Interval kinetic gravimetric sorption of acetone in random copolymers of poly(ethylene terephthalate) and poly(ethylene 2,6-naphthalate)

Interval sorption kinetics of acetone in solvent cast films of random poly(ethylene terephthalate)-co-(ethylene 2,6-naphthalate) (PET-co-PEN) are reported at 35°C and at acetone pressures ranging from 0 to 7.3 cm Hg. Polymer composition is varied systematically from 0% to 50% poly(ethylene 2,6-naphthalate). Equilibrium sorption is well described by the dual-mode sorption model. Interval sorption kinetics are described using a two-stage model that incorporates both Fickian diffusion and protracted polymer structural relaxation. The incorporation of low levels of PEN into PET significantly reduces the excess free volume associated with the glassy state and, for these interval acetone sorption experiments in ∼ 5 μm-thick films, decreases the fraction of acetone uptake controlled by penetrant-induced polymer structural relaxation. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 2973–2984, 1999     

Miscibility of poly(ethylene terephthalate)/poly(ethylene 2,6-naphthalate) blends by transesterification

The effects of transesterification on the miscibility of poly(ethylene terephthalate)/poly(ethylene 2,6-naphthalate) were studied. Blends were obtained by solution precipitation at room temperature to avoid transesterification during blend preparation. The physical blends and transesterified products were analyzed by wide-angle x-ray scattering, differential scanning calorimetry, and nuclear magnetic resonance spectroscopy. It was found that the physical blends are immiscible and when the extent of transesterification reaches 50% of the completely randomized state, independent of blend composition, the blends are not crystallizable and show a single glass transition temperature between those of starting polymers. The interchange reactions were significantly influenced by annealing temperature and time but negligibly by blend composition. © 1996 John Wiley & Sons, Inc.     

Water sorption/desorption kinetics in poly(ethylene naphthalene-2,6-dicarboxylate) and poly(ethylene terephthalate)

Water sorption/desorption experiments were carried out on films (～ 220 μm thick) of amorphous poly(ethylene naphthalene-2,6-dicarboxylate) (PEN) stored in ambient conditions for different periods of time (0.5-4 years) and of poly(ethylene terephthalate) (PET) with different degrees of crystalinity levels (0-29%) by means of FTIR spectroscopy. Water sorption/desorption kinetics follows Fick's law for all samples investigated. Water sorption isotherms, obtained from gravimetric methods, indicate a larger sorption capacity in the case of PEN materials. The apparent diffusion coefficients (D) are larger in the case of PET samples. The observed D values decrease with storage time (physical aging) of PEN samples and with the crystallinity of PET samples. © 1995 John Wiley & Sons, Inc.     

Non-isothermal crystallization kinetics of poly(trimethylene terephthalate)/poly(ethylene 2,6-naphthalate) blends

The glass-transition temperature and non-isothermal crystallization of poly(trimethylene terephthalate)/poly(ethylene 2,6-naphthalate) (PTT/PEN) blends were investigated by using differential scanning calorimeter (DSC). The results suggested that the binary blends showed different crystallization and melting behaviors due to their different component of PTT and PEN. All of the samples exhibited a single glass-transition temperature, indicating that the component PTT and PEN were miscible in amorphous phase. The value of T_g predicted well by Gordon-Taylor equation decreased gradually with increasing of PTT content. The commonly used Avrami equation modified by Jeziorny, Ozawa theory and the method developed by Mo were used, respectively, to fit the primary stage of non-isothermal crystallization. The kinetic parameters suggested that the PTT content improved the crystallization of PEN in the binary blend. The crystallization growth dimension, crystallization rate and the degree of crystallinity of the blends were increased with the increasing content of PTT. The effective activation energy calculated by the advanced iso-conversional method developed by Vyazovkin also concluded that the value of E_a depended not only on the system but also on temperature, that is, the binary blend with more PTT component had higher crystallization ability and the crystallization ability is increased with increasing temperature. The kinetic parameters U^* and K_g were also determined, respectively, by the Hoffman-Lauritzen theory.     

Poly(ethylene terephthalate) copolymers containing nitroterephthalic units. I. Synthesis and characterization

The synthesis, microstructure, and thermal behavior of a series of poly(ethylene terephthalate) (PET) copolymers containing nitroterephthalic units are described. These novel copolyesters were synthesized by transesterification followed by melt copolycondensation of dimethyl terephthalate and dimethyl nitroterephthalate mixtures with ethylene glycol. The molar ratio of the two comonomers in the feed varied from 95/5 to 25/75. Furthermore, PET and poly(ethylene nitroterephthalate) homopolymers were synthesized with the same method and comparatively studied. Copolyester compositions were practically the same as in the feed, and weight‐average molecular weights ranged from 10,000 to 60,000. The two monomeric units were randomly distributed along the polymer chain, and the experimentally determined average sequence lengths were in accordance with ideal copolycondensation statistics. Melting temperatures and enthalpies of the copolyesters decreased with increasing content in nitroterephthalic units, and they all showed a single glass‐transition temperature superior to that of PET. They appeared to be stable up to 300 °C, and thermal degradation occurred in two well‐differentiated steps. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 3761–3770, 2000     

Segmented block copolymers of poly(ethylene glycol) and poly(ethylene terephthalate)

A new series of segmented copolymers were synthesized from poly(ethylene terephthalate) (PET) oligomers and poly(ethylene glycol) (PEG) by a two‐step solution polymerization reaction. PET oligomers were obtained by glycolysis depolymerization. Structural features were defined by infrared and nuclear magnetic resonance (NMR) spectroscopy. The copolymer composition was calculated via ¹H NMR spectroscopy. The content of soft PEG segments was higher than that of hard PET segments. A single glass‐transition temperature was detected for all the synthesized segmented copolymers. This observation was found to be independent of the initial PET‐to‐PEG molar ratio. The molar masses of the copolymers were determined by gel permeation chromatography (GPC). © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4448–4457, 2004     

FTIR spectroscopic study on crystallization process of poly(ethylene-2,6-naphthalate)

In situ Fourier transform infrared (FTIR) measurements were carried out to elucidate conformation changes occurring during the isothermal melt crystallization of poly(ethylene-2,6-naphthalate) (PEN). Based on the band assignments for the components of the amorphous, α-crystal form, and β-crystal form of PEN in film samples, the in situ data was analyzed in terms of the amorphous- and crystal-trans conformations. It was observed at a higher isothermal crystallization temperature that the formation of amorphous-trans conformations precedes the growth of crystals. © 1997 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 35: 2741–2747, 1997     

Reactive blending of poly(ethylene 2,6-naphthalate) and Vectra A

In situ composites based on poly(ethylene 2,6-naphthalate) (PEN) and a thermotropic liquid crystal polymer (Vectra A950) were prepared by melt blending under different processing conditions. Thermal behaviour, mechanical and physical properties and morphology of the blends were investigated. The DSC analysis indicates that, as expected, Vectra enhances the crystallization process of PEN. Moreover, mechanical and thermal tests evidence the significant role of 20 wt% Vectra on increasing the material performances; tensile properties, coupled with SEM, show that strength and modulus of PEN are significantly improved when Vectra domains are long and continuous fibrils. The overall results can be attributed to the compatibilisation of the system induced by the mixing conditions that affect the extent of transreactions occurring in the melt. To deepen this aspect, the soluble and insoluble fractions in a PEN solvent were isolated and thoroughly characterized: both the fractions contain PEN/Vectra copolymers. The results underline the potentiality of the PEN/Vectra system for different high-performance applications requiring superior strength and modulus, heat stability or barrier properties.     

Acetone transport in poly(ethylene terephthalate) and related phenomena

The acetone transport in poly(ethylene terephthalate) (PET) and related phenomena was investigated. Based on Harmon's model for Case I, Case II, and the anomalous transport, we analyzed the data of mass uptake. The diffusivity for Case I and the velocity for Case II satisfied the Arrhenius plot. It was found that the solvent moves from outer surfaces to the center according to Case I kinetics, and there is movement in the opposite direction according to Case II kinetics during the mass uptake. This result indicated that pure Case II behavior did not appear in the PET–acetone system. The saturated amount of acetone in PET satisfied the van't Hoff plot. X-ray diffraction pattern and DSC curve showed solvent-induced crystallites and thermal crystallites. The results of density measurement explained the difference of the sorption kinetics between the acetone-treated PET crystallites and thermally treated PET. © 1998 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 36 : 163–169, 1998     

Synthesis and characterization of poly(ethylene glycol) methyl ether endcapped poly(ethylene terephthalate)

Linear and branched poly(ethylene terephthalate) (PET) copolymers with polyethylene glycol) (PEG) methyl ether (700 or 2000 g/mol) end groups were synthesized using conventional melt polymerization. DSC analysis demonstrated that low levels of PEG end groups accelerated PET crystallization. The incorporated PEG end groups also decreased the crystallization temperature of PET dramatically, and copolymers with a high content of PEG (>17.6 wt%) were able to crystallize at room temperature. Rheological analysis demonstrated that the presence of PEG end groups effectively decreased the melt viscosities and facilitated melt processing. XPS and ATR-FTIR revealed that the PEG end groups tended to aggregate on the surface, and the surface of compression molded films containing 34.0 wt% PEG were PEG rich (85 wt% PEG). PEG end-capped PET (34.0 wt% PEG) and PET films were immersed into a fibrinogen solution (0.7 mg/mL BSA) for 72 h to investigate the propensity for protein adhesion. XPS demonstrated that the concentration of nitrogen (1.05%) on the surface of PEG endcapped PET film was statistically lower than PET (7.67%). SEM analysis was consistent with XPS results, and revealed the presence of adsorbed protein on the surface of PET films.     

Transesterification kinetics of poly(ethylene terephthalate) and poly(ethylene 2,6‐naphthalate) blends with the addition of 2,2′‐bis(1,3‐oxazoline)

The kinetics of the transesterification reaction between poly(ethylene terephthalate) (PET) and poly(ethylene 2,6‐naphthalate) (PEN) with and without the addition of a chain extender were studied with ¹H NMR. Different kinetic approaches were considered, and a second‐order, reversible reaction was accepted for the PET/PEN reactive blend system. The addition of 2,2′‐bis(1,3‐oxazoline) (BOZ) promoted the transesterification reaction between PET and PEN in the molten state. The activation energy of the transesterification reaction for the PET/PEN reactive blend with BOZ (94.0 kJ/mol) was lower than that without BOZ (168.9KJ/mol). The rate constant k took an almost constant value for blend samples with different compositions mixed at 275 °C. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2607–2614, 2001     

Poly(ethylene terephthalate) copolymers containing 5‐nitroisophthalic units. I. Synthesis and characterization

Poly(ethylene terephthalate‐co‐5‐nitroisophthalate) copolymers, abbreviated as PETNI, were synthesized via a two‐step melt copolycondensation of bis(2‐hydroxyethyl) terephthalate and bis(2‐hydroxyethyl) 5‐nitroisophthalate mixtures with molar ratios of these two comonomers varying from 95/5 to 50/50. Polymerization reactions were carried out at temperatures between 200 and 270 °C in the presence of tetrabutyl titanate as a catalyst. The copolyesters were characterized by solution viscosity, GPC, FTIR, and NMR spectroscopy. They were found to be random copolymers and to have a comonomer composition in accordance with that used in the corresponding feed. The copolyesters became less crystalline and showed a steady decay in the melting temperature as the content in 5‐nitroisophthalic units increased. They all showed glass‐transition temperatures superior to that of PET with the maximum value at 85 °C being observed for the 50/50 composition. PETNI copolyesters appeared stable up to 300 °C and thermal degradation was found to occur in two well‐differentiated steps. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1934–1942, 2000     

Thermal,crystallization, mechanical,and rheological characteristics of poly(trimethylene terephthalate)/poly(ethylene terephthalate) blends

Blends of poly(trimethylene terephthalate) (PTT) and poly(ethylene terephthalate) in the amorphous state were miscible in all of the blend compositions studied, as evidenced by a single, composition‐dependent glass‐transition temperature observed for each blend composition. The variation in the glass‐transition temperature with the blend composition was well predicted by the Gordon–Taylor equation, with the fitting parameter being 0.91. The cold‐crystallization (peak) temperature decreased with an increasing PTT content, whereas the melt‐crystallization (peak) temperature decreased with an increasing amount of the minor component. The subsequent melting behavior after both cold and melt crystallizations exhibited melting point depression behavior in which the observed melting temperatures decreased with an increasing amount of the minor component of the blends. During crystallization, the pure components crystallized simultaneously just to form their own crystals. The blend having 50 wt % of PTT showed the lowest apparent degree of crystallinity and the lowest tensile‐strength values. The steady shear viscosity values for the pure components and the blends decreased slightly with an increasing shear rate (within the shear rate range of 0.25–25 s^?1); those of the blends were lower than those of the pure components. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 676–686, 2004     

Synthesis,morphology, and nonisothermal crystallization behavior of poly(trimethylene terephthalate)/poly(propylene glycol) segmented random copolymers

Poly(trimethylene terephthalate)/poly(propylene glycol) (PTT/PPG) segmented random copolymers were synthesized by melt copolycondensation. The weight fraction of PPG blocks was ranged from 12.1 to 33.4 wt%, which was confirmed by ¹H NMR spectroscopy. The result of wide‐angle X‐ray diffractometer indicated that all copolymers had the same crystal structure of PTT homopolymer at room temperature. At a determined crystallization temperature, ring‐banded spherulites could be observed in all copolymers samples, and the band spacing increased with the increase of PPG content. Morphologies of copolymers after nonisothermal crystallization process were strongly depended on the cooling rate. Well‐defined ring‐banded spherulites can be observed only at moderate cooling (20°C/min), while it was really hard to be observed at too low (2.5°C/min) or too high (by air‐quenching) cooling rate. Moreover, the size of spherulites decreased with the increase of cooling rate. Finally, different nonisothermal crystallization kinetics were adopt to analyze this copolymer system, and only the Mo method was suitable to describe this copolymer system. Copyright © 2016 John Wiley & Sons, Ltd.     

Synthesis and hydrolytic degradation of poly(ethylene succinate) and poly(ethylene terephthalate) copolymers

The conditions of synthesis of statistical poly(ethylene succinate-co-terephthalate) copolymers (2GTS) and high molecular weight poly(ethylene succinate) (PES) with good hydrolytic and optical parameters, designed for the production of biodegradable products and resins, are presented in this article. Copolymers were prepared by melt polycondensation of bis-(β-hydroxyethylene terephthalate) (BHET) and succinic acid (SA) with excess of ethylene glycol (2G) in the presence of a novel titanium/silicate catalyst (C-94) and catalytic grade of germanium dioxide (GeO₂) as cocatalyst. The chemical structure and physical properties of those materials were characterized by ¹H NMR, FT-IR, dynamical-mechanical thermal analyses (DMTA), differential scanning calorimetry (DSC), solution viscosity and spectroscopic methods. The hydrolytic degradation was performed in a water solution with variable pH, also in garden soil and in compost. The highest hydrolytic degradation rate was observed for pH 4 and for compost. Better hydrolytic degradation values in compost medium were observed for copolyester prepared in the presence of GeO₂ as polycondensation cocatalyst. The copolyester with 40 mol% of aliphatic units was chosen for industrial syntheses which were performed in ELANA and subsequently the processing parameters and compatibility with potato starch of this polyester were checked by BIOP Biopolymer Technologies AG.     

Relaxation behavior of poly(ethylene terephthalate)/poly(ethylene naphthalene 2,6‐dicarboxylate) blends prepared by cryogenic blending

A method including cryogenic grinding, melt pressing from the molten state, and quenching was used to prepare blends of poly(ethylene terephthalate) (PET) and poly(ethylene naphthalene 2,6‐dicarboxylate) (PEN) in which the two phases were highly dispersed. The effect of melt‐pressing times on the thermal properties and relaxation behavior of PET/PEN films were characterized with differential scanning calorimetry and dielectric spectroscopy. For short melt‐pressing times, two glass‐transition, two crystallization, and two melting peaks were observed, indicating the presence of PET‐rich and PEN‐rich phases in these blends. Longer melt‐pressing times revealed a single glass transition and a single α‐relaxation process, showing that PET–PEN block copolymers were likely to be formed during the melt pressing. The experimental findings were examined in terms of the transesterification reactions between the blend components, as revealed by ¹H NMR measurements. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 2570–2578, 2002     

Synthesis and non‐isothermal crystallization kinetics of poly(ethylene terephthalate)‐co‐poly(propylene glycol) copolymers

Poly(ethylene terephthalate)‐co‐poly(propylene glycol) (PET‐co‐PPG) copolymers with PPG ratio ranging from 0 to 0.90 mol% were synthesized by the melt copolycondensation. The intrinsic viscosity, structure, non‐isothermal crystallization behavior, nucleation and spherulitic growth of the copolymers were investigated by Ubbelohde viscometer, Proton Nuclear Magnetic Resonance (¹H‐NMR), differential scanning calorimetry, and polarized optical microscopy, respectively. The non‐isothermal crystallization process of the copolymers was analyzed by Avrami, Ozawa, Mo's, Kissinger, and Dobreva methods, respectively. The results showed that the crystallizability of PET was apparently enhanced with incorporating a small amount of PPG, which first rose and then reduced with increasing amount of PPG in the copolymers at a given cooling rate. The crystallization mechanism was a three‐dimensional growth with both instantaneous and sporadic nucleation. Particularly, PET‐co‐PPG containing 0.60 mol% PPG exhibited the highest crystallizability among all the copolymers. Copyright © 2015 John Wiley & Sons, Ltd.     

Subglass-transition-temperature annealing of poly(ethylene terephthalate) studied by FTIR

Using FTIR spectroscopy we have examined conformational changes in the quenched and slowly cooled amorphous PET films during physical aging process. It was observed that the amount of trans conformers for quenched sample decreased upon sub-T_g annealing. For the slowly cooled sample that corresponds to a state closer to equilibrium, the amount of trans conformers hardly decreased, but increased gradually during sub-T_g annealing process. The conformational populations of these two samples tend to be identical with annealing time. These results demonstrate that sub-T_g annealing will lead to closer interchain packing and result in the formation of new cohesional entanglements along the chains. In situ FTIR studies on the conformational changes of these samples were also carried out during heating up of the sample through the glass transition region. The results showed that incremental changes of the amount of trans conformers in Samples Q and SC were gradual, while an abrupt change of trans conformers occurred in the sub-T_g annealed samples. These results were in agreement with the formation of the interchain cohesional entanglement due to sub-T_g annealing. © 1998 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 36: 783–788, 1998     

Synthesis and characterization of novel biodegradable copolyesters by transreaction of poly(ethylene terephthalate) with copoly(succinic anhydride/ethylene oxide)

Poly(ethylene terephthalate)/copoly(succinic anhydride/ethylene oxide) copolymers, (PET/PES copolymers) were synthesized by the transreaction between PET and PES and characterized with GPC, ¹H NMR, and DSC. Most of the copolymers obtained were random copolymers. The films cast of these copolymers were transparent. The thermal, mechanical properties, and biodegradability of the copolymers obtained were studied with respect to the composition and lengths of aliphatic and aromatic units in the copolymers. In the copolymers having high PET content, the melting points, due to the PET segment, were observed by DSC measurement, although the fusion heats of the copolymers were small. The enzymatic hydrolyzability by a lipase from Rhizopus arrhizus and biodegradability by activated sludge of the copolymers decreased with an increase in PET content. When the length of succinic acid unit in the copolymer was below 2, the hydrolyzability of the copolymers decreased considerably. The tensile strengths of the cast films prepared from the copolymers synthesized by the transreaction increased with an increase in PET content, whereas, the elongations at break decreased. Their tensile strengths were half, and the elongations were double compared to those of PET homopolymer film. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 4478–4489, 2000     

Kinetics for the catalyzed formation of poly(ethylene 2,6-naphthalate) (PEN) by various metal compounds

The catalyzed transesterification between dimethyl 2,6-naphthalate and ethylene glycol and polycondensation of bis (2-hydroxyethyl) naphthalate have been investigated in the presence of various metal compounds as catalysts. The effect of the nature and concentration of these catalysts on both reactions has been studied. The observed overall rate of the transesterification was third order; first order with respect to dimethyl 2,6-naphthalate, ethylene glycol, and the catalyst including initial concentration of catalyst, respectively. The decreasing order in catalytic activity on the transesterification was the order of Pb(II) > Zn(II) > Mn(II) > Co(II) > Ti(IV) > Sn(II) > Mg(II) > Ca(II) > Na(I) > Sb(III). And also, the decreasing order in catalytic activity on the polycondensation was found to be Ti(IV) > mixtures of Ti(IV) and Sb(III) > Sn(II) > Sb(III) > Co(II) > Zn(II) > Pb(II) > Mn(II) > Mg(II). © 1994 John Wiley & Sons, Inc.