Ag@SiO2@Y2O3:RE3+（RE=Eu,Tb）核壳结构发光材料的制备与性能

采用均相沉淀法制备了Ag@SiO2@(Y,RE)(OH)CO3.H2O(RE=Eu,Tb)核壳结构微球,经过700℃焙烧后成功制备出Ag@SiO2@Y2O3:RE3+(RE=Eu,Tb)核壳结构发光材料。XRD谱图表明Ag核具有结晶良好的面心立方结构;SiO2层为无定型;Y2O3层为立方晶系。FTIR谱图表明核壳之间以化学键相结合。TEM照片表明合成了核壳结构的表面光滑的复合微球,分散良好,大小均匀,Ag核的粒径分布为50±20 nm;SiO2层的厚度为20～30 nm;Y2O3:RE3+(RE=Eu,Tb)层厚度约为125 nm。电子衍射图像表明Ag@SiO2@Y2O3:RE3+(RE=Eu,Tb)为多晶结构。UV-Vis光谱表明表面包覆使Ag离子的等离子体共振吸收峰发生了红移。荧光光谱表明Ag@SiO2@Y2O3:Eu3+具有Eu3+的特征红光发射,Ag@SiO2@Y2O3:Tb3+具有Tb3+的特征绿光发射,但是发光强度均比纯的Y2O3:RE3+有所减弱,说明贵金属的引入对稀土Y2O3:RE3+(RE=Eu,Tb)的发光起到了荧光猝灭的作用。     

Preparation and optical properties of ThO(2) and Eu-doped ThO(2) nanotubes by the sol-gel method combined with porous anodic aluminum oxide template

In this paper, we report the synthesis of thorium oxide and Eu-doped thorium oxide nanotubes for the first time using the sol-gel method in porous anodic aluminum oxide template. Transmission electron microscopy, X-ray diffraction, and X-ray photoelectron spectroscopy were applied to characterize the morphology and structure of the as-prepared nanotubes. It has been demonstrated that Eu(3+) ions were homogeneously doped into the ThO(2) crystal lattice. The optical properties resulting from Eu-doped products were investigated by means of photoluminescence spectroscopy. Strong visible light emissions were observed at low doping concentration, and the luminescent intensity decreased at high doping concentration. The luminescent centers were concluded to be the Eu(3+) ions in the cubic (O(h)) sites rather than the C(3v) sites, which accounted well for the decrease of luminescent intensity at high doping concentration.     

磁电CoFe2O4/BaTiO3纳米管的溶胶-凝胶模板法合成和表征

用溶胶-凝胶模板法合成了 CoFe2O4)/BaTiO3(CFO/BTO)复合纳米管,管的直径约为 100、200 和 300 nm,其长度约为100 μm.x射线衍射(xRD)和选区电子衍射(sAED)都显示复合纳米管中同时存在尖晶石相的CoFe2O4(CFO)和钙钛矿相的 BaTiO3(BTO),进一步的透射电子显微镜(TEM)研究证实合成的纳米复合物具有明显的管状结构.磁、电研究表明,该复合纳米管的磁性与纯 CFO 纳米管的磁性相当;而铁电性与纯BTO纳米管的铁电性相当.     

SrMgB6O11:Eu3+纳米材料的水热法制备及发光性能研究

采用水热法制备了Eu3+掺杂SrMgB6O11纳米发光材料.利用X射线粉末衍射仪(XRD)、场发射扫描电子显微镜(FESEM)和荧光光谱对SrMgB6O11:Eu3+样品进行表征.结果表明:采用水热法可以成功地合成粒度均匀、结晶完好的SrMgB6O11:Eu3+纳米发光粉.深入研究了反应温度和pH值对SrMgB6O11:Eu3+纳米材料的晶体结构及形貌的影响.结果表明,在120℃时形成了尖锐且强度最强的衍射峰,同时FESEM也表明此时所得材料为纳米棒组成的规则扇形形貌,此后随着温度的升高,XRD图中衍射峰的位置和强度发生变化,说明荧光粉的晶体结构发生变化,FESEM也表明该荧光粉已变为球形颗粒.归属了发射光谱和激发光谱中各激发峰所对应的能级跃迁.荧光光谱也显示:反应温度和pH值影响着Eu3+在晶格中的对称性,且反应温度为120℃及pH值为9时,Eu3+在晶格中的对称性较好.另外,还初步探讨了纳米粒子的生长机制.     

碳包覆Na2Ti6O13纳米管的电化学性能研究

以金红石型TiO2和NaOH为原料,由水热反应制备Na2Ti6O13纳米管.然后,在含有0.1 mol.L-1NaOH的葡萄糖水溶液中反应4 h制得碳包覆的Na2Ti6O13纳米管.X射线衍射(XRD)、扫描电子显微镜(SEM)和透射电子显微镜(TEM)等分析表明,该碳包覆Na2Ti6O13纳米管外径约14～19 nm,内径约2～5 nm,长度为数百纳米,有一层厚度约为2 nm的碳层包覆在纳米管外壁.以其作为锂离子电池负极材料,恒电流充放电测试表明,在50 mA.g-1电流密度下首周可逆容量达到161 mAh.g-1,循环100周后容量保持在147 mAh.g-1.相比于Na2Ti6O13纳米管,提高了20%以上.电流密度升至1600 mA.g-1充放电,碳包覆Na2Ti6O13纳米管可逆容量仍有70 mAh.g-1左右,远高于Na2Ti6O13纳米管,表现出良好的倍率性能.     

Phase structure and luminescence properties of Eu3+-doped TiO2 nanocrystals synthesized by Ar/O2 radio frequency thermal plasma oxidation of liquid precursor mists

Eu3+-doped TiO2 luminescent nanocrystals have been synthesized in this work via Ar/O2 thermal plasma oxidizing mists of liquid precursors containing titanium tetra-n-butoxide and europium(III) nitrate, with varied O2 input in the plasma sheath (10-90 L/min) and Eu3+ addition in the precursor solution (Eu/(Ti + Eu) = 0-5 atom%). The resultant nanopowders are mixtures of the anatase (30-36 nm) and rutile (64-83 nm) polymorphs in the studied range, but the rutile fraction increases steadily at a higher Eu3+ addition, as revealed by X-ray diffraction (XRD) and Raman spectroscopy, because of the creation of oxygen vacancies in the TiO2 gas clusters by substitutional Eu3+ doping. The amount of Eu3+ that can be doped into a TiO2 lattice was limited up to 0.5 atom%, above which Eu2Ti2O7 pyrochlore was formed in the final products. High resolution transmission electron microscopy (HRTEM) observation indicates that the particles are dense and have sizes ranging from several nanometers up to 180 nm. Efficient nonradiative energy transfer from the TiO2 host to Eu3+ ions, which was seldom reported in the wet-chemically derived nanoparticles or thin films of the current system, was confirmed by combined studies of excitation, UV-vis (ultraviolet-visible), and PL (photoluminescence) spectroscopy. As a consequence of this, bright red emissions were observed from the plasma-generated nanopowders either by exciting the TiO2 host with UV light shorter than 405 nm or by directly exciting Eu3+ at a wavelength beyond the absorption edge (405 nm) of TiO2.     

Structural features of titanate nanotubes/nanobelts revealed by Raman, X-ray absorption fine structure and electron diffraction characterizations

High-purity nanotubes and nanobelts could be controllably obtained in hydrothermal treatments of anatase TiO(2) in concentrated NaOH solution depending on treating temperature and duration. Their structural features were studied employing X-ray diffraction, Raman, X-ray absorption fine structure, and electron diffraction characterizations. The results reveal that both the nanotubes and nanobelts might be of layered titanate structure. The similarity and difference among the nanotubes/nanobelts and other bulk titanates represented by trititanate H(2)Ti(3)O(7) and lepidocrocite-type H(0.7)Ti(1.825) square(0.175)O(4.0).H(2)O were also presented.     

Y2O3:Eu纳米晶的硝基取代苯甲酸配合物固相热解制备和性能

以苯甲酸、邻硝基苯甲酸、间硝基苯甲酸、对硝基苯甲酸、3,5 二硝基苯甲酸等为配体制备了Y3+、Eu3+二元配合物,配合物中Y3+与Eu3+的摩尔比为9：1.利用这些配合物的爆炸式热分解特性通过固相热解反应制备了一系列Y2O3:Eu纳米晶.透射电镜观察,可以看出所得纳米晶呈球形,粒度介于40～60 nm,X射线衍射分析表明实验所得纳米晶属立方晶系,粒径与电镜观察所得结果基本一致；Eu3+的引入并不影响Y2O3的晶相组成；配体类型对纳米晶的结构没有显著影响,不过相对于硝基取代苯甲酸配合物,苯甲酸配合物热解所得Y2O3∶Eu纳米晶团聚严重；退火温度显著影响纳米晶粒度,退火温度高,纳米晶粒度大,反之亦然.荧光光谱测定表明所有Y2O3∶Eu纳米晶具有相似的发光行为,其中以苯甲酸配合物分解所得Y2O3:Eu纳米晶发光性能最为优越.     

Synthesis and characterization of ultrahigh crystalline TiO2 nanotubes

Ultrahigh crystalline TiO2 nanotubes were synthesized by hydrogen peroxide treatment of very low crystalline titania nanotubes (TiNT-as prepared), which were prepared with synthesized TiO2 nanoparticles by hydrothermal methods in an aqueous NaOH solution. Thus, prepared ultrahigh crystalline TiO2 nanotubes (TiNT-H2O2) showed comparable crystallinity with high crystalline TiO2 nanoparticles. The details of nanotubular structures were elucidated by high resolution-transmission electron microscopy (HR-TEM), field emission-scanning electron microscopy (FE-SEM), energy-dispersive X-ray analysis in transmission electron microscopy (TEM-EDX), X-ray diffraction (XRD), photoluminescence (PL), and BET surface area. TiNT-H2O2 was found to be a multiwalled anatase phase only with an average outer diameter of approximately 8 nm and an inner diameter of approximately 5 nm and grown along the [001] direction to 500-700 nm long with an interlayer fringe distance of ca. 0.78 nm. The photocatalytic activity of TiNT-H2O2 was about 2-fold higher than those of TiNT-as prepared, synthesized TiO2 nanoparticles, and TiO2-P25 (Degussa) in the photocatalytic oxidation of trimethylamine gas under UV irradiation.     

YF3:Eu3+纳米纤维/高分子复合纳米纤维的制备与表征

采用静电纺丝技术制备了Y2O3:Eu3+纳米纤维,使用NH4HF2为氟化剂,经双坩埚法氟化和脱氨后得到YF3:Eu3+纳米纤维,再采用静电纺丝技术制备了YF3:Eu3+纳米纤维/PVP复合纳米纤维. XRD分析表明,立方相的Y2O3:Eu3+氟化后,得到了正交相的YF3:Eu3+纳米纤维,空间群为Pnma;YF3:Eu3+纳米纤维/PVP复合纳米纤维具有明显的YF3:Eu3+的衍射峰. SEM分析表明,YF3:Eu3+纳米纤维与YF3:Eu3+纳米纤维/PVP复合纳米纤维的直径分别为91±11 nm、319±43 nm,表面光滑. 用Shapiro-Wilk方法检验,纤维直径属于正态分布. 荧光光谱分析表明,YF3:Eu3+纳米纤维和YF3:Eu3+纳米纤维/PVP复合纳米纤维的最强发射峰均位于588 nm和595 nm,属于Eu3+的5D0→7F1跃迁,表明Eu3+占据YF3基质中Y3+晶格点的C2对称格位. PVP对YF3:Eu3+发光峰位没有影响,但发光强度降低;YF3:Eu3+的含量与YF3:Eu3+纳米纤维/PVP复合纳米纤维的发光强度成线性关系.     

Microwave-Assisted Heating Method for the Decoration of Carbon Nanotubes with Zinc Sulfide Nanoparticles

This study focuses on in situ synthesis of ZnS nanoparticles on the surface of multiwalled carbon nanotubes. By microwave-assisted chemical reaction of Zn(Ac)₂·2H₂O and NaS·9H₂O in glycol solution with carbon nanotubes, which were pretreated by oxidization in concentrated HNO₃. Zinc sulfide crystallite densely supported on carbon nanotubes with the diameter about 1 nm. The carbon nanotubes decorated by ZnS were characterized using transmission electron microscopy and x-ray diffraction. It is found that the multi-walled carbon nanotubes can not only act as a substrate but also change the crystal structures of ZnS in the reaction.     

多级结构ZSM-5沸石分子筛的合成及其Mo基催化剂在甲烷无氧脱氢芳构化中的应用

以经盐酸预处理的碳纳米管为第二模板,在不添加其它有机溶剂的情况下,仅通过控制晶化条件,即采用变温水热晶化法合成具有多级结构的ZSM-5分子筛.通过x射线衍射、红外光谱测试、透射电镜和N2吸附对合成的分子筛进行了表征,结果表明,该合成分子筛呈近球形,是由纳米棒自组装形成的具有多级结构的亚微米球.该分子筛改性后用于甲烷无氧脱氢芳构化反应,显示出良好的催化性能,甲烷转化率最初达到19%,反应至24 h时甲烷转化率仍保持在10%左右,并且保持了较高的芳香物选择性(达到50%以上).     

Optical properties of nanocrystalline Y2O3:Eu depending on its odd structure

The structure of nanocrystalline Y2O3:Eu prepared by a combustion reaction was analyzed by XRD and high-resolution electron microscopy. Compared with a large-scale particles, 5-nm Y2O3:Eu particles presented as distorted crystallite and rough surfaces. Luminescent and absorption properties of nano-Y2O3:Eu showed remarkably particle size effects. At Y2O3:Eu particle sizes smaller than 10 nm some new results were observed: (a) a red shift of the charge-transfer-state absorption; (b) new emission bands of Eu3+ in the 5D0 --> 7F2 region; (c) luminescent decay of energy level 5D0 of Eu3+ turning to a two-step exponential; and (d) a pronounced increase in quenching concentration and much lower phonon density compared with those of the bulk material. All these phenomena can be attributed to the effect of the softened lattice and surface state of the nanomaterial. The latter was confirmed by stronger excitation by the host absorption after the surface modification.     

Ce3+,Tb3+,Eu3+共掺杂Sr2MgSi2O7体系的白色发光和能量传递机理

通过正交试验,采用高温固相法制备了Sr2-x-y-zMgSi2O7∶xCe3+,yTb3+,zEu3+系列样品.使用X射线衍射仪和荧光光谱仪表征了样品的物相和发光性质,并讨论了Ce3+-Tb3+-Eu3+共掺杂Sr2MgSi2O7体系中的能量传递过程.实验结果表明,在327 nm波长激发下,所合成荧光粉的发射峰主要位于387 nm(蓝紫)、542nm(绿)和611 nm(红)处;分别以387,542和611 nm为监控波长,所得激发光谱显示荧光粉在327 nm处有最好的激发.在327 nm光激发下,系列样品发光进入白光区.最优化的荧光粉为Sr1.91MgSi2O7∶0.01Ce3+,0.05Tb3+,0.03Eu3+,其色坐标为(0.337,0.313),是一种潜在的发光二极管(LED)用白色荧光粉.     

Synthesis of vanadium oxide nanotubes via an ultrasonic method

Vanadium oxide nanotubes were synthesized using V₂O₅ powder as the precursor and hexadecylamine as the structure-directing template using a sol-gel reaction method followed by a one-step hydrothermal treatment. The effect of ultrasonics on the formation of nanotubes is reported. The structure and morphology of the nanotubes were investigated by X-ray diffraction, scanning electron microscopy, and transmission electron microscopy. The inner and outer diameters of the nanotubes varied from 20 to 40 nm and 80 to 100 nm, respectively. The nanotubes measured several micrometers in length.     

预还原催化剂LaNiO3, La4Ni3O10, La3Ni2O7和La2NiO4 催化分解CH4制碳纳米管 的研究

通过预还原的LaNiO3,La4Ni3O10,La3Ni2O7和La2NiO4催化分解CH4可以制备大量高度石墨化的碳纳米管。还原前后的催化剂的结构和组分通过X射线衍射(XRD)测定。所制得的碳纳米管由扫描电镜(TEM)、X射线光电子能谱(XPS)表征。碳纳米管在空气在的热氧化性由热重实验(TG)测定。实验结果表明不同催化剂前驱中的La/Ni比会影响碳纳米管的管径分布和石墨化程度。La/Ni比越小,碳纳米管的管径越大,石墨化程度越高。     

The fabrication of one-dimensional Ca4Y6(SiO4)6O: Ln3+ (Ln=Eu, Tb) phosphors by electrospinning method and their luminescence properties

One-dimensional Ca(4)Y(6)(SiO(4))(6)O: Ln(3+) (Ln=Eu, Tb) microfibers were fabricated by a simple and cost-effective electrospinning method. X-ray diffraction (XRD) pattern and high-resolution transmission electron microscopy (HRTEM) confirmed that the fibers were composed of hexagonal Ca(4)Y(6)(SiO4)(6)O phase. Thermogravimetric and differential scanning calorimetry (TG-DSC) results showed that the Ca(4)Y(6)(SiO4)(6)O phase began to crystallize at 740°C. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) results indicated that the diameter of as-prepared microfibers ranged from 390 to 900 nm and the diameter of the microfibers annealed at 1000°C ranged from to 120 to 260 nm. Under ultraviolet and low-voltage electron beams (3-5 kV) excitation, the Ca(4)Y(6)(SiO(4))(6)O: Ln(3+) (Ln=Eu, Tb) samples showed the red and green emission, corresponding to (5)D(0)→(7)F(2) transition of Eu(3+) and (5)D(4)→(7)F(5) transition of Tb(3+), respectively.     

磁电CoFe2O4/BaTiO3纳米管的溶胶-凝胶模板法合成和表征

用溶胶-凝胶模板法合成了CoFe2O4/BaTiO3(CFO/BTO)复合纳米管, 管的直径约为100、200和300 nm, 其长度约为100 μm. X射线衍射(XRD)和选区电子衍射(SAED)都显示复合纳米管中同时存在尖晶石相的CoFe2O4 (CFO)和钙钛矿相的BaTiO3(BTO), 进一步的透射电子显微镜(TEM)研究证实合成的纳米复合物具有明显的管状结构. 磁、电研究表明, 该复合纳米管的磁性与纯CFO纳米管的磁性相当; 而铁电性与纯BTO纳米管的铁电性相当.     

(-)-2，2′-(2，5-噻吩二甲酰氨基)二丙氨酸和4，4′-联吡啶构筑的铕配位聚合物的水热合成、晶体结构及性质研究

以(-)-2,2′-(2,5-噻吩二甲酰氨基)二丙氨酸(C12H14N2O6S)及4,4′-联吡啶(4,4′-bipy)为配体,在水热条件下合成了铕配位聚合物{[Eu2(C12H12N2O6S)3(4,4′-bipy)(H2O)2].(H2O)6}n。通过X-射线单晶衍射仪测定其结构,结果表明:晶体为正交晶系,晶胞参数a=1.113 992(18)nm,b=1.804 972(19)nm,c=2.933 80(3)nm,Z=4;2个Eu原子分别为九和八配位。测定发现配合物固体具有Eu3+的典型光致发光光谱,配合物中配体能有效提高稀土离子的发光效果。并通过热重分析对配合物进行了热稳定性研究。     

Uniform hollow Lu2O3:Ln (Ln = Eu3+, Tb3+) spheres: facile synthesis and luminescent properties

Uniform hollow Lu(2)O(3):Ln (Ln = Eu(3+), Tb(3+)) phosphors have been successfully prepared via a urea-assisted homogeneous precipitation method using carbon spheres as templates, followed by a subsequent calcination process. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transformed infrared (FT-IR), thermogravimetric and differential thermal analysis (TG-DTA), photoluminescence (PL) spectra, cathodoluminescence (CL) spectra, kinetic decays, quantum yields (QY), and UV-visible diffuse reflectance spectra were employed to characterize the samples. The results show that hollow Lu(2)O(3):Ln spheres can be indexed to cubic Gd(2)O(3) phase with high purity. The as-prepared hollow Lu(2)O(3):Ln phosphors are confirmed to be uniform in shape and size with diameter of about 300 nm and shell thickness of approximate 20 nm. The possible formation mechanism of evolution from the carbon spheres to the amorphous precursor and to the final hollow Lu(2)O(3):Ln microspheres has been proposed. Upon ultraviolet (UV) and low-voltage electron beams excitation, the hollow Lu(2)O(3):Ln (Ln = Eu(3+), Tb(3+)) spheres exhibit bright red (Eu(3+), (5)D(0)-(7)F(2)) and green (Tb(3+), (5)D(4)-(7)F(5)) luminescence, which may find potential applications in the fields of color display and biomedicine.