Enhanced luminescence of Ca3B2O6:Dy phosphors by Na-codoping for LED applications

The Ca_2.95−yDy_0.05B₂O₆:yNa⁺ (0≤y≤0.20) phosphors were synthesized at 1100 °C in air by the solid-state reaction route. The as-synthesized phosphors were characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), photoluminescence excitation (PLE), photoluminescence (PL) spectra and thermoluminescence (TL) spectra. The PLE spectra show the excitation peaks from 300 to 400 nm due to the 4f-4f transitions of Dy³⁺. This mercury-free excitation is useful for solid-state lighting and light-emitting diodes (LEDs). The emission of Dy³⁺ ions on 350 nm excitation was observed at 480 nm (blue) due to the ⁴F_9/2→⁶H_15/2 transitions, 575 nm (yellow) due to ⁴F_9/2→⁶H_13/2 transitions and 660 nm (red) due to weak ⁴F_9/2→⁶H_11/2 emissions. The PL results from the investigated Ca_2.95−yDy_0.05B₂O₆:yNa⁺ phosphors show that Dy³⁺ emissions increase with the increase of the Na⁺ codoping ions. The integral intensity of yellow to blue (Y/B) can be tuned by controlling Na⁺ content. By the simulation of white light, the optimal CIE value (0.328, 0.334) can be achieved when the content of Na⁺-codoping ions is y=0.2. The results imply that the Ca_2.95−yDy_0.05B₂O₆:yNa⁺ phosphors could be potentially used as white LEDs.     

Energy transfer in Y3Al5O12:Ce, Pr and CaMoO4:Sm, Eu phosphors

Non-radiative energy transfers (ET) from Ce³⁺ to Pr³⁺ in Y₃Al₅O₁₂:Ce³⁺, Pr³⁺ and from Sm³⁺ to Eu³⁺ in CaMoO₄:Sm³⁺, Eu³⁺ are studied based on photoluminescence spectroscopy and fluorescence decay patterns. The result indicates an electric dipole-dipole interaction that governs ET in the LED phosphors. For Ce³⁺ concentration of 0.01 in YAG:Ce³⁺, Pr³⁺, the rate constant and critical distance are evaluated to be 4.5×10⁻³⁶ cm⁶ s⁻¹ and 0.81 nm, respectively. An increase in the red emission line of Pr³⁺ relative to the yellow emission band of Ce³⁺, on increasing Ce³⁺ concentration is observed. This behavior is attributed to the increase of spectral overlap integrals between Ce³⁺ emission and Pr³⁺ excitation due to the fact that the yellow band shifts to the red spectral side with increasing Ce³⁺ concentration. In CaMoO₄:Sm³⁺, Eu³⁺, Sm³⁺-Eu³⁺ transfer occurs from ⁴G_5/2 of Sm³⁺ to ⁵D₀ of Eu³⁺. The rate constant of 8.5×10⁻⁴⁰ cm⁶ s⁻¹ and the critical transfer distance of 0.89 nm are evaluated.     

Synthesis and luminescent properties of Y6W2O15:Eu phosphors

In this paper, a novel phosphor, Y₆W₂O₁₅:Eu³⁺ was synthesized by thermal decomposition and phase transition of its decatungstate gel precursor. With stepwise increase of temperature to 750 °C, a crystalline phase of Y₆W₂O₁₅:Eu³⁺forms that gives intense red emission when excited at 466 nm, the emission is attributed to the Eu³⁺ ions transitions from ⁵D₀ excited states to ⁷F_J (J=0-4) ground states. The long excitation wavelength proves the Eu³⁺ transition follows the photoexcitation of the oxygen-metal (O→W lmct) charge transfer bands in yttrium tungstate. Some structural information regarding Y₆W₂O₁₅ provided by luminescence is in accord with that characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). The long-wavelength excitation properties of this material may find application in the production of red phosphors for white light-emitting diodes (LEDs).     

Enhanced photoluminescence of Sm/Bi co-doped Gd2O3 phosphors by combustion synthesis

Gd₂O₃:Sm³⁺ and Gd₂O₃:Sm³⁺,Bi³⁺ powders were prepared by a combustion method. Their structures were determined using X-ray diffraction. UV-visible absorption and photoluminescence spectra were investigated for Gd₂O₃:Sm³⁺ and Gd₂O₃:Sm³⁺,Bi³⁺ at different annealing temperatures and different doping concentrations. The emission spectra of all samples presented the characteristic emission narrow lines arising from the ⁴G_5/2→⁶H_J transitions (J=5/2, 7/2, and 9/2) of Sm³⁺ ions upon excitation with UV irradiation. The emission intensity of Sm³⁺ ions was largely enhanced with introducing Bi³⁺ ions into Gd₂O₃:Sm³⁺ and the maximum occurred at a Bi³⁺ concentration of 0.5 mol%. The relevant mechanisms were discussed with the sensitization theory by Dexter and the aggregation behavior of Bi³⁺ ions.     

Optical spectroscopy of Ca3Sc2Si3O12, Ca3Y2Si3O12 and Ca3Lu2Si3O12 doped with Pr

The silicates Ca₃Sc₂Si₃O₁₂, Ca₃Y₂Si₃O₁₂ and Ca₃Lu₂Si₃O₁₂, both undoped and doped with Pr³⁺ ions, have been synthesized by solid-state reaction at high temperature. The luminescence spectroscopy and the excited state dynamics of the materials have been studied upon VUV and X-ray excitation using synchrotron radiation. All doped samples have shown efficient 5d-4f emission upon direct VUV excitation of 5d levels, but only Ca₃Sc₂Si₃O₁₂:Pr³⁺ shows luminescence upon interband VUV or X-ray excitation. The VUV excited emission spectra of Ca₃Y₂Si₃O₁₂:Pr³⁺ and Ca₃Lu₂Si₃O₁₂:Pr³⁺ show features attributed to emission from two distinct sites accommodating the Pr³⁺ dopant. The decay kinetics of the Pr³⁺ 5d-4f emission in Ca₃Sc₂Si₃O₁₂:Pr³⁺ upon VUV excitation across the band gap are characterized by decay times in the range 25-28 ns with no significant rise after the excitation pulse. They appear to be faster upon X-ray irradiation than for VUV excitation. Weak afterglow components are attributed to defect luminescence.     

Sol-gel synthesis, structural and optical properties of rare earth ions (Sm or Dy) activated Ca3Ga2Si3O12 powder phosphors

Structural, morphological and optical properties of rare earth ions (RE³⁺=Sm³⁺ or Dy³⁺) activated Ca₃Ga₂Si₃O₁₂ (CaGaSi) phosphors synthesized by the sol-gel method are reported. XRD results confirmed the cubic phase structure of RE³⁺:CaGaSi phosphors. From the SEM images of RE³⁺:CaGaSi phosphors, it is observed that the particles are agglomerated. Photoluminescence spectra of Sm³⁺:CaGaSi phosphors have shown bright orange red emission at 598 nm (⁴G_5/2→⁶H_7/2) with an excitation wavelength of λ_exci=401 nm. In the case of Dy³⁺:CaGaSi phosphors bright yellow emission has been observed at 574 nm (⁴F_9/2→ ⁶H_13/2) with λ_exci=451 nm. From the PL spectral results, the rare earth ion concentration of CaGaSi phosphors is optimized.     

Luminescence studies on ZnO-P2O5 glasses doped with Gd2O3:Eu nanoparticles and Eu2O3

Zinc phosphate glasses doped with Gd₂O₃:Eu nanoparticles and Eu₂O₃ were prepared by conventional melt-quench method and characterized for their luminescence properties. Binary ZnO-P₂O₅ glass is characterized by an intrinsic defect centre emission around 324 nm. Strong energy transfer from these defect centres to Eu³⁺ ions has been observed when Eu₂O₃ is incorporated in ZnO-P₂O₅ glasses. Lack of energy transfer from these defect centres to Eu³⁺ in Gd₂O₃:Eu nanoparticles doped ZnO-P₂O₅ glass has been attributed to effective shielding of Eu³⁺ ions from the luminescence centre by Gd-O-P type of linkages, leading to an increased distance between the luminescent centre and Eu³⁺ ions. Both doped and undoped glasses have the same glass transition temperature, suggesting that the phosphate network is not significantly affected by the Gd₂O₃:Eu nanoparticles or Eu₂O₃ incorporation.     

Up-conversion white light of Tm/Er/Yb tri-doped CaF2 phosphors

Tm³⁺/Er³⁺/Yb³⁺ tri-doped CaF₂ phosphors were synthesized using a hydrothermal method. The phosphors were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), and up-conversion (UC) emission spectra. After annealing, the phosphors emitted white light under a 980 nm continuous wave diode laser (CW LD 2 W) excitation. As the excitation power density changed in the range of 20-260 W/cm², the chromaticity coordinates of the UC light of the phosphor Ca_0.885Tm_0.005Er_0.01Yb_0.1F₂ fell well in the white region of the 1931 CIE diagram. For the proportion of red, green and blue (RGB) in white light is strict, key factors for achieving UC white light, such as host materials, rare earth ions doping concentrations, annealing temperatures, as well as the excitation power densities, were investigated and discussed.     

Optical properties of (ZnO)0.5(P2O5)0.5 glasses doped with Gd2O3:Eu nanoparticles and Eu2O3

Binary (ZnO)_0.5(P₂O₅)_0.5 glasses doped with Eu₂O₃ and nanoparticles of Gd₂O₃:Eu were prepared by conventional melt-quench method and their luminescence properties were compared. Undoped (ZnO)_0.5(P₂O₅)_0.5 glass is characterized by a luminescent defect centre (similar to L-centre present in Na₂O-SiO₂ glasses) with emission around 324 nm and having an excited state lifetime of 18 ns. Such defect centres can transfer the energy to Eu³⁺ ions leading to improved Eu³⁺ luminescence from such glasses. Based on the decay curves corresponding to the ⁵D₀ level of Eu³⁺ ions in both Gd₂O₃:Eu nanoparticles incorporated as well as Eu₂O₃ incorporated glasses, a significant clustering of Eu³⁺ ions taking place with the latter sample is confirmed. From the lifetime studies of the excited state of L-centre emission from (ZnO)_0.5(P₂O₅)_0.5 glass doped with Gd₂O₃:Eu nanoparticles, it is established that there exists weak energy transfer from L-centres to Eu³⁺ ions. Poor energy transfer from the defect centres to Eu³⁺ ions in Gd₂O₃:Eu nanoparticles doped (ZnO)_0.5(P₂O₅)_0.5 glass has been attributed to effective shielding of Eu³⁺ ions from the luminescence centre by Gd-O-P type of linkages, leading to an increased distance between luminescent centre and Eu³⁺ ions.     

Synthesis and characterization of Sr3Al2O6：Eu2＋, Dy3＋ phosphors prepared by sol-gel-combustion processing

A type of red luminescent Sr3Al2O6:Eu2+, Dy3+ phosphor powder is synthesised by sol-gel-combustion processing, with metal nitrates used as the source of metal ions and citric acid as a chelating agent of metal ions. By tracing the formation process of the sol-gel, it is found that it is necessary to reduce the amount of NO3- by dropping ethanol into the solution for forming a stable and homogeneous sol-gel. Thermogravimetric and Differential Scanning Calorimeter Analysis, x-ray diffractionmeter, scanning electron microscopy and photoluminescence spectroscopy are used to investigate the luminescent properties of the as-synthesised Sr3Al2O6:Eu2+, Dy3+. The results reveal that the Sr3Al2O6 crystallises completely when the combustion ash is sintered at 1250 C. The excitation and the emission spectra indicate that the excitation broadband lies mainly in a visible range and the phosphors emit a strong light at 618 nm under the excitation of 472 nm. The afterglow of (Sr0.94Eu0.03Dy0.03)3Al2O6 phosphors sintered at 1250 ℃ lasts for over 1000 s when the excited source is cut off.     

Gd2O3:Eu3+纳米晶的燃烧合成及光致发光性质

采用柠檬酸作燃烧剂用燃烧合成法制备了Gd₂O₃:Eu³⁺纳米晶.用X射线衍射仪(XRD)、高分辨透射电子显微镜(HRTEM)和荧光分光光度计等对Gd₂O₃:Eu³⁺纳米晶的结构、形貌和发光性能进行了分析.结果表明：不同柠檬酸与稀土离子配比(C/M)制备的样品经800℃ 退火1 h后，均得到了纯立方相的Gd₂O₃:Eu³⁺纳米晶，晶粒尺寸约为30 nm，尺寸分布较窄，其中以C/M=1.0时制备的纳米晶结晶性最好，发光强度最大.Gd₂O₃:Eu³⁺纳米晶主发射峰位置均在612 nm处 (⁵D₀→⁷F₂跃迁)，激发光谱中电荷迁移态发生红移，观察到Gd³⁺向Eu³⁺的有效能量传递.对柠檬酸与稀土离子配比(C/M)对结晶度、发光性质等的影响也进行了分析和讨论.     

Synthesis and luminescence properties of nanocrystalline Gd2O3:Eu by combustion process

The nanocrystalline Gd₂O₃:Eu³⁺ powders with cubic phase were prepared by a combustion method in the presence of urea and glycol. The effects of the annealing temperature on the crystallization and luminescence properties were studied. The results of XRD show pure phase can be obtained, the average crystallite size could be calculated as 7, 8, 15, and 23 nm for the precursor and samples annealed at 600, 700 and 800 °C, respectively, which coincided with the results from TEM images. The emission intensity, host absorption and charge transfer band intensity increased with increasing the temperature. The slightly broad emission peak at 610 nm for smaller particles can be observed. The ratio of host absorption to O²⁻-Eu³⁺ charge transfer band of smaller nanoparticles is much stronger compared with that for larger nanoparticles, furthermore, the luminescence lifetimes of nanoparticles increased with increasing particles size. The effects of doping concentration of Eu³⁺ on luminescence lifetimes and intensities were also discussed. The samples exhibited a higher quenching concentration of Eu³⁺, and luminescence lifetimes of nanoparticles are related to annealing temperature of samples and the doping concentration of Eu³⁺ ions.     

The influence of Pr co-doping on the luminescent properties of Lu2O3:5 mol% Eu films

Uniform and crack free polycrystalline lutetium oxide (Lu₂O₃:(Eu,Pr)) films were fabricated by Pechini sol-gel method combined with the spin-coating technique. X-ray diffraction (XRD) and atomic force microscope (AFM) characterizations indicated that the obtained film was composed of polycrystalline cubic Lu₂O₃ phase with an average grain size around 30 nm. The photoluminescence(PL) spectra and decay performances of the Lu₂O₃:5 mol% Eu films co-doped by 0-0.5 mol% Pr³⁺ with different concentrations were characterized. It was found that the afterglow was reduced obviously due to the introduction of 0-0.5 mol% Pr³⁺ in the Lu₂O₃:5 mol% Eu films coupled by decrease in the emission intensity at 612 nm. The mechanism of afterglow diminishing was discussed based on the thermoluminescence measurements.     

Y2O3:Yb3+,Tm3+纳米材料的可见及紫外上转换发光

通过燃烧法制备了Yb³⁺-Tm³⁺共掺的Y₂O₃纳米粉体,并对样品在980 nm激光照射下的上转换发光特性进行了研究.实验发现,样品在可见光区域能够产生强烈的蓝色发光(476 nm和487 nm)和较弱的红色发光(约650 nm),而且同时观察到了两个紫外发光峰¹I₆→³H₆ (~297 nm)和^{1关键词： 2O₃:Yb3+')" href="#">Y₂O₃:Yb3+ 3+}')" href="#">Tm³⁺ 上转换光谱 敏化 紫外发光     

Upconversion emission enhancement of TiO2 coated lanthanide-doped Y2O3 nanoparticles

To investigate the upconversion emission,this paper synthesizes Tm3+ and Yb3+ codoped Y2O3 nanoparticles,and then coats them with TiO2 shells for different coating times.The spectral results of TiO2 coated nanoparticles indicate that upconversion emission intensities have respectively been enhanced 3.2,5.4,and 2.2 times for coating times of 30,60 and 90 min at an excitation power density of 3.21×102 W.cm 2,in comparison with the emission intensity of non-coated nanoparticles.Therefore it can be concluded that the intense upconversion emission of Y2O3:Tm3+,Yb3+ nanoparticles can be achieved by coating the particle surfaces with a shell of specific thickness.     

Hydrothermal synthesis, characterization and Raman studies of Eu activated Gd2O3 nanorods

Eu³⁺ (8 mol%) activated gadolinium oxide nanorods have been prepared by hydrothermal method without and with surfactant, cityl trimethyl ammonium bromide (CTAB). Powder X-ray diffraction (PXRD) studies reveal that the as-formed product is in hexagonal Gd(OH)₃:Eu phase and subsequent heat treatment at 350 and 600 °C transforms the sample to monoclinic GdOOH:Eu and cubic Gd₂O₃:Eu phases, respectively. The structural data and refinement parameters for cubic Gd₂O₃:Eu nanorods were calculated by the Rietveld refinement. SEM and TEM micrographs show that as-obtained Gd(OH)₃:Eu consists of uniform nanorods in high yield with uniform diameters of about 15 nm and lengths of about 50-150 nm. The temperature dependent morphological evolution of Gd₂O₃:Eu without and with CTAB surfactant was studied. FTIR studies reveal that CTAB surfactant plays an important role in converting cubic Gd₂O₃:Eu to hexagonal Gd(OH)₃:Eu. The strong and intense Raman peak at 489 cm⁻¹ has been assigned to A_g mode, which is attributed to the hexagonal phase of Gd₂O₃. The peak at ∼360 cm⁻¹ has been assigned to the combination of F_g and E_g modes, which is mainly attributed to the cubic Gd₂O₃ phase. The shift in frequency and broadening of the Raman modes have been attributed to the decrease in crystallite dimension to the nanometer scale as a result of phonon confinement.     

Synthesis of Gd2Ti2O7:Eu, V phosphors by sol-gel process and its luminescent properties

A red-emitting phosphor material, Gd₂Ti₂O₇:Eu³⁺, V⁴⁺, by added vanadium ions is synthesized using the sol-gel method. Phosphor characterization by high-resolution transmission electron microscopy shows that the phosphor possesses a good crystalline structure, while scanning electron microscopy reveals a uniform phosphor particle size in the range of 230-270 nm. X-ray photon electron spectrum analysis demonstrates that the V⁴⁺ ion promotes an electron dipole transition of Gd₂Ti₂O₇:Eu³⁺ phosphors, causing a new red-emitting phenomenon, and CIE value shifts to x=0.63, y=0.34 (a purer red region) from x=0.57, y=0.33 (CIE of Gd₂Ti₂O₇:Eu³⁺). The optimal composition of the novel red-emitting phosphor is about 26% of V⁴⁺ ions while the material is calcinated at 800  °C. The results of electroluminescent property of the material by field emission experiment by CNT-contained cathode agreed well with that of photoluminescent analysis.     

PL and CL degradation and characteristics of SrAl2O4: Eu,Dy phosphors

Strontium aluminate phosphors are ideal for luminescent infrastructure materials. Their brightness and persistent glow time are much higher than previously used sulphide phosphors. Strontium aluminates prepared by the sol–gel and combustion methods are compared with commercially available strontium aluminate. High luminescent efficient SrAl₂O₄:Eu²⁺,Dy³⁺ pulsed laser deposited (PLD) thin films were also produced using the commercially available powder. Photoluminescence (PL) degradation studies showed that the phosphor intensity decreased about 20% over a period of 2 weeks under ultraviolet (UV) irradiation. Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS) showed that cathodoluminescence (CL) degradation is due to the formation of SrO due to electron stimulated surface reactions. The light output mechanism of the phosphor is also discussed in more detail.     

Low temperature quenching and high efficiency Tm, La or Tb co-doped CaSc2O4:Ce phosphors for light-emitting diodes

Low temperature quenching and high efficiency CaSc₂O₄:Ce³⁺ (CSO:Ce³⁺) phosphors co-doped with Tm³⁺, La³⁺ and Tb³⁺ ions were prepared by a solid state method and the phase-forming, morphology, luminescence and application properties of these phosphors were investigated. The results showed that co-doping of Tm³⁺, La³⁺ and Tb³⁺ ions can improve the luminescence properties and decrease temperature quenching of CSO:Ce³⁺ phosphor remarkably. High efficiency green-light-emitting diodes were fabricated with the prepared phosphors and InGaN blue-emitting (∼460 nm) chips. The good performances of the green-light-emitting LEDs made from co-doped CSO:Ce³⁺ phosphors confirm the luminescence enhancement and indicate that Tm³⁺, La³⁺ and Tb³⁺ co-doped CSO:Ce³⁺ phosphors are suitable candidates for the fabrication of high efficiency white LEDs.     

Low thermal quenching and high-efficiency Ce, Tb-co-doped Ca3Sc2Si3O12 green phosphor for white light-emitting diodes

Low thermal quenching and high-efficiency Ca₃Sc₂Si₃O₁₂:Ce³⁺ (CSSO:Ce³⁺) phosphors with co-doping Tb³⁺ ion were prepared by a solid state method and the properties of these phosphors were investigated. The results showed that co-doping of Tb³⁺ not only enhances the photoluminescence remarkably and decreases the thermal quenching of the phosphor, but also heightens the performances of the LEDs fabricated with the phosphor. A high-efficiency and low color temperature white LED was fabricated with the prepared CSSO:1%Ce³⁺, 0.5%Tb³⁺ and a red phosphor, indicating that CSSO:1%Ce³⁺,0.5%Tb³⁺ phosphor is a suitable green phosphor for the fabrication of high-efficiency white LEDs.