Growth of ZnO nanorods by aqueous solution method with electrodeposited ZnO seed layers

ZnO nanorod arrays on ZnO-coated seed layers were fabricated by aqueous solution method using zinc nitrate and hexamethylenetetramine at low temperature. The seed layers were coated on ITO substrates by electrochemical deposition technique, and their textures were dominated by controlling the deposition parameters, such as deposition potential and electrolyte concentration. The effects of the electrodeposited seed layers and the growing parameters on the structures and properties of ZnO nanorod arrays were primarily discussed. The orientation and morphology of both the seed layer and successive nanorods were analyzed by using X-ray diffraction (XRD), SEM and TEM. The results show that the seed layer deposited at −700 mV has evenly distributed crystallites and (0 0 2) preferred orientation; the density of resultant nanorods is high and ZnO nanorods stand completely perpendicular onto substrates. Meanwhile, the size of nanorods quite also depends on the growth solution, and the higher concentration of growth solution primary leads to a large diameter of the ZnO nanorods.     

电沉积法制备ZnO纳米柱及其机制研究

采用阴极还原方法,以Zn(NO₃)₂水溶液为电解液制备ZnO纳米柱。分析了不同沉积电位和不同沉积时间的缓冲层对ZnO纳米柱的密度、形貌及取向的影响。通过分析缓冲层在不同沉积时间下的电流密度变化,研究了缓冲层对ZnO纳米柱密度影响的机理。利用扫描电子显微镜(SEM)和X射线衍射(XRD)分析了样品的表面形貌及结构。研究结果表明,缓冲层能够增加ZnO纳米柱的密度及c轴的取向性,当缓冲层的沉积时间为60 s时,可以得到密度最大、取向最好的ZnO纳米柱。     

ZnO nanorod arrays fabrication via chemical bath deposition: Ligand concentration effect study

A new ligand, N,N,N′,N′-tetramethylethylenediamine, has been used to grow ZnO nanorods on silicon substrates via a two steps approach. A preliminary seeding on silicon substrates has been combined with chemical bath deposition using a Zinc acetate–N,N,N′,N′-tetramethylethylenediamine aqueous solution. The used diamino ligand has been selected as Zn²⁺ complexing agent and the related hydrolysis generates the reacting ions (Zn²⁺ and OH⁻) responsible for the ZnO growth. The seed layer has been annealed at low temperature (<200 °C) and the ZnO nanorods have been grown on this ZnO amorphous layer. There is experimental evidence that the ligand concentration (ranging from 5 to 50 mM) strongly affects the alignment of ZnO nanorods on the substrate, their lateral dimension and the related surface density. Length and diameter of ZnO nanorods increase upon increasing the ligand concentration, while the nanorod density decreases. Even more important, it has been demonstrated, as proof of concept, that chemical bath deposition can be usefully combined with colloidal lithography for selective ZnO nanorod deposition. Thus, by patterning the ZnO seeded substrate with polystyrene microsphere colloidal lithography, regular Si hole arrays, spatially defined by hexagonal ZnO nanorods, have been successfully obtained.     

Alignment-controlled hydrothermal growth of well-aligned ZnO nanorod arrays

ZnO nanorod arrays (ZNAs) were prepared via a two-step seeding and solution hydrothermal growth process. Effects of preparing parameters such as seed layer, colloid concentration, substrate and precursor concentration, on the alignment control of ZNAs were systematically investigated. The deviation angle of ZnO nanorods was measured to evaluate the alignment of arrays. Results show that seed layer not only controls the vertical orientation of ZNAs, but also the compactness of ZNAs. Altering colloid concentration and substrate can influence the microstructure of ZnO seed layer and affect the ordered alignment of ZNAs. The precursor concentration has an insignificant effect on the alignment of ZNAs but has great impact on the morphology of ZNAs. Alignment-controlled and well-aligned ZnO nanorods with different diameter and aspect ratio can be obtained by properly controlling the preparing parameters. A growth mechanism was proposed for the growth of ZnO nanorods.     

Improving light trapping and conversion efficiency of amorphous silicon solar cell by modified and randomly distributed ZnO nanorods

Three-dimensional （3D） nanostructures in thin film solar cells have attracted significant attention due to their appli- cations in enhancing light trapping. Enhanced light trapping can result in more effective absorption in solar cells, thus leading to higher short-circuit current density and conversion efficiency. We develop randomly distributed and modified ZnO nanorods, which are designed and fabricated by the following processes： the deposition of a ZnO seed layer on sub- strate with sputtering, the wet chemical etching of the seed layer to form isolated islands for nanorod growth, the chemical bath deposition of the ZnO nanorods, and the sputtering deposition of a thin Al-doped ZnO （ZnO：Al） layer to improve the ZnO/Si interface. Solar cells employing the modified ZnO nanorod substrate show a considerable increase in solar energy conversion efficiency.     

Controlled synthesis of oriented ZnO nanorod arrays by seed-layer-free electrochemical deposition

Oriented ZnO nanorod arrays were successfully prepared on transparent conductive substrates by seed-layer-free electrochemical deposition in solution of Zn(NO₃)₂ at a low temperature of 70 °C without using any catalysts, additives, and additional seed crystals. The effects of the Zn(NO₃)₂ concentration, deposition time and applied current on the localized nanorod arrays are investigated. X-ray powder diffraction (XRD) and field emission scanning electron microscopy (FE-SEM) were used to characterize the structures and the morphologies of ZnO nanorod arrays. The heights and diameters of ZnO nanorods can be tuned by controlling the electrodeposition parameters.     

Aligned ZnO nanorod arrays fabricated on Si substrate by solution deposition

Aligned ZnO nanorod arrays were fabricated by chemical solution deposition based on Si substrate which was spin coated with ZnO colloid as nucleation seeds. Their microstructures were characterized by X-ray diffraction, scanning electron microscopy, and high-resolution transmission electron microscopy. The results indicated that ZnO nanorods nucleated and grew vertically on Si substrates along the [0 0 1] direction with single-crystalline structure. The diameter of ZnO nanorods was greatly affected by the grain size of ZnO seeds. Room-temperature photoluminescence of nanorods has a strong emission band at about 384 nm.     

Site‐specific deposition of Ag nanoparticles on ZnO nanorod arrays via galvanic reduction and their SERS applications

A controllable heterostructure consisting of ZnO nanorod arrays with attached Ag nanoparticles at only one end has been synthesized via a facile and convenient galvanic reduction method. Scanning electron microscopic images of these nanostructures showed good selectivity of Ag deposition on the tip of ZnO nanorod arrays. The formation of these regular Ag ZnO heterogeneous nanorod arrays can be explained by a localization of the electrons at the ends of the ZnO nanorods after the electron transfer step. By tuning the reaction time and the concentration of silver nitrate, the density of Ag nanoparticles on the tip of ZnO nanorods can be well controlled. Owing to the introduction of Ag nanoparticles with different densities, the resulting Ag ZnO heterogeneous nanorod arrays have been proved to be a versatile substrate for surface‐enhanced Raman scattering not only for common organic molecules but also for label‐free protein detection. Copyright © 2009 John Wiley & Sons, Ltd.     

醋酸锌热解温度对ZnO纳米棒的结构及光学性质的影响

采用水热法在普通载玻片上热解醋酸锌生成的ZnO种子层上制备ZnO纳米棒, 采用 X射线衍射仪、扫描电镜、分光光度计等测试手段详细研究了醋酸锌热解温度对 ZnO纳米棒的结构和光学性质的影响. 结果表明: 纳米棒的结晶质量、端面尺寸、宏观应力和透射率与醋酸锌热解温度有密切关系. 随着热解温度的增加, ZnO纳米棒具有的c轴择优取向性先增强后减弱, 拉应力先减小后增大, 可见光区的平均透射率先增大后减小. 热解温度为350 ℃时, ZnO纳米棒c轴择优取向性最强, 拉应力最小, 平均透射率最大. 端面尺寸诱导的表面散射 是影响ZnO纳米棒可见光区平均透射率的主要机制. 关键词： 醋酸锌 水热法 ZnO纳米棒     

聚乙烯亚胺对氧化锌纳米阵列形貌的影响

采用化学沉淀法,以硝酸锌和六次亚甲基四胺的水溶液为生长溶液,在涂覆氧化锌晶种层的玻璃衬底上制备了定向生长的氧化锌纳米棒阵列,并研究了添加剂聚乙烯亚胺的浓度对氧化锌纳米棒形貌和结构的影响。X射线衍射和场发射扫描电镜的结果表明,合成的氧化锌纳米棒阵列较为均匀致密,具有六方纤锌矿结构,且有沿(002)晶面择优生长的特性;随着聚乙烯亚胺浓度的增加,氧化锌纳米棒的直径减小,直径分布趋于均匀,且氧化锌纳米棒的形貌也从锥状转变为柱状结构;另外,聚乙烯亚胺的加入对氧化锌的生长速度具有抑制作用,当聚乙烯亚胺的浓度增加至0.012 mol·L-1时,无氧化锌阵列生长。对氧化锌纳米棒阵列进行了拉曼光谱表征,结果表明,随着溶液中聚乙烯亚胺浓度的增加,氧化锌纳米棒的氧空位缺陷减少。最后,对聚乙烯亚胺浓度对氧化锌纳米阵列影响的机理进行了探讨。     

Controllable growth of well-aligned ZnO nanorod arrays by low-temperature wet chemical bath deposition method

Well-aligned ZnO nanorod arrays were synthesized by low-temperature wet chemical bath deposition (CBD) method on Si substrate under different conditions. Results illustrated that dense ZnO nanorods with hexagonal wurtzite structure were vertically well-aligned and uniformly distributed on the substrate. The effects of precursor concentration, growth temperature and time on nanorods morphology were investigated systematically. The mechanism for the effect of preparation parameters was elucidated based on the chemical process of CBD and basic nucleation theory. It is demonstrated that the controllable growth of well-aligned ZnO nanorods can be realized by readily adjusting the preparation parameters. Strong near-band edge ultraviolet (UV) emission were observed in room temperature photoluminescence (PL) spectra for the samples prepared under optimized parameters, yet the usually observed defect related deep level emissions were nearly undetectable, indicating high optical quality ZnO nanorod arrays could be achieved via this easy process chemical approach at low temperature.     

Boundary layer-assisted chemical bath deposition of well-aligned ZnO rods on Si by a one-step method

ZnO seed layers and well-aligned ZnO single-crystalline micro/nanorods were synthesized on bare Si in one step without the assistance of catalysts by chemical bath deposition. Scanning electron microscopy (SEM) images and X-ray diffraction patterns show that the alignment of ZnO rods on Si(100) could be adjusted by varying the substrates’ angles of incline, the reaction temperature, and the precursor concentration. Transmission electron microscopy cross-sectional images demonstrate that a polycrystalline seed layer with (0002) preferred orientation was formed between the well-aligned rods and Si substrate placed vertically while a randomly oriented layer was formed between the randomly aligned rods and Si substrate placed horizontally. The formation of seed layers and alignment of as-synthesized ZnO rods were attributed to the assistance of boundary layers in a chemical bath deposition system.     

A template-free sol-gel technique for controlled growth of ZnO nanorod arrays

The growth of ZnO nanorod arrays via a template-free sol-gel process was investigated. The nanorod is single-crystalline wurtzite structure with [0 0 0 1] growth direction determined by the transmission electron microscope. The aligned ZnO arrays were obtained directly on the glass substrates by adjusting the temperatures and the withdrawal speeds, without seed-layer or template assistant. A thicker oriented ZnO nanorod arrays was obtained at proper experimental conditions by adding dip-coating layers. Room temperature photoluminescence spectrum exhibits an intensive UV emission with a weak broad green emission as well as a blue double-peak emission located at 451 and 468 nm, respectively. Further investigation results show that the difference in the alignment of nanorods ascribes to the different orientations of the nanoparticles-packed film formed prior to nanorods on the substrate. Well ordered ZnO nanorods are formed from this film with good c-axis orientation. Our study is expected to pave a way for direct growth of oriented nanorods by low-cost solution approaches.     

ZnO nanorod arrays with tunable size and field emission properties on an ITO substrate achieved by an electrodeposition method

In the present work,vertically aligned ZnO nanorod arrays with tunable size are successfully synthesized on nonseeded ITO glass substrates by a simple electrodeposition method.The effect of growth conditions on the phase,morphology,and orientation of the products are studied in detail by X-ray diffraction(XRD),scanning electron microscopy(SEM),and transmission electron microscopy(TEM).It is observed that the as-prepared nanostructures exhibit a preferred orientation along c axis,and the size and density of the ZnO nanorod can be controlled by changing the concentration of ZnCl2.Field emission properties of the as-synthesized samples with different diameters are also studied,and the results show that the nanorod arrays with a smaller diameter and appropriate rod density exhibit better emission properties.The ZnO nanorod arrays show a potential application in field emitters.     

ZnO薄膜的性质对水热生长ZnO纳米线阵列的影响

用水热法在ZnO薄膜上制备了直径、密度及取向可控的ZnO纳米线阵列。ZnO薄膜是通过原子层沉积(ALD)方法制备并在不同温度下退火处理得到的,退火温度对ZnO薄膜的晶粒尺寸、结晶质量和缺陷性质有很大的影响。而ZnO薄膜的性质对随后生长的ZnO纳米线的直径、密度及取向能起到调节控制的作用。通过扫描电子显微镜(SEM)、X射线衍射(XRD)仪和光致发光(PL)测试对ZnO薄膜和ZnO纳米线进行了表征。最后得到的垂直取向的ZnO纳米线阵列适合在发光二极管和太阳能电池等领域使用。     

Solution-based growth of ZnO nanorods for light-emitting devices: hydrothermal vs. electrodeposition

ZnO nanorods have been grown by two inexpensive, solution-based, low-temperature methods: hydrothermal growth and electrodeposition. Heterojunction n-ZnO nanorods/p-GaN light-emitting diodes have been studied for different nanorod growth methods and different preparation of the seed layer. We demonstrate that both the nanorod properties and the device performance are strongly dependent on the growth method and seed layer. All the devices exhibit light emission under both forward and reverse bias, and the emission spectra can be tuned by ZnO nanorod deposition conditions. Electrodeposition of rods or a seed layer results in yellow emission, while conventional hydrothermal growth results in violet emission.     

The super hydrophobicity of ZnO nanorods fabricated by electrochemical deposition method

Electrochemical deposition method was employed to fabricate ZnO nanorods on zinc foil substrate in this paper. The structural observations of ZnO nanorods with different aspect ratios were carried out by field-emission scanning electron microscopy. The microstructures of ZnO nanorods were also characterized by X-ray diffraction and the changes in surface hydroxyls with electrochemical deposition time were analyzed by X-ray photoelectron spectroscopy. The study results show the aspect ratios of ZnO nanorods and the density of their surface hydroxyls are responsible for their superhydrophobicity. The fluorinated polymer coated ZnO nanorods showed an excellent superhydrophobic behavior with 167° contact angle of water droplet, which is larger than that of fluorinated polymer flat surface. The more the surface hydroxyls are, the more hydrophilic the surfaces are. Meanwhile, the larger the aspect ratio of ZnO nanorod arrays is, the larger its drophobicity is. The results of this study might pave a simple and feasibility pathway to the fabrication of superhydrophobic cleaning materials used in engineering fields.     

Effect of growth time on Ti-doped ZnO nanorods prepared by low-temperature chemical bath deposition

Ti-doped ZnO nanorod arrays were grown onto Si substrate using chemical bath deposition (CBD) method at 93 °C. To investigate the effect of time deposition on the morphological, and structural properties, four Ti-doped ZnO samples were prepared at various deposition periods of time (2, 3.5, 5, and 6.5 h). FESEM images displayed high-quality and uniform nanorods with a mean length strongly dependent upon deposition time; i.e. it increases for prolonged growth time. Additionally, EFTEM images reveal a strong erosion on the lateral side for the sample prepared for 6.5 h as compared to 5 h. This might be attributed to the dissolution reaction of ZnO with for prolonged growth time. XRD analysis confirms the formation of a hexagonal wurtzite-type structure for all samples with a preferred growth orientation along the c-axis direction. The (100) peak intensity was enhanced and then quenched, which might be the result of an erosion on the lateral side of nanorods as seen in EFTEM. This study confirms the important role of growth time on the morphological features of Ti-doped ZnO nanorods prepared using CBD.     

The effect of pre-annealing of sputtered ZnO seed layers on growth of ZnO nanorods through a hydrothermal method

Oriented ZnO nanorods were grown on ion-beam-sputtered ZnO seed layers through a hydrothermal approach without any metal catalyst. The sputtered ZnO seed layers were pre-annealed at different temperatures before the growth of ZnO nanorods. The effects of pre-annealing of the ZnO seed layers on the growth rate, crystallinity and optical properties of ZnO nanorods thereon were studied. The obtained ZnO nanorods had a wurtzite structure and grew along the preferential [0001] orientation with a normal direction to the substrates. Results show that the growth rate and density of the ZnO nanorods strongly depend on the pre-treatment conditions of the ZnO seed layer. With higher pre-treatment temperature, the crystallinity and surface characteristics of the ZnO seed layer were improved and thereafter the growth rate of ZnO nanorods thereon increased. Photoluminescence spectroscopy results show that the UV emission also becomes stronger and sharper with increasing annealing temperature of the ZnO seed layer.     

Aqueous chemical growth of free standing vertical ZnO nanoprisms,nanorods and nanodiskettes with improved texture co-efficient and tunable size uniformity

Tuning the morphology, size and aspect ratio of free standing ZnO nanostructured arrays by a simple hydrothermal method is reported. Pre-coated ZnO seed layers of two different thicknesses (≈350 nm or 550 nm) were used as substrates to grow ZnO nanostructures for the study. Various parameters such as chemical ambience, pH of the solution, strength of the Zn²⁺ atoms and thickness of seed bed are varied to analyze their effects on the resultant ZnO nanostructures. Vertically oriented hexagonal nanorods, multi-angular nanorods, hexagonal diskette and popcorn-like nanostructures are obtained by altering the experimental parameters. All the produced nanostructures were analysed by X-ray powder diffraction analysis and found to be grown in the (002) orientation of wurtzite ZnO. The texture co-efficient of ZnO layer was improved by combining a thick seed layer with higher cationic strength. Surface morphological studies reveal various nanostructures such as nanorods, diskettes and popcorn-like structures based on various preparation conditions. The optical property of the closest packed nanorods array was recorded by UV-VIS spectrometry, and the band gap value simulated from the results reflect the near characteristic band gap of ZnO. The surface roughness profile taken from the Atomic Force Microscopy reveals a roughness of less than 320 nm.