Influences of different oxidants on characteristics of La_2O_3/Al_2O_3 nanolaminates deposited by atomic layer deposition

A comparative study of two kinds of oxidants(H_2O and O_3) with the combination of two metal precursors(TMA and La(~iPrCp)_3) for atomic layer deposition(ALD) La_2O_3/Al_2O_3 nanolaminates is carried out. The effects of different oxidants on the physical properties and electrical characteristics of La_2O_3/Al_2O_3 nanolaminates are studied. Initial testing results indicate that La_2O_3/Al_2O_3 nanolaminates could avoid moisture absorption in the air after thermal annealing. However, moisture absorption occurs in H_2O-based La_2O_3/Al_2O_3 nanolaminates due to the residue hydroxyl/hydrogen groups during annealing. As a result, roughness enhancement, band offset variation, low dielectric constant and poor electrical characteristics are measured because the properties of H_2O-based La_2O_3/Al_2O_3 nanolaminates are deteriorated. Addition thermal annealing effects on the properties of O_3-based La_2O_3/Al_2O_3 nanolaminates indicate that O_3 is a more appropriate oxidant to deposit La_2O_3/Al_2O_3 nanolaminates for electron devices application.     

Influences of different oxidants on the characteristics of HfAlOx films deposited by atomic layer deposition

A comparative study of two kinds of oxidants(H2O and O3) with the combinations of two metal precursors [trimethylaluminum(TMA) and tetrakis(ethylmethylamino) hafnium(TEMAH)] for atomic layer deposition(ALD) hafnium aluminum oxide(HfAlOx) films is carried out.The effects of different oxidants on the physical properties and electrical characteristics of HfAlOx films are studied.The preliminary testing results indicate that the impurity level of HfAlOx films grown with both H2O and O3 used as oxidants can be well controlled,which has significant effects on the dielectric constant,valence band,electrical properties,and stability of HfAlOx film.Additional thermal annealing effects on the properties of HfAlOx films grown with different oxidants are also investigated.     

Influence of annealing temperature on passivation performance of thermal atomic layer deposition Al_2O_3 films

Chemical and field-effect passivation of atomic layer deposition （ALD） Al2O3 films are investigated, mainly by corona charging measurement. The interface structure and material properties are characterized by transmission electron microscopy （TEM） and X-ray photoelectron spectroscopy （XPS）, respectively. Passivation performance is improved remarkably by annealing at temperatures of 450 ℃ and 500 ℃, while the improvement is quite weak at 600 ℃, which can be attributed to the poor quality of chemical passivation. An increase of fixed negative charge density in the films during annealing can be explained by the Al2O3/Si interface structural change. The Al–OH groups play an important role in chemical passivation, and the Al–OH concentration in an as-deposited film subsequently determines the passivation quality of that film when it is annealed, to a certain degree.     

Permeation barrier properties of an Al2O3/ZrO2 multilayer deposited by remote plasma atomic layer deposition

We report the permeation barrier properties of Al₂O₃/ZrO₂ multi-layers deposited by remote plasma atomic layer deposition. Electrical Ca degradation tests were performed to derive the water vapor transmission rate (WVTR) of Al₂O₃, ZrO₂ and Al₂O₃/ZrO₂ multi-layers at 50 °C and 50% relative humidity (RH). Al₂O₃/ZrO₂ multi-layers exhibit better barrier properties than Al₂O₃ and ZrO₂ layers, and when more individual layers were deposited in the same total thickness, the WVTR value was reduced further, indicating a better barrier property. The WVTR of the Al₂O₃ and ZrO₂ layers were 9.5 × 10⁻³ and 1.6 × 10⁻² g/m² day, respectively, but when deposited alternatively with 1 cycle of each layer, the WVTR decreased to 9.9 × 10⁻⁴ g/m² day. X-ray diffraction results indicated that ZrO₂ has a monoclinic structure but Al₂O₃ and Al₂O₃/ZrO₂ multi-layers show an amorphous structure. Cross sectional Al₂O₃/ZrO₂ multi-layer structures and the formation of a ZrAl_xO_y phase are observed by transmission electron microscopy (TEM). X-ray photoelectron spectrometry (XPS) results indicate that Al₂O₃ and ZrO₂ contain 33.7% and 37.8%, respectively, Al–OH and Zr–OH bonding. However, the ZrAl_xO_y phase contained 30.5% Al–OH and Zr–OH bonding. The results of transmittance measurement indicate that overall, Al₂O₃, ZrO₂ and Al₂O₃/ZrO₂ multi-layers show high transmittance greater than 80% in the visible region.     

Influences of annealing on structural and compositional properties of Al_2O_3 thin films grown on 4H–SiC by atomic layer deposition

Annealing effects on structural and compositional performances of Al_2O_3 thin films on 4H–Si C substrates are studied comprehensively. The Al_2O_3 films are grown by atomic layer deposition through using trimethylaluminum and H_2 O as precursors at 300?C, and annealed at various temperatures in ambient N_2 for 1 min. The Al_2O_3 film transits from amorphous phase to crystalline phase as annealing temperature increases from 750?C to 768?C. The refractive index increases with annealing temperature rising, which indicates that densification occurs during annealing. The densification and grain formation of the film upon annealing are due to crystallization which is relative with second-nearest-neighbor coordination variation according to the x-ray photoelectron spectroscopy(XPS). Although the binding energies of Al 2p and O 1s increase together during crystallization, separations between Al 2p and O 1s are identical between as-deposited and annealed sample, which suggests that the nearest-neighbour coordination is similar.     

等离子增强原子层沉积低温生长GaN薄膜

采用等离子增强原子层沉积技术在低温下于单晶硅衬底上成功生长了Ga N多晶薄膜,利用椭圆偏振仪、低角度掠入射X射线衍射仪、X射线光电子能谱仪对薄膜样品的生长速率、晶体结构及薄膜成分进行了表征和分析.结果表明,等离子增强原子层沉积技术生长Ga N的温度窗口为210—270?C,薄膜在较高生长温度下呈多晶态,在较低温度下呈非晶态;薄膜中N元素与大部分Ga元素结合成N—Ga键生成Ga N,有少量的Ga元素以Ga—O键存在,多晶Ga N薄膜含有少量非晶态Ga_2O_3.     

Preparation of tantalum oxide thin films by photo-assisted atomic layer deposition

Tantalum oxide thin films were prepared by photo-assisted atomic layer deposition (Photo-ALD) in the substrate temperature range of 170–400 °C using Ta(OC₂H₅)₅ and H₂O as precursors. The constant growth rates of 0.42 and 0.47 Å per cycle were achieved for the films grown by normal ALD and Photo-ALD, respectively. The increased growth rate in Photo-ALD is probably due to the reactive surface by photon energy and faster surface reaction. In Photo-ALD, however, the constant growth rate started at lower temperature of 30 °C and one cycle time shortened up to 5.7 s than that of normal ALD. The films grown by normal ALD and Photo-ALD were amorphous and very smooth (0.21–0.35 nm) as examined by X-ray diffractometer and atomic force microscopy, respectively. Also, the refractive index was found to be 2.12–2.16 at the substrate temperature of 190–300 °C, similar to that of the film grown by normal ALD. However, the remarkably low leakage current density of 0.6×10⁻⁶ A/cm² to 1×10⁻⁶ A/cm² at applied field of 1 MV/cm is several order of magnitude smaller than that of normal ALD, probably due to the presence of reactive atom species.     

等离子增强原子层沉积低温生长AlN薄膜

采用等离子增强原子层沉积技术在单晶硅基体上成功制备了AlN晶态薄膜, 利用椭圆偏振仪、原子力显微镜、小角掠射X射线衍射仪、高分辨透射电子显微镜、 X射线光电子能谱仪对样品的生长速率、表面形貌、晶体结构、薄膜成分进行了表征和分析, 结果表明, 采用等离子增强原子层沉积制备AlN晶态薄膜的最低温度为200 ℃, 薄膜表面平整光滑, 具有六方纤锌矿结构与(100)择优取向, Al_2p与N_1S的特征峰分别为74.1 eV与397.0 eV, 薄膜中Al元素与N元素以Al-N键相结合, 且成分均匀性良好. 关键词： 氮化铝 等离子增强原子层沉积 低温生长 晶态薄膜     

Low-temperature plasma enhanced atomic layer deposition of large area HfS_2 nanocrystal thin films

Hafnium disulfide(HfS2) is a promising two-dimensional material for scaling electronic devices due to its higher carrier mobility, in which the combination of two-dimensional materials with traditional semiconductors in the framework of CMOS-compatible technology is necessary. We reported on the deposition of HfS2 nanocrystals by remote plasma enhanced atomic layer deposition at low temperature using Hf(N(CH3)(C2H5))4 and H2S as the reaction precursors. Selflimiting reaction behavior was observed at the deposition temperatures ranging from 150℃ to 350℃, and the film thickness increased linearly with the growth cycles. The uniform HfS2 nanocrystal thin films were obtained with the size of nanocrystal grain up to 27 nm. It was demonstrated that higher deposition temperature could enlarge the grain size and improve the HfS2 crystallinity, while causing crystallization of the mixed HfO2 above 450℃. These results suggested that atomic layer deposition is a low-temperature route to synthesize high quality HfS2 nanocrystals for electronic device or electrochemical applications.     

原子层沉积HfO2薄膜的激光损伤特性分析

以目前激光惯性约束聚变中应用最广泛的高折射率材料二氧化铪(HfO2)为研究对象,在熔石英基底上分别采用TEMAH和HfCl4前驱体制备了HfO2薄膜,沉积温度分别为100,200和300 ℃。采用椭偏仪和激光量热计对薄膜的光学性能进行了测量分析,采用X射线衍射仪(XRD)对薄膜的微结构进行了测量。最后在小口径激光阈值测量平台上按照1-on-1测量模式对薄膜的损伤阈值进行了测试,并采用扫描电子显微镜（SEM）对损伤形貌进行了分析。研究表明,用同一种前驱体源时,随着沉积温度升高,薄膜折射率增加,吸收增多,损伤阈值降低。在相同温度下,采用有机源制备的薄膜更容易在薄膜内部形成有机残留,导致薄膜吸收增加,损伤阈值降低。采用HfCl4作为前驱体源在100℃制备氧化铪薄膜时,损伤阈值能够达到31.8 J/cm2 (1064 nm,3 ns)。     

原子层沉积Al2O3/n-GaN MOS结构的电容特性

利用原子层沉积技术制备了具有圆形透明电 极的Ni/Au/Al₂O₃/n-GaN金属-氧化物-半导体结构, 研究了紫外光照对样品电容特性及深能级界面态的影响, 分析了非理想样品积累区电容随偏压增加而下降的物理起源. 在无光照情形下, 由于极长的电子发射时间与极慢的少数载流子热产生速率, 样品的室温电容-电压扫描曲线表现出典型的深耗尽行为, 且准费米能级之上占据深能级界面态的电子状态保持不变. 当器件受紫外光照射时, 半导体耗尽层内的光生空穴将复合准费米能级之上的深能级界面态电子, 同时还将与氧化层内部的深能级施主态反应. 非理想样品积累区电容的下降可归因于绝缘层漏电导的急剧增大, 其诱发机理可能是与氧化层内的缺陷态及界面质量有关的“charge-to-breakdown”过程. 关键词： 原子层沉积 2O₃/n-GaN')" href="#">Al₂O₃/n-GaN 金属-氧化物-半导体结构 电容特性     

TiO2/Al2O3薄膜的原子层沉积和光学性能分析

采用原子层沉积技术在熔石英和BK7玻璃基片上镀制了TiO2/Al2O3薄膜,沉积温度分别为110℃和280℃。利用X射线粉末衍射仪对膜层微观结构进行了分析研究,并在激光损伤平台上进行了抗激光损伤阈值测量。采用Nomarski微分干涉差显微镜和原子力显微镜对激光损伤后的形貌进行了观察分析。结果表明,采用原子层沉积技术镀制的TiO2/Al2O3增透膜的厚度均匀性较好,Φ50 mm样品的膜层厚度均匀性优于99%;光谱增透效果显著,在1 064 nm处的透过率〉99.8%;在熔石英和BK7基片上,TiO2/Al2O3薄膜在110℃时的激光损伤阈值分别为（6.73±0.47）J/cm2和（6.5±0.46）J/cm2,明显高于在280℃时的损伤阈值。     

Effective silicon surface passivation by atomic layer deposited Al2O3/TiO2 stacks

In this work atomic layer deposition of Al₂O₃ and TiO₂ has been used to obtain dielectric stacks for passivation of silicon surfaces. Our experiments on n‐ and p‐type silicon wafers deposited by thin Al₂O₃/TiO₂ stacks show that a considerably improved passivation is obtained compared to the Al₂O₃ single layer. For Al₂O₃ films thinner than 20 nm the emitter saturation current density decreases with increasing TiO₂ thickness. Especially the passivation of ultrathin (～5 nm) Al₂O₃ is very effectively enhanced by TiO₂ due to a decreased interface defect density as well as an increased fixed negative charge in the stacks. Hence, the thin Al₂O₃/TiO₂ stacks developed in this work can be used as a passivation coating for Si‐based solar cells. (© 2014 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Characteristics and properties of metal aluminum thin films prepared by electron cyclotron resonance plasma-assisted atomic layer deposition technology

Metal aluminum (Al) thin films are prepared by 2450 MHz electron cyclotron resonance plasma-assisted atomic layer deposition on glass and p-Si substrates using trimethylaluminum as the precursor and hydrogen as the reductive gas. We focus our attention on the plasma source for the thin-film preparation and annealing of the as-deposited films relative to the surface square resistivity. The square resistivity of as-deposited Al films is greatly reduced after annealing and almost reaches the value of bulk metal. Through chemical and structural analysis, we conclude that the square resistivity is determined by neither the contaminant concentration nor the surface morphology, but by both the crystallinity and crystal size in this process.     

Atomic-layer-deposited Al_2O_3 and HfO_2 on InAlAs: A comparative study of interfacial and electrical characteristics

Al_2O_3 and HfO_2 thin films are separately deposited on n-type InAlAs epitaxial layers by using atomic layer deposition(ALD).The interfacial properties are revealed by angle-resolved x-ray photoelectron spectroscopy(AR-XPS).It is demonstrated that the Al_2O_3 layer can reduce interfacial oxidation and trap charge formation.The gate leakage current densities are 1.37×10~6 A/cm~2 and 3.22×10~6 A/cm~2 at+1V for the Al_2O_3/InAlAs and HfO_2/InAlAs MOS capacitors respectively.Compared with the HfO_2/InAlAs metal-oxide-semiconductor(MOS) capacitor,the Al_2O_3/InAlAS MOS capacitor exhibits good electrical properties in reducing gate leakage current,narrowing down the hysteresis loop,shrinking stretch-out of the C-V characteristics,and significantly reducing the oxide trapped charge(Q_(ot)) value and the interface state density(D_(it)).     

热原子层沉积氧化铝对硅的钝化性能及热稳定性

原子层沉积氧化铝已经成为应用于钝化发射极和背面点接触（PERC）型晶硅太阳能电池优异的钝化材料．对于基于丝网印刷技术的太阳能电池,钝化材料的钝化效果及其热稳定性是非常重要的．本文在太阳能级硅片上用热原子层沉积设备制备了20nm和30nm的氧化铝,少子寿命测试结果显示初始沉积的氧化铝薄膜具有一定的钝化效果,在退火后可达到100μs以上,相当于硅表面复合速度小于100cm／s．经过制备传统晶硅太阳能电池的烧结炉后,少子寿命能够保持在烧结前的一半以上,可应用于工业PERC型电池的制备．通过电子显微镜观察到了较厚的氧化铝薄膜有气泡,解释了30nm氧化铝比20nm氧化铝钝化性能和稳定性更差的异常表现．     

Controlled growth of rutile TiO2 by atomic layer deposition on oxidized ruthenium

Crystalline rutile TiO₂ films were grown by atomic layer deposition on oxidized Ru electrodes using a titanium methoxide as the metal precursor and O₃ as the oxidant. A protective layer of ～0.3 nm TiO₂ grown with H₂O as the oxidant was first deposited in order to avoid etching of the Ru bottom electrode by the O₃ used for the growth of the TiO₂ (bulk) layer. Electrical evaluation of the capacitor stacks with TiO₂ as dielectric, RuO₂/Ru and Pt as the bottom and top electrodes respectively, resulted in superior characteristics of the rutile phase as compared to the anatase. (© 2011 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Plasmonic tuning of aluminum doped zinc oxide nanostructures by atomic layer deposition

Currently there is a strong interest in plasmonic materials operating in the near‐infrared (NIR), however, conventional metals such as gold and silver possess high optical losses in this region. In this work we demonstrate localized surface plasmon resonances (LSPRs) with low loss in the NIR region by utilizing atomic layer deposition to deposit thin films of aluminium doped zinc oxide onto silicon nanopillars created via nanopshere lithography. The deposited films have excellent conformality and the LSPRs can be tuned from the mid‐infrared to the NIR by controlling the doping concentration, deposition temperature and nanostructure morphology. (© 2014 WILEY‐VCH Verlag GmbH &Co. KGaA, Weinheim)     

Enhanced water vapor barrier properties for biopolymer films by polyelectrolyte multilayer and atomic layer deposited Al2O3 double-coating

Commercial polylactide (PLA) films are coated with a thin (20 nm) non-toxic polyelectrolyte multilayer (PEM) film made from sodium alginate and chitosan and additionally with a 25-nm thick atomic layer deposited (ALD) Al₂O₃ layer. The double-coating of PEM + Al₂O₃ is found to significantly enhance the water vapor barrier properties of the PLA film. The improvement is essentially larger compared with the case the PLA film being just coated with an ALD-grown Al₂O₃ layer. The enhanced water vapor barrier characteristics of the PEM + Al₂O₃ double-coated PLA films are attributed to the increased hydrophobicity of the surface of these films.