Controlling growth and Raman spectra of individual suspended single-walled carbon nanotubes

Single-walled carbon nanotubes (SWNTs) were prepared with ethanol chemical vapor deposition (CVD) on SiO₂ flat and pillar-patterned Si substrates. The effect of CVD temperatures from 600 to 800 °C on SWNTs yields was investigated. By virtue of its unperturbed environment, an individual suspended SWNT grown between two different SiO₂ pillars provides a possibility to study the phonon band structure of SWNT itself at a single-nanotube level. Raman spectra of individual SWNTs grown between pillars were investigated systematically.     

Standing or lying C70s encapsulated in carbon nanotubes with different diameters

Single-walled carbon nanotubes (SWNTs) encapsulating C₇₀s, so-called C₇₀ peapods, were synthesized in high yield by a vapor-phase doping method. Raman spectra, high resolution transmission electron microscopy (HRTEM), and selected area electron diffraction (SAED) measurement indicate that the tube diameter is one of the important factors to determine the orientation of C₇₀ molecules inside the SWNTs. SWNTs with different diameters give different alignment of C₇₀ molecules. The lying orientation is favorable over the standing orientation in thin nanotube, i.e. 1.36 nm nanotubes, whereas the standing orientation is favorable in thick nanotubes, i.e. 1.49 and 1.61 nm nanotubes.     

Temperature and substrate dependence of structure and growth mechanism of carbon nanofiber

The carbon nanofibers were grown on Ni/Si and Ni/Ti/Si substrates in 1 atm CH₄ atmosphere at 640 °C and 700 °C by thermal chemical vapor deposition method. The carbon nanofibers were characterized by field emission scanning electron microscopy, transmission electron microscopy, and Raman spectrometry for morphology, microstructure, and crystallinity. The electron emission property of carbon nanofibers was also investigated by current-voltage (I-V) measurement. The results showed that the solid amorphous carbon nanofibers could be grown on Ni/Si substrate at 640 °C through tip growth mechanism, the carbon nanotubes could be grown on Ni/Si substrate at 700 °C through tip growth mechanism, and the carbon nanotubes could be grown on Ni/Ti/Si substrate at 700 °C through root growth mechanism.     

Effect of heat treatment on morphology, crystalline structure and photocatalysis properties of TiO2 nanotubes on Ti substrate and freestanding membrane

Highly ordered titanium oxide (TiO₂) nanotubes were prepared by electrolytic anodization of titanium electrodes. Morphological evolution and phase transformations of TiO₂ nanotubes on a Ti substrate and that of freestanding TiO₂ membranes during the calcinations process were studied by scanning electron microscopy, transmission electron microscopy, and X-ray diffraction microscopy. The detailed results and mechanisms on the morphology and crystalline structure were presented. Our results show that a compact layer exists between the tubular layer and Ti substrate at 600 °C, and the length of the nanotubes shortens dramatically at 750 °C. The freestanding membranes have many particles on their tubes during calcinations from 450 to 900 °C. The TiO₂ nanotubes on the Ti substrate transform to rutile crystals at 600 °C, while the freestanding TiO₂ membranes retain an anatase crystal with increasing temperature to 800 °C. The photocatalytic activity of TiO₂ nanotubes on a Ti substrate annealed at different temperatures was investigated by the degradation of methyl orange in aqueous solution under UV light irradiation. Due to the anatase crystals in the tubular layer and rutile crystals in the compact layer, TiO₂ nanotubes annealed at 450 °C with pure anatase crystals have a better photocatalytic activity than those annealed at 600 °C or 750 °C.     

Raman spectroscopy of SWNTs produced by a XeCl excimer laser ablation at high temperatures

Synthesis of single-wall carbon nanotubes (SWNTs) was carried out by an ablation method using a XeCl excimer laser. It was irradiated onto a graphite target containing Co and Ni at the temperatures of 1073, 1173, 1273, 1373, 1473, 1523 and 1623 K under the atmosphere (0.1 MPa) of Ar gas with the flow rate of 12 ml/min. The measurement by a scanning/transmission electron microscope and Raman spectroscopy found the formation of SWNTs with the diameter of about 1.3 nm and the length of about 2 μm in ablated carbonaceous soot. The ratio of peak intensity of 1590 cm⁻¹ (G band) to that of 1335 cm⁻¹ (D band) in the high frequency Raman spectra increased with increasing the ambient temperature. The radial breathing mode (RBM) in the low frequency Raman spectra shows that the mean diameter of SWNTs increased with increasing the ambient temperature.     

A novel continuous process for synthesis of carbon nanotubes using iron floating catalyst and MgO particles for CVD of methane in a fluidized bed reactor

A novel continuous process is used for production of carbon nanotubes (CNTs) by catalytic chemical vapor deposition (CVD) of methane on iron floating catalyst in situ deposited on MgO in a fluidized bed reactor. In the hot zone of the reactor, sublimed ferrocene vapors were contacted with MgO powder fluidized by methane feed to produce Fe/MgO catalyst in situ. An annular tube was used to enhance the ferrocene and MgO contacting efficiency. Multi-wall as well as single-wall CNTs was grown on the Fe/MgO catalyst while falling down the reactor. The CNTs were continuously collected at the bottom of the reactor, only when MgO powder was used. The annular tube enhanced the contacting efficiency and improved both the quality and quantity of CNTs.The SEM and TEM micrographs of the products reveal that the CNTs are mostly entangled bundles with diameters of about 10-20 nm. Raman spectra show that the CNTs have low amount of amorphous/defected carbon with I_G/I_D ratios as high as 10.2 for synthesis at 900 °C. The RBM Raman peaks indicate formation of single-walled carbon nanotubes (SWNTs) of 1.0-1.2 nm diameter.     

Fabrication of well-aligned CdS nanotubes by CVD-template method

Well-aligned CdS nanotubes have been synthesized within the nanochannels of the porous anodic alumina (PAA) membranes by pyrolyzing cadmium bis(diethyldithiocarbamate) [Cd(S₂CNEt₂)₂] at 400 °C. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) show that the CdS nanotubes are highly ordered with uniform diameter in range of 80-150 nm and the length up to tens of microns. X-ray diffraction (XRD), Raman spectrum, energy-dispersive spectroscopy (EDS) and selected-area electron diffraction (SAED) demonstrate that the nanotubes are composed of pure hexagonal phase polycrystalline CdS. The synthetic route can, in principle, be extended to fabricate other nanotubes of a wide range of semiconductors.     

Effects of different carbon precursors on synthesis of multiwall carbon nanotubes: Purification and Functionalization

Cyclohexanol and xylene were used as carbon precursors, for synthesis of multiwall carbon nanotubes (MWCNTs) arrays in a CVD system at temperature of 750 °C, using nitrogen as carrier gas and ferrocene as catalyst. Different characterization methods were employed to compare the MWCNTs structure synthesized by these two precursors. All scanning electron microscopy (SEM), transmission electron microscopy (TEM), thermal gravimetric analysis (TGA) and Raman spectroscopy results illustrated that using cyclohexanol could significantly reduce formation of amorphous carbon and catalyst particles in the as-grown CNTs. The less amorphous carbon can be attributed to in situ oxidation in presence of oxygen atom of cyclohexanol. Characterizations showed that MWCNTs with high purity could be obtained using cyclohexanol as carbon precursor. The as-grown MWCNTs were purified by oxidation and acid treatment. Characterization of the purified MWCNTs using HNO₃/H₂SO₄ (1/3 or 1/1), 8 M HCl or 8 M HNO₃ was carried out. The results showed that 8 M HNO₃ could be considered as the best chemical to obtain more pure MWCNTs, less amorphous and metal particles and less damaged MWCNTs. The Raman spectroscopy results demonstrated that HNO₃/H₂SO₄ (1/3) treatment could more disorder the MWCNTs structure and this was attributed to the bigger destroying effect of this acid treatment. Furthermore, the TEM analysis of MWCNTs before and after acid treatment revealed that acid treatment could remove encapsulated catalyst particles. The FTIR analysis illustrated that purification of the MWCNTs with nitric acid could connect the functional groups onto the outer surface of MWCNTs and this resulted in more dispersion of the MWCNTs in water.     

Synthesis of coiled carbon nanotubes on Co/Al2O3 catalysts in a fluidised-bed

Mixtures of regularly coiled and straight multi-walled carbon nanotubes (MWNTs) were synthesised on alumina supported Co catalysts prepared by pH controlled, wet impregnation. The synthesis reaction was performed under C₂H₂:H₂:N₂ at 750 °C in a fluidised-bed for 30 min. Scanning electron microscopy/energy dispersive X-ray spectroscopy shows good distribution of the active Co particles on the surface of the alumina support. Determined from 10 individual SEM images from the same product batch, the CNTs present are typically from 10 to 40 nm in diameter. Thermogravimetric analysis (TGA) and Raman spectroscopy indicate the total oxidative weight loss is independent of pH during catalyst preparation. This study is the first to report the use of a fluidised-bed for the synthesis of coiled MWNTs, using alumina supported Co catalysts.     

Selective hydrogenation of cinnamaldehyde to cinnamyl alcohol with carbon nanotubes supported Pt-Co catalysts

The Pt-Co catalysts supported on carbon nanotubes (CNTs) have been prepared by wet impregnation and the selective hydrogenation of cinnamaldehyde (CMA) to the corresponding cinnamyl alcohol (CMO) over the catalysts has been studied in ethanol at different reaction conditions. The results show that Pt-0.17 wt%Co/CNTs catalyst exhibits the highest activity and selectivity at a reaction temperature of 60 °C under a pressure of around 2.5 MPa, and 92.4% for the conversion of CMA and 93.6% for the selectivity of CMA to CMO, respectively. The selective hydrogenation for the CO double bond in CMA would be improved as increasing the H₂ pressure, and the selective hydrogenation for the CC double bond in CMA is enhanced as increasing the reaction temperature. In addition, these catalysts have also been characterized using transmission electron microscopy (TEM), energy dispersive X-ray spectrometry (EDS), X-ray photoelectron spectroscopy (XPS), H₂-temperature programmed reduction (H₂-TPR) and H₂-temperature programmed desorption (H₂-TPD) techniques. The results show that Pt particles are dispersed more homogeneously on the outer surface of the nanotubes, while the strong interaction between Pt and Co would improve the increasing of activated hydrogen number because of the hydrogen spillover from reduced Pt⁰ onto CNTs and increase the catalytic activity and selectivity of CMA to CMO.     

Synthesis and characterization of carbon nanotubes on carbon microfibers by floating catalyst method

In this paper, carbon nanotubes were synthesized on carbon microfibers by floating catalyst method with the pretreatment of carbon microfibers at the temperature of 1023 K, using C₂H₂ as carbon source and N₂ as carrier gas. The morphology and microstructure of carbon nanotubes were characterized by field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HRTEM). The composition of carbon nanotubes was determined by energy dispersive X-ray spectroscopy (EDX). The results showed that the surface of treated carbon microfibers was thickly covered by carbon nanotubes with diameters of about 50 nm. EDX image indicated that the composition of carbon nanotubes was carbon. In comparison with the sample grown on untreated carbon microfibers surface, it was found that after carbon microfibers were boiled in the solution of sulfur acid and nitric acid (VH₂SO₄:VHNO₃ = 1:3) and immersed in the solution of iron nitrate and xylene, carbon nanotubes with uniform density can be grown on carbon microfibers surface. Based on the results, we concluded that the pretreatment of carbon microfibers had great effect on the growth of carbon nanotubes by floating catalyst method.     

Single-wall carbon nanotube chemical attachment at platinum electrodes

Self-assembled monolayer (SAM) techniques were used to adsorb 4-aminothiophenol (4-ATP) on platinum electrodes in order to obtain an amino-terminated SAM as the base for the chemical attachment of single-wall carbon nanotubes (SWCNTs). A physico-chemical, morphological and electrochemical characterizations of SWCNTs attached onto the modified Pt electrodes was done by using reflection-absorption infrared spectroscopy (RAIR), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, scanning electron microscopy (SEM), atomic force microscopy (AFM), and cyclic voltammetry (CV) techniques. The SWNTs/4-ATP/Pt surface had regions of small, medium, and large thickness of carbon nanotubes with heights of 100-200 nm, 700 nm to 1.5 μm, and 1.0-3.0 μm, respectively. Cyclic voltammetries (CVs) in sulfuric acid demonstrated that attachment of SWNTs on 4-ATP/Pt is markedly stable, even after 30 potential cycles. CV in ruthenium hexamine was similar to bare Pt electrodes, suggesting that SWNTs assembly is similar to a closely packed microelectrode array.     

Growth of Y-junction bamboo-shaped CNx nanotubes on GaAs substrate using single feedstock

Nitrogen-doped Y-junction bamboo-shaped carbon nanotubes were synthesized by chemical vapor deposition of monoethanolamine/ferrocene mixture on GaAs substrate at 950 °C. The use of monoethanolamine as the C/N feedstock simplifies the experimental arrangement by producing ammonia during the growth process. The structure, morphology and graphitization of as-grown nitrogen-doped carbon nanotubes (CN_x) were examined by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Raman spectroscopy analysis. TEM analysis indicates that nanotubes have a bamboo-like structure. The nitrogen concentration on as-grown CN_x nanotube was found to be 7.8 at.% by X-ray photoelectron spectroscopy (XPS) analysis. XPS analysis also indicated that there are two different types of nitrogen atoms (pyridinic and graphitic) in these materials. The possible growth mechanism of formation of Y-junction CN_x nanotubes was briefly discussed. Field emission measurement suggested that as-grown CN_x nanotubes are excellent emitters with turn-on and threshold fields of 1.6 and 2.63 V/μm, respectively. The result indicated that monoethanolamine proves to be an advantageous precursor to synthesize Y-junction nitrogen-doped carbon nanotubes and such nanotubes might be an effective material to fabricate various field emission devices.     

Radial breathing modes of single-walled carbon nanotubes in resonance Raman spectra at high temperature and their chiral index assignment

Radial breathing modes (RBMs) in resonance Raman spectra from single-walled carbon nanotubes (SWCNTs) on a SiO₂/Si (0 0 1) substrate are studied between 25 and 720 °C. A change in the relative intensity of each RBM peak with temperature is observed, which originates from the temperature dependence of the resonance condition of nanotubes. For 25 °C, each RBM peak is reasonably assigned on the basis of data in the literature [J. Maultzsch, H. Telg, S. Reich, F. Hennrich, C. Thomsen, Phys. Rev. B 72 (2005) 205438]. By taking into account the temperature-dependent behavior of the relative intensity of the RBM peaks, each RBM peak is successfully assigned even for 720 °C. It is found that most of the observed RBM peaks for a laser excitation energy of E_exc = 1.96 eV are from chiral SWCNTs. These results make it possible to discuss further details of the chirality-dependent growth behavior observed for in situ Raman spectroscopy.     

Effect of Ni, Pd and Ni-Pd nano-islands on morphology and structure of multi-wall carbon nanotubes

In this research, the effect of Ni, Pd and Ni-Pd catalysts have studied on morphology and structure of synthesized multi-wall carbon nanotubes (MWCNTs). Initially, thin films of Ni (with two thicknesses of 10 and 20 nm), Pd/Ni (5/10 nm) and Pd (10 nm) were deposited as catalysts on SiO₂ (60 nm)/Si(1 0 0) substrates, using dc magnetron sputtering technique. The deposited films were annealed at 900 °C in ammonia environment for 45 min, in order to obtain nano-structured catalyst on the surface. Using scanning electron microscopy (SEM), the average size of Ni nano-islands (synthesized by the 10 and 20 nm Ni films), Pd and Ni-Pd nano-islands were measured about 55, 110, 45 and 50 nm, respectively. According to X-ray photoelectron spectroscopy analysis (XPS), the ratio of Ni/Pd on the surface was about 3 for the bilayer sample. The CNTs were synthesized on the nano-island catalysts at 940 °C in CH₄ ambient using a thermal chemical vapor deposition method. The results revealed that average diameter of the CNTs were about 70, 110, 120 nm for Ni, Ni-Pd and Pd catalysts, respectively. Raman spectra of the MWCNTs showed that intensity ratio of two main peaks located in the range of 1550-1600 and 1250-1450 cm⁻¹ (as a quality factor for the CNTs) for Ni, Pd and Ni-Pd catalysts were 1.42, 0.91 and 0.85, respectively. Therefore, based on our data analysis, although addition of Pd to Ni catalyst caused a considerable reduction in the quality of the grown MWCNTs as compared to the pure Ni catalyst, but it resulted in an enhancement in the methane decomposition rate. For the pure Pd catalyst samples, both a slow methane decomposition rate as compared with Ni-Pd catalyst samples and a poor quality of CNTs were observed as compared with the Ni catalyst, under similar experimental conditions.     

Effect of cobalt doping and annealing on properties of titania thin films prepared by sol-gel process

Undoped and cobalt doped titania (TiO₂) thin films have been prepared on Si(1 0 0) monocrystal and quartz substrate using the sol-gel deposition method and annealed in air at 450, 550, 650, 750, 850, 950 and 1050 °C. Several experimental techniques (AFM, XRD, Raman spectroscopy, XRR, EDX, XPS, XAS, UV-VIS spectroscopy) have been used to characterize these films. Further more the degree of light induced hydrophilicity was estimated by measuring the contact angle of a water droplet on the film. Increase of the annealing temperature and in smaller degree also cobalt doping predispose titania crystallite growth. The rutile phase was detected at lower temperatures in the cobalt doped films than in the undoped titania films. Cobalt in the cobalt doped TiO₂ was seen to be in Co²⁺ oxidation state, mainly in CoTiO₃ phase when films were annealed at temperatures higher than 650 °C. Cobalt compounds segregated into the sub-surface region and to the surface of the titania, where they formed islands. Cobalt doping red-shifted the fundamental absorption edge further into the visible range, however it did not enhance the light induced hydrophilicity of the thin film surface as compared to the undoped titania thin films.     

Investigation of thermal annealing effects on microstructural and optical properties of HfO2 thin films

In the present paper, we investigate the effect of thermal annealing on optical and microstructural properties of HfO₂ thin films (from 20 to 190 nm) obtained by plasma ion assisted deposition (PIAD). After deposition, the HfO₂ films were annealed in N₂ ambient for 3 h at 300, 350, 450, 500 and 750 °C. Several characterisation techniques including X-ray reflectometry (XRR), X-ray diffraction (XRD), spectroscopic ellipsometry (SE), UV Raman and FTIR were used for the physical characterisation of the as-deposited and annealed HfO₂ thin films. The results indicate that as-deposited PIAD HfO₂ films are mainly amorphous and a transition to a crystalline phase occurs at a temperature higher than 450 °C depending on the layer thickness. The crystalline grains consist of cubic and monoclinic phases already classified in literature but this work provides the first evidence of amorphous-cubic phase transition at a temperature as low as 500 °C. According to SE, XRR and FTIR results, an increase in the interfacial layer thickness can be observed only for high temperature annealing. The SE results show that the amorphous phase of HfO₂ (in 20 nm thick samples) has an optical bandgap of 5.51 eV. Following its transition to a crystalline phase upon annealing at 750 °C, the optical bandgap increases to 5.85 eV.     

Ordered mesoporous silica materials (SBA-15) with good heat-resistant magnetism

A series of highly ordered mesoporous materials (CF-SBA-15) with heat-resistant magnetism have been successfully prepared from impregnation of cobalt salt, iron salt, and citric acid with as-synthesized SBA-15. XRD and N₂ isotherms indicate that these materials have highly ordered hexagonal mesoporous symmetry and open pore systems. The measurement of magnetic property shows that these materials are ferromagnetic even if calcined at 550 °C for 10 h in air, indicating their good heat-resistant magnetism. These results would be very important for recycle and regeneration of adsorbents and catalysts in practical applications. Moreover, this method may be useful for other mesoporous materials with thermally stable magnetism from a combination of other mesoporous materials such as MCM-41 with magnetic nanoparticles of MnFe₂O₄ and NiFe₂O₄.     

Nano- and micro-powder of zirconia and ceria-supported cobalt catalysts for the steam reforming of bio-ethanol

The usefulness of nano- and micro-powders of ceria and zirconia as a support of the cobalt-based catalyst as well as additional modification of zirconia-supported cobalt catalysts with cerium for the production of hydrogen in the steam reforming of bio-ethanol (SRE) for fuel cell applications was studied. It was found that mainly different structural features of the nano- and micro-powder of ceria- and zirconia-supported cobalt catalysts are higher cobalt surface area and much smaller average sizes of cobalt crystallites for the catalysts with high-dispersed support. Similarly, the presence of high-dispersed ceria introduced to the zirconia-supported catalysts simultaneously with the deposition of cobalt increases their total and active surface area as well as decreases the size of cobalt crystallites, regardless of the initial dispersion of zirconia support. The results of the temperature-programmed reduction and the temperature-programmed desorption of hydrogen showed that small crystallites of the cobalt phase strongly interact with high-dispersed ceria.Ceria has a great influence on the effects of the SRE. For the nano-powder ceria-supported cobalt catalyst and for the nano-powder zirconia-supported catalysts with the cobalt-ceria active phase the yield of hydrogen formed from one molecule of ethanol supplied to the SRE process was the highest; even at the relatively low temperature of 420 °C it is close to 5.5 mol H₂/mol EtOH. At the same time there were achieved: complete conversion of ethanol, very close to that of water and 92%, 81-84%, 5-6% selectivities to hydrogen, carbon dioxide and carbon monoxide, respectively.     

Hydrogen adsorption on activated carbon nanotubes with an atomic-sized vanadium catalyst investigated by electrical resistance measurements

Activated multi-walled carbon nanotubes were prepared with appended vanadium as a hydrogen storage medium. The pore structure was significantly improved by an activation process that was studied using Raman spectroscopy, field emission transmission electron microscopy and pore analysis techniques. X-ray photoelectron spectroscopy and X-ray diffraction results reveal that the vanadium catalyst was introduced into the carbon nanotubes in controlled proportions, forming V₈C₇. The improved pore structure functioned as a path through the carbon nanotubes that encouraged hydrogen molecule adsorption, and the introduced vanadium catalyst led to high levels of hydrogen storage through the dissociation of hydrogen molecules via the spill-over phenomenon. The hydrogen storage behavior was investigated by electrical resistance measurements for the hydrogen adsorbed on a prepared sample. The proposed mechanism of hydrogen storage suggests that the vanadium catalyst increases not only the amount of hydrogen that is stored but also the speed at which it is stored. A hydrogen storage capacity of 2.26 wt.% was achieved with the activation effects and the vanadium catalyst at 30 °C and 10 MPa.