Effect of shear on the crystallization of the poly(ether ether ketone)

The effect of shear on the crystallization behavior of the poly(ether ether ketone) (PEEK) has been investigated by means of ex situ wide‐angle X‐ray diffraction (WAXD), small‐angle X‐ray scattering, and differential scanning calorimetry (DSC). The changes of the intensity of WAXD patterns along shear direction of the PEEK induced by short‐term shear were observed when the samples crystallized at 330 °C. The results showed that the dimensions of the crystallites perpendicular to the (110) and (111) planes reduced with the increase of shear rate, whereas the dimensions of the crystallites perpendicular to (200) plane increased with the increase of shear rate. Moreover, increasing shear rate can lead to the increase of the crystallinity as well as the average thickness of the crystalline layers. Correspondingly, a new melting peak at higher temperature was found during the subsequent DSC scanning when the shear rate was increased to 30 s^?1. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 220–225, 2010     

Synthesis of a random copolymer and its compatibility for thermotropic liquid crystalline polymer/poly(ether ether ketone) blends

A random copolymer (RCP) containing poly(ether ether ketone) (PEEK) and thermotropic liquid crystalline polymer (TLCP) segments was synthesized. Its chemical structure and liquid crystalline properties were characterized by FT‐IR, differential scanning calorimetry (DSC) and polar light microscopy (PLM) respectively. A single glass transition temperature (T_g) at 134.0°C, a melting temperature (T_m) at 282.0°C and a temperature of ignition (T_i) at 331.3°C can be observed. Blends of PEEK and TLCP with and without RCP as compatibilizer were prepared by extrusion and the effect of RCP on the thermal properties, dynamic mechanical properties, morphology and static tensile mechanical properties of blends was investigated by means of DSC, dynamic mechanical analysis (DMA), scanning electron microscopy (SEM), etc. Dynamic mechanical measurements indicated that there appeared to be only a single tan δ peak resulting from the glass transition of the PEEK‐rich phase and the T_g value shifted towards higher temperature due to the presence of compatibilizer, as suggested partial compatibility. Morphological investigations showed that the addition of RCP to binary blends reduced the dispersed phase size and improved the interfacial adhesion between the two phases. The ternary compatibilized blends showed enhanced tensile modulus compared to their binary blends without RCP. The strain at break decreased for the ternary blends due to embrittlement of the matrix by the incorporation of some RCP to the matrix phase. Copyright © 2007 John Wiley & Sons, Ltd.     

Rhythmic growth of ring‐banded spherulites in blends of liquid crystalline methoxy‐poly(aryl ether ketone) and poly(aryl ether ether ketone)

Rhythmic growth of ring‐banded spherulites in blends of liquid crystalline methoxy‐poly(aryl ether ketone) (M‐PAEK) and poly(aryl ether ether ketone) (PEEK) has been investigated by means of differential scanning calorimetry (DSC), polarized light microscopy (PLM), and scanning electron microscopy (SEM) techniques. The measurements reveal that the formation of the rhythmically grown ring‐banded spherulites in the M‐PAEK/PEEK blends is strongly dependent on the blend composition. In the M‐PAEK‐rich blends, upon cooling, an unusual ring‐banded spherulite is formed, which is ascribed to structural discontinuity caused by a rhythmic radial growth. For the 50:50 M‐PAEK/PEEK blend, ring‐banded spherulites and individual PEEK spherulites coexist in the system. In the blends with PEEK as the predominant component, M‐PAEK is rejected into the boundary of PEEK spherulites. The cooling rate and crystallization temperature have great effect on the phase behavior, especially the ring‐banded spherulite formation in the blends. In addition, the effects of M‐PAEK phase transition rate and phase separation rate on banded spherulite formation is discussed. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 3011–3024, 2007     

Thermal stability and nonisothermal crystallization of short fiber-reinforced poly(ether ether ketone) composites

The thermal stability of a short carbon-fiber-reinforced PEEK composite was assessed by thermogravimetry and by a Rheometrics dynamic analyzer. The results indicated that holding for 10 min at 380°C was a suitable melting condition to avoid the thermooxidative degradation under air. After proving that the heating rate of 50°C/min can be used to evaluate the crystallinity, a heating stage was used to prepare nonisothermally crystallized specimens using cooling rates from 1 to 100°C/min after melting at 400°C for 3 or 15 min. The degree of crystallinity and the melting behavior of these specimens were investigated by DSC at a heating rate of 50°C/min. The presence of three or four regions indicated that the upper melting temperature, T_m, changed with the crystallization temperature. The first region with the highest T_m, which corresponded to the cooling rate of 1°C/min, can be associated with the crystallization in regime II. There was a second region where T_m decreased as the amount of crystals formed in regime II decreased with increasing cooling rate from 5 to 20°C/min. The third region, a plateau region, corresponded to regime III condition in which the crystals were imperfect. In the fourth region, the cooling was so fast that crystallization was incomplete during the cooling for the melting condition of 400°C for 15 min. © 1998 John Wiley & Sons, Inc. J. Polym. Sci. B Polym. Phys. 36: 2225–2235, 1998     

Isothermal melt and cold crystallization kinetics of poly(aryl ether ketone ether ketone ketone)

The isothermal melt and cold crystallization kinetics of poly(aryl ether ketone ether ketone ketone) are investigated by differential scanning calorimetry over two temperature regions. The Avrami equation describes the primary stage of isothermal crystallization kinetics with the exponent n ≈ 2 for both melt and cold crystallization. With the Hoffman–Weeks method, the equilibrium melting point is estimated to be 406 °C. From the spherulitic growth equation proposed by Hoffman and Lauritzen, the nucleation parameter (K_g) of the isothermal melt and cold crystallization is estimated. In addition, the K_g value of the isothermal melt crystallization is compared to those of the other poly(aryl ether ketone)s. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 1992–1997, 2000     

Analysis of crystallization kinetics of poly(ether ether ketone)

An optical microscope equipped with a video photograph system was used to follow the growth of spherulites. Under nitrogen atmosphere, the growth rates at 290 and 300°C suggest that when the melt of PEEK has been equilibrated for 15 min at 400°C, the subsequent crystallization behavior was nearly independent of the prior thermal history. Linear growth rates of crystallization of PEEK have been measuredin the temperature range of 260–325°C for melt-pressed films and solvent cast films. Detailed kinetic analysis indicated that PEEK exhibited an unmistakable regime II → III transition at 296 ± 1°C. The II → III transition was clearly present irrespective of the rather drastic changes in U*. It is interesting that the branching and crosslinking retarded the growth rate of PEEK, but a transition from regime II to regime III still existed. For melt-pressed films after equilibration at 400°C for 15 min, values of σ and q suggest that U* should be taken nearer to 1500 cal/mol in the case of T_∞ = T_g − 30 K and 2000 cal/mol in the case of T_∞ = T_g − 51.6 K. The K_g(III)/K_g(II) ratio (1.32) was not as close to the predicted value of 2 as was Hoffman's ratio. For PEEK, the Thomas-Staveley constant (β) should be closer to 0.25 or 0.3 instead of 0.1. © 1998 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 36: 1335–1348, 1998     

Compressed‐gas‐induced crystallization in tert‐butyl poly(ether ether ketone)

tert‐Butyl‐substituted poly(ether ether ketone) (tBuPEEK), which does not undergo crystallization with thermal annealing, crystallizes readily when treated with compressed CO₂. The dissolved CO₂ causes a reduction in the glass‐transition temperature of the polymer–gas system and enhances the chain mobility of the macromolecules, thereby bringing about crystallization. In the presence of CO₂, crystallization is increasingly favored with increasing CO₂ pressure and treatment temperature. The melting point of tBuPEEK crystals increases linearly with the CO₂ pressure applied in the treatment, indicating an increase in the order and/or size of the crystals. The extent of crystallinity increases when small amounts of methanol or dichloromethane are used as a cosolute with CO₂. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 1505–1512, 2001     

Effects of carbon nanotubes on crystallization and melting behavior of poly(L‐lactide) via DSC and TMDSC studies

In this work, multiwalled carbon nanotubes (MWNTs) were surface‐modified and grafted with poly(L ‐lactide) to obtain poly(L ‐lactide)‐grafted MWNTs (i.e. MWNTs‐g‐PLLA). Films of the PLLA/MWNTs‐g‐PLLA nanocomposites were then prepared by a solution casting method to investigate the effects of the MWNTs‐g‐PLLA on nonisothermal and isothermal melt‐crystallizations of the PLLA matrix using DSC and TMDSC. DSC data found that MWNTs significantly enhanced the nonisothermal melt‐crystallization from the melt and the cold‐crystallization rates of PLLA on the subsequent heating. Temperature‐modulated differential scanning calorimetry (TMDSC) analysis on the quenched PLLA nanocomposites found that, in addition to an exothermic cold‐crystallization peak in the range of 80–120 °C, an exothermic peak in the range of 150–165 °C, attributed to recrystallization, appeared before the main melting peak in the total and nonreversing heat flow curves. The presence of the recrystallization peak signified the ongoing process of crystal perfection and, if any, the formation of secondary crystals during the heating scan. Double melting endotherms appeared for the isothermally melt‐crystallized PLLA samples at 110 °C. TMDSC analysis found that the double lamellar thickness model, other than the melting‐recrystallization model, was responsible for the double melting peaks in PLLA nanocomposites. Polarized optical microscopy images found that the nucleation rate of PLLA was enhanced by MWNTs. TMDSC analysis found that the incorporation of MWNTs caused PLLA to decrease the heat‐capacity increase (namely, ΔC_p) and the C_p at glass transition temperature. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 1870–1881, 2007     

Thermal analysis of ring‐opening metathesis polymerized healing agents

Dicyclopentadiene (DCPD) and 5‐ethylidene‐2‐norbornene (ENB) and their mixtures were analyzed after ring‐opening metathesis polymerization (ROMP) in the presence of Grubbs catalyst as potential candidate healing agents for self‐healing composite materials using two complementary methods, rotational dynamic mechanical analysis (DMA) and differential scanning calorimetry (DSC). Following isothermal DMA measurements at room temperature (RT = 25 °C) for 120 min, two consecutive dynamic temperature scan experiments were performed for each system. In the first dynamic temperature scans, there was an initial downward peak slightly above RT in the storage modulus versus temperature curve for samples with relatively slower reaction rates (i.e., DCPD and DCPD‐rich mixtures or low catalyst loadings) due to a combination of the glass transition followed by further residual reaction. However, no or negligible downward peaks were observed for the highly reactive ENB and ENB‐rich samples even at much lower catalyst loadings. Implications of the substantial decrease in storage modulus just above RT for the slowly reacting systems are discussed for healing of damage in composite materials at elevated temperatures. The maximum glass transition temperatures (T_g∞) from DMA of the fully cured samples were determined to be approximately 160 °C for DCPD and 120 °C for ENB, decreasing linearly with increased ENB in the blends. The glass transitions and further residual reactions above the glass transitions were confirmed by DSC. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 1771–1780, 2007     

Melting behavior of poly(ether ether ketone) in its blends with poly(ether imide)

We detail the melting behavior of poly(ether ether ketone) (PEEK) and investigate its melting behavior in miscible blends with poly(ether imide) (PEI). The determination of the equilibrium melting point (T_m⁰) of PEEK is discussed by considering its inhomogeneous morphology. T_m⁰ is obtained by a long extrapolation of a Hoffman–Weeks plot to 384°C. Hindrance of PEEK crystal reorganization induced by PEI during heating is observed over the blend composition investigated (20–75 wt % PEEK). This behavior is correlated with the incorporation of PEI in the interlamellar zones of PEEK crystals. The interaction parameter χ of PEEK/PEI blends is estimated by the equilibrium melting point depression. This gives the interaction density B = ?1.2 cal/cm³, and x = ?0.40 at 400°C. © 1993 John Wiley & Sons, Inc.     

Nonisothermal cold crystallization behavior and kinetics of polylactide/clay nanocomposites

The nonisothermal cold crystallization behavior of intercalated polylactide (PLA)/clay nanocomposites (PLACNs) was studied using differential scanning calorimetry, polarized optical microscope, X‐ray diffractometer, dynamic mechanical thermal analysis, and Fourier transform infrared spectrometer. The results show that both the cold crystallization temperature (T_cc) and melting point (T_m) of PLA matrix decreases monotonously with increasing of clay loadings, accompanied by the decreasing degree of crystallinity (X_c%) at the low heating rates (≤5 °C/min). However, the X_c% of PLACNs presents a remarkable increase at the high heating rate of 10 °C/min in contrast to that of neat PLA. The crystallization kinetics was then analyzed by the Avrami, Jezioney, Ozawa, Mo, Kissinger and Lauritzen–Hoffman kinetic models. It can be concluded that at the low heating rate, the cold crystallization of both the neat PLA and nanocomposites proceeds by regime III kinetics. The nucleation effect of clay promote the crystallization to some extent, while the impeding effect of clay results in the decrease of crystallization rate with increasing of clay loadings. At the high heating rate of 10 °C/min, crystallization proceeds mainly by regime II kinetics. Thus, the formation of much more incomplete crystals in the PLACNs with high clay loadings due to the dominant multiple nucleations mechanism in regime II, may have primary contribution to the lower crystallization kinetics, also as a result to the higher degree of crystallinity and lower melting point in contrast to that of neat PLA. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 1100–1113, 2007     

Glass transition and miscibility in blends of two semicrystalline polymers: Poly(aryl ether ketone) and poly(ether ether ketone)

Binary melt‐blended mixtures of two aryl ether ketone polymers (i.e., a new poly(aryl ether ketone) (code name PK99) and poly(ether ether ketone) (PEEK), have been studied. Polymer miscibility in glassy amorphous (or melt) domains has been demonstrated for the binary blend comprising of two aryl‐ether‐ketone‐type semicrystalline polymers. Composition‐dependent, single T_g was observed within full composition range in the PK99/PEEK blends, and the narrow T_g breadth also suggests that the scale of mixing was fine and uniform. To better resolve any possible overlapping T_g's, physical aging was imposed on a comparison set of blend samples for the purpose of improving detectability of overlapped multiple transitions if existing. The result still showed one single T_g. The relative sharp T_g and lack of cloud point transition suggest that the scale of molecular intermixing is good. Phase homogeneity was further confirmed using optical and scanning electron microscopy. The X‐ray diffractograms suggest that isomorphism does not exist in the PK99/PEEK blends and that the crystal forms of the respective polymers remain distinct and unchanged by the miscibility in the amorphous region. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 1485–1494, 1999     

Vitrification/devitrification phenomena during isothermal and nonisothermal crystallization of poly(aryl–ether–ether–ketone) (PEEK) and PEEK/poly(ether–imide) blends

We have established time–temperature transformation and continuous-heating transformation diagrams for poly(ether–ether–ketone) (PEEK) and PEEK/poly(ether–imide) (PEI) blends, in order to analyze the effects of relaxation control on crystallization. Similar diagrams are widely used in the field of thermosetting resins. Upon crystallization, the glass transition temperature (T_g) of PEEK and PEEK/PEI blends is found to increase significantly. In the case of PEEK, the shift of the α-relaxation is due to the progressive constraining of amorphous regions by nearby crystals. This phenomenon results in the isothermal vitrification of PEEK during its latest crystallization stages for crystallization temperatures near the initial T_g of PEEK. However, vitrification/devitrification effects are found to be of minor importance for anisothermal crystallization, above 0.1°C/min heating rate. In the case of PEEK/PEI blends, amorphous regions are progressively enriched in PEI upon PEEK crystallization. This promotes a shift of the α-relaxation of these regions to higher temperatures, with a consequent vitrification of the material when crystallized below the T_g of PEI. The data obtained for the blends in anisothermal regimes allow one to detect a region in the (temperature/heating rate) plane where crystallization proceeds in the continuously close proximity of the glass transition (dynamic vitrification). These experimental findings are in agreement with simple simulations based on a modified Avrami model coupled with the Fox equation. © 1998 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 36: 919–930, 1998     

Molecular analysis of the crystallization behavior of poly(aryl-ether-ether-ketone)

The crystallization behavior, via annealing, of PEEK was investigated using FTIR spectroscopy. It was found that predominantly amorphous PEEK (e.g., quenched polymer) follows two distinct mechanisms when it is annealed. One is a lower energy relaxation process that involves the partial rotation of the ether linkages, allowing the molecular chains in the disordered phase to become better packed, and occurs from 50 to 140°C (slightly below T_g). This relaxation process is also observed by dynamic mechanical analyses. The other process is a crystallization that takes place above the glass transition, with its onset characterized by the rotation of the benzophenone linkages near T_g. Isothermal crystallization kinetics data on PEEK can be described by an Avrami equation with an Avrami constant n of about 1.     

Polyetherether ketone/polyarylethersulfone blends: Thermal and compatibility aspects

The compatibility behavior of polyetherether ketone (PEEK) with poly(ether sulfone) (PES) has been reexamined using differential scanning calorimetry (DSC), scanning electron microscopy (SEM), and extrudate swell measurements. The blends were prepared by both melt‐blending and solution‐blending techniques. The phase behavior of blends is strongly affected by the blending technique used. Blends prepared by solution‐blending are compatible in the entire composition range on the basis of the single composition‐dependent glass transitions and exhibit lower critical solution temperature (LCST) behavior. LCST was near 340 °C around which the crystalline melting point of PEEK exists. Near LCST melting‐induced movement of molecular chains disturbs the initial homogeneous state of the solution blends and leads to a phase‐separated state that is thermodynamically more stable in the absence of strong specific interactions between the homopolymers. Contrary to the solution‐blended samples, melt‐blended samples were in the phase‐separated state even at a lower processing temperature of 300 °C. Two glass transitions corresponding to a PEEK‐rich and a PES‐rich phase were found for all compositions. From the measured glass transition of phase‐separated blends, weight fractions of PES and PEEK dissolved in each phase were determined using the Fox equation. Compatibility is greater in the PEEK‐rich compositions than in the PES‐rich compositions. PEEK dissolves more in PES‐rich phases than does PES in the PEEK‐rich phase. Variation of the specific heat increment (ΔC_p) at the glass transition with composition also supports these inferences. Solution‐blended samples, quenched from 380 °C, also indicated similar behavior but were slightly more compatible. The aforementioned results are consistent with those inferred from SEM studies and extrudate swell measurements that show a greater compatibility in PEEK‐rich compositions than in PES‐rich compositions. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 1407–1424, 2002     

Crystal modifications and multiple melting behavior of poly(L‐lactic acid‐co‐D‐lactic acid)

The crystal modifications and multiple melting behavior of poly(L ‐lactic acid‐co‐D ‐lactic acid) (98/2) as a function of crystallization temperature were studied by wide‐angle X‐ray diffraction (WAXD) and differential scanning calorimetry (DSC). It was found that the disorder (α′) and order (α) phases of poly(L ‐lactic acid) (PLLA) were formed in cold‐crystallized poly(L ‐lactic acid‐co‐D ‐lactic acid) samples at low (<110 °C) and high (≥110 °C) temperatures, respectively. A disorder‐to‐order (α′‐to‐α) phase transition occurred during the annealing process of the α′‐crystal at elevated temperatures, which proceeded quite slowly even at the peak temperature of the exotherm P_exo but much more rapidly at higher temperature close to the melting region. The presence or absence of an additional endothermic peak before the exotherm in the DSC thermograph of the α′‐crystal was strongly dependent on the heating rate, indicating that a melting process involved during the α′‐to‐α phase transition. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2011     

Structure–initiator activity dependence of aminimides as thermally latent initiators in the polymerization of glycidyl phenyl ether

Novel aliphatic aminimides were synthesized from the corresponding carboxylic acid esters, 1,1‐dimethylhydrazine, and epoxides in 54–95% yields. Bulk polymerization of glycidyl phenyl ether (GPE) with 3 mol % of the aminimides was evaluated by DSC as a model process for curing of epoxy resin. All the aminimides showed no exothermic DSC peak below 120 °C but showed sharp exothermic peaks above 137 °C, indicating good thermal latency. Good relationships were observed between the calculated bond length from the carbonyl carbon to the α‐carbon of the aliphatic group (R C), DSC onset temperatures, and the thermal dissociation temperatures (T_d 's) of the aminimides. The aminimide with a longer R C bond length showed lower T_d and DSC onset temperature, that is, higher activity. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 3428–3433, 2000     

Gas transport properties of substituted PEEKs

Tert-butyl and di-tert-butyl were added as pendant groups to the ether-ether phenyl ring of poly(ether ether ketone), PEEK. tert-butyl PEEK, TBPEEK, was amorphous and di-tert-butyl PEEK, DBPEEK, was semicrystalline. However, a 2 : 1 random copolymer of TBPEEK and DBPEEK, TBDBPEEK, was amorphous. Gas transport of N₂, O₂, CH₄, and CO₂ through amorphous films of PEEK, TBPEEK, TBDBPEEK, and tetramethylbiphenyl PEEK were determined at 35°C and at pressures to about 15 atm. The results support previous observations that tert-butyl and tetramethylbiphenyl groups are very effective in disrupting chain packing in the polymer. For the present polymers, these substitutions led to a 5–18-fold increase in permeability, and, in some cases, at no loss in permselectivity. © 1997 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 35 : 2355–2362, 1997     

Cold crystallization behavior of polyamide 6 in PS‐g‐PA6 graft copolymers

TEM micrographs show that the PA grafts of PS‐g‐PA6 graft copolymers, which are obtained directly by extracting homo‐PA6 out from the homo‐PA6/PS‐g‐PA6 blends, are in the form of wormlike structure. The wormlike PA6 domains can shrink into droplets after annealing at 250 °C for 15 min. The diameter of the droplet determined by TEM and SAXS is in the range of 50–60 nm. This article reports on a unique crystallization behavior of the PA6 grafts in PS‐g‐PA6 graft copolymers. In a DSC cooling scan, PA6 grafts do not crystallize from the melt with a cooling rate of 10 °C/min. However, there is a cold crystallization peak around 65 °C in the subsequent heating scan. This cold crystallization phenomenon, which has not yet been reported in the literature till now, follows well the homogeneous nucleation mechanism and is depressed at relatively slow cooling rates (2 °C/min) or even completely eliminated after annealing within a specific temperature range. It may be caused by the slow diffusion or transport rate of the less flexible PA6 grafts to the crystal fronts when crystallization takes place around its glass transition temperature. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 65–73, 2010     

Poly(ether ether ketone)/poly(aryl ether sulfone) blends: Melt rheological behavior

Dynamic rheological measurements were carried out on blends of poly(ether ether ketone) (PEEK)/poly(aryl ether sulfone) (PES) in the melt state in the oscillatory shear mode. The data were analyzed for the fundamental rheological behavior to yield insight into the microstructure of PEEK/PES blends. A variation of complex viscosity with composition exhibited positive–negative deviations from the log‐additivity rule and was typical for a continuous‐discrete type of morphology with weak interaction among droplets. The point of transition showed that phase inversion takes place at composition with a 0.6 weight fraction of PEEK, which agreed with the actual morphology of these blends observed by scanning electron microscopy. Activation energy for flow, for blend compositions followed additive behavior, which indicated that PEEK/PES blends may have had some compatibility in the melt. Variation of the elastic modulus (G′) with composition showed a trend similar to that observed for complex viscosity. A three‐zone model used for understanding the dynamic moduli behavior of polymers demonstrated that PEEK follows plateau‐zone behavior, whereas PES exhibits only terminal‐zone behavior in the frequency range studied. The blends of these two polymers showed an intermediate behavior, and the crossover frequency shifted to the low‐frequency region as the PEEK content in PES increased. This revealed the shift of terminal‐zone behavior to low frequency with an increased PEEK percentage in the blend. Variation of relaxation time with composition suggested that slow relaxation of PEEK retards the relaxation process of PES as the PEEK concentration in the blend is increased because of the partial miscibility of the blend, which affects the constraint release process of pure components in the blend. A temperature‐independent correlation observed in the log–log plots of G′ versus loss modulus (G″) for different blend systems fulfilled the necessary condition for their rheological simplicity. Further, the composition‐dependent correlations of PEEK/PES blends observed in a log–log plot of G′ versus G″ showed that the blends are either partially miscible or immiscible and form a discrete‐continuous phase morphology. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1548–1563, 2004