Preparation of indium sulfide thin films by spray pyrolysis using a new precursor indium nitrate

Indium nitrate and thiourea were used as the precursor solutions for preparing indium sulfide thin films using Chemical Spray Pyrolysis (CSP) technique. Films having various In/S ratios were characterized using X-Ray Diffraction (XRD), Energy Dispersive X-ray Analysis (EDX), Scanning Electron Microscopy (SEM), X-ray Photoelectron Spectroscopy (XPS), optical absorption, transmission and photosensitivity measurements. Sample having In/S ratio 2/3 showed better crystallinity with band gap 2.66 eV. Depth profile of the sample also indicated the formation of indium sulfide. It was also observed that In/S ratio in the initial precursor solution determined the composition as well as electrical properties of the films. Maximum photosensitivity was observed for the sample prepared using solution having In/S ratio 2/4.     

Effects of experimental parameters on composition of boron carbon nitride thin films deposited by magnetron sputtering

We have synthesized boron carbon nitride thin films by radio frequency magnetron sputtering. The films structure and composition were characterized by X-ray diffraction, Fourier transform infrared spectroscopy and X-ray photoelectron spectroscopy. The results indicate that the three elements of B, C, N are chemically bonded with each other and atomic-level hybrids have been formed in the films. The boron carbon nitride films prepared in the present experiment possess a disordered structure. The influence of PN₂/PN₂+Ar, total pressure and substrate bias voltage on the composition of boron carbon nitride films is investigated. The atomic fraction of C atoms increases and the fractions of B, N decrease with the decrease of PN₂/PN₂+Ar from 75% to 0%. There is an optimum total pressure. That is to say, the atomic fractions of B, N reach a maximum and the fraction of C atoms reaches a minimum at the total pressure of 1.3 Pa. The boron carbon nitride films exhibit lower C content and higher B, N contents at lower bias voltages. And the boron carbon nitride films show higher C content and lower B, N contents at higher bias voltages.     

Correlation between density and structure. in boron nitride thin films by X-ray diffraction

* _ion=100 eV. Above E^* _ion the average density (deduced from X-ray reflectivity) shows a strong increase, indicating the sudden appearance of the cubic boron nitride phase consistent with the sp³ concentration deduced from IR absorption spectroscopy. The in-plane X-ray diffraction shows that this cubic phase consists of small nanocrystals of 70 Å linear size. Received: 26 November 1996/Accepted: 27 January 1997     

Evaluation of carbon films electrodeposited on different substrates from different organic solvents

Diamond-like-carbon (DLC) films have been deposited on Si, aluminum and indium tin oxide-coated glass from several organic solvents with pulse-modulated power. The films are characterized by X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy. XPS spectra show that the main composition of the films is carbon and Raman spectra show that the films are typical DLC films and a high potential is preferable in the formation of sp ³-structure carbon. Comparing the results from different solvents and different substrates we deduce that the methyl group of the solvents has a critical function in forming the DLC films. However, the formation process and the characters of the films, such as appearance, resistivity and thickness, are mainly determined by the substrate. We may call this deposition a substrate-controlled reaction. Received: 31 May 2000 / Accepted: 9 January 2001 / Published online: 3 April 2001     

Properties of NiO thin films deposited by intermittent spray pyrolysis process

NiO thin films have been grown on glass substrates by intermittent spray pyrolysis deposition of NiCl₂·6H₂O diluted in distilled water, using a simple “perfume atomizer”. The effect of the solution molarity on their properties was studied and compared to those of NiO thin films deposited with a classical spray system. It is shown that NiO thin films crystallized in the NiO structure are achieved after deposition. Whatever the precursor molarity, the grain size is around 25-30 nm. The crystallites are preferentially oriented along the (1 1 1) direction. All the films are p-type. However, the thickness and the conductivity of the NiO films depend on the precursor contraction. By comparison with the properties of films deposited by classical spray technique, it is shown that the critical precursor concentration, which induces strong thin films properties perturbations, is higher when a perfume atomizer is used. This broader stability domain can be attributed to better chlorides decomposition during the rest time used in the perfume atomizer technique.     

Highly oriented (1 0 0) ZnO thin films by spray pyrolysis

Undoped ZnO thin films have been deposited onto glass substrates by spray pyrolysis. The structural, electrical and optical properties were studied on thin films, prepared from precursor solutions with varying the ethanol concentrations. X-ray diffraction studies have shown polycrystalline nature of the films with a hexagonal wurtzite-type structure. The preferential orientation plane (1 0 0) of the ZnO thin film is found to be sensitive to ethanol concentration. The texture coefficient (TC) and grain size value have been calculated. Also ethanol concentration was found to have significant effect on sheet resistivity of the films.     

Influence of substrate temperature on the chemical and microstructural properties of MO-CVD ZrTiO<Subscript>4</Subscript> thin films

In the last few years, intensive research activity has been focused on the development of suitable synthesis methods for high-permittivity materials, used for the realization of next-generation microdevices able to fulfil the previsions of the Technology Roadmap of Semiconductors. The use of high-permittivity materials can overcome the difficulties concerning the production of SiO₂-based ultra-thin dielectrics, such as the generation of pinholes and the non-uniformity of the film, which may result in a malfunction in high-density systems. Recently, zirconium titanate thin films were discovered to have very interesting dielectric properties, which suggests a use for them in microwave integrated systems, such as receivers or DRAMs, since they are monophasic, have little dissipation and show a good thermal stability and a high value for the dielectric constant, independent of frequency in the range from kilohertz to a few gigahertz. Real application is possible only in strict connection with the development of a suitable preparation method which allows production with controlled and reproducible characteristics. In this work, the synthesis and characterization of Zr_xTi_1-xO₄ (ZT) thin films grown via MO-CVD is described, studying the influence of growth parameters on their structural, chemical and physical properties. Received: 17 June 2002 / Accepted: 24 June 2002 / Published online: 4 November 2002 RID="*" ID="*"Corresponding author. Fax: +39-06/9067-2445, E-mail: Pad@mlib.cnr.it     

Growth of a textured quasicrystalline phase in Ti-Ni-Zr films prepared by pulsed laser deposition

The preparation in thin film form of the known icosahedral phase in Ti-Ni-Zr bulk alloys has been investigated as a function of substrate temperature. Films were deposited by pulsed laser deposition on sapphire substrates at temperatures ranging from room temperature to 350 °C. Morphological and structural modifications have been followed by grazing-incidence and θ–2θ X-ray diffraction, transmission electron diffraction and imaging. Chemical composition has been analyzed by electron probe microanalysis. The in-depth variation of composition has been studied by secondary neutral mass spectroscopy. We show that pulsed laser deposition at 275 °C makes the formation of a 1-μm-thick film of Ti-Ni-Zr quasicrystalline textured nanocrystallites possible. Received: 7 June 2001 / Accepted: 18 February 2002 / Published online: 3 June 2002 RID="*" ID="*"Corresponding author. Fax: +33-3/8357-6300, E-mail: brien@mines.u-nancy.fr     

Deposition and characterization of La2Ti2O7 thin films via spray pyrolysis process

Thin films of La₂Ti₂O₇ have been deposited on fused silica and Si substrates by a spray pyrolysis method using ethylene glycol solution of La(III)-Ti(IV)-citrate complexes as starting material and O₂ as a carrier gas. The composition, crystal structure and morphology of the films are studied.     

Atomic layer deposition of PbZrO3 thin films

In this paper, we report on the preparation of lead zirconate films for the first time using atomic layer deposition in an attempt to investigate some of the film properties and also to evaluate possible use of the precursor combination to prepare more complex lead titanate zirconate. In the depositions tetraphenyl lead (Ph₄Pb) was used as the lead and zirconium 2,2,6,6-tetramethyl-3,5-heptadionato (Zr(thd)₄) as the zirconium precursor, while ozone was used as the oxygen source. Film growth, stoichiometry and quality were studied using different pulsing ratios at deposition temperatures of 275 and 300 °C. According to X-ray diffraction, the crystalline perovskite phase was observed when films deposited on SrTiO₃(1 0 0) were annealed at 600 °C. Surface roughness was reduced for lead deficient films as well as in annealed samples.     

Formation of the ferroelectric domains in epitaxial PbTiO3 thin films grown by metalorganic chemical vapor deposition

3 thin films have been prepared by metalorganic chemical vapor deposition under reduced pressure. The formation of ferroelectric domains in films grown on SrTiO₃ and LaAlO₃ substrates was investigated by synchrotron radiation and Rutherford backscattering spectroscopy. Single-domain (3000-Å thick) and multi-domain (4500-Å thick) PbTiO₃ films were produced on SrTiO₃. For multi-domain PbTiO₃ film, the c-domain presented epitaxial structure with its c-axis perpendicular to the substrate surface, while a-domains aligned four-fold symmetrically with c-domains by 2.79^° off the c-axis of c-domains. In the film, the measured lattice constants (a, b and c) of the a- and c-domains were different from each other, indicating that the films suffered a modulated strain during domain formation. In contrast, both the a and c domains of films on LaAlO₃ were alternatively aligned on substrate with the a-axis of the a-domain and the c-axis of c-domains perpendicular to the substrate surface. Two-dimensional distribution of these domains is proposed and the formation of these kinds of domains is discussed. The surface morphology and phase transition process of single and multi domain PbTiO₃ film on SrTiO₃ were studied by atomic force microscope (AFM) and high temperature X-ray diffraction, respectively. Received: 15 August 1996/Accepted: 21 January 1997     

Spray pyrolysis deposition of YSZ and YSZ-Pt composite films

In the present paper procedures are described for spray pyrolysis deposition of YSZ films (0.1-30 μm in thickness) with 8 or 15 mole % of YO_1.5 on different substrates. Aqueous or ethylene glycol solutions of Y-Zr-citrates were used as starting material and O₂ as carrier gas. The crystal structure and the morphology of the films were studied.The optimal deposition and post-deposition annealing conditions were defined, taking into account the desired film thickness and characteristics. Substrate temperatures of 250 °C during the deposition followed by heating for 10 min to 400 °C after every spraying and to 590 °C after every three sprayings with final annealing at 590 °C for 2 h in static air atmosphere were found to be suitable for the production of dense, uniform and cracks-free films.     

Structure and optical properties of ZnS thin films grown by glancing angle deposition

The glancing angle deposition (GLAD) technique was used to deposit ZnS films by electron beam evaporation method. The cross sectional scanning electron microscopy (SEM) image illustrated a highly orientated microstructure composed of slanted column. The atomic force microscopy (AFM) analysis indicated that incident flux angle had significant effects on the nodule size and surface roughness. Under identical nominal thickness, the actual thickness of the GLAD films is related to the incident flux angle. The refractive index and in-plane birefringence of the GLAD ZnS films were discussed, and the maximum birefringence Δn = 0.036 was obtained at incident flux angle of α = 80°. Therefore, the glancing angle deposition technique is a promising way to create a columnar structure with enhanced birefringent property.     

Stable p-ZnO thin films by oxygen control using reverse spray dynamics

Semiconducting ZnO thin films were deposited on glass substrates by a modified CVD method using reverse spray of the precursor solutions. The films were characterized by X-ray diffraction (XRD) and Hall effect measurements at room temperature. The results of XRD analysis revealed polycrystalline nature of the grown films with different crystallographic orientations. The type of conductivity and the carrier concentration as determined from Hall effect measurements were dependent on the deposition temperature and annealing conditions. Oxygen control at 220 °C produced p-ZnO film with high hole mobility (193 cm²/V s). The electrical conductivity was correlated to the stoichiometry of the grown films.     

Chemical bath-deposited ZnS thin films: Preparation and characterization

Chemical bath deposition of ZnS thin films from NH₃/SC(NH₂)₂/ZnSO₄ solutions has been studied. The effect of various process parameters on the growth and the film quality are presented. The influence on the growth rate of solution composition and the structural, optical properties of the ZnS thin films deposited by this method have been studied. The XRF analysis confirmed that volume of oxygen of the as-deposited film is very high. The XRD analysis of as-deposited films shows that the films are cubic ZnS structure. The XRD analysis of annealed films shows the annealed films are cubic ZnS and ZnO mixture structure. Those results confirmed that the as-deposited films have amorphous Zn(OH)₂. SEM studies of the ZnS thin films grown on various growth phases show that ZnS film formed in the none-film phase is discontinuous. ZnS film formed in quasi-linear phase shows a compact and a granular structure with the grain size about 100 nm. There are adsorbed particles on films formed in the saturation phase. Transmission measurement shows that an optical transmittance is about 90% when the wavelength over 500 nm. The band gap (E_g) value of the deposited film is about 3.51 eV.     

Growth of thin, crystalline oxide, nitride, and oxynitride films on NiAl and CoGa surfaces

At 300 K, an amorphous Al-oxide film is formed on NiAl(001) upon oxygen adsorption. Annealing of the oxygen-saturated NiAl(001) surface to 1200 K leads to the formation of thin well-ordered θ-Al₂O₃ films. At 300 K, and low-exposure oxygen atoms are chemisorbed on CoGa(001) on defects and on step edges of the terraces. For higher exposure up to saturation, the adsorption of oxygen leads to the formation of an amorphous Ga-oxide film. The EEL spectrum of the amorphous film exhibits two losses at ≈400 and 690 cm^-1. After annealing the amorphous Ga-oxide films to 550 K thin, well-ordered β-Ga₂O₃ films are formed on top of the CoGa(001) surface. The EEL spectrum of the β-Ga₂O₃ films show strong Fuchs-Kliewer (FK) modes at 305, 455, 645, and 785 cm^-1. The β-Ga₂O₃ films are well ordered and show (2×1) LEED pattern with two domains, oriented perpendicular to each other. The STM study confirms the two domains structure and allows the determination of the two-dimensional lattice parameters of β-Ga₂O₃. The vibrational properties and the structure of β-Ga₂O₃ on CoGa(001) and θ-Al₂O₃ on NiAl(001) are very similar. Ammonia adsorption at 80 K on NiAl(111) and NiAl(001) and subsequent thermal decomposition at elevated temperatures leads to the formation of AlN. Well-ordered and homogeneous AlN thin films can be prepared by several cycles of ammonia adsorption and annealing to 1250 K. The films render a distinct LEED pattern with hexagonal [AlN/NiAl(111)] or pseudo-twelve-fold [AlN/NiAl(001)] symmetry. The lattice constant of the grown AlN film is determined to be a_AlN= 3.11 Å. EEL spectra of AlN films show a FK phonon at 865 cm^-1. The electronic gap is determined to be E_g= 6.1±0.2 eV. GaN films are prepared by using the same procedure on the (001) and (111) surfaces of CoGa. The films are characterized by a FK phonon at 695 cm^-1 and an electronic band gap E_g= 3.5±0.2 eV. NO adsorption at 75 K on NiAl(001) and subsequent annealing to 1200 K leads to the formation of aluminium oxynitride (AlON). An oxygen to nitrogen atomic ratio of ≈2:1 was estimated from the analysis of AES spectra. The AlON films shows a distinct (2×1) LEED pattern and the EEL spectrum exhibits characteristic Fuchs-Kliewer modes. The energy gap is determined to be E_g= 6.6±0.2 eV. The structure of the AlON film is derived from that of θ-Al₂O₃ formed on NiAl(001). Received: 21 March 1997/Accepted: 12 August 1997     

Al2O3 thin films by plasma-enhanced chemical vapour deposition using trimethyl-amine alane (TMAA) as the Al precursor

2 O₃ thin films by plasma-enhanced chemical vapour deposition (PECVD) using trimethyl-amine alane (TMAA) as the Al precursor. The thin films were deposited on both Si and quartz silica (SiO₂) substrates. Deposition rates were typically 60 Å min^-1 keeping the TMAA temperature constant at 45 °C. The deposited Al₂O₃ thin films were stoichiometric alumina with low carbon contamination (0.7–1.3 At%). The refractive index ranged from 1.54 to 1.62 depending on the deposition conditions. The deposition rate was studied as a function of both the RF power and the substrate temperature. The structure and the surface of the deposited Al₂O₃ thin films were studied using X-ray diffraction, atomic force microscopy (AFM) and scanning electron microscopy (SEM). Received: 20 May 1997/Accepted: 12 June 1997     

Study on the orientation of silver films by ion-beam assisted deposition

Low energy ion beam assisted deposition (IBAD) was employed to prepare Ag films on Mo/Si (100) substrate. It was found that Ag films deposited by sputtering method without ion beam bombardment were preferred (111) orientation. When the depositing film was simultaneously bombardment by Ar⁺ beam perpendicular to the film surface at ion/atom arrival ratio of 0.18, the prepared films exhibited weak (111) and (200) mixed orientations. When the direction of Ar⁺ beam was off-normal direction of the film surface, Ag films showed highly preferred (111) orientation. Monte Carlo method was used to calculate the sputtering yields of Ar⁺ ions at various incident and azimuth angles. The effects of channeling and surface free energy on the crystallographic orientation of Ag films were discussed.     

High-throughput synthesis and characterization of Mg1−xCaxO films as a lattice and valence-matched gate dielectric for ZnO based field effect transistors

Using composition-spread technique, we have grown metastable Mg_1−xCa_xO solid solution films on ZnO layers by pulsed laser deposition. All the films exhibited (1 1 1) oriented cubic phase. Despite a large miscibility gap, no phase separation took place at growth temperatures up to 700 °C, whereas an optimal growth temperature was found at 400 °C in terms of the crystallinity. The composition-spread films were characterized by X-ray diffraction mapping technique. Both lattice parameters and diffraction intensity increased with increasing the CaO composition. The present isovalent heterointerfaces realized the perfect lattice-matching by properly adjusting the CaO composition, leading to particular interest for ZnO based field effect transistors.     

Effect of thickness on structural, optical and electrical properties of nanostructured ZnO thin films by spray pyrolysis

Transparent conducting zinc oxide thin films were prepared by spray pyrolytic decomposition of zinc acetate onto glass substrates with different thickness. The crystallographic structure of the films was studied by X-ray diffraction (XRD). XRD measurement showed that the films were crystallized in the wurtzite phase type. The grain size, lattice constants and strain in films were calculated. The grain size increases with thickness. The studies on the optical properties show that the direct band gap value increases from 3.15 to 3.24 eV when the thickness varies from 600 to 2350 nm. The temperature dependence of the electrical conductivity during the heat treatment was studied. It was observed that heat treatment improve the electrical conductivity of the ZnO thin films. The conductivity was found to increase with film thickness.