Characterization of ramiform precipitates formed on SiO2–TiO2 gel coatings by electric field hot water treatment

The shape of the precipitates on sol–gel derived SiO₂–TiO₂ coatings at the negative electrode changed from granular to ramiform by applying an electric field to the substrates during a hot water treatment, whereas such changes in the shape of titania nanocrystals with the electric field were not observed at the positive electrode. The granular and ramiform precipitates were identified as anatase (TiO₂) and hydrated titania (n(TiO₂) · mH₂O), respectively. The ramiform shape of the titania precipitates became significant with increasing the applied voltage, while the coatings gradually became dark-colored due to the reduction of Ti⁴⁺ to Ti³⁺. The coatings with ramiform precipitates showed an excellent wettability for water.     

Influence of thermal and thermoelectric treatments on structure and electric properties of B2O3–Li2O–Nb2O5 glasses

A transparent glass with the composition 60B₂O₃–30Li₂O–10Nb₂O₅ (mol%) was prepared by the melt quenching technique. The glass was heat-treated with and without the application of an external electric field. The as-prepared sample was heat-treated (HT) at 450, 500 and 550 °C and thermoelectric treated (TET) at 500 °C. The following electric fields were used: 50 kV/m and 100 kV/m. Differential thermal analysis (DTA), X-ray diffraction (XRD), scanning electron microscopy (SEM), Raman, dc and ac conductivity, as a function of temperature, were used to investigate the glass and glass-ceramics properties. LiNbO₃ crystals were detected, by XRD, in the 500 °C HT, 550 °C HT and 500 °C TET samples. The presence of an external electric field, during the heat-treatment process, improves the formation of LiNbO₃ nanocrystals at lower temperatures. However, in the 550 °C HT and in the TET samples, Li₂B₄O₇ was also detected. The value of the σ_dc decreases with the rise of the applied field, during the heat-treatment. This behavior can indicate an increase in the fraction of the LiNbO₃ crystallites present in these glass samples. The dc and ac conduction processes show dependence on the number of the ions inserted in the glass as network modifiers.The Raman analysis suggests that the niobium ions are, probably, inserted in the glass matrix as network formers.These results reflect the decisive effect of temperature and electric field applied during the thermoelectric treatment in the structure and electric properties of glass-ceramics.     

Thermal and electric transport properties of (60−x)V2O5–xAs2O3–20Fe2O3–10CaO–10Li2O unconventional glassy system

This paper presents the results of kinematical studies of glass transition and crystallization in the unconventional glassy system (60?x)V₂O₅–xAs₂O₃–20Fe₂O₃–10CaO–10Li₂O (x = 0, 10, 20, 30, 40 mol%) using differential scanning calorimetry (DSC). The glass transition temperatures (T_g), the onset crystallization temperatures (T_c), and the peak temperatures of crystallization (T_p) were found to be dependent on the compositions and the heating rates. From the dependence on heating rates of (T_g) and (T_p) the activation energy for glass transition (E_g) and the activation energy for crystallization (E_c) are calculated. The thermal stability of (60?x)V₂O₅–xAs₂O₃–20Fe₂O₃–10CaO–10Li₂O was evaluated in term of, criteria ΔT = T_c ? T_g. All the results confirm that the thermal stability increase with increasing As₂O₃ contents. From the electric–dielectric measurements it was found that, σ_dc, σ_ac(ω) and θ_D/2 decrease with increasing As₂O₃ contents. It is also observed that the dielectric constant (ε₁(ω)) and the loss factor (tan δ) decrease with increasing As₂O₃ contents in this glass system.