Influence of Concentration of Vanadium in Zinc Oxide on Structural and Optical Properties with Lower Concentration

ZnO films doped with different vanadium concentrations are deposited onto glass substrates by dc reactive magnetron sputtering using a zinc target doped with vanadium. The vanadium concentrations are examined by energy dispersive spectroscopy （EDS） and the charge state of vanadium in ZnO thin films is characterized by x-ray photoelectron spectroscopy. The results of x-ray diffraction （XRD） show that all the films have a wurtzite structure and grow mainly in the c-axis orientation. The grain size and residual stress in the deposited films are estimated by fitting the XRD results. The optical properties of the films are studied by measuring the transmittance. The optical constants （refractive index and extinction coefficient） and the film thickness are obtained by fitting the transmittance. All the results are discussed in relation with the doping of the vanadium.     

Crystalline structure and morphological properties of undoped and Sn doped ZnO thin films

Undoped and tin (Sn) doped ZnO thin films have been prepared by spray pyrolysis method. Effect of Sn dopant on the crystalline structure and morphological properties of ZnO thin films has been investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM) method. XRD patterns confirm that the films have polycrystalline nature. While undoped ZnO film has (101) as the preferred orientation, Sn doped ZnO thin films have (002) as the preferred orientation. Grain sizes, lattice parameters and texture coefficient values of the films were determined. Microstructure was analyzed by SEM and the influence of the doping concentration in the microstructure of the films is investigated.     

钼掺杂氧化锌薄膜的结构、光学和表面等离子体特性研究

室温下,通过直流磁控反应溅射在石英衬底上制备一系列钼掺杂氧化锌薄膜。分别采用X射线衍射(XRD)、原子力显微镜(AFM)、分光光度计及拉曼光谱仪研究了钼掺杂浓度对氧化锌薄膜结构、表面形貌、光学性能和表面等离子体特性的影响。XRD测试结果表明,零掺杂氧化锌薄膜结晶良好,呈c轴择优取向,掺杂后薄膜缺陷增多,结晶质量下降,当掺杂浓度达到3.93 Wt%时,薄膜由c轴择优取向的晶态转变为非晶态。AFM测试结果表明非晶态掺钼氧化锌薄膜表面光滑,粗糙度最低可达489 pm。透射光谱表明所有薄膜样品在可见光范围(400～760 nm)平均透过率均达到80%,禁带宽度随着掺杂浓度的提高从3.28 eV单调增加至3.60 eV。吸收光谱表明氧化锌薄膜表面等离子体共振吸收峰随钼掺杂量的增大发生蓝移,而拉曼光谱表明Mo重掺杂时ZnO薄膜表面拉曼散射信号强度显著降低。通过Mo掺杂获得非晶态氧化锌薄膜,拓宽了氧化锌薄膜材料的应用领域,同时研究了Mo掺杂浓度对氧化锌薄膜表面等离子体的调控作用,这对制备氧化锌基光子器件具有重要参考价值。     

Al掺杂ZnO薄膜的厚度对其结构及磁学性能的影响

采用直流磁控共溅的方法在玻璃基底上制备了不同厚度的Al掺杂ZnO薄膜,并在真空和空气中分别退火.利用X射线衍射仪(XRD)和物理性能测量仪(PPMS)对系列薄膜的结构和磁性进行了表征.XRD结果显示:随着膜厚的增加,晶粒尺寸逐渐增大,薄膜的内应力逐渐减小.在空气退火的薄膜样品中观察到了室温的铁磁性,薄膜的饱和磁化强度M_s 随着膜厚的增加而增大,而矫顽力H_c却随着膜厚的增加而减小. 关键词： Al掺杂ZnO薄膜 薄膜厚度 应力 铁磁性     

Effect of dopants on the structural,optical and electrical properties of sol–gel derived ZnO semiconductor thin films

Undoped, Ga-, In-, Zr-, and Sn-doped ZnO transparent semiconductor thin films were deposited on alkali-free glasses by sol–gel method. 2-methoxyethanol (2-ME) and diethanolamine (DEA) were chosen as a solvent and a stabilizer, respectively. The doping concentration was maintained at 2 at.% in the impurity doping precursor solutions. The effects of different dopants on the structural, optical, and electrical properties of ZnO thin films were investigated. XRD results show that all annealed ZnO-based thin films had a hexagonal (wurtzite) structure. ZnO thin films doped with impurity elements obviously improved the surface flatness and enhanced the optical transmittance. All impurity doped ZnO thin films showed high transparency in the visible range (>91%). The Ga- and In- doped ZnO thin films exhibited higher Hall mobility and lower resistivity than did the undoped ZnO thin film.     

Co,Sn共掺ZnO薄膜结构与光致发光的研究

采用溶胶-凝胶旋涂法在玻璃衬底上制备了Co,Sn掺杂ZnO系列薄膜.通过金相显微镜和X射线衍射(XRD)研究了Co与Sn掺杂对薄膜的表面形貌和微结构的影响.XRD结果表明,所有ZnO薄膜样品都存在(002)择优取向,特别Sn单掺ZnO薄膜的c轴择优取向最为显著,而且晶粒尺寸最大.XPS测试表明样品中Co和Sn的价态分别为2+和4+,证实Co²⁺,Sn⁴⁺进入了ZnO的晶格.室温光致发光谱(PL)显示在所有的样品中都有较强的蓝光双峰发射和较弱的绿光发 关键词： ZnO薄膜 溶胶-凝胶 掺杂 光致发光     

p-type ZnO thin films grown by RF plasma beam assisted Pulsed Laser Deposition

The high exciton binding energy and band gap energy of ZnO thin films open the prospect of fabricating semiconductor lasers in the ultraviolet spectral range. A prerequisite for laser diode fabrication is highly p-doped ZnO which was not reproducibly obtained up to now. Without intentional doping ZnO exhibits n-type conduction. ZnO thin films have been obtained by radio-frequency assisted pulsed laser deposition. A metallic Zn target was used for ablation in an oxygen and nitrogen RF discharge. The electrical and morphological properties of the films grown on Si were studied by Atomic Force Microscopy (AFM), X-ray diffraction (XRD), Transmission Electron Microscopy (TEM), optical absorption and Hall Effect measurements for different ratios between the nitrogen and oxygen content. The AFM images of the as-grown ZnO films reveal high quality surfaces with low values for the surface roughness and a sharp distribution of grains sizes as an effect of the RF discharge. The XRD patterns for all samples exhibit only (002) and (004) peaks indicating that the c-axis is always oriented normal to the substrate surface. The films present p-type conductivity with different carrier concentration and mobility depending on the nitrogen/oxygen ratio.     

Cubic ZnO films obtained at low pressure by molecular beam epitaxy

A zinc oxide thin film in cubic crystalline phase, which is usually prepared under high pressure, has been grown on the Mg O(001) substrate by a three-step growth using plasma-assisted molecular beam epitaxy. The cubic structure is confirmed by in-situ reflection high energy electron diffraction measurements and simulations. The x-ray photoelectron spectroscopy reveals that the outer-layer surface of the film(less than 5 nm thick) is of ZnO phase while the buffer layer above the substrate is of ZnMgO phase, which is further confirmed by the band edge transmissions at the wavelengths of about 390 nm and 280 nm, respectively. The x-ray diffraction exhibits no peaks related to wurtzite ZnO phase in the film. The cubic ZnO film is presumably considered to be of the rock-salt phase. This work suggests that the metastable cubic ZnO films, which are of applicational interest for p-type doping, can be epitaxially grown on the rock-salt substrates without the usually needed high pressure conditions.     

过渡金属与F共掺杂ZnO薄膜结构及磁、光特性

采用溶胶-凝胶法在玻璃衬底上制备了过渡金属元素与F共掺杂Zn_0.98-xTM_xF_0.02O (TM_x=Cu_0.02, Ni_0.01, Mn_0.05, Fe_0.02, Co_0.05)薄膜, 进而利用X射线衍射仪、扫描电子显微镜、紫外-可见透过谱、光致发光及振动样品磁强计等研究了薄膜的表面形貌、微结构、禁带宽度及光致发光(PL)和室温磁学特性. 研究表明: 掺杂离子都以替位的方式进入了ZnO晶格, 掺杂不会破坏ZnO的纤锌矿结构. 其中Zn_0.93Co_0.05F_0.02O薄膜样品的颗粒尺寸最大, 薄膜的结晶度最好且c轴择优取向明显; Zn_0.93Mn_0.05F_0.02O薄膜样品的颗粒尺寸最小, 薄膜结晶度最差且无明显的c轴择优取; Cu, Ni, Fe与F共掺杂样品的颗粒尺寸大小几乎相同. TM掺杂样品均表现出很高的透过率, 同时掺杂后的薄膜样品的禁带宽度都有不同程度的红移. PL谱观察到Zn_0.98-xTM_xF_0.02O薄膜的发射峰主要由较强的紫外发射峰和较弱的蓝光发射峰组成. Zn_0.93Mn_0.05F_0.02O薄膜样品的紫外发光峰最弱, 蓝光发射最强, 饱和磁化强度最大; 与之相反的是Zn_0.96Cu_0.02F_0.02O薄膜, 其紫外发光峰最强, 蓝光发射最弱, 饱和磁化强度最小. 结合微结构和光学性质对Zn_0.98-xTM_xF_0.02O薄膜的磁学性质进行了讨论.     

ZnO：V薄膜后退火处理前后的微结构与发光特性

利用溶胶-凝胶(Sol-gel)法在单晶硅(100)衬底上分别制备了ZnO:V薄膜和纯ZnO薄膜。为进一步研究后退火对ZnO:V薄膜结构和发光性质的影响,在两段式快速退火后又在800℃下进行了后退火处理。X射线衍射的结果表明:后退火处理前,钒(V)的掺入使ZnO结晶质量变差,而800℃退火处理后,从ZnO的衍射峰中可以看出,相对于无V杂样品其结晶质量变好。扫描电子显微镜形貌图中可以看出制备的样品薄膜颗粒大小均匀,薄膜致密度较高。光致发光(PL)谱的研究表明:ZnO:V薄膜在800℃退火处理后,紫外和绿带发光峰均增强,但紫外发光峰增强得更多;与同样条件下制备的纯ZnO薄膜的PL谱比较,发现V掺杂后样品的紫外激子复合发光峰的强度明显增强且峰位发生蓝移,而缺陷引起的绿带发光峰的强度降低。     

Effects of Ti-doped concentration on the microstructures and optical properties of ZnO thin films

The Ti-doped ZnO (ZnO:Ti) thin films have been deposited on glass substrates by radio frequency (RF) reactive magnetron sputtering technique with different Ti doping concentrations. The effect of Ti contents on the crystalline structure and optical properties of the as-deposited ZnO:Ti films was systematically investigated by X-ray diffraction (XRD), scanning electronic microscopy (SEM) and fluorescence spectrophotometer. The XRD measurements revealed that all the films had hexagonal wurtzite type structure with a strong (100) preferential orientation and relatively weak (002), (101), and (110) peaks. It was found that the intensity of the (100) diffraction peaks was strongly dependent on the Ti doping concentration. And the full width at half-maximum (FWHM) of (002) diffraction peaks constantly changed at various Ti contents, which decreased first and then increased, reaching a minimum of about 0.378° at 1.43 at.% Ti. The morphologies of ZnO:Ti films with 1.43 at.% Ti showed a denser texture and better smooth surface. All the films were found to be highly transparent in the visible wavelength region with an average transmittance over 90%. Compared with E_g = 3.219 eV for pure ZnO film, all the doping samples exhibited a blue-shift of E_g. It can be attributed to the incorporation of Ti atoms and raising the concentration of carriers. Five emission peaks located at 412, 448, 486, 520, and 550 nm were observed from the photoluminescence spectra measured at room temperature and the origin of these emissions was discussed.     

Nitrogen doping in pulsed laser deposited ZnO thin films using dense plasma focus

Pulsed laser deposition synthesized ZnO thin films, grown at 400 °C substrate temperature in different oxygen gas pressures, were irradiated with 6 shots of pulsed nitrogen ions obtained from 2.94 kJ dense plasma focus to achieve the nitrogen doping in ZnO. Structural, compositional and optical properties of as-deposited and nitrogen ion irradiated ZnO thin films were investigated to confirm the successful doping of nitrogen in irradiated samples. Spectral changes have been seen in the nitrogen irradiated ZnO thin film samples from the low temperature PL measurements. Free electron to acceptor emissions can be observed from the irradiated samples, which hints towards the successful nitrogen doping in films. Compositional analysis by X-ray photoelectron spectroscopy and corresponding shifts in binding energy core peaks of oxygen and nitrogen confirmed the successful use of plasma focus device as a novel source for nitrogen ion doping in ZnO thin films.     

A comparative study of the microstructures and optical properties of Cu- and Ag-doped ZnO thin films

Cu- and Ag-doped ZnO films were deposited by direct current co-reactive magnetron sputtering technique. The microstructure, the chemical states of the oxygen, zinc, copper and silver and the optical properties in doped ZnO films were investigated by X-ray diffraction spectroscopy (XRD), X-ray photoelectron spectroscopy (XPS) and UV-Visible spectroscopy. XRD analysis revealed that both of Cu- and Ag-doped ZnO films consist of single phase ZnO with zincite structure while the doping elements had an evident effect on the (0 0 2) preferential orientation. The XPS spectra showed that the chemical states of oxygen were different in Cu- and Ag-doped ZnO thin films, which may lead to the shift of the band gap as can be observed in the transmittance and absorption spectra. Meanwhile, the widths of band tails of ZnO films became larger after Cu and Ag doping.     

Effects of doping concentration on properties of Mn-doped ZnO thin films

This paper reports that the radio frequency magnetron sputtering is used to fabricate ZnO and Mn-doped ZnO thin films on glass substrates at 500~°C. The Mn-doped ZnO thin films present wurtzite structure of ZnO and have a smoother surface, better conductivity but no ferromagnetism. The x-ray photoelectron spectroscopy results show that the binding energy of Mn_2p3 / 2 increases with increasing Mn content slightly, and the state of Mn in the Mn-doped ZnO thin films is divalent. The chemisorbed oxygen in the Mn-doped ZnO thin films increases with increasing Mn doping concentration. The photoluminescence spectra of ZnO and Mn-doped ZnO thin films have a similar ultraviolet emission. The yellow green emissions of 4~wt.% and 10~wt.% Mn-doped thin films are quenched, whereas the yellow green emission occurs because of abundant oxygen vacancies in the Mn-doped ZnO thin films after 20~wt.% Mn doping. Compared with pure ZnO thin film, the bandgap of the Mn-doped ZnO thin films increases with increasing Mn content.     

衬底对原位氧化制备的ZnO薄膜结构和光学性质的影响

 采用射频反应溅射法在不同衬底上制备Zn₃N₂薄膜,然后对其原位氧化制备ZnO薄膜。利用X射线衍射分析(XRD)、扫描电子显微镜(SEM)和光致发光谱(PL)等表征技术研究了不同衬底对ZnO薄膜的结晶特性和发光性能的影响。XRD研究结果显示:Zn₃N₂薄膜在500 ℃原位氧化3 h后完全转变为ZnO薄膜,在玻璃和熔融石英衬底上制备的多晶ZnO薄膜无择优取向,而单晶硅（100）衬底上的多晶ZnO薄膜具有较好的沿（002）方向的择优取向。PL测试结果显示:硅和熔融石英衬底上的多晶ZnO薄膜发光性能良好,激子复合产生的紫外发光峰很强,且半高宽较窄,而来自于深能级发射的绿色发光峰很弱;而玻璃衬底上的多晶ZnO薄膜发光性能较差。     

硼对氮掺杂的p型ZnO薄膜的影响

利用分子束外延设备在蓝宝石衬底上生长了B/N共掺的p型ZnO薄膜,对比了B/N共掺和N单掺杂样品的物理学性能。通过X射线光电子能谱测试证明了在薄膜中存在有B和B-N键。B/N共掺样品的空穴浓度比单一N掺杂样品高近两个量级。且ZnO：（B,N）薄膜在两年多的时间内一直显示稳定的p型电导。这是由于B-N键的存在提高了N在ZnO薄膜中的固溶度,且B-N键之间强的键能和B占据Zn位所表现的弱施主特性不会带来强的施主补偿效应,说明B是N掺杂ZnO薄膜的一种良好的共掺元素。     

Structural,electrical and optical studies on spray-deposited aluminium-doped ZnO thin films

Thin films of zinc oxide (ZnO) were deposited on cleaned glass substrates by chemical spray pyrolysis technique using Zn(CH₃COO)₂ as precursor solution. Also, aluminium-doped thin films of ZnO were prepared by using AlCl₃ as doping solution for aluminium. The dopant concentration [Al/Zn atomic percentage (at%)] was varied from 0 to 1.5 at% in thin films of ZnO prepared in different depositions. Structural characterization of the deposited films was performed with X-ray diffraction (XRD) studies. It confirmed that all the films were of zinc oxide having polycrystalline nature and possessing typical hexagonal wurtzite structure with crystallite size varying between 100.7 and 268.6 nm. The films exhibited changes in relative intensities and crystallite size with changes in the doping concentration of Al. The electrical studies established that 1 at% of Al-doping was the optimum for enhancing electrical conduction in ZnO thin films and beyond that the distortion caused in the lattice lowered the conductivity. The films also exhibited distinct changes in their optical properties at different doping concentrations, including a blue shift and slight widening of bandgap with increasing Al dopant concentration.     

Co与Cu掺杂ZnO薄膜的制备与光致发光研究

采用溶胶-凝胶旋涂法在玻璃衬底上制备了Co, Cu单掺杂及Co,Cu共掺杂ZnO薄膜.用金相显微镜观察了Co与Cu掺杂对ZnO薄膜形貌的影响.X射线衍射（XRD）研究揭示所有ZnO薄膜样品都存在（002）择优取向,在Cu单掺的ZnO薄膜中晶粒尺寸最大.对所有样品的室温光致发光测量都观察到较强的蓝光双峰发射和较弱的绿光发射,其中长波长的蓝光峰和绿光峰都能够通过掺杂进行控制.对不同掺杂源的ZnO薄膜发光性能进行了分析,认为蓝光峰来源于电子由导带底到锌空位能级的跃迁及锌填隙到价带顶的跃迁,绿光峰是由于掺杂造成的 关键词： ZnO薄膜 溶胶-凝胶 Co Cu掺杂 光致发光     

Effects of oxygen pressures on pulsed laser deposition of ZnO films

Zinc oxide (ZnO) thin films on Si (1 1 1) substrates were deposited by pulsed laser ablation of ZnO target at different oxygen pressures. A pulsed Nd:YAG laser with wavelength of 1064 nm was used as laser source. The deposited thin films have been characterized by X-ray diffraction (XRD), Atomic force microscopy (AFM), and Raman spectroscopy. XRD measurements indicate that the ZnO thin films deposited at the oxygen pressure of 1.3 Pa have the best crystalline quality. AFM results show that the surface roughness of ZnO film increases with the increase of oxygen pressure. The Raman results indicate that oxygen ambient plays an important role in removing defects due to excess zinc.     

Fabrication of p-ZnO:ZrN thin films by RF magnetron sputtering

An attempt has been made to fabricate p-ZnO thin films from the ZrN mixed ZnO targets by RF magnetron sputtering. The targets of different ZrN concentrations (0, 1, 2, and 4?mol%) have been prepared by solid-state reaction route. The ZrN-codoped ZnO films grown on semi-insulating Si (100) substrates have been characterized by X-ray diffraction (XRD), photoluminescence (PL), Hall effect measurement, time-of-flight secondary ion mass spectrometer (ToF-SIMS), and atomic force microscopy (AFM). XRD studies reveal that all films are oriented along (002) plane. The Hall measurements showed p-conductivity for 1 and 2?mol% ZrN-codoped ZnO films. Further, it has been found that 1?mol% ZrN-codoped film has low resistivity (7.5?×?10^?2?Ω?cm) and considerable hole concentration (8.2?×?10¹⁸?cm^?3) by optimum incorporation of nitrogen due to best codoping. The red shift in near-band-edge emission observed from PL well acknowledged the p-conduction in 1 and 2?mol% ZrN-codoped ZnO film. The incorporation of N and Zr atoms in the ZnO matrix has been confirmed by ToF-SIMS analysis. The increase in peak to valley roughness (R _pv) with increase of doping concentration has been observed from AFM analysis. ZnO homojunction has also been fabricated with the best codoped p-ZnO film and it showed typical rectification behavior of a diode. The junction parameters have also been determined for the fabricated homojunction.