Release of charges under external fields of PbLa（Zr,Sn,Ti）O3 ceramic

This paper investigates the pyroelectric of poled antiferroelectric (AFE) ceramic Pb 0.97 La 0.02 (Zr 0.69 Sn 0.196 Ti 0.114)O 3 and its remnant polarization dependence of hydrostatic pressure.The results show that the bound charges of poled sample can be released in short time by temperature field or pressure field.The released charge abruptly forms a large pulse current.The phenomena of released charge under external fields result in the ferroelectric-AFE phase transition induced by temperature or hydrostatic pressure.     

等静压诱导的PbLa(Zr,Sn,Ti)O3陶瓷铁电-反铁电相变性能研究

 研究了等静压诱导掺镧La的Pb(Zr,Sn ,Ti)O₃（PLZST）陶瓷材料的铁电-反铁电相变和介电压谱,结果发现介电压谱具有明显的扩散相变和频率弥散的特点,这一现象有利于拓宽人们对压力诱导的多组元弛豫型铁电体的扩散相变行为的认识和理解。     

等静压和温度诱导的PbLa(Zr,Sn,Ti)O3反铁电陶瓷相变和介电性能研究

研究了等静压和温度诱导掺镧La的Pb(Zr,Sn,Ti)O₃(PLZST)陶瓷材料的铁电反铁电相变、介电压力谱和介电温度谱,研究了温度对压致相变和介电压力谱的影响,结果发现温度使铁电反铁电相变压力降低,介电压力谱具有明显的扩散相变和频率弥散的特点;研究了等静压对介电温度谱的影响,结果表明等静压使铁电反铁电相变温度降低,反铁电顺电相变温度升高.这些现象有利于丰富和拓宽人们对温度和压力诱导的多组元弛豫型铁电体和弛豫型反铁电体扩散相变和弛豫行为的认识和理解. 关键词： 等静压和压致相变 铁电反铁电相变 介电压力谱 介电温度谱     

Pb(Zr,Sn,Ti)O3反铁电陶瓷的低温相变扩散与极化弛豫

用弱场介电温谱、热释电流谱、强场电滞回线和变温X射线衍射谱研究了微量La掺杂Pb(Zr,Sn,Ti)O₃(PZST)反铁电(AFEt)陶瓷在-100—180℃温区内的结构与电学特性.弱场介电温谱显示,AFEt陶瓷在低温段(-100—50℃)呈现介电频率弥散(0.1—100kHz)和扩散型相变的特征,而变温X射线衍射谱却表明材料在这一温区内保持四方相结构;低温下经强场作用后,AFEt被诱导为亚稳三方铁电态,介电频率弥散消失.基于多元复杂化合物的组分起伏理论,讨论了PZST AFEt陶瓷 关键词： Pb(Zr Sn 3反铁电陶瓷')" href="#">Ti)O₃反铁电陶瓷 反铁电弛豫 相变 变温X射线衍射     

直流偏压对压力诱导反铁电陶瓷去极化性能的影响

采用掺铌的锆钛锡酸铅（PNZST）反铁电陶瓷作为研究对象,研究了不同的直流电场作用下,等静压力诱导极化态反铁电陶瓷发生去极化过程（同时发生铁电/反铁电相变）的规律.当极化态样品两端电场强度为6 kV/cm时,去极化压力为128.8 MPa;当极化态样品两端电场强度为-6 kV/cm时,去极化压力为74.2 MPa.在与极化电场方向相反的外加电场作用下极化态样品具有较小的去极化压力.讨论了外加直流电场影响极化态反铁电陶瓷去极化压力的内在机理.得到了不同外置电场下的去极化压力,并绘制了该材料的外加直流电场（< 关键词： 去极化 反铁电体 相变     

(PbBa)(Zr,Sn,Ti)O_3反铁电/弛豫型铁电相界陶瓷的相变与介电、热释电性质

通过对(Pb087Ba01La002)(Zr06TixSn04-x)O3(004≤x≤020)固溶体的介电和偏压热释电性质的研究发现,当Ti含量004≤x≤007时,材料是反铁电四方相,而当009≤x≤020时,材料向弛豫型铁电体转化.在温度Ti含量相图中,x=009附近形成了反铁电铁电顺电三相共存点(Ttr).该点的相变温度最底;对于004≤x≤007的反铁电四方相,低温下呈现介电弛豫特征,并可被外电场诱导为亚稳铁电态,温度升高时,亚稳铁电→反铁电相变,反铁电→顺电相变引起两个热释电流峰,偏置电场下峰位和峰强均发生移动,在温度电场相图中也形成了铁电反铁电顺电三相点.从复杂化合物纳米相分离的观点和晶格动力学出发,讨论了相变与电学性能随Ti含量(x)和外电场(E)变化的物理机理. 关键词： 反铁电/弛豫型铁电相界 介电性能 偏压热释电性质 铁电-反铁电-顺电三相点     

掺镧锆锡钛酸铅陶瓷极化强度变化量对电子发射电流强度的影响

铁电阴极因其优异的电子发射性能在高功率微波管的电子束源、平板显示技术以及宇航推进器等领域 有着广阔应用前景而日益受到人们的重视.大量研究表明,铁电阴极电子发射性能受阴极材料性能的影响. 在激励电场作用下,铁电阴极材料会产生表面非屏蔽电荷而引起极化强度的变化, 这表明铁电阴极电子发射性能可能与阴极材料的极化强度变化量存在着某种关系. 为研究阴极材料极化强度变化量对铁电阴极电子发射性能的影响,以掺镧锆锡钛酸铅铁电和反铁电陶瓷样品 作为阴极材料,通过正半周电滞回线测试得到阴极材料在不同电场强度下的极化强度变化量, 测量得到电子发射电流强度随激励电场的变化曲线,并分析了电子发射电流强度与极化强度变化量的关系. 结果表明,两种样品电子发射电流强度与极化强度变化量正相关.     

锆钛酸钡陶瓷的电场诱导相变特性研究

Ba（Zr0.2Ti0.8）O3（BZT）陶瓷，其铁电相变温度接近室温。对BZT陶瓷的电场诱导相变进行了研究，结果表明介电常数随着电场的增加而减小，预示着电场诱导相变行为。电场强度影响陶瓷的介电常数峰值的位置，并且在广泛温度范围内影响介电常数的大小。介电常数峰值位置随电场的变化量△Tm与电场满足如下关系：△Tm～E^2/3，说明BZT发生了类似的二级相变行为。     

Pb(Zr,Sn,Ti)O3反铁电陶瓷场诱相变性能的改进

为了获得场诱反铁电(AFE_t)—铁电(FE_Ｒ)相变临界电场E_{f小、电滞ΔE小、场致应变x适当的反铁电陶瓷,对Pb(Zr, Sn, Ti)O3采用Ba ^2＋置换Pb^2＋,同时在四方反铁电相AFEt—三方铁电F EＲ相界附近调节Ti/Sn比,来控制FEＲ-AFEt,AFEt关键词： Pb(Zr Sn 3基反铁电陶瓷')" href="#">Ti)O3基反铁电陶瓷 场诱相变 场致应变 掺杂改性}     

Evolution of electric response of Pb0.99(Zr0.95Ti0.05)0.98Nb0.02O3 and Pb0.99[(Zr0.90Sn0.10)0.96Ti0.04]0.98Nb0.02O3 ferroelectric ceramics under shock wave compression

The objective of this work is to investigate the dependence of the electric behavior on shock pressure in Pb_0.99(Zr_0.95Ti_0.05)_0.98Nb_0.02O₃ (PZT 95/5-2Nb) and Pb_0.99[(Zr_0.90Sn_0.10)_0.96Ti_0.04]_0.98Nb_0.02O₃ (PZST) ferroelectric ceramics under shock wave compression. PZT 95/5-2Nb and PZST ceramics were subjected to high dynamic pressure generated by plate impacts. The output currents were measured under the short-circuit condition in the pressure range from 0.23 to 4.50 GPa. The evolution of the electric response exhibits three distinct regions: (1) Below the critical phase transition pressure (σ_C), alternate negative and positive piezoelectric currents are observed and the corresponding piezoelectric constant is e ₃₁. (2) Above σ_C and below the complete phase transition pressure (σ_H), released charge increases with increasing shock pressure, illustrating the transition of ferroelectric to antiferroelectric phase. (3) Above σ_H, the output current is insensitive to the shock pressure. A similar evolutionary process is also observed in hydrostatic and uniaxial stress experiments.     

(Ba, Ca)(Ti, Zr)O3-BiFeO3 lead-free piezoelectric ceramics

Effects of BiFeO₃ (BFO) content on the microstructure and electrical properties of Ba_0.85Ca_0.15Ti_0.90Zr_0.10O₃ (BCTZ) ceramics prepared by normal sintering in air were investigated. A stable solid solution is formed between BCTZ and BFO. The grain size gradually becomes smaller, and the ceramics become denser with increasing the BFO content. The Curie temperature, dielectric constant, and dielectric loss of BCTZ ceramics decrease simultaneously with the introduction of BFO. Moreover, the remanent polarization reaches a maximum at x = 0.2 mol%, and the coercive field continuously increases with increasing the BFO content due to the introduction of BFO with a higher coercive field. Improved piezoelectric properties (d₃₃ ∼ 405 pC/N and k_p ∼ 0.44) are demonstrated for the BCTZ ceramic with x = 0.2 mol%.     

La调节Pb(Zr,Sn,Ti)O_3反铁电陶瓷的相变与电学性质

利用X射线衍射、弱场介电温度谱、强场极化强度研究了不同La含量(Pb1-xLa2x3)(Zr06Sn03Ti01)O3(000≤x≤012)(PLZSnT)陶瓷的相变与电学特性.实验发现,随La含量增大,室温下材料由铁电三方相(x=000)转变为反铁电四方相(003≤x≤009)和立方相(x=012).介电测试表明,La含量增大,反铁电→顺电相变温度降低,峰值介电常量减小.在x=006的PLZSnT三元相图中,反铁电四方相区扩大到Ti含量约为18at%,该系统反铁电陶瓷具有“窄、斜”型双电滞回线和“三电滞回线”;在高Zr、高Sn区,反铁电→顺电相变呈现弥散相变和介电频率色散特征,即反铁电极化弛豫现象.从ABO3钙钛矿结构的容忍因子(t)和反铁电相的结构特征出发,讨论了La对Pb(Zr,Sn,Ti)O3相变与电学性质的影响机理 关键词： 场诱相变 弛豫型反铁电体 介电性能 La调节Pb(Zr Sn Ti)O3     

La诱导(Pb(1-3x/2)Lax)(Zr0.5Sn0.3Ti0.2)O3反铁电介电弛豫研究

采用标准电子陶瓷工艺制备了(Pb_(1-3x/2)La_x)(Zr_0.5Sn_0.3Ti_0.2)O₃(PLZST,0.00≤x≤0.18)反铁电陶瓷,利用X射线衍射、不同频率下弱场介电温谱、强场下的极化强度-电场(P-E)测试研究了材料相结构和电学性能.实验结果发现,随La含量x增大,室温下材料由铁电三方相(关键词： 反铁电陶瓷 介电频率色散 相变弥散 介电弛豫     

Relaxor behavior of (Ba,Sr)(Zr,Ti)O3 ferroelectric ceramics

We examine the ferroelectric-relaxor behavior of (Ba_0.65Sr_0.35)(Zr_0.35Ti_0.65)O₃ (BSZT) ceramics in the temperature range from 80 to 380 K. A broad dielectric maximum, which shifts to higher temperature with increasing frequency, signifies the relaxor-type behavior of these ceramics. The value of the relaxation parameter γ∼2 estimated from the linear fit of the modified Curie-Weiss law, indicates the relaxor nature of the BSZT ceramics. The dielectric relaxation rate follows the Vogel-Fulcher relation with T_VF=107 K, E_a=0.121 eV, and ν₀=6.83×10¹⁴ Hz, further supports such relaxor nature. The slim P-E hysteresis loop and ‘butterfly’ shape dc bias field dependence of permittivity at T>T_m (T_m, the temperature of permittivity maximum) clearly signifies the occurrence of nanopolar clusters, which is the typical characteristic of ferroelectric relaxor. At 300 K and 10 kHz, the dielectric constant and loss tan δ are ∼1100 and 0.0015, respectively. The high tunability (∼25%) and figure of merit (∼130) at room temperature show that the BSZT ceramics could be a promising candidate for tunable capacitor applications.     

Ferroelectric relaxor behaviour in Pb(Fe0.5Ta0.5)O3

The relaxor ferroelectric lead iron tantalate, Pb(Fe_0.5Ta_0.5)O₃ (PFT) is synthesized by Coulombite precursor method. The X-ray diffraction pattern of the sample at room temperature shows a cubic phase. The field dependence of dielectric response is measured in a frequency range 0.1 kHz — 1 MHz and in a temperature range from 173–373 K. The temperature dependence of permittivity (ɛ′) shows broad maxima at various frequencies. The frequency dependence of the permittivity maximum temperature (T _m ) has been modelled using Vogel-Fulcher relation.      

Influence of B2O3 on electrical properties and phase transition of lead-free Ba(Ti0.9Sn0.1)O3 ceramics

The phase transition and electrical properties of Ba(Ti_0.9Sn_0.1)O₃ ceramics with B₂O₃ added were investigated to explore the effect of B₂O₃ addition on enhanced densification and dielectric constant of these ceramics. With increasing B₂O₃ content, a linear reduction of ferroelectric to paraelectric transition temperature was observed. In addition, higher B₂O₃ concentrations enhanced a ferroelectric relaxor behavior in the ceramics. Changes in this behavior were related to densification, second-phase formation and compositional variation of the ceramics.     

Pb(Zr,Sn,Ti)O3反铁电陶瓷的低温相变扩散与极化弛豫

用弱场介电温谱、热释电流谱、强场电滞回线和变温X射线衍射谱研究了微量La掺杂Pb(Zr ,Sn ,Ti)O3(PZST)反铁电 (AFEt)陶瓷在 - 10 0— 180℃温区内的结构与电学特性 .弱场介电温谱显示 ,AFEt陶瓷在低温段(- 10 0— 5 0℃ )呈现介电频率弥散 (0 1— 10 0kHz)和扩散型相变的特征 ,而变温X射线衍射谱却表明材料在这一温区内保持四方相结构 ;低温下经强场作用后 ,AFEt被诱导为亚稳三方铁电态 ,介电频率弥散消失 .基于多元复杂化合物的组分起伏理论 ,讨论了PZSTAFEt陶瓷的相变扩散与极化弛豫新现象 .     

Dielectric studies of the phase transition in {N(CH3)4}2HgCl4

Dielectric properties of single-crystal {N(CH₃)₄}₂HgCl₄ (structure at room temperature; orthorhombic Pmcn) have been measured in a temperature range from 4 K to about 370 K. The dielectric constant along the a-, b-, and c-axes shows a break at 278 K. No other anomalies are detected in the temperature range studied. The transition temperature increases linearly with increasing hydrostatic pressure at a rate of 0.20 K/MPa. Twin boundaries are observed in the low-temperature phase on b-plate specimens. The results indicate that the phase transition in {N(CH₃)₄}₂HgCl₄ is ferroelastic, as in {N(CH₃)₄}₂XBr₄ (X: Mn, Co, Zn).