Planar Er- and Yb-doped amplifiers and lasers

New results in erbium-doped planar waveguide amplifiers and lasers are presented. The waveguides are produced in silica-on-silicon technology using plasma-enhanced chemical vapor deposition. Waveguide propagation losses outside the erbium absorption band are improved to values below 0.05 dB/cm for a core–cladding index step of around 1.4%. Amplifier arrays show a net gain of more than 12 dB over the entire C-band. Received: 13 June 2001 / Published online: 23 October 2001     

Femtosecond laser micromachined optical waveguides in LiTaO3 crystal

By using femtosecond laser micromachining, optical wave guides in both depressed cladding and dual‐line configurations have been produced in LiTaO₃ crystal. The guiding properties and the thermal stability have been investigated for both geometries, which exhibit different performance. Depressed cladding waveguides support guidance along both extraordinary and ordinary index polarizations, while dual‐line waveguides support only extraordinary index polarization. Thermal annealing has been proved to be an effective method to reduce the propagation losses. For the cladding waveguide, the lowest propagation loss was as low as 0.38 dB/cm after the annealing treatment at 400 °C. (© 2013 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Reduction of insertion loss after annealing of silicon oxynitride optical waveguides

The insertion losses of silicon oxynitride (SiON) waveguides have been measured in the 1550 nm wavelength region. The waveguide structure consisted of a 2.0μm SiON waveguide core with a refractive index of 1.50, a 0.5μm SiO₂ upper cladding and a 5.0μm SiO₂ lower cladding with a refractive index of 1.45. It was found that the wavelength-dependent insertion losses of the waveguide were greatly reduced by annealing, and the loss was decreased more than 5.7 dB/cm at 1550 nm after annealing at optimum conditions. The former was attributed to the reduction of the absorption caused by N-H and Si-H vibration modes, and the latter was due to the improvement of the interface roughness and homogeneity in the waveguides after annealing.     

Transmission of terahertz radiation using a microstructured polymer optical fiber

A hollow-core microstructured polymer optical fiber was analyzed in the terahertz (THz) region. Spectral analysis of time domain data shows propagation of THz waves in both the hollow-core and the microstructured cladding with a time delay of approximately 20 ps. The frequency range and shift of the transmission bands between different sized waveguides suggested photonic bandgap or resonant guidance. Finite-difference time domain calculations agree relatively well to the experimental transmission results. Propagation losses were estimated to be as low as 0.9 dB/cm.     

Optofluidic microchannels in aerogel

We report optofluidic waveguides made by filling microchannels in aerogel with water. The aerogel cladding is a nanoporous material with an extremely low refractive index of ~1.05, giving a large index step from the water core. Channels were formed by removing embedded optical fibers, which could be nonuniform or multiple. The porosity of the aerogel allowed air to be displaced from the channel, preventing the trapping of bubbles. The attenuation of red light in the highly multimode water core waveguide was no greater than 1.5 dB/cm.     

Hybrid Integration of 1 × 12 Metal-Semiconductor-Metal Photodetector and Polyimide Waveguide Array

We report here a demonstration of hybrid integration of a 1 × 12 metal-semiconductor-metal (MSM) photodetector array and polyimide channel waveguides via 45° total-internal-reflection (TIR) micro-couplers. The two-layer polyimide waveguide array was constructed using Ultradel 9120D for the core and Ultradel 9020 for the lower cladding layer. The coupling loss and propagation loss of the waveguide are 0.2dB and 0.21 dB/cm, respectively. The cross talk of the adjacent channels is -32 dB. The MSM photodetector array was fabricated on a semi-insulated GaAs wafer. The photodetectors are integrated to operate in the conventional vertical illumination mode. We measured the external quantum-efficiency and 3 dB bandwidth of the integrated MSM photodetectors at 0.4 A/W and 2.648 GHz, respectively. The aggregate 3 dB bandwidth of the 12-channel integrated system is 32 GHz.     

Single-mode SiON/SiO2/Si optical waveguides prepared by plasma-enhanced chemical vapor deposition

We present the characteristics of low-propagation-loss single-mode SiON / SiO₂ / Si planar optical waveguides using plasma-enhanced chemical vapor deposition (PECVD). Using a thermal annealing process and a thick silicon dioxide buffer layer, we get an improvement on the propagation loss by the amounts of 1.24 dB /cm and 1.1 dB /cm, respectively. Optical waveguides with propagation loss lower than 0.3 dB /cm can be achieved.     

Synthesis of a fluorinated photoresist for optical waveguide devices

A linear fluorinated bis-phenol-A novolac resin (LFAR) for optical waveguide was synthesized based on 4,4′-(hexafluoro-isopropylidene)diphenol, epoxy chloropropane and formaldehyde. Negative fluorinated photoresist (FP) was made by composing the LFAR, diphenyl iodonium salt and solvent. The film, which was made by spin-coating FP, had good UV light lithograph sensitivity, large hardness and high glass transition temperature (T _g >170°C, after crosslinking). Low-loss optical waveguides with very smooth top surface were fabricated from the resulting FP by direct UV exposure and chemical development. For waveguides without upper cladding, the propagation loss of the channel waveguides was measured to be 0.21 dB/cm at 1550 nm.     

溶胶-凝胶法制备SiO2-TiO2平板光波导工艺研究

采用溶胶-凝胶法制备了SiO₂-TiO₂平板光波导,计算了平板光波导通光条件,分析了硅/钛溶胶-凝胶材料的热性能,观测了平板光波导的结构形貌,并测试了其通光损耗。结果表明：经过200℃,30 min干燥处理的凝胶薄膜呈疏松多孔状态,对于非对称平板波导,存在芯层通光截止厚度,而且当SiO₂-TiO₂芯层厚度为0.5 μm时,SiO₂下包层厚度至少有6 μm才能防止1550 nm波长光泄露入单晶硅衬底中。制备的光波导对于1550 nm波长光传输损耗最小值为0.34 dB/cm。     

Polymer-based waveguides with low propagation loss and polarization-dependent loss

Polymeric optical waveguides based on a new synthesized bisphenol A–aldehyde polymer (PA-1 resin) have been fabricated using photolithography and reactive ion etching technique. The polymer is novel with relatively high refractive index, low birefringence and absorption at the optical communication wavelengths. The single-mode channel waveguides exhibit a propagation loss of 0.41±0.05 dB/cm at a wavelength of and 0.5±0.05 dB/cm at for both the TE and TM polarizations. The polarization-dependent loss of the waveguides is 0.1±0.05 dB/cm at these wavelengths.     

Engineering optical gradient force from coupled surface plasmon polariton modes in nanoscale plasmonic waveguides

We explore the dispersion properties and optical gradient forces from mutual coupling of surface plasmon polariton(SPP) modes at two interfaces of nanoscale plasmonic waveguides with hyperbolic metamaterial cladding.With Maxwell's equations and Maxwell stress tensor,we calculate and compare the dispersion relation and optical gradient force for symmetric and antisymmetric SPP modes in two kinds of nanoscale plasmonic waveguides.The numerical results show that the optical gradient force between two coupled hyperbolic metamaterial waveguides can be engineered flexibly by adjusting the waveguide structure parameters.Importantly,an alternative way to boost the optical gradient force is provided through engineering the hyperbolic metamaterial cladding of suitable orientation.These special optical properties will open the door for potential optomechanical applications,such as optical tweezers and actuators.     

Optical waveguides structured with photoaligning polymers

We present a novel fast fabrication method for making optical waveguides by using a photoaligning and a liquid-crystal polymer. A difference in the refractive indices in the core and cladding regions is achieved by use of polarized UV light to align the polymer chains differently. A refractive-index difference of Deltan = 0.07 was achieved. The propagation loss in a channel waveguide is 4 dB/cm at a wavelength of 1.55 microm. The fabrication method has only a few processing steps and yields short fabrication times. The waveguide structures offer possibilities for generating devices with new applications related to the polarization of the guided light.     

1.5μm Ti:LiNbO_3光波导TE_0模偏振器

在1.523μm波长He-Ne激光,对于Z切Ti扩散LiNbO_3光波导及其带有金属包覆/介质缓冲层的偏振器结构,理论上计算了单模波导的工艺参数和基模的吸收损耗系数.文中用TM_0模的共振吸收效应,在1.5μm波长首次研制成Ti:LiNbO_3光波导TE_0模偏振器.当器件长度为2mm和9mm时,其消光比分别为20dB和25dB.     

制备多模聚硅氧烷光波导关键技术的改进

本文利用浇铸法,使用M&N胶和OE6450两种聚硅氧烷制备光波导.通过改进制备光波导的多个关键技术, 解决了波导制备过程中的气泡问题、脱模问题、芯层不固化问题、芯层和覆盖层产生化学反应等难题,提出了 比较完备和科学的聚硅氧烷波导制备工艺流程,从而使得波导的制备成品率从原来低于40%提高到高于80%, 波导的最大长度从原来的21 cm增加到22.5 cm,波导的损耗(截断法测量结果)从最初的0.3dB/cm(850 nm)降低到了 0.21dB/cm(850nm).本文在波导制备技术方面具有重要的实际意义和价值.     

Reduction of scattering loss of silicon slot waveguides by RCA smoothing

Because of stronger optical confinement density, silicon slot waveguides tend to have higher scattering loss than normal ridge waveguides with same sidewall roughness. A wet chemical process is found to be highly effective in reducing the surface roughness and scattering loss. A reduction in scattering loss by 10.2 dB/cm for TE and 8.5 dB/cm for TM polarizations has been achieved.     

Synthesis of photosensitive poly(methyl methacrylate-co-glycidyl methacrylate) for optical waveguide devices

Photosensitive poly(MMA-co-GMA) for optical waveguide was synthesized, and the refractive index of the polymer film was tuned in the range of 1.481–1.588 at 1550 nm by mixing with bis-phenol-A epoxy resin. The film, which was made by spinning coated the poly(MMA-co-GMA) with photo initiator, had good UV light lithograph sensitivity, high glass transition temperature (T _g : 153°C, after crosslinking) and good thermal stabilities (T _d : up to 324°C, after crosslinking). The optical waveguides with very smooth top surface were fabricated from the resulting polymer by direct UV exposure and chemical development. For waveguides with cladding, the propagation losses of the channel waveguides were measured to be below 3 dB/cm at 1550 nm.     

利用51微米激光器测量中红外光波导损耗(英文)

一种新型的采用AlGaAs材料设计制成的光波导显示了其在中红外激光器方面的应用。波导部分包含在两个GaAs的包层之间,两个包层的掺杂材料限制光场在波导中传播并且降低损耗。三个不同长度的波导经过切入式测量得到它们的内部传播损耗为1 5dB/cm和耦合损耗为9dB。所采用的中红外激光器的波长是5 1μm,输出功率在45毫瓦以上。从光波导输出的光功率只有几个毫瓦。     

Polymer waveguides from alicyclic methacrylate copolymer fabricated by deep-UV exposure

We have investigated the fabrication of waveguides from alicyclic methacrylate copolymer based on refractive-index modification by deep-UV exposure. By optimizing the UV-exposure process, we were able to obtain single-mode waveguides with a propagation loss of 0.8 dB/cm at 1550 nm, which is due only to material losses in this wavelength range. The loss obtained here is comparable with that of poly(methyl methacrylate) (PMMA) waveguides fabricated by deep-UV exposure. The fabricated waveguide is also single mode at 808 nm, and its propagation loss is 0.6 dB/cm. This alicyclic methacrylate copolymer is a promising material for the fabrication of polymer waveguides by use of deep-UV exposure.     

Improved design of polarization-maintaining photonic crystal fibers

We propose the realization of single-polarization operation in highly birefringent photonic crystal fibers. The suppression of one of the polarization states is realized by introducing index-matched cladding defect waveguides. The leakage loss of the index-matched polarization state can be enhanced by nearly 4 orders of magnitude. In particular, polarization-dependent loss larger than 2.97 dB/m with transmission loss lower than 0.03 dB/m in a wavelength region ranging from 1.54 to 1.566 microm can be realized in one such fiber.     

Low-loss large-area GaAs/GaAsP heterostructure as optical waveguide at 10.6 μm

GaAs/GaAsP heterostructures are fabricated as optical waveguides at 10.6 μm. The wafers are being grown with maximum dimensions of the order of 5 cm by vapor phase epitaxy. An attenuation rate of 2 dB/cm for a single mode waveguide and 1.5 dB/cm for a two-mode waveguide has been measured for the TE₀ mode.