Combustion synthesis and luminescence properties of NaY1−xEux(WO4)2 phosphors

The red phosphors NaY_1−xEu_x(WO₄)₂ with different concentrations of Eu³⁺ were synthesized via the combustion synthesis method. As a comparison, NaEu(WO₄)₂ was prepared by the solid-state reaction method. The phase composition and optical properties of as-synthesized samples were studied by X-ray powder diffraction and photoluminescence spectra. The results show that the red light emission intensity of the combustion synthesized samples under 394 nm excitation increases with increase in Eu³⁺ concentrations and calcination temperatures. Without Y ions doping, the emission spectra intensity of the NaEu(WO₄)₂ phosphor prepared by the combustion method fired at 900 °C is higher than that prepared by the solid-state reaction at 1100 °C. NaEu(WO₄)₂ phosphor synthesized by the combustion method at 1100 °C exhibits the strongest red emission under 394 nm excitation and appropriate CIE chromaticity coordinates (x=0.64, y=0.33) close to the NTSC standard value. Thus, its excellent luminescence properties make it a promising phosphor for near UV InGaN chip-based red-emitting LED application.     

Luminescent properties of HTP AgGd1−xW2O8:Eux and AgGd1−x(W1−yMoy)2O8:Eux phosphor for white LED

Intense red phosphors, AgGd_1−xEu_x(W_1−yMo_y)₂O₈ (x=0.0-1.0, y=0.0-1.0), have been synthesized through traditional solid-state reaction and characterized by X-ray diffraction (XRD) and photoluminescence (PL). XRD results reveal that AgGd_1−xEu_xW₂O₈ synthesized at 1000 °C has a tetragonal crystal structure, which is named as high temperature phase (HTP) AgGdW₂O₈. All phosphors compositions with Eu³⁺ show red and green emission on excitation either in the charge-transfer or Eu³⁺ levels. Analysis of the emission spectra with different Eu³⁺ concentrations reveal that the optimum dopant concentration for Eu³⁺ is x=0.6 in the HTP AgGd_1−xEu_xW₂O₈ (x=0.0-1.0). Studies on the AgGd_0.4Eu_0.6(W_1−yMo_y)₂O₈ (y=0.0-1.0) and AgGd_1−xEu_x(W_0.7Mo_0.3)₂O₈ (x=0.0-1.0) show that the emission intensity is maximum for compositions with y=0.3 and x=0.5, respectively, and a decrease in emission intensity is observed for higher y or x values. The Mo⁶⁺ and Eu³⁺ co-doped AgGd(WO₄)₂ phosphors show higher emission intensity in comparison with the singly Eu³⁺-doped AgGd(WO₄)₂ in UV region. The intense emission of the tungstate/molybdate phosphors under 394 and 465 nm excitations, respectively, suggests that these materials are promising candidates as red-emitting phosphors for near-UV/blue GaN-based white LED for white light generation.     

Low-voltage cathodoluminescence property of Li-doped Gd2−xYxO3:Eu

Cathodoluminescent (CL) spectra of Li-doped Gd_2−xY_xO₃:Eu³⁺ solid-solution (0.0?x?0.8) were investigated at low voltages (300 V-1 kV). The CL intensity is maximum for the composition of x=0.2 and gradually reduces with increasing the amount of substituted Y content. In particular, small (∼100 nm) particles of Li-doped Gd_1.8Y_0.2O₃:Eu³⁺ are obtained by firing the citrate precursors at only 650°C for 18 h. Relative red-emission intensity at 300 V of this phosphor is close to 180% in comparison with that of commercial red phosphor Y₂O₃:Eu³⁺. An increase of firing temperature to 900°C results in 400-600 nm sized spherical particles. At low voltages (300-800 V), the CL emission of 100 nm sized particles is much stronger than that of 400-600 nm sized ones. In contrast, the larger particles exhibit the higher CL emission intensity at high voltages (1-10 kV). Taking into consideration small spherical morphology and effective CL emission, Li-doped Gd_1.8Y_0.2O₃:Eu³⁺ appears to be an efficient phosphor material for low voltage field emission display.     

Luminescent properties of green- or red-emitting Eu-doped Sr3Al2O6 for LED

Eu²⁺-doped Sr₃Al₂O₆ (Sr_3−xEu_xAl₂O₆) was synthesized by a solid-state reaction under either H₂ and N₂ atmosphere or CO atmosphere. When H₂ was used as the reducing agent, the phosphor exhibited green emission under near UV excitation, while CO was used as the reducing agent, the phosphor mainly showed red emission under blue light excitation. Both emissions belong to the d-f transition of Eu²⁺ ion. The relationship between the emission wavelengths and the occupation of Eu²⁺ at different crystallographic sites was studied. The preferential substitution of Eu²⁺ into different Sr²⁺ cites at different reaction periods and the substitution rates under different atmospheres were discussed. Finally, green-emitting and red-emitting LEDs were fabricated by coating the phosphor onto near UV- or blue-emitting InGaN chips.     

Green emitting long lasting phosphorescence (LLP) properties of Mg2SnO4:Mn phosphor

A novel long-lasting phosphorescence phosphor, Mn²⁺-activated Mg₂SnO₄, has been synthesized and its optical properties have been investigated. The Mg₂SnO₄:Mn²⁺ emits green light with high luminance, upon UV irradiation, centered at 499 nm from the spin forbidden transitions of the d-electrons in Mn²⁺ ions. The CIE chromaticity coordinates of the Mg₂SnO₄:Mn²⁺ phosphor are x=0.0875 and y=0.6083 under 254 nm UV excitation. The phosphorescence can be observed by the naked eyes (0.32 mcd/m²) in the dark clearly for over 5 h after the 5 min UV irradiation. Thermoluminescence has been studied and the mechanism of the long-lasting phosphorescence has been discussed.     

White light-emitting diodes using blue and yellow-orange-emitting phosphors

A blue-emitting phosphor, BaMgAl₁₀O₁₇:Eu²⁺ (BAM) and a yellow-orange phosphor, Ba²⁺-codoped Sr₃SiO₅:Eu²⁺ were prepared by the solid-state reaction. Excitation and emission spectra results showed that BAM and Ba²⁺-codoped Sr₃SiO₅:Eu²⁺ can be efficiently excited by near-ultraviolet (n-UV)-visible light from 250 to 440 nm. The effects of the doped-Eu²⁺ concentration in BAM and Ba²⁺-codoped Sr₃SiO₅:Eu²⁺ on the photoluminescence were investigated in detail. White light-emitting diodes (LED) was obtained by combining n-UV LED chip (GaN-based 380 nm emitting) with BaMgAl₁₀O₁₇:0.09Eu²⁺ and 0.1Ba²⁺-codoped Sr₃SiO₅: 0.2Eu²⁺ phosphors with the characteristic of color-rendering index of 86, CIE chromaticity coordinates (x,y) of (0.3216,0.3096), and color temperature T_c of 5700 K. As the current increases, the relative intensity simultaneously increases. The CIE chromaticity coordinates (x,y) of the white LED tends to decrease. The correlated color temperature T_c increases from 4100 to 7500 K and the color-rendering index R_a increases from 82 to 87 simultaneously.     

Improved luminescent properties of red-emitting Ca0.54Sr0.16Eu0.08Gd0.12(MoO4)0.2(WO4)0.8 phosphor for LED application by charge compensation

The red-emitting Ca_0.54Sr_0.16Eu_0.08Gd_0.12(MoO₄)_0.2(WO₄)_0.8 phosphor is improved in the emission charateristics by charge compensation, of which chromaticity coordinates (CIE) are x=0.66 and y=0.33. Three approaches to charge compensation are investigated, namely (a) 3Ca²⁺/Sr²⁺→2Eu³⁺/Gd³⁺+vacancy, (b) 2Ca²⁺/Sr²⁺→Eu³⁺/Gd³⁺+M⁺(M⁺ is a monovalent cation like Li⁺, Na⁺ and K⁺ employed as a charge compensator) and (c) Ca²⁺/Sr²⁺→Eu³⁺/Gd³⁺+N⁻ (N⁻ is a monovalent anion like F⁻, Cl⁻, Br⁻ and I⁻ employed as charge compensation ions). Through photoluminescent spectra analyzing the radiative and non-radiative relaxation mechanisms of luminescent system are obtained. Under 20 mA forward-bias current, one red-emitting LED is made by combining 390-405 nm-emitting LED chip and the phosphor. The red-emitting phosphor has broad prospects in LED application field.     

Synthesis and luminescent properties of Y6W2O15:Eu phosphors

In this paper, a novel phosphor, Y₆W₂O₁₅:Eu³⁺ was synthesized by thermal decomposition and phase transition of its decatungstate gel precursor. With stepwise increase of temperature to 750 °C, a crystalline phase of Y₆W₂O₁₅:Eu³⁺forms that gives intense red emission when excited at 466 nm, the emission is attributed to the Eu³⁺ ions transitions from ⁵D₀ excited states to ⁷F_J (J=0-4) ground states. The long excitation wavelength proves the Eu³⁺ transition follows the photoexcitation of the oxygen-metal (O→W lmct) charge transfer bands in yttrium tungstate. Some structural information regarding Y₆W₂O₁₅ provided by luminescence is in accord with that characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). The long-wavelength excitation properties of this material may find application in the production of red phosphors for white light-emitting diodes (LEDs).     

Photoluminescence properties and effects of dopant concentration in Bi2ZnB2O7:Tb phosphor

A novel green phosphor, Tb³⁺ doped Bi₂ZnB₂O₇ was synthesized by conventional solid state reaction method. The phase of synthesized materials was determined using the XRD, DTA/TG and FTIR. The photoluminescence characteristics were investigated using spectrofluorometer at room temperature. Bi₂ZnB₂O₇:Tb³⁺ phosphors excited by 270 nm and 485 nm wavelengths. The emission spectra were composed of three bands, in which the dominated emission of green luminescence Bi₂ZnB₂O₇:Tb³⁺ attributed to the transition ⁵D₄ → ⁷F₅ is centered at 546 nm. The dependence of the emission intensity on the Tb³⁺ concentration for the Bi_2−xTb_xZnB₂O₇ (0.01 ≤ x ≤ 0.15) was studied and observed that the optimum concentration of Tb³⁺ in phosphor was 13 mol% for the highest emission intensity at 546 nm.     

Synthesis and Eu concentration-dependent photoluminescence of Gd2−xEuxO3 nanowires

The nanowire growth behavior and photoluminescence characteristics of red-emitting oxide phosphor Gd_2−xEu_xO₃ have been investigated in the function of activator (Eu³⁺) concentrations (x=0.08, 0.12, 0.16, 0.20, and 0.24). Nanowires of Gd_2−xEu_xO₃ phosphor were prepared by the dehydration of corresponding hydroxides Gd_1−x/2Eu_x/2(OH)₃ obtained by the hydrothermal reaction. Highly uniform nanowires of 20-30 nm in diameter can grow up to several tens of micrometers in length. A number of defects on the surface of Gd_1.92Eu_0.08O₃ nanowires, which are induced during structural transformation from hexagonal hydroxide to cubic oxide, strongly decrease the luminescence efficiency in comparison with that of the bulk phosphor. In contrast, the photoemission intensity of nanowires is significantly improved with increasing Eu³⁺ content (x) of Gd_2−xEu_xO₃ solid solution. The highest relative emission intensity of nanowires is observed when the x value is close to x=0.20. This content is much higher than the optimal concentration of Eu³⁺ (x=0.08-0.10) for the bulk Gd₂O₃:Eu powder.     

Luminescent properties of Eu-activated Sr3B2SiO8: A red-emitting phosphor for white light-emitting diodes

Single-phased Sr₃B₂SiO₈:Eu³⁺ phosphor was prepared by a solid-state method at 1020 °C. The luminescence spectra showed that Sr₃B₂SiO₈:Eu³⁺ phosphor can be effectively excited by near ultraviolet light (393 nm) and blue light (464 nm). When excited at 393 or 464 nm Sr₃B₂SiO₈:Eu³⁺ exhibited the main emission peaks at 611 and 620 nm, which resulted from the supersensitive ⁵D₀→⁷F₂ transition of Eu³⁺. The luminescence intensity of Sr₃B₂SiO₈:Eu³⁺ at 611 and 620 nm reached the maximum when the doping content of Eu³⁺ was 4.5 mol%. Its chromaticity coordinates (0.646, 0.354) were very close to the NTSC standard values (0.67, 0.33). Thus, Sr₃B₂SiO₈:Eu³⁺ is considered to be an efficient red-emitting phosphor for long-UV InGaN-based light-emitting diodes.     

Emission analysis of Pr and Tm: Ca2Gd2W3O14 phosphors

5 mol% of Pr³⁺ and Tm³⁺ ions activated calcium gadolinium tungstate (Ca₂Gd₂W₃O₁₄₎ phosphors were synthesized by traditional solid state reaction method. Crystalline phase structure was identified from the X-ray diffraction (XRD) profiles. From the scanning electron microscopy (SEM) images, we have observed the agglomeration of the particles, and average grain size is around 40-300 nm. Using the energy dispersive X-ray analysis (EDAX) and Fourier transform infrared (FTIR) spectra, identified the elements and functional groups present in the prepared phosphors. The emission spectrum of Pr³⁺: Ca₂Gd₂W₃O₁₄ powder phosphors have shown an intense red emission at 615 nm with the excitation wavelength λ_exci=450 nm and thus these red color emitting powder phosphors are used as one of the components in the preparation of WLEDs. The excitation spectrum of Tm³⁺: Ca₂Gd₂W₃O₁₄ powder phosphor has shown a ligand to metal charge transfer (W-O) band (LMCT) within the WO₄²⁻ group. Emission spectrum of Tm³⁺: Ca₂Gd₂W₃O₁₄ phosphors have shown blue emissions at 453 nm (¹D₂→³F₄).     

Luminescent properties of KGd1−x(WO4)2:Eux and KGd1−x(WO4)2−y(MoO4)y:Eux phosphors in UV-VUV regions

KGd_1−x(WO₄)_2−y(MoO₄)_y:Eu³⁺_x(0.1?x?0.75, y=0 and 0.2) phosphors are synthesized through traditional solid-state reaction and their luminescent properties in ultraviolet (UV) and vacuum ultraviolet (VUV) regions are investigated. Under 147 nm excitation, these phosphors show characteristic red emission with good color purity. In order to improve their emission intensity, the MoO₄²⁻ (20 wt%) is introduced into the anion of KGd_1−x(WO₄):Eu³⁺_x. The Mo⁶⁺ and Eu³⁺ co-doped KGd(WO₄)₂ phosphors show higher emission intensity in comparison with the singly Eu³⁺-doped KGd(WO₄)₂ in VUV region. The chromaticity coordination of KGd_0.45(WO₄):Eu³⁺_0.55 is (x=0.669, y=0.331), while that of KGd_0.45(WO₄)_1.8(MoO₄)_0.2:Eu³⁺_0.55 is (x=0.666, y=0.334) in VUV region.     

Luminescence studies on ZnO-P2O5 glasses doped with Gd2O3:Eu nanoparticles and Eu2O3

Zinc phosphate glasses doped with Gd₂O₃:Eu nanoparticles and Eu₂O₃ were prepared by conventional melt-quench method and characterized for their luminescence properties. Binary ZnO-P₂O₅ glass is characterized by an intrinsic defect centre emission around 324 nm. Strong energy transfer from these defect centres to Eu³⁺ ions has been observed when Eu₂O₃ is incorporated in ZnO-P₂O₅ glasses. Lack of energy transfer from these defect centres to Eu³⁺ in Gd₂O₃:Eu nanoparticles doped ZnO-P₂O₅ glass has been attributed to effective shielding of Eu³⁺ ions from the luminescence centre by Gd-O-P type of linkages, leading to an increased distance between the luminescent centre and Eu³⁺ ions. Both doped and undoped glasses have the same glass transition temperature, suggesting that the phosphate network is not significantly affected by the Gd₂O₃:Eu nanoparticles or Eu₂O₃ incorporation.     

Luminescence properties of Y2WO6:Eu incorporated with Mo or Bi ions as red phosphors for light-emitting diode applications

In this study, the red phosphors, Y₂W_1−xMo_xO₆:Eu³⁺ and Y₂WO₆:Eu³⁺,Bi³⁺, have been investigated for light-emitting diode (LED) applications. In Y₂WO₆:Eu³⁺, the excitation band edge shifts to longer wavelength with the incorporation of Mo⁶⁺ or Bi³⁺ ions. The emission spectra exhibit ⁵D₀→⁷F₁ and ⁵D₀→⁷F₂ transition of Eu³⁺ ion at 588, 593, and 610 nm, respectively. Moreover, the bluish-green luminescence of the WO₆⁶⁻ at about 460 nm is observed to decrease with the incorporation of Mo⁶⁺, which results in pure red color. Thus, this study shows that the red phosphor, Y₂WO₆:Eu³⁺, incorporated with Mo⁶⁺ or Bi³⁺ ions is advantageous for LEDs applications.     

Sol-gel growth of Gd2MoO6:Eu nanocrystalline layers on SiO2 spheres (SiO2@Gd2MoO6:Eu) and their luminescent properties

SiO₂@Gd₂MoO₆:Eu³⁺ core-shell phosphors were prepared by the sol-gel process. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), field emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectra (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra as well as kinetic decays were used to characterize the resulting SiO₂@Gd₂MoO₆:Eu³⁺ core-shell phosphors. The XRD results demonstrate that the Gd₂MoO₆:Eu³⁺ layers on the SiO₂ spheres begin to crystallize after annealing at 600 °C and the crystallinity increases with raising the annealing temperature. The obtained core-shell phosphors have a near perfect spherical shape with narrow size distribution (average size ca. 600 nm), are not agglomerated, and have a smooth surface. The thickness of the Gd₂MoO₆:Eu³⁺ shells on the SiO₂ cores could be easily tailored by varying the number of deposition cycles (50 nm for four deposition cycles). The Eu³⁺ shows a strong PL luminescence (dominated by ⁵D₀-⁷F₂ red emission at 613 nm) under the excitation of 307 nm UV light. The PL intensity of Eu³⁺ increases with increasing the annealing temperature and the number of coating cycles.     

Characterization of the VUV excitation spectrum of BaZr(BO3)2:Eu

The excitation spectra of M (M=Si⁴⁺, Ti⁴⁺) and Eu³⁺ co-doped BaZr(BO₃)₂, BaZrO₃:Eu and La₂Zr₂O₇:Eu in the vacuum ultraviolet (VUV) regions of 110-300 nm are investigated and the host-lattice absorption are characterized. The result indicated that BaZr(BO₃)₂:Eu³⁺ phosphor has a strong absorption under the VUV excitation, and in the host-lattice excitation, the strong band at 130-160 nm could be due to the BO₃ atomic groups; the band at 160-180 nm is related to the excitation of Ba-O; 180-200 nm corresponds to the charge transfer (CT) transition of Zr-O. The band at 200-235 nm due to the CT band of Eu³⁺-O²⁻ and a bond valence study explained the observed weak CT band of Eu³⁺-O²⁻ in the excitation spectra of BaZr(BO₃)₂:Eu³⁺. The emission results show that Si⁴⁺ can sensitize luminescence in the host of BaZr(BO₃)₂:Eu but Ti⁴⁺ has no improvement effect on luminescence.     

Photoluminescence and EPR studies of BaMgAl10O17:Eu phosphor with blue-emission synthesized by the solution combustion method

A blue phosphor, BaMgAl₁₀O₁₇:Eu²⁺, has been synthesized in the furnace at a temperature of 500 °C by solution combustion method. The formation of the as-prepared BaMgAl₁₀O₁₇:Eu²⁺ phosphor was confirmed by the powder X-ray diffraction technique. The EPR spectrum exhibited an intense resonance signal centered at g=4.63 at 150 mT along with a number of resonances in the vicinity of g>2.0 and g<2.0. The number of spins participating in resonance (N) and the susceptibility (c) for the resonance signal at g=4.63 have been calculated as a function of temperature. The excitation spectrum of BaMgAl₁₀O₁₇:Eu²⁺ phosphor showed a strong peak near 336 nm (4f⁷ (⁸S)→5d¹(t_2g) transition) with a staircase like structure in the region 376-400 nm owing to crystal field splitting of the Eu²⁺ d-orbital. The 336 nm excitation produced a broad blue emission at 450 nm corresponding to 4f⁶5d→4f⁷ transition. PL studies reveal the two emission centers one at 450 nm and the other at 490 nm in this phosphor.     

Effect of Eu,Tb codoping on the luminescent properties of Y2O3 nanorods

Red-emitting Y₂O₃:Eu³⁺ and green-emitting Y₂O₃:Tb³⁺ and Y₂O₃:Eu³⁺, Tb³⁺ nanorods were synthesized by hydrothermal method. Their structure and micromorphology have been analyzed by X-ray powder diffraction (XRD) and transmission electron microscopy (TEM). The photoluminescence (PL) property of Y₂O₃:Eu³⁺,Tb³⁺ phosphor was investigated. In the same host (Y₂O₃), upon excitation with ultraviolet (UV) irradiation, it is shown that there are strong emissions at around 610 and 545 nm corresponding to the forced electric dipole ⁵D₀-⁷F₂ transition of Eu³⁺ and ⁵D₄-⁷F₅ transition of Tb³⁺, respectively. Different qualities of Eu³⁺and Tb³⁺ ions are induced into the Y₂O₃ lattice. From the excitation spectrum, we speculate that there exists energy transfer from Tb³⁺ to Eu³⁺ ions .The emission color of powders reveals regular change in the separation of light emission. These powders can meet with the request of optical display material for different colors or can be potentially used as labels for biological molecules.     

Optical properties of (ZnO)0.5(P2O5)0.5 glasses doped with Gd2O3:Eu nanoparticles and Eu2O3

Binary (ZnO)_0.5(P₂O₅)_0.5 glasses doped with Eu₂O₃ and nanoparticles of Gd₂O₃:Eu were prepared by conventional melt-quench method and their luminescence properties were compared. Undoped (ZnO)_0.5(P₂O₅)_0.5 glass is characterized by a luminescent defect centre (similar to L-centre present in Na₂O-SiO₂ glasses) with emission around 324 nm and having an excited state lifetime of 18 ns. Such defect centres can transfer the energy to Eu³⁺ ions leading to improved Eu³⁺ luminescence from such glasses. Based on the decay curves corresponding to the ⁵D₀ level of Eu³⁺ ions in both Gd₂O₃:Eu nanoparticles incorporated as well as Eu₂O₃ incorporated glasses, a significant clustering of Eu³⁺ ions taking place with the latter sample is confirmed. From the lifetime studies of the excited state of L-centre emission from (ZnO)_0.5(P₂O₅)_0.5 glass doped with Gd₂O₃:Eu nanoparticles, it is established that there exists weak energy transfer from L-centres to Eu³⁺ ions. Poor energy transfer from the defect centres to Eu³⁺ ions in Gd₂O₃:Eu nanoparticles doped (ZnO)_0.5(P₂O₅)_0.5 glass has been attributed to effective shielding of Eu³⁺ ions from the luminescence centre by Gd-O-P type of linkages, leading to an increased distance between luminescent centre and Eu³⁺ ions.