在正丙醇与水的混合溶剂体系中以Ti(SO4)2为前驱物制备得到了粒径分布窄,分散性好的球形TiO2.对表面活性剂种类及用量,反应物浓度及焙烧温度和时间等影响因素进行了研究,结果表明,在正丙醇与水的体积比为1∶1的条件下,以聚乙烯吡咯烷酮(PVP)为表面活性剂,温度为70-90℃时可制得粒径分布窄、分散性好的高质量的球形TiO2颗粒.通过TG-DSC、SEM、XRD等分析表明,颗粒粒度大小及粒径分布受表面活性剂浓度和反应前驱物浓度影响大;物相间的转化主要由焙烧温度和时间来决定.并引入LaMer模型对颗粒形核、长大的过程进行理论说明.     

粒径可控球形TiO2的制备

在正丙醇与水的混合溶剂体系中以Ti(SO4)2为前驱物制备得到了粒径分布窄, 分散性好的球形TiO2. 对表面活性剂种类及用量, 反应物浓度及焙烧温度和时间等影响因素进行了研究, 结果表明, 在正丙醇与水的体积比为1:1的条件下, 以聚乙烯吡咯烷酮(PVP)为表面活性剂, 温度为70-90 ℃时可制得粒径分布窄、分散性好的高质量的球形TiO2颗粒. 通过TG-DSC、SEM、XRD等分析表明, 颗粒粒度大小及粒径分布受表面活性剂浓度和反应前驱物浓度影响大; 物相间的转化主要由焙烧温度和时间来决定. 并引入LaMer模型对颗粒形核、长大的过程进行理论说明.     

电化学溶解钛金属直接水解法制备纳米TiO2

Metallic titanium was electrochemically dissoluted in absolute ethanol in the presence of Et4N•Br(as electro conductive additive),The electrolyte solution was then directly hydrolysized to obtain nanocrystalline TiO2.The powder obtained was calcined at 720℃ for 1 h.FT IR,Raman spectra,XRD and TEM were used to investigate the structure and particle size of the powder.Studies showed that the nanocrystalline TiO2 prepared by this method was of monocline structure with high textural stability and narrow size distribution of 10－20 nm,and its Raman spectra showed a shift of about 25 cm－1.The experiments also showed that the product yield could be improved by controlling the temperature under 50－60℃,selecting R4N•Br as conductive additive and preventing titanium anode from being passivated.The electrochemical dissolution of metal anode may be recommanded as a promising technique for the synthesis of nanomaterials.     

水溶液法制备图案化TiO2薄膜

从硫酸钛Ti(SO4)2的水溶液出发, 采用化学浴沉积和电沉积法来制备图案化TiO2薄膜. 通过硫酸和双氧水来稳定Ti4+, 配制了pH=1.0的硫酸钛溶液和pH=1.6的过氧硫酸钛溶液. 结合微接触印刷术在硅基底上制得自组装膜预图案, 再化学浴沉积TiO2即可得规则图纹. 无机配体对钛溶液的稳定性和TiO2的晶型均有影响, 溶液的酸度关系到所得图案的质量. 过氧硫酸钛溶液同样适用于电沉积, 在导电玻璃基底上旋涂光刻胶后选择性曝光、显影, 通过控制阴极电位可获得高差达200 nm的清晰图案.     

Ti(SO4)2沸腾水解法制备纳米TiO2及光催化研究

纳米二氧化钛是一种新型的无机功能材料,它具有许多独特的性质,如化学活性高、可见光透过性好、吸收紫外光性能强、具有超亲水性等[1-2],可用于制造电介质材料、光催化薄膜、化学传感器等[3]。TiO2作为光催化剂几乎能氧化降解水体和空气中的绝大多数有机污染物。制备纳米TiO2的     

球形TiO2-Al2O3的制备、结构和理化性能研究

将Ti(SO4)2溶于稀盐酸合成酸性钛溶胶,再将其与铝溶胶和六次甲基四胺溶液混合后采用油柱成型法制备了球形TiO2-Al2O3复合氧化物。通过XRD、低温氮吸附-脱附与NH3-TPD等手段对样品进行表征,结果表明600℃焙烧得到的球形TiO2-Al2O3中TiO2以无定型形式存在;随TiO2含量的增加,球形TiO2-Al2O3的比表面积、孔容和平均孔径呈增加趋势;TiO2的引入没有对球形TiO2-Al2O3的强酸和弱酸中心的强度产生影响,弱酸中心数量显著增加,强酸中心数量稍有增加;球形TiO2-Al2O3的堆密度和压碎强度随TiO2含量的增加而减小,颗粒直径基本保持不变。     

电化学溶解钛金属直接水解法制备纳米TiO_2

纳米材料是目前材料科学的热点 .TiO2作为一种重要的无机功能材料 ,具有温敏、气敏、光催化等功能 ,广泛用于光电材料、涂料、传感器、介电材料、催化剂及载体等重要领域 .由于其各种应用都与粉体的性能有直接关系 ,因此研究纳米 TiO2的制备方法具有重要的实际意义 [1].近年来 ,纳米 TiO2粉体制备方法有了很大的发展 ,如 TiCl4气相水解沉淀法 [2],乳浊液法和 Ti(OC4H9)4水解沉淀法 [1],喷雾热解法 [3],放电爆炸法 [4],反应电极埋弧法 [5],溶胶凝胶 (Sol gel)法 [6]等 ,其中溶胶凝胶法是制备纳米材料的有效方法 .但这些方法存在…     

TiO2 /wAC复合光催化剂的酸催化水解合成及表征

以TiCl4为钛源, 采用酸催化水解法合成了活性炭(AC)复合光催化剂TiO2/wA(w:AC 的质量分数, %). 通过对苯酚、甲基橙以及六价铬的光催化降解, 考察了AC 含量、反应溶液初始pH值、使用次数对TiO2/wAC光催化剂催化活性的影响,并采用重力沉降法测试了催化剂分离性能. 采用XRD、DRS、FTIR、SEM、低温液氮吸附等对光催化剂晶相结构、光谱特征、表面结构等进行了表征. 结果表明, 适宜AC 含量的TiO2/wAC(wAC=5%, 记为5AC)具有较高的光催化活性.AC 掺杂可减小TiO2粒子凝聚, 而对TiO2的晶相结构、晶粒大小以及表面性质影响不大, 对TiO2能阈结构不产生影响. TiO2与AC结合牢固, 接触界面处有Ti—O—C 键生成. TiO2/5AC 表现出高光催化活性的主要原因是, AC 所提供的适宜高浓度环境及对纳米尺寸TiO2团聚的有效抑制. TiO2/5AC的高活性, 不易失活, 易分离以及活性受pH 变化影响较小的特性,使其在实际废水处理方面具有潜在应用价值.     

真空吸附水解制备活性炭负载TiO2及其光催化降解间二氯苯

采用直接真空吸附钛酸四丁酯后水解法制备了以活性炭为载体的负载型TiO₂光催化剂,以间二氯苯为探针分子研究了催化剂光催化降解反应性能.实验结果表明:随着热处理温度的不同,催化剂的光催化活性有很大的变化.对催化剂多次反复使用,其活性基本不变.     

硅氧烷的水解-缩聚反应动力学

综述了硅氧烷的水解动力学的主要影响因素(硅氧烷上的基团和水解反应催化剂等)、单组分以及多组分硅氧烷缩聚反应动力学、硅氧烷共缩聚产物结构控制策略。     

Kinetics of Spontaneous Hydrolysis of O-(2,2-Dimethylcyclopentyl)-methylfluorophosphonate and of Hydrolysis During Constant pH Value of the Reaction Medium

Hydrolysis of O-(2,2-dimethylcyclopentyl)-methylfluorophosphonate in dilute aqueous solution was investigated. Rates of hydrolysis of O-(2,2-dimethylcyclopentyl)-methylfluorophosphonate were measured as a function of pH (in the range from 3 to 9 and without keeping the pH-value constant--in a spontaneous hydrolysis) and temperature (in the range from 25°;C to 40°;C). Objective of these investigations was to simulate real processes of degradation of highly toxic compounds in nature, getting information about rates of degradation, in order to obtain most efficient systems for their removal.     

酸催化水解法制备可见光响应N掺杂纳米TiO2催化剂

 以TiCl4为钛源,采用酸催化水解法合成了TiO2前驱体,在NH3/N2气氛中经程序升温处理制得不同N掺杂量的TiO2可见光响应催化剂. 以苯酚为模型物,考察了催化剂在可见光及紫外光区的催化活性. 采用X射线衍射、紫外-可见漫反射光谱、傅里叶变换红外光谱、扫描电镜和低温氮物理吸附对光催化剂的晶相结构、光谱特征和表面结构进行了表征. 结果表明,掺杂N后锐钛矿TiO2的可见光催化活性显著提高,在500 ℃焙烧5 h制得的催化剂在可见光区及紫外光区均表现出最高的光催化活性. N掺杂对TiO2的晶粒大小、比表面积和晶相结构影响不大. 适量N掺杂可在TiO2表面形成Ti-O-N键,形成了新的能级结构,使催化剂的吸收带边红移至490～550 nm; 同时该结构也可有效提高TiO2的紫外光催化活性.     

TiO2纳米薄膜的溶胶-凝胶工艺制备和表征

通过sol-gel工艺在普通钠钙玻璃表面制备了均匀透明的锐钛矿型TiO2纳米薄膜.TiO2薄膜的X射线衍射分析表明,当薄膜的厚度小于0.46μm时,薄膜中未出现锐钛矿的衍射峰.随着镀膜次数或薄膜厚度的增加,薄膜中TiO2纳米微晶的平均晶粒大小逐渐增大,TiO2薄膜的透光率略有减小,其吸收阈值发生了明显的红移.XPS实验结果表明：薄膜中除含有Ti、O元素外,还有一定量来自有机前驱物中未完全燃烧的碳和少量从玻璃表面扩散到薄膜中的Na和Ca元素.     

Preparation and Kinetics of a Novel Glutathione Peroxidase Mimic- Selenium-modified Hyaluronic Acid

A selenium-modified hyaluronic acid（HA） compound（SeHA） was synthesized as a mimic of glutathione peroxidase（GPX）. IR and NMR spectra of SeHA predict that the --CH2OH group of the N-acetyl-D-glucosamine in HA was modified by group --Sell. There are averagely 152 --Sell groups in one SeHA molecule. The GPX activities are 103.88, 32. 15 and 152. 71 U/μmol, respectively, when the substrates were H2O2, BuOOH and CuOOH. Ping-pong mechanism was observed in the steady-state kinetic studies of the reactive oxygen species（ROS） consuming reaction. Result of reactions of SeHA with free radical capturer 2,6-di-tert-butyl-4-methylphenol（BHT） shows that the catalysis is based on a non-free radical-mechanism and the SeHA can not be inhibited by iodoacetate, an enzyme inhibitor.     

镧系离子掺杂TiO2的制备及其对咪唑降解反应的光催化活性

 以TiCl4和镧系元素的氯化盐溶液为前驱体,采用溶胶-凝胶法制备了不同含量镧系离子掺杂的TiO2光催化剂,用X射线衍射(XRD)、 光致发光光谱(PLS)、 表面光电压谱(SPS)和X射线光电子能谱(XPS)对催化剂进行了表征. XRD结果表明,样品为锐钛矿和金红石的混晶相,镧系离子未进入到TiO2晶格中. PLS和SPS测定结果表明,随着掺杂离子的不同和掺杂含量的不同,样品的谱强度呈现有规律的变化. 在紫外光照射下,以咪唑为目标降解物比较了催化剂的光催化活性. 结果表明,适当含量的镧系离子掺杂可有效促进TiO2表面光生载流子的分离,从而显著提高其光催化活性.     

表面覆CoOOH的球形Ni(OH)2的制备及快充性能

应用化学沉淀-电化学氧化法,于球形N i(OH)2颗粒表面生成CoOOH包覆层,研究包覆处理对AA型高容MH/N i电池快充性能的影响,并由红外光谱和扫描电镜表征覆钴样品.结果表明,以包覆CoOOH的N i(OH)2作正极活性材料装配的电池较之于正极单一添加CoO的电池,其内阻降低了约3.4 mΩ,该电池快充时充电电压平台较低且在充电末期电池温度不超过55℃,首次放电效率达90.6%,快充循环寿命达300周次.     

临界溶剂化作用对水解反应动力学的影响

用过渡态及Kirkwood介电模型考察近临界水中醋酸甲酯(MeAc)水解动力学.实验结果表明,临界溶剂化作用使本体系在623K附近出现反应活化体积(ΔV^≠)极负值现象,同时反应表观活化能降低至(23.5±8.29)kJ/mol.利用lnkc与反应场的线性关系可修正压力因素对水解动力学的影响,并证实了近临界水介质中MeAc水解S_N2反应机理的可靠性.     

超声波作用下的钛醇盐水解法制备纳米TiO2

近十几年来, 有关二氧化钛光催化性能的研究已引起人们的浓厚兴趣, 在此方面进行了大量研究. 目前, 纳米二氧化钛的制备方法主要有化学沉淀法、溶胶-凝胶法、气相法和水热法等[1,2]. 超声化学是近年来新兴的一门边缘交叉学科, 已被应用于制备具有特殊结构和性能的纳米材料, 如金属[3]、碳化物[4]、氮化物[5]、氧化物[6]、合金[7]以及生物材料[8]等, 但对于超声作用在纳米粒子晶型转变方面的研究报道较少.     

LiF掺杂TiO2的制备及其光催化性能

采用溶胶-凝胶法制备了LiF掺杂的TiO2光催化剂,并采用X射线衍射、X射线光电子能谱和光致发光光谱等技术对样品进行了表征.以亚甲基蓝的光催化降解为反应模型,考察了LiF掺杂量、退火温度和溶液pH值对催化剂光催化性能的影响.结果表明,LiF的掺杂降低了金红石相的形成温度,同时在TiO2表面引入大量羟基氧并提高了TiO2表面氧空穴浓度,因此提高了TiO2的光催化性能.在LiF掺杂量为8%,退火温度为500℃和反应液pH值为6.6的条件下,LiF掺杂的TiO2的光催化活性是未掺杂TiO2的6倍.