以平均粒径为19.71μm的天然微细鳞片石墨为原料,通过化学氧化法制备了具有不同氧化程度的可膨胀石墨,采用XRD、FTIR、Raman、SEM等对可膨胀石墨的结构与膨胀性进行了表征。结果表明:当氧化程度较低时制得的微细鳞片可膨胀石墨由石墨、石墨层间化合物和氧化石墨三相组成;随着氧化程度的增加,氧化石墨相含量与可膨胀石墨结构无序程度逐渐增高,石墨层间化合物相含量先增加后减少,石墨相含量则逐渐降低;氧化促使HSO4-或SO42-插入石墨层间,插入层间的HSO4-或SO42-量是决定可膨胀石墨膨胀容积的关键因素,制备的微细鳞片膨胀石墨的膨胀容积可达65.9mL·g-1。 相似文献
4.
5.
膨胀石墨经过超声处理制备了纳米石墨薄片。以其为导电填料,对甲苯磺酸为掺杂剂,FeCl3·6H2O为氧化剂,引发吡咯单体发生原位聚合,制备出纳米石墨薄片/聚吡咯(NanoGs/PPy)复合材料。利用红外光谱(FTIR)、扫描电镜(SEM)和透射电镜(TEM)表征了材料的组成和结构。结果表明,石墨薄片被聚吡咯完全包覆;并且以纳米级尺寸分散在聚吡咯基体中。热失重(TG)分析和电导率测试结果表明,复合材料的耐热性能和导电性能较纯聚吡咯有所提高。 相似文献
6.
以平均粒径为19.71μm的天然微细鳞片石墨为原料,通过化学氧化法制备了具有不同氧化程度的可膨胀石墨,采用XRD、FTIR、Raman、SEM等对可膨胀石墨的结构与膨胀性进行了表征。结果表明:当氧化程度较低时制得的微细鳞片可膨胀石墨由石墨、石墨层间化合物和氧化石墨三相组成;随着氧化程度的增加,氧化石墨相含量与可膨胀石墨结构无序程度逐渐增高,石墨层间化合物相含量先增加后减少,石墨相含量则逐渐降低;氧化促使HSO4-或SO42-插入石墨层间,插入层间的HSO4-或SO42-量是决定可膨胀石墨膨胀容积的关键因素,制备的微细鳞片膨胀石墨的膨胀容积可达65.9mL·g-1。 相似文献
7.
尼龙6/石墨纳米导电复合材料的制备与性能 总被引:30,自引:0,他引:30
通过原位插层聚合制备了尼龙 6 /石墨纳米导电复合材料 ,其室温导电渗滤阈值为 =0 75vol% ,远远低于常规导电粒子填充的聚合物复合材料 .当石墨体积分数为 2 0vol%时 ,室温电导率可达 10 -4 S/cm .透射电镜研究表明 :由于石墨经高温膨胀后其片层被剥离导致了片状石墨粒子具有巨大的径厚比 ,经原位插层聚合其片层厚度进一步被剥离为几十个纳米 ,同时原位插层聚合使得石墨粒子能够均匀分散在尼龙 6基体中 ,因而导致了该导电复合材料的低渗滤阈值和高导电性能 . 相似文献
8.
以可膨化石墨为原料,高温处理得到膨化石墨,再经过超声处理,得到纳米薄片石墨。将得到的纳米薄片石墨与甲基丙烯酸甲酯单体在超声作用下预聚,灌模,得到块状的聚甲基丙烯酸甲酯(PMMA)/石墨复合材料。用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、选区电子衍射SAD、红外、热重等分析仪器表征了纳米石墨薄片及PMMA/石墨复合材料。测试了复合材料的力学、电学性能,发现在室温下该复合材料的渗滤阀值为1.3%(wt),且保证石墨含量在1.4%(wt)时,即可保证复合材料具有良好的电学和力学性能。 相似文献
9.
10.
11.
12.
可膨胀石墨催化合成乙酸苄酯 总被引:4,自引:0,他引:4
可膨胀石墨作为一种重要的非金属材料已广泛应用于各工业领域 ,将其作为有机质反应催化剂的研究尚不多见[1~ 3] 。工业上 ,乙酸苄酯常是以浓H2 SO4、对甲苯磺酸等质子酸作催化剂由乙酸和苄醇制得[4] ,但此法腐蚀设备 ,污染环境 ,且副反应多。近年来 ,为了寻找对设备腐蚀性小的酯化反应催化剂进行了一些研究 ,如曾报道的酯化反应催化剂有 :四氯化锡复合物[5] 、复合固体超强酸[6] 、稀土硫酸盐[7]等。本文报道可膨胀石墨催化乙酸苄酯的合成 ,与其它催化剂相比 ,具有催化活性高 ,反应温度低 ,反应时间短 ,收率高 ,易分离及再生处理简单等… 相似文献
13.
A facile process for the synthesis of exfoliated graphite and polyaniline/graphite (PANI/graphite) nanocomposite was developed. Graphite nanosheets were prepared via the microwave irradiation and sonication from synthesized expandable graphite. The nanocomposites were fabricated via in situ polymerization of aniline monomer in the presence of graphite nanosheets. The nanoscale dispersion of graphite sheets was evidenced by the SEM and TEM examinations. According to the electrical conductivity test, the conductivity of the final PANI/graphite nanocomposites were dramatically increased compared with pristine PANI. From the thermogravimetric analysis, the introduction of graphite exhibits a beneficial effect on the thermal stability of PANI. 相似文献
14.
氧化石墨的制备及其有机化处理 总被引:10,自引:2,他引:10
Graphite oxide(GO) was successfully prepared by using expandable graphite, which is a new starting material instead of the normally adopted natural graphite. XRD and XPS data indicated that, in the same reaction condition due to the application of expandable graphite, the extent of oxidation for the product, GO, was considerably en-hanced and the period required for oxidation was greatly shortened. In addition, the prepared GO was modified by surfactant, that is the new sample, S-GO, was obtained. As a consequence the extended interlayer space has proved itself to be successfully intercalated by the surfactant. 相似文献
15.
A new method for the synthesis of exfoliated graphite and polyaniline (PANI)/graphite nanocomposites was developed. Exfoliated graphite nanosheets were prepared through the microwave irradiation and sonication of synthesized expandable graphite. The nanocomposites were fabricated via the in situ polymerization of the monomer at the presence of graphite nanosheets. The as-synthesized graphite nanosheets and PANI/graphite nanocomposite materials were characterized with Fourier transform infrared spectroscopy, scanning electron microscopy, transmission electron microscopy, and thermogravimetric analysis (TGA). The conductivity of the PANI/graphite nanocomposites was dramatically increased over that of pure PANI. TGA indicated that the incorporation of graphite greatly improved the thermal stability of PANI. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1972–1978, 2004 相似文献
16.
用化学共沉淀法和原位乳液聚合法分别制备了钴铁氧体/膨胀石墨复合微粒(CF/EG)和钴铁氧体/膨胀石墨/聚吡咯复合物(CF/EG/PPy)。用现代分析技术表征了样品的组成、结构、形貌、电-磁性能和油水分离性能。结果表明,CF粒子已填嵌入到膨胀石墨的层间,CF/EG/PPy复合物的核(CF/EG)和壳(PPy)之间存在着一定的相互作用,样品的油水分离效果与膨胀石墨的层间空隙成正比,其次序为:EG>CF/EG>CF/EG/PPy。磁性的CF/EG微粒回收容易,重复使用性能优良,循环5次的效率不低于90%。 相似文献
17.
以棒状石墨为原料,采用改良的Hummers法与热处理制备得到膨胀氧化石墨(E-GO),利用在酸性水溶液中归中化学反应的方法合成纳米尺寸的硫颗粒,使其嵌入到膨胀氧化石墨的内部,制备了膨胀氧化石墨-硫复合材料。采用红外光谱,X-射线光电子能谱表征了膨胀氧化石墨表面官能团的存在和种类;X-射线衍射分析结果表明生成的硫属于斜方晶结构;扫描电子显微镜和透射电镜分析证明了材料中硫的均匀分布。恒电流充放电结果表明该复合正极材料的首次放电容量为1 020 mAh.g-1,100周循环之后其容量还保持在650 mAh.g-1左右;材料的倍率性能和库伦效率优异,这可能得益于小尺寸的硫在材料中均匀分布,以及表面官能团对硫的固定化作用。 相似文献