Growth and Raman spectroscopic characterization of As4S4 (II) single crystals

As described by Kutoglu (1976 [16]), single crystals of As₄S₄ (II) phase have been grown using a new two-step synthesis that drastically increases the reproducibility that is attainable in synthetic experiments. First, through photo-induced phase transformation, pararealgar powder is prepared as a precursor instead of AsS melt. Then it is dissolved and recrystallized from CS₂ solvent. Results show that single crystals of the As₄S₄ (II) phase were obtained reproducibly through the dissolution–recrystallization process. Single crystals of As₄S₄ (II) obtained using this method were translucent and showed a uniform yellow-orange color. The crystal exhibits a platelet-like shape as a thin film with well-developed faces (0 1 0) and (0 1¯ 0). The grown crystals are as large as 0.50×0.50×0.01 mm. They were characterized using powder and single crystal X-ray diffraction techniques to confirm the phase identification and the lattice parameters. The As₄S₄ (II) phase crystallizes in monoclinic system with cell parameters a=11.202(4) Å, b=9.954(4) Å, c=7.142(4) Å, β=92.81(4)°, V=795.4(6) Å³, which shows good agreement with the former value. Raman spectroscopic studies elucidated the behavior of the substance and the relation among phases of tetra-arsenic tetrasulfide.     

Growth and properties of Pb[(Zn1/3Nb2/3)0.91Ti0.09]O3 single crystals directly from melt

Pb[(Zn_1/3Nb_2/3)_0.91Ti_0.09]O₃ (PZNT91/9) single crystals were grown by a modified Bridgman method directly from melt using an allomeric Pb[(Mg_1/3Nb_2/3)_0.69Ti_0.31]O₃ (PMNT69/31) single crystal as a seed. X-ray diffraction (XRD) measurement confirmed that the as-grown PZNT91/9 single crystals are of pure perovskite structure. Electrical properties and thermal stabilization of PZNT91/9 crystals grown directly from melt exhibit different characters from those of PZNT91/9 crystals grown from flux, although segregation and the variation of chemical composition are not seriously confirmed by X-ray fluorescence analysis (XPS). The [0 0 1]-oriented PZNT91/9 crystals cut from the middle part of the as-grown crystal boules exhibit broad dielectric-response peaks at around 105 °C, accompanied by apparent frequency dispersion. The values of piezoelectric constant d₃₃, remnant polarization P_r, and induced strain are about 1800–2200 pC/N, 38.8 μC/cm², and 0.3%, respectively, indicating that the quality of PZNT crystals grown directly from melt can be comparable to those of PZNT91/9 single crystals grown from flux. However, further work deserves attention to improve the dielectric properties of PZNT crystals grown directly from melt. Such unusual characterizations of dielectric properties of PZNT crystals grown directly from melt are considered as correlating with defects, microinhomogeneities, and polar regions.     

Study on the properties of CuInSe2 ingots grown from the melt using stoichiometric and non-stoichiometric charges

CuInSe₂ (CIS) ingots have been prepared by direct reaction of stoichiometric and non-stoichiometric proportions of high-purity Cu, In and Se. Two approaches, namely the one-ampoule process (quartz crucible) and two-ampoule process (graphite crucible) were investigated to grow the crystals, using starting charges with excess copper, and (nearly stoichiometric and with excess indium), respectively. The effect of deviation from stoichiometry in the charge on the physical properties of the resulting polycrystals is presented. Compositional analysis of the best part of the ingots with starting metals ratio (Cu/In) greater than or equal to 1 showed that the matrix preserved the original character of the charge and evidenced that the CIS chalcopyrite structure, -CIS, tolerates well a large In excess. In contrast, the composition of the crystal prepared with a 10% Cu excess was nearly-stoichiometric, with chemical images revealing the formation of heterogeneous phases besides -CIS. The inclusions precipitation was found to increase toward the ingot base. Interestingly, powder X-ray diffraction measurements revealed the presence of secondary phases rather in all the samples. The corresponding diffraction peaks were however few and very weak, with intensities of less than 3% the maximum value recorded for the CIS (1 1 2) plane.     

Flux growth and characterizations of NdPO4 single crystals

Neodymium phosphate single crystals, NdPO₄, have been grown by a flux growth method using Li₂CO₃-2MoO₃ as a flux. The as-grown crystals were characterized by X-ray powder diffraction(XRPD), differential thermal analysis (DTA) and thermogravimetric analysis (TG) techniques. The results show that the as-grown crystals were well crystallized. The crystal was stable over the temperature range from 26 to 1200 °C in N₂. The specific heat of NdPO₄ crystal at room temperature was 0.41 J/g °C. The absorption and the fluorescence spectra of NdPO₄ crystal were also measured at room temperature.     

Resistivity distribution of silicon single crystals using codoping

Numerous studies including continuous Czochralski method and double crucible technique have been reported on the control of macroscopic axial resistivity distribution in bulk crystal growth. The simple codoping method for improving the productivity of silicon single-crystal growth by controlling axial specific resistivity distribution was proposed by Wang [Jpn. J. Appl. Phys. 43 (2004) 4079]. Wang [J. Crystal Growth 275 (2005) e73] demonstrated using numerical analysis and by experimental results that the axial specific resistivity distribution can be modified in melt growth of silicon crystals and relatively uniform profile is possible by B–P codoping method. In this work, the basic characteristic of 8 in silicon single crystal grown using codoping method is studied and whether proposed method has advantage for the silicon crystal growth is discussed.     

Sn3O4 single crystal nanobelts grown by carbothermal reduction process

This article reports on the growth of single crystal Sn₃O₄ nanobelts and SnO by a carbothermal reduction process in two different regions of a furnace tube. Even though intermediate tin oxide compounds (Sn₃O₄) have been observed experimentally, the study of structures based on them is a challenging task. Characterization data allowed us to propose that Sn₃O₄ nanobelts grew by vapor–solid mechanism while SnO grew by self-catalyst vapor–liquid–solid mechanism. Electrical measurements of a single Sn₃O₄ nanobelt were performed at different temperatures, revealing undoped semiconductor characteristics.     

Growth and spectral properties of Nd-doped Sr3Y(BO3)3 crystal

A new crystal of Nd³⁺:Sr₃Y(BO₃)₃ with dimension up to 25×35 mm² was grown by Czochralski method. Absorption and emission spectra of Nd³⁺: Sr₃Y(BO₃)₃ were investigated . The absorption band at 807 nm has a FWHM of 18 nm. The absorption and emission cross sections are 2.17×10⁻²⁰ cm² at 807 nm and 1.88×10⁻¹⁹ cm² at 1060 nm, respectively. The luminescence lifetime τ_f is 73 μs at room temperature     

Growth and characterization of CdSe single crystals by modified vertical vapor phase method

Good quality, large single crystals of CdSe were grown by the modified growth method (i.e., vertical unseeded vapor phase growth with multi-step purification of the starting material in the same quartz ampoule without any manual transfer between the steps). Lower temperature gradients (8–9°C/cm) at the growth interface were used for the crystal growth. As-grown CdSe crystals was characterized by X-ray diffraction, scanning electron microscopy, energy dispersive analyzer of X-rays, high-resistance instrument measurement, and etch-pit observation. It is found that there are two cleavage faces of (1 0 0) and (1 1 0) orientations on the crystal, the resistivity is about 10⁸ Ω cm, and the density of etch pits is about 10^3–4/cm². The crystal was cut into wafers and was fabricated into detectors. The detectors were tested using an ²⁴¹Am radiation source. γ-ray spectra at 59.5 keV were obtained. The results demonstrated that the quality of the as-grown crystals was good. The crystals were useful for fabrication of room-temperature-operating nuclear radiation detectors. Therefore, the modified growth technique is a promising, convenient, new method for the growth of high-quality CdSe single crystals.     

Ambient-condition growth of superconducting YBa2Cu4O8 single crystals using KOH flux

YBa₂Cu₄O₈ is a stoichiometric oxide superconductor of T_c80 K. Unlike YBa₂Cu₃O_7−δ, this compound is free from oxygen vacancy or twin formation and does not have any microscopic disorder in the crystal. Doping with Ca raises its T_c to 90 K. The compound is a promising superconductor for technological application. Up to now, single crystals have not been grown without using specialized apparatus with extremely high oxygen pressure up to 3000 bar and at over 1100 °C due to the limited range of reaction kinetics of the compound. This fact has delayed the progress in the study of its physical properties and potential applications. We present here a simple growth method using KOH as flux that acts effectively for obtaining high-quality single crystals in air/oxygen at the temperature as low as 550 °C. As-grown crystals can readily be separated from the flux and exhibit a perfect orthorhombic morphology with sizes up to 0.7×0.4×0.2 mm³. Our results are reproducible and suggest that the crystals can be grown using a conventional flux method under ambient condition.     

Growth and optical properties of self-frequency-doubling laser crystal Yb:LuAl3(BO3)4

Single crystal of Yb:LuAl₃(BO₃)₄(Yb:LuAB) was grown by the flux method for the first time. The cell parameters of the grown crystal were estimated by X-ray diffraction analysis. The result indicates the symmetry of trigonal space group R32, with lattice parameters a=b=9.26372 Å, c=7.21405 Å, V=536.14 Å³, and Z=4. The absorption and emission spectra of Yb:LuAB crystal at room temperature has also been studied. The fluorescence lifetime for Yb:LuAB crystal is about 1.48 ms. The heat capacity was measured from 25 to 500 °C. Its second harmonic generation efficiency in LuAl₃(BO₃)₄ crystal is 3–4 times that of KDP crystal. These results show that Yb:LuAB crystal would be a potential self-frequency-doubling laser crystal.     

Flux growth of PbMg1/3Ta2/3O3 single crystals

Single crystals of PbMg_1/3Ta_2/3O₃ (PMT) were grown by the flux method. The PbO–Pb₃O₄–B₂O₃ system was used as a solvent. Transparent and light yellow PMT single crystals of rectangular shape and dimensions up to 10×6×4 mm³ were obtained. For the applied growth conditions only, the crystals of the perovskite structure were grown. X-ray diffraction tests showed that at room temperature PMT exhibits cubic symmetry with lattice parameter a=4.042(1) Å. Dielectric studies pointed to relaxor properties of PMT. The characteristic broad and frequency-dependent maximum of dielectric permittivity was observed at 179.7 K (1 kHz).     

Growth and spectral properties of Nd:LaVO4 crystal

This paper reports the growth and spectral properties of 3.5 at% Nd³⁺:LaVO₄ crystal with diameter of 20×15 mm² which has been grown by the Czochralski method. The spectral parameters were calculated based on Judd–Ofelt theory. The intensity parameters Ω_λ are: Ω₂=2.102×10⁻²⁰ cm², Ω₄=3.871×10⁻²⁰ cm², Ω₆=3.235×10⁻²⁰ cm². The radiative lifetime τ_r is 209 μs and calculated fluorescence branch ratios are: β₁(0.88μm)=45.2, β₂(1.06μm)=46.7, β₃(1.34μm)=8.1. The measured fluorescence lifetime τ_f is 137 μm and the quantum efficiency η is 65.6%. The absorption band at 808 nm wavelength has an FWHM of 20 nm. The absorption and emission cross sections are 3×10⁻²⁰ and 6.13×10⁻²⁰ cm², respectively.     

Defect characterization and composition distributions of mercury indium telluride single crystals

A mercury indium telluride (MIT) ingot was grown by the vertical Bridgman method. The defects in MIT crystals were characterized by the chemical etching method. A defect etchant for MIT crystals was developed. The etch pits of dislocations, microcracks and boundary was observed by scanning electron microscopy. It was elucidated that the etch pits density of dislocations of MIT wafers was about 4×10⁵ cm⁻². Te and In reduced at the grain boundaries, but were homogeneously distributed within the grains in the as-grown MIT crystals. The distribution of In in MIT crystals along the growth direction and radial direction was analyzed by electronic probe microscopy. It was found that In concentration was higher in the initial part and lower in the final part of the MIT ingot, which indicated that the segregation coefficient of In in MIT crystals was 1.15. The radial In concentration increased from the center to edge of the wafers and homogeneous in the middle part.     

Growth and characterization of ferromagnetic shape memory alloy Co50Ni20FeGa29 single crystals

Single crystals of Co₅₀Ni₂₀FeGa₂₉ with B2 phase have been obtained in a deep supercooling condition. The interface-facets and the segregation effect lead to the formation of ordered defects that store a directional internal stress. These defects give to a large energy barrier that leads to a very sharp martensitic transformation within a temperature window of only 2 K. The single crystals show good shape memory effect and superelasticity, which are anisotropic between the growth direction [0 0 1] and its equivalent direction [0 1 0]. The anisotropic behaviors are attributed to the directional internal stress caused by the ordered defects.     

Dynamic process of crystallization of Sb2Se3 from Sb50Se50 amorphous film

Dynamics of crystallization of amorphous antimony-selenium film deposited on carbon substrate have been studied by the high-resolution transmission electron microscopy. The amorphous film was suddenly crystallized at 200°C by heating in vacuum. By the electron beam irradiation crystallization occurred at the focused electron beam region in the amorphous film. The growth process of crystallization by electron beam irradiation was recorded on a video image at the atomic resolution mode. The growth front of crystallization showed nano-concave and -convex shapes. The recrystallization with the different orientation at the first grown crystal have been found, and discussed as the influence of remaining antimony crystallites at the first crystallized film region.     

Thermal and laser properties of Yb:YAl3(BO3)4 crystal

Large optical-quality Yb:YAl₃(BO₃)₄(Yb:YAB) crystals have been grown by the flux method. The thermal properties of Yb:YAB crystal were measured for the first time. The thermal properties of Yb:YAB crystal with different Yb³⁺ ion concentrations are also reported. The results show that the ytterbium concentration influences the properties of Yb:YAB crystal. The specific heat decreases with the increase of Yb³⁺ ion concentrations in the experiment range. Apparently, the thermal expansion coefficient increases along the c-direction with the increase of Yb³⁺ ion concentrations, while it changes slightly along the a-direction. The output laser in 1120–1140 nm ranges has been demonstrated pumped by InGaAs laser. The slope efficiency is 3.8%. The self-frequency-doubling output power of 1 mW is achieved.     

Raman scattering study of crystalline and melting states of BaO·2B2O3

Melting and crystallization scenarios of barium tetraborate BaB₄O₇ (BaO·2B₂O₃) are studied in situ by Raman spectroscopy. It is shown that the scenario depends on the temperature–time history of melt. Crystallization conditions of the beta modification of barium tetraborate (β-BaB₄O₇) from a stoichiometric glass structure BaO·2B₂O₃ were investigated.     

Growth, thermal and spectral properties of Nd-doped NaGd(MoO4)2 crystal

Nd³⁺-doped NaGd(MoO₄)₂ crystal with dimensions were grown by Czochralski method. Nd³⁺:NaGd(MoO₄)₂ crystal melts at 1182 °C. The hardness of Nd³⁺:NaGd(MoO₄)₂ crystal is 334 VDH. The specific heat is 72.6 cal/mol K. The thermal expansion coefficients are for c-axis and for a-axis, respectively. The absorption cross-sections of Nd³⁺:NaGd(MoO₄)₂ crystal are with a FWHM of 9 nm at the 804 nm for π-polarization and with a FWHM of 17 nm at 807 nm for σ-polarization, respectively. The emission cross-section σ_em are at 1063 nm for π-polarization and 1.94×10^-20 at 1070 nm cm² for σ-polarization, respectively. The fluorescence lifetime τ_f is 93.9 μs at room temperature.     

Synthesis, thermal and magnetic properties of new metal iodate: (LiFe1/3)(IO3)2

This paper reports the detail synthesis of a new kind of metal iodate, anhydrous (LiFe_1/3)(IO₃)₂, from aqueous solutions. The synthesized compound shows spinal morphology and is chemical stable up to 400°C. The iodate shows paramagnetic behavior from room temperature down to 4.2 K. At room temperature, the new compound has a hexagonal structure with the lattice parameters a=5.4632(2) Å, c=5.0895(6) Å, Z=1, space group of P6₃.     

Synthesis and characterization of large single crystals of NpPd3 by flux method

Synthesis of the active [Ni–Fe]-hydrogenase in prokaryotes requires a series of ancillary maturation factors. Among them, the HypF maturation factor is a multidomain 82 kDa protein, whose N-terminal domain displays sequence and structural similarities to acylphosphatases. Acylphosphatases are small enzymes that are able to catalyze carboxyl-phosphate bond hydrolysis in acylphosphates, as well as in nucleoside di- and tri-phosphates and in arylphosphates. Here, we present a crystallographic comparison between microgravity and earth-grown crystals of the HypF N-terminal domain. Both crystals were of excellent quality, thereby allowing us to collect very high resolution datasets. A detailed analysis of data collection and refinement statistics, together with an analysis of the diffraction pattern showed that microgravity would appear to further improve the internal order of crystals.