Effect of Y2O3 addition on the conductivity and elastic modulus of (CeO2)1 − x(YO1.5)x

The conductivity and elastic modulus of (CeO₂)_1 − x(YO_1.5)_x for x values of 0.10, 0.15, 0.20, 0.30, and 0.40 were investigated by experiments and molecular dynamics simulations. The calculated conductivity exhibited a maximum value at approximately 15 mol% Y₂O₃; this trend agreed with that of the experimental results. In order to clarify the reason for the occurrence of the maximum conductivity, the paths for the transfer of oxygen vacancies were counted. The numerical result revealed that as the content of Y₂O₃ dopant increases, the number of paths for the transfer of oxygen vacancies decreases, whereas the number of oxygen vacancies for conductivity increases. Thus, the trade-off between the increase in the number of vacancy sites and the decrease in the vacancy transfer was considered to be the reason for the maximum conductivity occurring at the Y₂O₃ dopant content of approximately 15 mol%. The calculated elastic modulus also exhibited a minimum value at approximately 20 mol% Y₂O₃, which also agreed with the experimental results. It was shown that the Y–O–Y bonding energy increased with the increasing content of Y₂O₃ dopant. Thus, the trade-off between the increase in the number of vacancy sites and that in the Y–O–Y bonding energy was considered to be the reason for the minimum elastic modulus occurring at the Y₂O₃ dopant content of approximately 20 mol%.     

Defect chemical and statistical thermodynamic studies on oxygen nonstoichiometric Nd2 − xSrxNiO4 + δ

In order to elucidate how oxygen content changes in Nd_2 − xSr_xNiO_4 + δ (x = 0, 0.2, 0.4), defect chemical and statistical thermodynamic analyses were carried out. The relationship among δ, P(O₂), and T were analyzed by a defect equilibrium model. Since Nd_2 − xSr_xNiO_4 + δ shows metal like band conduction at high temperatures, chemical potential of hole is expressed by the integration of the Fermi-Dirac distribution function and the density of state. The nonstoichiometric variation of oxygen content in Nd_2 − xSr_xNiO_4 + δ can be explained by the defect equilibrium model with a regular solution approximation. Partial molar entropy and partial molar enthalpy of oxygen are calculated from the nonstoichiometric data and Gibbs–Helmholtz equation. The relationship among defect structure, defect equilibrium, and thermodynamic quantities is elucidated by the statistical thermodynamic model. Thermodynamic quantities are calculated by the statistical thermodynamic model with the results of defect chemical analysis and compared with those obtained from experimental results. Thermodynamic quantities calculated by the statistical thermodynamic model can explain rough tendency of those obtained from the δ–T–P(O₂) relationship.     

Lithium ion conductive glass–ceramics with Li3Fe2(PO4)3 and YAG laser-induced local crystallization in lithium iron phosphate glasses

The glasses with the composition of 37.5Li₂O–(25 − x)Fe₂O₃–xNb₂O₅–37.5P₂O₅ (mol%) (x = 5,10,15) are prepared, and it is found that the addition of Nb₂O₅ is effective for the glass formation in the lithium iron phosphate system. The glass–ceramics consisting of Nasicon-type Li₃Fe₂(PO₄)₃ crystals with an orthorhombic structure are developed through conventional crystallization in an electric furnace, showing electrical conductivities of 3 × 10^− 6 Scm^− 1 at room temperature and the activation energies of 0.48 eV (x = 5) and 0.51 eV (x = 10) for Li⁺ ion conduction in the temperature range of 30–200 °C. A continuous wave Nd:YAG laser (wavelength: 1064 nm) with powers of 0.14–0.30 W and a scanning speed of 10 μm/s is irradiated onto the surface of the glasses, and the formation of Li₃Fe₂(PO₄)₃ crystals is confirmed from XRD analyses and micro-Raman scattering spectra. The crystallization of the precursor glasses is considered as new route for the fabrication of Li₃Fe₂(PO₄)₃ crystals being candidates for use as electrolyte materials in lithium ion secondary batteries.     

Conductivity and water uptake of Sr4(Sr2Nb2)O11·nH2O and Sr4(Sr2Ta2)O11·nH2O

The hydrated oxygen deficient complex perovskite-related materials Sr₄(Sr₂Nb₂)O₁₁·nH₂O and Sr₄(Sr₂Ta₂)O₁₁·nH₂O were studied at high water vapour pressures over a large temperature range by electrical conductivity measurements, thermogravimetry (TG), and X-ray powder diffraction (XRPD). In humid atmospheres both materials are known to exhibit protonic conductivity below dehydration temperatures, with peak-shaped maxima at about 500 °C. In this work we show that the peaks expand to plateaus of high conductivity from 500 to 700 °C at a water vapour pressure of 1 atm. However, in situ synchrotron XRPD of Sr₄(Sr₂Nb₂)O₁₁·nH₂O as a function of temperature shows that these observations are in fact coincident with melting and dehydration of a secondary phase Sr(OH)₂. The stability of Sr₄(Sr₂Nb₂)O₁₁·nH₂O and Sr₄(Sr₂Ta₂)O₁₁·nH₂O in humid atmospheres is thus insufficient, causing decomposition into perovskites with lower Sr content and SrO/Sr(OH)₂ secondary phases. This, in turn, rationalizes the observation of peaks and plateaus in the conductivity of these materials.     

Ab initio study of the chemical states of water on Cr2O3(0 0 0 1): From the isolated molecule to saturation coverage

The reactivity of the (0 0 0 1)-Cr–Cr₂O₃ surface towards water was studied by means of periodic DFT + U. Several water coverages were studied, from 1.2H₂O/nm² to 14.1H₂O/nm², corresponding to ¼, 1, 2 and 3 water/Cr at the (0 0 0 1)-Cr₂O₃ surface, respectively. With increasing coverage, water gradually completes the coordination sphere of the surface Cr atoms from 3 (dry surface) to 4 (1.2 and 4.7H₂O/nm²), 5 (9.4H₂O/nm²) and 6 (14.1H₂O/nm²). For all studied coverages, water replaces an O atom from the missing above plane. At coverages 1.2 and 4.7H₂O/nm², the Cr–O_s (surface oxygen) acid–base character and bond directionality govern the water adsorption. The adsorption is molecular at the lowest coverage. At 4.7H₂O/nm², molecular and dissociative states are isoenergetic. The activation energy barrier between the two states being as low as 12 kJ/mol, allowing protons exchanges between the OH groups, as evidenced by ab inito molecular dynamics at room temperature. At coverages of 9.4 and 14.1H₂O/nm², 1D- (respectively, 2D-) water networks are formed. The resulting surface terminations are –Cr(OH)₂ and –Cr(OH)₃– like, respectively. The increased stability of those terminations as compared to the previous ones are due to the stabilization of the adsorbed phase through a H-bond network and to the increase in the Cr coordination number, stabilizing the Cr (t_2g) orbitals in the valence band. An atomistic thermodynamic approach allows us to specify the temperature and water pressure domains of prevalence for each surface termination. It is found that the –Cr(OH)₃-like, –Cr(OH)₂ and anhydrous surfaces may be stabilized depending on (T, P) conditions. Calculated energies of adsorption and OH frequencies are in good agreement with published experimental data and support the full hydroxylation model, where the Cr achieves a 6-fold coordination, at saturation.     

Effect of Ca doping on the superconducting properties of GdBaSrCu3O7−δ bulk samples

Gd_1−xCa_xBaSrCu₃O_7−δ samples (0  x  0.1) were prepared via solid-state reaction. Four-point probes method was used for resistance versus temperature measurements. Results show decrease in T_c by increasing x content. This variation is assumed to be irrelevant to the different phases or impurity effects since X-ray patterns show all samples are tetragonal single-phase. Ca doping decreases the oxygen content and lattice parameters of the samples. It is suggested that Ca prevents the dislocation of oxygen, and then disrupts the hole concentration of the system and antiferromagnetic correlation at CuO₂ planes. Subsequently, destroys the superconductivity of the samples.     

Li mobility in Li0.5 − xNaxLa0.5TiO3 perovskites (0 ≤ x ≤ 0.5): Influence of structural and compositional parameters

The dependence of Li mobility on structure and composition of Li_0.5 − xNa_xLa_0.5TiO₃ perovskites (0 ≤ x ≤  0.5) has been investigated by means of neutron diffraction, nuclear magnetic resonance and impedance spectroscopy. At 300 K, all samples display a rhombohedral superstructure (R-3c S.G.), where octahedra are out of phase tilted along [111] direction of the ideal cubic cell. The elimination of the octahedral tilting is responsible for the rhombohedral–cubic transformation, detected near 1000 K. In these perovskites, La and Na cations are randomly distributed in A sites, but Li ions are fourfold coordinated at unit cell faces of the cubic perovskite. Lithium conductivity, σ_300 K, decreases with the sodium content, decreasing from values typical of fast ionic conductors, 10^− 3 S/cm, to those of good insulators, 10^− 10 S/cm, when the interconnectivity between vacant A sites is lost (x > 0.3). In samples with x < 0.3, dc conductivity displays a non-Arrhenius behaviour, decreasing activation energy from ~ 0.37 to 0.25 eV when the sample is heated between 77 and 500 K. The temperature dependence of B_Li factors shows the existence of two regimes for Li motion. Below 373 K, Li ions remain partially located near square oxygen windows that connect contiguous A sites, but above 400 K, extended Li motions become dominant. The additional decrease of activation energy from 0.25 to 0.16 eV (low-temperature ⁷Li NMR value), should require the full elimination of octahedral tilting which is only produced above 1000 °C.     

The (γ,p) reaction in Au

Proton energy spectra of the ¹⁹⁷Au(e,p) reaction were measured in the region between 17 and 30 MeV at three angles: 40°, 90° and 140°. Two prominent bumps were observed in the (γ,p) spectra converted using virtual photon theory. The higher-energy bump shifts with photon energies and the lower-energy one stays at 10.5 MeV. The higher-energy bump is much larger at 40° than at 140°; on the contrary the angular dependence of the lower-energy bump is small. Neither bump can be described by a statistical calculation. A calculation of a microscopic shell model shows that the lower-energy bump is attributed to the decay of proton-particle–neutron-hole pairs in the T_> states, leaving a neutron hole around the Fermi surface. The higher-energy bump can be ascribed to the direct–semidirect mechanism. This paper gives the solution to a part of the long-standing question about the origin of photo-proton emission in heavy nuclei.     

Effect of BiFeO3 addition on Bi2O3–ZnO–Nb2O5 based ceramics

In this paper, low temperature sintering of the Bi₂(Zn_1/3Nb_2/3)₂O₇ (β-BZN) dielectric ceramics was studied with the use of BiFeO₃ as a sintering aid. The effects of BiFeO₃ contents and the sintering temperature on the phase structure, density and dielectric properties were investigated. The results showed that the sintering temperature could be decreased and the dielectric properties could be retained by the addition of BiFeO₃. The structure of BiFeO₃ doped β-BZN was still the monoclinic pyrochlore phase. The sintering temperature of BiFeO₃ doped β-BZN ceramics was reduced from 1000 °C to 920 °C. In the case of 0.15 wt.% BiFeO₃ addition, the β-BZN ceramics sintered at 920 °C exhibited good dielectric properties, which were listed as follows: ε_r = 79 and tan δ = 0.00086 at a frequency of 1 MHz. The obtained properties make this composition to be a good candidate for the LTCC application.     

Microwave dielectric properties of (1 − x)(Mg0.95Co0.05)TiO3–x(Na0.5La0.5)TiO3 ceramic system

The microstructures and the microwave dielectric properties of the (1 − x)(Mg_0.95Co_0.05)TiO₃–x(Na_0.5La_0.5)TiO₃ ceramic system were investigated. Two-phase system was confirmed by the XRD patterns and the EDX analysis. A co-existed second phase (Mg_0.95Co_0.05)Ti₂O₅ was also detected. The microwave dielectric properties are strongly related to the density and the matrix of the specimen. A new microwave dielectric material 0.88(Mg_0.95Co_0.05)TiO₃–0.12(Na_0.5La_0.5)TiO₃, possessing an excellent combination of dielectric properties: ε_r  22.36, Q × f  110,000 GHz (at 9 GHz), τ_f  2.9 ppm/°C), is proposed as a candidate dielectric for GPS patch antennas.     

Oxide ion conductivity and relaxation in CaREZrNbO7 (RE = La, Nd, Sm, Gd, and Y) system

CaREZrNbO₇ (RE = La, Nd, Sm, Gd and Y) system changed from fluorite (F)-type to pyrochlore (P)-type structure when the ionic radius ratios, r(Ca²⁺–RE³⁺)_av/r(Zr⁴⁺–Nb⁵⁺)_av were larger than 1.34. Thus, the La, Nd, and Sm compounds have a cubic P-type structure and the Gd and Y ones have a defect F-type structure. The electrical conductivity was measured using complex-plane impedance analysis over a wide temperature (300–750 °C) and frequency (1 Hz–1 MHz) ranges. The conductivity relaxation phenomenon was observed in these compounds and the relaxation frequencies were found to show Arrhenius-type behavior and activation energies were in good agreement with those obtained from high temperature conductivity plots. These results support the idea that the relaxation process and the conductivity have the same origin. The ionic conductivity of CaREZrNbO₇ (RE = La, Nd, Sm, Gd and Y) system showed the maximum at the phase boundary between the F-type and P-type phases. On the other hand, the activation energy for the conduction decreased in the F-type phase and increased in the P-type phase with increasing ionic radius ratio. Among the prepared compounds, CaGdZrNbO₇ showed the highest ionic conductivity of 9.47 × 10^− 3 S/cm at 750 °C which was about twice as high as that observed in Gd₂Zr₂O₇ (4.2 × 10^− 3 S/cm at 800 °C). The grain morphology observation by scanning electron microscope (SEM) showed well-sintered grains. AC impedance measurements in various atmospheres further indicated that they are predominantly oxide ion conductors at elevated temperatures (> 700 °C).     

Reduced anti-ferromagnetism promoted by Zn 3d substitution at CuO2 planar sites of Cu0.5Tl0.5Ba2Ca3Cu4O12−δ superconductors

The role of charge carriers in ZnO₂/CuO₂ planes of Cu_0.5Tl_0.5Ba₂Ca₃Cu_4−yZn_yO_12−δ material in bringing about superconductivity has been explained. Due to suppression of anti-ferromagnetic order with Zn 3d¹⁰ (S=0) substitution at Cu 3d⁹ sites in the inner CuO₂ planes of Cu_0.5Tl_0.5Ba₂Ca₃Cu₄O_12−δ superconductor, the distribution of charge carriers becomes homogeneous and optimum, which is evident from the enhanced superconductivity parameters. The decreased c-axis length with the increase of Zn doping improves interlayer coupling and hence the three dimensional (3D) conductivity in the unit cell is enhanced. Also the softening of phonon modes with the increased Zn doping indicates that the electron–phonon interaction has an essential role in the mechanism of high-T_c superconductivity in these compounds.     

Growth and properties of air-processed GdBa2Cu3O7−δ superconductors with fined Gd2BaCuO5 and Gd2Ba4CuFeOy additions

We have succeeded in synthesizing a powder form of Gd₂Ba₄CuFeO_y (Gd2411) in air. GdBa₂Cu₃O_7−δ (Gd123)/Gd₂BaCuO₅ (Gd211) precursor powders added with different amounts of Gd₂Ba₄CuFeO_y (x = 0, 0.002, 0.004, 0.02) in molar ratio to Gd123 have been fabricated successfully into the form of large, single grains by the top seeded melt growth (TSMG) process. The relation between the additions amounts of Gd2411/Gd211 and critical current density (J_C) was analyzed. We found Gd2411 particles stably exist in the Gd123 matrix without degradation of superconducting properties owing to the existence of the Fe magnetic ion. The trapped field was observed to increase significantly compared with the bulk without Gd2411 additions.     

Electrical and mechanical properties of proton conducting SrCe0.95Yb0.05O3 − α

Yb³⁺-doped ceramic strontium cerate of exactly the composition SrCe_0.95Yb_0.05O_{3 − α} was prepared, having a relative density of 99.0 (± 0.3%). Great care was taken to obtain homogeneous, carbonate free material. Analysis are made of the X-ray powder diffraction pattern of the as-prepared dense ceramic, resulting in the orthorhombic unit cell parameters a = 6.997(2) Å, b = 12.296(3) Å, c = 8.588(2) Å, Z = 8 and d_x = 5.806(2) g cm⁻³. Bending strength values of the ceramic in non-proton and proton conducting state are found to be 177 and 194 MPa respectively. The ceramic kept under proton conducting conditions for 500 h at 300 °C to 800 °C in a N₂ flow containing 155 mbar water vapour and 245 mbar H₂, have shown to remain chemically and structurally stable. Impedance spectroscopy measurements of the bulk conductivity of the proton conducting ceramic revealed an activation energy of 53.2 kJ mol⁻¹ and a preexponential factor of 359.1 (Ω cm)⁻¹ K. In the non-proton conducting state the ceramic is mainly oxygen ion vacancy conducting, which indicates that charge compensation on substituting Yb⁺³ in SrCeO₃ takes place by oxygen ion vacancies.     

Thermal stability, oxygen non-stoichiometry and transport properties of LaNi0.6Fe0.4O3

Thermal stability, oxygen non-stoichiometry and electrical conductivity of LaNi_0.6Fe_0.4O_3−δ were investigated in the temperature region of 20-1000 °C in Ar/O₂ gas flows at oxygen partial pressures between 0.5 and 21,000 Pa. Diffusion mobility was measured in Ar/O₂ gas flow at pO₂ = 18 Pa. Crystal structure of this compound was found to be stable at the mentioned experimental conditions. LaNi_0.6Fe_0.4O_3−δ is a p-type semiconductor with metallic type conductivity above 150 °C at the investigated pO₂ range. Two different (fast and slow) oxygen exchange areas on the temperature-pO₂ diagram were established, which are due to two different oxygen anion positions in the double B-site mixed perovskite structure. Oxygen non-stoichiometry in the fast oxygen exchange region reaches about 0.005 of oxygen atomic index. Chemical diffusion and oxygen surface exchange coefficients do not vary at 600-800 °C, but show visible increase above 800-850 °C.     

Preparation and electrical properties of a pyrochlore-related Ce2Zr2O8−x phase

A pyrochlore-related Ce₂Zr₂O_8−x phase has been prepared in a reduction reoxidation process from Ce_0.5Zr_0.5O₂ powders. Ce₂Zr₂O_8−x, based on a cubic symmetry with a=1.053 nm, decomposes in nitrogen at 800 °C, but remains stable up to 900 °C in air. It shows mixed oxygen ionic and electronic conductivity. The bulk conductivity at 700 °C is 4×10⁻⁴ S cm⁻¹ in air and 1×10⁻² S cm⁻¹ in nitrogen, and the activation energy is 1.27 eV in air. In nitrogen, the Arrhenius law is not obeyed, and a curved plot was obtained from 400 to 700 °C; then, the conductivity decreased rapidly due to the thermal decomposition of Ce₂Zr₂O_8−x.     

Preparation and properties of composite ceramic coating containing Al2O3–ZrO2–Y2O3 on AZ91D magnesium alloy by plasma electrolytic oxidation

A composite ceramic coating containing Al₂O₃–ZrO₂–Y₂O₃ was successfully prepared on AZ91D magnesium alloy by plasma electrolytic oxidation (PEO) technique in an alkaline aluminate electrolyte. The morphology, elemental and phase composition, corrosion behavior and thermal stability of the uncoated and coated samples were studied by environmental scanning electron microscopy (ESEM), energy dispersive X-ray spectrometer (EDS), X-ray diffractometer (XRD), electrochemical corrosion test, high temperature oxidation test and thermal shock test. The results showed that the composite ceramic coating was composed of Al₂O₃, c-ZrO₂, t-ZrO₂, Y₂O₃ and some magnesium compounds, such as MgO, MgF₂ and MgAl₂O₄. After PEO treatment, the corrosion potential of AZ91D alloy was increased and the corrosion current density was significantly reduced. Besides, the coated magnesium alloys also showed excellent high temperature oxidation resistance and thermal shock resistance at 500 °C environment.     

GaAs(0 0 1) (2 × 4) to c(4 × 4) transformation observed in situ by STM during As flux irradiation

Atomic resolution scanning tunnelling microscopy (STM) has been used to study in situ the As-terminated reconstructions formed on GaAs(0 0 1) surfaces in the presence of an As₄ flux. The relationship between the As-rich (2 × 4) and c(4 × 4) surfaces is observed throughout the gradual evolution of the reconstruction transformation. The results suggest that during the initial stage of the transformation, Ga-rich As-terminated variations of the c(4 × 4) form in order to accommodate excess mobile Ga produced by pit formation. These transient structures later planarize, as excess Ga is incorporated at step/island edges. Successive imaging of the same sample area during As₄ irradiation allows point-by-point adatom binding to be analysed in a way inaccessible to MBE–STM systems relying on sample quenching and transfer.     

Conversion of egg shell membrane to inorganic porous CexZr1−xO2 fibrous network

The binary system CeO₂–ZrO₂ is thermally stable and has superior reduction–oxidation properties. It has been commonly used in the three-way catalytic converters for automobiles. In this work, an inorganic biomorphic porous Ce_xZr_1−xO₂ fibrous network was successfully synthesized by using the egg shell membrane (ESM) as templates, and its morphology was a perfect replica of the original ESM. The synthesis involved a simple infiltration and calcination process. A fresh ESM was peeled from a chicken egg shell. It was soaked in a Ce(NO₃)₃ and Zr(NO₃)₄ mixture before it was calcined at 700 °C in ambient environment. The fibers in the biomorphic network had diameter ranged from 1 to 4 μm, and they were composed of Ce_xZr_1−xO₂ nanocrystallites having an average grain size of 10 nm.     

Temperature dependence of the indirect band gap, steepness parameter and related optical constants of [Kx(NH4)1−x]2ZnCl4 mixed crystals

Optical transmittance measurements near the absorption edge of [K_x(NH₄)_1−x]₂ZnCl₄ mixed crystals, where x=0.00, 0.232, 0.522, 0.644, 0.859 and 1.00, are reported over 276–350 K range. Analysis reveals that the type of transition is the indirect allowed one. The absorption edge shifted towards lower energy with increasing temperature. It is shown that [K_x(NH₄)_1−x]₂ZnCl₄ mixed crystals with x0.644 reveal a phase transition at 319 K, this phase disappeared at high concentrations of K⁺ ions. The steepness parameter is given, its value is used to estimate the temperature dependence of the indirect energy gap. In the region of the absorption edge, the absorption coefficient obeys Urbach's rule. Urbach parameters are investigated as a function of temperature.