Cationic copolymerization of 2-methylene-5,5-dimethyl-1,3-dioxane with 2-methylene-1,3-dioxolane and 2-methylene-1,3-dioxane

Copolymers of the cyclic ketene acetals, 2-methylene-5,5-dimethyl-1,3-dioxane, 3 , (M₁) with 2-methylene-1,3-dioxolane, 4 , (M₂) or 2-methylene-1,3-dioxane, 5 , (M₂), were synthesized by cationic copolymerization. An experimental method was designed to study the reactivity of these very reactive and extremely acid sensitive cyclic ketene acetal monomers. The reactivity ratios, calculated using a computer program based on a nonlinear minimization algorithm, were r₁ = 6.36 and r₂ = 1.25 for the copolymerization of 3 with 4 , and r₁ = 1.56 and r₂ = 1.42 for the copolymerization of 3 with 5. FTIR and ¹H-NMR spectra when combined with the values of r₁ and r₂ showed that these copolymers were formed by a cationic 1,2-polymerization (ring-retained) route. Furthermore the tendency existed to form very short blocks of M₁ or M₂ within the copolymers. Cationic copolymerization of cyclic ketene acetals have the potential to be used for synthesis of novel polymers. © 1996 John Wiley & Sons, Inc.     

Copolymerization of ethylene with cyclopentene or 2‐butene with half titanocenes‐based catalysts

Half titanocenes (CpCH₂CH₂O)TiCl₂ (1), (CpCH₂CH₂OCH₃)TiCl₃ (2), and CpTiCl₃ (3), activated by methylaluminoxane (MAO) were tested in copolymerization of ethylene with internal olefins such as cyclopentene. All the catalysts were able to give incorporation of cyclopentene in polyethylene matrix. ¹³C NMR analysis of obtained copolymers showed that the catalytic systems have low regiospecificity. In fact, in ethylene–cyclopentene copolymers, cyclic olefin inserts with both 1,2 and 1,3‐enchainment. X‐ray powder diffraction analysis of these copolymers confirmed that 1,2 inserted cyclopentene units are excluded from crystalline phase, whereas 1,3‐cyclopentene units are included, giving rise to expansion of unit cell of crystalline polyethylene. Titanium‐based catalysts were investigated also in the copolymerization of ethylene with E and Z‐2‐butene. Only complex (1) was able to give copolymers and ¹³C NMR analysis of products showed 2‐3, 1‐3, and 1‐2 insertion of 2‐butene. Differential scanning calorimetry analysis displayed that ethylene–cyclopentene, as well as ethylene‐2‐butene, copolymers are crystalline and their melting point decreases by increasing the comonomer content. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 4725–4733, 2008     

Controlled cationic alternating copolymerization of various enol ethers and benzaldehyde derivatives: Effects of enol ether structures

Significant structural effects of enol ether monomers were demonstrated in cationic alternating copolymerizations with benzaldehyde derivatives (BzAs). α‐Methyl, β‐methyl, β,β‐dimethyl, and cyclic enol ethers were copolymerized with BzAs by the EtSO₃H/GaCl₃ system with 1,4‐dioxane in toluene at ?78 °C. β‐Methyl and cyclic monomers, β‐monosubstituted compounds, induced copolymerizations with BzAs, some of which were well controlled to yield alternating copolymers with controlled molecular weights (MWs) and narrow MW distributions. Conversely, an α‐methyl vinyl ether (VE) did not copolymerize with BzAs at all, probably due to its high reactivity and unfavorable ketal linkage formations. In addition, a β,β‐dimethyl VE underwent only cyclotrimerizations because of its larger steric repulsion. The product alternating copolymers, especially those with cyclic units, exhibited improved thermal properties compared to those with simple VEs units. Under appropriate conditions, the alternating copolymers selectively degraded into the corresponding cinnamaldehyde derivatives by acid hydrolysis. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 1334–1343     

Selectively degradable alternating copolymers of isobutyl vinyl ether and plant‐derived aldehydes with acyclic side chains: Effects of side group structures on copolymerization behaviors

Side group structures of aldehydes were demonstrated to have decisive effects on cationic copolymerizations with alkyl vinyl ether (VE). Alternating copolymerizations of isobutyl VE (IBVE) and plant‐derived aldehydes with acyclic side chains such as trans‐2,cis‐6‐nonadienal, trans‐2‐nonenal, and citral proceeded under appropriate reaction conditions with the EtSO₃H/GaCl₃ initiating system. In addition, some aldehydes copolymerized in a well‐controlled fashion to yield alternating copolymers with controlled molecular weights and narrow molecular weight distributions. Quantitative and selective acid hydrolysis of the resulting alternating copolymers, based on the acetal structures in the main chains, was also achieved to give other conjugated aldehydes as nearly sole degradation products. Copolymerization results of IBVE and various plant‐derived aldehydes with acyclic or cyclic side groups suggested that electron‐donating ability and bulkiness of the side groups were most likely responsible for the alternating and/or controlled copolymerization behaviors. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013 , 51, 4684–4693     

Novel photoinitiated cationic copolymerizations of 4-methylene-2-phenyl-1,3-dioxolane

Photoinitiated polymerization of 4-methylene-2-phenyl-1,3-dioxolane ( 1 ) was carried out using either tris (4-methylphenyl) sulfonium hexafluoroantimonate or 4-decyloxyphenyl phenyliodonium hexafluoroantimonate as initiators. ¹H-NMR analyses confirmed exclusive ring-opening while DSC and SEC were used to determine the glass transition temperatures (T_gs) and molecular weights, respectively. Photoinitiated cationic copolymerizations of 1 were investigated with several acyclic and cyclic monomers. Copolymerization of 1 with vinyl ethers and a spiroorthoester resulted in copolymers whose thermal properties were dependent on comonomer ratios. Copolymers of 1 and dihydrofuran or dihydropyran afforded soluble polymers with T_gs significantly higher than the homopolymer of 1 . © 1997 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 35 : 2207–2219, 1997     

Copolymerization of styrene with (Z)-1,3-pentadiene in the presence of a syndiotactic-specific catalyst

Copolymerization of styrene with (Z)-1,3-pentadiene affords copolymers mostly containing 1,2 pentadiene units. Both the styrene and the pentadiene units are in syndiotactic arrangement but the comonomer sequence distribution is far from bernoullian. Interestingly, the behavior of (Z)-1,3-pentadiene does not change much when polymerization temperature raises from −20 to +20°C, notwithstanding that (Z)-1,3-pentadiene affords a 1,2-syndiotactic homopolymer at −20°C but a prevailingly 1,4 cis homopolymer at +20°C. © 1997 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 35 : 2697–2702, 1997     

cis‐1,4‐specific carbocationic polymerization and copolymerization of 1,3‐dienes initiated by (S,S)‐bis(oxazolinylphenyl)amine chromium complexes

Two new chiral (S,S)‐bis(oxazolinylphenyl)amine chromium dichloride complexes have been synthesized and structurally characterized. In combination with 2 equiv. of borate and an excess of AlR₃, such Cr complexes serve as effective cationic initiators in the stereoregular carbocationic polymerization of 1,3‐dienes such as isoprene (IP) and myrcene (MY), affording cyclized cis‐1,4‐PIPs/PMys (cis‐1,4‐selectivity up to 96%) with cyclic sequence contents ranging from 26% to 87%. Moreover, these Cr initiator systems also exhibit an unprecedented control over sequence distribution of comonomers in the carbocationic copolymerization of IP and MY, preparing novel copolymers with different microstructures from mainly cyclized cis‐1,4‐specific statistical copolymers to cyclic olefin copolymers. The nature of Cr complex, borate, AlR₃, temperature, molar ratio of comonomers has considerable effect on the (co)polymer's yield, stereoselectivity, cyclization, and comonomer sequence distribution. A plausible mechanism is suggested, which gives a new strategy for biomimetic synthesis of natural rubber. © 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 55, 1250–1259     

Cationic ring‐opening polymerization behavior of a five‐membered cyclic thiocarbonate having a spiro‐linked adamantane moiety

This work deals with the synthesis and cationic ring‐opening polymerization behavior of a novel five‐membered cyclic thiocarbonate bearing a spiro‐linked adamantane moiety, tricyclo[3.3.1.1^3,7]decane‐2‐spiro‐4′‐(1′,3′‐dioxolane‐2′‐thione) ( TC2 ). The cationic ring‐opening polymerization of TC2 did not proceed with trifluoromethanesulfonic acid, methyl trifluoromethanesulfonate, triethyloxonium tetrafluoroborate (Et₃OBF₄), boron trifluoride etherate (BF₃OEt₂), titanium tetrachloride, or methyl iodide as the initiator, presumably because of the steric hindrance of the adamantane moiety. However, the cationic ring‐opening copolymerization of TC2 with five‐ or six‐membered cyclic thiocarbonates, that is, 1,3‐dioxolane‐2‐thione, 1,3‐dioxane‐2‐thione, 5‐methyl‐1,3‐dioxane‐2‐thione, or 5,5‐dimethyl‐1,3‐dioxane‐2‐thione, initiated by BF₃OEt₂ or Et₃OBF₄, proceeded to afford the corresponding copolymer via a selective ring‐opening direction. The increase in the feed ratio of TC2 in the copolymerization increased the unit ratio derived from TC2 in the copolymer; however, the molecular weight of the copolymer decreased. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 699–707, 2003     

Bisphosphonate units in the main polymer chain: The first synthesis

Radical copolymerization of tetraethyl vinylidene phosphonate ( B ) with vinyl monomers has been described for the first time. In copolymerization with vinyl acetate ( V ) strictly alternating copolymer was formed even when [ V ]₀/[ B ]₀ was equal to 80. In copolymerization with acrylic acid ( A ) copolymers of the general structure ‐[( B )₁ A _x)]_n‐ were formed. The number of A units (x) was shown to depend on the [ A ]₀/[ B ]₀ ratio in the monomers feed. The reactivity ratio r_A was determined as equal to 2.1 and on this basis, the distribution of x as a function of [ A ]₀/[ B ]₀ was found. Bisphosphonic units were deblocked and the corresponding polyacids were analyzed by NMR spectra. M_n > 0.5 × 10⁶ were measured by SEC for copolymers of B with A . © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Ethylene copolymerization with cyclic dienes using rac‐Et[Ind]2ZrCl2–Methylaluminoxane

The effect of the copolymerization temperature and amount of comonomer in the copolymerization of ethylene with 1,3‐cyclopentadiene, dicyclopentadiene, and 4‐vinyl‐1‐cyclohexene and the rac‐Et[Ind]₂ZrCl₂–methylaluminoxane metallocene system was studied. The amount of comonomer present in the reaction media influenced the catalytic activity. Dicyclopentadiene was the most reactive comonomer among the cyclic dienes studied. In general, copolymers synthesized at 60 °C showed higher catalytic activities. Ethylene–dicyclopentadiene copolymers with high comonomer contents (>9%) did not show melting temperatures. 1,3‐Cyclopentadiene dimerized into dicyclopentadiene during the copolymerization, giving a terpolymer of ethylene, cyclopentadiene, and dicyclopentadiene. A complete characterization of the products was carried out with ¹H NMR, ¹³C NMR, heteronuclear chemical shift correlation, differential scanning calorimetry, and gel permeation chromatography. © 2002 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 471–485, 2002; DOI 10.1002/pola.10133     

Living/controlled cationic cyclopolymerization of divinyl ether with a cyclic acetal moiety: Synthesis of poly(vinyl ether)s with high glass transition temperature based on incorporation of cyclized main chain and cyclic side chains

Cationic cyclopolymerization of 2‐methyl‐5,5‐bis(vinyloxymethyl)‐1,3‐dioxane ( 1 ), a divinyl ether with a cyclic acetal group, was investigated with the HCl/ZnCl₂ initiating system in toluene and methylene chloride at ?30 °C. The reaction proceeded quantitatively to give gel‐free, soluble polymers in organic solvents. The number‐average molecular weight (M_n) of the polymers increased in direct proportion to monomer conversion, and further increased on addition of a fresh monomer feed to the almost completely polymerized reaction mixture, indicating that the polymerization proceeded in living/controlled manner. The contents of the unreacted vinyl groups in the produced soluble polymers were less than ～3 mol %, and therefore, the degree of cyclization was determined to be ～97%. In contrast, the pendant cyclic acetal groups remained intact in the polymers under the present cationic polymerization conditions. These facts show that cyclopolymerization of 1 almost exclusively occurred and the poly(vinyl ether)s with the cyclized repeating units and cyclic pendant acetal rings were obtained. Glass transition temperature (T_g) and thermal decomposition temperature (T_d) of poly( 1 ) (M_n = 7870, M_w/M_n = 1.57) were found to be 166 and 338 °C, respectively, indicating that poly( 1 ) had high T_g and high thermal stability. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 952–958, 2010     

Copolymerization of styrene and conjugated dienes with half‐sandwich titanium(IV) catalysts: The effect of the ligand structure on the monomer reactivity,monomer sequence distribution,and insertion mode of dienes

The copolymerization of styrene and 1,3‐butadiene (Bd) or isoprene (Ip) was carried out with half‐sandwich titanium(IV) Cp′TiCl₃ catalysts (where Cp′ is cyclopentadienyl 1 , indenyl 2 , or pentamethylcyclopentadienyl 3 ) with methylaluminoxane as a cocatalyst. For the copolymerization with Bd, catalyst 3 gave the copolymers containing the highest amount of Bd among the catalysts used. The resulting copolymers were composed of a styrene–Bd multiblock sequence. High melting points were observed in the copolymers prepared with catalyst 1 . The structures of hydrogenated poly(styrene‐co‐Bd) were studied by ¹³C NMR spectroscopy, and the long styrene sequence length was detected in the copolymers prepared with catalyst 1 . For styrene/Ip copolymerization, random copolymers were obtained. Among the used catalysts, catalyst 1 gave the copolymers containing the highest amount of Ip. The copolymers prepared with catalyst 1 showed a steep melting point depression with increasing Ip content because of the high ratio of 1,4‐inserted Ip units and/or the low molecular weights of the copolymers. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 939–946, 2003     

Synthesis and Degradation of Vinyl Polymers with Evenly Distributed Thioacetal Bonds in Main Chains: Cationic DT Copolymerization of Vinyl Ethers and Cyclic Thioacetals

We report a novel method to synthesize degradable poly(vinyl ether)s with cleavable thioacetal bonds periodically arranged in the main chains using controlled cationic copolymerization of vinyl ethers with a 7-membered cyclic thioacetal ( 7-CTA ) via degenerative chain transfer (DT) to the internal thioacetal bonds. The thioacetal bonds, which are introduced into the main chain by cationic ring-opening copolymerization of 7-CTA with vinyl ethers, serve as in-chain dormant species to allow homogeneous propagation of vinyl ethers for all internal segments to afford copolymers with controlled overall and segmental molecular weights. The obtained polymers can be degraded into low- and controlled-molecular-weight polymers with narrow molecular weight distributions via hydrolysis. Various vinyl ethers with hydrophobic, hydrophilic, and functional pendants are available. Finally, one-pot synthesis of multiblock copolymers and their degradation into diblock copolymers are also achieved.     

Copolymerization of 3,4-dimethyltetrahydrofuran with cyclic ethers

The copolymerization of 3,4-dimethyltetrahydrofuran with selected cyclic ethers was studied. Although 3,4-dimethyltetrahydrofuran did not homopolymerize, it readily copolymerized with propylene oxide and epichlorohydrin in an alternating fashion using the cationic initiator PF₅. The reactivity ratios r₁ and r₂ for the copolymerization of 3, 4-dimethyltetrahydrofuran and epichlorohydrin were r₁ = 0.22 ± 0.05 and r₂ = 0.11 ± 0.01, respectively.     

Unzipping and scrambling reaction-induced sequence control of copolymer chains via temperature changes during cationic ring-opening copolymerization of cyclic acetals and cyclic esters

A temperature change-dependent sequence transformation of copolymer chains was demonstrated by a method based on tandem depolymerization and transacetalization reactions during the cationic ring-opening copolymerization of cyclic acetals and cyclic esters. In this study, the position of polymerization-depolymerization equilibrium was controlled by the reaction temperature rather than by the decrease in monomer concentration under vacuum conditions, as in our previous study. First, the conditions for efficient copolymerization were optimized, with a particular focus on the structures of cyclic acetals and cyclic esters. Subsequently, sequence transformation induced by temperature change was examined during the copolymerization of 2-methyl-1,3-dioxepane (generated in situ from 4-hydroxybutyl vinyl ether) and δ-valerolactone using EtSO₃H. The homosequence length of cyclic acetals decreased during depolymerization (unzipping) at the oxonium chain ends upon increasing the temperature from 30 to 90 °C, while transacetalization (scrambling) of the main chain transferred midchain cyclic acetal homosequences to the oxonium chain ends. As a result of the cycle of unzipping and scrambling reactions, an alternating-like copolymer was obtained. Interestingly, the possibility of reversible sequence transformation upon heating and cooling was also demonstrated.     

Copolymerization of styrene and butadiene with Ni(acac)2-methylaluminoxane catalyst

Copolymerization of styrene (St) and butadiene (Bd) with nickel(II) acetylacetonate [Ni(acac)₂]-methylaluminoxane (MAO) catalyst was investigated. Among the metal acetylacetonates [Mt(acac)_x] examined, Ni(acac)₂ showed a high activity for the copolymerization of St and Bd giving copolymers having high cis-1,4-microstructure in Bd units in the copolymer. The effect of alkylaluminum as a cocatalyst on the copolymerization of St and Bd with the Ni(acac)₂-MAO catalyst was observed, and MAO was found to be the most effective cocatalyst for the copolymerization. The monomer reactivity ratios for the copolymerization of St and Bd with the Ni(acac)₂-MAO catalyst were determined to be r_St = 0.07 and r_Bd = 3.6. Based on the obtained results, it was presumed that the random copolymers with high cis-1,4-microstructure in Bd units could be synthesized with the Ni(acac)₂-MAO catalyst without formation of each homopolymer. The polymerization mechanism with the Ni(acac)₂-MAO catalyst was also discussed. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 3838–3844, 1999     

Synthesis of degradable poly(methyl methacrylate) star polymers via RAFT copolymerization with cyclic ketene acetals

Copolymerization of the cyclic ketene acetal 5,6‐benzo‐2‐methylene‐1,3‐dioxepane (BMDO) with methyl methacrylate (MMA) is studied with respect to its copolymerization parameters and the suitability to control BMDO/MMA copolymerizations via the reversible addition‐fragmentation chain transfer (RAFT) technique to obtain linear and 4‐arm star polymers. BMDO shows disparate copolymerization behavior with MMA and r₁ = 0.33 ± 0.06 and r₂ = 6.0 ± 0.8 have been determined for polymerization at 110 °C in anisole from fitting copolymer composition vs. comonomer feed data to the Lewis–Mayo equation. Copolymerization of the two monomers is successful in RAFT polymerization employing a trithiocarbonate control agent. As desired, polymers contain only little amount of polyester units stemming from BMDO units and preliminary degradation experiment show that the polymer degrades slowly, but steadily in aqueous 1 M NaOH dispersion. Within ten days, the polymers are broken down to low molecular weight segments from an initial molecular weight of M_n = 6000 g mol^?1. Star (co)polymerization with an erythritol‐based tetra‐functional RAFT agent following the Z‐group approach proceeds efficiently and polymers with a number‐average molecular weight of 10,000 g mol^?1 are readily obtained that degrade in similar manner as the linear copolymer counterparts. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 1633–1641     

Synthesis and characterization of original alternated fluorinated copolymers bearing glycidyl carbonate side groups

A vinyl ether bearing a carbonate side group (2‐oxo‐1,3‐dioxolan‐4‐yl‐methyl vinyl ether, GCVE) was synthesized and copolymerized with various commercially available fluoroolefins [chlorotrifluoroethylene (CTFE), hexafluoropropylene (HFP), and perfluoromethyl vinyl ether (PMVE)] by radical copolymerization initiated by tert‐butyl peroxypivalate. Although HFP, PMVE, and vinyl ether do not homopolymerize under radical conditions, they copolymerized easily yielding alternating poly(GCVE‐alt‐F‐alkene) copolymers. These alternating structures were confirmed by elemental analysis as well as ¹H, ¹⁹F, and ¹³C NMR spectroscopy. All copolymers were obtained in good yield (73–85%), with molecular weights ranging from 3900 to 4600 g mol^?1 and polydispersities below 2.0. Their thermogravimetric analyses under air showed decomposition temperatures at 10% weight loss (T_d,10%) in the 284–330°C range. The HFP‐based copolymer exhibited a better thermal stability than those based on CTFE and PMVE. The glass transition temperatures were in the 15–65°C range. These original copolymers may find potential interest as polymer electrolytes in lithium ions batteries. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Synthesis and enzymatic degradation of 2‐methylene‐1,3‐dioxepane and methyl acrylate copolymers

Copolymers of 2‐methylene‐1,3‐dioxepane (MDO) and methyl acrylate (MA) containing ester units both in the backbone and as pendant groups were synthesized by free‐radical copolymerization. The influence of reaction conditions such as the polymerization time, temperature, initiator concentration, and comonomer feed ratio on the yield, molecular weight, and copolymer composition was investigated. The structure of the copolymers was confirmed by ¹H NMR, ¹³C NMR, and IR spectroscopy. Differential scanning calorimetry indicated that the copolymers had a random structure. An NMR study showed that hydrogen transfer occurred during the copolymerization. The reactivity ratios of the comonomers were r_MDO = 0.0235 and r_MA = 26.535. The enzymatic degradation of the copolymers obtained was carried out in the presence of proteinase K or a crude enzyme extracted from earthworms. The experimental results showed that the higher ester molar percentage in the backbone caused a faster degradation rate. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2898–2904, 2003     

Cationic ring-opening polymerizations of cyclic ketene acetals initiated by acids at high temperatures

Three unsubstituted cyclic ketene acetals (CKAs), 2-methylene-1,3-dioxolane, 1a , 2-methylene-1,3-dioxane, 2a , and 2-methylene-1,3-dioxepane, 3a , undergo exclusive 1,2-addition polymerization at low temperatures, and only poly(CKAs) are obtained. At higher temperatures, ring-opening polymerization (ROP) can be dominant, and polymers with a mixture of ester units and cyclic ketal units are obtained. When the temperature is raised closer to the ceiling temperature (T_c) of the 1,2-addition propagation reaction, 1,2-addition polymerization becomes reversible and ring-opened units are introduced to the polymer. The ceiling temperature of 1,2-addition polymerization varies with the ring size of the CKAs (lowest for 3a , highest for 2a ). At temperatures below 138°C, 2-methylene-1,3-dioxane, 2a , underwent 1,2-addition polymerization. Insoluble poly(2-methylene-1,3-dioxane) 100% 1,2-addition was obtained. At above 150°C, a soluble polymer was obtained containing a mixture of ring-opened ester units and 1,2-addition cyclic ketal units. 2-Methylene-1,3-dioxolane, 1a , polymerized only by the 1,2-addition route at temperatures below 30°C. At 67–80°C, an insoluble polymer was obtained, which contained mostly 1,2-addition units but small amounts of ester units were detected. At 133°C, a soluble polymer was obtained containing a substantial fraction of ring-opened ester units together with 1,2-addition cyclic ketal units. 2-Methylene-1,3-dioxepane, 3a , underwent partial ROP even at 20°C to give a soluble polymer containing ring-opened ester units and 1,2-addition cyclic ketal units. At −20°C, 3a gave an insoluble polymer with 1,2-addition units exclusively. Several catalysts were able to initiate the ROP of 1a, 2a , and 3a , including RuCl₂(PPh₃)₃, BF₃, TiCl₄, H₂SO₄, H₂SO₄ supported on carbon, (CH₃)₂CHCOOH, and CH₃COOH. The initiation by Lewis acids or protonic acids probably occurs through an initial protonation. The propagation step of the ROP proceeds via an S_N2 mechanism. The chain transfer and termination rates become faster at high temperatures, and this may be the primary reason for the low molecular weights (M_n ≤ 10³) observed for all ring-opening polymers. The effects of temperature, monomer and initiator concentration, water content, and polymerization time on the polymer structure have been investigated during the Ru(PPh₃)₃Cl₂-initiated polymerization of 2a . High monomer concentrations ([M]/[ln]) increase the molecular weight and decreased the amount of ring-opening. Higher initiator concentrations (Ru(PPh₃)₃Cl₂) and longer reaction times increase molecular weight in high temperature reactions. Successful copolymerization of 2a with hexamethylcyclotrisiloxane was initiated by BF₃OEt₂. The copolymer obtained displayed a broad molecular weight distribution; M̄_n = 6,490, M̄_w = 15,100, M̄_z = 44,900. This polymer had about 47 mol % of ( Me₂SiO ) units, 35 mol % of ring-opened units, and 18 mol % 1,2-addition units of 2a . © 1997 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 35: 3655–3671, 1997