钽离子掺杂对LiFePO4 / C物理和电化学性能的影响

采用PAM(聚丙烯酰胺)模板-溶胶凝胶法在惰性气氛下合成钽掺杂的LiFePO₄/C复合正极材料，考察了钽对目标化合物的物理和电化学性能的影响。研究结果表明，0.33C的电流下充放电时，掺杂前后第2个循环的放电容量分别为138.6 mAh·g^-1和155.5 mAh·g^-1，循环20次后容量为141 mAh·g^-1和156 mAh·g^-1。电化学交流阻抗表明，掺杂后的材料阻抗R_ct从180 Ω减小到120 Ω。振实密度比掺杂前提高0.312 g·cm^-3。     

锂离子电池正极材料LiNi0.75-xCoxMn0.25O2的合成及电化学性能研究

以LiOH·H₂O、Ni(OAc)₂·4H₂O、Co(OAc)₂·4H₂O和MnO₂为原料，在水热反应釜中预处理，然后进行高温固相反应，合成了一系列锂镍钴锰氧化物LiNi_0.75-xCo_xMn_0.25O₂(x=0.05,0.10,0.15,0.20,0.25)。通过X射线衍射(XRD)、扫描电子显微镜（SEM）和电化学性能测试对所得样品的结构、形貌、粒径及电化学性能进行了表征。结果表明，当x=0.20时，所合成的正极材料具有很好的α-NaFeO₂型层状晶体结构，晶胞参数a=0.286 1 nm，c=1.416 4 nm， V=0.100 4 nm³，以50 mA·g^-1的电流密度在3～4.3 V(vs Li/Li⁺)充放电时，首次放电比容量达172.5 mAh·g^-1，首次放电效率高达90.9%，30个循环后其放电比容量依然保持在161.1 mAh·g^-1。     

新型正极材料三硫代环磷氮烯无机聚合物的合成

采用缩合聚合方法合成了新型三硫代环磷氮烯无机聚合物[(NPS₃)₃]_n，利用红外光谱测试与元素含量分析技术证明了[(NPS₃)₃]_n的分子结构与组成，并对聚合物材料的粒度、比表面积及微观形貌进行了考察。TG/DTA 实验证明材料在200 ℃ 以下具有良好的热稳定性。循环伏安测试表明[(NPS₃)₃]_n正极材料在锂电池体系具有2.15 V的电化学还原电位和2.45 V的电化学氧化电位，经充放电循环实验观察，材料的首次放电容量达到749.0 mAh·g^-1，与理论容量(759.0 mAh·g^-1)十分接近；经过50次充放电循环后，放电容量保持在674.8 mAh·g^-1，具有很高的使用容量和优秀的循环性能。     

以微乳液法制备的锰源合成LiMn2O4

采用CTAB-C₈H₁₈-C₄H₉OH-H₂O微乳体系制备出MnCO₃，将其灼烧成Mn₂O₃之后，与Li₂CO₃混合，800 ℃高温焙烧，获得了颗粒大小为数百纳米，均匀分布的纯相尖晶石LiMn₂O₄。这一材料的电化学性能优秀，0.5C的电流在3～4.2 V之间充放电时，首次放电比容量为124 mAh·g^-1，经过110次循环，保留比容量118 mAh·g^-1，平均每次容量损失<0.05%。该材料的倍率性能尤为优异，10C放电的比容量在110 mAh·g^-1以上，功率约为0.2C时功率的45倍。     

Al掺杂对正极材料LiNi0.33-xMn0.33Co0.33AlxO2结构和电化学性能的影响

以柠檬酸为螯合剂利用快速湿化学法合成了具有α-NaFeO₂型层状结构的LiNi_0.33-xMn_0.33Co_0.33Al_xO₂(x=0.00,0.01,0.02, 0.04)正极材料,并通过X-射线衍射、充放电测试、循环伏安和交流阻抗对材料的结构和电化学性能进行了系统研究。XRD结果表明此方法合成的材料具有很好的层状结构且阳离子的混排度随着Al³⁺含量的增加而下降。电化学测试表明,LiNi_0.31Mn_0.33Co_0.33Al_0.02O₂具有很好的电化学性能和和循环性能,1C放电倍率下首次放电比容量达到176.9 mAh·g^-1,且Al³⁺的掺杂能有效提高电荷在电极界面间转移并抑制了在高压循环过程中电荷转移阻抗的增加。     

导电氧化物AZO对尖晶石型LiMn2O4高温性能的改善及研究

采用溶胶凝胶法对尖晶石型LiMn₂O₄正极材料进行铝掺杂氧化锌(AZO)包覆改性,并通过XRD、SEM、EDS、TEM、EIS、ICP -AES和充放电测试等手段对其结构,形貌及电化学性能进行表征。研究结果表明,AZO包覆层有效的阻止了LiMn₂O₄颗粒和电解液的直接接触,抑制了高温下锰溶解,明显改善了LiMn₂O₄的高温循环性能。1.5wt% AZO包覆的LiMn₂O₄正极材料在高温(55℃)1C时,首次放电比容量为114 mAh·g^-1,经过100次循环后,容量保持率仍高达95.4%,远高于未包覆LiMn₂O₄的70.6%。此外,1.5wt% AZO包覆的LiMn₂O₄表现出了优越的大倍率放电性能,在10C下放电比容量能达到99 mAh·g^-1。     

二价与四价金属离子等摩尔共掺杂的锂离子电池正极材料LiMn1.9Mg0.05Ti0.05O4的制备与表征

以氢氧化锂、乙酸锰、硝酸镁和钛酸丁酯为原料, 以柠檬酸为螯合剂, 采用溶胶-凝胶法制备了二价镁离子与四价钛离子等摩尔共掺杂的尖晶石型锂离子电池正极材料LiMn_1.9Mg_0.05Ti_0.05O₄. 采用热重分析(TGA), X射线衍射(XRD), 扫描电子显微镜(SEM), 透射电子显微镜(TEM)和电化学性能测试(包括循环伏安(CV)和电化学交流阻抗谱(EIS)测试)对所得样品的结构、形貌及电化学性能进行了表征. 结果表明: 780℃下煅烧12 h 得到了颗粒均匀细小的尖晶石型结构的LiMn_1.9Mg_0.05Ti_0.05O₄材料, 该材料具有良好的电化学性能, 在室温下以0.5C倍率充放电, 在4.35-3.30 V电位范围内放电比容量达到126.8 mAh·g^-1, 循环50 次后放电比容量仍为118.5mAh·g^-1, 容量保持率为93.5%. 在55℃高温下循环30次后的放电比容量为111.9 mAh·g^-1, 容量保持率达到91.9%, 远远高于未掺杂的LiMn₂O₄的容量保存率. 二价镁离子与四价钛离子等摩尔共掺杂LiMn₂O₄, 改善了尖晶石锰酸锂的电子导电和离子导电性能, 使其倍率性能和高温性能都得到了明显的提高.     

球形尖晶石LiMn2O4掺杂钇的性能研究

利用控制结晶方法, 在前驱体碳酸锰中共沉淀掺杂适量的钇, 得到球形掺杂钇的碳酸锰, 在540 ℃预烧后, 与锂盐一起焙烧, 可以得到高活性的掺钇球形尖晶石LiMn₂O₄. XRD分析表明, 产物中无杂相产生. 研究表明, 掺杂钇与掺杂其它金属离子的特性不一样, 钇具有催化特性, 掺杂钇可以提高尖晶石LiMn₂O₄中锰的活性. 掺钇使得更多的Mn^3＋参加电化学反应, 增加容量; 但同时也使更多的锰与电解液反应, 造成锰的溶解, 容量损失. 掺钇量越多, 锰的溶解量越大. 因此, 合适的掺杂量对于保证产品良好的电化学性能至关重要. 实验证明, 掺钇0.5%的产品Li(Y_0.005Mn_0.995)₂O₄具有较好的电化学性能. 其常温初始比容量为130 mAh•g^－1, 大于纯相的锰酸锂的125 mAh•g^－1, 100次循环后比容量为120 mAh•g^－1, 容量保持率为92.3%.     

Si-Fe复合SiOx/石墨基负极材料的电化学性能

针对硅氧基负极材料的主要缺陷,在SiO_x/石墨基负极材料中巧妙地引入了Si-Fe、SnO₂合金化合物,以改善其电化学性能,并通过机械球磨、喷雾干燥和高温热解策略制备了一系列硅氧基复合负极材料。采用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、能谱仪(EDS)和恒流充放电测试仪对复合材料的物相、微观形貌及电化学性能进行了表征。电化学测试结果表明,复合质量分数5% Si-Fe的目标材料充电容量高达443.4 mAh·g^-1,首次库仑效率达75.2%,循环310圈之后容量仍有369.1 mAh·g^-1,容量保持率为81.0%(相对第11圈);同时,经Si-Fe复合之后,锂离子扩散速率得到了明显改善。     

层状LiCo1/3Ni1/3Mn1/3O2正极材料的合成及电化学性能研究

采用液相法在800 ℃空气中烧结20 h合成出层状LiCo_1/3Ni_1/3Mn_1/3O₂正极材料。通过XRD、IR、SEM、XPS和电化学性能测试考察了产物的组成、结构、形貌及电化学性能。结果表明，所合成的LiCo_1/3Ni_1/3Mn_1/3O₂为六方单相，层状结构发育完善；产物呈球形且粒度小，分布窄，平均粒径为0.3 μm。以1 mA·cm^-2的电流密度，在2.7～4.3 V区间进行充放电测试，前4周的充放电比容量分别为168/160 mAh·g^-1、169/162 mAh·g^-1、165/160 mAh·g^-1、163/158 mAh·g^-1，循环性能优良。循环伏安实验表明，该材料在3.9 V附近出现了一对对称性好的氧化还原峰。     

多环芳二酐型聚酯亚胺膜的透气性能

多环芳二酐型聚酯亚胺膜的透气性能李悦生，丁孟贤，徐纪平（浙江大学高分子科学与工程研究所，杭州，３１００２７）（中国科学院长春应用化学研究所）关键词聚醚酰亚胺，聚酯酰亚胺，膜，透气性通常的聚酰亚胺加工性能较差，在芳环二酐的苯环间引入醚键等柔性基团后，其...     

微量元素与疾病诊断治疗的研究现状及展望

对国内外微量元素与疾病的关系及其诊断治疗的研究现状及研究动向进行了综述，包括：微量元素与地方病、癌肿、心血管病、糖尿病、眼病、神经系统病等。参考文献72篇。     

Determination and study on residue and dissipation of benazolin-ethyl and quizalofop-p-ethyl in rape and soil

A QuEChERS (quick, easy, cheap, effective, rugged, and safe) method for the determination of benazolin-ethyl and quizalofop-p-ethyl in rape and soil by high-performance liquid chromatography-tandem mass spectrometry has been developed in this study. The residue and dissipation of benazolin-ethyl and quizalofop-p-ethyl in rape and soil were determined with the developed method. The half-lives of benazolin-ethyl in rape straw and soil were 3.7–5.1 days and 14.3–26.3 days, respectively. The half-lives of quizalofop-p-ethyl in rape straw and soil were 5.0-6.1 days and 0.3–9.7 days, respectively. The residue of benazolin-ethyl and quizalofop-p-ethyl in rapeseed and soil were below the detection limit (i.e., 0.5?mg?kg^?1, the maximum residue level of European Union for quizalofop-p-ethyl).     

Synthesis and Optical and Redox Properties of Symmetric and Asymmetric BODIPYs

Herein, we present the synthetic route and the photophysical, electrochemical as well as laser properties of novel red‐emitting boron‐dipyrromethenes (BODIPYs) bearing arylethyne moieties. Such functionality is added along the main axis of the chromophore leading to single‐ and double‐substituted derivatives. The relationship between the dye structure and the lasing properties is studied in detail with the help of the photophysical and electrochemical properties as well as quantum mechanical simulations. The asymmetric substitution of the parent dye induces inhomogeneities in the charge distribution, which leads to an overall loss of the fluorescence capacity, mainly in polar media. Such non‐radiative deactivation processes can be softened by decreasing the electron‐donor ability of the substituent or even avoided by symmetrical substitution. Thus, grafting of the arylethyne moieties at the longitudinal axis of the indacene core results in an effective strategy to develop red‐edge BODIPYs with highly efficient and photostable laser emission.     

Ti-V基储氢合金及其氢化物的物相结构与组分优化设计

Ti-V基储氢合金在室温、常压下即可表现出良好的储氢特性,且质量储氢容量明显高于传统AB₅型储氢合金,从而在氢气的精制和回收、运输和储存及热泵等方面有较早的应用。 此外,在混合气体分离、核反应堆中处理氢的同位素、镍氢电池及燃料电池负极材料等方面也得到了广泛的研究与关注。 基于目前Ti-V基储氢合金的研究现状,概述了该类合金的优势、限制性因素(包括成因)及改性手段。 此外,为了进一步理解Ti-V基合金储氢机理、构建合金组分与储氢特性之间的对应关系,本工作重点围绕Ti-V基储氢合金及其氢化物的结构、组分优化设计展开综述,并对其未来研究方向做出展望。     

钒与糖代谢及糖尿病

微量元素钒作为生物体内必需元素，经证实有很重要的生理学功能，与机体糖代谢有十分密切的关系，且能降低糖尿病动物模型的高血糖，极有可能被开发为治疗糖尿病的药物。     

Conformations and steric and stacking interactions of trisubstituted ureas and thioureas with alkyl and phenyl groups

The monomeric ν(N—H) vibrations of various trisubstituted ureas of the R₂UPh type and -thioureas of the R₂TUPh type have been studied. The trans—out isomerism in the former and the trans—out—cis isomerism in the latter are discussed from the point of view of steric effect. The monomeric ν(N—H) vibrations of RPhUPh and RPhTUPh are also examined. The single band appearing in the spectrum of both ureas is characteristic of the cis form; this suggests the existence of phenyl—phenyl interaction (the stacking interaction proposed by Galabov et al. [10]). Behavior of ν(N—H) vibrations at several concentrations is shown to be clearly different in the three forms (trans, out and cis). The presence of the cis form is confirmed by solvent effect experiments.     

Synthesis of Tyrosol and Hydroxytyrosol Glycofuranosides and Their Biochemical and Biological Activities in Cell-Free and Cellular Assays

Tyrosol (T) and hydroxytyrosol (HOT) and their glycosides are promising candidates for applications in functional food products or in complementary therapy. A series of phenylethanoid glycofuranosides (PEGFs) were synthesized to compare some of their biochemical and biological activities with T and HOT. The optimization of glycosylation promoted by environmentally benign basic zinc carbonate was performed to prepare HOT α-L-arabino-, β-D-apio-, and β-D-ribofuranosides. T and HOT β-D-fructofuranosides, prepared by enzymatic transfructosylation of T and HOT, were also included in the comparative study. The antioxidant capacity and DNA-protective potential of T, HOT, and PEGFs on plasmid DNA were determined using cell-free assays. The DNA-damaging potential of the studied compounds for human hepatoma HepG2 cells and their DNA-protective potential on HepG2 cells against hydrogen peroxide were evaluated using the comet assay. Experiments revealed a spectrum of different activities of the studied compounds. HOT and HOT β-D-fructofuranoside appear to be the best-performing scavengers and protectants of plasmid DNA and HepG2 cells. T and T β-D-fructofuranoside display almost zero or low scavenging/antioxidant activity and protective effects on plasmid DNA or HepG2 cells. The results imply that especially HOT β-D-fructofuranoside and β-D-apiofuranoside could be considered as prospective molecules for the subsequent design of supplements with potential in food and health protection.     

Ferrocene and ferrocenium modified clays and their styrene and EVA composites

In this work, ferrocene- and ferrocenium-containing salts were employed to modify montmorillonite. X-ray measurements show an increase in the interlayer spacing upon clay modification, which means that the larger and more organophilic cations were inserted into the gallery space of montmorillonite. Attempts to prepare nanocomposites of polystyrene and ethylene vinyl acetate copolymers lead to immiscible systems; the morphology of these systems was elucidated with TEM, XRD and cone calorimetry. The thermal stability of the composites is greater than that of the virgin polymer.