固载杂多酸盐催化剂的制备与性能研究

介绍了固载型杂多酸盐催化剂TiSiW12 O4 0 /TiO2 的两种制备方法 ,并以乙酸正丁酯的合成 ,考察了制备条件对其催化活性的影响 ,结果令人满意     

TiSiW12O40／TiO2催化合成苯甲酸酯

首次报道了以固载杂多酸盐TiSiW12O40/TiO2为催化剂,对以丙醇、丁醇、正戊醇、异戊醇和苯甲酸为原料,合成相应苯甲酸酸的反应条件进行了研究。实验表明,TiSiW12O40/TiO2是合成苯甲酸酯的良好催化剂,最佳反应条件为：醇酸摩尔比为4：1,催化剂用量为反应物料总质量的1.5%,反应时间为2.5h。在此条件下,苯甲酸丙酯及苯甲酸正丁酯的产率分别为70.5%及75.6%,苯甲酸戊酯和苯甲酸异戊酯的产率分别达96.7%和83.3%。     

TiSiW12O40/TiO2催化合成丙酸异戊酯

丙酸异戊酯是一种具有菠萝或洋梨果香味的无色液体 ,可作食用香料及多种工业溶剂。传统工业采用浓硫酸催化丙酸和异戊醇合成丙酸异戊酯[1 ,2 ] ,但原料利用率及产率较低 ,环境污染严重。近年来 ,有关杂多酸及其盐类的催化作用的研究发展迅速[3～ 7] 。我们合成了杂多酸盐ＴｉＳｉＷ1 2 Ｏ40 /ＴｉＯ2 催化剂 ,研究其对丙酸异戊酯的催化合成反应 ,取得了较为满意的结果。1　实验1 1　仪器试剂ＰＫＷ 型电子节能控温仪 ;Ａｂｂｅ折光仪 ;ＩＭＰ41 0红外光谱仪 (ＫＢｒ压片 ,40 0～2 0 0 0ｃｍ- 1 ) ;Ｄ/ＭＡＸ ⅢＣ自动Ｘ射线衍射仪 (Ｃｕ靶 …     

TiSiW12O40/TiO2催化合成己酸异戊酯

报道了以固载杂多酸盐TiSiW12O40/TiO4为多相催化剂，通过己酸和异戊醇反应合成了己酸异戊酯，探讨了TiSiW12O40/TiO4对酯化反应的催化活性，较系统地研究了醇酸摩尔比，催化剂用量，反应时间诸因素对收率的影响，实验表明：TiSiW12O40/TiO4是合成己酸异戊酯的良好催化剂，在n(醇）：n(酸）＝1．6：1，催化剂用量为反应物总质量的1．5％，反应时间45min，使用环己烷为带水剂的适宜条件下，己酸异戊酯的收率可达91．9％。     

磷钨酸催化合成乙酸戊酯

以磷钨酸为催化剂,冰醋酸和戊醇为原料,催化合成了乙酸戊酯.探讨了催化剂用量、醇酸比、反应时间等对酯化反应的影响.研究结果表明:取冰醋酸40mL,正戊醇25mL,磷钨酸2.0g,反应时间为2h时,酯的产率大于80%.     

TiSiW12O40/TiO2催化合成丙酸乙酯

以自制的固载杂多酸(盐)TiSiW12O40／TiO2为复相催化剂，通过丙酸和无水乙醇反应合成了丙酸乙酯，探讨了诸因素对酯化率的影响，结果表明，在最佳反应条件下，收率可达78．1％。     

磷酸铝分子筛催化合成戊酸正戊酯

首次用磷酸铝分子筛催化戊酸与正戊醇的酯化反应合成了戊酸正戊酯。适宜的酯化条件为:戊酸50mmol,n(正戊醇)∶n(戊酸)=1.2∶1.0,回流反应3 h~5 h,1 mol戊酸用催化剂2.0 g,酯化率高于90%。     

TiSiW12O40/TiO2催化合成苹果酯

以固载杂多酸盐TiSiW12O40/TiO2为多相催化剂，通过乙酰乙酸乙酯和乙二醇反应合成了苹果酯，探讨TiSiW12O40/TiO2对缩酮反应的催化活性，较系统地研究了原料量比，催化剂肜量，反应时间诸因素对产品收率的影响，实验表明：TiSiW12O40/TiO2是合成苹果酯的良好催化剂，在n(乙酰乙酸乙酯）：n(乙二醇）＝1：1．5，催化剂用量为反应物料总质量的1．0％，环己烷为带水剂，反应时间50min的优化条件下，苹果酯的收率可达84．1％。     

对甲苯磺酸催化合成乳酸异戊酯

报道了对甲苯磺酸在异戊醇和乳酸酯化反应中的应用 ,讨论了合成条件。实验表明其催化活性良好。     

杂多配合物催化合成羧酸异戊酯的研究

杂多配合物催化合成羧酸异戊酯的研究王玉和，周百斌，关良智，王晓光，单永奎，李萍，周宏立（哈尔滨师范大学化学系哈尔滨１５００８０）关键词杂多酸，酯化作用，异戊酯，催化羧酸异戊酯广泛用于调制各种香型的食品香料，用作溶剂、萃取剂、制革、人造丝、涂料、化妆品...     

TiSiW12O40/TiO2催化合成乙酸环己酯

以固载杂多酸TiSiWl2O40／TiO2催化乙酸和环己醇合成了乙酸环己酯。实验确定最佳反应条件为：n(乙酸)：n(环己醇)=1．0：1．1，TiSiW12O40／TiO2用量为乙酸质量的5％，反应时间1．5h，酯化率达95．5％。     

TiSiW12O40／TiO2催化合成葡萄糖五丁酸酯的研究

首次报道了新型催化剂TiSiW12O40/TiO2催化酯化合成葡萄五丁酸酯,考察了糖酸比、催化剂用量、反应时间、反应温度诸因素对产率的影响。实验表明,TiSiW12O40/TiO2是合成葡萄糖五丁酸酯的良好催化剂。最佳反应条件为：糖酸摩尔比1：6,催化剂的用量为反应物料总量的2.0%,酯化反应时间为2.0h,反应温度90-95℃。反应产率可达85.4%。     

Synthesis of 4-Methyl-2-Isopropyl- 1,3 -Dioxolane by TiSiW12O40/ TiO2 as Catalyst

Acetals and ketals are a kind of the important compounds and used to protect carbonyl,middle material of the organic synthesis. What's more, they are a sort of the widely use flavor substance. 4-Methyl-2-isopropyl-1,3-dioxolane has fresh fruit odor and apple note. It is used to producing many sorts of essence. And the conventional method to synthesize 4-methyl-2-isopropyl-1,3-dioxolane makes use of sulfuric acid as catalyst in factories. But it causes many problems, such as the erosion of production equipment, difficulty after-treatment, low quality of the products, etc. HPA and its salts shows excellent catalytic activity to the esterification and have recently attracted much attention as catalysts for various industrial processes, because their acidic and redox properties can be controlled at atomic/molecular levels. Misono, Pope [1], and Wang [2]have reviewed the homogeneous catalysis and fine organic synthesis catalyzed by heteropoly compounds. However, there is no report on the synthesis of 4-methyl-2-isopropyl-1,3-dioxolane catalyzed by TiSiW12O40/TiO2. TiSiW12O40/TiO2 was prepared according to reference [3] and identified by means of IR and XRD. The reaction was carried out in a three-neck flask equipped with a stirrer, a reflux condenser, and a thermometer. A certain amounts of isobutyraldehyde,1,2-propanediol and the catalyst was heated to boiling and refluxed until no water flowed off. The purified product was analyzed by IR spectra and 1HNMR.In this paper, we report 4-methyl-2-isopropyl-1,3-dioxolane was synthesized from isobutyraldehyde and 1,2-propanediol in the presence of TiSiW12O40/TiO2. The factors influencing the yield of product and the optimum reaction conditions were discussed. The optimum conditions are molar ratio of isobutyraldehyde to 1,2-propanediol was 1:1.5, the quantity of catalyst was equal to 0.5% feed stock, and the reaction time was 1.0 h. TiSiW12O40/TiO2 was an excellent catalyst to synthesize 4-methyl-2-isopropyl-1,3-dioxolane and the yield can be up to 92.1%. IR spectra of 4-methyl-2-isopropyl- 1,3-dioxolane shows peaks at 1191,1100,1022,950 cm-1; 1HNMR (δH, ppm):4.65-4.67 (d, 1H, CH), 4.02-4.20 (m, 1H, CH), 3.81-3.92 (d, 1H, CH), 3.35-3.43 (t, 1H, CH),1.61～1.85 (m, 1H, CH), 1.14-1.29 (d, 3H, CH3), 0.96 (m, 6H, CH3); nD20=1.4135; b.p. 127-130 ℃.And we found that the catalyst can be utilized repeatedly, moreover, the catalytic activities of the catalyst are almost unchanged after it has been used five times. From the above results and discussion, we can see that the synthesis of 4-methyl-2-isopropyl-1,3-dioxolane catalyzed by TiSiW12O40/TiO2 instead of sulfuric acid has a great prospect of application.     

TiSiW_(12)O_(40)/TiO_2催化合成磷酸三甲苯酯的研究

应用TiSiW_(12)O_(40)/TiO_2催化剂合成磷酸三甲苯酯研究结果表明，该催化 剂具有较高的催化活性。考察了催化剂用量、反应温度和反应时间对酯产率的影响 。在典型反应条件（催化剂用量为原料总量的1.0%，反应温度为100-120 ℃，反应 时间为8h）下所得磷酸三甲苯酯的产率为85.5%。该催化剂易于回收且可重复使用 ，具有良好的活性稳定性。     

Hydrothermal Synthesis of H3PW12O40/TiO2 Nanometer Photocatalyst and Its Catalytic Performance for Methyl Orange

H3PW12O40/TiO2 nanometer photocatalyst was prepared by one step hydrothermal synthesis from H3PW12O40′nH2O and Ti(OBu)4,simultaneously realizing the load and modification of H3PW12O40.The catalyst was ...     

微波增强H3PW12O40／TiO2光催化降解染料和水杨酸的研究

以孔雀石绿为模型分子, 考察了微波无极灯的形状、微波功率和溶液初始浓度对光催化降解效果的影响. 并且在最佳微波反应条件下, 考察了通过溶胶-凝胶再结合程序升温水热法制备的复合材料H3PW12O40/TiO2对刚果红、酸性黑、酸性品红和水杨酸的光催化降解情况. 结果表明, 微波无极灯具有更好地增强H3PW12O40/TiO2光催化降解有机污染物的作用.