines,and coexisting densities and viscosities

We measured the cloud-point curves of eight-arm star polystyrene (sPS) in methylcyclohexane (MCH) for polymer samples of three total molecular masses [weight-average molecular weight (M_w) × 10⁻³ = 77, 215, or 268]. We found a downward shift of 5–15 K in the critical temperature (T_c) of the star polymer solutions with respect to linear polystyrene (PS) solutions of the same M_w. The shift in T_c became smaller as M_w increased. The critical volume fraction for eight-arm sPS in MCH was equal within experimental uncertainty (10–40%) to that of linear PS in MCH. For sPS of M_w = 77,000 in MCH, we studied the mass density (ρ) as a function of temperature (T). As for linear polymers in solution, the difference in ρ between coexisting phases (Δρ) could be described over t = (T_c − T)/T_c for 1.1 × 10⁻⁴ < t < 4.7 × 10⁻³ with the Ising value of the exponent β in the expression Δρ = B t^β. Both ρ(T) above T_c and the average value of ρ below T_c were linear functions of temperature; no singular corrections were observed. The measurements of the shear viscosity (η) near T_c for sPS (M_w = 74,000) in MCH indicated a strong critical anomaly in η, but the data were not precise enough for a quantitative analysis. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 129–145, 2004     

Effect of end group chemistry on surface molecular motion of monodisperse polystyrene films

The surface molecular motion of monodisperse polystyrene (PS) with various chain end groups was investigated on the basis of temperature‐dependent scanning viscoelasticity microscope (TDSVM). The surface glass transition temperatures, T_g^ss for the proton‐terminated PS (PS‐H) films with number‐average molecular weight, M_n of 4.9k–1,450k measured by TDSVM measurement were smaller than those for the bulk one, with corresponding M_ns, and the T_g^ss for M_n smaller than ca. 50k were lower than room temperature (293 K). In the case of M_n = ca. 50k, the T_g^ss for the α,ω‐diamino‐terminated PS (α,ω‐PS(NH₂)₂) and α,ω‐dicarboxy‐terminated PS (α,ω‐PS(COOH)₂) films were higher than that of the PS‐H film. On the other hand, the T_g^s for the α,ω‐perfluoroalkylsilyl‐terminated PS (α,ω‐PS(SiC₂C^F₆)₂) film with the same M_n was much lower than those for the PS films with all other chain ends. The change of T_g^s for the PS film with various chain end groups can be explained in terms of the depth distribution of chain end groups at the surface region.     

Sub‐glass‐transition temperature interface formation between an immiscible glass rubber pair

We used neutron reflectivity to measure the interfacial width in the immiscible system polystyrene/poly(n‐butyl methacrylate) (PS/PnBMA). Measurements were made on the same samples at temperatures ranging from below the glass‐transition temperature (T_g) of PS to slightly above. We observed significant broadening of the interface at temperatures below the T_g of PS, indicating chain mobility below the bulk T_g value. The interfacial width exhibited a plateau at a value of 20 Å in the temperature range of 365 K < T < 377 K. A control experiment involving hydrogenated and deuterated PS films (hPS/dPS) showed no such broadening over the same temperature region. The results are consistent with a reduction of the T_g of PS in the interfacial region of ～20 K. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2664–2670, 2001     

Synthesis of thermotropic LCPs using p‐methoxycarbonyloxy aromatic acids

4‐Methoxycarbonyloxybenzoic acid (MCOBA) and 6‐methoxycarbonyloxy‐2‐naphthoic acid (MCONA) were synthesized as new monomers to replace 4‐acetoxybenzoic acid (ABA) and 6‐acetoxy‐2‐naphthoic acid (ANA) in the synthesis of liquid crystal polymers. MCOBA and MCONA (73 : 27, mol : mol) were reacted at temperatures ranging from 220 to 325°C in bulk. The copolymer (M_w = 14,200) has a T_g (90°C) and a T_m (249°C). The MCOBA/MCONA copolymer is lighter in color than the ABA/ANA copolymer. During the copolymerization, six by‐products were collected, isolated, and analyzed, and their formation was investigated. The copolymerization rate was studied by the measurement of evolved carbon dioxide. The polymerization of MCOBA and MCONA is cleaner and faster than the polymerization of ABA and ANA. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1703–1707, 1999