Study of Sm-doped ZnO samples sintered in a nitrogen atmosphere and deposited on n-Si(1 0 0) by evaporation technique

The samarium doping zinc oxide (Zn_1-xSm_xO) with (x=0.0, 0.04, 0.05 and 0.17) polycrystalline thin films have been deposited on n-Si(1 0 0) substrate using thermal evaporation technique. Ceramic targets for deposition were prepared by the standard solid-state reaction method and sintered in nitrogen atmospheres. X-ray diffraction and scanning electron microscopy analyses show that the bulk and films features reveal wurtzite crystal structure with a preferential (1 0 1) crystallographic orientation and grows as hexagonal shape grains. According to the results of the Hall effect measurements, all the films show p-type conductivity, possibly a result of nitrogen incorporation into the Sm-doped ZnO samples. Magnetic measurements show that ferromagnetic behavior depends on the Sm³⁺ concentration. For a film with lower Sm₂O₃ contents (x=0.04), a phenomenon of paramagnetism has been observed. While, with further increase of Sm³⁺ contents (x=0.05) the ferromagnetic behavior has been observed at room temperature. However, at higher doping content of Sm³⁺, the ferromagnetic behavior was suppressed. The decrease of ferromagnetism with increasing doping concentration demonstrates that ferromagnetism observed at room temperature is an intrinsic property of Zn_1-xSm_xO films.     

The role of adsorption of sodium bis(2-ethylhexyl) sulfosuccinate in wetting of glass and poly(methyl methacrylate) surface

Advancing contact angles, θ, for aqueous solutions of the anionic surfactant, sodium bis(2-ethylhexyl) sulfosuccinate (AOT) were measured on glass and poly(methyl methacrylate) (PMMA) surface. Using the obtained results we determined the properties of aqueous AOT solutions in wetting of these surfaces. It occurs that the wettability of glass and PMMA by these solutions depends on the concentration of AOT in solution. There is almost linear dependence between the contact angle (θ) and concentration of AOT (log C) in the range from 5 × 10⁻⁴ to 2.5 × 10⁻³ M/dm³ (value of the critical micelle concentration of AOT—CMC) both for glass and PMMA surface. For calculations of AOT adsorption at solid (glass, PMMA)-solution drop-air system interfaces the relationship between the adhesion tension (γ_LV cos θ) and surface tension (γ_LV) and the Gibbs and Young equations were taken into account. From the measurement and calculation results the slope of the γ_LV cos θ − γ_LV curve was found to be constant and equal 0.7 for glass and −0.1 for PMMA over the whole range of AOT concentration in solution. From this fact it can be concluded that if Γ_SV is equal zero then Γ_SL > 0 for the PMMA-solution and Γ_SL < 0 for glass-solution systems. It means that surfactant concentration excess at PMMA-solution interface is considerably lower than at solution-air interface, but this excess of AOT concentration at glass-solution interface is lower than in the bulk phase. By extrapolating the linear dependence between the adhesion and surface tension the value of the critical surface tension (γ_c) of wetting for glass and PMMA was also determined, that equaled 25.9 and 25.6 mN/m for glass and PMMA, respectively. Using the value of the glass and PMMA surface tension as well as the measured surface tension of aqueous AOT solutions in Young equation, the solid-liquid interface tension (γ_SL) was found. There was a linear dependence between the γ_SL and γ_LV both for glass and PMMA, but there were different slope values of the curves for glass and PMMA, i.e. −0.7 and 0.1, respectively. The dependence between the work of adhesion (W_A) and surface tension (γ_LV) was also linear of different slopes for glass and for PMMA surface.     

Spectroscopic ellipsometry study of above-band gap optical constants of layered structured TlGaSe2, TlGaS2 and TlInS2 single crystals

Spectroscopic ellipsometry measurements on TlGaSe₂, TlGaS₂ and TlInS₂ layered crystals were carried out on the layer-plane (0 0 1) surfaces, which are perpendicular to the optic axis c^?, in the 1.2–6.2 eV spectral range at room temperature. The real and imaginary parts of the pseudodielectric function as well as pseudorefractive index and pseudoextinction coefficient were found as a result of analysis of ellipsometric data. The structures of critical points in the above-band gap energy range have been characterized from the second derivative spectra of the pseudodielectric function. The analysis revealed four, five and three interband transition structures with critical point energies 2.75, 3.13, 3.72 and 4.45 eV (TlGaSe₂), 3.03, 3.24, 3.53, 4.20 and 4.83 eV (TlGaS₂), and 3.50, 3.85 and 4.50 eV (TlInS₂). For TlGaSe₂ crystals, the determined critical point energies were assigned tentatively to interband transitions using the available electronic energy band structure.     

Growth temperature dependence of the hysteretic behavior of Ni0.5Zn0.5Fe2O4 thin films

Herein, a discussion of the effect of deposition temperature on the magnetic behavior of Ni_0.5Zn_0.5Fe₂O₄ thin films. The thin films were grown by r.f. sputtering technique on (1 0 0) MgO single-crystal substrates at deposition temperatures ranging between 400 and 800 °C. The grain boundary microstructure was analyzed via atomic force microscopy (AFM). AFM images show that grain size (φ∼70-112 nm) increases with increasing deposition temperature, according to a diffusion growth model. From magneto-optical Kerr effect (MOKE) measurements at room temperature, coercive fields, H_c, between 37and 131 Oe were measured. The coercive field, H_c, as a function of grain size, reaches a maximum value of 131 Oe for φ ∼93 nm, while the relative saturation magnetization exhibits a minimum value at this grain size. The behaviors observed were interpreted as the existence of a critical size for the transition from single- to multi-domain regime. The saturation magnetization (21 emu/g<M_s<60 emu/g) was employed to quantify the critical magnetic intergranular correlation length (L_c≈166 nm), where a single-grain to coupled-grain behavior transition occurs. Experimental hysteresis loops were fitted by the Jiles-Atherton model (JAM). The value of the k-parameter of the JAM fitted by means of this model (k/μ_o∼50 A m²) was correlated to the domain size from the behavior of k, we observed a maximum in the density of defects for the sample with φ∼93 nm.     

High-temperature electrical properties of magnesiowustite Mg1 − xFexO and spinel Fe3 − x − yMgxCryO4 ceramics

Phase relationships, thermal expansion and electrical properties of Mg_1 − xFe_xO (x = 0.1-0.45) cubic solid solutions and Fe_{3 − x − y}Mg_xCr_yO_4 ± δ (x = 0.7-0.95; y = 0 or 0.5) spinels were studied at 300-1770 K in the oxygen partial pressure range from 10 Pa to 21 kPa. Increasing iron content enlarges the spinel phase stability domain at reduced oxygen pressures and elevated temperatures. The total conductivity of the spinel ceramics is predominantly n-type electronic and is essentially p(O₂)-independent within the stability domain. The computer simulations using molecular dynamics technique confirmed that overall level of ion diffusion remains low even at high temperatures close to the melting point. Temperature dependencies of the total conductivity in air exhibit a complex behavior associated with changing the dominant defect-chemistry mechanism from prevailing formation of the interstitial cations above 1370-1470 K to the generation of cation vacancies at lower temperatures, and with kinetically frozen cation redistribution in spinel lattice below 700-800 K. The average thermal expansion coefficients of the spinel ceramics calculated from dilatometric data in air vary in the range (9.6-10.0) × 10^− 6 K^− 1 at 300-500 K and (13.2-16.1) × 10^− 6 K^− 1 at 1050-1370 K. Mg_1 − xFe_xO solid solutions undergo partial decomposition on heating under oxidizing and mildly reducing conditions, resulting in the segregation of spinel phase and conductivity decrease.     

Effect of glycyl dipeptides on the micellar behavior of gemini surfactant: A conductometric and fluorescence spectroscopic study

The effect of glycyl dipeptides (glycylglycine, glycyl-L-valine, and glycyl-L-leucine) on the micellar properties of gemini surfactant pentamethylene-1,5-bis(dodecyldimethylammonium bromide) (12-5-12) has been investigated by means of conductivity and fluorescence spectroscopy. The results obtained from conductivity show that the effect of glycyl dipeptides depends upon their nature and concentration, as well as the temperature. The values of critical micelle concentration (cmc) of 12-5-12 have been estimated in water + glycyl dipeptide media at various concentrations of dipeptide in the 293.15-318.15 K temperature range at 5 K intervals. From cmc values, it is observed that the micellization tendency of the surfactant increases in the presence of glycyl dipeptides. Thermodynamic parameters (ΔG_m^o, ΔH_m^o, and ΔS_m^o) of micellization of 12-5-12 in aqueous glycyl dipeptide solutions have been obtained by applying the mass action model and an enthalpy-entropy compensation effect was observed. The pyrene fluorescence spectra were used to study the change of micropolarity produced by the interaction of 12-5-12 with glycyl dipeptides, and the aggregation behavior of 12-5-12.     

The wettability of poly(tetrafluoroethylene) by aqueous solutions of ternary surfactant mixtures

Contact angle measurements on poly(tetrafluoroethylene) (PTFE) surface were carried out for the systems containing ternary mixtures of cetyltrimethylammonium bromide (CTAB) and p-(1,1,3,3-tetramethylbutyl)phenoxypoly(ethylene glycols), Triton X-100 (TX100) and Triton X-165 (TX165). The aqueous solution of ternary surfactant mixtures were prepared by adding the third surfactant to the binary mixture of the surfactants where the synergetic effect in the reduction of the surface tension of water was determined, to compare the influence of the third surfactants on the values of surface tension of this binary mixture and the values of the contact angle on PTFE. The obtained results and calculations indicate that the ternary mixtures of CTAB + TX165 (αCTAB = 0.2, γ_LV = 60 and 50 mN/m) + TX100 (C = 10⁻⁸ to 10⁻² M) have the biggest efficiency of the reduction of contact angle of water on PTFE in comparison to aqueous solutions of the single surfactants and their binary and ternary mixtures. Also in the case of all studied ternary mixtures of surfactants at concentrations of the bulk phase corresponding to unsaturated monolayer at water-air interface the adsorption of surfactants at PTFE-water interface is different than that at water-air interface, but is the same at concentrations near the critical micelle concentration (CMC). Thus the linear dependences between γ_LV cos θ − γ_LV and cos θ − 1/γ_LV, in the range of concentration studied for all systems confirm the same adsorption at two interfaces only at C near the CMC.     

The wettability of polytetrafluoroethylene and polymethylmethacrylate by aqueous solutions of Triton X-100 and propanol mixtures

Measurements of advancing contact angles (θ) were carried out for aqueous solutions of Triton X-100 (TX-100) and propanol mixtures at constant TX-100 concentration equal to 1 × 10⁻⁷, 1 × 10⁻⁶, 1 × 10⁻⁵, 1 × 10⁻⁴, 6 × 10⁻⁴ and 1 × 10⁻³ M, respectively, on polytetrafluoroethylene (PTFE) and polymethyhmethacrylate (PMMA). Using obtained results the changes of cosθ and adhesional tension against surface tension of all series of aqueous solutions of TX-100 and propanol mixtures (γ_LV) for PTFE and PMMA surfaces were shown. On the basis of these changes it was deduced that adsorption of TX-100 and propanol mixtures at PTFE-solution and solution-air interfaces is the same but the adsorption of TX-100 and propanol mixtures at solution-air interface is considerably higher than at PMMA-solution one. In the case of PTFE this conclusion was confirmed by relationship between cosθ and the reciprocal of the surface tension of solution. Extrapolation of the relationships between cosθ and/or adhesional tension and the surface tension of solutions to the points corresponding to the cosθ = 1 and adhsional tension equal to the surface tension of solution, the critical surface tension of PTFE and PMMA wetting was determined. The average values of critical surface tension of wetting determined from these relationships for PTFE are lying in the range of its surface tension values determined from contact angles of different kinds of liquids, which can be find in the literature, but for PMMA are considerably lower than the surface tension. The double value of the critical surface tension of PTFE wetting is equal to adhesion work of the solution to its surface and for PMMA there is not any correlation between these magnitudes.Using the measured values of the contact angles and Young equation the PTFE(PMMA)-aqueous solution interfacial tension was determined. The interfacial tension values of PTFE-aqueous solution were also calculated from the Fainerman and Miller equation in which the correcting parameter of nonideality of the surface monolayer was introduced and compared to those obtained from Young equation. From this comparison it results that the changes of PTFE-solution interface tension as a function of propanol concentration can be described by the Fainerman and Miller equation.     

Probing the magnetic state by linear and non-linear ac magnetic susceptibility measurements in under-doped manganite Nd0.8Sr0.2MnO3

We have thoroughly investigated the entire magnetic states of under-doped ferromagnetic-insulating manganite Nd_0.8Sr_0.2MnO₃ through temperature-dependent linear and non-linear complex ac magnetic susceptibility measurements. This ferromagnetic-insulating manganite is found to have frequency-independent ferromagnetic to paramagnetic transition temperature at around 140 K. At around 90 K (≈T_?) the sample shows a second frequency-dependent re-entrant magnetic transition as explored through complex ac susceptibility measurements. Non-linear ac susceptibility measurements (higher harmonics of ac susceptibility) have also been performed (with and without the superposition of a dc magnetic field) to further investigate the origin of this frequency dependence (dynamic behavior at this re-entrant magnetic transition). Divergence of 3rd harmonic of ac susceptibility in the limit of zero exciting field indicates a spin-glass-like freezing phenomena. However, large value of spin-relaxation time (τ₀=10⁻⁸ s) and small value of coercivity (∼22 Oe) obtained at low temperature (below T_?) from critical slowing down model and dc magnetic measurements, respectively, are in contrast with what generally observed in a canonical spin glass (τ₀=10⁻¹²-10⁻¹⁴ s and very large value of coercivity below freezing temperature). We have attributed our observation to the formation of finite size ferromagnetic clusters which are formed as consequence of intrinsic phase separation and undergo cluster glass-like freezing below certain temperature in this under-doped manganite. The results are supported by the electronic- and magneto-transport data.     

Structure, thermal and transport properties of PVAc-LiClO4 solid polymer electrolytes

The lithium ion conducting solid polymer electrolytes (SPE) based on PVAc-LiClO₄ of various compositions were prepared by solution casting technique. Structure and surface morphology characterization were studied by X-ray diffraction (XRD) analysis and scanning electron microscopy (SEM) measurements, respectively. Thermal and conductivity behavior of polymer-salt complexes were studied by employing differential scanning calorimetry (DSC) and ac impedance measurements, respectively. XRD and SEM analyses indicate the amorphous nature of the polymer-salt complexes. DSC measurements show decrease in T_g with the increase in LiClO₄ concentrations. The bulk conductivity of the PVAc:LiClO₄ polymer electrolytes was found to vary between 7.6×10⁻⁷ and 6.2×10⁻⁵ S cm⁻¹ at 303 K with the increase in salt concentration. The temperature dependence of the polymer electrolyte complexes appear to obey Arrhenius law.     

The wettability of polytetrafluoroethylene and polymethylmethacrylate by aqueous solutions of Triton X-100 and short chain alcohol mixtures

Measurements of advancing contact angles (θ) were carried out for aqueous solutions of Triton X-100 (TX-100) and methanol and ethanol mixtures at constant TX-100 concentration equal to 1 × 10⁻⁷, 1 × 10⁻⁶, 1 × 10⁻⁵, 1 × 10⁻⁴, 6 × 10⁻⁴ and 1 × 10⁻³ M, respectively, on polytetrafluoroethylene (PTFE) and polymethylmethacrylate (PMMA). Using measured contact angle values the relationships between cos θ, adhesion tension and surface tension of the solutions were determined, and on their basis the critical surface tension of PTFE and PMMA wetting was calculated. The obtained average value of the critical surface tension of PTFE wetting is lying in the range of the PTFE surface tension values which can be found in the literature, while for PMMA it is even lower than the Lifshitz-van der Waals component of its surface tension. From the relationship between the adhesion and surface tension and Lucassen-Reynders equation it results that in the case of PTFE the adsorption at the PTFE-solution and solution-air interfaces is the same, which was confirmed by a linear relationship between the cos θ and 1/γ_LV and intercept on cos θ axis equal to −1. However, for PMMA the adsorption of the surface active agents at solution-air interface is higher than at PMMA-solution. Using the values of the contact angle the values of the adhesion work of solution to the PTFE and PMMA surface were also determined, which are constant for PTFE, but for PMMA decrease with alcohol concentration increase. Next, using the contact angle values in the Young equation, the PTFE(PMMA)-solution interface tension was also calculated. The obtained values of PTFE-solution interface tension were compared with those evaluated from the Szyszkowski, Connors and Fainerman and Miller equations, and good agreement between these values was observed for all series of TX-100 and alcohol mixtures at a low alcohol concentration.     

The influence of chromium on the defect structure and their mobility in nonstoichiometric cobaltous oxide

Defect structure and the mobility of point defects in pure metal deficient cobalt oxide (Co_1−yO) and in Co_1−yO-Cr₂O₃ solid solutions have been studied as a function of temperature (1223-1573 K) and oxygen pressure (10-10⁵ Pa) using microthermogravimetric techniques. It has been shown that the predominant defects in pure and Cr-doped cobaltous oxide are singly ionized cation vacancies, and 3% at of dopant is high enough to fix the concentration of predominant defects in such solid solutions on a constant level being much higher than in pure Co_1−yO. Re-equilibration rate measurements have demonstrated that the chemical diffusion coefficient and thereby the mobility of point defects in pure Co_1−yO is concentration independent, strongly suggesting that in spite of rather high their concentration no interactions and clustering of defects is to be expected. On the other hand, in Cr-doped cobaltous oxide, re-equilibration rate measurements have shown, that in this case the defect structure is more complicated, although singly ionized cation vacancies seem to be still predominant defects.     

Investigation of energy band gap and optical properties of cubic CdS epilayers

High quality cubic CdS epilayers were grown on GaAs (1 0 0) substrates by the hot-wall epitaxy method. The crystal structure of the grown epilayers was confirmed to be the cubic structure by X-ray diffraction patterns. The optical properties of the epilayers were investigated in a wide photon energy range between 2.0 and 8.5 eV using spectroscopic ellipsometry (SE) and were studied in the transmittance spectra at a wavelength range of 400-700 nm at room temperature. The data obtained by SE were analyzed to find the critical points of the pseudodielectric function spectra, 〈?(E)〉 = 〈?₁(E)〉 + i〈?₂(E)〉, such as E₀, E₁, E₂, E^′₀, and E^′₁ structures. In addition, the optical properties related to the pseudodielectric function of CdS, such as the absorption coefficient α(E), were investigated. All the critical point structures were observed, for the first time, at 300 K by ellipsometric measurements for the cubic CdS epilayers. Also, the energy band gap was determined by the transmittance spectra of the free-standing film, and the results were compared with the E₀ structure obtained by SE measurement.     

Synthesis and characterization of a nano-scaled barium cerate perovskite powder using starch as polymerization agent

The preparation of nano-sized BaCeO₃ powder using starch as a polymerization agent is described herein. Phase evolution during the decomposition process of a (BaCe)-gel was monitored by XRD. A phase-pure nano-sized BaCeO₃ powder was obtained after calcining of the (BaCe)-gel at 920 °C. The resulting powder has a specific surface area of 15.4 m²/g. TEM investigations reveal particles mainly in the size range of 30 to 65 nm. The shrinkage and sintering behavior of resulting powder compacts were studied in comparison to a coarse-grained mixed-oxide BaCeO₃ powder (S_BET = 2.1 m²/g). Dilatometric measurements show that the beginning of shrinkage of compacts from the nano-sized powder is downshifted by 300 °C compared to mixed-oxide powder. Compacts from the nano-sized powder reach a relative density of 91% after sintering at 1450 °C for 10 h.     

Thermal equation-of-state of osmium: a synchrotron X-ray diffraction study

The pressure-volume-temperature behavior of osmium was studied at pressures and temperatures up to 15 GPa and 1273 K. In situ measurements were conducted using energy-dispersive synchrotron X-ray diffraction in a T-cup 6-8 high pressure apparatus. A fit of room-temperature data by the third-order Birch-Murnaghan equation-of-state yielded isothermal bulk modulus K₀=435(19) GPa and its pressure derivative K′₀=3.5(0.8) GPa. High-temperature data were analyzed using Birch-Murnaghan equation of state and thermal pressure approach. The temperature derivative of bulk modulus was found to be −0.061(9) GPa K⁻¹. Significant anisotropy of osmium compressibility was observed.     

Phase behavior of unsymmetrical dimers on a square lattice

Monte Carlo simulations in the grand canonical ensemble have been carried out to study phase transitions in monolayers formed by heterogeneous dimers, composed of segments A and B, on a square lattice. The unsymmetrical segment-segment interactions are assumed (u_AA ≠ u_BB). The systems with u_AB = u_BB = −1 and different AA-interactions studied in our previous work [W. R?ysko, M. Borówko, Surf. Sci. 520 (2002) 151] are reconsidered. The structural phase transitions at high temperatures are investigated. It is shown that topology of a phase diagram depends on the energy u_AA. For repulsive AA-interactions a triple point is found and the system belongs to the universality class of a tricritical point. When u_AA < 0 the critical line of the order-disorder transition terminates at a critical end point and the system belongs to the universality class of the 2D Ising model.     

Conversion behavior comparison of TFA–MOD and non-fluorine solution-deposited YBCO films

The densification behavior during conversion of YBa₂Cu₃O_7−x (YBCO) films formed by the trifluoroacetate (TFA)-based metal–organic deposition (MOD) technique was compared to a non-fluorine oxycarbonate-based MOD process and nitrate-based polymer-assisted deposition (PAD). The critical current densities obtained in all processes exceeded 10⁶ A/cm² in films at least 300 nm thick. Rapid densification of films was observed in all processes, beginning at 700 °C in the TFA and PAD processes and 650 °C in the oxycarbonate process. YBCO nucleation occurred shortly after densification began in all processes. Residual carbon measurements were performed using wavelength dispersive spectroscopy (WDS). Carbon persisted in films from all processes until after densification began, but it was reduced to background levels soon after YBCO nucleation. Film density and second phase morphology were controlled through adjustments to the ambient oxygen partial pressure. Morphological evidence of extensive transient liquid phase formation was observed in PAD films and is consistent with the densification and nucleation behavior. The common behavior between the PAD, oxycarbonate–MOD, and TFA–MOD processes suggests that a melt forms in all systems, but the extent of this melt varies.     

Magnetic properties of ErxY1−xF3 solid solutions

The Er_xY_1−xF₃ (x=0.1, 0.2, 0.7, 0.9, 1) solid solutions were synthesized and characterized by X-ray powder diffraction and magnetic measurements. The crystal structure refinements done by the Rietveld profile method show that no significant change of the structure parameters with the erbium concentration occurs. On the basis of DC susceptibility measurements in the 2-300 K range the lowest four crystal field levels have been determined, giving the ground level magnetic moment value of 6.7 μ_B. Results of M(H) studies point to the presence of complex exchange interactions between erbium ions.     

The role of adsorption of dodecylethyldimethylammonium bromide and benzyldimethyldodecylammonium bromide surfactants in wetting of polytetrafluoroethylene and poly(methyl methacrylate) surfaces

The role of adsorption of dodecylethyldimethylammonium bromide (C₁₂(EDMAB)) and benzyldimethyldodecylammonium bromide (BDDAB) at water-air and polytetrafluoroethylene (PTFE)-water and poly(methyl methacrylate) (PMMA)-water interface, in wetting of PTFE and PMMA surface, was established from the measured values of the contact angle (θ) of aqueous C₁₂(EDMAB) and BDDAB solutions in PTFE (PMMA)-solution drop-air system, and from the measured values of the surface tension of aqueous C₁₂(EDMAB) and BDDAB solutions. Adsorption of C₁₂(EDMAB) and BDDAB at water-air interface was determined earlier from the Gibbs equation. Adsorption at solid-water interface was deduced from the Lucassen-Reynders equation based on the relationship between adhesion tension (γ_LV cos θ) and surface tension (γ_LV). The slope of the γ_LV cos θ-γ_LV curve was found to be constant and equal to −1, and about −0.3 for PTFE and PMMA surface, respectively (in the case of both surfactant studied: C₁₂(EDMAB) and BDDAB, and in the whole range of surfactants concentration in solution). It means that the amount of the surfactant adsorbed at the PTFE-water interface, Γ_SL, was essentially equal to its amount adsorbed at water-air interface, Γ_LV. However, Γ_SL at the PMMA-water interface was about three times smaller as compared to that at water-air interface. By extrapolating the linear dependence between γ_LV cos θ-γ_LV and dependence between cos θ-γ_LV and cos θ = 1 we determined the value of the critical surface tension of PTFE and PMMA surface wetting, γ_c. The obtained values of γ_c for PTFE surface were equal 23.4 and 23.8 mN/m, 23.1 and 23.2 mN/m for C₁₂(EDMAB) and BDDAB, respectively and they were higher than the surface tension of PTFE (20.24 mN/m). On the other hand, the obtained values of γ_c for PMMA surface were equal 31.4 and 30.9 mN/m, 31.7 and 31.3 mN/m for C₁₂(EDMAB) and BDDAB, respectively and they were smaller than the surface tension of PMMA (39.21 mN/m). Using the values of PTFE and PMMA surface tension and the measured values of the surface tension of aqueous C₁₂(EDMAB) and BDDAB solutions in the Young equation, the PTFE (PMMA)-solution interfacial tension, γ_SL, was also determined. Next, the work of adhesion (W_A) was deduced, and it occurred that the dependence between the W_A and the surface tension (γ_LV) for both studied solids was linear. However, the values of the W_A for PMMA change as a function of log C (C—surfactant concentration) changed from 91.7 to 68.5 mJ/m² and from 91.8 to 65.1 mJ/m² for C₁₂(EDMAB) and BDDAB, respectively. On the other hand, the work of adhesion of both studied surfactants solutions to the PTFE surface was practically constant (an average value was equal 45.8 and 45.4 mJ/m², respectively). These values were close to the value of the work of water adhesion to PTFE surface (45.5 mJ/m²).     

Adsorption of sodium bis(2-ethylhexyl) sulfosuccinate and wettability in polytetrafluoroethylene-solution-air system

The role of sodium bis(2-ethylhexyl) sulfosuccinate (AOT) adsorption at water-air and polytetrafluoroethylene-water (PTFE) interfaces in wetting of low energy PTFE was established from measurements of the contact angle of aqueous AOT solutions in PTFE-solution drop-air systems and the aqueous AOT solution surface tension measurements. For calculations of the adsorption at these interfaces the relationship between adhesion tension (γ_LV cos θ) and surface tension (γ_LV), and the Gibbs and Young equations were taken into account. On the basis of the measurements and calculations the slope of the γ_LV cos θ-γ_LV curve was found to be constant and equal −1 over the whole range of surfactant concentration in solution. It means that the amount of surfactant adsorbed at the PTFE-water interface, Γ_SL, is essentially equal to its amount adsorbed at water-air interface, Γ_LV. By extrapolating the linear dependence between γ_LV cos θ and γ_LV to cos θ = 1 the determined value of critical surface tension of PTFE surface wetting, γ_C, was obtained (23.6 mN/m), and it was higher than the surface tension of PTFE (20.24 mN/m). Using the value of PTFE surface tension and the measured surface tension of aqueous AOT solution in Young equation, the PTFE-solution interface tension, γ_SL, was also determined. The shape of the γ_SL-log C curve occurred to be similar to the isotherm of AOT adsorption at water-air interface, and a linear dependence existed between the PTFE-solution interfacial tension and polar component of aqueous AOT solution. The dependence was found to be established by the fact that the work of adhesion of AOT solution to the PTFE surface was practically constant amounting 46.31 mJ/m² which was close to the work of water adhesion to PTFE surface.