Characterization of optical and nonlinear optical properties of silver nanoparticles prepared by laser ablation in various liquids

The optical, structural, and nonlinear optical properties of silver nanoparticles prepared by laser ablation in various liquids were investigated at 397.5, 532, and 795 nm. The TEM and spectral measurements have shown temporal dynamics of size distribution of Ag nanoparticles in solutions. The thermal-induced self-defocusing dominated in the case of high pulse repetition rate as well as in the case of nanosecond pulses. In the case of low pulse repetition rate, the self-focusing (γ = 3 × 10⁻¹³ cm² W⁻¹) and saturated absorption (β = −1.5 × 10⁻⁹ cm W⁻¹) of picosecond and femtosecond radiation were observed in these colloidal solutions. The nonlinear susceptibility of Ag nanoparticles ablated in water was measured to be 5 × 10⁻⁸ esu (at λ = 397.5 nm).     

Visible photoluminescence from a-Si : H/SiO2 superlattices fabricated by UHV evaporation

Hydrogenated amorphous-Si/SiO₂ (a-Si:H/SiO₂) superlattices with different a-Si : H thickness in the range of a few nanometers have been fabricated by ultra high vacuum evaporator (UHV evaporator). The photoluminescence (PL) of our superlattices is observed in the visible spectral region and the peak energy shifts to higher energy as the a-Si : H layer thickness decreases. The temperature dependence of the PL spectra reveals four sub-bands by fitting. Bands at 2.2, 1.9, 1.65 and 1.45 eV are detected and are attributed to E′δ centers, nonbridging-oxygen–hole centers (NBOHC), Si/SiO₂ interface and a-Si : H layer, respectively. We explain the overall blueshift of the PL spectra by the modification of the contribution of these sub-bands.     

Transport properties of SrCe0.95Y0.05O3−δ and its application for hydrogen separation

Transport properties of SrCe_0.95Y_0.05O_3−δ were studied by impedance spectroscopy and by measuring open-cell voltage (OCV) and gas permeation. Ionic transference numbers were determined by measuring the OCV of concentration cells and water vapor evolution of an O₂/H₂ fuel cell. We observed interfacial polarization on the basis of the I–V curves obtained by discharging a hydrogen concentration cell or an O₂/H₂ fuel cell. The observed high protonic conductivity (high proton and low oxide ion transference numbers) makes SrCe_0.95Y_0.05O_3−δ a potential material for hydrogen separation. From proton conductivity measurements, under a given hydrogen partial pressure difference of 4%/0.488%, the hydrogen permeation rate (of a dense membrane with 0.11 cm in thickness) was calculated to be ≈0.072 cm³ (STP) cm⁻² min⁻¹ at 800°C, whereas the permeation rate calculated from short-circuit current measurements was ≈0.023 cm³ (STP) cm⁻² min⁻¹ at 800°C. The difference between calculated and observed permeation rates is probably due to interfacial polarization.     

Electron–hole liquid formation by exciton and biexciton resonant excitation in CuCl

The dynamics of a cold photoexcited electron–hole system created by resonant excitation with picosecond optical pulses are studied by time-resolved emission and pump–probe measurements. A rapid build-up of strong metallic reflection in the mid-infrared region was observed, which indicates the creation of electron–hole plasma via the exciton or biexciton Mott transition. Transient reflection spectra clearly show the transformation of high-density electron–hole plasma into a metallic colloid-like state within 10 ps. In the meantime, broad plasma emission turns to a narrow emission band, in which the spectral profile does not change within several tens of picoseconds. These features in the emission spectra disappear when switched to the band-to-band excitation. An analysis of the reflection and emission spectra reveals that the density of metastable electron–hole liquid is as high as 10²⁰ cm⁻³. This indicates that the plasma formation via the Mott transition is crucial to eliminate excess heating for reaching the low-temperature states of an electron–hole ensemble.     

Study of effects of Mn in CdS nanocrystals

Mn²⁺-doped CdS nanocrystals have been synthesized by adopting an aqueous solution precipitation method. These nanocrystals have been studied using X-ray diffraction (XRD), X-ray fluorescence (XRF), optical absorbance, photoluminescence (PL), DC electrical conductivity measurements and positron annihilation lifetime spectroscopy (PALS). The system has been found to be in the hexagonal phase. PL spectra have been studied on most prominent exciton peaks within the wavelength range (586–731 nm). The emission intensity is found to increase on increasing Mn²⁺ ion concentration (0–5%). Electrical conductivity lies within 0.819×10⁻⁶ to 1.69×10⁻⁶ Ω⁻¹ m⁻¹ and the system shows power law dependence for n=3–3.77. The Cd vacancies concentration has been found to decrease on increasing Mn%.     

Domain wall pinning in polycrystalline perovskite La0.7Sr0.3MnO3

Reversible and irreversible domain wall (DW) motions have been investigated in La_0.7Sr_0.3MnO₃ ceramic samples using frequency-response complex permeability with various amplitudes of AC field. We also examine the effects of temperature in the range from 293 to 368 K and transverse DC magnetic field with a maximum of 4.40×10⁵ A/m on the real part of permeability (μ′). Two relaxations corresponding to reversible wall motions and domain rotations occur in low and high frequency regions, respectively. The irreversible DW displacements can be activated as the amplitude larger than the pinning field of 3 A/m, leading to an increase in μ′. The μ′ obeys a Rayleigh law at the temperature below 343 K or under DC field of less than 4.22×10⁴ A/m. The Rayleigh constant η increases from 5.45×10⁻² to 1.54×10⁻¹ (A/m)⁻¹ as the temperature rises from 293 to 343 K, and η decreases from 5.58×10⁻² to 3.67×10⁻² (A/m)⁻¹ with increasing DC field from 1.99×10³ to 4.22×10⁴ A/m.     

Density, viscosity and ultrasonic velocity studies of aqueous solutions of sodium acetate at different temperatures

The densities and viscosities of aqueous solutions of sodium acetate have been measured at 298.15, 303.15, 308.15 and 313.15 K and at atmospheric pressure. The molality range has been studied between 6.09 × 10^− 2 to 7.314 × 10^− 1 mol kg^− 1. The experimental values of density have been used to calculate apparent molar volume, partial molar volume, solute–solute interaction parameter, and Hepler's constant. The viscosity data have been analyzed with Jone–Dole equation. Furthermore, ultrasonic velocity measurements of aqueous solutions of sodium acetate have been made at 298.15 and 308.15 K and at atmospheric pressure. From experimental values of ultrasonic velocity, apparent molar isentropic compressibility and limiting apparent molar isentropic compressibility have been calculated. All the parameters calculated from density, viscosity, and ultrasonic velocity indicate that the sodium acetate is water structure maker.     

Experimental research into the cavitation noise spectrum in water solutions of high molecular weight polymers

The paper presents cavitation noise spectrum measurements results for water and a water solution of polyacryloamide with the 1.5 × 10⁷ g mol⁻¹ particle mass. Cavitation noise spectrum characteristics were shown for different ultrasound intensity, with different sonification times (at a constant ultrasound intensity) as well as characteristics which enable comparing particular sonification parameters.     

Analysis of frequency-dependent series resistance and interface states of In/SiO2/p-Si (MIS) structures

In this work, the investigation of the interface state density and series resistance from capacitance–voltage (C–V) and conductance–voltage (G/ω−V) characteristics in In/SiO₂/p-Si metal–insulator–semiconductor (MIS) structures with thin interfacial insulator layer have been reported. The thickness of SiO₂ film obtained from the measurement of the oxide capacitance corrected for series resistance in the strong accumulation region is 220 Å. The forward and reverse bias C–V and G/ω−V characteristics of MIS structures have been studied at the frequency range 30 kHz–1 MHz at room temperature. The frequency dispersion in capacitance and conductance can be interpreted in terms of the series resistance (R_s) and interface state density (D_it) values. Both the series resistance R_s and density of interface states D_it are strongly frequency-dependent and decrease with increasing frequency. The distribution profile of R_s–V gives a peak at low frequencies in the depletion region and disappears with increasing frequency. Experimental results show that the interfacial polarization contributes to the improvement of the dielectric properties of In/SiO₂/p-Si MIS structures. The interface state density value of In/SiO₂/p-Si MIS diode calculated at strong accumulation region is 1.11×10¹² eV⁻¹ cm⁻² at 1 MHz. It is found that the calculated value of D_it (≈10¹² eV⁻¹ cm⁻²) is not high enough to pin the Fermi level of the Si substrate disrupting the device operation.     

Structural and electrical properties of crystalline (1−x)Ta2O5−xTiO2 thin films fabricated by metalorganic decomposition

Polycrystalline (1−x)Ta₂O₅−xTiO₂ thin films were formed on Si by metalorganic decomposition (MOD) and annealed at various temperatures. As-deposited films were in the amorphous state and were completely transformed to crystalline after annealing above 600 °C. During crystallization, a thin interfacial SiO₂ layer was formed at the (1−x)Ta₂O₅−xTiO₂/Si interface. Thin films with 0.92Ta₂O₅–0.08TiO₂ composition exhibited superior insulating properties. The measured dielectric constant and dissipation factor at 1 MHz were 9 and 0.015, respectively, for films annealed at 900 °C. The interface trap density was 2.5×10¹¹ cm⁻² eV⁻¹, and flatband voltage was −0.38 V. A charge storage density of 22.8 fC/μm² was obtained at an applied electric field of 3 MV/cm. The leakage current density was lower than 4×10⁻⁹ A/cm² up to an applied electric field of 6 MV/cm.     

Z-scan determination of the third-order optical nonlinearity of a triphenylmethane dye using 633 nm He–Ne laser

The third-order nonlinear optical response of a triphenylmethane dye (Acid blue 7) was studied using the Z-scan technique with a continuous-wave He–Ne laser radiation at 633 nm. The magnitude and sign of the third-order nonlinear refractive index n₂ of aqueous solution of Acid blue 7 dye were determined; the negative sign indicates a self-defocusing optical nonlinearity in the sample studied. The negative nonlinear refractive index n₂ and nonlinear absorption coefficient β were estimated to be −1.88 × 10⁻⁷ cm²/W and −3.08 × 10⁻³ cm/W, respectively, corresponding to Re(χ⁽³⁾) = −8.35 × 10⁻⁶ esu, and Im(χ⁽³⁾) = −6.88 × 10⁻⁷ esu. The experimental results show that Acid blue 7 dye have potential applications in nonlinear optics.     

Formation of high-density hexagonal networks of InGaAs ridge quantum wires by atomic hydrogen-assisted selective molecular beam epitaxy

Feasibility of growth of InGaAs ridge quantum wire (QWR) hexagonal network structures by atomic hydrogen (H^*)-assisted selective molecular beam epitaxy (MBE) is investigated for use in novel hexagonal quantum circuits based on the binary-decision diagram (BDD) architecture. The fabricated structures were characterized in detail by SEM, AFM, PL and CL measurements.

By using patterned substrates with mesa-pattern directions of 1 0 0– and 5 1 0– together with optimized H^*-assisted selective MBE, hexagonal networks of the sharp and uniform InGaAs ridge structures were realized down to submicron pitches. Embedded InGaAs QWR hexagonal networks were successfully formed on the ridge structures, giving prospects of realizing a node device density lager than 10⁸ cm⁻².     

Optical constants of Tl4Ga3InSe8 layered single crystals

The optical properties of Tl₄Ga₃InSe₈ layered single crystals have been studied by means of transmission and reflection measurements in the wavelength range of 500–1100 nm. The analysis of the room temperature absorption data revealed the presence of both optical indirect and direct transitions with band gap energies of 1.94 and 2.20 eV, respectively. Transmission measurements carried out in the temperature range of 10–300 K revealed that the rate of change of the indirect band gap with temperature is γ=−4.1×10⁻⁴ eV/K. The absolute zero value of the band gap energy was obtained as E_gi(0)=2.03 eV. The dispersion of the refractive index is discussed in terms of the Wemple–DiDomenico single-effective-oscillator model. The refractive index dispersion parameters: oscillator energy, dispersion energy, oscillator strength and zero-frequency refractive index were found to be 4.10 eV, 23.17 eV, 6.21×10¹³ m⁻² and 2.58, respectively. From X-ray powder diffraction study, the parameters of monoclinic unit cell were determined.     

Dislocation-related luminescence in Er-implanted silicon

The behavior of luminescence spectra and structural defects in single crystal Czochralski silicon after erbium implantation at 1–1.8 MeV energies and 1×10¹³ cm⁻² dose with subsequent annealing at 1000–1200°C for 0.25–3 h in argon and a chlorine-containing ambience (CCA) was studied by photoluminescence (PL), transmission electron microscopy and chemical etching/Nomarski microscopy. We have found that annealing in CCA gives rise to dislocation loops and pure edge dislocations with dominant dislocation-related lines in the PL spectrum. Pure edge dislocations are responsible for the appearance of the lines.     

Methane mobility in carbon nanotubes

Quasi-elastic neutron scattering has been used to characterize the diffusivity of CH₄ molecules condensed in single-wall carbon nanotubes. It is shown that the two sites of adsorption, previously observed by adsorption volumetry and calorimetry measurements, correspond to a solid-like phase for the more strongly bound site at T<120 K and to a liquid-like component for the more weakly bound site at 70<T<120 K. The diffusion coefficients of the mobile molecules range between 3×10⁻⁷ to 15×10⁻⁷ cm² s⁻¹. The fraction of this viscous liquid diminishes as the temperature is decreased; the adsorbate is fully solidified at 50 K and below.     

The origin of photoluminescence in Ge-implanted SiO2 layers

Ge ions were implanted at 100 keV with 3×10¹⁶ cm⁻² into a 300  nm thick SiO₂ layer on Si. Visible photoluminescence (PL) around 2.1 eV from an as-implanted sample is observed, and faded out by subsequent annealing at 900°C for 2 h. However, PL shows up again after annealing above 900°C at the same peak position. Compared with the as-implanted sample, significant increase of Ge–Ge bonds is measured in X-ray photoelectron spectroscopy, and the formation of Ge nanocrystals with a diameter of 5 nm are observed in transmission electron microscopy from the sample annealed at 1100°C. We conclude that the PL peak from the sample annealed above 900°C is caused by the quantum confinement effects from Ge nanocrystals, while the luminescence from the as-implanted sample is due to some radiative defects formed by Ge implantation.     

Structural and compositional analysis of InBixAsySb(1−x−y) films grown on GaAs(0 0 1) substrates by liquid phase epitaxy

The growth of epitaxial InBi_xAs_ySb_(1−x−y) layers on highly lattice mis-matched semi-insulating GaAs substrates has been successfully achieved via the traditional liquid phase epitaxy. Orientation and single crystalline nature of the film have been confirmed by X-ray diffraction. Scanning electron micrograph shows abrupt interface at micrometer resolution. Surface composition of Bi(x) and As(y) in the InBi_xAs_ySb_(1−x−y) film was measured using energy dispersive X-ray analysis and found to be 2.5 and 10.5 at.%, respectively, and was further confirmed with X-ray photoelectron spectroscopy. Variation of the composition with depth of the film was studied by removing the layers with low current (20 μA) Ar⁺ etching. It was observed that with successive Ar⁺ etching, In/Sb ratio remained the same, while the As/Sb and Bi/Sb ratios changed slightly with etching time. However after about 5 min etching the As/Sb and Bi/Sb ratios reached constant values. The room temperature band gap of InBi_0.025As_0.105Sb_0.870 was found to be in the range of 0.113–0.120 eV. The measured values of mobility and carrier density at room temperature are 3.1×10⁴ cm² V⁻¹ s⁻¹ and 8.07×10¹⁶ cm⁻³, respectively.     

Effect of oxide thickness on the capacitance and conductance characteristics of MOS structures

In this work, the investigation of the interface states density and series resistance from capacitance–voltage (C–V) and conductance–voltage (G–V) characteristics in Au/SnO₂/n-Si (MOS) structures prepared at various SnO₂ layer thicknesses by spray deposition technique have been reported. It is fabricated five samples depending on deposition time. The thicknesses of SnO₂ films obtained from the measurement of the oxide capacitance in the strong accumulation region for MOS Schottky diodes are 37, 79, 274, 401, and 446 Å, for D1, D2, D3, D4, and D5 samples, respectively. The C–V and G–V measurements of Au/SnO₂/n-Si MOS structures are performed in the voltage range from −6 to +10 V and the frequency range from 500 Hz to 10 MHz at room temperature. It is observed that peaks in the forward C–V characteristics appeared because of the series resistance. It has been seen that the value of the series resistance R_s of samples D1 (47 Ω), D2 (64 Ω), D3 (98 Ω), D4 (151 Ω), and D5 (163 Ω) increases with increasing the oxide layer thickness. The interface state density D_it ranges from 2.40×10¹³ cm⁻² eV⁻¹ for D1 sample to 2.73×10¹² cm⁻² eV⁻¹ for D5 sample and increases with increasing the oxide layer thickness.     

Electrical characterization of low temperature deposited TiO2 films on strained-SiGe layers

Thin films of titanium dioxide have been deposited on strained Si_0.82Ge_0.18 epitaxial layers using titanium tetrakis-isopropoxide [TTIP, Ti(O-i-C₃H₇)₄] and oxygen by microwave plasma enhanced chemical vapor deposition (PECVD). The films have been characterized by X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR). Dielectric constant, equivalent oxide thickness (EOT), interface state density (D_it), fixed oxide charge density (Q_f/q) and flat-band voltage (V_FB) of as-deposited films were found to be 13.2, 40.6 Å, 6×10¹¹ eV⁻¹ cm⁻², 3.1×10¹¹ cm⁻² and −1.4 V, respectively. The capacitance–voltage (C–V), current–voltage (I–V) characteristics and charge trapping behavior of the films under constant current stressing exhibit an excellent interface quality and high dielectric reliability making the films suitable for microelectronic applications.     

Defect versus nanocrystal luminescence emitted from room temperature and hot-implanted SiO2 layers

Silicon nanocrystals have been synthesized in SiO₂ matrix using Si ion implantation. Si ions were implanted into 300-nm-thick SiO₂ films grown on crystalline Si at energies of 30–55 keV, and with doses of 5×10¹⁵, 3×10¹⁶, and 1×10¹⁷ cm⁻². Implanted samples were subsequently annealed in an N₂ ambient at 500–1100°C during various periods. Photoluminescence spectra for the sample implanted with 1×10¹⁷ cm⁻² at 55 keV show that red luminescence (750 nm) related to Si-nanocrystals clearly increases with annealing temperature and time in intensity, and that weak orange luminescence (600 nm) is observed after annealing at low temperatures of 500°C and 800°C. The luminescence around 600 nm becomes very intense when a thin SiO₂ sample is implanted at a substrate temperature of 400°C with an energy of 30 keV and a low dose of 5×10¹⁵ cm⁻². It vanishes after annealing at 800°C for 30 min. We conclude that this luminescence observed around 600 nm is caused by some radiative defects formed in Si-implanted SiO₂.