Investigation of recombination and trapping processes in 3As2Se32Sb2Se3 amorphous films by photoconductivity method

Photoconductivity experiment has been performed on high resistivity ($\text{π ? 10}{}^9\text{Ω-}\text{cm}$) 3As₂Se₃2Sb₂Se₃ amorphous films in the temperature range from 278°K to 308°K, as a function of light intensity, I₀. The results are that at intermediate light levels the photocurrent varies as I₀^0.7 and at high light levels the photocurrent is directly proportional to I₀. A simple recombination and trapping model is developed to interpret the observed photoconductivity data. From the temperature dependence of the photocurrent, an effective trap level located 0.3 eV below the band edge is deduced.     

X-ray investigation of the crystallization of chalcogenide glasses of the type (As2Se3)1−x:(Tl2Se)x

Amorphous and crystalline states of As₂Se₃, (As₂Se₃)₃ : Tl₂Se and As₂Se₃ : Tl₂Se have been studied using X-ray diffraction techniques. Structural changes arise during the process of annealing in the temperature range between their softening and melting points are reported and their rates investigated. The crystallization temperatures were found to be 105 ± 5 °C, 135 ± 5 °C and 180 ± 5 °C respectively. The unit cell parameters are identified for each of the three resulting crystalline phases, that for As₂Se₃ : Tl₂Se being orthorhombic while the other two are monoclinic.     

Devitrification characteristics of GexSe1−x glasses

Amorphous Ge_xSe_1?x compounds have been prepared and carefully characterized in the range 0 ? x ? 0.43 (density and micro-hardness measurements and DTA experiments). By heating samples from the amorphous phase, the crystallization process has been investigated for 0.15 ? x ? 0.30. An immiscibility gap in the vitreous region is determined by optical microscopy, from phase-separation observations; moreover, a new metastable crystalline phase appearing as an intermediate step between phase separation and stable GeSe₂ is described.     

Photoconductivity of oxychalcogenide glasses in the system As2Se3CdO

The photoconductivity of oxychalcogenide glasses in the system As₂Se₃CdO was investigated. When 2–3 mol % CdO was added, the photoresponse peak of the parent glass As₂Se₃ in the vicinity of 740 nm became broader and a little weaker. The addition of more than about 4 mol % CdO brought about a sharp and strong peak at 720 nm and a broad peak at 860 nm. X-ray diffraction and electron microscopic observations revealed the presence of crystalline CdSe in the glass matrix, indicating that the reaction As₂Se₃ + 3CdO → As₂O₃ + 3CdSe took place in the melting process of these glasses. Tempeature and light intensity dependences of the photocurrent lead to the conclusion that the above spectral photoresponse is greatly affected by the presence of the dispersed crystalline CdSe.     

中远红外非线性光学晶体AgGaS2、AgGaSe2和AgGa1-xInxSe2研究进展

综合报道了本实验室关于黄铜矿类I-III-VI2型系列晶体的研究进展。采用两温区气相输运温度振荡法合成出高纯、单相、致密的多晶材料,在三温区立式炉中用坩埚旋转下降法生长出AgGaS2、AgGaSe2和AgGa1-xInxSe2等系列单晶体,X射线单晶衍射谱和回摆谱表明晶体的结晶性好,结构完整;红外透过率接近理论值,吸收系数低于0.017 cm-1,表明生长的晶体光学质量高。研究出一种新的能对AgGa1-xInxSe2晶体(112)晶面进行择优腐蚀的腐蚀剂:(30 g CrO3+10 mL H2O)∶H4PO4(85%)∶HNO3(65～68%)∶HF(40%)=10∶10∶10∶2(体积比),在60℃下腐蚀40 min,能够清晰地显示出AgGa1-xInxSe2晶体(112)面取向一致的三角形腐蚀坑,边界清晰,蚀坑密度大约为105/cm2数量级。采用自行研制的晶体定向切割新方法,加工出AgGa1-xInxSe2-OPO器件,获得了3～5μm的激光输出,光-光转换效率达21%。     

ac Conductivity of 4.5 TiO2−x · 2 P2O5

The ac conductivity of a member of the family of glasses 4.5 TiO_2?x · 2 P₂O₅ has been measured between 77 and 300 K, and up to 100 kHz. The dc conductivity was measured over only part of this temperature range. The measured ac conductivity can be represented by σ_ac = σ₀ + σ₁ω^s, with s < 1, and temperature dependent. A similar equation describes the ac dielectric constant, ?_ac = ?₀ + ?₁ω^s?1, where $\text{?}{}_1\text{= σ}{}_1\text{tan}\text{1}\text{2}\text{sπ}$. A simple proportionality of s to temperature holds at low temperature; at the higher temperatures, the T-dependence of s is no longer simple. The observed behaviour of the ac properties of this glass is in general accordance with a recently proposed model for systems where transport occurs by hopping. The over-all behaviour is comparable to other transition metal glasses.Using the model and treating the carriers as polarons yields an expression for s in terms of temperature. Values for the polaron radius and the effective dielectric constant are then extracted from the measurements. These values are in good agreement with values for similar systems obtained by other means.     

二维层状In2Se3材料的快速制备及结构特性研究

In₂Se₃二维层状材料具有优异的光电、热电和铁电特性。目前In₂Se₃二维层状材料大部分通过对化学气相输运(CVT)法制备的块体In₂Se₃进行机械剥离获得，CVT法制备工艺复杂、制备时间长、成本高，与之相比，布里奇曼(B-S)法具有制备工艺简单、制备效率高、成本低的优势。为此，本文对CVT法和B-S法制备的块体In₂Se₃分别进行了机械剥离，并转移到SiO₂/Si(111)基底，获得了相应的二维层状In₂Se₃样品。同时利用原子力显微镜(AFM)、激光拉曼和X射线衍射(XRD)对两样品进行表面形貌、晶格振动谱和结晶质量的测量，发现用B-S法制备、剥离的样品具有与CVT法制备、剥离样品几乎相同的表面原子级平整度和单晶结晶质量。本文为高质量二维层状In₂Se₃材料的获得提供了更为经济实用的途径。     

Structure, thermal, and infrared analyses of [NH3(CH2)3NH3]2[Ni(HP2O7)2(H2O)2] ? 4H2O

[NH₃(CH₂)₃NH₃]₂[Ni(HP₂O₇)₂(H₂O)₂] 4H₂O (NiDAP) is a new diphosphate of transition metallic and organic cations obtained from a mixture of H₄P₂O₇, 2NiCO₃ Ni(OH)₂ 4H₂O and NH₂(CH₂)₃NH₂ in a 1:1/6:1 molar ratio. This mixed organo-mineral compound crystallizes in the triclinic system, P¯, with the unit cell dimensions: a = 7.3678(3)~Å, b = 7.8018(5)Å, c = 11.1958(7)Å, = 76.914(4), = 81.052(4), = 85.46(1), V = 618.57(6)ų and Z = 1. The crystal structure of NiDAP consists of a complex anion, [Ni(HP₂O₇)₂(H₂O)₂]^4– and a diammoniumpropane cation. The complex anion is built up from two neutral water molecules (OW1) and two diphosphosphoric anions coordinated to Ni(II) in a bidentate chelating manner. (OW1) molecules link anionic complexes, [Ni(HP₂O₇)₂(H₂O)₂]^4– to create a thick bidimensional layers parallel to the (a, b) plane. These layers are interconnected in three dimensions through hydrogen bonds established between organic cations, the remaining water molecules OW2, OW3, and some external oxygen atoms of the anionic complex arrays. NiDAP was also characterized by IR spectroscopy, TG-DTA, and DSC analyses.     

Glass formation and structure of glasses in B2O3―Bi2O3―MoO3 system

The purpose of this paper is to study the glass formation tendency in the ternary system B₂O₃―Bi₂O₃―MoO₃ and to define the main structural units building the amorphous network. A wide glass formation area was determined which is situated near the Bi₂O₃―B₂O₃ side. A liquid phase separation region was observed near the MoO₃―B₂O₃ side for compositions containing below 25 mol% Bi₂O₃ and their microheterogeneous structure was observed by SEM. The phase formation was characterized by X-ray diffraction (XRD). By DTA was established the glass transition temperature (T_g) in the range of 380-420 °C and crystallization temperature (T_x) vary between 420 and 540 °C. The main building units forming the amorphous network are BO₃ (1270 and 1200 cm^− 1), BO₄ (930-880, 1050-1040 cm^− 1), MoO₄ (840-760 cm^− 1) and BiO₆ (470 cm^− 1). It was proved that Bi₂O₃ favors the BO₃ → BO₄ transformations while MoO₃ preserves BO₃ units in the amorphous network.     

Synthesis and structure of {NH2(C2H5)2}2[(UO2)2(C2O4)(CH3COO)4] · 2H2O

Single crystals of the compound {NH₂(C₂H₅)₂}₂[(UO₂)₂C₂O₄(CH₃COO)₄] · 2H₂O (I) are synthesized, and their structure is investigated using X-ray diffraction. Compound I crystallizes in the monoclinic system with the unit cell parameters a = 9.210(2) ?, b = 14.321(3) ?, c = 12.659(3) ?, β = 105.465(13)°, V = 1609.2(6) ?³, space group P2₁/c, Z = 2, and R = 0.0198. The structural units of crystals I are binuclear groups of the composition [(UO₂)₂C₂O₄(CH₃COO)₄]²⁻ with an island structure, which belong to the crystal-chemical group A ₂ K ⁰² B ₄⁰¹ (A = UO₂²⁺, K ⁰² = C₂O₄²⁻, B ⁰¹ = CH₃COO⁻) of the uranyl complexes, diethylammonium cations, and water molecules. The uranium-containing groups are joined into a three-dimensional framework through electrostatic interactions with diethylammonium cations and a system of hydrogen bonds, which are formed with the participation of the atoms involved in the composition of the water molecules, oxalate ions, acetate ions, and diethylammonium cations. Original Russian Text ? L.B. Serezhkina, A.V. Vologzhanina, N.A. Neklyudova, V.N. Serezhkin, 2009, published in Kristallografiya, 2009, Vol. 54, No. 1, pp. 65–67.     

Synthesis and structure of K2[(UO2)4(O)2(OH)2(C2O4)(CH3COO)2(H2O)2]·2H2O

Single crystals of the compound K₂[(UO₂)₄(O)₂(OH)₂(C₂O₄)(CH₃COO)₂(H₂O)₂]·2H₂O (I) are synthesized, and their structure is investigated using X-ray diffraction. Crystals of compound I belong to the triclinic system with the unit cell parameters a = 7.6777(6) ?, b = 7.9149(7) ?, c = 10.8729(9) ?, α = 72.379(2)°, β = 86.430(3)°, γ = 87.635(2)°, V = 628.33(9) ?³, space group P , Z = 1, and R ₁ = 0.0323. The main structural units of the crystals are [(UO₂)₄(O)₂(OH)₂(C₂O₄)(CH₃COO)₂(H₂O)₂]²⁻ chains, which belong to the crystal-chemical group A ₄ M ₂³ M ₂² K ⁰² B ₂⁰¹ M ₂¹ (A = UO₂²⁺, M ³ = O²⁻, M ² = OH⁻, K ⁰² = C₂O₄²⁻, B ⁰¹ = CH₃COO⁻, M ¹ = H₂O) of the uranyl complexes. The chains are formed by linking the centrosymmetric tetramers of the composition (UO₂)₄(O)₂(OH)₂(CH₃COO)₂(H₂O)₂ via tetradentate bridging oxalate ions. The uranium-containing groups are joined into a three-dimensional framework through the electrostatic interaction with potassium cations and a system of hydrogen bonds, which are formed with the participation of atoms involved in the composition of the water molecules, hydroxide ions, and uranyl ions. Original Russian Text ? L.B. Serezhkina, A.V. Vologzhanina, N.A. Neklyudova, V.N. Serezhkin, 2009, published in Kristallografiya, 2009, Vol. 54, No. 3, pp. 483–487.     

Raman and infrared spectra of As2Sx chalcogenide glasses with x ⩽ 3

Raman laser and far infrared spectra of As₂S_x glasses with x ? 3 are given and discussed. The purpose of the work is to bring a vibrational spectroscopic contribution to the study of these glasses and to the hypothesis, still under discussion in the literature, that they might be constituted either by a homogeneous vitreous phase or by a mixture of As₂S₃ and As₄S₄.Our results confirm a phase separation, with formation of ß-As₄S₄, below a certain value of x, which depends not only on the preparation method of the samples but also on other factors such as melting time. Laser irradiation of ß-As₄S₄ modifies its Raman spectrum. Such a phenomenon is attributable to two principal factors, either a partial polymerization or formation of a species richer in arsenic. A structural and formation model of the As₂S_x glasses is given, starting from a more generalized structural model of vitreous As₂S₃ which is an accord with the vibrational results and those by the diffraction method in the literature.     

Investigations of 2-Thiazoline-2-thiol as a Ligand: Synthesis and X-ray Structures of [Mn2(CO)7(μ-NS2C3H4)2] and [Mn(CO)3(PPh3)(κ2-NS2C3H4)]

Abstract  Treatment of Mn₂(CO)₁₀ with 2-thiazoline-2-thiol in the presence of Me₃NO at room temperature afforded the dimanganese complexes [Mn₂(CO)₇(μ-NS₂C₃H₄)₂] (1) and [Mn₂(CO)₆(μ-NS₂C₃H₄)₂] (2) in 51 and 34% yields, respectively. Compound 1 was quantitatively converted into 2 when reacted with one equiv of Me₃NO. Reaction of 1 with triphenylphosphine at room temperature furnished the mononuclear complex [Mn(CO)₃(PPh₃)(κ ²-NS₂C₃H₄)] (3) in 66% yield. All three new complexes have been characterized by elemental analyzes and spectroscopic data together with single crystal X-ray diffraction studies for 1 and 3. Compound 1 crystallizes in the orthorhombic space group Pbca with a = 12.4147(2), b = 16.2416(3), c = 19.0841(4) ?, β = 90°, Z = 8 and V = 3848.01(12) ?³ and 3 crystallizes in the monoclinic space group P 2₁/n with a = 10.41730(10), b = 14.7710(2), c = 14.9209(2) ?, β = 91.1760(10)°, Z = 4 and V = 2295.45(5) ?³. Graphical Abstract  Two new dimanganese complexes [Mn₂(CO)₇(μ-NS₂C₃H₄)₂] (1) and [Mn₂(CO)₆(μ-NS₂C₃H₄)₂] (2) were formed when [Mn₂(CO)₁₀] was treated with 2-thiazoline-2-thiol in the presence of Me₃NO. Compound 2 reacts with PPh₃ to give the monomeric complex [Mn(CO)₃(PPh₃ )(κ ²-NS₂C₃H₄)]. The structures of 1 and 3 were established by crystallography. Shishir Ghosh, Faruque Ahmed, Rafique Al-Mamun, Daniel T. Haworth, Sergey V. Lindeman, Tasneem A. Siddiquee, Dennis W. Bennett, Shariff E. Kabir Investigations of 2-thiazoline-2-thiol as a ligand: Synthesis and X-ray structures of [Mn₂(CO)₇(μ-NS₂C₃H₄)₂] and [Mn(CO)₃ (PPh3)(κ ²-NS₂C₃H₄)].      

0.2wt% Bi2O3、CuO、B2O3对5Ca0.6La0.267TiO3-5Ca(Mg1/3Nb2/3)O3微波介质陶瓷的性能影响

采用传统的固相反应法,研究了三种烧结助剂Bi2O3、CuO、B2O3对5Ca0.6La0.267TiO3-5Ca(Mg1/3Nb2/3)O3微波介质陶瓷的烧结性能和介电性能的影响。实验结果表明,掺入0.2wt%的Bi2O3、CuO、B2O3产生了液相,有效地降低了体系的烧结温度。Bi2O3和CuO的加入没有改变烧结体的微观形貌,它们介电常数和品质因数随烧结温度的变化趋势和体积密度趋于一致,均在体积密度最大时最高。当温度大于1300℃时,加入0.2wt%B2O3试样有柱状晶体生成,并随着烧结温度的升高而增多,柱状晶体的存在可能促使Q×f值较大的提高,当烧结温度过高时(1350℃),由于柱状晶体过多使得烧结体不均匀导致Q×f值下降。Bi2O3、CuO、B2O3的加入没有改变烧结体的晶相组成,因此所有烧结体均有近零的温度系数。结果表明,加入0.2wt%B2O3的5Ca0.6La0.267TiO3-5Ca(Mg1/3Nb2/3)O3在1325℃烧结温度具有最佳的介电性能:εr=54.87,Q×f=55 726 GHz,τf=-0.6 ppm/℃。     

自润滑Al2O3/TiC/CaF2复合陶瓷材料摩擦特性

为了探索自润滑陶瓷材料的开发及应用,采用冷压烧结工艺制备Al2O3/TiC/CaF2自润滑复合陶瓷材料。在摩擦磨损实验机上对其进行摩擦磨损实验,并对其摩擦磨损行为及自润滑效应进行分析。结果表明:在实验过程中,Al2O3/TiC/CaF2复合陶瓷材料物理机械性能优于同条件下制备的Al2O3/TiC复合陶瓷材料,且具有较低的摩擦因数和磨损率,其减摩抗磨效果明显,具有一定的自润滑效应,其减摩抗磨机理为摩擦驱动下CaF2存在于摩擦副表面,形成减摩抗磨层,在表面形成一层平整、光滑的自润滑层,增加摩擦表面实际接触面积,起到自润滑效应。     

Reactivity of [Re2(CO)8(MeCN)2] With 1-vinylimidazole: X-ray Structures of [Re2(CO)8{η1-NC3H3N(CH=CH2)}2] and [ReCl2(CO)2{η1-NC3H3N(CH=CH2)}2]

Abstract  Treatment of [Re₂(CO)₈(MeCN)₂] with excess 1-vinylimidazole in refluxing benzene gives three new compounds [Re₂(CO)₉{η ¹-NC₃H₃N(CH=CH₂)}] (1), [Re₂(CO)₈{η ¹-NC₃H₃N(CH=CH₂)}₂] (2) and [ReCl₂(CO)₂{η ¹-NC₃H₃N(CH=CH₂)}₂] (3) in 11, 32 and 2% yields, respectively. The solid-state structures of complexes 2 and 3 have been determined by single crystal X-ray diffraction studies. Compound 2 crystallizes in the monoclinic space group C2/c, with lattice parameters a = 13.8378(5) ?, b = 11.8909(5) ?, c = 14.4591(6) ?, β = 116.6470(10)°, Z = 4 and V = 2131.99(15) ?³. Compound 3 crystallizes in the monoclinic space group C2/c, with lattice parameters a = 10.1028(3) ?, b = 13.5640(5) ?, c = 12.5398(4) ?, β = 109.637(2)°, Z = 4 and V = 1618.4(9) ?³. The disubstituted dinuclear compound 2 contains two 1-vinylimidazole ligands coordinated through the imino nitrogen atoms at the equatorial sites, whereas the mononuclear compound 3 contains two carbonyl ligands, two N coordinated η ¹-1-vinylimidazole ligands and two terminal Cl ligands. Graphical Abstract  Two dinuclear complesxes [Re₂(CO)₉{η ¹-NC₃H₃N(CH=CH₂)}] (1) and [Re₂(CO)₈{η ¹-NC₃H₃N(CH=CH₂)}₂] (2) and the mononuclear [ReCl₂(CO)₂{η ¹-NC₃H₃N(CH=CH₂)}₂] (3) were obtained from the reaction of [Re₂(CO)₈(MeCN)₂] with excess 1-vinylimidazole at 80 °C. The X-ray structrures of 2 and 3 are described.      

Synthesis and X-ray structural investigation of (C3N6H7)4(CN3H6)2[UO2(CrO4)4] · 4H2O and (H3O)6[UO2(CrO4)4]

Single crystals of the compounds (C₃N₆ H₇)₄(CN₃H₆)₂[UO₂(CrO₄)₄] · 4H₂O (I) and (H₃O)₆[UO₂(CrO₄)₄] (II) are synthesized, and their structures are investigated using X-ray diffraction. Compound I crystallizes in the triclinic system with the unit cell parameters a = 6.3951(8) ?, b = 10.8187(16) ?, c = 16.9709(18) ?, α = 93.674(4)°, β = 97.127(4)°, γ = 92.020(4)°, space group, P Z = 1, V = 1161.6(3) ?³, and R = 0.0470. Crystals of compound II belong to the monoclinic system with the unit cell parameters a = 14.3158(4) ?, b = 11.7477(3) ?, c = 13.1351(4) ?, β= 105.836(1)°, space group C2/c, Z = 4, V = 2125.2(1) ?³, and R = 0.0213. The uranium-containing structural units of crystals I and II are mononuclear anionic complexes of the composition [UO₂(CrO₄)₄]⁶⁻ with an island structure, which belong to the crystal-chemical group Am ₁⁴ (A = UO₂₊², M ¹ = CrO₂₋⁴) of the uranyl complexes. The [UO₂(CrO₄)₄]⁶⁻ anionic complexes are joined into a three-dimensional framework through the electrostatic interactions with outer-sphere cations and a system of hydrogen bonds. Original Russian Text ? L.B. Serezhkina, E.V. Peresypkina, A.V. Virovets, A.G. Verevkin, D.V. Pushkin, 2009, published in Kristallografiya, 2009, Vol. 54, No. 2, pp. 284–290.     

Y2O3/ZrO2复合泡沫陶瓷烧结的初步研究

本文采用有机泡沫浸渍法制备了Y2O3/ZrO2双层复合、Y2O3/Y2O3-ZrO2/ZrO2三层复合及Y2O3和ZrO2单相泡沫陶瓷,分析了两种复合泡沫陶瓷层间的结合及各层显微结构随烧结温度的变化,并与单相氧化物陶瓷进行了对比。结果表明:双层复合陶瓷层间有较大缝隙,这是因为两种氧化物陶瓷烧结不同步造成的。三层复合陶瓷中Y2O3-ZrO2混合中间层的存在减弱了Y2O3、ZrO2烧结不同步引起的层间应力,层间结合明显改善,并大大减少了泡沫陶瓷表面宏观裂纹。两种复合陶瓷的ZrO2内层的烧结程度都低于单相ZrO2,这主要是因为先于ZrO2烧结的Y2O3外层阻碍了内部气体的排出从而阻碍ZrO2的烧结所致。     

3LiMnPO4·Li3V2（PO4）3正极材料的制备及其电化学性能研究

以五氧化二钒干凝胶、碳酸锰、磷酸二氢铵、碳酸锂、乙炔黑为原料,采用固相法在相对较低的温度条件下合成了x Li Mn PO4·y Li3V2(PO4)3锂离子电池复合正极材料。采用X射线衍射(XRD)、扫描电镜(SEM)对其晶体结构和表面形貌进行表征。结果表明,750℃下烧结15 h合成的3Li Mn PO4·Li3V2(PO4)3为结晶良好的两相结构,颗粒粒径较小且分布比较均匀,其在室温、0.2 C倍率下首次充放电容量分别为144.8 m Ah/g和139.8 m Ah/g,循环50次后容量为130.5 m Ah/g。     

Immiscibility and liquidus temperatures in the pseudobinary chalcogenide system PbSeGe1.5As0.5Se3

Electron microscopy studies of growth of microstructure or crystal size as a function of heat treatment temperature have been used to determine immiscibility and liquidus temperatures in the pseudobinary chalcogenide system PbSeGe_1.5As_0.5Se₃. The immiscibility dome was found to span nearly the entire pseudobinary composition region, in good agreement with the results of a previous heat capacity study of this system in the glass transition region.