Effects of CPII implantation on the characteristics of diamond-like carbon films

A diamond-like carbon film (DLC) was successfully synthesized using a hybrid PVD process, involving a filter arc deposition source (FAD) and a carbon plasma ion implanter (CPII). A quarter-torus plasma duct filter markedly reduced the density of the macro-particles. Graphite targets were used in FAD. Large electron and ion energies generated from the plasma duct facilitate the activation of carbon plasma and the deposition of high-quality DLC films. M2 tool steel was pre-implanted with 45 kV carbon ions before the DLC was deposited to enhance the adhesive and surface properties of the film. The ion mixing effect, the induction of residual stress and the phase transformation at the interface were significantly improved. The hardness of the DLC increased to 47.7 GPa and 56.5 GPa, and the wear life was prolonged to over 70 km with implantation fluences of 1 × 10¹⁷ ions/cm² and 2 × 10¹⁷ ions/cm², respectively.     

Nanoindentation measurements on modified diamond-like carbon thin films

In the present study, we explored the effect of metallic interlayers (Cu and Ti) and indentation loads (5-20 mN) on the mechanical properties of plasma produced diamond-like carbon (DLC) thin films. Also a comparison has been made for mechanical properties of these films with pure DLC and nitrogen incorporated DLC films. Introduction of N in DLC led to a drastic decrease in residual stress (S) from 1.8 to 0.7 GPa, but with expenses of hardness (H) and other mechanical properties. In contrast, addition of Cu and Ti interlayers between substrate Si and DLC, results in significant decrease in S with little enhancement of hardness and other mechanical properties. Among various DLC films, maximum hardness 30.8 GPa is observed in Ti-DLC film. Besides hardness and elastic modulus, various other mechanical parameters have also been estimated using load versus displacement curves.     

The effect of applied negative bias voltage on the structure of Ti-doped a-C:H films deposited by FCVA

Ti-doped hydrogenated diamond-like carbon (DLC) films were deposited on Si(1 0 0) substrates by a filtered cathodic vacuum arc (FCVA) method using Ar and CH₄ as the feedstock. The composition and microstructure of the films were investigated by Raman spectroscopy, X-ray photoelectron spectroscopy and IR spectroscopy. The internal stress was determined by the radius of curvature technique. The influence of the bias voltage on the microstructure of the as-deposited films was investigated. It was found that the graphite-like bonds was dominated in the Ti-doped DLC film deposited at 0 V bias voltage. When bias voltage was increased to −150 V, more diamond-like bond were produced and the sp³ content in film reached the maximum value, after which it decreased and more graphite-like bonds feature produced with further increase of the negative bias voltage. The compressive internal in the Ti-doped DLC films also exhibited a maximum value at −150 V bias voltage. IR results indicated that CH bonded intensity reduced, and H atoms bonded with C atoms were substituted for the Ti atoms as the negative bias voltage increasing. All the composition and microstructure change can be explained by considering the plasma conditions and the effect of negative bias voltage applied to the substrate.     

Quantification of oxygenated species on a diamond-like carbon (DLC) surface

This paper discusses the use of chemical derivatization methods for surface chemical composition analysis of diamond-like carbon (DLC) films synthesized through plasma-enhanced chemical vapor deposition with X-ray photoelectron spectroscopy (XPS). The main challenge in applying chemical derivatization reactions for titration of organic functional groups on the DLC surface is that sub-surface oxygenated species are not accessible to the derivatizing agent. As a simple approximation, a functional group that can be quantified unambiguously with XPS can be used as an internal reference to estimate the accessible-to-inaccessible ratio, and this information can be used to estimate the total amount of other functional groups from the chemical-derivatization-assisted XPS analysis. The use of this principle to obtain the surface composition of hydroxyl, ether, carbonyl, and carboxyl groups in the oxidized surface region of the DLC film was demonstrated.     

Diamond-like carbon films deposited by a hybrid ECRCVD system

A novel hybrid technique for diamond-like carbon (DLC) film deposition has been developed. This technique combines the electron cyclotron resonance chemical vapor deposition (ECRCVD) of C₂H₂ and metallic magnetron sputtering. Here we described how DLC film is used for a variety of applications such as stamper, PCB micro-tools, and threading form-tools by taking advantage of hybrid ECRCVD system. The structure of the DLC films is delineated by a function of bias voltages by Raman spectroscopy. This function includes parameters such as dependence of G peak positions and the intensity ratio (I_D/I_G). Atomic force microscope (AFM) examines the root-mean-square (R.M.S.) roughness and the surface morphology. Excellent adhesion and lower friction coefficients of a DLC film were also assessed.     

Studies of diamond-like carbon （DLC） films deposited on stainless steel substrate with Si/SiC intermediate layers

In this work, diamond-like carbon （DLC） films were deposited on stainless steel substrates with Si/SiC intermediate layers by combining plasma enhanced sputtering physical vapour deposition （PEUMS-PVD） and microwave electron cyclotron resonance plasma enhanced chemical vapour deposition （MW-ECRPECVD） techniques. The influence of substrate negative self-bias voltage and Si target power on the structure and nano-mechanical behaviour of the DLC films were investigated by Raman spectroscopy, nano-indentation, and the film structural morphology by atomic force microscopy （AFM）. With the increase of deposition bias voltage, the G band shifted to higher wave-number and the integrated intensity ratio ID/IG increased. We considered these as evidences for the development of graphitization in the films. As the substrate negative self-bias voltage increased, particle bombardment function was enhanced and the sp^3-bond carbon density reducing, resulted in the peak values of hardness （H） and elastic modulus （E）. Silicon addition promoted the formation of sp^3 bonding and reduced the hardness. The incorporated Si atoms substituted sp^2- bond carbon atoms in ring structures, which promoted the formation of sp^3-bond. The structural transition from C-C to C-Si bonds resulted in relaxation of the residual stress which led to the decrease of internal stress and hardness. The results of AFM indicated that the films was dense and homogeneous, the roughness of the films was decreased due to the increase of substrate negative self-bias voltage and the Si target power.     

Ordered ultra thin ZnO films on metal substrate

Ultra thin ZnO films were prepared on metal Mo(1 1 0) substrate under ultrahigh vacuum conditions either by depositing Zn in 10⁻⁵ Pa oxygen or by oxidizing pre-deposited Zn films. The films were characterized in situ by various surface analytical techniques, including Auger electron spectroscopy, X-ray and ultraviolet photoelectron spectroscopies, low energy electron diffraction and high resolution electron energy loss spectroscopy. The results indicate that a long-range ordered and stoichiometric ZnO films are formed along its [0 0 0 1] direction. The annealing experiments show that as-prepared ZnO films are thermal stable until 800 K. This study provides constructive information to further understand the growth mechanism of ZnO films on different substrates.     

不同能级加速过滤电弧沉积四面体非晶碳膜的结构和性能

采用过滤阴极真空电弧技术，通过施加0—2000 V衬底负偏压使沉积离子获得不同能级的入射能量，在单晶硅上制备了四面体非晶碳薄膜.拉曼光谱分析表明，薄膜的结构为非晶sp³骨架中镶嵌着平面关联长度小于1 nm的sp²团簇.原子力显微镜研究表明：在低能级、富sp³能量窗口和次高能级，薄膜中sp³的含量越多，其表面就越光滑，应用sp³浅注入生长机制能够圆满地解释薄膜表面形态与离子入射能量之间的关系；但在高 关键词： 四面体非晶碳 过滤阴极真空电弧 能级     

Influence of Si substrate preparation on surface chemistry and morphology of L-CVD SnO2 thin films studied by XPS and AFM

Results of experimental studies of the influence of substrate preparation on the surface chemistry and surface morphology of the laser-assisted chemical vapour deposition (L-CVD) SnO₂ thin films are presented in this paper. The native Si(1 0 0) substrate cleaned by UHV thermal annealing (TA) as well as thermally oxidized Si(1 0 0) substrate cleaned by ion bombardment (IBA) have been used as the substrates. X-ray photoemission spectroscopy (XPS) has been used for the control of surface chemistry of the substrates as well as of deposited films. Atomic force microscopy (AFM) has been used to control the surface morphology of the L-CVD SnO₂ thin films deposited on differently prepared substrates. Our XPS shows that the L-CVD SnO₂ thin films deposited on thermally oxidized Si(1 0 0) substrate after cleaning with ion bombardment exhibit the same stoichiometry, i.e. ratio [O]/[Sn] = 1.30 as that of the layers deposited on Si(1 0 0) substrate previously cleaned by UHV prolonged heating. AFM shows that L-CVD SnO₂ thin films deposited on thermally oxidized Si(1 0 0) substrate after cleaning with ion bombardment exhibit evidently increasing rough surface topography with respect to roughness, grain size range and maximum grain height as the L-CVD SnO₂ thin films deposited on atomically clean Si substrate at the same surface chemistry (nonstoichiometry) reflect the higher substrate roughness after cleaning with ion bombardment.     

Formation of diamond-like carbon (DLC) film on the NiTi alloys via plasma immersion ion implantation and deposition (PIIID) for improving corrosion resistance

NiTi alloys are potentially useful in biomedical application due to their unique superelasticity and shape memory effect. However, the materials are vulnerable to surface corrosion and the most serious issue is out-diffusion of toxic Ni ions from the substrate into body tissues and fluids. In this paper, Diamond-like carbon (DLC) film is fabricated on the NiTi alloys using plasma immersion ion implantation and deposition (PIIID) at room temperature to improve their corrosion resistance and block the out-diffusion of the Ni ions. The results show that the DLC films cannot only improve the corrosion resistance of the NiTi substrate, but also effectively suppress the Ni ions release from the substrate. The reason that the corrosion resistance of the coated samples is markedly improved due to the DLC films formation is systematically investigated.     

Study of porous carbon thin films produced by pulsed laser deposition

Amorphous carbon is an interesting material and its properties can be varied by tuning its diamond-like (sp³) fractions. The diamond-like fractions in an amorphous carbon films depends on the kinetic energy of the deposited carbon ions. Porous amorphous carbon thin films were deposited onto silicon substrates at room temperature in a vacuum chamber by Glancing Angle Pulsed Laser Deposition (GAPLD). Krypton fluoride (248 nm) laser pulses with duration of 15 ns and intensities of 1-20 GW/cm² were used. In GAPLD, the angles between the substrate normal and the trajectory of the incident deposition flux are set to be almost 90°. Porous thin films consisting of carbon nanowires with diameters less than 100 nm were formed due to a self-shadowing effect. The kinetic energies of the deposited ions, the deposition rate of the films and the size of the nanowires were investigated. The sp³ fraction of the porous carbon films produced at intensity around 20 GW/cm² were estimated from their Raman spectra.     

磁过滤器电流对非晶碳薄膜摩擦学特性影响的研究

研究了过滤阴极真空电弧技术中,不同的磁过滤器电流下(5—13 A),制备的四面体非晶碳(ta-C)薄膜对摩擦学特性的影响.通过对薄膜厚度,薄膜结构以及薄膜表面粗糙度随磁过滤电流的变化结果进行了测试,结果表明,随着磁过滤器电流的增大,薄膜的sp³键含量逐渐减少,表面粗糙度从0.13增大到0.38.磁过滤器电流在5 A时,薄膜的摩擦系数最小约为0.08,当电流增大到7 A时,摩擦系数显著增大,磁过滤器电流从7 A增大到13 A时,薄膜的摩擦系数再次减小约为0.1. 关键词： 四面体非晶碳 过滤阴极真空电弧 磁过滤器电流 摩擦系数     

Design and fabrication of ultra broadband infrared antireflection hard coatings on ZnSe in the range from 2 to 16 μm

In conventional infrared multilayer antireflection coatings (MLAR) materials of fluoride and chalcogenide types are used, which are disadvantaged due to their low mechanical strength and poor stability against humidity and environmental impacts. In this paper, we show that high performance ultra broadband and hard infrared multilayer antireflection coatings on ZnSe substrates in the wavelength range from 2 to 16 μm can be designed and fabricated. Diamond-like carbon (DLC) hard coating as a mechanical and environmental protection layer was proposed and deposited onto MLAR surfaces (MLAR + DLC) using a pulsed vacuum arc ion deposition technique. The thickness of the high optical quality DLC can be optimized in the design simulation to achieve a practically best antireflection and surface protection performance. We show that a germanium thin film (15 nm) between the MLAR and DLC surfaces can be used as a transition layer for optical and material match. The average transmission of the fabricated MLAR+DLC surfaces was 93.1% in the wavelength range between 2 and 16 μm. The peak transmission was about 97.6%, close to the simulated values. The durability and stability against mechanical impacts and environmental tests was improved significantly compared with the conventional infrared windows.     

Low-temperature deposited ZnO thin films on the flexible substrate by cathodic vacuum arc technology

In this paper, un-doped zinc oxide (ZnO) films with various thicknesses (150, 250, 350, 450 and 550 nm) were successfully prepared onto PET substrates using cathodic vacuum arc technique at low-temperature (<40 °C). Their microstructure, optical and electrical properties were investigated and discussed. The films showed (0 0 2) peaks, an average transmittance over 80% in the visible region. Calculated values of the band gap are around 3.29-3.33 eV when the film thickness increased, indicating a slight blue shift of optical transmission spectra. The lowest resistivity about 5.26 × 10⁻³ Ω cm could be achieved for the un-doped ZnO film with thickness of 550 nm.     

Thermal stability of ultrathin amorphous carbon films synthesized by plasma-enhanced chemical vapor deposition and filtered cathodic vacuum arc

Abstract

Ultrathin hydrogenated amorphous carbon (a-C:H) films deposited by plasma-enhanced chemical vapor deposition (PECVD) and hydrogen-free amorphous carbon (a-C) films of similar thickness deposited by filtered cathodic vacuum arc (FCVA) were subjected to rapid thermal annealing (RTA). Cross-sectional transmission electron microscopy (TEM) and electron energy loss spectroscopy (EELS) were used to study the structural stability of the films. While RTA increased the thickness of the intermixing layer and decreased the sp³ content of the a-C:H films, it did not affect the thickness or the sp³ content of the a-C films. The superior structural stability of the FCVA a-C films compared with PECVD a-C:H films, demonstrated by the TEM and EELS results of this study, illustrates the high potential of these films as protective overcoats in applications where rapid heating is critical to the device functionality and performance, such as heat-assisted magnetic recording.     

Low energy repetitive miniature plasma focus device as high deposition rate facility for synthesis of DLC thin films

Diamond-like carbon (DLC) films were deposited on Si (1 0 0) substrate using a low energy (219 J) repetitive (1 Hz) miniature plasma focus device. DLC thin film samples were deposited using 10, 20, 50, 100 and 200 focus shots with hydrogen as filling gas at 0.25 mbar. The deposited samples were analyzed by XRD, Raman Spectroscopy, SEM and XPS. XRD results exhibited the diffraction peaks related to SiO₂, carbon and SiC. Raman studies verified the formation amorphous carbon with D and G peaks. Corresponding variation in the line width (FWHM) of the D and G positions along with change in intensity ratio (I_D/I_G) in DLC films was investigated as a function of number of deposition shots. XPS confirmed the formation sp² (graphite like) and sp³ (diamond like) carbon. The cross-sectional SEM images establish the 220 W repetitive miniature plasma focus device as the high deposition rate facility for DLC with average deposition rate of about 250 nm/min.     

Anomalous scaling in surface roughness evaluation of electrodeposited nanocrystalline Pt thin films

Atomic force microscopy (AFM) is used to measure the surface roughness of crystalline Pt thin films as a function of film thickness and growth rate. Our films were electrodeposited on Au/Cr/glass substrates, under galvanostatic control (constant current density), from a single electrolyte containing Pt⁴⁺ ions. Crystalline structure of the films was confirmed by X-ray diffraction (XRD) technique. The effect of growth rate (deposition current density) and film thickness (deposition time) on the kinetic roughening of the films were studied using AFM and roughness calculation. The data is consistent with a rather complex behaviour known as “anomalous scaling” where both local and large scale roughnesses show power law dependence on the film thickness.     

Surface roughness characterization of Al-doped zinc oxide thin films using rapid optical measurement

Transparent conductive oxide thin films have been widely investigated in photoelectric devices such as flat panel display (FPD) and solar cells. Al-doped zinc oxide (AZO) thin films have been widely employed in FPD. Measuring the surface roughness of AZO thin films is important before the manufacturing of photoelectric device using AZO thin films because surface roughness of AZO thin films will significantly affect the performance of photoelectric device. Traditional methods to measure surface roughness of AZO thin films are scanning electron microscopy and atomic force microscopy. The disadvantages of these approaches include long lead time and slow measurement speed. To solve this problem, an optical inspection system for rapid measurement of the surface roughness of AZO thin films is developed in this study. It is found that the incident angle of 60° is a good candidate to measure the surface roughness of AZO thin films. Based on the trend equation y=−3.6483x+2.1409, the surface roughness of AZO thin films (y) can be directly deduced from the peak power density (x) using the optical inspection system developed. The maximum measurement-error rate of the optical inspection system developed is less than 8.7%.The saving in inspection time of the surface roughness of AZO thin films is up to 83%.     

Effect of pulsed bias on the properties of ZrN/TiZrN films deposited by a cathodic vacuum arc

ZrN/TiZrN multilayers are deposited by using the cathodic vacuum arc method with different substrate bias(from 0 to 800 V),using Ti and Zr plasma flows in residual N 2 atmosphere,combined with ion bombardment of sample surfaces.The effect of pulsed bias on the structure and properties of films is investigated.Microstructure of the coating is analyzed by X-ray diffraction(XRD),and scanning electron microscopy(SEM).In addition,nanohardness,Young’s modulus,and scratch tests are performed.The experimental results show that the films exhibit a nanoscale multilayer structure consisting of TiZrN and ZrN phases.Solid solutions are formed for component TiZrN films.The dominant preferred orientation of TiZrN films is(111) and(220).At a pulsed bias of 200 V,the nanohardness and the adhesion strength of the ZrN/TiZrN multilayer reach a maximum of 38 GPa,and 78 N,respectively.The ZrN/TiZrN multilayer demonstrates an enhanced nanohardness compared with binary TiN and ZrN films deposited under equivalent conditions.     

Argon-dominated plasma beam generated by filtered vacuum arc and its substrate etching

A new technique to etch a substrate as a pre-treatment prior to functional film deposition was developed using a filtered vacuum arc plasma. An Ar-dominated plasma beam was generated from filtered carbon arc plasma by introducing appropriate flow rate of Ar gas in a T-shape filtered arc deposition (T-FAD) system. The radiation spectra emitted from the filtered plasma beam in front of a substrate table were measured. The substrate was etched by the Ar-dominated plasma beam. The principal results are summarized as follows. At a high flow rate of Ar gas (50 ml/min), when the bias was applied to the substrate, the plasma was attracted toward the substrate table and the substrate was well etched without film formation on the substrate. Super hard alloy (WC), bearing steel (SUJ2), and Si wafer were etched by the Ar-dominated plasma beam. The etching rate was dependent on the kind of substrate. The roughness of the substrate increased, when the etching rate was high. A pulse bias etched the substrate without roughening the substrate surface excessively.