Structural relaxation of amorphous Ge38S62 studied by length dilatometry and calorimetry

The structural relaxation of Ge₃₈S₆₂ glass has been studied by length dilatometry and calorimetry. The Tool-Narayanaswamy-Moynihan model was applied on obtained data of structural relaxation and parameters of this model were determined: Δh*= 483±2 kJ mol^-1, ln(A/s)= -81±1, β= 0.7±0.1 and x=0.6±0.1. Both dilatometric and calorimetric relaxation data were compared on the basis of the fictive relaxation rate. It was found that the relaxation rates are very similar and well correspond to the prediction of phenomenological model. This revised version was published online in July 2006 with corrections to the Cover Date.     

Study of the dissolution process of polystyrene in concentrated cyclohexane solution by MNR relaxation

 ¹³C-NMR relaxation times of polystyrene (PS) chains in its theta solvent, cyclohexane, have been measured at different temperatures. It was found that relaxation of carbon nuclei of the side-chain-phenyl groups and those of main chains have remarkably different temperature-dependent relaxation behaviors in the solvent. A two-step model for the dissolution process is proposed. According to the model, swelling of the polymer below θ temperature corresponds mainly to the gradual dispersion of the side-chain phenyl groups; while the complete dissolution above θ temperature corresponds mainly to the gradual dispersion of the main chains at a molecular level. These dispersions reflect the fact that cohesional interaction among side-chain-phenyl rings or main chains are weakened by solvent molecules, which shows the existence of the cohesional entanglements among polymer chains. The results of T ₁(C) are confirmed by the biexponential dependence of ¹H-NMR spin–spin relaxation on temperature. Received: 2 July 1997 Accepted: 21 October 1997     

Dielectric relaxation studies of aromatic polyamides

Dielectric relaxation spectroscopy (DRS) is presented for a family of four aromatic polyamides trying to relate the structure of the lateral groups to the molecular mobility. A prominent sub-T_g absorption is always seen followed in some cases by remanent dielectric activity at room temperature and a subsequent increase of the loss permittivity. The low temperature relaxation is analyzed in terms of a Fuoss–Kirkwood equation to obtain the broadness and the strength of these relaxations as well as the activation energy (ranging from 10 to 11 Kcal/mol). The low frequency conductive peak shows in each case a half-width higher (1.30) than those corresponding to a single relaxation time peak (1.144). These values of the half-width are an indication of the complex character of these phenomena. A final discussion of the rotational barriers of the lateral chains rules out that such motions are the only molecular origin for the gamma relaxation. Instead, some kind of motion involving the main chain and where the interchain interactions play a significant role should be considered as responsible for that relaxation. © 1997 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 35 : 919–927, 1997     

Structural relaxation behavior of strain hardened shape memory polymer fibers for self‐healing applications

In this study, shape‐memory polyurethane (SMPU) fibers were strain hardened by cold‐drawing programming (CDP) process. The programmed fibers are experimentally studied on the physical and thermomechanical properties. Structural relaxation, which determines shape memory capability of the SMP fibers, is quantified by conformational entropy change. Based on the entanglement tube theory and reptation theory, the entropic force is derived as a “bridge” to link the stress relaxation and structural relaxation, and thus structural relaxation can be evaluated by stress relaxation. It was found that the CDP SMPU fibers would still have good crackclosing capability after 13 years of hibernation in polymer matrix composite. © 2013 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2013 , 51, 966–977     

Effect on structural relaxation of the poly(methyl‐methacrylate) copolymers chain flexibility

The structural relaxation of poly(methyl‐methacrylate) (PMMA)‐based copolymers with different chain flexibility has been studied by DSC with the classical procedure of the isothermal and dynamical approach. Modified PMMA with different chain flexibility have been prepared by free radical polymerization in solution using a mixture of monomers containing 10 mol % of alkyl methacrylate (i.e., ethyl, buthyl, and hexyl methacrylate). The molecular characteristics of all the prepared copolymers have been performed by a multiangle laser light scattering (MALS) photometer on‐line to a size exclusion chromatography (SEC) system (SEC‐MALS) after and before the thermal treatments, NMR (¹H and ¹³C) and MALDI‐TOF mass spectrometry. A comparison of the apparent relaxation rate (R_H) was appraised from the enthalpy loss by annealing the different samples at the same level of undercooling (T_a = T_g ? 18 °C). It was found an increase of R_H increasing the chain flexibility in the copolymers. Dynamical tests, performed at different cooling rates, have been used to estimate the apparent activation energy of the relaxation process. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 596–607, 2009     

Frequency and molecular-mass-dependent nonexponential proton NMR relaxation in polymer melts

A theoretical treatment of the nonexponential relaxation behavior of the different proton nuclear magnetic resonance (NMR) relaxation processes in polymer melts is presented. Formulas are derived for a three-component model given by two versions and a homogeneous distribution of correlation times. The theoretical results were tested with measurements of T₁, T_2e, and T₂ as functions of frequency and molecular mass in linear fractionated polyethylene samples. While the T₁ relaxation always yields exponential magnetization decays, the T_2e and T₂ measurements show biexponential relaxation behavior. From the calculations it was found that the correlation time of the local motion is independent of the molecular mass, whereas the correlation time of the slowest motional process increases with M^2.8_w for the three-component model and with M^2.2_w for the distribution of correlation times, respectively. © 1992 John Wiley & Sons, Inc.     

Mechanical relaxation spectroscopy of three triepoxide-based polymers

Three network structure polymers formed by the chemical reactions of a triepoxide with aniline, 3-chloroaniline,and 4-chloroaniline were prepared and their shear modulus relaxation spectra studied over the 10⁻³- to 1-Hz range and temperatures up to their rubber modulus region. The decrease in the unrelaxed modulus with increase in temperature is found to be a reflection of both an increase in volume, and a decrease in the relaxed modulus of the sub-T_g relaxations process. It is quantitatively shown that the increase in the rubber modulus with increase in temperature above T_g is predominantly due to an increase in the entropy and not to a decrease in the number of cross-links density on thermal expansion. The unrelaxed modulus remained unaffected by the change in the overall size of the phenyl groups of the amines and of the steric hindrance to their rotations caused by the proximity of the chlorine atom to the cross-linking N-atom in the network structure, but the rubber modulus was effected. The shear modulus spectra could be fitted to a stretched exponential decay function with a temperature-independent stretch parameter of 0.25 for two polymers and 0.22 for one. The time–temperature superposition of the spectra did not yield a master curve, and a vertical displacement of the data also failed to produce it. This was more clearly demonstrated by the spectra of the mechanical loss tangent. After considering the various contributions to the shear modulus, it was concluded that deviations from the time–temperature superposition of the spectra are intrinsic to these polymers and arise from the change in the viscoelastic functions for segmental dynamics on change in the temperature such that the overall distribution of relaxation times remains unaffected. The mechanical loss tangent of the three polymers is found to be higher than that of polycarbonate at ambient temperature, implying a higher loss of mechanical energy before these polymers may fracture. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 3071–3083, 1999     

Unusual relaxation process in polybutadiene: Resolving the controversy

We report the observation of an unusual relaxation process in depolarized light scattering spectra of polybutadiene (PBD) with two different vinyl contents. The process showed up in the gigahertz frequency range with relatively mild temperature dependence and was similar to a secondary relaxation process. The most surprising observation was that the process exists even at high temperatures and does not merge with the segmental relaxation up to a temperature of 400 K (T > 2T_g). Possible mechanisms of this particular relaxation in PBD are discussed. The process is compared to the so‐called E process, double‐bond hopping process, and dielectric β process. We emphasize that this process differs from the dielectric β process, is unique for 1,4‐PBD, and has not been observed in other polymers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 994–999, 2004     

Structural relaxation of stacked ultrathin polystyrene films

The T_g depression and kinetic behavior of stacked polystyrene ultrathin films is investigated by differential scanning calorimetry (DSC) and compared with the behavior of bulk polystyrene. The fictive temperature (T_f) was measured as a function of cooling rate and as a function of aging time for aging temperatures below the nominal glass transition temperature (T_g). The stacked ultrathin films show enthalpy overshoots in DSC heating scans which are reduced in height but occur over a broader temperature range relative to the bulk response for a given change in fictive temperature. The cooling rate dependence of the limiting fictive temperature, T_f′, is also found to be higher for the stacked ultrathin film samples; the result is that the magnitude of the T_g depression between the ultrathin film sample and the bulk is inversely related to the cooling rate. We also find that the rate of physical aging of the stacked ultrathin films is comparable with the bulk when aging is performed at the same distance from T_g; however, when conducted at the same aging temperature, the ultrathin film samples show accelerated physical aging, that is, a shorter time is required to reach equilibrium for the thin films due to their depressed T_g values. The smaller distance from T_g also results in a reduced logarithmic aging rate for the thin films compared with the bulk, although this is not indicative of longer relaxation times. The DSC heating curves obtained as a function of cooling rate and aging history are modeled using the Tool-Narayanaswamy-Moynihan model of structural recovery; the stacked ultrathin film samples show lower β values than the bulk, consistent with a broader distribution of relaxation times. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 2741–2753, 2008     

Correlation between dipolar TSDC and AC dielectric spectroscopy at the PVDF glass transition

The α_a-mode (associated to the dynamic glass transition) in PVDF-α has been studied by Thermally Stimulated Depolarization Currents (TSDC) and Dielectric Spectroscopy (DS) techniques. The distribution of relaxation parameters, reorientation energies, characteristic temperature, and preexponential factors of the Vogel–Tammann–Fulcher relaxation times have been precisely determined by using the Simulated Annealing Direct Signal Analysis applied to a partially discharged TSDC α_a peak. This distribution has been used to predict the variation of the dielectric loss, ε″(ω, T), in the temperature and frequency range where the DS measurements were made on the same material. The simulated ε′(T, ω) for various ω, are compared to the experimental values. The width of the peak is always too low, due to the restricted distribution used for the generation of the curves. A relaxation map including the TSDC results is used to determine the relaxation time variation. In the limited frequency range where the AC DS experiments are performed (10² ≤ f ≤ 10⁵ Hz) a master curve is drawn and the exponents of the frequency dependence are found at low and high frequency; also, a fitting to the Havriliak–Negami distribution is successfully performed. © 1997 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 35 : 2483–2493, 1997     

Physical aging studies of amorphous linear polyesters. Part II. Dependence of structural relaxation parameters on the chemical structure

The enthalpy relaxation of a series of linear amorphous polyesters (poly(propylene isophthalate) (PPIP), poly(propylene terephthalate) (PPTP), poly(ethylene terephthalate) (PETP), and poly(dipropylene terephthalate) (PDPT)) has been investigated by differential scanning calorimetry (DSC). These polyesters have been annealed at equal undercooling below their respective glass transition temperatures, T_g, (T_g − 27°C, T_g − 15°C, and T_g − 9°C) for periods of time from 15 min to 480 h. The key parameters of structural relaxation, namely the apparent activation energy (Δh*), the nonlinearity parameter (x) and the nonexponentiality parameter (β), have been determined for each polyester and related to an effective relaxation rate (1/τ_eff) and to the chemical structure. We observe that the variation of the structural relaxation parameters shows a trend that is common to other polymeric systems, whereby an increase of x and β corresponds a decrease in Δh*. The comparison of these parameters in PETP and in PPTP gives information about the effect of the introduction of a methyl group pendant from the main chain; the x parameter increases (i.e., a reduced contribution of the structure to the relaxation times), β increases (i.e., a narrow distribution of relaxation times), and Δh* decreases. Additionally, enthalpy relaxation experiments show that a decrease of Δh* correlates with an increase of 1/τ_eff, when they are measured at a fixed value of the excess enthalpy, δ_H. The introduction of an isopropyl ether group in PDPT with respect to PPTP decreases both x and β, but increases Δh*, which the rate of relaxation decreases. The ring substitution in PPTP and PPIP originates less significant changes in the structural parameters. © 1998 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 36 : 113–126, 1998     

Dynamic mechanical behavior of fluorinated aromatic poly(ethers)

The relaxation behavior of six fluorinated aromatic poly(ethers) was investigated using dynamic mechanical analysis. The glass transition temperature was found to increase as the size and rigidity of linking groups increased and varied between 168°C for a dimethyl linking group and 300°C for a bicyclic benzoate ether-linking group. For the α-relaxation the steepness of time/temperature plots and broadness of the loss curves could be qualitatively correlated with chemical structure in a manner predicted by the coupling model of relaxation. Well-separated sub-T_g transitions were also observed, as a shoulder on the low temperature side of the α-peak, and as a broad, low loss transition around −100°C. The higher temperature process was similar to the structural relaxation often found in quenched glassy polymers, while the position, intensity, and breadth of the subambient process was sensitive to chemical structure. © 1997 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 35: 1963–1971, 1997     

Molecular relaxation of isotactic polystyrene: Real‐time dielectric spectroscopy and X‐ray scattering studies*

The molecular relaxation processes and structure of isotactic polystyrene (iPS) films were investigated with real‐time dielectric spectroscopy and simultaneous wide‐ and small‐angle X‐ray scattering. The purpose of this work was to explore the restrictions imposed on molecular mobility in the vicinity of the α relaxation (glass transition) for crystallized iPS. Isothermal cold crystallization at temperatures of T_c = 140 or 170 °C resulted in a sigmoidal increase of crystallinity with crystallization time. The glass‐transition temperature (T_g), determined calorimetrically, exhibited almost no increase during the first stage of crystal growth before impingement of spherulites. After impingement, the calorimetric T_g increased, suggesting that confinement effects occur in the latter stages of crystallization. For well‐crystallized samples, the radius of the cooperativity region decreased substantially as compared with the purely amorphous sample but was always smaller than the layer thickness of the mobile amorphous fraction. Dielectric experiments directly probed changes in the amorphous dipole mobility. The real‐time dielectric data were fitted to a Havriliak–Negami model, and the time dependence of the parameters describing the distribution of relaxation times and dielectric strength was obtained. The central dipolar relaxation time showed little variation before spherulite impingement but increased sharply during the second stage of crystal growth as confinement occurred. Vogel–Fulcher–Tammann analysis demonstrated that the dielectric reference temperature, corresponding to the onset of calorimetric T_g, did not vary for well‐crystallized samples. This observation agreed with a model in which constraints affect primarily the modes having longer relaxation times and thus broaden the glass‐transition relaxation process on the higher temperature side. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 777–789, 2004     

Orientation and relaxation study of polystyrene: Polystyrene/poly(phenylene oxide) blends

Polarization modulation infrared linear dichroism has been used to study the molecular orientation and relaxation of polystyrene/poly(2,6‐dimethyl 1,4‐phenylene oxide) (PS/PPO) miscible blends, containing up to 20% PPO, during and after a rapid uniaxial deformation above T_g. In general, it is found that both the PS and PPO chain orientation functions increase with stretching rate and PPO content, and decrease with temperature. For all blends investigated, between T_g + 5 and T_g + 13 °C, the relaxation occurs at the same rate for PS and PPO and, therefore, the relaxation times calculated are similar indicating, under those conditions, a strong relaxation coupling between the two polymers at both short and long times. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 1405–1415, 2000     

Pressure‐temperature study of dielectric relaxation of a polyurethane elastomer

The effect of hydrostatic pressure up to 1,361 atms on the dielectric properties of a segmented polyurethane elastomer (Dow 2103‐80AE) is studied at temperatures from 0°C to 80°C. The experimental results show that the relaxation time for both the I–process, associated with the molecular motions in the hard segments, and the α–process, associated with the glass transition, increases with pressure, and this shift is more pronounced for the I–process. Besides the glass transition, it is found that the I–process can be described by the Vogel–Fulcher (V–F) and Williams–Landel–Ferry (WLF) relations. At atmospheric pressure, T_g and T₀ for the I–process are 235.9 K and 4.2 × 10³ K, respectively. Based on the V–F and WLF relations and experimental results, it is found that a parameter, C₁, in the WLF relation is independent of the pressure. Thus, a method is introduced to determine the values of both the characteristic transition temperature (T_g) and activation energy (T₀) for the processes at different pressures. As the pressure increases from atmospheric to 1,361 atms, the increase of T_g for the I–process is about 30°C. The results also show that, for both the I– and the α–processes, T₀ decreases with increasing pressure. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 983–990, 1999     

Microcellular processing and relaxation of poly(ether ether ketone)

The semicrystalline microcellular closed‐cell foams are prepared by a two‐stage batch foaming process from poly(ether ether ketone) and characterized by scanning electronic microscopy. It can be observed that there are two kinds of cells with obviously different cellular sizes in the same transect and the distribution of larger cells (about 7 μm) looks like sandwich. The effects of foaming temperatures and transfer times on the cellular sizes and cell densities of porous materials were discussed. Particular emphasis was given to the effects of crystalline on the microcellular morphology. The relaxation mechanism of microcellular materials was systemically investigated by dynamic mechanics analysis. A plain on the storage modulus curve before T_g was observed due to the densification of cells. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 2890–2898, 2007     

Compression stress relaxation in carbon black reinforced HNBR at low temperatures

Findings of a study of stress relaxation behaviour of hydrogenated nitrile butadiene rubber (HNBR) at nominal compressive strains up to 0.4 and temperatures above and below the glass transition temperature T_g are reported. Two formulations of a model HNBR with 36% acrylonitrile content and carbon black (CB) loading of 0 and 50 phr were investigated. The relaxation function of HNBR is found to be independent of strain at temperatures right above the T_g or at times longer than 10⁻³ s for the deformations employed. CB imparts higher long-term stiffness and also larger relaxation strength at times longer than 10⁻⁴ s to the HNBR, but it does not affect the relaxation behaviour of the rubber in the time span from 10⁻³ – 10⁴ s. In addition, the relationship between the strain energy function of HNBR and temperature is demonstrated to have a complex concave-downward shape which is affected by two competing contributions of entropy elasticity and the stress relaxation.     

Influence of the chemical structure on the kinetics of the structural relaxation process of acrylate and methacrylate polymer networks

The enthalpy relaxation of poly(hydroxyethyl methacrylate) (PHEMA), poly(ethyl methacrylate) (PEMA) and poly(ethyl acrylate) (PEA) networks, obtained by DSC, are compared. The temperature interval of the glass transition broadens in the sequence PEA-PEMA-PHEMA. The plots of the enthalpy loss during the annealing for 200 min at different temperatures below T_g show that the structural relaxation process also takes place in PHEMA in a broader temperature interval than in PEA or PEMA. The modelling of the structural relaxation process using a phenomenological model allows determining the temperature dependence of the relaxation times concluding that the fragility in PHEMA is significantly lower than in PEMA. Both features are ascribed to the connectivity of the polymer chains in PHEMA via hydrogen bonding. The role of the presence of the methyl group bonded to the main chain is analysed by comparing the results obtained in PEA and PEMA.     

Dielectric relaxation behavior of poly(methyl methacrylate) under high‐pressure carbon dioxide

An in situ dielectric measurement for atactic poly(methyl methacrylate) (at‐PMMA) was performed under high‐pressure CO₂ under various pressures and temperatures. The at‐PMMA has the acetate side group with a large dipole moment. In the glassy state, a local relaxation process (β‐process) can be observed using dielectric measurement. In the rubbery state, the micro‐Brownian motion of main chain (α‐process) occurs, and the β‐process changes into αβ‐process coordinated with the α‐process. The dielectric loss (ε″) spectrum of at‐PMMA in the glassy state is asymmetric because of the density fluctuation for the amorphous structure. The loss peak frequency shifted to higher frequencies, and the relaxation strength increased with increasing CO₂ pressure. In the glassy state, the shape of ε″ spectrum became more symmetric with increasing CO₂ pressure. These show that the molecular mobility enhanced by the plasticization effect of CO₂ allows the dipolar side groups in the high‐density region to contribute to the relaxation process. We also found that the apparent activation energy decreased under high‐pressure CO₂. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 2951–2962, 2005