Synthesis and hydrolytic degradation of stereoregular aromatic poly(ester amide)s derived from D‐xylose

Stereoregular poly(ester amide)s (PEAs) were prepared by the polycondensation method using naturally occurring D ‐xylose and aromatic diacids as the starting materials. The polymers were characterized by elemental analysis, GPC, IR, and ¹H‐ and ¹³C NMR spectroscopies. Thermal and X‐ray diffraction studies revealed them to be mainly amorphous. The polymers are hydrophilic and their degradation studies were carried out at 37 and 80 °C in buffered salt solution at pH 8. The degradation study was monitored by mass loss, GPC, IR, and NMR spectroscopies. The hydrolytic degradation of these PEAs occurred rapidly by hydrolysis of the ester functions to a final compound, which maintained the amide functions. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2010     

Photocrosslinkable vinylamine copolymers. I. Synthesis and photosensitivity of cinnamoylated polyvinylamine

Vinylamine copolymers prepared by the Hofmann reaction were functionalized by amidification with cinnamoyl chloride. The resulting photosensitive polymers, which are the nitrogen analogues of poly(vinylcinnamate), can be prepared with various contents of cinnamamide side groups. The polymers exhibit a marked hydrophilicity and undergo efficient crosslinking upon exposure to 250–300 nm UV light. The sensitivity S expressed in cm²·J⁻¹ was shown to be higher for a given content, τ, in cinnamamide groups expressed in mol·g⁻¹ when the residual vinyl amine units are in the ammonium form. The dependence of S upon τ was of the second order for the free base form of the photopolymers, but a higher order with S approximately proportional to τ³ for the hydrochloride form of the photosensitive polymers. © 1997 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 35 : 2513–2520, 1997     

Functionalized poly(phenylene‐alt‐bithiophenes): Synthesis,chiroptical properties,and interaction with chiral amines

New functionalized, (a)chiral poly(phenylene‐alt‐bithiophene)s were prepared and their chiroptical properties were studied. The polymers were prepared by a Stille coupling reaction and were functionalized with protected carboxylic acid and amino functions (tert‐butyl ester and BOC respectively). The polymers are present as well conjugated rigid rods in solution, which (chirally) aggregate in nonsolvents and film. In a next step, the protecting group (tert‐butyl ester in case of the carboxylic acid) was removed. Aggregation of this polymer can be induced by addition of amines; if chiral amines are used, the polymer chains chirally stack. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 4817–4829, 2008     

Synthesis and properties of fluorene‐based polyheteroarylenes for photovoltaic devices

Novel copolymers consisting of the alternating push–pull comonomers fluorene and thieno[3,4‐b]pyrazine/quinoxaline were synthesized by a palladium‐catalyzed Suzuki cross‐coupling reaction in 60–80% yields. The structure of the deeply colored copolymers was confirmed with ¹H and ¹³C NMR. All the new materials were characterized with spectroscopic and electrochemical methods. Bulk heterojunction organic solar cells based on some of the novel polymers in combination with the well‐known fullerene acceptor [6,6]‐phenyl C₆₁–butyric acid methyl ester were fabricated, and their photovoltaic parameters were measured. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6952–6961, 2006     

Tuning the optical properties of hyperbranched polymers through the modification of the end groups

Dye‐capped, hyperbranched, conjugated polymers were prepared by the modification of the peripheral bromo end groups of the hyperbranched polymer core with a palladium‐catalyzed Suzuki–Miyaura cross‐coupling reaction. The dye‐modified, hyperbranched polymers had high molecular weights and displayed good solubility in common organic solvents such as tetrahydrofuran, toluene, and chloroform. The structure of the dye‐modified, hyperbranched polymers was characterized by ¹H and ¹³C NMR and elemental analysis. The thermal properties of five kinds of hyperbranched polymers were investigated with thermogravimetric analysis and differential scanning calorimetry. The optical properties of the dye‐capped, hyperbranched polymers were investigated with ultraviolet‐absorption and fluorescence spectroscopy. The hyperbranched structure could effectively reduce the aggregation of the peripheral dyes. The emission colors of the hyperbranched polymers could be easily tuned by end‐group modification. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 111–124, 2007     

Polymerization of bisdithiafulvenes with conjugated spacers using oxidative dimerization

Novel vinylogous tetrathiafulvalene (TTF) containing polymers ( 13 and 14 ) were prepared by the oxidative dimerization polymerization of bisdithiafulvenes. The obtained polymers were soluble in common organic solvents such as CHCl₃. The structures of the polymers were confirmed by ¹H NMR and cyclic voltammetry analysis. The number‐average molecular weights of 13 and 14 were estimated from gel permeation chromatography to be 3600 and 3800, respectively. Through the introduction of phenylene or phenylene–vinylene spacers, distortion between dialkoxybenzene and vinylogous TTF units was effectively prevented according to ultraviolet–visible analysis. The polymers exhibited a strong electron‐donating property investigated by cyclic voltammetry analysis. Chemical doping by CF₃SO₃H gave doped polymers having a cationic radical and a dication of a vinylogous TTF unit. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2027–2033, 2006     

Synthesis and characterization of novel π‐conjugated polymers with phosphole ring derivatives

Novel π‐conjugated polymers ( 8 – 10 ) were prepared by the palladium‐catalyzed Sonogashira coupling reaction of three kinds of phosphole‐ring‐containing monomers with 2,5‐dihexyloxyl‐1,4‐diethynylbenzene. The obtained polymers ( 8 – 10 ) were regioregulated with the 2,5‐substituted phosphole ring in the polymer main chain and characterized with ¹H, ¹³C, and ³¹P NMR and FTIR. Polymers 8 – 10 were found to have an extended π‐conjugated system according to the results of UV–vis absorption spectra. In the fluorescence emission spectra of 8 – 10 , moderate emission peaks were observed in the visible blue‐to‐green region. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 2867–2875, 2007     

Geminal poly(silyl ester)s: Highly labile degradable polymers

Geminal silyl ester linkages were used for the backbone construction of linear polymers, which exhibit rapid cleavage in the presence of atmospheric water. A series of poly(gem-silyl ester)s with two ester groups flanking each silicon atom were synthesized, in order to probe the effects of different silyl-substituted side-chain groups upon the physical and chemical properties. The transsilylation condensation reaction of bis(trimethylsilyl) terephthalate with dichlorodiisopropylsilane, dichlorodicyclohexylsilane, dichloromethyl-n-octadecylsilane, and dichloromethyl-4-methylphenethylsilane gave the four poly(gem-silyl ester)s with two isopropyl, two cyclohexyl, one methyl plus one octadecyl, and one methyl plus one 4-methyl-phenethyl side-chain groups per silicon, respectively. The polymers were characterized by NMR (¹H, ¹³C, and ²⁹Si), infrared spectroscopy (IR), size-exclusion chromatography (SEC), differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA). Hydrolytic degradation studies of the polymers solvated in tetrahydrofuran and as bulk samples in the solid state were performed in the presence of atmospheric water as the nucleophilic cleavage agent, and the molecular weight loss was monitored by SEC. Poly(diisopropylsilyl terephthalate) (1a) and poly(dicyclohexylsilyl terephthalate) (1b) were found to be more stable towards nucleophilic degradation in comparison to poly(methyl-n-octadecylsilyl terephthalate) (1c) and poly(methyl-4-methylphenethylsilyl terephthalate) (1d), due to the presence of sterically bulky isopropyl or cyclohexyl groups attached to the silicon atoms. All of the polymers degraded into small molecules upon hydrolysis, with the exception that the degradation products of 1c and 1d self-condensed in the solid state to form the respective polysiloxanes. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 3606–3613, 1999     

Oligomerization and cyclization of 1,2-ethanedithiol (EDT), HSCH2CH2SH,by selenium dioxide and iodine

The reaction of 1,2 ethanedithiol (EDT) with selenous acid in water or alcohol leads to selenopolysulfide chains or cycles, (C₂H₄SSeSC₂H₄SS)_n, with randomly distributed  SSeS and  SS moieties. The reaction in water produces incompletely reacted material, which on recrystallization, gives an oligomer corresponding to 5 EDT units (pentamer) as confirmed by molecular mass determination, Se analysis, ¹H- and ⁷⁷Se-NMR spectroscopy. In both the pentamer and cyclic forms the incidence of neighboring  SSeS moieties is higher than that expected statistically. The mechanism for the reaction of thiols with selenous acid provides some rationalization for this observation in as much as neighboring  SSeS groups, or groups that will lead rapidly to neighboring  SSeS groups are formed in general before  SS links can be formed. The Raman spectrum of these products show typical strong SS, SeS, and CS stretching bands at 510, 370, and 730 cm⁻¹. The high frequency of ν_CS is attributed to a preferred gauche conformation at the CS bonds. For comparison, polydisulfides were also prepared from EDT and iodine in methanol. These products consist of at least seven cyclic polymers ranging from the four-membered 1,2-dithietane to higher members. Heating above 100°C in chloroform for several hours gives a solution containing the four lowest molecular mass rings, which on standing for 24 h, precipitate highly insoluble material, which is probably chain or large-ring polymer. Molecular mass determination in camphor indicates that, like yellow sulphur, chain polymers are formed at the melting point of camphor (170°C). © 1998 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 36 : 379–390, 1998     

Synthesis of hyperbranched poly(ether nitrile)s by one‐step polycondensation of an AB2 monomer

Hyperbranched poly(ether nitrile)s were prepared from a novel AB₂ type monomer, 2‐chloro‐4‐(3,5‐dihydroxyphenoxy)benzonitrile, via nucleophilic aromatic substitution. Soluble and low‐viscous hyperbranched polymers with molecular weights upto 233,600 (M_w) were isolated. According to the ¹H NMR and GPC data, the unique polymerization behavior was observed, which implies that the weight average molecular weight increased after the number average molecular weight reached plateau region. Model compounds were prepared to characterize the branching structure. Spectroscopic measurements of the model compounds and the resulting polymers, such as ¹H, DEPT ¹³C NMR, and MS, strongly suggest that the ether exchange reaction and cyclization are involved in the propagation reaction. The side reactions would affect the unique polymerization behavior. The resulting polymers showed a good solubility in organic solvents similar to other hyperbranched aromatic polymers. The hydroxy‐terminated polymer was even soluble in basic water. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 5835–5844, 2009     

Synthesis and characterization of side-chain liquid-crystalline poly(ether ester)s having p-substituted biphenyl mesogenic side groups

Several novel mesogenic spiro-orthoester monomers such as 1,6,10-trioxaspiro[4,5]decanes 4 , containing biphenyl mesogens at the C-8 positions of the five- and six-membered spirocyclic ring, through the alkylene spacers of different lengths were prepared by condensation reaction of the corresponding biphenyl mesogenic 1,3-propanediol 3 with 2,2-diethoxytetrahydrofuran, with 50–75% yields. Through cationic double ring-opening polymerization, carried out with boron trifluoride etherate as an initiator (5 mol % vs. monomer) in bulk at 150°C, spiro-orthoester monomers 4 afforded a novel class of side-chain thermotropic LC polymers with a poly(ether ester) as the main chain 8 . The liquid-crystalline properties of the spiro-orthoester monomers and the resulting polymers were examined by differential scanning calorimetry and optical polarized microscopy. Biphase separation was observed in the side-chain liquid-crystalline poly(ether ester)s upon annealing in the broad isotropic region. © 1998 John Wiley & Sons, Inc. J. Polym. Sci. A Polym. Chem. 36: 2439–2455, 1998     

Water‐soluble,biocompatible polyphosphazenes with controllable and pH‐promoted degradation behavior

The synthesis of a series of novel, water‐soluble poly(organophosphazenes) prepared via living cationic polymerization is presented. The degradation profiles of the polyphosphazenes prepared are analyzed by GPC, ³¹P NMR spectroscopy, and UV–Vis spectroscopy in aqueous media and show tunable degradation rates ranging from days to months, adjusted by subtle changes to the chemical structure of the polyphosphazene. Furthermore, it is observed that these polymers demonstrate a pH‐promoted hydrolytic degradation behavior, with a remarkably faster rate of degradation at lower pH values. These degradable, water soluble polymers with controlled molecular weights and structures could be of significant interest for use in aqueous biomedical applications, such as polymer therapeutics, in which biological clearance is a requirement and in this context cell viability tests are described which show the non‐toxic nature of the polymers as well as their degradation intermediates and products. © 2013 The Authors Journal of Polymer Science Part A: Polymer Chemistry Published by Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 287–294     

Synthesis of cationic diacetylene‐co‐carbazole‐co‐fluorene polymers and their sensitive fluorescent quenching properties with DNA

Two neutral precursor conjugated copolymers based 2,7‐diethynylfluorene and 3,6‐diethynylcarbazole units in the main chain ( PFC and PF2C ) were prepared by Hay coupling polymerization. Their cationic copolymers ( CPFC and CPF2C ) were prepared by the methylation of their diethylpropylamino groups with CH₃I. For comparison, neutral conjugated homopolymers of 2,7‐diethynylfluorene ( PF ), 3,6‐diethynylcarbazole units ( PC ) and their cationic polymers ( CPF and CPC ) were also prepared with the same method. A comparative study on the optical properties of cationic polymers CPFC and CPF2C in DMF and DMF/H₂O showed that they underwent water‐induced aggregation. The spectral behaviors of CPFC and CPF2C with calf thymus DNA showed that a distinct fluorescent quenching took place with minute addition of CT DNA (3.3 × 10^?13 M). The results showed that the polymers would be promising biosensor materials for sensitive detection of DNA. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 4168–4177, 2010     

Terpyridine‐substituted,fluorescent polymers and their chelation with zinc ion: The ligand‐to‐metal ratio and optical properties

Soluble, fluorescent, terpyridine‐substituted, conjugated polymers were prepared and characterized. The polymer chains included a defined oligo(phenylenevinylene) fragment, on which the terpyridine‐functional group was attached. The polymers were blue‐fluorescent with emission peaks at 400–427 nm in tetrahydrofuran solutions. Upon chelation with the Zn(II) cation, the emission maxima were shifted to a longer wavelength by as much as 113 to 506–526 nm. A model compound was also prepared to aid the structural characterization. The ratio of terpyridine to Zn²⁺ in the polymer complex was found to be 1:1 on the basis of spectroscopic evidence, which included mass spectrometry, ¹H NMR, and Job titration. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2338–2345, 2006     

Synthesis and properties of novel conjugated poly(silylacetylene silazane)s

A series of novel conjugated polymers, poly(silylacetylene silazane)s having different substituents, were prepared by ammonolysis of the corresponding α,ω‐dichlorosilyleneacetylene oligomers. The structures and properties of the poly(silylacetylene silazane)s were characterized by Fourier transform infrared, ¹H, ¹³C, ²⁹Si NMR, and elemental analyses, gel permeation chromatography, thermogravimetric analysis, differential scanning calorimetry, and spectrofluorophotometry. The resulting polymers had good thermal properties and were moderately fluorescent. Their thermal stability was improved, and obvious red shift was observed when a phenyl substituent was attached on a silicon atom of polymers in the emission spectra. These polymers have the potential to be used as light‐emitting materials with good thermal stability. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2897–2903, 2004     

Synthesis of polymers containing 1,2,4‐oxadiazole as an electron‐acceptor moiety in their main chain and their solar cell applications

To explore the aptitude of 1,2,4‐oxadiazole‐based electron‐acceptor unit in polymer solar cell applications, we prepared four new polymers (P1–P4) containing 1,2,4‐oxadiazole moiety in their main chain and applied them to solar cell applications. Thermal, optical, and electrochemical properties of the polymers were studied using thermogravimetric, absorption, and cyclic voltammetry analysis, respectively. All four polymers showed high thermal stability (5% degradation temperature over 335 °C), and the optical band gaps were calculated to be 2.20, 1.72, 1.37, and 1.74 eV, respectively, from the onset wavelength of the film‐state absorption band. The energy levels of the polymers were found to be suitable for bulk heterojunction (BHJ) solar cell applications. The BHJ solar cells were prepared by using the synthesized polymers as a donor and PC₇₁BM as an electron acceptor with the configuration of ITO/PEDOT:PSS/polymer:PC₇₁BM (1:3 wt %)/LiF/Al. One of the polymers was found to show the maximum power conversion efficiency of 1.33% with a Jsc of 4.95 mA/cm², a V_oc of 0.68 V, and a FF of 40%, measured using AM 1.5 G solar simulator at 100 mW/cm₂ light illumination. © 2013 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Nitroxide-mediated styrene polymerization initiated by an oxoaminium chloride

An oxoaminium chloride that is prepared by reacting 2,2,6,6-tetramethylpiperidinyl-1-oxy (TEMPO) with chlorine in carbon tetrachloride initiates radical polymerization of styrene at 120°C. In the early stages of polymerization, a monomeric adduct, 2,2,6,6-tetramethyl-1-(2-chloro-1-phenylethoxy)piperidine, is formed. Thereafter, styrene polymerization exhibiting the characteristics of living polymerization proceeds. High molecular weight polymers with relatively narrow molecular weight distributions are obtained by this polymerization. ¹H-NMR spectra of the polymers reveal that a chlorine atom and a TEMPO group are present at the α- and ω-termini, respectively. The monomeric adduct was prepared by heating the oxoaminium chloride and styrene in carbon tetrachloride at 65–70°C, and was characterized by ¹H- and ¹³C-NMR spectroscopy. It was found to be suitable as an initiator for nitroxide-mediated radical polymerization of styrene to make polymers with chlorine on the chain end. © 1998 John Wiley & Sons, Inc. J. Polym. Sci. A Polym. Chem. 36: 2555–2561, 1998     

Alkyl-substituted poly(2,5-benzophenone)s synthesized via Ni(0)-catalyzed coupling of aromatic dichlorides and their miscible blends

High molecular weight poly(2,5-benzophenone) derivatives were prepared by Ni(0)-catalyzed coupling of 4′-substituted 2,5-dichlorobenzophenones. Monomers were synthesized by the Friedel–Crafts reaction of 2,5-dichlorobenzoyl chloride and alkyl-substituted benzenes in the presence of aluminum chloride. The resulting polymers are soluble and show no evidence of crystallinity by DSC. Number average molecular weights are in the range of 9.2 × 10³–11.7 × 10³ g/mol by multiple angle laser light scattering (MALLS). Molecular weights obtained by MALLS are only slightly lower (∼90%) than those obtained by GPC (polystyrene standards). These polymers exhibit high thermal stability with glass transition temperatures ranging from 173 to 225°C and weight loss occurring above 450°C in nitrogen and 430°C in air. Additionally, the polymers were blended and the resulting polymer films appear to be miscible by DSC results. © 1998 John Wiley & Sons, Inc. J. Polym. Sci. A Polym. Chem. 36: 2611–2618, 1998     

Rigid-rod liquid crystalline polyesters based on n-alkoxyterephthalic acid and 4,4′-dihydroxybiphenyl

The synthesis and the characterization of a set of polymers obtained by polycondensation of n-alkoxyterephthalic acid (n = 1, 3, 5, 7) and 4,4′-dihydroxybiphenyl are reported. The n-alkoxy insertion promotes the processability of the material by lowering the melting temperature. All polymers show the nematic phase at about 300°C, almost independently of the length of lateral substituent. The isotropization is not observed up to 450°C, where thermal decomposition occurs. The temperature of glass transition decreases with increasing n, ranging from 170°C (n = 5) to 220°C (n = 1). © 1998 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 36: 263–267, 1998     

Effect of branched alkyl side chains on the performance of thin‐film transistors and photovoltaic cells fabricated with isoindigo‐based conjugated polymers

New isoindigo and di(thienyl)ethylene‐containing π‐extended conjugated polymers with different branched side chains were synthesized to investigate their physical properties and device performance in thin‐film transistors and photovoltaic cells. 11‐Butyltricosane (S3) and 11‐heptyltricosane (S6) groups were used as side‐chain moieties tethered to isoindigo units. The linking groups between the polymer backbone and bifurcation point in the branched side chain differ in the two polymers (i.e., PIDTE‐S3 and PIDTE‐S6 ). The polymers bearing S6 side chains showed much better charge transport behavior than those with S3 side chains. Thermally annealed PIDTE‐S6 film exhibited an outstanding hole mobility of 4.07 cm² V^?1 s^?1 under ambient conditions. Furthermore, bulk heterojunction organic photovoltaic cells made from a blend film of PIDTE‐S3 and (6,6)‐phenyl C61‐butyric acid methyl ester demonstrated promising device performance with a power conversion efficiency in the range of 4.9–5.0%. © 2015 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 2015 , 53, 1226–1234