Electrochemical behavior of Li intercalation processes into a Li[NixLi(1/3−2x/3)Mn(2/3−x/3)]O2 cathode

Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ (X=0.17, 0.25, 0.33, 0.5) compounds are prepared by a simple combustion method. The Rietvelt analysis shows that these compounds could be classified as having the α-NaFeO₂ structure. The initial charge-discharge and irreversible capacity increases with the decrease of x in Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂. Indeed, Li[Ni_0.50Mn_0.50]O₂ compound shows relatively low initial discharge capacity of 200 mAh/g and large capacity loss during cycling, with Li[Ni_0.17Li_0.22Mn_0.61]O₂ and Li[Ni_0.25Li_0.17Mn₀.₅₈]O₂ compounds exhibit high initial discharge capacity over 245 mAh/g and stable cycle performance in the voltage range of 4.8 -2.0 V. On the other hand, XANES analysis shows that the oxidation state of Ni ion reversibly changes between Ni²⁺ and about Ni³⁺, while the oxidation state of Mn ion sustains Mn⁴⁺ during charge-discharge process. This result does not agree with the previously reported ‘electrochemistry model’ of Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂, in which Ni ion changes between Ni²⁺ and NI⁴⁺. Based on these results, we modified oxidation-state change of Mn and Ni ion during charge-discharge process.     

Investigation of spectroscopic properties and thermal stability of Er/Yb-co-doped Bi2O3-B2O3-Ga2O3 glasses

A series of Er³⁺/Yb³⁺-co-doped 60Bi₂O₃-(40−x) B₂O₃ -xGa₂O₃ (BBGA x=0, 4, 8, 12, 16 mol%) glasses have been prepared. The absorption spectra, emission spectra, fluorescence lifetime of Er³⁺:⁴I_13/2 level and thermal stability were measured and investigated. Three Judd-Ofelt intensity parameters Ω_t (t=2,4,6) (Ω₂=(4.67-5.93)×10⁻²⁰ cm², Ω₄=(1.50-1.81)×10⁻²⁰ cm², Ω₆=(0.92-1.17)×10⁻²⁰ cm²) of Er³⁺ ions were calculated by Judd-Ofelt theory. It is found that the Ω₆ first increases with the increase of Ga₂O₃ content from 0 to 8 mol% and then decreases, which is mainly affected by the number of non-bridging oxygen ions of the glass network. The high peak of stimulated emission cross-section () of Er³⁺: ⁴I_13/2→⁴I_15/2 transition were obtained according to McCumber theory and broad full width at half maximum (FWHM=69-76 nm) of the ⁴I_13/2→⁴I_15/2 transition of Er³⁺ ions were measured. The results indicate that these new BBGA glasses can be used as a candidate host material for potential broadband optical amplifiers.     

Structural and electrical transport properties of ZnxFe3−xO4 thin film deposited on Si (1 1 1) by pulsed-laser deposition

Polycrystalline thin films of Fe_3−xZn_xO₄ (x = 0.0, 0.01 and 0.02) were prepared by pulsed-laser deposition technique on Si (1 1 1) substrate. X-ray diffraction studies of parent as well as Zn doped magnetite show the spinel cubic structure of film with (1 1 1) orientation. The order–disorder transition temperature for Fe₃O₄ thin film with thickness of 150 nm are at 123 K (Si). Zn doping leads to enhancement of resistivity by Zn²⁺ substitution originates from a decrease of the carrier concentration, which do not show the Verwey transition. The Raman spectra for parent Fe₃O₄ on Si (1 1 1) substrate shows all Raman active modes for thin films at energies of T_2g¹, T_2g³, T_2g², and A_1g at 193, 304, 531 and 668 cm⁻¹. It is noticed that the frequency positions of the strongest A_1g mode are at 668.3 cm⁻¹, for all parent Fe₃O₄ thin film shifted at lower wave number as 663.7 for Fe_2.98Zn_0.02O₄ thin film on Si (1 1 1) substrate. The integral intensity at 668 cm⁻¹ increased significantly with decreasing doping concentration and highest for the parent sample, which is due to residual stress stored in the surface.     

Synthesis and electrochemical performances of Li4Ti4.95Al0.05O12/C as anode material for lithium-ion batteries

Spinel compounds Li₄Ti_5−xAl_xO₁₂/C (x=0, 0.05) were synthesized via solid state reaction in an Ar atmosphere, and the electrochemical properties were investigated by means of electronic conductivity, cyclic voltammetry, and charge-discharge tests at different discharge voltage ranges (0-2.5 V and 1-2.5 V). The results indicated that Al³⁺ doping of the compound did not affect the spinel structure but considerably improved the initial capacity and cycling performance, implying the spinel structure of Li₄Ti₅O₁₂ was more stable when Ti⁴⁺ was substituted by Al³⁺, and Al³⁺ doping was beneficial to the reversible intercalation and deintercalation of Li⁺. Al³⁺ doping improved the reversible capacity and cycling performance effectively especially when it was discharged to 0 V.     

Synthesis and magnetic characterization of cobalt-substituted ferrite (CoxFe3−xO4) nanoparticles

Cobalt-substituted ferrite nanoparticles were synthesized with a narrow size distribution using reverse micelles formed in the system water/AOT/isooctane. Fe:Co ratios of 3:1, 4:1, and 5:1 were used in the synthesis, obtaining cobalt-substituted ferrites (Co_xFe_3−xO₄) and some indication of γ-Fe₃O₄ when 4:1 and 5:1 Fe:Co ratios were used. Inductively coupled plasma mass spectroscopy (ICP-MS) verified the presence of cobalt in all samples. Fourier transform infrared (FTIR) showed bands at ∼560 and ∼400 cm⁻¹, characteristic of the metal–oxygen bond in ferrites. Transmission electron microscopy showed that the number median diameter of the particles was ∼3 nm with a geometric deviation of ∼0.2. X-ray diffraction (XRD) confirmed the inverse spinel structure typical of ferrites with a lattice parameter of a=8.388 Å for Co_0.61Fe_0.39O₄, which is near that of CoFe₂O₄ (a=8.394 Å). Magnetic properties were determined using a superconducting quantum interference device (SQUID). Coercivities higher than 8 kOe were observed at 5 K, whereas at 300 K the particles showed superparamagnetic behavior. The anisotropy constant was determined based on the Debye model for a magnetic dipole in an oscillating field and an expression relating χ′ and the temperature of the in-phase susceptibility peak. Anisotropy constant values in the order of ∼10⁶ erg/cm³ were determined using the Debye model, whereas anisotropy constants in the order of ∼10⁷ erg/cm³ were calculated assuming Ωτ=1 at the temperature peak of the in-phase component of the susceptibility curve as commonly done in the literature. Our analysis demonstrates that the assumption Ωτ=1 at the temperature peak of χ′ is rigorously incorrect.     

Influence of B2O3 to the inhomogeneous broadening and spectroscopic properties of Er/Yb codoped fluorophosphate glasses

In a three-components fluorophosphate glass system, the introduction of H₃BO₃ brings some valuable influence to the spectroscopic and thermal properties of the glasses. With H₃BO₃ increases from 2 to 20 mol%, Ω₆, S_ed4I13/2, FWHM, T_g and fluorescence lifetime change from 3.21×10⁻²⁰ cm², 1.77×10⁻²⁰ cm², 45 nm, 480 °C and 8.8 ms to 4.66×10⁻²⁰ cm², 2.11×10⁻²⁰ cm², 50 nm, 541 °C and 7.4 ms, respectively. σ_abs, σ_emi, FWHM×τ_f×σ_emi has a maximum when H₃BO₃ is 11 mol%. T_g and T_x−T_g increases with H₃BO₃ introduction. Results showed that in fluorophosphate glasses, proper amount of B₂O₃ can be used as a modifier to suppress upconversion and improve spectroscopic properties, broadband property and crystallization stability of the glasses while keeps the fluorescence lifetime relatively high.     

Effect of Bi2O3 on EPR, optical transmission and DC conductivity of vanadyl doped alkali bismuth borate glasses

Glasses with composition xBi₂O₃·(30−x)M₂O·70B₂O₃ (M=Li, Na) containing 2 mol% V₂O₅ have been prepared over the range 0≤x≤15 (x is in mol%). The electron paramagnetic resonance spectra of VO²⁺ of these glasses have been recorded in the X-band (≈9.3 GHz) at room temperature (RT≈300 K). Spin Hamiltonian parameters, g_∥, g_⊥, A_∥, A_⊥, dipolar hyperfine coupling parameter, P, and Fermi contact interaction parameter, K, have been calculated. The molecular orbital coefficients, α² and γ², have been calculated by recording the optical transmission spectra. In xBi₂O₃·(30−x)Li₂O·70B₂O₃ glasses there is decrease in the tetragonality of the V⁴⁺O₆ complex for x up to 6 mol% whereas for x≥6 mol%, tetragonality increases. In xBi₂O₃·(30−x)Na₂O·70B₂O₃ glasses there is increase in the tetragonality of the V⁴⁺O₆ complex with increasing x. The 3d_xy orbit expands with increase in Bi₂O₃:M₂O ratio. Values of the theoretical optical basicity, Λ_th, have also been reported. The DC conductivity increases with increase in temperature. The order of conductivity is 10⁻⁵ ohm⁻¹ m⁻¹ at low temperature and 10⁻³ ohm⁻¹ m⁻¹ at high temperature. The DC conductivity decreases and the activation energy increases with increase in Bi₂O₃:M₂O ratio.     

Heat capacity and magnetic properties of pyrochlore Hg2Os2O7

Hg₂Os₂O₇, which has the cubic pyrochlore structure, remains metallic down to the liquid helium temperature unlike its isostructural counterpart Cd₂Os₂O₇, which shows metal-insulator transition at 226 K. Magnetization and heat capacity data for Hg₂Os₂O₇ are presented. The magnetic anomaly at T_N=88 K shares many characteristics in common with the metal-insulator transition in Cd₂Os₂O₇, though Hg₂Os₂O₇ remains metallic below T_N. The heat capacity C_p shows no or very little change in the magnetic entropy around T_N, supporting the view that there is no long-range ordering of localized spins. The measured value of electronic heat-capacity coefficient γ=21 mJ K⁻²mol⁻¹ is comparable to the value obtained from band-structure calculation on Cd₂Os₂O₇, suggesting that mass-enhancement is small in Hg₂Os₂O₇. There is a pronounced peak in C_p/T³ at 13.1 K, which corresponds to a peak in the phonon density of states at 40 cm⁻¹.     

Enhanced ferroelectric properties of (Pb0.90La0.10)Ti0.975O3 multilayered thin films prepared by RF magnetron sputtering

The (Pb_0.90La_0.10)Ti_0.975O₃/PbTiO₃ (PLT/PT), PbTiO₃/(Pb_0.90La_0.10)Ti_0.975O₃/PbTiO₃ (PT/PLT/PT) multilayered thin films with a PbO_x buffer layer were in situ deposited by RF magnetron sputtering at the substrate temperature of 600 °C. With this method, highly (1 0 0)-oriented PLT/PT and PT/PLT/PT multilayered thin films were obtained. The PbO_x buffer layer leads to the (1 0 0) orientation of the films. The dielectric, ferroelectric and pyroelectric properties of the PLT multilayered thin films were investigated. It is found that highly (1 0 0)-oriented PT/PLT/PT multilayered thin films possess higher remnant polarization 2P_r (44.1 μC/cm²) and better pyroelectric coefficient at room temperature p (p = 2.425 × 10⁻⁸ C/cm² K) than these of PLT and PLT/PT thin films. These results indicate that the design of the PT/PLT/PT multilayered thin films with a PbO_x buffer layer should be an effective way to enhance the dielectric, ferroelectric and pyroelectric properties. The mechanism of the enhanced ferroelectric properties was also discussed.     

Structural and transport properties of cubic spinel ZnCo2O4 thin films grown by reactive magnetron sputtering

We report on the growth of cubic spinel ZnCo₂O₄ thin films by reactive magnetron sputtering and bipolarity of their conduction type by tuning of oxygen partial pressure ratio in the sputtering gas mixture. Crystal structure of zinc cobalt oxide films sputtered in an oxygen partial pressure ratio of 90% was found to change from wurtzite Zn_1−xCo_xO to spinel ZnCo₂O₄ with an increase of the sputtering power ratio between the Co and Zn metal targets, D_Co/D_Zn, from 0.1 to 2.2. For a fixed D_Co/D_Zn of 2.0 yielding single-phase spinel ZnCo₂O₄ films, the conduction type was found to be dependent on the oxygen partial pressure ratio: n-type and p-type for the oxygen partial pressure ratio below ∼70% and above ∼85%, respectively. The electron and hole concentrations for the ZnCo₂O₄ films at 300 K were as high as 1.37×10²⁰ and 2.81×10²⁰ cm⁻³, respectively, with a mobility of more than 0.2 cm²/V s and a conductivity of more than 1.8 S cm⁻¹.     

Spectral properties of Nd:Ca2Nb2O7 crystal

This paper reports the spectral properties of Nd³⁺:Ca₂Nb₂O₇. The spectral parameters of Nd³⁺ in Nd³⁺:Ca₂Nb₂O₇ crystal have been investigated based on Judd-Ofelt theory. The spectral parameters were obtained. The parameters of line strengths Ω_λ are Ω₂=4.967×10⁻²⁰ cm², Ω₄=5.431×10⁻²⁰ cm², Ω₆=5.693×10⁻²⁰ cm². The radiative lifetime, the fluorescence lifetime and the quantum efficiency are 122 μs, 103 μs and 84.4%, respectively. The fluorescence branch ratios calculated: β₁=0.425, β₂=0.479, β₃=0.091, β₄=0.004. The emission cross section at 1068 nm is 6.204×10⁻²⁰ cm².     

Preparation and multi-properties of insulated single-phase BiFeO3 ceramics

Six types of BiFeO₃ ceramic samples, with subtle differences in synthesis conditions, were prepared. The comparison of their phases, electrical resistivity, and porosity revealed that the use of Bi₂O₃ and Fe₂O₃ powders of <1 μm size and a rapid liquid-phase sintering process of 855 °C for 5 min at 100 °C/s is beneficial to synthesize poreless single-phase BiFeO₃ samples with high electrical resistivity of ∼5×10¹² Ω cm. Deoxygenated Bi_xFe_yO_{1.5x+1.5y−δ} (x≠y, δ≥0) impurities were identified and found to be the main cause of low electrical resistivity and high porosity in the multi-phase samples. Large saturation polarization of 16.6 μC/cm² and low leakage current density of 30 mA/m², both at a high electric field of 145 kV/cm, were measured in the optimized single-phase samples at room temperature besides a large piezoelectric d₃₃ coefficient of 27 pC/N and an obvious canted antiferromagnetic behavior.     

Thermal, electrical, and electrochemical properties of Lanthanum-doped Ba0.5Sr0.5 Co0.8Fe0.2O3-δ

Crystal structure, thermogravimetry (TG), thermal expansion coefficient (TEC), electrical conductivity and AC impedance of (Ba_0.5Sr_0.5)_1-xLa_xCo_0.8Fe_0.2O_3-δ (BSLCF; 0.05?x?0.20) were studied in relation to their potential use as intermediate temperature solid oxide fuel cell (IT-SOFC) cathode. A single cubic pervoskite was observed by X-ray diffraction (XRD). The TEC of BSLCF was increasing slightly with the increasing content of La, and all the compounds showed abnormal expansion at high temperature. Proved by the TG result, it was associated with the loss of lattice oxygen. The electrical conductivity, which is the main defect of Ba_0.5Sr_0.5 Co_0.8Fe_0.2O_3-δ (BSCF), was improved by La doping, e.g., the compound of x=0.20 demonstrated a conductivity of σ=376 S cm⁻¹ at 392 °C. The increase of electrical conductivity resulted from the increased concentration of charge carrier induced by La doping. In addition, the AC impedance revealed the better electrochemical performance of BSLCF. For example, at 500 °C, the sample with composition x=0.15 yielded the resistance values of 2.12 Ω cm², which was only 46% of BSCF.     

Characteristics of spherical-shaped Li4Ti5O12 anode powders prepared by spray pyrolysis

Spherical-shaped Li₄Ti₅O₁₂ anode powders with a mean size of 1.5 μm were prepared by spray pyrolysis. The precursor powders obtained by spray pyrolysis had no peaks of crystal structure of Li₄Ti₅O₁₂. The powders post-treated at temperatures of 800 and 900 °C had the single phase of spinel Li₄Ti₅O₁₂. The powders post-treated at a temperature of 1000 °C had main peaks of the Li₄Ti₅O₁₂ phase and small impurity peaks of Li₂Ti₃O₇. The spherical shape of the precursor powders was maintained after post-treatment at temperatures below 800 °C. The Brunauer-Emmett-Teller (BET) surface areas of the Li₄Ti₅O₁₂ anode powders post-treated at temperatures of 700, 800 and 900 °C were 4.9, 1.6 and 1.5 m²/g, respectively. The initial discharge capacities of Li₄Ti₅O₁₂ powders were changed from 108 to 175 mAh/g when the post-treatment temperatures were changed from 700 to 1000 °C. The maximum initial discharge capacity of the Li₄Ti₅O₁₂ powders was obtained at a post-treatment temperature of 800 °C, which had good cycle properties below current densities of 0.7 C.     

Electrical and electrochemical properties of molten salt-synthesized Li4Ti5−xSnxO12 (x=0.0, 0.05 and 0.1) as anodes for Li-ion batteries

Submicron-sized polyhedral Li₄Ti_5−xSn_xO₁₂ (x=0.0, 0.05, and 0.1) materials were successfully prepared by a single-step molten salt method. The structural, morphological, transport and electrochemical properties of the Li₄Ti_5−xSn_xO₁₂ were studied. X-ray diffraction patterns showed the formation of a cubic structure with a lattice constant of 8.31 Å, and the addition of dopants follows Vegard's law. Furthermore, FT-IR spectra revealed symmetric stretching vibrations of octahedral groups of MO₆ lattice in Li₄Ti₅O₁₂. The formation of polyhedral submicron Li₄Ti_5−xSn_xO₁₂ particles was inferred from FE-SEM images, and a particle size reduction was observed for Sn-doped Li₄Ti₅O₁₂. The chemical composition of Ti, O and Sn was verified by EDAX. The DC electrical conductivity was found to increase with increasing temperature, and a maximum conductivity of 8.96×10⁻⁶ S cm⁻¹ was observed at 200 °C for Li₄Ti₅O₁₂. The galvanostatic charge–discharge behavior indicates that the Sn-doped Li₄Ti₅O₁₂ could be used as an anode for Li-ion batteries due to its enhanced electrochemical properties.     

Ferromagnetism of epitaxially grown CaRu1−xMxO3 (M=Ti, Mn) films

Epitaxial thin films of CaRu_1−xM_xO₃ (M=Ti, Mn) were fabricated on a (0 0 1)-SrTiO₃ substrate by spin-coat method using organometallic solutions (metal alkoxides). Results of X-ray diffraction and transmission electron microscopy indicate that the epitaxial films were grown pseudomorphically so as to align the [0 0 l] axis of the CaRu_1−xM_xO₃ films perpendicular to the (0 0 1) plane of the SrTiO₃ substrate. Ferromagnetism and metal-insulator transition are induced by the substitution of transition metal ions. The occurrence of ferromagnetism was explained qualitatively assuming a TiRu₆ cluster model for CaRu_1−xTi_xO₃ film and a mixed valence model for CaRu_1−xMn_xO₃ film. Ferromagnetism was also observed for layered CaRuO₃/CaMnO₃ film and CaRuO₃/CaMnO₃/CaRuO₃/CaMnO₃ multilayer film and the magnetism was explained by an interfacial exchange interaction model with magnetic Mn³⁺, Mn⁴⁺, and Ru⁵⁺ ions.     

Reactivity and XAFS study on (1−x)CeO2-xNiO (x=0.025-0.3) system in the two-step water-splitting reaction for solar H2 production

The redox reaction of Ce⁴⁺-Ce³⁺ promoted by the catalytic function of nickel ions in a (1−x)CeO₂-xNiO solid solution was investigated for solar H₂ production by the two-step water-splitting reaction. By irradiation using an infrared imaging lamp as a solar simulator, the O₂-releasing reaction with (1−x)CeO₂-xNiO solid solution proceeded at 1673-1873 K, and its reduced form was produced. The amounts of H₂ gas evolved by the reduced form were 1.2-2.5 cm³/g and the evolved gases amounts ratio of H₂/O₂ was nearly 2, which is equal to the stoichiometric value of the water-splitting reaction (H₂O=H₂+1/2O₂). The maximum amounts of evolved H₂ and O₂ gases were obtained at the Ce:Ni mole ratio of 0.95:0.05 (x=0.05) in the (1−x)CeO₂-xNiO system. The X-ray absorption fine structure (XAFS) measurement showed that the O₂-releasing and H₂-generation reactions with (1−x)CeO₂-xNiO solid solution were repeatable with the redox system of Ce⁴⁺-Ce³⁺, which was enhanced by the catalytic function of Ni²⁺-Ni⁰.     

Charge-discharge characteristics of nanocrystalline Co3O4 powders via aerosol flame synthesis

Nanocrystalline Co₃O₄ powders were synthesized by aerosol flame synthesis (AFS) method for the anode of lithium ion batteries and the basic electrochemical properties were investigated. The effects of synthesis conditions and heat-treatment temperature on the morphology, crystallite size and electrochemical properties were investigated. As-prepared soot contained Co₃O₄, CoO and Co(OH)₂, which were eventually converted into cubic spinel Co₃O₄ by post heat treatment. The as-prepared particle size was in the range of 10-30 nm and grew to 50-85 nm by the heat treatment. With growing particle size and improved crystallinity, charge-discharge capacity and cycle performance were improved and the discharge capacity of the powder heat-treated at 700 °C was 571 mAh/g after 30 cycles, which was better than Co₃O₄ powder reported in the previous literature.     

Structural and magnetic properties of Mg(In2−xMnx)O4 system

We synthesized the Mn-doped Mg(In_2−xMn_x)O₄ oxides with 0.03?x?0.55 using a solid-state reaction method. The X-ray diffraction patterns of the samples were in a good agreement with that of a distorted orthorhombic spinel phase. Their lattice parameters and unit-cell volumes decrease with x due to the substitution of the smaller Mn³⁺ ions to the larger In³⁺ ions. The undoped MgIn₂O₄ oxide presents diamagnetic signals for 5 K?T?300 K. The M(H) at T=300 K reveals a fairly negative-sloped linear relationship. Neither magnetic hysteresis nor saturation behavior was observed in this parent sample. For the Mn-doped samples, however, positive magnetization were observed between 5 and 300 K even if the x value is as low as 0.03. The mass susceptibility enhances with Mn content and it reaches the highest value of 1.4×10⁻³ emu/g Oe (at T=300 K) at x=0.45. Furthermore, the Mn-doped oxides with x=0.06 and 0.2, respectively, exhibit nonlinear magnetization curves and small hysteretic loops in low magnetic fields. Susceptibilities of the Mn-doped samples are much higher than those of MnO₂, Mn₂O₃ oxides, and Mn metals. These results show that the oxides have potential to be magnetic semiconductors.     

Effect of Al2O3 on the electrical properties of ZnO-Pr6O11-based varistor ceramics

The effect of Al₂O₃ on the electrical properties of ZnO-Pr₆O₁₁-based ceramics is investigated in this work. The average grain size of ZnO increased as the Al₂O₃ content increased from 10.3 to 13.5 μm. It was found that a sample doped with Al₂O₃ of 0.005 mol% showed the highest nonlinear current-voltage characteristics with a nonlinear exponent of 43.8 and a leakage current of 0.66 μA. When the Al₂O₃ content was increased, the donor concentration was increased from 0.51×10¹⁸/cm³ to 1.59×10¹⁸/cm³, but the barrier height was decreased from 1.01 to 0.87 eV. The best electrical stability against aging stress was obtained by doping Al₂O₃ of 0.001 mol%.