Preparation and magnetic properties of BaFe12O19/Ni0.8Zn0.2Fe2O4 nanocomposite ferrite

Nanocomposite of hard (BaFe₁₂O₁₉)/soft ferrite (Ni_0.8Zn_0.2Fe₂O₄) have been prepared by the sol–gel process. The nanocomposite ferrite are formed when the calcining temperature is above 800 °C. It is found that the magnetic properties strongly depend on the presintering treatment and calcining temperature. The “bee waist” type hysteresis loops for samples disappear when the presintering temperature is 400 °C and the calcination temperature reaches 1100 °C owing to the exchange-coupling interaction. The remanence of BaFe₁₂O₁₉/Ni_0.8Zn_0.2Fe₂O₄ nanocomposite ferrite with the mass ratio of 5:1 is higher than a single phase ferrite. The specific saturation magnetization, remanence magnetization and coercivity are 63 emu/g, 36 emu/g and 2750 G, respectively. The exchange-coupling interaction in the BaFe₁₂O₁₉/Ni_0.8Zn_0.2Fe₂O₄ nanocomposite ferrite is discussed.     

Synthesis of (Mg0.476Mn0.448Zn0.007)(Fe1.997Ti0.002)O4 powder and sintered ferrites by high energy ball-milling process

(Mg_0.476Mn_0.448Zn_0.007)(Fe_1.997Ti_0.002)O₄ nanocrystalline powder prepared by high energy ball-milling process were consolidated by microwave and conventional sintering processes. Phases, microstructure and magnetic properties of the ferrites prepared by different processes were investigated. The (Mg_0.476Mn_0.448Zn_0.007)(Fe_1.997Ti_0.002)O₄ nanocrystalline powder could be prepared by high energy ball-milling process of raw Fe₃O₄, MnO₂, ZnO, TiO₂ and MgO powders. Prefired and microwave sintered ferrites could achieve the maximum density (4.86 g/cm⁻³), the average grain size (15 μm) was larger than that (10 μm) prepared by prefired and conventionally sintered ferrites with pure ferrite phase, and the saturation magnetization (66.77 emu/g) was lower than that of prefired and conventionally sintered ferrites (88.25 emu/g), the remanent magnetization (0.7367 emu/g) was higher than that of prefired and conventionally sintered ferrites (0.0731 emu/g). Although the microwave sintering process could increase the density of ferrites, the saturation magnetization of ferrites was decreased and the remanent magnetization of ferrites was also increased.     

Magnetic properties of c-axis oriented Sr0.8La0.2Fe11.8Co0.2O19 ferrite film prepared by chemical solution deposition

A Sr_0.8La_0.2Fe_11.8Co_0.2O₁₉ ferrite film has been prepared on a (0 0 1) sapphire substrate by chemical solution deposition. Structural characteristics indicate that the film is c-axis oriented and single-phase with space group P6₃/mmc. The grains are regular columnar with diameter between 50 and 100 nm as determined by atomic force microscopy. The sample possesses high saturation magnetization (130 emu/cm³), high coercivity (6.9 kOe), and large squareness ratio (0.9) at room temperature, which makes it a promising recording material.     

Study on dielectric and magnetic properties of Ho3Fe5O12 ceramics

Ho₃Fe₅O₁₂ ceramics with garnet structure were prepared by the solid-state reaction method. The results revealed the existence of Fe²⁺ ions have intensive influence on dielectric and magnetic properties of Ho₃Fe₅O₁₂ ceramics, which could be further confirmed by oxygen treatment. With a magnetic field lower than 10 kOe, the ME coefficient reaches 33 ps m⁻¹ at room temperature. And the ME coupling was further verified by dielectric anomaly near Néel temperature.     

Effect of Sr concentration on microstructure and magnetic properties of (Ba1−xSrx)(Ti0.3Fe0.7)O3 ceramics

Fe-doped (Ba_1−xSr_x)TiO₃ ceramics were prepared by solid-state reaction, and ferromagnetism was realized at room temperature. The microstructure and magnetism were modified by the Sr concentration control (0≤x≤75 at%) at a fixed Fe concentration, and the relevant magnetic exchange mechanism was discussed. All the samples are shown to have a single perovskite structure. When increasing the Sr concentration, the phase structure is transformed from a hexagonal perovskite into a cubic perovskite, with a monotonic decrease in lattice parameters induced by ionic size effect. The room-temperature ferromagnetism is expected to originate from the super-exchange interactions between Fe³⁺ on pentahedral and octahedral Ti sites mediated by the O²⁻ ions. The increase in Sr addition modifies two main influencing factors in magnetic properties: the ratio of pentahedral to octahedral Fe³⁺ and the concentration of oxygen vacancies, leading to a gradually enhanced saturation magnetization. The highest value, obtained for Fe-doped (Ba_0.25Sr_0.75)TiO₃, is an order of magnitude higher than that of the Fe-doped BaTiO₃ system with similar Fe concentration and preparation conditions, which may indicate (Ba_1−xSr_x)TiO₃ as a more suitable matrix material for multiferroic research.     

Synthesis, structural and magnetic properties of the nanocomposite Fe63B23Nd7Y3Nb3Cr1 magnets

The Fe₆₃B₂₃Nd₇Y₃Nb₃Cr₁ nanocomposite magnets in the form of sheets have been prepared by copper mold casting technique. The phase evolution, crystal structure, microstructural and magnetic properties have been investigated in the as-cast and annealed states. The as-cast sheets show magnetically soft behaviors which become magnetically hard by thermal annealing. The optimal annealed microstructure was composed of nanosize soft magnetic α-Fe (19-29 nm) and hard magnetic Nd₂Fe₁₄B (45-55 nm) grains. The best hard magnetic properties such as intrinsic coercivity, _jH_c of 1119 kA/m, remanence, B_r of 0.44 T, magnetic induction to saturation magnetization ratio, M_r/M_s=0.61 and maximum energy product, (BH)_max of 55 kJ/m³ was obtained after annealing at 680 °C for 15 min. The annealing treatment above 680 °C results in non-ideal phase grains growth, which degrade the magnetic properties.     

Synthesis,magnetic and electrical transport properties of magnetoresistance material Sr2FeMoO6 by microwave sintering

Magnetoresistance material Sr₂FeMoO₆ with double perovskite structure was synthesized by microwave sintering method using SrCO₃, Fe₂O₃ and MoO₃ as raw materials, with MnO₂ for microwave absorber. The phase structure, magnetic and electrical transport properties were investigated by X-ray powder diffraction (XRD) and vibrating-sample magnetometer. XRD analysis shows that the as-synthesized sample is Sr₂FeMoO₆ with tetragonal crystal structure and I4/mmm space group. The unit cell parameters are a=0.5587 nm, c=0.7894 nm, volume=0.2464 nm³. The calculated grain size of the sample is 31.62 nm, which is obtained by the Scherrer formula using the diffraction data. Magnetism testing results show that the sample Sr₂FeMoO₆ is ferromagnetic with the magnetic transition temperature of about 380 K. Under 1.0 T magnetic field, the saturation and spontaneous magnetization of Sr₂FeMoO₆ is 1.25 μ_B/f.u. and 1.00 μ_B/f.u. at room temperature. The magnetoresistance ratio of the sample is 28%. Electrical transport properties testing results indicate that the sample exhibits typical semiconductor behavior. The conductive mechanism of Sr₂FeMoO₆ is highly dependent on temperature: within the temperature range of 100–300 K, the mechanism is attributed to the small polaron variable-range hopping model; while it is ascribed to the adiabatic small polaron model within the temperature range of 80–100 K.     

High heat generation ability in AC magnetic field for nano-sized magnetic Y3Fe5O12 powder prepared by bead milling

Nano-sized magnetic Y₃Fe₅O₁₂ ferrite having a high heat generation ability in an AC magnetic field was prepared by bead milling. A commercial powder sample (non-milled sample) of ca. 2.9 μm in particle size did not show any temperature enhancement in the AC magnetic field. The heat generation ability in the AC magnetic field improved with a decrease in the average crystallite size for the bead-milled Y₃Fe₅O₁₂ ferrites. The highest heat ability in the AC magnetic field was for the fine Y₃Fe₅O₁₂ powder with a 15-nm crystallite size (the samples were milled for 4 h using 0.1 mm? beads). The heat generation ability of the excessively milled Y₃Fe₅O₁₂ samples decreased. The main reason for the high heat generation property of the milled samples was ascribed to an increase in the Néel relaxation of the superparamagnetic material. The heat generation ability was not influenced by the concentration of the ferrite powder. For the samples milled for 4 h using 0.1 mm? beads, the heat generation ability (W g⁻¹) was estimated using a 3.58×10⁻⁴ fH² frequency (f/kHz) and the magnetic field (H/kA m⁻¹), which is the highest reported value of superparamagnetic materials.     

Effect of sintering temperature and the particle size on the structural and magnetic properties of nanocrystalline Li0.5Fe2.5O4

Sintering temperature and particle size dependent structural and magnetic properties of lithium ferrite (Li_0.5Fe_2.5O₄) were synthesized and sintered at four different temperatures ranging from 875 to 1475 K in the step of 200 K. The sample sintered at 875 K was also treated for four different sintering times ranging from 4 to 16 h. Samples sintered at 1475 K have the cubic spinel structure with a small amount of α-Fe₂O₃ (hematite) and γ-Fe₂O₃ (maghemite). The samples sintered at≤1275 K do not show hematite and maghemite phases and the crystals form the single phase spinel structure with the cation ordering on octahedral sites. Particle size of lithium ferrite is in the range of 13-45 nm, and is depend on the sintering temperature and sintering time. The saturation magnetization increased from 45 to 76 emu/g and coercivity decreases from 151 to 139 Oe with an increase in particle size. Magnetization temperature curve recorded in ZFC and FC modes in an external magnetic field of 100 Oe. Typical blocking effects are observed below about 244 K. The dielectric constant increases with an increase in sintering temperature and particle size.     

Microstructures and multiferroic properties of textured Bi0.8La0.2FeO3 thin films

La-substituted BiFeO₃, Bi_0.8La_0.2FeO₃, thin films were fabricated on Pt/Ti/SiO₂/Si substrates by pulsed laser deposition. X-ray diffraction and high-resolution transmission electron microscope were used to analyze the structures of the films. The results show the films fabricated under optimized growth condition are (0 1 2) textured. X-ray photoemission spectroscopy results indicate that the oxidation state of Fe ion is Fe³⁺ in the films without detectable Fe²⁺. The films show low leakage current and excellent dielectric characters. Multiferroic properties with a remnant ferroelectric polarization of 5.2 μC/cm² and a remanent magnetization of 0.02 μ_B/Fe were established. These results have some implications for further research.     

Cation distribution dependence of magnetic properties of sol-gel prepared MnFe2O4 spinel ferrite nanoparticles

MnFe₂O₄ nanoparticles have been synthesized with a sol-gel method. Both differential thermal and thermo-gravimetric analyses indicate that MnFe₂O₄ nanoparticles form at 400 °C. Samples treated at 450 and 500 °C exhibit superparamagnetism at room temperature as implied from vibrating sample magnetometry. Mössbauer results indicate that as Mn²⁺ ions enter into the octahedral sites, Fe³⁺ ions transfer from octahedral to tetrahedral sites. When the calcination temperature increases from 450 to 700 °C, the occupation ratio of Fe³⁺ ions at the octahedral sites decreases from 43% to 39%. Susceptibility measurements versus magnetic field are reported for various temperatures (from 450 to 700 °C) and interpreted within the Stoner-Wohlfarth model.     

Effect of high magnetic field annealing on the microstructure and magnetic properties of Co-Fe layered double hydroxide

The effects of high magnetic field (10 T) on the products obtained by calcination of Co-Fe LDH precursors at different temperatures were investigated. The XRD results indicated that Fe^III substituted for Co^III in Co₃O₄ to yield Co^IICo^IIIFe^IIIO₄ under the calcination of Co-Fe LDH precursors at 400 °C. The products obtained by magnetic field annealing at 400 °C had a porous plate-like morphology, whereas the products without magnetic field annealing were composed of nanoparticles. It was seen that CoFe₂O₄ phase could be formed at low temperature (about 500 °C) under the magnetic field annealing. The grain size of products obtained by magnetic field annealing at 800 °C was larger than that of zero magnetic field. It was found that the saturation magnetization was significantly enhanced after magnetic field annealing, especially at lower temperature (≤600 °C). The possible reason for the effects on the microstructure and magnetic properties of products obtained by magnetic field annealing was discussed.     

Magnetic properties of Ni-substituted BiFeO3

BiFe_1−xNi_xO₃ ceramic powders with x up to 0.10 have been prepared by the sol-gel technique. The band gap of BiFeO₃ is 2.23 eV, and decreases to 2.09 eV for BiFe_0.95Ni_0.05O₃ and BiFe_0.90Ni_0.10O₃. The Mössbauer spectra show sextet at room temperature, indicating the magnetic ordering and the presence of only Fe³⁺ ions. Superparamagnetism with blocking temperature of 31 K for BiFe_0.95Ni_0.05O₃ and 100 K for BiFe_0.90Ni_0.10O₃ was observed. Enhanced magnetization at room temperature have been observed (1.0 emu/g for BiFe_0.95Ni_0.05O₃ and 2.9 emu/g for BiFe_0.90Ni_0.10O₃ under magnetic field of 10,000 Oe), which is one order larger than that of BiFeO₃ (0.1 emu/g under magnetic field of 10,000 Oe). The enhanced magnetization was attributed to the suppression of the cycloidal spin structure by Ni³⁺ substitution and the ferrimagnetic interaction between Fe³⁺ and Ni³⁺ ions.     

Microwave-assisted synthesis of SrFe12O19 hexaferrites

Ultra-fine and homogeneous SrFe₁₂O₁₉ hexaferrites were synthesized by a microwave-assisted calcination route. The calcined precursors were prepared by a sol-gel auto-combustion method using Fe(NO₃)₃·9H₂O, Sr(NO₃)₂ and citric acid as starting materials. The structures, powder morphology and magnetic properties of the products were characterized by X-ray diffraction, scanning electron microscope and vibrating sample magnetometer. The results showed that microwaves are helpful to reduce the calcination temperature and shorten the calcination time. The ferrites with saturation magnetization, remanence and intrinsic coercivity of 54.80 emu/g, 29.52 emu/g and 5261 Oe, respectively, were obtained in samples calcined at 800 °C for 80 min.     

Exchange coupling behavior in bimagnetic CoFe2O4/CoFe2 nanocomposite

In this work we report a study of the magnetic behavior of ferrimagnetic oxide CoFe₂O₄ and ferrimagnetic oxide/ferromagnetic metal CoFe₂O₄/CoFe₂ nanocomposite. The latter compound is a good system to study hard ferrimagnet/soft ferromagnet exchange coupled. Two steps were followed to synthesize the bimagnetic CoFe₂O₄/CoFe₂ nanocomposite: (i) first, preparation of CoFe₂O₄ nanoparticles using a simple hydrothermal method, and (ii) second, reduction reaction of cobalt ferrite nanoparticles using activated charcoal in inert atmosphere and high temperature. The phase structures, particle sizes, morphology, and magnetic properties of CoFe₂O₄ nanoparticles were investigated by X-Ray diffraction (XRD), Mossbauer spectroscopy (MS), transmission electron microscopy (TEM), and vibrating sample magnetometer (VSM) with applied field up to 3.0 kOe at room temperature and 50 K. The mean diameter of CoFe₂O₄ particles is about 16 nm. Mossbauer spectra revealed two sites for Fe³⁺. One site is related to Fe in an octahedral coordination and the other one to the Fe³⁺ in a tetrahedral coordination, as expected for a spinel crystal structure of CoFe₂O₄. TEM measurements of nanocomposite showed the formation of a thin shell of CoFe₂ on the cobalt ferrite and indicate that the nanoparticles increase to about 100 nm. The magnetization of the nanocomposite showed a hysteresis loop that is characteristic of exchange coupled systems. A maximum energy product (BH)_max of 1.22 MGOe was achieved at room temperature for CoFe₂O₄/CoFe₂ nanocomposites, which is about 115% higher than the value obtained for CoFe₂O₄ precursor. The exchange coupling interaction and the enhancement of product (BH)_max in nanocomposite CoFe₂O₄/CoFe₂ are discussed.     

Luminescence of Ce and Pr doped Sr2Mg(BO3)2 under VUV-UV and X-ray excitation

This report presents the luminescence properties of Ce³⁺ and Pr³⁺ activated Sr₂Mg(BO₃)₂ under VUV-UV and X-ray excitation. The five excitation bands of crystal field split 5d states are observed at about 46 729, 44 643, 41 667, 38 314 and 29 762 cm⁻¹ (i.e. 214, 224, 240, 261 and 336 nm) for Ce³⁺ in the host lattice. The doublet Ce³⁺ 5d→4f emission bands were found at about 25 840 and 24 096 cm⁻¹ (387 and 415 nm). The influence of doping concentration and temperature on the emission characteristics and the decay time of Ce³⁺ in Sr₂Mg(BO₃)₂ were investigated. For Pr³⁺ doped samples, the lowest 5d excitation band was observed at about 42017 cm⁻¹ (238 nm), a dominant band at around 35714 cm⁻¹ (280 nm) and two shoulder bands were seen in the emission spectra. The excitation and emission spectra of Ce³⁺ and Pr³⁺ were compared and discussed. The X-ray excited luminescence studies show that the light yields are ∼3200±230 and ∼1400±100 photons/MeV of absorbed X-ray energy for the samples Sr_1.86Ce_0.07Na_0.07Mg(BO₃)₂ and Sr_1.82Pr_0.09Na_0.09Mg(BO₃)₂ at RT, respectively.     

Structure and magnetic properties of nanocrystalline cobalt ferrite powders synthesized using organic acid precursor method

Nanocrystalline octahedra of cobalt ferrite CoFe₂O₄ powders were synthesized using the organic acid precursor route. The effect of the calcination temperature, Fe³⁺/Co²⁺ molar ratio, calcination time and type of organic acid (oxalic, benzoic and tartaric acids) on the formation, crystallite size, microstructure and magnetic properties was studied systematically. The Fe³⁺/Co²⁺ molar ratio was varied from 2 to 1.739 while the annealing temperature was controlled from 400 to 1000 °C for various periods from 0.5 to 2 h. The resulting powders were investigated using X-ray diffraction (XRD) analysis, Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and vibrating sample magnetometer (VSM). XRD results indicate that a well crystallized, single spinel cobalt ferrite phase was formed for the precursors annealed at 600-800 °C for 2 h, using oxalic and tartaric acids as precursors for Fe³⁺/Co²⁺ molar ratio 1.818. The crystallite size of as-formed powders was in the range of 38.0-92.6 nm at different operating conditions. The calcination temperature and Fe³⁺/Co²⁺ molar ratio have a significant effect on the microstructure of the produced cobalt ferrite. The microstructure of the produced powders was found to be octahedra-shaped. The crystalline, pure cobalt ferrite powders with magnetic properties having a maximum saturation magnetization (76.1 emu/g) was achieved for the single phase at Fe³⁺/Co²⁺ molar ratio 1.818 and annealing temperature of 600 °C for 2 h using tartaric acid precursor.     

Spectral properties of Nd-doped Sr3Ga2Ge4O14 crystal

Neodymium doped strontium gallogermanate crystals were grown successfully by the Bridgman technique. The linear thermal expansion coefficients for the c- and a-axes were measured as 5.8 × 10⁻⁶ °C⁻¹ and 6.5 × 10⁻⁶ °C⁻¹. Absorption spectra, and fluorescence spectra, as well as fluorescence decay curves of Nd³⁺-doped Sr₃Ga₂Ge₄O₁₄ crystal, have been recorded at room temperature and used to calculate the absorption and stimulated emission cross-sections. Based on the Judd-Ofelt theory, three intensity parameters were obtained. The luminescent quantum efficiency of the ⁴F_3/2 level was determined to be approximately 73.8% for this material. Compared with other Nd³⁺-doped laser crystals, Nd³⁺-doped Sr₃Ga₂Ge₄O₁₄ crystal displays special laser properties due to its disorder structure.     

High temperature ferromagnetism of the vacuum-annealed (In1−xFex)2O3 powders

(In_1−xFe_x)₂O₃ (x = 0.02, 0.05, 0.2) powders were prepared by a solid state reaction method and a vacuum annealing process. A systematic study was done on the structural and magnetic properties of (In_1−xFe_x)₂O₃ powders as a function of Fe concentration and annealing temperature. The X-ray diffraction and high-resolution transmission electron microscopy results confirmed that there were not any Fe or Fe oxide secondary phases in vacuum-annealed (In_1−xFe_x)₂O₃ samples and the Fe element was incorporated into the indium oxide lattice by substituting the position of indium atoms. The X-ray photoelectron spectroscopy revealed that both Fe²⁺ and Fe³⁺ ions existed in the samples. Magnetic measurements indicated that all samples were ferromagnetic with the magnetic moment of 0.49-1.73 μ_B/Fe and the Curie temperature around 783 K. The appearance of ferromagnetism was attributed to the ferromagnetic coupling of Fe²⁺ and Fe³⁺ ions via an electron trapped in a bridging oxygen vacancy.     

Effects of dopant concentrations on phosphorescence properties of Eu/Dy-doped Sr3MgSi2O8

Long afterglow Sr₃MgSi₂O₈: Eu, Dy phosphor with high brightness was prepared by sintering at high temperature and weak reductive atmosphere. The luminescent properties of this photoluminescent pigment were studied systematically by investigating concentration effects. The analytical results indicated that the main emission peaks appear at 482 nm. The excitation and emission spectra of this phosphor show that both of them are broadband. This is ascribed to the 4f⁷→4f⁶5d¹ transition of Eu²⁺ in the pigment matrix, which is in good agreement with the calculated value of 470 nm, and implies that luminescent centers Eu²⁺ occupy the deca-coordinated Sr²⁺ sites with the host of Sr₃MgSi₂O₈.