Crystallization behavior of Zr41Ti14Cu12.5Ni10Be22.5 bulk metallic glass under the action of high-density pulsing current

The crystallization behavior of Zr₄₁Ti₁₄Cu_12.5Ni₁₀Be_22.5 bulk metallic glass (Vit1 BMG) under the action of high-density pulsing current (HDPC) have been studied experimentally. It has been found that high-density pulsing current can directly induce the rapid nanocrystallization of Vit1 BMG. The multiple crystallization processes of Vit1 BMG induced by HDPC have been confirmed as Amorphous → Amorphous + i-phase → Be₂Zr + Zr₂Cu + Ni₇Zr₂ + FCC phase + other phases → Zr₂Cu + Ni₇Zr₂ + FCC phase + other phases. By comparing to the crystallization behavior of Vit1 BMG induced by isothermal annealing, the crystallization temperature is reduced and crystallizing process is significantly shortened, while the sequence of crystallization process in both cases is basically same. The present results show that the HDPC has significantly influenced the crystallizing kinetics of Vit1 BMG due to that it can greatly promote the movement and rearrangement of atoms, which will result in a rapid nanocrystallization. It suggests that HDPC treatment can be an effective way to induce the rapid nanocrystallization of BMGs.     

The effect of PbF2 content on the microstructure and upconversion luminescence of Er-doped SiO2-PbF2-PbO glass ceramics

The Er³⁺ doped transparent oxyfluoride glass ceramics were obtained by appropriate heat treatment of the precursor glasses with composition (mol%) 50SiO₂-xPbF₂-(50 − x)PbO-0.5ErF₃. The microstructure and optical properties of the glasses and glass ceramics were determined by differential scanning calorimetry (DSC), X-ray diffraction (XRD), absorption spectra and luminescence spectra. The intensity of upconversion luminescence significantly increased in glass ceramics compared to that in precursor glass. The emission bands centered around 660 nm (⁴F_9/2 → ⁴I_15/2) and 410 nm (²H_9/2 → ⁴I_15/2) were simultaneously observed in glass ceramics but cannot be seen in the corresponding precursor glass. The influence of different PbF₂ content on the microstructure and upconversion luminescence of the samples was analyzed in detail. The results indicated that with the increase of PbF₂ content, the Ω₂ was almost the same and the ratios of red to green upconversion luminescence decreased in glass ceramics.     

Glass formation ability and mechanical properties of Ti40Cu40Zr10Ni10 alloy

Melt-spun ribbon and bulk samples in cylindrical rod form with diameter ranging from 2 mm to 4 mm of Ti₄₀Cu₄₀Zr₁₀Ni₁₀ alloy were prepared by melt-spinning technique and copper mould casting method, respectively. The microstructure, thermal stability and mechanical properties of the bulk samples were investigated. A completely glassy single phase is formed in the 2 mm rod sample. Increasing the diameter of the rod samples resulted in the formation of CuTi crystalline phase in the 3 mm and 4 mm rod samples. The 2 mm single glassy rod sample exhibited a large supercooled liquid region ΔT_x = 58 K and γ = T_x/(T_g + T_l) is 0.390, which indicated that the alloy possessed a good glass-forming ability. The bulk samples also exhibited good mechanical properties. The 2 mm rod sample showed the highest yield strength of about 2086 MPa. The 3 mm rod sample not only showed high yield strength of about 2000 MPa, but also enhanced plastic strain of about 0.71%.     

Mg based bulk metallic glasses: Glass transition temperature and elastic properties versus toughness

In this work, optimal compositions for bulk metallic glasses (BMGs) formation in the ternary Mg-Cu-Nd and Mg-Ni-Nd systems are located at the Mg₅₇Cu₃₄Nd₉ and Mg₆₄Ni₂₁Nd₁₅, respectively, with the critical diameter of 4 mm for the rods fabricated by copper mold casting. As indicated by notch toughness testing, Mg₆₄Ni₂₁Nd₁₅ BMG (K_Q = 5.1 MPa√m) manifests higher toughness with respect to the Mg₅₇Cu₃₄Nd₉ (K_Q = 3.6 MPa√m), even though both BMGs have similar compressive fracture strength of 870-880 MPa. Such an improvement in toughness for Mg BMGs correlates with the reduction of shear modulus and the enhancement of thermal stability to resist to the structural relaxation at room temperature, which is indicated by the elevated glass transition temperature T_g. Under the Mode I loading condition, morphology in fracture surface of the Mg₆₄Ni₂₁Nd₁₅ BMG varies along the crack propagation path. Fractographic evolution of the fracture surface follows the Taylor's meniscus instability criterion. For the Mg-based BMGs, shear modulus scales with the glass transition temperature, and can be expressed as μ = 4.7 + 625T_g/V_m[1-4/9(T/T_g)^2/3]. Meanwhile, correlation between the calorimetric T_g and elastic properties at T_g can be rationalized with Egami's model.     

Structure and properties of Ni60(Nb100−xTax)34Sn6 bulk metallic glass alloys

Refractory bulk metallic glasses and bulk metallic glass composites are formed in quaternary Ni-Nb-Ta-Sn alloy system. Alloys of composition Ni₆₀(Nb_100−xTa_x)₃₄Sn₆ (x = 20, 40, 60, 80) alloys were prepared by injection-casting the molten alloys into copper molds. Glassy alloys are formed in the thickness of half mm strips. With thicker strips (e.g., 1 mm), Nb₂O₅ and Ni₃Sn phases and the amorphous phase form an in situ composite. Glass transition temperatures, crystallization temperatures, and ΔT_x, defined as T_x1 − T_g (T_x1: first crystallization temperature, T_g: glass transition temperature) of the alloys increase dramatically with increasing Ta contents. These refractory bulk amorphous alloys exhibit high Young’s modulus (155-170 GPa), shear modulus (56-63 GPa), and estimated yield strength (3-3.6 GPa).     

The glass transition temperature and infrared absorption spectra of: (70−x)TeO2 + 15B2O3 + 15P2O5 + xLi2O glasses

Glasses of the system: (70−x) TeO₂ + 15B₂O₃ + 15P₂O₅ + xLi₂O, where x = 5, 10, 15, 20, 25 and 30 mol% were prepared by melt quench technique. Dependencies of their glass transition temperatures (T_g) and infrared (IR) absorption spectra on composition were investigated. It is found that the gradual replacement of oxides, TeO₂ by Li₂O, decreases the glass transition temperature and increases the fragility of the glasses. Also, IR spectra revealed broad weak and strong absorption bands in the investigated range of wave numbers from 4000 to 400 cm⁻¹. These bands were assigned to their corresponding bond modes of vibration with relation to the glass structure.     

Role of nickel ion coordination on spectroscopic and dielectric properties of ZnF2-As2O3-TeO2:NiO glass system

20ZnF₂-30As₂O₃-(50 − x)TeO₂:xNiO (0 ≤ x ≤ 2.0) glasses were synthesized. The glasses were characterized by X-ray diffraction, scanning electron microscopy, EDS and DSC techniques. A variety of properties, i.e. optical absorption, infrared, magnetic susceptibilities and dielectric properties (constant ?′, loss tan δ, a.c. conductivity σ_ac over a wide range of frequency and temperature) of these glasses have been carried out. The analysis of results of all these studies has indicated that the nickel ions occupy both octahedral and tetrahedral positions and the gradual increase of NiO content in the glass matrix causes growing proportions of Ni²⁺ ions that occupy octahedral positions. The luminescence spectra of these glasses have exhibited a broad emission band in region 1200-1450 nm identified due to ³T₂(3F) → ³A₂(3F) octahedral transition of Ni²⁺ ions. The luminescence efficiency and cross section have been found to be the highest for the glass containing highest concentration of NiO. Finally it is concluded that the higher the concentration of octahedrally positioned Ni²⁺ ions, the higher is the luminescence efficiency.     

Three-dimensional structure of fast ion conducting 0.5Li2S + 0.5[(1 − x)GeS2 + xGeO2] glasses from high-energy X-ray diffraction and reverse Monte Carlo simulations

A high-energy X-ray diffraction study has been carried out on a series of 0.5Li₂S + 0.5[(1 − x)GeS₂ + xGeO₂] glasses with x = 0.0, 0.1, 0.2, 0.4, 0.6 and 0.8. Structure factors were measured to wave vectors as high as 30 Å⁻¹ resulting in atomic pair distribution functions with high real space resolution. The three dimensional atomic-scale structure of the glasses was modeled by reverse Monte Carlo simulations based on the diffraction data. Results from the simulations show that at the atomic-scale 0.5Li₂S + 0.5[(1 − x)GeS₂ + xGeO₂] glasses may be viewed as an assembly of independent chains of (Li^+-S)₂GeS_2/2 and (Li^+-O)₂GeO_2/2 tetrahedra as repeat units, where the Li ions occupy the open space between the chains. The new structure data may help understand the reasons for the sharp maximum in the Li⁺ ion conductivity at x ∼ 0.2.     

Non-isothermal crystallization kinetics study on new amorphous Ga20Sb5S75 and Ga20Sb40S40 chalcogenide glasses

Bulk glasses of the system Ga₂₀Sb_xS_80−x (x = 5 and 40) were prepared for the first time by the known melt quenching technique. Non-isothermal differential scanning calorimetric (DSC) measurements of as-quenched Ga₂₀Sb_xS_80−x (x = 5 and 40) chalcogenide glasses reveal that the characteristic temperatures e.g. the glass transition temperature (T_g), the temperature corresponding to the maximum crystallization rate (T_p) recorded in the temperature range 400-650 K for x = 5 and 480-660 K for x = 40 are strongly dependent on heating rate and Sb content. Upon heating, these glasses show a single glass transition temperature (T_g) and double crystallization temperatures (T_p1 and T_p2) for x = 5 which overlapped and appear as a single crystallization peak (T_p) for x = 40. The activation energies of crystallization E_c were evaluated by three different methods. The crystallization data were examined in terms of recent analysis developed for non-isothermal conditions. The crystalline phases resulting from (DSC) have been identified using X-ray diffraction.     

Effect of Bi2O3 proportion on physical, structural and electrical properties of zinc bismuth phosphate glasses

The variation in physical, structural and electrical properties has been studied as a function of Bi₂O₃ content in 20ZnF₂-(10 + x) Bi₂O₃-(70-x) P₂O₅, 0 ≤ x ≤ 10 mol% glasses, which were prepared by melt quenching technique and characterized by differential thermal analysis (DTA). Colorless samples, which have no absorption peaks, are obtained for 10 and 12 mol% of Bi₂O₃ and the glasses are slowly becoming brownish from 15 to 20 mol% of Bi₂O₃ which exhibit two absorption peaks at ~ 370 nm, ~ 450 nm correspond to Bi° transitions ⁴S_3/2 → ²P_3/2 and ⁴S_3/2 → ²P_1/2 respectively. The decrease in ³P₁ → ¹S₀ transition of Bi³⁺ photo luminescence emission for 18 and 20 mol% of Bi₂O₃ and increase in optical absorption area shows the reduction of Bi³⁺ to Bi°. From FTIR studies it is observed that an addition of Bi₂O₃ decreases the P―O―P covalent bond by forming P―O―Bi bonds due to high polarizing nature of Bi³⁺ ions. Dielectric parameters like ε', tan δ and a.c. conductivity σ_ac are found to increase and activation energy for a.c. conduction is found to decrease with the increase in the concentration of Bi₂O₃. Density of defect energy states is found to increase for higher concentration of Bi₂O₃ and is discussed according to quantum mechanical tunneling (QMT) model.     

Phase separation and crystallization in the system SiO2-Al2O3-P2O5-B2O3-Na2O glasses

The phase separation and crystallization behavior in the system (80 − X)SiO₂ · X(Al₂O₃ + P₂O₅) · 5B₂O₃ · 15Na₂O (mol%) glasses was investigated. Glasses with X = 20 and 30 phase separated into two phases, one of which is rich in Al₂O₃-P₂O₅-SiO₂ and forms a continuous phase. Glasses containing a larger amount of Al₂O₃-P₂O₅ (X = 40 and 50) readily crystallize and precipitates tridymite type AlPO₄ crystals. It is estimated that the phase separation occurs forming continuous Al₂O₃-P₂O₅-SiO₂ phase at first, and then tridymite type AlPO₄ crystals precipitate and grow in this phase. Highly transparent glass-ceramics comparable to glass can be successfully obtained by controlling heat treatment precisely. The crystal size and percent crystallinity of these transparent glass-ceramics are 20-30 nm and about 50%, respectively.     

Broadband infrared luminescence of Ni-doped silicate glass-ceramics containing lithium aluminate spinel nanocrystals

Transparent Ni²⁺-doped SiO₂-Al₂O₃-Ga₂O₃-Li₂O (LGAS) glass-ceramics embedding lithium aluminate spinel nanocrystals was prepared. After heat treatment, LiAl₅O₈ crystallite was precipitated in the glasses, and its size was about 3 nm. It was confirmed from the absorption spectra that the ligand environment of Ni²⁺ ions changed from the trigonal bi-pyramid fivefold sites in the as-made glass to the octahedral sites in the glass-ceramics. Upon excitation at 980 nm, broadband infrared luminescence centered at around 1250 nm with full width at half maximum (FWHM) more than 250 nm was observed originating from the ³T₂(³F) → ³A₂(³F) transition of Ni²⁺ in octahedral sites. The broadband near-infrared (NIR) emission from Ni²⁺-doped glass-ceramics can be as host materials for broadband optical amplifier.     

Photoluminescence properties of PVP/Eu(TTA)2(Phen3PO)2NO3 nanocomposites

Thin films (1-10 μm thickness) of nanocomposites (NC) based on organic coordinated compound (OCC) Eu(TTA)₂(Phen₃PO)₂NO₃ (where TTA is thenoyltrifluoroacetonate (C₈H₅F₃O₂S), Phen - 1,10-phenanthroline (C₁₂H₈N₂)) and polymer - polyvinylpyrrolidone ((C₆H₉NO)_n) (PVP)) were obtained by chemical methods. NC were characterized by measurements of optical transmission, and photoluminescence (PL) at different concentrations of Eu(TTA)₂(Phen₃PO)₂NO₃ in NC. Using the optical transmission spectra, the characteristic parameters of NC such as threshold of absorbance and the position of the absorption edge on the concentration of the OOC in NC, etc., were determined. The light displacement of threshold absorption to infrared region was observed with increasing of concentration of coordinated material in NC. It was established that the excitation spectrum at which the photoluminescence in NC take place cover the range of wavelength from 200 to 410 nm. The PL of nanocomposites was detected as specific for internal transitions 4f-4f of the Eu³⁺ ion ⁵D₀ → ⁷F_i (i = 0,1,2,3 and 4) centred at 537, 580, 615, 650 and 702 nm, respectively at T = 300 K. The dominant PL was observed at 615 nm and its halfwidth is less than 10 nm. The intensity of photoluminescence at 615 nm of NC is 2 times higher than the value of intensity of PL of Eu(TTA)₂(Phen₃PO)₂NO₃ powders at equal conditions of excitation.     

Potentiodynamic polarization studies on amorphous Zr46.75Ti8.25Cu7.5Ni10Be27.5, Zr65Cu17.5Ni10Al7.5, Zr67Ni33 and Ti60Ni40 in aqueous HNO3 solutions

Potentiodynamic polarization studies were carried out on virgin specimens of Zr-based bulk amorphous alloys Zr_46.75Ti_8.25Cu_7.5Ni₁₀Be_27.5 and Zr₆₅Cu_17.5Ni₁₀Al_7.5, and conventional-type binary amorphous alloys Zr₆₇Ni₃₃ and Ti₆₀Ni₄₀ in solutions of 0.2 M, 0.5 M and 1.0 M HNO₃ at room temperature. The values of the corrosion current density (I_corr) for the bulk amorphous alloy Zr_46.75Ti_8.25Cu_7.5Ni₁₀Be_27.5 were found to be comparable with those of Zr₆₅Cu_17.5Ni₁₀Al_7.5 in 0.2 M and 0.5 M HNO₃, but the value of I_corr for the former was almost three times more than that of the latter in 1.0 M HNO₃. In the case of conventional binary amorphous alloys, Ti₆₀Ni₄₀ showed lower value of I_corr as compared to Zr₆₇Ni₃₃ in 0.5 M and 1.0 M HNO₃ and a comparable value of I_corr in 0.2 M HNO₃. In general, the binary Ti₆₀Ni₄₀ displayed the best corrosion resistance among all the alloys in all the cases and the corrosion current density (I_corr) for all the alloys was found to increase with the increasing concentration of nitric acid. It is noticed that the bulk amorphous alloys do not possess superior corrosion resistance as compared to conventional binary amorphous alloys in aqueous HNO₃ solutions. The observed differences in their corrosion behavior are attributed to different alloy constituents and composition of the alloys investigated.     

Fabrication and properties of novel low-melting glasses in the ternary system ZnO-Sb2O3-P2O5

Glasses in the ternary system ZnO-Sb₂O₃-P₂O₅ were investigated as potential alternatives to lead based glasses for low temperature applications. The glass-forming region of ZnO-Sb₂O₃-P₂O₅ system has been determined. Structure and properties of the glasses with the composition (60 − x)ZnO-xSb₂O₃-40P₂O₅ were characterized by infrared spectra (IR), differential thermal analysis (DTA) and X-ray diffraction (XRD). The results of IR indicated the role of Sb³⁺ as participant in glass network structure, which was supported by the monotonic and remarkable increase of density (ρ) and molar volume (V_M) with increasing Sb₂O₃ content. Glass transition temperature (T_g) and thermal stability decreased, and coefficient of thermal expansion (α) increased with the substitution of Sb₂O₃ for ZnO in the range of 0-50 mol%. XRD pattern of the heat treated glass containing 30 mol% Sb₂O₃ indicated that the structure of antimony-phosphate becomes dominant. The improved water durability of these glasses is consistent with the replacement of easily hydrated phosphate chains by corrosion resistant P-O-Sb bonds. The glasses containing ?30 mol% Sb₂O₃ possess lower T_g (<400 °C) and better water durability, which could be alternatives to lead based glasses for practical applications with further composition improvement.     

Influence of outphase Cu50Ti50 amorphous alloy addition on microstructural evolution of mechanically alloyed Zr66.7Ni33.3 amorphous alloy

The influence of outphase Cu₅₀Ti₅₀ amorphous alloy addition on microstructural evolution of Zr_66.7Ni_33.3 amorphous alloy has been investigated using a mechanical alloying method. It has been found that the milling induced microstructural evolution is related to the change of peak positions of the first maximum on X-ray diffraction patterns of the as-obtained amorphous alloys. With increasing milling time, the 3 wt.% Cu₅₀Ti₅₀ addition can give rise to the cyclic amorphization transformation of the as-milled alloy. The mechanical stability of the mixing amorphous phase can be greatly enhanced with increasing Cu₅₀Ti₅₀ addition up to 10 wt.%. Moreover, the addition of outphase Cu₅₀Ti₅₀ amorphous alloy not only increases the onset crystallization temperature of Zr_66.7Ni_33.3 amorphous alloy but also alters its crystallization mode. The effect of outphase amorphous addition on the mechanical stability of the Zr_66.7Ni_33.3 amorphous phase has been discussed based upon the bond order theory.     

Composition dependent upconversion of Er-doped PbF2-TeO2 glasses

The upconversion properties of Er³⁺ ions were studied for heavy metal oxyfluoride tellurite glass hosts xPbF₂-(100−x)TeO₂ under 975 nm excitation. The intense green (529 and 545 nm) and relative weak red (657 nm) emissions corresponding to the transitions ⁴S_3/2 → ⁴I_15/2, ²H_11/2 → ⁴I_15/2 and ⁴F_9/2 → ⁴I_15/2, respectively, were simultaneously observed at room temperature. The PbF₂ content has an important influence on upconversion luminescence emission. With increasing PbF₂ content, the intensities of green (529 nm) and red (657 nm) emissions increase slightly, while the green (545 nm) emission increases significantly. These results indicate that PbF₂ has more influence on the green (545 nm) emission than the green (529 nm) and red (657 nm) emissions. The intense green emission observed suggest that Er³⁺-doped heavy metal oxyfluoride tellurite glasses can become candidates for developing upconversion optical devices.     

Occurrence of Kondo-like behavior in electrical-conductivity of Al70Pd20+xMn10−x (x = 0, 1 and 2) icosahedral quasicrystals

Zero-field and in-field (at 8 T) conductivity vs temperature (σ-T), magneto-resistance (Δρ/ρ), magnetization vs temperature (M-T) and magnetization vs field (M-H) of unannealed Al₇₀Pd₂₀Mn₁₀ and annealed Al₇₀Pd₂₀Mn₁₀, Al₇₀Pd₂₁Mn₉ and Al₇₀Pd₂₂Mn₈ quasicrystalline alloys have been studied in the temperature range of 1.4-300 K. Room temperature resistivity and the low-temperature magneto-resistance show a correlation with the corresponding magnetization. The σ-T for all the studied samples shows a pair of minima and maxima. The σ-T maxima show a correlation with the total magnetization. The analysis shows that σ-T is dominated by weak-localization effects. The minima are arising due to competing inelastic scattering times τ_i (e-ph scattering in the dirty metallic limit, τ_i ∝ T⁻²) and the Kondo-type spin-flip scattering time τ_sf whereas the maxima has been attributed to ‘Kondo-maxima’, occurring due to maxima in the spin-flip rate . The magneto-resistance of these samples shows a changeover from negative to positive where the negative component shows a correlation with the magnetization of the sample. The values of parameters derived from refinement give spin-flip scattering fields, which are found to be correlated with the total sample magnetization.     

Structure and electrical conductivity of new Li2O-CeO2-B2O3 glasses

Fourier transformation infrared spectra, density and DC electrical conductivity of 30Li₂O · xCeO₂⋅(70 − x)B₂O₃ glasses, where x ranged between 0 and 15 mol%, have been investigated. The results suggested that CeO₂ plays the role of network modifier up to 7.5 mol%. At higher concentrations it plays a dual role; where most of ceria plays the role of network former. The density was observed to increase with increasing CeO₂ content. The effect on density of the oxides in the glasses investigated is in the succession: B₂O₃ < Li₂O < CeO₂. Most of CeO₂ content was found to be associated with B₂O₃ network to convert BO₃ into B O₄⁻ units. The contribution of Li⁺ ions in the conduction process is much more than that due to small polarons. The conductivity of the glasses is mostly controlled by the Li⁺ ions concentration rather than the activation energy for CeO₂ > 5 mol%. Lower than 5 mol% CeO₂ the conductivity is controlled by both factors. The dependence of W on BO₄⁻ content supports the idea of ionic conduction in these glasses.