Synthesis of polymers in aqueous solutions: Synthesis of polysulfide by reaction of bis(4‐mercaptophenyl) sulfide with bis(4‐chloro‐3‐nitrophenyl) sulfone using various bases in aqueous solutions

The polycondensation of bis(4‐mercaptophenyl) sulfide (BMPS) with bis(4‐chloro‐3‐nitrophenyl) sulfone (BCNPS) was examined using various organic or inorganic bases in mixed solvents of N‐methyl‐2‐pyrrolidone (NMP) with water or in plain water. The reaction of BMPS with BCNPS proceeded smoothly to give the corresponding polysulfide in mixed solvents of NMP with water at 60 °C using 1,8‐diazabicyclo[5.4.0]undecene‐7 as a base, although the rate of the reaction decreased gradually as the water in the solvent increased. Polysulfide can also be obtained by reaction in plain water using appropriate organic bases such as tripropylamine (TPA) or quinoline. The polysulfide with a number‐average molecular weight of 45,100 was synthesized in 62% yield when the reaction of BMPS with BCNPS was performed using TPA as a base at 60 °C for 48 h in plain water. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 3399–3404, 2000     

Synthesis of polymers with pendant hydroxyl groups by polyaddition of bis(oxetane)s with dithiols

Addition reaction of (3-methyl-3-oxetanyl)methyl acetate (MOMA) with bis(4-mercaptophenyl) sulfide (BMPS) was examined in certain organic solvents. When the reaction of MOMA with BMPS was performed without any catalyst in hexamethylphosphoric triamide (HMPA) and N-methyl-2-pyrrolidone (NMP) at 130°C for 24 h, conversions of the corresponding adduct were 96 and 36%, respectively, which was confirmed by ¹H-NMR spectra. On the other hand, when the reaction was carried out using tetraphenylphosphonium bromide (TPPB) as a catalyst under the same conditions, conversions of the adduct were 96 and 81% in HMPA and NMP, respectively. This result shows that although the addition reaction of oxetane compound with aromatic dithiol proceeds without any catalyst in HMPA, the reaction was strongly enhanced by adding TPPB in NMP. On the basis of the above results, polyadditions of bis((3-methyl-3-oxetanyl)methyl) terephthalate (BMOT) and bis((3-ethyl-3-oxetanyl)methyl) terephthalate with BMPS were performed using TPPB as the catalyst in NMP at 130°C for 24 h. As a result, the corresponding high molecular weight polymers 1 (M_n = 22,400) and 2 (M_n = 12,800) with pendant primary hydroxyl groups were obtained in 83 and 89% yields without any gel products, respectively. Furthermore, a low molecular weight oligomer was obtained from the polyaddition of BMOT with aliphatic dithiol, bis(mercaptomethyl)benzene, under the same reaction conditions. The catalytic activity on the polyaddition of BMOT with BMPS was also examined, and it was found that thermally stable TPPB and crown ether complexes at the reaction temperature (130°C) have higher catalytic activity than tetrabutylammonium bromide and tetrabutylphosphonium bromide to produce polymer 1 with high molecular weight. © 1998 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 36: 2873–2880, 1998     

A novel synthesis of reactive polymers with pendant halomethyl groups by the polyaddition reaction of bis(epoxide)s with bis(chloroacetoxy)esters or bis(bromoacetoxy)esters

New reactive polymers with pendant halomethyl groups were successfully synthesized by polyaddition reactions of bis(epoxide)s with bis(chloroacetoxy)ester such as 1,4-bis [(chloroacetoxy)methyl]benzene (BCAMB) or 1,4-bis[(bromoacetoxy)methyl]benzene (BBAMB) using quaternary onium salts or crown ether complexes as catalysts. The polyaddition reaction of diglycidyl ether of bisphenol A (DGEBA) with BCAMB proceeded very smoothly with high yields (83–96%) by the addition of quaternary onium salts such as tetrabutylphosphonium bromide (TBPB) or crown ether complexes such as 18-crown-6/KBr as catalysts to produce high molecular weight polymers, although the reaction occurred without any catalyst to give low molecular weight polymer in low yield at 90°C for 48 h. It was also found that the reaction proceeded smoothly in aprotic polar solvents such as N-methyl-2-pyrrolidone (NMP) and N,N-dimethylacetamide (DMAc) to produce high molecular weight polymers. Polyaddition reactions of DGEBA or digylcidyl ether of ethylene glycol (DGEEG) with BBAMB, other bis(chloroacetoxy)esters or bis(bromoacetoxy)esters using TBPB in DMAc also proceeded smoothly to give the corresponding polymers. The resulting poly(ether-ester)s contain reactive halomethyl groups as side chains, which were introduced during main chain formation. © 1997 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 35: 3791–3799, 1997     

Copolymerization of bis(2-oxazoline)s,anhydrides, and diols or diamines. Reaction mechanisms and polymer properties

The preparation of linear poly(ester-amide)s from monoanhydrides, bis(2-oxazoline)s (namely 2,2′-(1,4-phenylene)bis(2-oxazoline)) and a third comonomer is discussed. The polymerization reactions were carried out in bulk between 150 and 200°C. When the third monomer is a diol, poly(ester-ester-amide)s are obtained. Diols of different structure were used: α,ω-diols having up to 12 carbon atoms, ethylene glycol oligomers (two or three repeating units), cyclic diols, etc.; glutaric, 3,3-dimethylglutaric and maleic anhydrides were used as monoanhydrides. The polymers were studied from the point of view of thermal properties, finding a substantial agreement between the structure of the monomers and the glass transition temperature of the polymers. By using primary diamines as a third comonomer, the reaction does not lead to the formation of a polymeric product. The failure of the polymerization was attributed to a competitive reaction that prevents the polymerization. After the amine group has reacted with the anhydride, cyclization of the so-formed carboxyalkylamide occurs, giving an imide derivative, unable to react further. Therefore, only a mixture of low molecular weight compounds is obtained in this case. When the diamine is secondary, the imidization reaction is not possible, and linear poly(amide-ester-amide)s are obtained. © 1997 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 35: 3241–3248, 1997     

Poly(arylether amides) and poly(aryletherketone amides) via aromatic nucleophilic substitution reactions of self‐polymerizable AB and AB2 monomers

Two new extended self‐polymerizable AB monomers, N‐(4‐fluorobenzoyl)‐4‐amino‐4′‐hydroxydiphenylether and N‐(4‐fluorobenzoyl)‐4‐amino‐4′‐hydroxybiphenyl, were prepared. The monomers were homopolymerized and copolymerized to high‐molecular‐weight, linear poly(arylether amides) in N‐methylpyrrolidone (NMP)/toluene in the presence of potassium carbonate at elevated temperature. The polymers retained NMP up to 200 °C. Samples containing small amounts of the solvent (5–10 wt %) were soluble in polar aprotic solvents. However, after complete removal of the NMP, the polymers were only soluble in strong acids such as sulfuric acid and methanesulfonic acid (MSA). The polymers, which had intrinsic viscosities of 0.57–1.49 dL/g (30.1 ± 0.1 °C in MSA), were semicrystalline with melting temperatures above 400 °C. Two new self‐polymerizable AB₂ amide monomers, N,N′‐bis(4‐fluorobenzoyl)‐3,4‐diamino‐4′‐hydroxydiphenylether and N,N′‐bis(4‐fluorobenzoyl)‐3,5‐diamino‐4′‐hydroxybenzophenone, were also prepared and polymerized to give a hyperbranched poly(arylether amide) and a hyperbranched poly(aryletherketone) amide. The arylfluoride‐terminated, amorphous polymers had intrinsic viscosities of 0.34 and 0.24 dL/g (30.0 ± 0.1 °C in m‐cresol), glass‐transition temperatures of 210–269 °C, and were soluble in a wide variety of organic solvents. Matrix‐assisted laser desorption/ionization time‐of‐flight analysis indicated that the components of the low‐molecular‐weight fractions contained cyclic structures. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2374–2389, 2003     

Preparation and properties of poly(alkyl vinyl ether-2-ethyl-2-oxazoline) diblock copolymers

A method for the synthesis of well-defined poly(alkyl vinyl ether–2-ethyl-2-oxazoline) diblock copolymers with hydrolytically stable block linkages has been developed. Monofunctional poly(alkyl vinyl ether) oligomers with nearly Poisson molecular weight distributions were prepared via a living cationic polymerization method using chloroethyl vinyl ether together with HI/ZnI₂ as the initiating system and lithium borohydride as the termination reagent. Using the resultant chloroethyl ether functional oligomers in combination with sodium iodide as macroinitiators, 2-ethyl-2-oxazoline was polymerized in chlorobenzene/NMP to afford diblock copolymers. A series of poly(methyl vinyl ether–2-ethyl-2-oxazoline) diblock materials were found to have polydispersities of ≈ 1.3–1.4 and are microphase separated as indicated by two T_g's in their DSC thermograms. These copolymers are presently being used as model materials to study fundamental parameters important for steric stabilization of dispersions in polar media. © 1993 John Wiley & Sons, Inc.     

New poly(amide–imide)s syntheses. XXIII. Synthesis and properties of poly(amide–imide)s derived from 4,4′‐[1,4‐phenylenebis(isopropylidene‐1,4‐phenyleneoxy)]dianiline and various bis(trimellitimide)s

A series of poly(amide–imide)s III_a–m containing flexible isopropylidene and ether groups in the backbone were synthesized by the direct polycondensation of 4,4′‐[1,4‐phenylenebis(isopropylidene‐1,4‐phenyleneoxy)]dianiline (PIDA) with various bis(trimellitimide)s II_a–m in N‐methyl‐2‐pyrrolidone (NMP) using triphenyl phosphite and pyridine as condensing agents. The resulting poly(amide–imide)s had inherent viscosities in the range of 0.80–1.36 dL/g. Except for those from the bis(trimellitimide)s of p‐phenylenediamine and benzidine, all the polymers could be cast from DMAc into transparent and tough films. They exhibited excellent solubility in polar solvents. The 10% weight loss temperatures of the polymers in air and in nitrogen were all above 495°C, and their T_g values were in the range of 201–252°C. Some properties of poly(amide–imide)s III were compared with those of the corresponding poly(amide–imide)s V prepared from the bis(trimellitimide) of diamine PIDA and various aromatic diamines. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 69–76, 1999     

Synthesis and characterization of new poly(amide–imide)s from 1,4-bis(4-trimellitimidophenoxy)-2-tert-butylbenzene with various diamines

New poly(amide–imide)s were prepared from a diimide–dicarboxylic acid, 1,4-bis(4-trimellitimidophenoxy)-2-tert-butylbenzene ( BTTB ), with various diamines by the direct polycondensation in N-methyl-2-pyrrolidinone (NMP) using triphenyl phosphite and pyridine as condensing agents. The new diimide–dicarboxylic acid BTTB containing an ether linkage and tert-butyl substituent was synthesized by the condensation reaction of 1,4-bis(4-aminophenoxy)-2-tert-butylbenzene with trimellitic anhydride. All the polymers were obtained in quantitative yields with inherent viscosities of 0.62–1.06 dL g⁻¹. The polymers were amorphous, and most of them were readily soluble in aprotic polar solvents such as NMP, N,N-dimethylacetamide (DMAc), and N,N-dimethylformamide (DMF), as well as in less polar solvents such as dimethyl sulfoxide (DMSO), m-cresol, pyridine, and γ-butyrolactone, and also even in tetrahydrofuran. The glass transition temperatures of the polymers were determined by DSC method, and they were in the range of 238–279°C. These polymers were stable up to 408–449°C in air and 451–483°C in nitrogen and lose 10% weight in the range of 479–525°C in air and 480–528°C in nitrogen atmosphere. The polymer films had a tensile strength range of 71–115 MPa, an elongation at break range of 4–14%, and a tensile modulus range of 2.3–3.1 GPa. © 1998 John Wiley & Sons, Inc. J. Polym. Sci. A Polym. Chem. 36: 2301–2307, 1998     

Synthesis and properties of novel poly(arylene ether)s and poly(arylene thioether)s based on a pyridazine biphenol or a phthalazine biphenol

Novel sulfur‐containing biphenol monomers were prepared in high yields by the reaction of 4‐mercaptophenol with chloropyridazine or chlorophthalazine compounds. High‐molecular‐weight poly(arylene ether)s were synthesized by a nucleophilic substitution reaction between these sulfur‐containing monomers and activated difluoro aromatic compounds. The inherent viscosities of these polymers ranged from 0.34 to 0.93 dL/g. The poly(pyridazine)s exhibited glass‐transition temperatures greater than 165 °C. The poly(phthalazine)s showed higher glass‐transition temperatures than the poly(pyridazine)s. A polymer synthesized from a bisphthalazinebiphenol and bis(4‐fluorophenyl)sulfone had the highest glass‐transition temperature (240 °C). The thermal stabilities of the poly(pyridazine)s and poly(phthalazine)s showed similar patterns of decomposition, with no significant weight loss below 390 °C. The poly(phthalazine)s were soluble in chlorinated solvents such as chloroform, and the poly(pyridazine)s were soluble in dipolar aprotic solvents such as N,N′‐dimethylacetamide. The soluble poly(pyridazine)s and poly(phthalazine)s could be cast into flexible films from solution. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 262–268, 2007     

Synthesis and characterization of poly(aryl amide imide)s derived from diphenyltrimellitic anhydride

The synthesis and characterization of a series of novel poly(aryl amide imide)s based on diphenyltrimellitic anhydride are described. The poly(aryl amide imide)s, having inherent viscosities of 0.39–1.43 dL/g in N-methyl-2-pyrrolidinone at 30°C, were prepared by polymerization with aromatic diamines in N,N-dimethylacetamide and subsequent chemical imidization. All the polymers were amorphous, readily soluble in aprotic polar solvents such as DMAC, NMP, dimethylsulfoxide, N,N-dimethylformamide, and m-cresol, and could be cast to form flexible and tough films. The glass transition temperatures were in the range of 284–366°C, and the temperatures for 5% weight loss in nitrogen were above 468°C. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 4541–4545, 1999     

Synthesis and characterization of phthalazinone containing poly(arylene ether)s via a novel N–C coupling reaction

High‐molecular‐weight poly(phthalazinone)s with very high glass‐transition temperatures (T_g's) were synthesized via a novel N–C coupling reaction. New bisphthalazinone monomers ( 7a–e ) were synthesized from 2‐(4‐chlorobenzoyl) phthalic acid in two steps. Poly(phthalazinone)s, having inherent viscosities in the range of 0.34–0.91 dL/g, were prepared by the reaction of the bis(phthalazinone) monomers with an activated aryl halide in a dipolar aprotic solvent in the presence of potassium carbonate. The poly(phthalazinone)s exhibited T_g's greater than 230 °C. polymer 8b synthesized from diphenyl biphenol and bis(4‐flurophenyl) sulfone demonstrated the highest T_g of 297 °C. Thermal stabilities of the poly(phthalazinone)s were determined by thermogravimetric analysis. All the poly(phthalazinone)s showed a similar pattern of decomposition with no weight loss below 450 °C in nitrogen. The temperatures of 5% weight loss were observed to be about 500 °C. The poly(phthalazinone)s containing 4,4′‐isopropylidenediphenol and 4,4′‐(hexafluoroisopropylidene) diphenol and diphenyl ether linkage were soluble in chlorinated solvents such as chloroform. Other poly‐(phthalazinone)s were soluble in dipolar aprotic solvents such as N,N′‐dimethylacetamide. The soluble poly(phthalazinone)s can be cast as flexible films from solution. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2481–2490, 2003     

Synthesis and properties of organosoluble poly(amide‐imide)s with propeller‐shaped 1,1,1‐triphenylethane units in the main chain

A dicarboxylic acid {1,1‐bis[4‐(4‐trimellitimidophenoxy)phenyl]‐1‐phenylethane ( II )} bearing two performed imide rings was prepared from the condensation of 1,1‐bis[4‐(4‐aminophenoxy)phenyl]‐1‐phenylethane and trimellitic anhydride in a 1/2 molar ratio. A novel family of poly(amide‐imide)s with inherent viscosities of 0.83–1.51 dL/g was prepared by triphenyl phosphite‐activated polycondensation from the diimide‐diacid II with various aromatic diamines in a medium consisting of N‐methyl‐2‐pyrrolidinone (NMP), pyridine, and calcium chloride. Because the 1,1,1‐triphenylethane group of II was unsymmetrical, most of the resulting polymers showed an amorphous nature and were readily soluble in polar solvents such as NMP and N,N‐dimethylacetamide. All the soluble poly(amide‐imide)s afforded tough, transparent, and flexible films, which had tensile strengths ranging from 88 to 102 MPa, elongations at break from 6 to 11%, and initial moduli from 2.23 to 2.71 GPa. The synthesized poly(amide‐imide)s possessed glass‐transition temperatures from 250 to 287 °C. The poly(amide‐imide)s exhibited excellent thermal stabilities and had 10% weight losses from 501 to 534 °C under a nitrogen atmosphere. A comparative study of some corresponding poly(amide‐imide)s is also presented. © 2001 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 775–787, 2001     

Preparation and properties of new poly(amide‐imide)s based on 1,4‐bis(4‐trimellitimidophenoxy)naphthalene and aromatic diamines

A diimide dicarboxylic acid, 1,4‐bis(4‐trimellitimidophenoxy)naphthalene (1,4‐BTMPN), was prepared by condensation of 1,4‐bis(4‐aminophenoxy)naphthalene and trimellitic anhydride at a 1 : 2 molar ratio. A series of novel poly(amide‐imide)s (IIa–k) with inherent viscosities of 0.72 to 1.59 dL/g were prepared by triphenyl phosphite‐activated polycondensation from the diimide‐diacid 1,4‐BTMPN with various aromatic diamines (Ia–k) in a medium consisting of N‐methyl‐2‐pyrrolidinone (NMP), pyridine, and calcium chloride. The poly(amide‐imide)s showed good solubility in NMP, N,N‐dimethylacetamide, and N,N‐dimethylformamide. The thermal properties of the obtained poly(amide‐imide)s were examined with differential scanning calorimetry and thermogravimetry analysis. The synthesized poly(amide‐imide)s possessed glass‐transition temperatures in the range of 215 to 263°C. The poly(amide‐imide)s exhibited excellent thermal stabilities and had 10% weight losses at temperatures in the range of 538 to 569°C under a nitrogen atmosphere. A comparative study of some corresponding poly(amide‐imide)s also is presented. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1–8, 2000     

Synthesis of polyamide-imide by blocked-methylene diisocyanates

The synthesis of polyamide-imide (PAI) can be performed by the reaction of p-chlorophenol-(PCP) blocked 4,4′-diphenyl methane diisocyanates (BMDI) with trimellitic anhydride (TMA) using a two-stage heating. At 80°C the polyimide oligomers were first formed and the high molecular weight PAI can not be available until the temperature was increased to 120°C and stayed for 3 h, during which the amide groups were formed and the molecular weight was increased. The molecular weights of the synthesized PAIs on various conditions were analyzed by measuring the intrinsic viscosity, amide/imide ratio from IR spectra, and average chain length from GPC. The best reaction conditions for obtaining a high molecular weight PAI by the solution polymerization are: (a) using N-methyl pyrollidone (NMP) as solvent, (b) adding more BMDI/TMA ratio, and (c) adding tert-n-butyl amine as the catalyst for the dissociation of blocked MDI and controlling the catalyst concentration at 0.162M. © 1997 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 35 : 1711–1717, 1997     

Synthesis and characterization of fluorinated poly(amide imide)s derived from 1,4‐bis(2′‐trifluoromethyl‐4′‐trimellitimidophenoxy)benzene and aromatic diamines

A series of fluorinated poly(amide imide)s were prepared from 1,4‐bis(2′‐trifluoromethyl‐4′‐trimellitimidophenoxy)benzene and various aromatic diamines [3,3′,5,5′‐tetramethyl‐4,4′‐diaminediphenylmethane, α,α‐bis(4‐amino‐3,5‐dimethyl phenyl)‐3′‐trifluoromethylphenylmethane, 1,4‐bis(4′‐amino‐2′‐trifluoromethylphenoxy)benzene, 4‐(3′‐trifluoromethylphenyl)‐2,6‐bis(3′‐aminophenyl)pyridine, and 1,1‐bis(4′‐aminophenyl)‐1‐(3′‐trifluoromethylphenyl)‐2,2,2‐trifluoroethane]. The fluorinated poly(amide imide)s, prepared by a one‐step polycondensation procedure, had good solubility both in strong aprotic solvents, such as N‐methyl‐2‐pyrrolidinone, dimethylacetamide, dimethylformamide, dimethyl sulfoxide, and cyclopentanone, and in common organic solvents, such as tetrahydrofuran and m‐cresol. Strong and flexible polymer films with tensile strengths of 84–99 MPa and ultimate elongation values of 6–9% were prepared by the casting of polymer solutions onto glass substrates, followed by thermal baking. The poly(amide imide) films exhibited high thermal stability, with glass‐transition temperatures of 257–266 °C and initial thermal decomposition temperatures of greater than 540 °C. The polymer films also had good dielectric properties, with dielectric constants of 3.26–3.52 and dissipation factors of 3.0–7.7 × 10^?3, and acceptable electrical insulating properties. The balance of excellent solubility and thermal stability associated with good mechanical and electrical properties made the poly(amide imide)s potential candidates for practical applications in the microelectronics industry and other related fields. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 1831–1840, 2003     

Soluble poly(amide–imide)s prepared by one‐pot solution condensation

A new one‐pot procedure for imide–acid monomer synthesis and polymerization is reported for four new poly(amide–imide)s. Bisphenol A dianhydride (BPADA) was reacted with twice the molar amount of 3‐aminobenzoic acid (3ABA) or 3‐amino‐4‐methylbenzoic acid (3A4MBA) in 1‐methyl‐2‐pyrrolidinone (NMP) and toluene mixture, and the amic acid intermediates cyclized in solution to give two diimide‐containing dicarboxylic acid monomers. Without isolation, the diacid monomers were then polymerized with either 1,3‐diaminomesitylene (DAM) or 1,5‐diaminonaphthalene (1,5NAPda) using triphenyl phosphite‐activation to give a series of four soluble poly(amide–imide)s, PAI. Isolation and purification of the dicarboxylic acid monomers was not necessary for formation of high molecular weight polymers as indicated by intrinsic viscosities of 0.64–1.04 dL/g determined in N,N‐dimethylacetamide (DMAc). All of the PAI were soluble in polar aprotic solvents such as NMP, DMAc, and dimethyl sulfoxide (DMSO). Glass transition temperatures ranged from 243 to 279°C by DSC, and 5% weight loss temperatures were above 400°C in both air and nitrogen. Flexible films cast from DMAc were light yellow, transparent, and tough. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1183–1188, 1999     

Synthesis and properties of aromatic poly(ester amide)s with pendant phosphorus groups

Two series of phosphorus‐containing aromatic poly(ester amide)s with inherent viscosities of 0.46–3.20 dL/g were prepared by low‐temperature solution polycondensation from 1,4‐bis(3‐aminobenzoyloxy)‐2‐(6‐oxido‐6H‐dibenz〈c,e〉〈1,2〉oxaphosphorin‐6‐yl)naphthalene and 1,4‐bis(4‐aminobenzoyloxy)‐2‐(6‐oxido‐6H‐dibenz〈c,e〉〈1,2〉oxaphosphorin‐6‐yl)naphthalene with various aromatic diacid chlorides. All the poly(ester amide)s were amorphous and readily soluble in many organic solvents, such as N,N‐dimethylformamide, N,N‐dimethylacetamide (DMAc), and N‐methyl‐2‐pyrrolidone (NMP). Transparent, tough, and flexible films of these polymers were cast from DMAc and NMP solutions. Their casting films had tensile strengths of 71–214 MPa, elongations to break of 5–10%, and initial moduli of 2.3–6.0 GPa. These poly(ester amide)s had glass‐transition temperatures of 209–239 °C (m‐series) and 222–267 °C (p‐series). The degradation temperatures at 10% weight loss in nitrogen for these polymers ranged from 462 to 489 °C, and the char yields at 800 °C were 55–63%. Most of the poly(ester amide)s also showed a high char yield of 35–45%, even at 800 °C under a flow of air. The limited oxygen indices of these poly(ester amide)s were 35–46. © 2002 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 459–470, 2002; DOI 10.1002/pola.10129     

Synthesis and properties of novel aromatic polyhydrazides and poly(amide–hydrazide)s based on the bis(ether benzoic acid)s from hydroquinone and substituted hydroquinones

4,4′‐(1,4‐Phenylenedioxy)dibenzoic acid as well as the 2‐methyl‐, 2‐tert‐butyl‐, or 2‐phenyl‐substituted derivatives of this dicarboxylic acid were synthesized in two main steps from p‐fluorobenzonitrile and hydroquinone or its methyl‐, tert‐butyl‐, or phenyl‐substituted derivatives. Polyhydrazides and poly(amide–hydrazide)s were prepared from these bis(ether benzoic acid)s or their diacyl chlorides with terephthalic dihydrazide, isophthalic dihydrazide, or p‐aminobenzoyl hydrazide by means of the phosphorylation reaction or low‐temperature solution polycondensation. Most of the hydrazide polymers and copolymers are amorphous and readily soluble in various polar solvents such as N‐methyl‐2‐pyrrolidone (NMP) and dimethyl sulfoxide. They could be solution‐cast into transparent, flexible, and tough films. These polyhydrazides and poly(amide–hydrazide)s had T_gs in the range of 167–237°C and could be thermally cyclodehydrated into the corresponding poly(1,3,4‐oxadiazole)s and poly(amide–1,3,4‐oxadiazole)s approximately in the region of 250–350°C, as evidenced by the DSC thermograms. All the tert‐butyl‐substituted oxadiazole polymers and those derived from isophthalic dihydrazide were organic soluble. The thermally converted oxadiazole polymers exhibited T_gs in the range of 208–243°C and did not show significant weight loss before 450°C either in nitrogen or in air. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1169–1181, 1999     

Synthesis and characterization of new soluble polyamides derived from 3,3′,5,5′-tetramethyl-2,2-bis[4-(4-carboxyphenoxy)phenyl]propane

A series of new soluble polyamides having isopropylidene and methyl-substituted arylene ether moieties in the polymer chain were prepared by the direct polycondensation of 3,3′,5,5′-tetramethyl-2,2-bis[4-(4-carboxyphenoxy)phenyl]propane and various diamines in N-methyl-2-pyrrolidinone (NMP) containing CaCl₂ using triphenyl phosphite and pyridine as condensing agents. Polymers were produced with moderate to high inherent viscosities of 0.85–1.47 dL g⁻¹ while the weight-average molecular weight and number-average molecular weight were in the range of 86,700–259,000 and 43,300–119,000, respectively. All the polymers were readily dissolved in polar aprotic solvents such as NMP, N,N-dimethylacetamide, and N,N-dimethylformamide, as well as less polar solvents such as m-cresol and pyridine, and even soluble in tetrahydrofuran. These polymers were solution-cast into transparent, flexible and tough films. All of the polymers were amorphous and the polyamide films had a tensile strength range of 82–122 MPa, an elongation at break range of 6–18%, and a tensile modulus range of 2.0–2.8 GPa. These polyamides had glass transition temperatures between 233–260°C and 10% weight loss temperatures in the range of 450–489 and 459–493°C in nitrogen and air atmosphere, respectively. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1997–2003, 1999     

Synthesis and properties of novel cardo aromatic poly(ether‐benzoxazole)s

Three new bis(ether‐acyl chloride) monomers, 1,1‐bis[4‐(4‐chloroformylphenoxy)phenyl]cyclohexane ( 1a ), 5,5‐bis[4‐(4‐chloroformylphenoxy)phenyl]‐4,7‐methanohexahydroindan ( 1b ), and 9,9‐bis[4‐(4‐chloroformylphenoxy)phenyl]fluorene ( 1c ), were synthesized from readily available compounds. Aromatic polybenzoxazoles bearing ether and cardo groups were obtained by the low‐temperature solution polycondensation of the bis(ether‐acyl chloride)s with three bis(aminophenol)s and the subsequent thermal cyclodehydration of the resultant poly(o‐hydroxy amide)s. The intermediate poly(o‐hydroxy amide)s exhibited inherent viscosities in the range of 0.35–0.71 dL/g. All of the poly(o‐hydroxy amide)s were amorphous and soluble in many organic polar solvents, and most of them could afford flexible and tough films by solvent casting. The poly(o‐hydroxy amide)s exhibited glass‐transition temperatures (T_g's) in the range of 141–169 °C and could be thermally converted into the corresponding polybenzoxazoles approximately in the region of 240–350 °C, as indicated by the DSC thermograms. Flexible and tough films of polybenzoxazoles could be obtained by thermal cyclodehydration of the poly(o‐hydroxy amide) films. All the polybenzoxazoles were amorphous and showed an enhanced T_g but a dramatically decreased solubility as compared with their poly(o‐hydroxy amide) precursors. They exhibited T_g's of 215–272 °C by DSC and showed insignificant weight loss before 500 °C in nitrogen or air. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 4014–4021, 2001