Transesterification kinetics of poly(ethylene terephthalate) and poly(ethylene 2,6‐naphthalate) blends with the addition of 2,2′‐bis(1,3‐oxazoline)

The kinetics of the transesterification reaction between poly(ethylene terephthalate) (PET) and poly(ethylene 2,6‐naphthalate) (PEN) with and without the addition of a chain extender were studied with ¹H NMR. Different kinetic approaches were considered, and a second‐order, reversible reaction was accepted for the PET/PEN reactive blend system. The addition of 2,2′‐bis(1,3‐oxazoline) (BOZ) promoted the transesterification reaction between PET and PEN in the molten state. The activation energy of the transesterification reaction for the PET/PEN reactive blend with BOZ (94.0 kJ/mol) was lower than that without BOZ (168.9KJ/mol). The rate constant k took an almost constant value for blend samples with different compositions mixed at 275 °C. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2607–2614, 2001     

双噁唑啉扩链尼龙1010

对尼龙 10 10的加成型化学扩链做了系统的研究 ,并对 2 ,2′ 双 (2 唑啉 ) (BOZ)和 1,4 双 (2 唑啉基 )苯 (PBO)的偶联效果和扩链产物的性能做了详细的探讨 ,前者的扩链效果较好 .研究结果表明 ,尼龙10 10熔体的转矩随着反应时间的延长显著增加 .但转矩达到极大值后开始缓慢下降 ,表明扩链产物在高温条件下发生热降解 .扩链剂的用量存在最佳值 ,用量不足时偶联反应不充分 ,用量过量时封端反应加剧 .扩链以后尼龙 10 10的端羧基含量大大降低 ,反应温度对反应速率的影响符合阿累尼乌斯关系式 .扩链产物极限粘度大大高于尼龙原料 ,表明分子量显著提高     

Synthesis of trans‐4‐hydroxy‐L‐proline‐based telechelic prepolymers and poly(ester‐urethane)

The synthesis of hydroxyproline‐based telechelic prepolymers by the condensation polymerization of trans‐4‐hydroxy‐N‐benzyloxycarbonyl‐L ‐proline methyl ester was investigated. All the polymerizations were carried out in the melt with stannous octoate as the catalyst and with different diols. The products were characterized by differential scanning calorimetry, proton nuclear magnetic resonance, infrared spectrophotometry, and inherent viscosity (η_inh). According to the analytic results, the η_inh value of the prepolymers depended on the kind and amount of diols that were added. With an increase in the 1,6‐hexanediol feed from 2 to 10 mol %, there was a decrease in η_inh from 0.78 to 0.41 along with a decrease in the glass‐transition temperature (T_g ) from 63 to 42 °C. When 2 mol % of different kinds of diols were used, η_inh ranged from 0.78 to 0.21, and T_g varied from 70 to 43 °C. These new prepolymers could be linked to poly(ester‐urethane) by the chain extender 1,6‐hexamethylene diisocyanate. The poly(ester‐urethane) was amorphous, and the T_g was 76 °C. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 2449–2455, 2000     

Synthesis and properties of aromatic polyimides derived from 2,2,′3,3′‐biphenyltetracarboxylic dianhydride

2,2,′3,3′‐Biphenyltetracarboxylic dianhydride (2,2,′3,3′‐BPDA) was prepared by a coupling reaction of dimethyl 3‐iodophthalate. The X‐ray single‐crystal structure determination showed that this dianhydride had a bent and noncopolanar structure, presenting a striking contrast to its isomer, 3,3,′4,4′‐BPDA. This dianhydride was reacted with aromatic diamines in a polar aprotic solvent such as N,N‐dimethylacetamide (DMAc) to form polyamic acid intermediates, which imidized chemically to polyimides with inherent viscosities of 0.34–0.55 dL/g, depending on the diamine used. The polyimides from 2,2,′3,3′‐BPDA exhibited a good solubility and were dissolved in polar aprotic solvents and polychlorocarbons. These polyimides have high glass transition temperatures above 283°C. Thermogravimetric analyses indicated that these polyimides were fairly stable up to 500°C, and the 5% weight loss temperatures were recorded in the range of 534–583°C in nitrogen atmosphere and 537–561°C in air atmosphere. All polyimides were amorphous according to X‐ray determination. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1425–1433, 1999     

Polyamide‐6,6‐based blocky copolyamides obtained by solid‐state modification

Copolyamides based on polyamide‐6,6 (PA‐6,6) were prepared by solid‐state modification (SSM). Para‐ and meta‐xylylenediamine were successfully incorporated into the aliphatic PA‐6,6 backbone at 200 and 230 °C under an inert gas flow. In the initial stage of the SSM below the melting temperature of PA‐6,6, a decrease of the molecular weight was observed due to chain scission, followed by a built up of the molecular weight and incorporation of the comonomer by postcondensation during the next stage. When the solid‐state copolymerization was continued for a sufficiently long time, the starting PA‐6,6 molecular weight was regained. The incorporation of the comonomer into the PA‐6,6 main chain was confirmed by size exclusion chromatography (SEC) with ultraviolet detection, which showed the presence of aromatic moieties in the final high‐molecular weight SSM product. The occurrence of the transamidation reaction was also proven by ¹H nuclear magnetic resonance (NMR) spectroscopy. As the transamidation was limited to the amorphous phase, this SSM resulted in a nonrandom overall structure of the PA copolymer as shown by the degree of randomness determined using ¹³C NMR spectroscopy. The thermal properties of the SSM products were compared with melt‐synthesized copolyamides of similar chemical composition. The higher melting and higher crystallization temperatures of the solid state‐modified copolyamides confirmed their nonrandom, block‐like chemical microstructure, whereas the melt‐synthesized copolyamides were random. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013 , 51, 5118–5129     

Effects of diamines and their fluorinated groups on the color lightness and preparation of organosoluble aromatic polyimides from 2,2‐bis[4‐(4‐amino‐2‐trifluoromethylphenoxy)phenyl]‐hexafluoropropane

To investigate the position and amount of the CF₃ group affecting the coloration of polyimides (PIs), we prepared 2,2‐bis[4‐(4‐amino‐2‐trifluoromethylphenoxy)phenyl]hexafluoropropane ( 2 ) with four CF₃ groups with 2‐chloro‐5‐nitrobenzotrifluoride and 2,2‐bis(4‐hydroxyphenol)hexafluoropropane. A series of soluble and light‐colored fluorinated PIs ( 5 ) were synthesized from 2 and various aromatic dianhydrides ( 3a – 3f ). 5a – 5f had inherent viscosities ranging from 0.80 to 1.19 dL/g and were soluble in amide polar solvents and even in less polar solvents. The glass‐transition temperatures of 5 were 221–265 °C, and the 10% weight‐loss temperatures were above 493 °C. Their films had cutoff wavelengths between 343 and 390 nm, b* values (a yellowness index) ranging from 5 to 41, dielectric constants of 2.68–3.01 (1 MHz), and moisture absorptions of 0.03–0.29 wt %. In a comparison of the PI series 6 – 8 based on 2,2‐bis[4‐(4‐aminophenoxy)phenyl]hexafluoropropane, 2,2‐bis[4‐(4‐amino‐2‐trifluoromethylphenoxy)phenyl]propane, and 2,2‐bis[4‐(4‐aminophenoxy)phenyl]propane, we found that the CF₃ group close to the imide group was more effective in lowering the color; this means that CF₃ of 5 , 7 , and 8f was more effective than that of 6c . The color intensity of the four PI series was lowered in the following order: 5 > 7 > 6 > 8 . The PI 5f , synthesized from diamine 2 and 4,4′‐hexafluoroisopropylidenediphthalic anhydride, had six CF₃ groups in a repeated segment, so it exhibited the lightest color among the four series. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 922–938, 2003     

Chain extension of adipic acid and (or) succinic acid/butanediol polyesters with 2,2′‐(1,4‐phenylene)‐bis(2‐oxazoline) and adipoylbiscaprolactamate combined chain extenders

This paper provided an easy and flexible method to synthesize high molecular weight polyesters by polycondensation and chain extension. Low molecular weight polybutylene adipate, polybutylene succinate, and poly(butylene succinate‐co‐butylene adipate) (PBSA) were synthesized through melt condensation polymerization from adipic acid and/or succinic acid with butanediol. The prepolyesters obtained had different amount of ? COOH and ? OH terminal groups. Chain extension of them was carried out at 180–240°C using 2,2′‐(1,4‐phenylene)‐bis(2‐oxazoline) and adipoyl biscaprolactamate as combined chain extenders. The influencing factors of the chain extension were studied. At the optimal conditions, chain‐extended polybutylene adipate with M_n up to 39,100, polybutylene succinate with intrinsic viscosity of 0.99 dl/g, and PBSA with intrinsic viscosity from 0.73 to 0.81 dl/g were synthesized. The chain‐extended polyesters were characterized by IR spectrum, ¹H NMR spectrum, differential scanning calorimetry, thermogravimetric analysis (TGA), wide angle X‐ray scattering, and tensile test. The thermal analysis showed that chain extension often led to slight decrease of the regularity, the crystallinity, and the melting point. This deterioration of the properties is not harmful enough to impair their thermal properties and obstruct them from being used as biodegradable thermoplastics. The TGA showed that the chain‐extended polyesters were stable with initial decomposition temperature over 354.7°C. The tensile strength of the chain extended PBS and PBSAs with butylene adipate units less than 20 mol% was in the range of 18.95–31.22 MPa. Copyright © 2010 John Wiley & Sons, Ltd.     

Synthesis and self‐assembly behavior study of α,ω‐dicarboxyl‐poly(ethylene glycol)–permethyl‐6‐amino‐6‐deoxy‐β‐cyclodextrin‐monoamide: A new β‐cyclodextrin conjugate

A new type of amphiphilic macromolecule was synthesized through the attachment of a poly(ethylene glycol) chain to a permethyl‐amino‐β‐cyclodextrin ring. The structure of the product was studied with 1D and 2D NMR experiments and with MALDI‐TOF MS. The resulting comet‐shaped molecule showed self‐assembly behavior in polar solvents. The presence of supramolecular structures in aqueous media was detected with dynamic light scattering and proven also by 2D NOESY and DOSY experiments. The supramolecular structures that formed could serve as starting materials for new types of drug delivery bioconjugates containing two independent dopable sites, that is, the cyclodextrin ring and the core of the supramolecular structure. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 5149–5155, 2007     

Synthesis,characterization, and cross‐linking of a library of statistical copolymers based on 2‐“soy alkyl”‐2‐oxazoline and 2‐ethyl‐2‐oxazoline

The synthesis of statistical copolymers consisting of 2‐ethyl‐2‐oxazoline (EtOx) and 2‐“soy alkyl”‐2‐oxazoline (SoyOx) via a microwave‐assisted cationic ring‐opening polymerization procedure is described. The majority of the resulting copolymers revealed polydispersity indices below 1.30. The reactivity ratios (r_EtOx 1.4 ± 0.3; r_SoyOx = 1.7 ± 0.3) revealed a clustered monomer distribution throughout the polymer chains. The thermal and surface properties of the pEtOx‐stat‐SoyOx copolymers were analyzed before and after UV‐curing demonstrating the decreased chain mobility after cross‐linking. In addition, the cross‐linked materials showed shape‐persistent swelling upon absorption of water from the air, whereby as little as 5 mol % SoyOx was found to provide efficient cross‐linking. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 5371,–5379, 2007     

Synthesis and characterization of novel π‐conjugated polymers with phosphole ring derivatives

Novel π‐conjugated polymers ( 8 – 10 ) were prepared by the palladium‐catalyzed Sonogashira coupling reaction of three kinds of phosphole‐ring‐containing monomers with 2,5‐dihexyloxyl‐1,4‐diethynylbenzene. The obtained polymers ( 8 – 10 ) were regioregulated with the 2,5‐substituted phosphole ring in the polymer main chain and characterized with ¹H, ¹³C, and ³¹P NMR and FTIR. Polymers 8 – 10 were found to have an extended π‐conjugated system according to the results of UV–vis absorption spectra. In the fluorescence emission spectra of 8 – 10 , moderate emission peaks were observed in the visible blue‐to‐green region. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 2867–2875, 2007     

Simple synthesis,photophysics, and electroluminescent properties of poly[2,7‐bis(4‐tert‐butylstyryl)fluorene‐9, 9‐diyl‐alt‐alkane‐α,ω‐diyl]

A simple synthetic route was used for the synthesis of a novel series of alternating copolymers based on substituted 2,7‐distyrylfluorene bridged through alkylene chains. First, 2,7‐dibromofluorene was reacted with 2 equiv of butyllithium, and this was followed by a treatment with 1 equiv of α,ω‐dibromoalkane to yield the intermediate, poly(2,7‐dibromofluorene‐9,9‐diyl‐alt‐alkane‐α,ω‐diyl). ( 1 ) Heck coupling of the latter with 1‐tert‐butyl‐4‐vinylbenzene afforded the target, poly[2,7‐bis(4‐tert‐butylstyryl)fluorene‐9,9‐diyl‐alt‐alkane‐α,ω‐diyl] ( 2 ). The two versions of 2 ( 2a and 2b which have hexane and decane, respectively, as alkane groups) were readily soluble in common organic solvents. Their glass‐transition temperature was relatively low (52 and 87 °C). An intense blue photoluminescence emission with maxima at about 408 and 409 nm was observed in tetrahydrofuran solutions, whereas thin films exhibited an orange emission with maxima at 569 and 588 nm. Very large redshifts of the photoluminescence maxima and Stokes shifts in thin films indicated strong aggregation in the solid state. Both polymers oxidized and reduced irreversibly. Single‐layer light‐emitting diodes with hole‐injecting indium tin oxide and electron‐injecting aluminum electrodes were fabricated. They emitted orange light with external electroluminescence efficiencies of 0.52 and 0.36% photon/electron, as determined in light‐emitting diodes made of 2a and 2b , with alkylenes of (CH₂)₆ and (CH₂)₁₀, respectively. An increase in the external electroluminescence efficiency up to 1.5% was reached in light‐emitting diodes made of polymer blends consisting of 2a and poly(9,9‐dihexadecylfluorene‐2,7‐diyl), which emitted blue‐white light. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 809–821, 2007.     

Polymerization of conjugated 5‐[(5‐ethynyl‐1‐naphthyl)ethynyl]‐N,N‐dimethylnaphthalen‐1‐amine with rhodium and palladium complexes

The monomer 5‐[(5‐ethynyl‐1‐naphthyl)ethynyl]‐N,N‐dimethylnaphthalen‐1‐amine was satisfactory obtained through the heterocoupling reaction of 5‐ethynyl‐N,N‐dimethylnaphthalen‐1‐amine and 4‐(5‐iodo‐1‐naphthyl)‐2‐methyl‐3‐butyn‐2‐ol catalyzed by a palladium–copper system, followed by acetone elimination. Poly{5‐[(5‐ethynyl‐1‐naphthyl)ethynyl]‐N,N‐dimethylnaphthalen‐1‐amine} was obtained through the reaction of the acetylene monomer with homogeneous rhodium and palladium catalyst complexes. The structure of the polymers always showed a trans–cisoidal chain configuration on the basis of IR and NMR spectra. Moreover, only for the rhodium catalyst complex in methanol was a dimeric product isolated in a very low yield, having a conjugated terminal ene–yne structure, which permitted the consideration of a metallated chain‐transfer intermediate in the polymer propagation. The mass determination of the polymers, by osmometry and gel permeation chromatography techniques, showed low average molecular weights. The kinetics of the catalyzed polymerization were analyzed. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 2038–2047, 2007     

Electric‐field‐induced molecular alignment of side‐chain liquid‐crystalline polyacetylenes containing biphenyl mesogens

Electric‐field‐induced molecular alignments of side‐chain liquid‐crystalline polyacetylenes [? {HC?C[(CH₂)_mOCO‐biph‐OC₇H₁₅]}? , where biph is 4,4′‐biphenylyl and m is 3 (PA3EO7) or 9 (PA9EO7)] were studied with X‐ray diffraction and polarized optical microscopy. An orientation as high as 0.84 was obtained for PA9EO7. Furthermore, the molecular orientation of PA9EO7 was achieved within a temperature range between the isotropic‐to‐smectic A transition temperature and 115 °C, and this suggested that the orientational packing was affected by the thermal fluctuation of the isotropic liquid and the mobility of the mesogenic moieties. The maximum achievable orientation for PA9EO7 was much greater than that for PA3EO7. This was the first time that the electric‐field‐induced molecular orientation of a side‐chain liquid‐crystalline polymer with a stiff backbone was studied. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1333–1341, 2004     

Synthesis and characterization of soluble polyimides derived from 2,2′‐Bis(3,4‐dicarboxyphenoxy)‐9,9′‐spirobifluorene dianhydride

The synthesis of aromatic poly(ether imide)s containing spirobifluorene units in the polymer backbone is described. 2,2′‐Bis(3,4‐dicarboxyphenoxy)‐9,9′‐spirobifluorene dianhydride, which was used as a new monomer, was synthesized with 2,2′‐dihydroxy‐9,9′‐spirobifluorene as the starting material. In the spiro‐segment, the rings of the connected bifluorene were orthogonally arranged. This bis(ether anhydride) monomer was employed in reactions with a variety of aromatic diamines to furnish poly(ether imide)s, involving an initial ring‐opening polycondensation and subsequent chemically induced cyclodehydration. Excellent solubility in common organic solvents at room temperature, good optical transparency, and high thermal stability are the prominent characteristic features of these new polymers, which can be attributed to the presence of spiro‐fused orthogonal bifluorene segments along the polymer chain. The glass‐transition temperatures of the polyimides were 240–293 °C, and the 5% weight‐loss temperatures were greater than 500 °C. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 262–268, 2002     

Synthesis of high‐molecular‐weight aliphatic–aromatic copolyesters from poly(ethylene‐co‐1,6‐hexene terephthalate) and poly(L‐lactic acid) by chain extension

A series of aliphatic–aromatic multiblock copolyesters consisting of poly(ethylene‐co‐1,6‐hexene terephthalate) (PEHT) and poly(L ‐lactic acid) (PLLA) were synthesized successfully by chain‐extension reaction of dihydroxyl terminated PEHT‐OH prepolymer and dihydroxyl terminated PLLA‐OH prepolymer using toluene‐2,4‐diisoyanate as a chain extender. PEHT‐OH prepolymers were prepared by two step reactions using dimethyl terephthalate, ethylene glycol, and 1,6‐hexanediol as raw materials. PLLA‐OH prepolymers were prepared by direct polycondensation of L ‐lactic acid in the presence of 1,4‐butanediol. The chemical structures, the molecular weights and the thermal properties of PEHT‐OH, PLLA‐OH prepolymers, and PEHT‐PLLA copolymers were characterized by FTIR, ¹H NMR, GPC, TG, and DSC. This synthetic method has been proved to be very efficient for the synthesis of high‐molecular‐weight copolyesters (say, higher than M_w = 3 × 10⁵ g/mol). Only one glass transition temperature was found in the DSC curves of PEHT‐PLLA copolymers, indicating that the PLLA and PEHT segments had good miscibility. TG curves showed that all the copolyesters had good thermal stabilities. The resulting novel aromatic–aliphatic copolyesters are expected to find a potential application in the area of biodegradable polymer materials. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 5898–5907, 2009     

Synthesis and properties of ortho‐linked aromatic polyimides based on 1,2‐bis(4‐aminophenoxy)‐4‐tert‐butylbenzene

A bis(ether amine) containing the ortho‐substituted phenylene unit and pendant tert‐butyl group, 1,2‐bis(4‐aminophenoxy)‐4‐tert‐butylbenzene, was synthesized and used as a monomer to prepare polyimides with six commercial dianhydrides via a conventional two‐stage procedure. The intermediate poly(amic acid)s had inherent viscosities of 0.78–1.44 dL/g, and most of them could be thermally converted into transparent, flexible, and tough polyimide films. The inherent viscosities of the resulting polyimides were in the range of 0.46–0.87 dL/g. All polyimides were noncrystalline, and most of them showed excellent solubility in polar organic solvents. The glass‐transition temperatures of these polyimides were in the range of 222–259 °C in differential scanning calorimetry and 212–282 °C in thermomechanicl analysis. These polyimides showed no appreciable decomposition up to 500 °C in thermogravimetric analysis in air or nitrogen. A comparative study of the properties with the corresponding polyimides without pendant tert‐butyl groups derived from 1,2‐bis(4‐aminophenoxy)benzene is also presented. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1551–1559, 2000     

An efficient synthesis of telechelic poly (N‐isopropylacrylamides) and its application to the preparation of α,ω‐dicholesteryl and α,ω‐dipyrenyl polymers

Poly(N‐isopropylacrylamide)s (PNIPAMs) with cholesteryl or pyrenyl moieties at each chain end (CH‐PNIPAMs or Py‐PNIPAMs) were prepared via end‐group modification of α,ω‐dimercapto poly(N‐isopropylacrylamides), ranging in molecular weight from ～ 7000 to 45,000 g mol^?1 with a polydispersity index of 1.10 or lower. The telechelic thiol functionalized PNIPAMs were obtained by aminolysis of α,ω‐di(isobutylthiocarbonylthio)‐poly(N‐isopropylacrylamide)s (iBu‐PNIPAMs) obtained by reversible addition‐fragmentation chain transfer (RAFT) polymerization of N‐isopropylacrylamide in the presence of the difunctional chain transfer agent, diethylene glycol di(2‐(1‐isobutyl)sulfanylthiocarbonylsulfanyl‐2‐methyl propionate) (DEGDIM). The self‐assembly of the polymers in water was assessed by fluorescence spectroscopy, using the intrinsic emission of Py‐PNIPAM or the emission of pyrene added as a probe in aqueous solutions of CH‐PNIPAM. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 314–326, 2008     

Thermal oxidative stability and effect of water on gas transport and mechanical properties in PA6‐EVOH films

The thermal oxidative stability and the effect of water on gas transport and mechanical properties of blends of polyamide 6 (PA6) with ethylene‐co‐vinyl alcohol (EVOH) and EVOH modified with carboxyl groups (EVOH‐COOH) have been investigated. The presence of EVOH reduces water vapor and oxygen gas permeability of polyamide, as well as small amounts of EVOH‐COOH further improve barrier properties, especially to oxygen. This has been explained in terms of improved interactions of the blend constituents in the amorphous phase, due to ionic linkages between the polyamide amino groups and the carboxyls of modified EVOH. The permeation to gases was found to increase with the amount of sorbed water. The morphology of the samples was found to have an effect on barrier properties, as the presence of EVOH causes the PA6 α crystalline form to increase, lowering the permeability to oxygen and water vapor. Mechanical properties are strongly affected by water sorption, as tensile modulus and strength decrease with increasing water content. Chemiluminescence (CL), infrared spectroscopy (FTIR), and tensile test were employed in order to assess the correlation between chemical composition and the thermal oxidative stability of the films aged at 110 °C in air. CL experiments suggest that the presence of EVOH and EVOH‐COOH efficiently inhibits the formation of peroxidized species during the processing, and increases the thermal oxidative stability of the films. Infrared spectroscopy showed a build‐up of carbonyl absorption in the range 1700–1780 cm^?1, due to the formation of oxidation products, which is greater in the case of the pure polymer. Tensile tests on films revealed a reduction in ductility as a result of ageing for neat PA6, whereas in comparison the blends exhibit a far better long‐term stability. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 840–849, 2007     

High‐efficiency blue light‐emitting polymers based on 3,6‐silafluorene and 2,7‐silafluorene

A novel blue‐emitting polymer based on 3,6‐silafluorene and 2,7‐silafluorene was synthesized via the Suzuki polycondensation. The resulting polymers are readily soluble in common organic solvents, such as toluene, xylene, THF, and chloroform. The thermal, electrochemical, photophysical, and electroluminescence properties of the resulting polymers were investigated. The device fabricated from the copolymer with a configuration of ITO/PEDOT:PSS/PVK/polymer/Ba/Al exhibited an external quantum efficiency of 1.95%, a luminous efficiency of 1.69 cd A^?1 and a maximal brightness of 6000 cd m^?2. It has been found that the incorporation of the 3,6‐silafluorene unit into the poly(2,7‐silafluorene) main chain can not only improve the color purity of the devices from the resulting copolymer but also enhance its device efficiency. Moreover, no undesired long‐wavelength green emission was observed in the PL spectra of P36‐27SiF90 compared to that of PFO with a dominating emission at 500–600 nm after thermal annealing at 200 °C for 8 h. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4941–4949, 2007     

Synthesis of perfectly bifunctional polyacrylates by single‐electron‐transfer living radical polymerization

Poly(methyl acrylate)s, poly(ethyl acrylate)s, and poly(butyl acrylate)s with α,ω‐di(bromo) chain ends and M_n from 8500 to 35,000 were synthesized by single‐electron‐transfer living radical polymerization (SET‐LRP). The analysis of their chain ends by a combination of ¹H and 2D‐NMR, GPC, MALDI‐TOF MS, chain end functionalization, chain extension, and halogen exchange experiments demonstrated the synthesis of perfectly bifunctional polyacrylates by SET‐LRP. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4684–4695, 2007