Eu3+∶Sm3+∶Cr3+∶YAG红色单晶荧光体

报道外延生长的多激活中心掺杂的红色单晶荧光体Eu3 ∶Sm3 ∶Cr3 ∶YAG ,其直径达到54mm ,荧光色坐标为x=0 .6 137,y =0 .3738,相当于波长λ=599nm的红色荧光 ,具有较高的色饱和度。这种单晶材料具有很好的抗电子束灼伤能力 ,在入射能量达到 10 5W/m2 时无发光猝灭现象 ,是一种较理想的红色单晶荧光材料。     

Yb3+离子掺杂浓度对Yb∶YAG晶体发光及荧光寿命的影响

研究了不同掺杂浓度Yb∶YAG晶体的发光特性和荧光寿命.Yb3+在YAG晶体中的掺杂浓度分别为5at%、10at%、20at%、30at%.Yb3+离子掺杂浓度越高，Yb∶YAG晶体的吸收系数越大.采用940 nm波长的LD泵浦源和TRIA X550荧光谱仪，对这一系列掺有不同浓度Yb3+的Yb∶YAG晶体进行了荧光光谱的测定.结果表明:在1030 nm主发光波段的荧光强度以10at%Yb∶YAG的为最强.同时发现它在450 nm-680 nm波段有明显的可见发光，其强度随Yb3+掺杂浓度的增加而迅速地增强.Yb∶YAG晶体的荧光寿命存在浓度猝灭现象，对猝灭机制进行了分析研究，指出浓度猝灭的主要原因是合作发光和痕量稀土离子的上转换发光.     

YAG:Pr3+的真空紫外光谱分析及其4f5d能级的研究

用共沉淀法制备出不同掺杂浓度的钇铝石榴石(Y3Al5O12,YAG):Pr3+粉末.在不同温度下用同步辐射的真空紫外光(VUV)作为激发光源测量了其发射和激发光谱.对YAG:Pr3+被VUV激发后的发光过程进行了分析,并估算了YAG:Pr3+的声子能量、黄昆因子S及Stokes位移.当用170nm光激发样品时,可能存在自陷激子和通过自陷激子能量传递引发的3P0发射,这种跃迁途径不同于用240nm和289nm两个波长激发后的跃迁途径;对Pr3+在YAG中的4f5d能级进行了研究,从而对其4f5d组态有了一个较清晰的认识.     

白光LED用新型Ce,Pr掺杂的YAG单晶荧光材料的光谱性能研究

为了改善白光LED用荧光材料效率低、均匀性差、光衰大、寿命短及物化性能差等不足,本文采用单晶荧光材料取代荧光粉来制备白光LED,并对白光LED用新型YAG单晶荧光材料的制备和光谱性能进行了研究.采用提拉法生长了白光LED用Ce∶YAG及Pr,Ce∶YAG晶体,并通过吸收光谱,激发、发射光谱对晶体材料的光谱特性进行表征.研究表明,Ce∶YAG单晶荧光材料可以被发射波长460 nm左右的蓝光芯片有效激发,产生一个范围为480~650 nm宽峰发射.通过Pr3+,Ce3+离子共掺杂可以有效补偿Ce3+离子单掺杂YAG荧光材料发光中的红色发光成分.     

NaZnLa(PO_4)_2中Ce~(3+)和Tb~(3+)的发光

采用高温固相反应合成了NaZnLa(PO4 ) 2 中掺杂Ce3 +、Tb3+的荧光体 ,对其晶体结构、发光行为进行了研究 ,并尝试对NaZnLa(PO4 ) 2 ∶Ce ,Tb荧光体进行调制。NaZnLa(PO4 ) 2 是LaPO4 的同构物 ,为单斜晶系独居石结构 ,从XRD谱数据得到NaZnLa(PO4 ) 2 基质的晶胞参数为a =0 6 82 3nm ,b =0 70 45nm ,c =0 6 497nm ,β =10 3 9° ,V =0 30 3nm3,其晶胞参数与单斜LaPO4 的晶胞参数相似。在NaZnLa(PO4 ) 2 ∶Ce ,Tb荧光体中 ,Ce3 +对Tb3+有良好的敏化作用 ,掺杂适量的BO3 -3 、Al3 +、Dy3 +,可以增强发光亮度     

YAG:Pr3+的真空紫外光谱分析及其4f5d能级的研究

用共沉淀法制备出不同掺杂浓度的钇铝石榴石(Y₃Al₅O_{12，YAG)：Pr³⁺粉末.在不同温度下用同步辐射的真空紫外光(VUV)作为激发光 源测量了其发射和激发光谱.对YAG：Pr³⁺被VUV激发后的发光过程进行了分析， 并估算了YAG：Pr³⁺的声子能量、黄昆因子S及Stokes位移.当用170nm光激发样 品时，可能存在自陷激子和通过自陷激子能量传递引发的³P0发射 ，这种跃迁途径不同于用240nm和289nm两个波长激发后的跃迁途径；对Pr³⁺在Y AG中的4f5d能级进行了研究，从而对其4f5d组态有了一个较清晰的认识. 关键词： 3+')" href="#">YAG：Pr³⁺ 同步辐射 4f5d能级 VUV}     

Yb :YAG晶体的闪烁特性

通过不同Yb³⁺掺杂浓度(5%~30%,原子数分数)的Yb:YAG晶体的阴极射线发光谱、衰减时间、光输出及其温度依赖关系的测量,研究了Yb:YAG晶体的闪烁性能.不同Yb³⁺掺杂浓度的Yb:YAG晶体具有不同的光输出和猝灭温度,光输出随Yb³⁺掺杂浓度的增大而降低,猝灭温度则随掺杂浓度的增大而升高.室温下Yb:YAG晶体的发光衰减时间较短,均小于50ns.Yb³⁺掺杂浓度为5%的Yb:YAG晶体具有较高的光输出和较低的猝灭温度.     

Yb~(3 )离子掺杂浓度对Yb∶YAG晶体发光及荧光寿命的影响

研究了不同掺杂浓度Yb∶YAG晶体的发光特性和荧光寿命·Yb3 在YAG晶体中的掺杂浓度分别为5at%、10at%、20at%、30at%·Yb3 离子掺杂浓度越高,Yb∶YAG晶体的吸收系数越大·采用940nm波长的LD泵浦源和TRIAX550荧光谱仪,对这一系列掺有不同浓度Yb3 的Yb∶YAG晶体进行了荧光光谱的测定.结果表明:在1030nm主发光波段的荧光强度以10at%Yb∶YAG的为最强·同时发现它在450nm~680nm波段有明显的可见发光,其强度随Yb3 掺杂浓度的增加而迅速地增强·Yb∶YAG晶体的荧光寿命存在浓度猝灭现象,对猝灭机制进行了分析研究,指出浓度猝灭的主要原因是合作发光和痕量稀土离子的上转换发光·     

Yb∶YAG晶体的闪烁特性

通过不同Yb3+掺杂浓度(5%~30%,原子数分数)的Yb∶YAG晶体的阴极射线发光谱、衰减时间、光输出及其温度依赖关系的测量,研究了Yb∶YAG晶体的闪烁性能。不同Yb3+掺杂浓度的Yb∶YAG晶体具有不同的光输出和猝灭温度,光输出随Yb3+掺杂浓度的增大而降低,猝灭温度则随掺杂浓度的增大而升高。室温下Yb∶YAG晶体的发光衰减时间较短,均小于50 ns。Yb3+掺杂浓度为5%的Yb∶YAG晶体具有较高的光输出和较低的猝灭温度。     

Y3Al5O12:Ce3+,Cr3+和Y3Al5O12:Ce3+,pr3+,Cr3+荧光粉体系中的能量传递

通过在YAG:Ce3+和YAG:Ce3+,pr3+荧光粉体系中分别掺入Cr3+离子来提高蓝光管芯白光LED的显色指数.Cr3+离子的加入,增加了红光发射,这归因于Cr3+的2E-4 A2跃迁的零声子线和声子边带发光.Ce3+→Cr3+的能量传递是增强红光发射的重要方式,在YAG:Ce3+,Cr3+体系中,由发射光谱得到...     

高亮度高分辨率电子枪

 论述了一种已用于122cm背投式和183cm前投式电视机的新型的7.6cm钇铝石镏石(YAG)投影阴极射线管中的电子枪。在YAG绿色投影管中,当阴极电流为0.5～1mA时,其光点直径为0.065～0.08mm,该投影管分辨率大于1400电视线。     

Optical characteristics of Cr and Nd codoped Y3Al5O12 ceramics

The optical characteristics of Cr³⁺ and Nd³⁺ codoped Y₃Al₅O₁₂ (YAG) ceramics are measured. These measurements are done using two pumping sources, a 808 nm laser diode (LD) and a Xe short-arc lamp, to simulate solar radiation. The specimens used are 0.1%Cr³⁺/1.0%Nd³⁺ and 3.0%Cr³⁺/1.0%Nd³⁺ (atomic%) codoped YAG ceramics. A Nd:YAG crystal doped with 1.0%Nd³⁺ is used as a reference. The saturation intensities of the Cr/Nd:YAG ceramics pumped by the LD are the same as that of the Nd:YAG crystal, while they are higher when they are pumped by the Xe lamp. The saturation intensities are for the 0.1% Cr-doped ceramic and for the 3.0%Cr-doped ceramic. The small signal gains of the 0.1%Cr-doped and 3.0%Cr-doped ceramics are measured and found to be 1.8 times and 7.0 times higher than that of Nd:YAG for the same intensity of solar pumping, respectively. The quantum efficiency of energy transfer from Cr³⁺ to Nd³⁺ is estimated to be 0.88±0.09 for the 0.1%Cr-doped ceramic and 0.67±0.08 for the 3.0%Cr-doped ceramic.     

Tunable single-longitudinal-mode operation of a sandwich-type YAG/Ho:YAG/YAG ceramic laser

We present a 2.09 μm single-longitudinal-mode sandwich-type YAG/Ho:YAG/YAG ceramic laser pumped by a Tm-doped fiber laser for the first time. A pair of F-P etalons was used to achieve tunable single-longitudinal-mode operation. The maximum single-longitudinal-mode output power of 530 mW at 2091.4 nm was obtained with an absorbed pump power of 8.06 W, corresponding to an optical conversion efficiency of 6.6% and a slope efficiency of 12.7%. Wavelength tunable was achieved by tuning the angle of etalons and the wavelength could be tuned from 2091.1 nm to 2092.1 nm, corresponding to a tuning frequency of 68 GHz. The M² factor was measured to be 1.23.     

YAG及其掺杂纳米粉体的结构与光学特性

由于透明多晶钇铝石榴石(YAG)陶瓷在高功率全固态激光器中巨大的应用价值,所以其研究在近几年引起了广泛的关注。YAG陶瓷与其单晶材料相比,可以实现大尺寸激光晶体,高掺杂浓度,并且制备的成本低。我们报道水热方法制备的纯YAG和硅、铷掺杂YAG陶瓷纳米粉体中掺杂与煅烧温度对陶瓷相组分、晶格参数和晶粒尺寸的影响。通过XRD和透射电子显微镜表征了YAG陶瓷及掺杂粉体的结构及其受到掺杂和烧结的作用,利用光吸收和发射谱研究了共掺杂和煅烧温度对YAG陶瓷粉体光学特性的影响。结果表 Si⁴⁺和Nd³⁺的共掺杂提高了Nd³⁺在YAG纳米体中的可溶度,促进了YAG相的生成,单相纳米Si/Nd:YAG粉体在920℃煅烧温度即可获得。它的光学特性与报道的单晶Nd:YAG一致。     

被动调Q激光器输出特性的实验研究

被动调Q晶体Cr∶YAG对激光器的性能起着重要的作用。对Cr∶YAG被动调Q Nd∶YAG激光器进行了实验研究。着重研究了抽运功率、腔长、输出镜透过率以及初始透过率等因素对激光输出脉冲序列的重复率、脉冲宽度以及输出功率的影响。实验结果表明，抽运功率是影响重复率的最大因素，抽运功率的增大可以提高重复率，并减小脉冲宽度；它对腔长的影响效果刚好相反；存在一个可使输出功率最大的最佳输出镜透过率；不同的初始透过率对输出有一定的影响。分析表明被动调Q技术适用于DPL。     

高峰值266nm紫外激光器

报道了一种激光二极管(LD)端面泵浦的Nd:YAG声光Q开关高峰值功率266nm紫外激光器。该激光器采用紧凑的平平腔结构,LBO和BBO分别作为其二倍频和四倍频晶体。分别利用高偏振比LD阵列(40∶1)、低偏振比LD阵列(5∶1)及低偏振LD阵列腔内放置布氏片结构进行了实验。当注入功率为25W、调制频率为10kHz时,以上结构分别得到功率0.85,0.61和0.72W的266nm紫外光输出。其中,采用高偏振比LD阵列的输出功率最高,单脉冲能量为85μJ,脉宽为5ns,峰值功率高达17kW,泵浦光到紫外光的光-光转换率达3.4%。     

碳酸铵均相共沉淀法制备Nd∶YAG透明激光陶瓷纳米粉体

初步采用碳酸铵作为沉淀剂,采用均相共沉淀法,通过仔细控制沉淀过程的工艺参数,得到了煅烧后可直接生成纯相Nd∶YAG的前驱体。通过热重/差热分析(TG/DTA)、红外光谱(IR)、X射线衍射(XRD)、透射电镜(TEM)等测试手段对前驱物及煅烧粉体进行表征,研究结果表明:碳酸铵和金属离子的摩尔比为7:1时,体系的pH值基本保持在9,无需外加氨水调节溶液的pH值,简化了试验步骤,同时也减少了污染。XRD分析表明,在900℃煅烧该前驱体,得到Nd∶YAG纯晶相;根据谢乐方程计算和TEM分析,经过900℃煅烧所得纳米粉体颗粒尺寸为30～50nm,具有良好的分散性和烧结活性。     

梯度掺杂Yb:YAG重频激光器热管理研究

为了改善重频激光器的热性能,本文采用了键合Yb:YAG晶体薄片作为激光增益介质,介质中掺杂粒子浓度呈梯度分布.文章计算了不同参数条件下介质抽运过程,得到介质内部的储能,温度和应力分布,并从中选出较为优化的介质参数.计算表明,采用梯度掺杂的方法,介质温度降低,形变和热应力减小,波前畸变改善.理论上证明了采用梯度掺杂的方法改善热管理的可行性.     

阵列口径Nd：YAG片状激光器重复频率输出特性研究

 介绍了一种新型阵列口径的固体片状激光器的设计及初步实验，研究了其激光输出特性。激光器采用2×1阵列的以布儒斯特角放置的片状Nd:YAG激光头模块，并采用氙灯泵浦方式，由平均功率为60 kW电池组电源供电；电源采用大电流恒流放电，对输出放电进行可编程控制。实验得到32 J的单脉冲输出，小信号增益系数为0.047 5 cm^-1；泵浦单脉冲运行，脉宽为1~5 ms时，输出能量呈线性增长；当重复频率为20 Hz时，5 ms脉宽比1 ms脉宽输出功率下降30%，其原因是布儒斯特角结构存在时，由热应力引起的热致双折射损耗造成输出下降。