Li_(1.3)Ti_(1.7)Al_(0.3)(PO_4)_3,Na_(1.3)Ti_(1.7)Al_(0.3)(PO_4)_3的离子交换研究

研究了在不同温度下的NaNO3和AgNO3水溶液中Li1.3Ti1.7Al0.3(PO4)3和Na1.3Ti1.7Al0.3(PO4)3离子交换行为.实验表明Li1.3Ti1.7Al0.3(PO4)3和Na1.3Ti1.7Al0.3(PO4)3均显示出了高选择性与Na+和Ag+进行离子交换的特征,且对Ag+的选择性高于Na+.升高温度可显著提高Ag/Li和Ag/Na的交换反应速度.     

Crystal growth, structure determination, and optical properties of new potassium-rare-earth silicates K3RESi2O7 (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu)

Single crystals of K₃RESi₂O₇ (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu) were grown from a potassium fluoride flux. Two different structure types were found for this series. Silicates containing the larger rare earths, RE=Gd, Tb, Dy, Ho, Er, Tm, Yb crystallize in a structure K₃RESi₂O₇ that contains the rare-earth cation in both a slightly distorted octahedral and an ideal trigonal prismatic coordination environment, while in K₃LuSi₂O₇, containing the smallest of the rare earths, lutetium is found solely in an octahedral coordination environment. The structure of K₃LuSi₂O₇ crystallizes in space group P6₃/mmc with a=5.71160(10) Å and c=13.8883(6) Å. The structures containing the remaining rare earths crystallize in the space group P6₃/mcm with the lattice parameters of a=9.9359(2) Å, c=14.4295(4) Å, (K₃GdSi₂O₇); a=9.88730(10) Å, c=14.3856(3) Å, (K₃TbSi₂O₇); a=9.8673(2) Å, c=14.3572(4) Å, (K₃DySi₂O₇); a=9.8408(3) Å, c=14.3206(6) Å, (K₃HoSi₂O₇); a=9.82120(10) Å, c=14.2986(2) Å, (K₃ErSi₂O₇); a=9.80200(10) Å, c=14.2863(4) Å, (K₃TmSi₂O₇); a=9.78190(10) Å, c=14.2401(3) Å, (K₃YbSi₂O₇). The optical properties of the silicates were investigated and K₃TbSi₂O₇ was found to fluoresce in the visible.     

电感耦合等离子体光谱法(ICP-AES)测定银精矿中铜、铅、锌、砷、镉、钙、镁、锰含量

针对银精矿样品复杂,难消解的特点,研究了不同酸溶法和碱熔法对样品的消解情况,建立了硝酸,盐酸,氢氟酸,高氯酸消解银精矿的方法。根据元素灵敏度和抗干扰性,选定各元素的测定波长。通过酸溶样和碱熔样测定结果比对,验证了方法准确性。建立了四酸消解-电感耦合等离子体光谱法测定银精矿中铜、铅、锌、砷、镉、钙、镁、锰含量的方法,元素的线性相关系数均在0.9999以上。通过共存元素干扰实验,确定了银精矿中高含量元素(铜、铅、锌、铁、锑、铋等)对测定元素结果没有影响。方法检出限：Cu 0.0063 mg/L, Pb 0.0159 mg/L ,Zn 0.0090 mg/L,As 0.0192 mg/L, Cd 0.0093 mg/L ,Ca 0.0084 mg/L, Mg 0.0075 mg/L, Mn 0.0081 mg/L。测定下限：Cu 0.0105mg/L,Pb 0.0265 mg/L, Zn 0.0150 mg/L, As 0.0320 mg/L, Cd 0.0155 mg/L, Ca 0.0140 mg/L, Mg 0.0125 mg/L,Mn 0.0135 mg/L。3个样品的相对标准偏差在0.87%~3.56%之间,加标回收率在95.00%~103.56%之间。方法流程短,操作简单,快速,灵敏度和再现性高,结果准确可靠,可以满足银精矿中铜、铅、锌、砷、镉、钙、镁、锰含量的测定。     

Near infrared study of aqueous rare-earth ethylsulfates

The near infrared spectra of aqueous solutions of the ethylsulfates of La, Nd, Gd, Tb, Er, Yb, Lu, Y, and Na have been determined from about 0.2 mol-dm^–3 to nearly saturation. The extinction coefficients of water have been calculated taking into account the absorption of ethylslfate anions determined in separate experiments. Their values appeared to be nearly the same as that of pure water. The relative contents of free OH groups in 0.5 and 0.7M solutions have been estimated from the absorbances at 1160 nm. They were lower in solutions of the heavy rare-earth ethylsulfates (Tb, Er, Yb, Lu) than in equimolar solutions of the lighter ones (La, Nd), confirming our previous view that secondary hydration of the heavy trivalent rare-earth cations is distinctly stronger than that of the lighter ones. A comparison of the spectra of these aqueous ethylsulfates with those of perchlorates shows that the structure-breaking ability of the C₂H₅SO ₄ ^– ion is much smaller than that of perchlorate anion.     

Structural studies of five layer Aurivillius oxides: A2Bi4Ti5O18 (A=Ca, Sr, Ba and Pb)

The room temperature structures of the five layer Aurivillius phases A₂Bi₄Ti₅O₁₈ (A=Ca, Sr, Ba and Pb) have been refined from powder neutron diffraction data using the Rietveld method. The structures consist of [Bi₂O₂]²⁺ layers interleaved with perovskite-like [A₂Bi₂Ti₅O₁₆]²⁻ blocks. The structures were refined in the orthorhombic space group B2eb (SG. No. 41), Z=4, and the unit cell parameters of the oxides are a=5.4251(2), b=5.4034(1), c=48.486(1); a=5.4650(2), b=5.4625(3), c=48.852(1); a=5.4988(3), b=5.4980(4), c=50.352(1); a=5.4701(2), b=5.4577(2), c=49.643(1) for A=Ca, Sr, Ba and Pb, respectively. The structural features of the compounds were found similar to n=2-4 layers bismuth oxides. The strain caused by mismatch of cell parameter requirements for the [Bi₂O₂]²⁺ layers and perovskite-like [A₂Bi₂Ti₅O₁₆]²⁻ blocks were relieved by tilting of the TiO₆ octahedra. Variable temperature synchrotron X-ray studies for Ca and Pb compounds showed that the orthorhombic structure persisted up to 675 and 475 K, respectively. Raman spectra of the compounds are also presented.     

The crystal chemistry of Bi6TP2O15+x, T=Fe, Ni, Zn: Isomorphism and polymorphism, structural relationship to Bi6TiP2O16

The crystal structures of compounds with nominal compositions Bi₆FeP₂O_15+x (I), Bi₆NiP₂O_15+x (II) and Bi₆ZnP₂O_15+x (III) were determined from single-crystal X-ray diffraction data. They are monoclinic, space group I2, Z=2. The lattice parameters for (I) are a=11.2644(7), b=5.4380(3), c=11.1440(5) Å, β=96.154(4)°; for (II) a=11.259(7), b=5.461(4), c=11.109(7) Å, β=96.65(1)°; for (III) a=19.7271(5), b=5.4376(2), c=16.9730(6) Å, β=131.932(1)°. Least squares refinements on F² converged for (I) to R1=0.0554, wR₂=0.1408; for (II) R₁=0.0647, wR₂=0.1697; for (III) R₁=0.0385, wR₂=0.1023. The crystals are complexly twinned by 2-fold rotation about , by inversion and by mirror reflection. The structures consist of edge-sharing articulations of OBi₄ tetrahedra forming layers in the a-c plane that then continue by edge-sharing parallel to the b-axis. The three-dimensional networks are bridged by Fe and Ni octahedra in (I) and (II) and by Zn trigonal bipyramids in (III) as well as by oxygen atoms of the PO₄ moieties. Bi also randomly occupies the octahedral sites. Oxygen vacancies exist in the structures of the three compounds due to required charge balances and they occur in the octahedral coordination polyhedron of the transition metal. In compound (III), no positional disorder in atomic sites is present. The Bi-O coordination polyhedra are trigonal prisms with one, two or three faces capped. Magnetic susceptibility data for compound (I) were obtained between 4.2 and 350 K. Between 4.2 and 250 K it is paramagnetic, μ_eff=6.1 μ_B; a magnetic transition occurs above 250 K.     

Preparation of ZrO2-TiO2-CeO2 and Its Application in the Selective Catalytic Reduction of NO with NH3

TiO₂,ZrO₂-TiO₂,andZrO₂-TiO₂-CeO₂ were prepared by co-precipitation method and characterized by X-ray diffraction (XRD), specific surface area measurements (BET), temperature programmed desorption (NH₃-TPD), oxygen storage capacity (OSC), and temperature programmed reduction (H₂-TPR). The results showed that ZrO₂-TiO₂-CeO₂ exhibited large number of surface strong acid, possessed some oxygen storage capacity, and strong redox property. The three materials were used as supports and the monolith catalysts were prepared with 1% (w) V₂O₅ and 9% (w)WO₃ for selective catalytic reduction (SCR) of NO with ammonia in the presence of excessive O₂, and the results of catalytic activity showed that the catalyst used ZrO₂-TiO₂-CeO₂ as support yielded nearly 100% NO conversion at 275 °C at a gas hourly space velocity (GHSV) of 10000 h⁻¹, and it had the best catalytic activity and showed great potential for practical application.     

Solid-solid interactions in pure and Li2O-doped manganese and magnesium mixed oxides system

The solid-solid interactions between manganese and magnesium oxides in absence and in presence of small amounts of Li₂O have been investigated. The molar ratios between manganese and magnesium oxides in the form of Mn₂O₃ and MgO were varied between 0.05:1 to 0.5:1. The mixed solids were calcined in air at 400-1000°C. The techniques employed were DTA, XRD and H₂O₂ decomposition at 20-40°C.The results obtained revealed that solid-solid interactions took place between the reacting solids at 600-1000°C yielding magnesium manganates (Mg₂MnO₄, Mg₆MnO₈, MgMnO₄ besides unreacted portions of MgO, Mn₂O₃ and Mn₃O₄). Li₂O-doping (0.75-6 mol%) of the investigated system followed by calcination at 600 and 800°C decreased progressively the intensity of the diffraction lines of Mn₂O₃ (Bixbyite) with subsequent increase in the lattice parameter 'a' of MgO to an extent proportional to the amount of Li₂O added. This finding might suggest that the doping process enhanced the dissolution of Mn₂O₃ in MgO forming solid solution. This treatment led also to the formation of Li₂MnO₃. Furthermore, the doping with 3 and 6 mol% Li₂O conducted at 800°C resulted in the conversion of Mn₂O₃ into Mn₃O₄, a process that took place at 1000°C in absence of Li₂O. The produced Li₂MnO₃ phase remained stable by heating at up to 1000°C. Furthermore, Li₂O doping of the investigated system at 400-1000°C resulted in a progressive measurable increase in the particle size of MgO.The catalytic activity measurements showed that the increase in the molar ratio of Mn₂O₃ in the samples precalcined at 400-800°C was accompanied by a significant increase in the catalytic activity of the treated solids. The maximum increase in the catalytic activity expressed as reaction rate constant measured at 20°C (k _20°C) attained 3.14, 2.67 and 3.25-fold for the solids precalcined at 400, 600 and 800°C, respectively. Li₂O-doping of the samples having the formula 0.1 Mn₂O₃/MgO conducted at 400-600°C brought a progressive significant increase in its catalytic activity. The maximum increase in the value of k _20°C due to Li₂O attained 1.93 and 2.75-fold for the samples preheated at 400 and 600°C, respectively and opposite effect was found for the doped samples preheated at 800°C.This revised version was published online in November 2005 with corrections to the Cover Date.     

The Phase Relations in the System In2O3–TiO2–MgO at 1100 and 1350°C

The phase relations in the system In₂O₃–TiO₂–MgO at 1100 and 1350°C are determined by a classical quenching method. In this system, there are four pseudobinary compounds, In₂TiO₅, MgTi₂O₅ (pseudobrookite type), MgTiO₃ (ilmenite type), and Mg₂TiO₄ (spinel type) at 1100°C. At 1350°C, in addition to these compounds there exist a spinel-type solid solution Mg_2−xIn_2xTi_1−xO₄ (0≤x≤1) and a compound In₆Ti₆MgO₂₂ with lattice constants a=5.9236(7) Å, b=3.3862(4) Å, c=6.3609(7) Å, β=108.15(1)°, and q=0.369, which is isostructural with the monoclinic In₃Ti₂FeO₁₀ in the system In₂O₃–TiO₂–MgO. The relation between the lattice constants of the spinel phase and the composition nearly satisfies Vegard's law. In₆Ti₆MgO₂₂ extends a solid solution range to In₂₀Ti₁₇Mg₃O₆₇ with lattice constants of a=5.9230(5) Å, b=3.3823(3) Å, c=6.3698(6) Å, β=108.10(5)°, and q=0.360. The distributions of constituent cations in the solid solutions are discussed in terms of their ionic radius and site preference effect.     

Microstructures of Some Bi-W-Nb-O Phases

Microstructures of three Bi-W-Nb-O phases have been examined by using high-resolution transmission electron microscopy. Bi₁₇W₂Nb₃O₃₉ and Bi₁₇WNb₃O₃₆ have incommensurate superstructures derived from the defect fluorite-type δ-Bi₂O₃ and can be regarded as intermediate phases between the type II solid solutions in the Bi-Nb-O and Bi-W-O systems. Bi₈W₂Nb₂O₂₃ has a Bi₂WO₆-like subunit cell with a stepped superstructure. Formation mechanisms of various superstructures are discussed.     

Sol-gel synthesis of K3InF6 and structural characterization of K2InC10O10H6F9, K3InC12O14H4F18 and K3InC12O12F18

K₃InF₆ is synthesized by a sol-gel route starting from indium and potassium acetates dissolved in isopropanol in the stoichiometry 1:3, with trifluoroacetic acid as fluorinating agent. The crystal structures of the organic precursors were solved by X-ray diffraction methods on single crystals. Three organic compounds were isolated and identified: K₂InC₁₀O₁₀H₆F₉, K₃InC₁₂O₁₄H₄F₁₈ and K₃InC₁₂O₁₂F₁₈. The first one, deficient in potassium in comparison with the initial stoichiometry, is unstable. In its crystal structure, acetate as well as trifluoroacetate anions are coordinated to the indium atom. The two other precursors are obtained, respectively, by quick and slow evaporation of the solution. They correspond to the final organic compounds, which give K₃InF₆ by decomposition at high temperature. The crystal structure of K₃InC₁₂O₁₄H₄F₁₈ is characterized by complex anions [In(CF₃COO)₄(OH_x)₂]^(5−2x)− and isolated [CF₃COOH_2−x]^(x−1)− molecules with x=2 or 1, surrounded by K⁺ cations. The crystal structure of K₃InC₁₂O₁₂F₁₈ is only constituted by complex anions [In(CF₃COO)₆]³⁻ and K⁺ cations. For all these compounds, potassium cations ensure only the electroneutrality of the structure. IR spectra of K₂InC₁₀O₁₀H₆F₉ and K₃InC₁₂O₁₂F₁₈ were also performed at room temperature on pulverized crystals.     

Structure Study of Bi2.5Na0.5Ta2O9 and Bi2.5Nam−1.5NbmO3m+3 (m=2-4) by Neutron Powder Diffraction and Electron Microscopy

The crystal structures of Bi_2.5Na_0.5Ta₂O₉ and Bi_2.5Na_m-1.5Nb_mO_3m+3 (m=3,4) have been investigated by the Rietveld analysis of their neutron powder diffraction patterns (λ=1.470 Å). These compounds belong to the Aurivillius phase family and are built up by (Bi₂O₂)²⁺ fluorite layers and (A_m-1B_mO_3m+1)^2- (m=2-4) pseudo-perovskite slabs. Bi_2.5Na_0.5Ta₂O₉ (m=2) and Bi_2.5Na_2.5Nb₄O₁₅ (m=4) crystallize in the orthorhombic space group A2₁am, Z=4, with lattice constants of a=5.4763(4), b=5.4478(4), c=24.9710 (15) and a=5.5095(5), b=5.4783(5), c=40.553(3) Å, respectively. Bi_2.5Na_1.5Nb₃O₁₂ (m=3) has been refined in the orthorhombic space group B2cb, Z=4, with the unit-cell parameters a=5.5024(7), b=5.4622(7), and c=32.735(4) Å. In comparison with its isostructural Nb analogue, the structure of Bi_2.5Na_0.5Ta₂O₉ is less distorted and bond valence sum calculations indicate that the Ta-O bonds are somewhat stronger than the Nb-O bonds. The cell parameters a and b increase with increasing m for the compounds Bi_2.5Na_m-1.5Nb_mO_3m+3 (m=2-4), causing a greater strain in the structure. Electron microscopy studies verify that the intergrowth of mixed perovskite layers, caused by stacking faults, also increases with increasing m.     

Reactivity of Binary Mixtures of La(III) Oxide and Cu(II) Oxalate or Nitrate and Synthesis of La(III) Cuprate

Reactivity of mixtures of La(III) oxide and Cu(II) oxalate/nitrate in hydrated as well as anhydrous state was studied using TG, DTA and XRD. Cu(II) oxide formed in the endothermic decomposition of mixture containing hydrated Cu(II) nitrate and La(III) oxide could not form La₂CuO₄ while Cu(II) oxide formed in the exothermic decomposition of mixture containing hydrated/anhydrous Cu(II) oxalate and La(III) oxide reacts with La(III) oxide and develops the phases CuLaO₃ and La₂CuO₄. The maximum reactivity with respect to the formation of La₂CuO₄phase was observed in mixture containing anhydrous Cu(II) oxalate. This revised version was published online in July 2006 with corrections to the Cover Date.     

Metal-organic deposition of YBa2Cu3Ox and Bi2Sr2Ca1Cu2Ox films on various substrates starting from different fluorine-free metallorganic compounds

YBa₂Cu₃O_x (Y-123) and Bi₂Sr₂Ca₁Cu₂O_x (Bi-2212) films on various substrates have been prepared by Metal-Organic Deposition starting from different metallorganic fluorine-free compounds and using a very simple instrumentation. The processing conditions include a rapid pyrolysis step in air and an annealing step in oxygen for Y-123 and in air for Bi-2212. The films obtained have been characterized by X-ray diffraction (XRD) and the formation of a superconducting phase of Y-123 or Bi-2212 was confirmed measuring the critical temperature (T _c) with Ac-susceptibility and resistive measurements. Microstructure and final cationic ratios have been studied by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS).     

Li2O-TiO2-SiO2-P2O5和Li2O-TiO2-Al2O3-P2O5体系锂离子固体电解质的制备及性能研究

一些具有NASICON型网格结构的固体电解质具有高的电导率和好的稳定性,NASICON的意思是Na Super Ionic Conductor[1]。当NaZr2(PO4)3中P5 被Si4 部分取代时便可以得到具有NASICON结构的Na1 xZr2SixP3-xO12体系,其具有高的钠离子电导率。然而有相同结构的Li1 xZr2SixP3-xO12体系的离子电导率却很低,这是因为Li 半径太小,而NASICON三维网格结构的离子通道太大,两者不匹配而使电导率下降[2]。但当LiZr2(PO4)3中Zr4 被离子半径小些的Ti4 取代,所得LiTi2(PO4)3的通道就与Li 半径相匹配,适合于锂离子的迁移,从而使其电导率…     

Unusual phase characteristics in binary thallium telluride-metal telluride systems

The phase characteristics and some properties of alloys in the two most interesting of the binary thallium telluride systems (Tl₂Tl-Ag₂Te and Tb₂Te-Bi₂Te₃) are discussed and the phase diagrams of the systems are reviewed.     

Temperature dependence of the polarization resistance of the O<Subscript>2</Subscript>,Au/La<Subscript>0.88</Subscript>Sr<Subscript>0.12</Subscript>Ga<Subscript>0.82</Subscript>Mg<Subscript>0.18</Subscript>O<Subscript>2.85</Subscript> electrode system

The impedance of a porous gold electrode in contact with solid electrolyte La_0.88Sr_0.12Ga_0.82Mg_0.18O_2.85 and the effect of the manufacture conditions on its polarization resistance are studied at 600–800°C in air. The overall oxygen reaction rate on a gold electrode is described as the sum of two partial constituents, namely, the oxygen exchange at the gas/electrolyte interface at the gold/gas/electrolyte triple-phased boundary.Translated from Elektrokhimiya, Vol. 41, No. 2, 2005, pp. 190–197.Original Russian Text Copyright © 2005 by Shkerin, Sokolova, Khlupin, Beresnev.This revised version was published online in April 2005 with corrections to the article note and article title and cover date.     

Non-centrosymmetric Ba3Ti3O6(BO3)2

The compound previously reported as Ba₂Ti₂B₂O₉ has been reformulated as Ba₃Ti₃B₂O₁₂, or Ba₃Ti₃O₆(BO₃)₂, a new barium titanium oxoborate. Small single crystals have been recovered from a melt with a composition of BaTiO₃:BaTiB₂O₆ (molar ratio) cooled between 1100°C and 850°C. The crystal structure has been determined by X-ray diffraction: hexagonal system, non-centrosymmetric space group, a=8.7377(11) Å, c=3.9147(8) Å, Z=1, wR(F²)=0.039 for 504 unique reflections. Ba₃Ti₃O₆(BO₃)₂ is isostructural with K₃Ta₃O₆(BO₃)₂. Preliminary measurements of nonlinear optical properties on microcrystalline samples show that the second harmonic generation efficiency of Ba₃Ti₃O₆(BO₃)₂ is equal to 95% of that of LiNbO₃.     

Syntheses and characterization of two oxoborates, (Pb3O)2(BO3)2MO4 (M=Cr, Mo)

Two oxoborates, (Pb₃O)₂(BO₃)₂MO₄ (M=Cr, Mo), have been prepared by solid-state reactions below 700 °C. Single-crystal XRD analyses showed that the Cr compound crystallizes in the orthorhombic group Pnma with a=6.4160(13) Å, b=11.635(2) Å, c=18.164(4) Å, Z=4 and the Mo analog in the group Cmcm with a=18.446(4) Å, b=6.3557(13) Å, c=11.657(2) Å, Z=4. Both compounds are characterized by one-dimensional chains formed by corner-sharing OPb₄ tetrahedra. BO₃ and CrO₄ (MoO₄) groups are located around the chains to hold them together via Pb–O bonds. The IR spectra further confirmed the presence of BO₃ groups in both structures and UV–vis diffuse reflectance spectra showed band gaps of about 1.8 and 2.9 eV for the Cr and Mo compounds, respectively. Band structure calculations indicated that (Pb₃O)₂(BO₃)₂MoO₄ is a direct semiconductor with the calculated energy gap of about 2.4 eV.     

Phase relations, crystal chemistry, and dielectric properties in sections of the La2O3-CaO-MgO-TiO2 system

Subsolidus phase equilibria and crystal chemistry were studied for the La₂O₃-MgO-TiO₂ system and for the ternary sections LaMg_1/2Ti_1/2O₃-CaTiO₃-La₂O₃ and LaMg_1/2Ti_1/2O₃-CaTiO₃-La_0.833Mg_0.25Ti_0.75O₃ in the quaternary La₂O₃-CaO-MgO-TiO₂ system. Dielectric properties (relative permittivity and temperature coefficient of resonant frequency, τ_f) were measured at 5-10 GHz and mapped onto the phase equilibria relations to reveal the compositions of temperature-stable (τ_f=0) compounds and mixtures. Phase equilibria relations were obtained by X-ray powder diffraction analysis of approximately 80 specimens prepared by solid-state reactions in air at ∼1450°C. Six ternary phases were found to form in the La₂O₃-MgO-TiO₂ system, including the three previously reported compounds LaMg_1/2Ti_1/2O₃, La₅Mg_0.5Ti_3.5O₁₅, and “La₆MgTi₄O₁₈”; and the new phases La₁₀MgTi₉O₃₄, La₉Mg_0.5Ti_8.5O₃₁, and a perovskite-type solid solution (1−x)LaMg_1/2Ti_1/2O₃-xLa_2/3TiO₃ (0?x?0.5). The phase previously reported as “La₆MgTi₄O₁₈” was found to form off-composition, apparently as a point compound, at La₆Mg_0.913Ti_4.04O₁₈. Indexed experimental X-ray powder diffraction patterns are given for LaMg_1/2Ti_1/2O₃, La₅Mg_0.5Ti_3.5O₁₅, La₆Mg_0.913Ti_4.04O₁₈, La₁₀MgTi₉O₃₄, and La₉Mg_0.5Ti_8.5O₃₁. LaMg_1/2Ti_1/2O₃ exhibits a slightly distorted perovskite structure with ordered B-cations (P2₁/n; a=5.5608(2) Å, b=5.5749(3) Å, c=7.8610(5) Å, β=90.034(4)°). La₅Mg_0.5Ti_3.5O₁₅ (Pm1; a=5.5639(1), c=10.9928(5) Å) and La₆Mg_0.913Ti_4.04O₁₈ (R3m; a=5.5665(1), c=39.7354(9) Å) are n=5 and n=6 members, respectively, of the (111) perovskite-slab series A_nB_n−1O_3n. The new phases La₁₀MgTi₉O₃₄ (a=5.5411(2), b=31.3039(9), c=3.9167(1) Å) and La₉Mg_0.5Ti_8.5O₃₁ (a=5.5431(2), b=57.055(1), c=3.9123(1) Å) are n=5 and n=4.5 members, respectively, of the (110) perovskite-slab series A_nB_nO_3n+2, which exhibit orthorhombic subcells; electron diffraction revealed monoclinic superlattices with doubled c-parameters for both compounds. Extensive perovskite-type solid solutions form in the ternary sections LaMg_1/2Ti_1/2O₃-CaTiO₃-La₂O₃ and LaMg_1/2Ti_1/2O₃-CaTiO₃-La_0.833Mg_0.25Ti_0.75O₃. The La₂O₃-MgO-TiO₂ system contains two regions of temperature-stable (τ_f=0) compositions. The quaternary La₂O₃-CaO-MgO-TiO₂ system contains an extensive single-phase perovskite-type volume through which passes a surface of temperature-stable compositions with permittivities projected to be in the 40-50 range. Traces of this surface occur as lines of τ_f=0 perovskite-type phases in the ternary sections LaMg_1/2Ti_1/2O₃-CaTiO₃-La₂O₃ and LaMg_1/2Ti_1/2O₃-CaTiO₃-La_0.833Mg_0.25Ti_0.75O₃.