Optical anisotropy and surface morphology of InGaAs lattice-mismatched with GaAs(0 0 1)

We investigated surface morphology and optical anisotropy of strained InGaAs films grown on GaAs(0 0 1) substrate using atomic force microscopy (AFM) and reflectance difference/reflectance anisotropy spectroscopy (RDS/RAS). High temperature (HT)-grown samples were found to have a rippled surface structure, however for films grown using a low temperature (LT) growth technique, the surface morphology was significantly improved, without the ripple structure seen on the HT samples. Furthermore, ex situ RD spectra of LT-grown samples showed notable peaks near the critical energies of band structure originated from bulk electronic transitions.     

牺牲Ni退火对硅衬底GaN基发光二极管p型接触影响的研究

本文通过在硅衬底发光二极管(LED)薄膜p-GaN表面蒸发不同厚度的Ni覆盖层,将其在N₂ ∶O₂=4 ∶1的气氛中、400℃—750℃的温度范围内进行退火,在去掉薄膜表面Ni覆盖层之后制备Pt/p-GaN欧姆接触层.实验结果表明:退火温度和Ni覆盖层厚度均对硅衬底GaN基LED薄膜p型欧姆接触有重要影响,Ni覆盖退火能够显著降低p型层中Mg受主的激活温度.经牺牲Ni退火后,p型比接触电阻率随退火温度的升高呈先变小后变大的规律,随Ni覆盖层厚度的增加呈先变小后变 关键词： 氮化镓 发光二极管 牺牲Ni退火 p型接触     

Effects of growing conditions on the electric and magnetic properties of strained La2/3Sr1/3MnO3 thin films

We investigate the growing condition dependences of magnetic and electric properties of the La_2/3Sr_1/3MnO₃ thin films grown on SrTiO₃（001） substrates.With reducing the film thickness and growth pressure,the Curie temperature（T_c）drops off,and the magnetism and metallicity are suppressed.At an appropriate deposition temperature,we can obtain the best texture and remarkably enhance the magnetic and electrical properties.However,the resistivity of film cannot be modulated by changing the dc current and green light intensity.This result may be induced by the coherent strains in the epitaxially grown film due to its lattice mismatching that of the SrTiO₃ substrate.Furthermore,we show that the relations between the magnetism and the resistivity for the typical films with different thickness values.For the 13.4-nm-thick film,the R-T curve presents two transition behaviors:insulator-to-metal and metal-to-insulator in the cooling process:the former corresponds to magnetic transition,and the later correlates with thermal excitation conduction.     

磷离子注入纳米金刚石薄膜的n型导电性能与微结构研究

系统研究了磷离子注入并在不同温度退火后的纳米金刚石薄膜的微结构和电学性能.研究表明,当退火温度达到800 ℃以上时,薄膜呈良好的n型电导.Raman光谱和电子顺磁共振谱的结果表明,薄膜中金刚石相含量越高和完整性越好,薄膜电阻率越低. 这说明纳米金刚石晶粒为薄膜提供了电导.1000 ℃退火后,薄膜晶界中的非晶石墨相有序度提高,碳悬键数量降低,薄膜电阻率升高.薄膜导电机理为磷离子注入的纳米金刚石晶粒提供了n型电导,非晶碳晶界为其电导提供了传输路径. 关键词： 纳米金刚石薄膜 n型 磷离子注入     

多晶TaN1-δ薄膜的电输运性质研究

利用射频溅射法在石英玻璃基底上制备了一系列面心立方结构的多晶TaN_1-δ薄膜, 并对其晶体结构和2–350 K温度范围的电子输运性质进行了系统研究. 薄膜呈多晶结构, 并且平均晶粒尺寸随着基底温度的升高逐渐增大. 电输运测量结果表明, TaN_1-δ薄膜在5 K以下表现出类似超导体-绝缘体颗粒膜的电输运性质; 随着温度的升高, 薄膜在10–30 K表现出类似金属-绝缘体颗粒膜的性质; 在70 K以上, 热涨落诱导的遂穿导电机理主导着电阻率的温度行为. 我们的结果表明: TaN_1-δ多晶薄膜的类颗粒膜属性使其具有较高的电阻率和负的电阻温度系数.     

Physical properties of carbon films obtained by methane pyrolysis in an electric field

A method of synthesizing carbon films on single-crystal silicon substrates by methane pyrolysis in an electrical field is suggested. The pressure and temperature arising in a working chamber when the substrate is exposed to C^–4 ions during pyrolysis are measured. Ion bombardment generates nuclei in the form of fibers about 2 μm in diameter providing the growth of a polycrystalline film. The resulting material is examined using electron microscopy and photo- and cathodoluminescence. Synthesized films are a composite material the matrix of which contains nanoclusters of a dissimilar crystalline nature. The effect of considerable two-stage decrease in the resistivity of the film material with increasing temperature from 300 to 1750 K is discovered. This points to the semiconducting properties of thick carbon films.     

Optical and Electrical Properties Evolution of Diamond-Like Carbon Thin Films with Deposition Temperature

Optical and electrical properties of diamond-like carbon （DLC） films deposited by pulsed laser ablation of graphite target at different substrate temperatures are reported. By varying the deposition temperature from 400 to 25℃, the film optical transparency and electrical resistivity increase severely. Most importantly, the transparency and resistivity properties of the DLC films can be tailored to approaching diamond by adjusting the deposition temperature, which is critical to many applications. DLC films deposited at low temperatures show excellent optical transmittance and high resistivity. Over the same temperature regime an increase of the spa bonded C content is observed using visible Raman spectroscopy, which is responsible for the enhanced transparency and resistivity properties.     

Opto-Electronic Properties of MBE-Grown ZnSSe Thin Films on ITO Substrates

The opto-electronic properties of molecular-beam-epitaxy (MBE)-grown ZnSSe thin films on indium-tin-oxide (ITO) glass substrates were investigated in this work. Ultraviolet (UV) photoresponsivity as high as 0.01 A/W and three orders of visible rejection power were demonstrated. The results of d.c. resistivity measurements revealed that the resistivity of the ZnSSe thin films decreased as the crystal size increases and reaches a value of 4.3 × 10¹¹ Ω cm for a thin film grown at the optimized substrate temperature of 290°C. The results of a.c. impedance measurements performed in the frequency range of 40 to 4000 Hz further indicated that the impedance of this alloy thin film can provide a good match with the liquid crystal layer of a liquid crystal light valve for UV imaging applications.     

磁控溅射制备氧化硅薄膜生长速率

氧化硅薄膜是半导体工业中常见的薄膜材料,通常采用化学气相沉积方法制备。但是这种制备方法存在缺欠。采用磁控溅射的方法首先在石英衬底上制备了氧化硅薄膜。研究了射频功率、氧气含量和溅射压强对氧化硅薄膜沉积速率的影响。发现沉积速率随着射频功率的增加而增加;随着氧气含量的增加,先减小后增大;当溅射压强在0.4~0.8 Pa之间变化时,沉积速率变化很小,当溅射压强超过0.8 Pa时沉积速率迅速下降。讨论了不同生长条件下造成氧化硅薄膜生长速率变化的原因。     

Electron transport in semiconducting nanoparticle and nanocluster carbon-polymer composites

The electron transport properties of two types of carbon-polyimide (C-PI) nanocomposite thin films have been evaluated. Conductive nanocomposites formed by incorporation of 30 nm carbon particles prior to polymer cross linking (ex situ formation) has been compared to high energy ion beam irradiation in situ formation of nanoscale carbon clusters within the polymer composite. Addition of carbon nanoparticles were able to reduce the resistivity by 13 orders of magnitude for 8 vol% carbon content. The irradiated in situ formed film showed a comparable resistivity to this 8% C-PI film. All the films exhibited negative temperature coefficient of resistance (NTCR) behaviour. While in the ex situ films the NTCR decreased progressively with increasing temperature above 350 K, the in situ film exhibited a constant NTCR value at ambient as well as elevated temperatures indicating that films formed by ion beam irradiation eliminate possible clustering of nanoparticles prior to crosslinking seen in the ex situ films. The optimum hop energies for the ex situ films ranged from 23.1 to 8.05 meV when carbon content increased from 1 to 8 vol% and the corresponding value for the in situ formed film was 34.94 meV. These films had appreciable NTCR values, and were evaluated for their thermistor behaviour as a class of material with potential for temperature sensing devices.     

生长温度对Ga掺杂ZnO薄膜光电性能的影响

在不同衬底温度(室温~750 ℃)条件下,采用脉冲激光沉积(PLD)方法在石英玻璃和单晶硅(111)衬底上制备了Ga掺杂ZnO(GZO)薄膜。结果显示:衬底温度的变化导致衬底表面吸附原子扩散速率和脱附速率的不同,从而导致合成薄膜结晶质量的差异,衬底温度450 ℃时制备的GZO薄膜具有最好的结晶特性;GZO薄膜中载流子浓度随衬底温度升高而单调减小的现象与GZO薄膜中的本征缺陷密切相关,晶界散射强度的变化导致迁移率出现先增大后减小的趋势,衬底温度450 ℃时制备的GZO薄膜具有最小的电阻率~0.02 Ω·cm;随着衬底温度的升高,薄膜载流子浓度的单调减小导致了薄膜光学带隙变窄,所有合成样品的平均可见光透过率均达到85%以上。采用PLD方法制备GZO薄膜,衬底温度的改变可以对薄膜的光电性能起到调制作用。     

AgO_x界面插入层对GZO电极LED器件性能的影响

采用磁控溅射的方法在p-GaN上制备了GZO透明导电薄膜,通过在p-GaN和GZO界面之间插入AgOx薄层来改善LED器件的接触性能。研究结果表明:氮气退火后,采用界面插入层的AgOx/GZO薄膜电阻率为5.8×10-4Ω.cm,在可见光的透过率超过80%。AgOx界面插入层有效地降低了GZO与p-GaN之间的接触势垒,表现出良好的欧姆接触特性,同时使LED器件的光电性能获得了显著的提高。在50 mA的注入电流下,相比于常规的GZO电极LED器件,AgOx/GZO电极LED器件的正向电压由9.68 V降至6.92 V,而发光强度提高了13.5%。     

Studies on highly resistive ZnO thin films grown by DC-discharge-assisted pulsed laser deposition

It was found that by changing the substrate temperature from room temperature to ～850 °C, ZnO thin films with widely varying resistivity values could be grown on sapphire substrates using DC-discharge-assisted pulsed laser deposition (PLD) in oxygen ambient. The resistivity of the film grown at room temperature was too high to measure using our existing setup. However, as the growth temperature was increased from 550 °C to 750 °C, the resistivity first decreased slowly from ～14.0 to 4.4 Ω?m and then dropped suddenly to get saturated at ～2.0×10^?3 Ω?m as the growth temperature was further increased. In contrast to these, when there was no DC-discharge, the variation of resistivity for ZnO thin films grown by PLD was marginal up to the substrate temperature of ～850 °C. The reason for these observations was found to be the combined effects of reduction in donor defect densities like oxygen vacancies and zinc interstitials, introduction of acceptor type defects like interstitial oxygen and zinc vacancies, and the resultant poor carrier mobility at lower growth temperatures. At higher growth temperatures (800 °C and above), the appearance of oxygen vacancies and increase in mobility due to better crystalline quality were found to be responsible for reducing the resistivity. The PL of these films had significant emission in the green and red regions of the spectrum due to the aforesaid defect related transitions. Such highly resistive and luminescent films might be suited for applications such as resistive RAM, UV-photo detector, TFT, piezoelectric, transparent phosphor, and broadband LED applications.     

GaN基紫光LED的高反射率p型欧姆接触

研究用于GaN基大功率倒装焊(Flip-chip)紫光LED(UV-LED)的高反射率p型欧姆接触的电学和光学性能。用磁控溅射的方法在GaN基LED外延片表面沉积了不同厚度Ag,Al,Au和Pd四种金属,测量了样品的反射率和透射率。结合同步辐射高强度X射线衍射和AFM对金属薄膜的晶体结构进行分析,并对表面形貌进行了观测,对由金属薄膜构成的多层膜结构及其对光反射率的作用机理进行了研究。测量结果表明,在入射光波长为400nm时,Ni/Au/Ag和Ni/Au/Al电极的反射率比Ni/Au的反射率提高了三倍。同时与p-GaN有良好的欧姆接触特性。     

温度对AZO薄膜红外辐射性能的影响

随着全球资源的减少和环境的恶化,节能减排已成为人们关注的焦点,具有保温隔热功能的低辐射玻璃成为研究的热点。提高玻璃保温隔热性能最有效的方法就是在其表面涂覆低辐射率层。原材料丰富、导电性能好、可见光透过率高等优势使得Al掺杂ZnO (AZO)薄膜成为最具潜力的低辐射率层。系统研究了温度对AZO薄膜红外辐射性能的影响,分析了变化机理。首先研究了在一定的温度下持续一段时间后,AZO薄膜的红外比辐射率的变化情况。然后研究了在变温环境中红外比辐射率的变化情况。采用直流磁控溅射法在室温下玻璃基片上沉积500 nm厚的AZO薄膜,将薄膜放到马弗炉中进行热处理,在100～400 ℃空气气氛下保温1 h,随炉冷却。采用X射线衍射仪对AZO薄膜进行物相分析,采用扫描电子显微镜观察薄膜表面形貌变化。利用四探针测试法测量AZO薄膜的电阻率,采用红外比辐射率测试仪测试薄膜红外比辐射率, 可见分光光度计测量可见光谱。测试的结果表明,薄膜热处理前后均为六角纤锌矿结构,(002)择优取向。300 ℃及以下热处理1 h后,(002)衍射峰增强,半高宽变窄,晶粒尺寸长大。随着热处理温度的升高,薄膜的电阻率先减小后增大,200 ℃热处理后的薄膜具有最小的电阻率(0.9×10-3 Ω·cm)。热处理温度升高,晶粒长大使得薄膜电阻率降低。热处理温度过高,薄膜会从空气中吸收氧,电阻率下降。薄膜的红外比辐射率变化趋势和电阻率的一致,在200 ℃热处理后获得最小值(0.48)。自由电子对红外光子有较强的反射作用,当电阻率低,自由电子浓度高的时候,更多的红外光子被反射,红外辐射作用弱,红外比辐射率小。薄膜的可见光透过率随着热处理温度的升高先减小后增大,200 ℃热处理后的薄膜的可见光透过率最小,但仍高达82%。这种变化是由于自由电子浓度变化引起的,自由电子对可见光有很强的反射作用。选取未热处理和200 ℃热处理后的样品进行变温红外比辐射率的测量,将样品放在可加热的样品台上,位置固定,在室温到350 ℃的升温和降温过程中每隔25 ℃测量一次红外比辐射率,结果表明,在室温到350 ℃的温度范围内,AZO薄膜的红外比辐射率在升温过程中随着温度的上升而增大,在降温过程中减小,经过整个升、降温过程后,薄膜的红外比辐射率增大。     

退火温度和退火气氛对Ni/Au与p-GaN之间欧姆接触性能的影响

研究了不同退火温度和气氛对Ni/Au与p-GaN之间欧姆接触性能的影响. 采用圆形传输线模型方法得到不同退火温度和不同退火气氛下的比接触电阻率. 结果表明, 较适宜的退火温度为500 ℃左右, 退火温度太高或太低都会导致比接触电阻率的增大; 较适宜的退火气氛为适量含氧的氮气气氛, 且氧气含量对比接触电阻率大小的影响并不显著. 经过对退火条件的优化, 得到的比接触电阻率可达7.65×10^-4 Ω·cm². 关键词： p-GaN 欧姆接触 圆形传输线模型 快速热退火     

p型GaN低温粗化提高发光二极管特性

利用金属有机物化学气相沉积技术在蓝宝石衬底上低温生长GaN:Mg薄膜,对不同源流量的GaN:Mg材料特性进行优化研究.研究表明二茂镁(CP2Mg)和三甲基镓(TMGa)物质的量比([CP2Mg]/[TMGa])在1.4×10-3—2.5×10-3范围内,随[CP2Mg]/[TMGa]增加,晶体质量提高,空穴浓度线性增加.当[CP2Mg]/[TMGa]为2.5×10-3时获得空穴浓度与在较高温度生长获得的空穴浓度相当,且薄膜表面较粗糙.采用[CP2Mg]/[TMGa]为2.5×10-3的p型GaN层制备的发光二极管,在注入电流为20mA时,输出光强提高了17.2%.     

p型氮化镓的低温生长及发光二极管器件的研究

采用金属有机物化学气相淀积技术(MOCVD)在蓝宝石衬底上低温(870—980℃)生长p型氮化镓 (p-GaN).用Hall测试仪测量材料的电学性能，发现当温度低于900℃时，材料的电阻率较高 ；在900—980℃均可获得导电性能良好的p-GaN.另外，电导性能除与掺杂浓度有关，还与p- GaN生长条件有关，氮镓摩尔比过低导电性能就较差，过高则会引起表面粗糙.采用优化后的 p-GaN制作了绿光发光二极管器件，发现生长温度越低器件发光强度越高，反向电压也越高 ，但正向电压只是略有升高. 关键词： Ⅲ-Ⅴ族半导体 氮化镓 发光二极管 金属有机物化学气相淀积     

CH基团与金刚石(111)面的碰撞反应及其对碳膜生长的影响

等离子体增强化学气相沉积技术中的碳膜选择性自组装机理是高性能碳膜制备过程中的挑战性基础课题.采用经典分子动力学方法,模拟了不同能量(1.625-65 eV)的CH基团在清洁金刚石和吸氢金刚石(111)面上的轰击行为,获得了吸附、反弹、反应等各类事件的发生概率,并据此探讨了含氢碳膜制备过程中CH基团的贡献.结果表明,随着入射能量的增加,CH基团对薄膜生长的贡献由单纯的吸附、反弹机理向反应、吸附混合机理转变,其中最主要的反应过程是释放一个或两个氢原子的反应,而释放氢分子的反应则很少发生.这些反应不仅使薄膜生长过程更均匀、薄膜表面更平整,还降低了薄膜的氢含量.生长机理的转变导致低能量条件下所成薄膜中的多数碳原子都包含一个氢原子作为配位原子,而高能量条件下的薄膜中的碳原子则很少有氢原子作为配位原子.另外,通过分析sp~3-C和sp~2-C数目的变化,研究了CH基团对金刚石基底的破坏作用.     

退火温度对硼掺杂纳米金刚石薄膜微结构和p型导电性能的影响

采用热丝化学气相沉积法制备硼掺杂纳米金刚石 (BDND) 薄膜, 并对薄膜进行真空退火处理, 系统研究退火温度对BDND薄膜微结构和电学性能的影响. Hall效应测试结果表明掺B浓度为5000 ppm (NHB) 的样品的电阻率较掺B浓度为500 ppm (NLB) 的样品的低, 载流子浓度高, Hall迁移率下降. 1000 ℃退火后, NLB和NHB 样品的迁移率分别为53.3和39.3 cm²·V^-1·s^-1, 薄膜的迁移率较未退火样品提高, 电阻率降低. 高分辨透射电镜、紫外和可见光拉曼光谱测试结果表明, NLB样品的金刚石相含量较NHB样品高, 高的硼掺杂浓度使薄膜中的金刚石晶粒产生较大的晶格畸变. 经1000 ℃退火后, NLB和NHB薄膜中纳米金刚石相含量较未退火时增大, 说明薄膜中部分非晶碳转变为金刚石相, 为晶界上B扩散到纳米金刚石晶粒中提供了机会, 使得纳米金刚石晶粒中B浓度提高, 增强纳米金刚石晶粒的导电能力, 提高薄膜电学性能. 1000 ℃退火能够恢复纳米金刚石晶粒的晶格完整性, 减小由掺杂引起的内应力, 从而提高薄膜的电学性能. 可见光Raman光谱测试结果表明, 1000℃退火后, Raman谱图中反式聚乙炔 (TPA) 的1140 cm^-1峰消失, 此时薄膜电学性能较好, 说明TPA减少有利于提高薄膜的电学性能. 退火后金刚石相含量的增大、金刚石晶粒的完整性提高及TPA含量的大量减少有利于提高薄膜的电学性能. 关键词： 硼掺杂纳米金刚石薄膜 退火 微结构 电学性能