(Dy,Mn)MCM-41介孔分子筛的合成与表征

在碱性条件下, 以十六烷基三甲基溴化铵为模板剂, Na2Si3O7为硅源, 用水热法合成了双金属介孔分子筛(Dy, Mn)MCM-41. 并用XRD, FT-IR, SEM, X射线荧光分析法、紫外漫反射等对样品进行表征. 实验结果证实所合成的产物为(Dy,Mn)MCM-41.     

YOx -MCM-41介孔分子筛的合成与表征

以十六烷基三甲基溴化铵为模板剂,偏硅酸钠为硅源,硝酸钇为钇源,用水热法合成了YOx-MCM-41介孔分子筛,经X射线粉末衍射法,FT-IR,热重分析,紫外漫反射法及N2吸附-脱附法表征。结果表明,该分子筛具有热稳定性好、比表面积大、孔道均一等典型的MCM-41介孔分子筛的特征。     

Sm-Al-MCM-41分子筛的合成与表征

以十六烷基三甲基溴化铵为模板剂, Na2Si3O7为硅源,采用水热合成方法制备了双金属Sm-Al-MCM-41介孔分子筛,并用XRD, FT-IR, SEM, TG-DTA等方法对样品进行表征.结果表明该分子筛具有典型的MCM-41介孔分子筛特征.     

骨架掺杂La／SBA-15介孔分子筛的合成与表征

以三嵌段共聚物P123为模板剂,正硅酸乙酯作为硅源,利用水热法,于80℃晶化合成了骨架掺杂La/SBA-15介孔分子筛,其结构经UV-Via,XRD,FT-IR,TEM和N2等温吸附-脱附法表征.结果表明,La离子直接进入了SBA-15分子筛的骨架;La/SBA-15分子筛具有规则的六方孔道结构,较高的比表面积(566.5 m2·g-1)和孔容(0.50 cm3·g-1),孔半径主要集中在1.70 nm.     

介孔材料MCM-41的合成与性能表征

在水热条件下用新的合成控制手段得到孔壁较厚的MCM-41介孔分子筛材料,并采用XRD、N2吸附、TG-DTA、SEM和吡啶程序升温脱附等测试手段对合成的MCM-41样品进行表征,结果表明合成的介孔材料结晶度比较高,具有六方排列的孔道结构,孔径分布较窄,BET表面积较大,样品热稳定性高,吡啶-TPD谱图表明样品具有弱的或中等强度的酸性.用MCM-41作为活性组分制备成催化剂,进行微反活性实验,表明其裂化活性较低,但对柴油有较高的选择性.     

杂化介孔分子筛HMS的合成与表征

以十六胺(HDA)为模板剂,通过正硅酸乙酯和硅烷偶联剂一步法合成了杂化介孔分子筛HMS,并通过XRD、N2吸脱附、FT-IR、TG、SEM等手段对其进行结构表征.结果表明合成的材料具有良好有序的介孔结构、大的孔径(≈2.04.0 nm)和比表面积(>600 m2g-1),接近球形颗粒,尺寸在0.51μm之间.     

纯二氧化钛介孔分子筛的合成与表征

分别用不同链长的烷基磷酸酯和脂肪胺两类不同表面活性剂为模板剂合成了纯二氧化钛介孔分子筛（Ti-TMS1，Ti-TMS2），并用溶剂法代替高温焙烧法成功地脱除了模板剂。用 XRD、TEM等测试手段对这类材料的结构进行了表征，研究了反应条件对所制备样品的结构的影响。结果表明：得到的纯二氧化钛介孔分子筛为较规则的六角堆积排列，孔径为2.7～4.4 nm, 且其纳米孔径大小可以通过改变烷基磷酸酯模板剂的烷基链长而调节。此外还发现，采用的烷基磷酸酯模板剂的烷基链越长，制得的二氧化钛介孔分子筛结构及晶型的完整性越好。进一步的研究表明，模板剂脱除之后，Ti-TMS2结构的晶体完整性和稳定性明显不如Ti-TMS1的好，且Ti-TMS1的介孔结构优于Ti-TMS2的介孔结构。     

介孔分子筛V-MCM-41的水热法制备与合成机理

 以十六烷基三甲基溴化铵为模板剂,廉价的工业级高模数比(3.3)的硅酸钠为硅源,通过水热法合成了V-MCM-41介孔分子筛. 考察了合成条件对产物织构的影响,并采用低温氮吸附法分析探讨了介孔分子筛V-MCM-41的合成机理. 结果表明,模板剂用量、 pH值、加料方式、晶化温度、晶化时间、陈化时间和焙烧气氛等合成条件对介孔分子筛的制备均有影响,其中晶化温度、 pH值和模板剂用量的影响最为明显. X射线衍射谱表明合成的介孔分子筛具有六方晶体结构. 红外光谱和紫外可见光谱表明V进入了介孔分子筛的骨架结构.     

铈掺杂的介孔分子筛的水热合成与结构性能

以硅酸钠、硝酸铈铵为原料,十六烷基三甲基溴化铵为模板剂,通过水热法合成铈掺杂的介孔分子筛CeMCM-41.分别采用X射线粉末衍射(XRD)、透射电子显微镜(TEM)、红外光谱(FT-IR)、紫外-可见分光光度计(UV-Vis)和N2吸附-脱附等技术对产物的晶相、结构、形貌、比表面积和孔径进行表征.同时研究硅铈物质的量比对合成材料结构性能的影响.实验结果表明:水热条件下成功合成出铈掺杂的MCM-41介孔分子筛,其比表面积为480.5～1 295.2m2/g,平均孔径在2.70～6.29 nm之间.随着稀土元素铈的掺杂量的增加,CeMCM-41介孔分子筛的比表面积和孔体积变小,介孔有序性变差.     

超声波合成介孔分子筛

介孔分子筛MCM鄄41自问世以来一直是材料研究的热门领域之一[1,2],目前报道的主要合成方法有水热合成法[3,4]、微波法[5,6]等。其中水热法反应时间长达3~5d,耗能大,不利于实用化生产。超声波化学又称声化学,是一门新兴的交叉学科。超声波的波长远大于分子尺寸,因而不能对分子直     

高纯度中孔分子筛MCM-41的合成与表征

用不同pH值的混合物制备了不同孔径的全硅MCM-41和不同金属离子取代的M-MCM-41(M=Al,Mn,Fe和V)分子筛.这些试样均呈现MCM-41的X射线粉末衍射特征峰和Ⅳ型氮气吸附等温线,但混有不同含量的无定形氧化硅.样品中MCM-41晶体的含量与溶胶的pH值和所用表面活性剂的碳链链长有关.骨架硅的金属离子取代降低了MCM-41的有序度,并且(100)面衍射峰强度从Al到V依次减弱.     

Acid Properties of SiMCM-41 Mesoporous Molecular Sieve

The SiMCM-41 mesoporous molecular sieve was synthesised by the hydrothermal method. The physicochemical characterisation by infrared spectroscopy, X-ray diffraction and thermogravimetry, showed that the material presents a well-defined structure. In this study, the determination of the total acidity and relative strength of the acid sites of the SiMCM-41,was performed by desorption of adsorbed n-butylamine combined with thermogravimetric measurements. The total acidity, determined by means of the amount of amine desorbed normalised by mass of solid, was equivalent to 0.927 mmol g^–1, in the temperature range from 96 to 235°C. By using the Flynn and Wall integral kinetic model, at 5, 10 and 20°C min^–1 heating rates, it was determined that the activation energy to desorb n-butylamine was 90.7 kJ mol^–1, in the same temperature range, evidencing that SiMCM-41 presents only weak acid sites on its surface. This revised version was published online in July 2006 with corrections to the Cover Date.     

萘普生在介孔分子筛MCM-41中的负载及其溶出性能

用含氨基的偶联剂修饰介孔分子筛MCM-41的表面,将修饰前和修饰后的介孔分子筛分别负载难溶性药物萘普生（NAP）,利用X射线衍射、傅里叶变换红外光谱、差示扫描量热分析、扫描电子显微镜、透射电子显微镜和N2吸附 脱附分析等技术分别对其进行了结构表征和性能测试。 结果表明,药物分子存在于分子筛的孔道中。 负载在MCM-41中的萘普生溶出速率远优于原料药,60 min时大约溶出70%。 氨基修饰后的药物释放速率比修饰前有所减慢,表明可通过氨基修饰调节释放速率。     

非水介质中合成介孔分子筛MCM-41

首次采用十六烷基三甲基溴化铵为模板剂、正硅酸乙酯为硅源, 分别使用无机和有机弱碱, 溶剂热晶化法在非水甘油介质中合成了介孔分子筛MCM-41, 通过XRD, N₂吸附-脱附, TG-DTG, IR, SEM等测试手段对样品进行了表征分析, 结果表明在甘油体系中得到的样品具有优良的孔结构性质. 相比于氢氧化钠, 以有机弱碱(无水乙二胺、三乙胺)作为碱源, 可以得到有序性更好、结晶度高的样品, 样品具有较窄的孔径分布.     

介孔分子筛MCM-41表面的有机胺功能化及其应用

采用γ-胺丙基三甲氧基硅烷与表面硅羟基的反应,对介孔分子筛MCM-41进行了有机胺功能化.并对其进行了表征.XRD、比表面积测定、元素分析、TG、FT-IR和TEM的测定结果均表明,MCM-41表面成功地接枝上了有机胺功能基团而六方结构特征基本保持.在有机胺功能化的MCM-41上固载Ru基催化剂,并将其用于CO2加H2合成HCOOH反应,所显示的活性优于相应的均相催化剂,并且该催化剂具有较好的回收再用性能.     

含钛中孔分子筛Ti-MSU的合成和表征

作为一种具有新型结构的功能材料、中孔分子筛以其具有较大的孔径、很大的比表面积和优良的吸附性能等诸多优点而引起了催化、吸附分离、无机合成及材料科学等许多领域内研究者的广泛关注.M41S[1]、HMS[2]、SBA-n[3]及MSU[4]等一系列的中孔分子筛相继问世.在这几类中孔分子筛中,MSU系列中孔分子筛因使用价廉、无毒、可生物降解的聚氧乙烯基醚类非离子型表面活性剂作为模板剂而对于当今世界人们普遍关注的环境友好化学具有尤为重要的意义.     

中孔分子筛MCM-41形成机理的考察

MCM－41分子筛是九十年代初期美国Mobil公司开发的一种新型中孔（mesoporous）材料[1]．它以C8－C16季俊碱表面活性剂作为模板剂水热法合成，具有2－10nm的孔径，孔道六方有序排列，高比表面和高吸附容量，中等酸性和稳定性，是一种有潜在应用前景的吸附和催化材料．目前，关于     

表面功能化的介孔分子筛SBA-3的表征

采用γ-氨丙基三乙氧基硅烷（AM）,通过表面硅烷化反应,对脱模板后的纯 硅六方介孔分子筛SBA-3进行了表面功能化,并通过XRD,TEM,低温N_2吸附, FTIR和吸附染料分子的UV-vis漫反射光谱等对功能化样品的结构、孔性质和表面极 性等进行了详细表征。结果表明,功能分子锚接后,样品的六方结构基本保持。样 品的表面硅羟基由于被消耗而明显减少,导致表面极性降低。另外,由于功能分子 占据了部分孔道空间,样品的孔容、表面积和孔径下降。