Preparation and characterization of Cu(In,Ga)(Se,S)2 films without selenization by co-sputtering from Cu(In,Ga)Se2 quaternary and In2S3 targets

In this study, Cu(In,Ga)(Se,S)₂ (CIGSS) thin films were deposited onto a bi-layer Mo coated soda-lime glass by co-sputtering a chalcopyrite Cu(In,Ga)Se₂ (CIGS) quaternary alloy target and an In₂S₃ binary target. A one-stage annealing process was performed to form CIGSS chalcopyrite phase without post-selenization. Experimental results show that CIGSS films were prepared by the proposed co-sputter process via CIGS (70 W by radio frequency) and In₂S₃ (30 W by direct current) with a substrate temperature of 373 K, working pressure of 0.67 Pa, and one-stage annealing at 798 K for 30 min. The stoichiometry ratios of the CIGSS film were Cu/(In + Ga) = 0.92, Ga/(In + Ga) = 0.26, and Se/(S) = 0.49 that approached device-quality stoichiometry ratio (Cu/(In + Ga) < 0.95, Ga/(In + Ga) < 0.3, and (Se/S) ≈ 0.5). The resistivity of the sample was 14.8 Ω cm, with a carrier concentration of 3.4 × 10¹⁷ cm⁻³ and mobility of 1.2 cm² V⁻¹ s⁻¹. The resulting film exhibited p-type conductivity with a double graded band-gap structure.     

Characterization of AgInS2 thin films prepared by vacuum evaporation

We characterized AgInS₂ thin films prepared by vacuum evaporation. In the case of thin films annealed at 400 °C, diffraction peaks were observed only for the chalcopyrite AgInS₂ phase. The chemical composition of the thin films annealed at 400 °C was 26.5 at% Ag, 23.8 at% In, and 49.7 at% S. PL spectra of the AgInS₂ thin films at 10.7 K showed peaks at 1.70, 1.80, and 1.83 eV. The PL peak at1.80 eV was attributed to sulfur deficiency.     

Investigations on co-evaporated Cu2SnSe3 and Cu2SnSe3-ZnSe thin films

Cu₂SnSe₃ is an important precursor material for the growth of Cu₂ZnSnSe₄, an emerging solar cell absorber layer via solid state reaction of Cu₂SnSe₃ and ZnSe. In this study, we have grown Cu₂SnSe₃ (CTSe) and Cu₂SnSe₃-ZnSe (20%) films onto soda-lime glass substrates held at 573 K by co-evaporation technique. The effect of annealing of these films at 723 K for an hour in selenium atmosphere is also investigated. XRD studies of as-deposited Cu₂SnSe₃ and Cu₂SnSe₃-ZnSe films indicated SnSe as secondary phase which disappeared on annealing. The direct optical band gap of annealed Cu₂SnSe₃ and Cu₂SnSe₃-ZnSe films were found to be 0.90 eV and 0.94 eV respectively. Raman spectroscopy studies were used to understand the effect of ZnSe on the properties of Cu₂SnSe₃.     

Influence of postdeposition annealing on structural properties and electrical characteristics of thin Tm2O3 and Tm2Ti2O7 dielectrics

We describe the structural properties and electrical characteristics of thin thulium oxide (Tm₂O₃) and thulium titanium oxide (Tm₂Ti₂O₇) as gate dielectrics deposited on silicon substrates through reactive sputtering. The structural and morphological features of these films were explored by X-ray diffraction, X-ray photoelectron spectroscopy, secondary ion mass spectrometry, and atomic force microscopy, measurements. It is found that the Tm₂Ti₂O₇ film annealed at 800 °C exhibited a thinner capacitance equivalent thickness of 19.8 Å, a lower interface trap density of 8.37 × 10¹¹ eV⁻¹ cm⁻², and a smaller hysteresis voltage of ∼4 mV than the other conditions. We attribute this behavior to the Ti incorporated into the Tm₂O₃ film improving the interfacial layer and the surface roughness. This film also shows negligible degrees of charge trapping at high electric field stress.     

Annealing effects on the structural and electrical transport properties of n-type Bi2Te2.7Se0.3 thin films deposited by flash evaporation

N-type Bi₂Te_2.7Se_0.3 thermoelectric thin films with thickness 800 nm have been deposited on glass substrates by flash evaporation method at 473 K. Annealing effects on the thermoelectric properties of Bi₂Te_2.7Se_0.3 thin films were examined in the temperature range 373-573 K. The structures, morphology and chemical composition of the thin films were characterized by X-ray diffraction, field emission scanning electron microscope and energy dispersive X-ray spectroscopy, respectively. Thermoelectric properties of the thin films have been evaluated by measurements of the electrical resistivity and Seebeck coefficient at 300 K. The Hall coefficients were measured at room temperature by the Van der Pauw method. The carrier concentration and mobility were calculated from the Hall coefficient. The films thickness of the annealed samples was measured by ellipsometer. When annealed at 473 K, the electrical resistivity and Seebeck coefficient are 2.7 mΩ cm and −180 μV/K, respectively. The maximum of thermoelectric power factor is enhanced to 12 μW/cm K².     

Laser synthesis of thin layers of In4Se3, In4Te3 and modification of their structure and characteristics

Trends of structural modifications and phase composition occurring in In₄Se₃ thin films and In₄Se₃-In₄Te₃ epitaxial heterojunctions under laser irradiations have been investigated. Dynamics of the layer structure modification, depending on laser modes, i.e. pulse duration τ = 2-4 ms, irradiation intensity I₀ = 10-50 kW/cm², number of pulses N = 5-50, was studied by electron microscopy. An increase in laser influence promotes enlargement of the layer grains and transformation of their polycrystalline structure towards higher degree of stoichiometry. As a result of laser solid restructuring heterojunctions of In₄Se₃-In₄Te₃, being photosensitive within 1.0-2.0 μm and showing fast time of response, have been obtained. Laser modification of structure enables one to optimize electrical and optical properties of functional elements on the base of thin films and layers of In₄Se₃, In₄Te₃, widely used as infrared detectors and filters.     

Structural and optical properties of Er, Yb co-doped Y2O3 thin films

Thin Er³⁺, Yb³⁺ co-doped Y₂O₃ films were grown on (1 0 0) YAG substrates by pulsed laser deposition. Ceramic targets having different active ion concentration were used for ablation. The influence of the rare-earth content and oxygen pressure applied during the deposition on the structural, morphological and optical properties of the films were investigated. The films deposited at the lower pressure, 1 Pa, and at 1/10 Er to Yb doping ratio are highly textured along the (1 1 1) direction of the Y₂O₃ cubic phase. In addition to the crystalline structure, these films possess smoother surface compared to those prepared at the higher pressure, 10 Pa. All other films are polycrystalline, consisting of cubic and monoclinic phases of Y₂O₃. The rougher surface of the films produced at the higher-pressure leads to higher scattering losses and different behavior of the reflectivity spectra. Optical anisotropy in the films of less than 0.004 was measured regardless of the monoclinic structure obtained. Waveguide losses of about 1 dB/cm at 633 nm were obtained for the films produced at the lower oxygen pressure.     

Characterization of chemically deposited ZnSe/SnO2/glass films: Influence of annealing in Ar atmosphere on physical properties

The Zinc Selenide (ZnSe) thin films have been deposited on SnO₂/glass substrates by a simple and inexpensive chemical bath deposition (CBD). The structural, optical and electrical properties of ZnSe films have been characterized by X-ray diffraction (XRD), Energy Dispersive X-ray Analysis (EDAX), optical absorption spectroscopy, and four point probe techniques, respectively. The films have been subjected to different annealing temperature in Argon (Ar) atmosphere. An increase in annealing temperature does not cause a complete phase transformation whereas it affects the crystallite size, dislocation density and strain. The optical band gap (E_g) of the as-deposited film is estimated to be 3.08 eV and decreases with increasing annealing temperature down to 2.43 eV at 773 K. The as-deposited and annealed films show typical semiconducting behaviour, dρ/dT > 0. Interestingly, the films annealed at 373 K, 473 K, and 573 K show two distinct temperature dependent regions of electrical resistivity; exponential region at high temperature, linear region at low temperature. The temperature at which the transition takes place from exponential to linear region strongly depends on the annealing temperature.     

Influence of heating rate on the crystalline properties of 0.7BiFeO3-0.3PbTiO3 thin films prepared by sol-gel process

0.7BiFeO₃-0.3PbTiO₃ (BFPT7030) thin films were deposited on SiO₂/Si substrates by sol-gel process. The influence of heating rate on the crystalline properties of BFPT7030 thin films were studied by X-ray diffraction (XRD), scanning electron microscope (SEM), atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS). XRD patterns of the films showed that a pure perovskite phase exists in BFPT7030 films annealed by rapid thermal annealing (RTA) technique. SEM and AFM observations demonstrated that the BFPT7030 films annealed by RTA at 700 °C for 90 s with the heating rate of 1 °C s⁻¹ could show a dense, crack-free surface morphology, and the films’ grains grow better than those of the films annealed by RTA at the same temperature with other heating rates. XPS results of the films indicated that the ratio of Fe³⁺:Fe²⁺ is about 21:10 and 9:5 for the films annealed by RTA at 700 °C for 90 s with the heating rate of 1 and 20 °C s⁻¹, respectively. That means the higher the heating rate, the higher the concentration of Fe²⁺ in the BFPT7030 thin films.     

CuInS2 thin films obtained through the annealing of chemically deposited In2S3-CuS thin films

In this work, we report the formation of CuInS₂ thin films on glass substrates by heating chemically deposited multilayers of copper sulfide (CuS) and indium sulfide (In₂S₃) at 300 and 350 °C in nitrogen atmosphere at 10 Torr. CIS thin films were prepared by varying the CuS layer thickness in the multilayers with indium sulfide. The XRD analysis showed that the crystallographic structure of the CuInS₂ (JCPDS 27-0159) is present on the deposited films. From the optical analysis it was estimated the band gap value for the CIS film (1.49 eV). The electrical conductivity varies from 3 × 10⁻⁸ to 3 Ω⁻¹ cm⁻¹ depending on the thickness of the CuS film. CIS films showed p-type conductivity.     

High temperature annealing effect on structure, optical property and laser-induced damage threshold of Ta2O5 films

Ta₂O₅ films were deposited by conventional electron beam evaporation method and then annealed in air at different temperature from 873 to 1273 K. It was found that the film structure changed from amorphous phase to hexagonal phase when annealed at 1073 K, then transformed to orthorhombic phase after annealed at 1273 K. The transmittance was improved after annealed at 873 K, and it decreased as the annealing temperature increased further. The total integrated scattering (TIS) tests and AFM results showed that both scattering and root mean square (RMS) roughness of films increased with the annealing temperature increasing. X-ray photoelectron spectroscopy (XPS) analysis showed that the film obtained better stoichiometry and the O/Ta ratio increased to 2.50 after annealing. It was found that the laser-induced damage threshold (LIDT) increased to the maximum when annealed at 873 K, while it decreased when the annealing temperature increased further. Detailed damaged models dominated by different parameters during annealing were discussed.     

Fabrication of nanostructured CuInS2 thin films by ion layer gas reaction method

CuInS₂ thin films were prepared by a two-stage ion layer gas reaction (ILGAR) process in which the Cu and In precursors were deposited on glass substrate by using a simple and low-cost dip coating technique and annealed in H₂S atmosphere at different temperatures. The influence of the annealing temperature (250-450 °C) on the particle size, crystal structure and optical properties of the CuInS₂ thin films was studied. Transmission electron microscopy revealed that the particle radii varied in the range 6-21 nm with annealing. XRD and SAED patterns indicated polycrystalline nature of the nanoparticles. The optical band gap (E_g) varied from 1.48 to 1.56 eV with variation of particle size. The variation of Urbach tail with temperature indicated higher density of the defects for the films annealed at lower temperature. From the Raman study, it was observed that the FWHM of the A₁ mode at ∼292 cm⁻¹ corresponding to the chalcopyrite phase of CuInS₂ decreased with increasing annealing temperature.     

Preparation of sol-gel ZrO2-SiO2 highly reflective multilayer films and laser-induced damage threshold characteristic

Sol-gel (ZrO₂/SiO₂)¹² ZrO₂ films were prepared by spin coating method. The reflectivity spectrum of the films was measured with a Lambda 900 spectrometer. In order to investigate laser-induced damage threshold (LIDT) characteristic of highly reflective films, one-layer ZrO₂ and SiO₂ films, two-layer ZrO₂/SiO₂ and SiO₂/ZrO₂ films were also prepared by spin coating method. LIDT of each film was measured. Damage morphology after laser irradiation was characterized by optical microscopy (Nikon E600K). The experimental results showed that the reflectivity of (ZrO₂/SiO₂)¹² ZrO₂ film at 1064 nm and 355 nm wavelength is 99.7%. The LIDT results decreases as the number of layer of films increases. All the films have similar damage morphology. The experimental results are explained by the different temperature profiles of the films.     

Annealing effect on CdS/SnO2 films grown by chemical bath deposition

The extensive investigation of the annealing effect in nitrogen atmosphere on the structural optical and electrical properties of chemically deposited CdS films on SnO₂ has been performed. The as-deposited film shows 2.45 eV band gap (E_g) and decreases with increasing annealing temperature. The film annealed at 623 K having pure hexagonal phase (a = 4.14 Å, c = 6.71 Å for [1 0 0] plane) and E_g = 2.36 eV shows 10 times higher conductivity for all temperature range, and shows two different activation energies E_a = 0.114 eV and E_a = 0.033 eV for the temperature range 395 K ≤ T ≤ 515 K and 515 K ≤ T ≤ 585 K, respectively. The structural parameters such as dislocation density, strain and optical parameters such as absorption and extinction coefficient are calculated and compared for all the films.     

Optical properties of ITO/TiO2 single and double layer thin films deposited by RPLAD

Indium tin oxide (ITO) and titanium dioxide (TiO₂) single layer and double layer ITO/TiO₂ films were prepared using reactive pulsed laser ablation deposition (RPLAD) with an ArF excimer laser for applications in dye-sensitized solar cells (DSSCs). The films were deposited on SiO₂ substrates either at room temperatures (RT) or heated to 200-400 °C. Under optimized conditions, transmission of ITO films in the visible (vis) range was above 89% for films produced at RT and 93% for the ones deposited at higher temperatures. Increasing the substrate temperature from RT to 400 °C enhances the transmission of TiO₂ films in the vis-NIR from about 70% to 92%. High transmission (≈90%) was observed for the double layer ITO/TiO₂ with a transmission cut-off above 900 nm. From the transmission data, the energies gaps (E_g), as well as the refractive indexes (n) for the films were estimated. n ≈ 2.03 and 2.04, respectively for ITO films and TiO₂ film deposited at 400 °C in the visible region. Post-annealing of the TiO₂ films for 3 h at 300 and 500 °C was performed to enhance n. The refractive index of the TiO₂ films increases with the post-annealing temperature. The direct band gap is 3.6, 3.74 and 3.82 eV for ITO films deposited at RT, 200, and 400 °C, respectively. The TiO₂ films present a direct band gap of 3.51 and 3.37 eV for as deposited TiO₂ films and when annealed at 400 °C, respectively. There is a shift of about 0.1 eV between ITO and ITO/TiO₂ films deposited at 200 °C. The shift decreases by half when the TiO₂ film was deposited at 400 °C. Post-annealing was also performed on double layer ITO/TiO₂.     

TiO2 thick films supported on reticulated macroporous Al2O3 foams and their photoactivity in phenol mineralization

TiO₂ thick films deposited on macroporous reticulated Al₂O₃ foams with pore size of 10 ppi and 15 ppi were prepared using dip coating from slurries of Aeroxide^® P25 nanopowder and precipitated titania. All prepared films have sufficiently good adhesion to the surface of the substrate also in case of strongly cracked films. No measurable release of deposited TiO₂ after repeated photocatalytic cycles was observed. The photocatalytic activity was characterized as the rate of mineralization of aqueous phenol solution under irradiation of UVA light by TOC technique. The best activity was obtained with Aeroxide^® P25 coated Al₂O₃ foam with the pore size of 10 ppi, annealed at 600 °C. The optimal annealing temperature for preparation of films from precipitated titania could be determined at 700 °C. Films prepared by sol-gel deposition technique were considerably thinner compared to coatings made of suspensions and their photocatalytic activity was significantly smaller.     

AgSbSe2 and AgSb(S,Se)2 thin films for photovoltaic applications

Silver antimony selenide (AgSbSe₂) thin films were prepared by heating sequentially deposited multilayers of antimony sulphide (Sb₂S₃), silver selenide (Ag₂Se), selenium (Se) and silver (Ag). Sb₂S₃ thin film was prepared from a chemical bath containing SbCl₃ and Na₂S₂O₃, Ag₂Se from a solution containing AgNO₃ and Na₂SeSO₃ and Se thin films from an acidified solution of Na₂SeSO₃, at room temperature on glass substrates. Ag thin film was deposited by thermal evaporation. The annealing temperature was 350 °C in vacuum (10⁻³ Torr) for 1 h. X-ray diffraction analysis showed that the thin films formed were polycrystalline AgSbSe₂ or AgSb(S,Se)₂ depending on selenium content in the precursor films. Morphology and elemental analysis of these films were done using scanning electron microscopy and energy dispersive X-ray spectroscopy. Optical band gap was evaluated from the UV-visible absorption spectra of these films. Electrical characterizations were done using Hall effect and photocurrent measurements. A photovoltaic structure: glass/ITO/CdS/AgSbSe₂/Al was formed, in which CdS was deposited by chemical bath deposition. J-V characteristics of this structure showed V_oc = 435 mV and J_sc = 0.08 mA/cm² under illumination using a tungsten halogen lamp. Preparation of a photovoltaic structure using AgSbSe₂ as an absorber material by a non-toxic selenization process is achieved.     

The enhanced conductivity and stability of AZO thin films with a TiO2 buffer layer

Aluminum doped zinc oxide (AZO) films were substitutes of the SnO₂:F films on soda lime glass substrate in the amorphous thin-film solar cells due to good properties and low cost. In order to improve properties of AZO films, the TiO₂ buffer layer had been introduced. AZO films with and without TiO₂ buffer layer were deposited on soda lime glass substrates by r.f. magnetron sputtering. Subsequently, one group samples were annealed in vacuum (0.1 Pa) at 500 °C for 120 s using the RTA system, and the influence of TiO₂ thickness on the properties of AZO films had been discussed. The XRD measurement results showed that all the films had a preferentially oriented (0 0 2) peak, and the intensity of (0 0 2) peak had been enhanced for the AZO films with TiO₂ buffer layer. The resistivity of TiO₂ (3.0 nm)/AZO double-layer film is 4.76×10⁻⁴ Ω cm with the maximum figure merit of 1.92×10⁻² Ω⁻¹, and the resistivity has a remarkable 28.7% decrease comparing with that of the single AZO film. The carrier scattering mechanism of TiO₂ (3.0 nm)/AZO double-layer film had been described by Hall measurement in different temperatures. The average transmittance of all the films exceeded 92% in the visible spectrum. Another group samples were heat treated in the quartz tube in air atmosphere, and the effect of TiO₂ thickness on thermal stability of AZO films had been discussed.     

Influence of Au thickness on the optical and electrical properties of transparent and conducting TiO2/Au/TiO2 multilayer films

Au-intermediate TiO₂/Au/TiO₂ (TAT) multilayer films were deposited by RF magnetron sputtering onto glass substrates. Changes in the optical and electrical properties of the films were investigated with respect to the thickness of the Au interlayer.The observed optical and electrical properties were dependent on the thickness of the Au interlayer. The resistivity decreased to 3.3 × 10⁻⁴ Ω cm for TiO₂ films with a 20 nm-thick Au interlayer and the optical transmittance was also influenced by the Au interlayer. Although optical transmittance deteriorated as Au thickness increased, TiO₂ films with a 5 nm-thick Au interlayer showed a relatively high optical transmittance of 80% at a wavelength of 550 nm. In addition, since a TAT film with a 5 nm-thick Au interlayer showed a relatively high work function value, it is an alternative candidate for use as a transparent anode in OLEDs and flat panel displays.     

Study of polycrystalline bulk CuIn1-xGaxTe2

Polycrystalline CuIn_1−xGa_xTe₂ bulk films were synthesized by reacting, in stoichiometric proportions, high purity Cu, In, Ga and Te in a vacuum sealed quartz ampoule. The phase structure and composition of the bulk films were analysed by X-ray diffraction and energy-dispersive X-ray analysis, respectively. The bulk samples, of p-type conductivity, are found to be near-stoichiometric, polycrystalline, with tetragonal chalcopyrite structure, predominantly oriented along a direction perpendicular to the (1 1 2) plane. Photoluminescence spectra were recorded at 7 K and 700 mW to characterize the defects and the structural quality. The main peak as a function of composition has been studied.