电化学制备薄黑硅抗反射膜

采用计算机控制电流密度按指数规律衰减对单晶硅进行电化学腐蚀,得到了折射率随薄膜厚度连续均匀变化的抗反射膜,即黑硅样品. 这种在制取上快速、经济和工艺非常简单的样品,不仅在较宽波段范围内反射率小于5%,且整个薄膜厚度不足1μm. 利用传输矩阵方法对黑硅样品的反射谱进行模拟,得到了理论与实验符合较好的结果. 关键词： 多孔硅 折射率 抗反射膜 黑硅     

Low-porosity porous silicon nanostructures on monocrystalline silicon solar cells

In this work we present a study of low-porosity porous silicon (PS) nanostructures stain etched on monocrystalline silicon solar cells. The PS layers reduce the reflectance, improve the diffusion of dopants by rapid thermal processes, and increase the homogeneity of the sheet resistance. Some samples were subjected to chemical oxidation in HNO₃ to reduce the porosity of the surface layer. After the diffusion process, deposition of a SiN_x antireflection layer, and screen printing of the samples, an efficiency of 15.5% is obtained for low-porosity PS solar cells, compared with an efficiency of 10.0% for standard PS cells and 14.9% for the reference Cz cells.     

Boron-doped nanocrystalline silicon thin films for solar cells

This article reports on the structural, electronic, and optical properties of boron-doped hydrogenated nanocrystalline silicon (nc-Si:H) thin films. The films were deposited by plasma-enhanced chemical vapour deposition (PECVD) at a substrate temperature of 150 °C. Crystalline volume fraction and dark conductivity of the films were determined as a function of trimethylboron-to-silane flow ratio. Optical constants of doped and undoped nc-Si:H were obtained from transmission and reflection spectra. By employing p⁺ nc-Si:H as a window layer combined with a p′ a-SiC buffer layer, a-Si:H-based p-p′-i-n solar cells on ZnO:Al-coated glass substrates were fabricated. Device characteristics were obtained from current-voltage and spectral-response measurements.     

Structural and optical features of nanoporous silicon prepared by electrochemical anodic etching

Nanoporous silicon (NPS) samples were prepared by electrochemical anodic etching of p-type (0 0 1) silicon wafers in HF solution, and some of them were aged in air. The nanostructural, optical and chemical features of the NPS were investigated in terms of etching and aging conditions. The surface of the porous Si exhibits an etched layer with a thickness of 30–40 nm; this layer appears to consist of aggregates of 5–10 nm size nano-crystallites. The NPS exhibited broad photoluminescence (PL) spectra with its peak in the red light region (740 nm). After aging the porous samples for 4 weeks in air, we observed the PL intensity became approximately a fifth of that of the as-prepared one, along with a blue shift. It is very likely that the blue shift of the PL peak was caused by the shrinkage of the Si nano-crystallites due to the oxidation in the surface of the nano-crystallites.     

Development of sulphurized SnS thin film solar cells

Thin films of tin sulphide (SnS) have been grown by sulphurization of sputtered tin precursor layers in a closed chamber. The effect of sulphurization temperature (T_s) that varied in the range of 150–450 °C for a fixed sulphurization time of 120 min on SnS film was studied through various characterization techniques. X-ray photoelectron spectroscopy analysis demonstrated the transformation of metallic tin layers into SnS single phase for T_s between 300 °C and 350 °C. The X-ray diffraction measurements indicated that all the grown films had the (111) crystal plane as the preferred orientation and exhibited orthorhombic crystal structure. Raman analysis showed modes at 95 cm⁻¹, 189 cm⁻¹ and 218 cm⁻¹ are related to the A_g mode of SnS. AFM images revealed a granular change in the grain growth with the increase of T_s. The optical energy band gap values were estimated using the transmittance spectra and found to be varied from 1.2 eV to 1.6 eV with T_s. The Hall effect measurements showed that all the films were p-type conducting nature and the layers grown at 350 °C showed a low electrical resistivity of 64 Ω-cm, a net carrier concentration of 2 × 10¹⁶ cm⁻³ and mobility of 41 cm² V⁻¹ s⁻¹. With the use of sprayed Zn_0.76Mg_0.24O as a buffer layer and the sputtered ZnO:Al as window layer, the SnS based thin film solar cell was developed that showed a conversion efficiency of 2.02%.     

Biological functionalization and patterning of porous silicon prepared by Pt-assisted chemical etching

Porous silicon fabricated via Pt-assisted chemical etching of p-type Si (1 0 0) in 1:1:1 EtOH/HF/H₂O₂ solution possesses a longer durability in air and in aqueous media than anodized one, which is advantageous for biomedical applications. Its surface SiHx (x = 1 and 2) species can react with 10-undecylenic acid completely under microwave irradiation, and subsequent derivatizations of the end carboxylic acid result in affinity capture of proteins. We applied two approaches to produce protein microarrays: photolithography and spotting. The former provides a homogeneous microarray with a very low fluorescence background, while the latter presents an inhomogeneous microarray with a high noise background.     

高压射频等离子体增强化学气相沉积制备高效率硅薄膜电池的若干关键问题研究

报道了采用高压射频等离子体增强化学气相沉积(RF-PECVD) 制备高效率单结微晶硅电池和非晶硅/微晶硅叠层电池时几个关键问题的研究结果, 主要包括: 1)器件质量级本征微晶硅材料工艺窗口的确定及其结构和光电性能表征; 2)孵化层的形成机理以及减小孵化层的有效方法; 3)氢稀释调制技术对本征层晶化率分布及其对提高电池性能的作用; 4)高电导、高晶化率的微晶硅p型窗口层材料的获得, 及其对减小微晶硅电池p/i界面孵化层厚度和提高电池性能的作用等. 在解决上述问题的基础上, 采用高压RF-PECVD制备的单结微晶硅电池效率达8.16%, 非晶硅/微晶硅叠层电池效率11.61%.     

The effect of anti-reflection coating of porous silicon on solar cells efficiency

Anti-reflection coatings of solar cells have been fabricated using different techniques. The techniques used include SiO₂ thermal oxidation, ZnO/TiO₂ sputtering deposition and porous silicon prepared by electrochemical etching. Surface morphology and structural properties of solar cells were investigated by using scanning electron microscopy and atomic forces microscopy. Optical reflectance was obtained by using optical reflectometer. I-V characterizations were studied under 80 mW/cm² illumination conditions. Porous silicon was found to be an excellent anti-reflection coating against incident light when it is compared with another anti-reflection coating and exhibited good light-trapping of a wide wavelength spectrum which produced high efficiency solar cells.     

Plasmon enhanced light trapping in thin film GaAs solar cells by Al nanoparticle array

Light trapping is a crucial factor to enhance the performance of thin film solar cells. For effective light trapping, we introduced Al nanoparticle array on the top and rear surface of thin film GaAs solar cells. The effect of both array on the optical absorption and current density of solar cells is investigated by using finite difference time domain (FDTD) method. The optimization process of top and rear array in solar cells is done systematically. The results indicate that by plasmonic action of arrays, the optical absorption is significantly enhanced and optimized structure yields a current density of 25.77 mA/cm². These enhancements are mainly attributed to surface plasmon effects induced by Al nanoparticles and the light grating properties of the arrays.     

Tuning of the open‐circuit voltage by wide band‐gap absorber and doped layers in thin film silicon solar cells

We present an experimental study combined with computer simulations on the effects of wide band‐gap absorber and window layers on the open‐circuit voltage (V_oc) in single junction thin film silicon solar cells. The quantity ΔE_p, taking as the difference between the band gap and the activation energy in ?p? layer, is treated as a measure of the p‐layer properties and shows a linear relation with V_oc over a range of 100 mV with a positive slope of around 430 mV/eV. Two limiting mechanisms of V_oc are identified: the built‐in potential at lower ΔE_p and the band gap of the absorber layer at higher ΔE_p. The results of the experimental findings are confirmed by computer simulations. (© 2015 WILEY‐VCH Verlag GmbH &Co. KGaA, Weinheim)     

The characteristic of Cu2ZnSnS4 thin film solar cells prepared by sputtering CuSn and CuZn alloy targets

Recent study shows that the main reason for limiting CZTS device performance lies in the low open circuit voltage, and crucial factor that could affect the V_oc is secondary phases like ZnS existing in absorber layer and its interfaces. In this work, the Cu₂ZnSnS₄ thin film solar cells were prepared by sputtering CuSn and CuZn alloy targets. Through tuning the Zn/Sn ratios of the CZTS thin films, the crystal structure, morphology, chemical composition and phase purity of CZTS thin films were characterized by X-Ray Diffraction (XRD), scanning electron microscopy (SEM) equipped with an energy dispersive spectrometer (EDS) and Raman spectroscopy. The statistics data show that the CZTS solar cell with a ratio of Zn/Sn = 1.2 have the best power convention efficiency of 5.07%. After HCl etching process, the CZTS thin film solar cell with the highest efficiency 5.41% was obtained, which demonstrated that CZTS film solar cells with high efficiency could be developed by sputtering CuSn and CuZn alloy targets.     

Optimized emitter contacting on multicrystalline silicon thin film solar cells

We present an optimized contacting scheme for multicrystalline silicon thin film solar cells on glass based on epitaxially crystallized emitters with a thin Al₂O₃ layer and a silver back reflector. In a first step a 6.5 µm thick amorphous silicon absorber layer is crystallized by a diode laser. In a second step a thin silicon emitter layer is epitaxially crystallized by an excimer laser. The emitter is covered by an Al₂O₃ layer with a thickness ranging from 1.0 nm to 2.5 nm, which passivates the surface and acts as a tunnel barrier. On top of the Al₂O₃ layer a 90–100 nm thick silver back reflector is deposited. The Al₂O₃ layer was found to have an optimal thickness of 1.5 nm resulting in solar cells with back reflector that achieve a maximum open‐circuit voltage of 567 mV, a short‐circuit current density of 27.9 mA/cm², and an efficiency of 10.9%. (© 2015 WILEY‐VCH Verlag GmbH &Co. KGaA, Weinheim)     

Unlinking absorption and haze in thin film silicon solar cells front electrodes

We study the respective influence of haze and free carrier absorption (FCA) of transparent front electrodes on the photogenerated current of micromorph thin film silicon solar cells. To decouple the haze and FCA we develop bi‐layer front electrodes: a flat indium tin oxide layer assures conduction and allows us to tune FCA while the haze is adjusted by varying the thickness of a highly transparent rough ZnO layer. We show how a minimum amount of FCA leads only to a few percents absorption for a single light path but to a strong reduction of the cell current in the infrared part of the spectrum. Conversely, a current enhancement is shown with increasing front electrode haze up to a saturation of the current gain. This saturation correlates remarkably well with the haze of the front electrode calculated in silicon. This allows us to clarify the requirements for the front electrodes of micromorph cells. (© 2010 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

薄膜硅/晶体硅异质结电池中本征硅薄膜钝化层的性质及光发射谱研究

本文采用甚高频等离子体化学气相沉积技术 (VHF-PECVD) 制备薄膜硅/晶体硅异质结电池中的本征硅薄膜钝化层, 光发射谱 (OES) 测量技术研究了硅薄膜沉积过程中等离子体发光谱随时间的变化. 结果表明: 在实验优化条件下等离子体发光谱很快达到稳定 (大约25 s), 并且SiH^*/H_α^* 的比值随时间变化较小, 避免了生长过程中硅薄膜结构的不均匀性, 这主要是SiH₄没有完全耗尽避免了SiH₄的反向扩散. 进一步研究了沉积参数对稳态发光谱和硅薄膜性质的影响, 结果表明: 随着硅烷浓度增加, H_α^*峰强度减小, SiH^*峰强度增加, 薄膜从微晶转变成非晶, 非晶硅薄膜钝化效果好; 随着沉积气压增大, H_α^*和 SiH^*峰强度先增加后减小, 高气压下H_α^*和 SiH^*峰强度下降主要是反应前驱物的聚合形成高聚合物, 不利于形成高质量的硅薄膜, 因此钝化效果下降; 随着反应功率密度增加, H_α^*和 SiH^*峰强度增大, 当功率密度为150 mW/cm² 趋于饱和, 硅薄膜的致密度和钝化效果也开始下降, 50 mW/cm²的低功率密度下硅薄膜钝化效果差可能是由于原子H 浓度低, 不能完全钝化单晶硅表面的悬挂键. 关键词： 薄膜硅 异质结 光发射谱 钝化     

Photonic nanostructures for advanced light trapping in silicon solar cells: the impact of etching on the material electronic quality

Dry plasma etching, commonly used by the Photonics community as the etching technique for the fabrication of photonic nanostructures, could be a source of device performance limitations when used in the frame of silicon photovoltaics. So far, the lack of silicon solar cells with state‐of‐the‐art efficiencies utilizing nanophotonic concepts shows how challenging their integration is, owing to the trade‐off between optical and electrical properties. In this study we show that dry plasma etching results in the degradation of the silicon material quality due to (i) a high density of dangling bonds and (ii) the presence of sub‐surface defects, resulting in high surface recombination velocities and low minority carrier lifetimes. On the contrary, wet chemical anisotropic etching used as an alternative, leads to the formation of inverted nanopyramids that result in low surface recombination velocity and low density of dangling bonds. The proposed inverted nanopyramids could enable high efficiency photonic assisted solar cells by offering the potential to achieve higher short‐circuit current without degrading the open circuit voltage. (© 2016 WILEY‐VCH Verlag GmbH &Co. KGaA, Weinheim)     

Optical properties of cadmium sulfide nanocrystal film prepared by electrochemical synthesis at liquid-liquid interface

Dendritic nanocrystalline CdS film was deposited at liquid-liquid interface of surfactants and an electrolyte containing 4 mmol L⁻¹ cadmium chloride (CdCl₂) and 16 mmol L⁻¹ thioacetamide (CH₃CSNH₂) with an initial pH value of 5 at 15 °C by electrochemical synthesis. The nanofilm was characterized by transmission electron microscopy (TEM), field emission scanning electron microscope (FE-SEM), atomic force microscopy (AFM), ultraviolet visible (UV-vis) absorption spectroscopy and fluorescence spectroscopy. The surface morphology and particle size of the nanofilm were investigated by AFM, SEM and TEM, and the crystalline size was 30-50 nm. The thickness of the nanofilm calculated by optical absorption spectrum was 80 nm. The microstructure and composition of the nanofilm was investigated by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS), showing its polycrystalline structure consisting of CdS and Cd. Optical properties of the nanofilm were investigated systematically by UV-vis absorption and fluorescence spectroscopy. A λ_onset blue shift compared with bulk CdS was observed in the absorption spectra. Fluorescence spectra of the nanofilm indicated that the CdS nanofilm emitted blue and green light. The nanocomposites film electrode will bring about anodic photocurrent during illumination, showing that the transfer of cavities produces photocurrent.     

Application of stain-etched porous silicon in light emitting diodes and solar cells

Porous silicon/c-Si heterostructures have been formed by the method of stain etching.The properties of light emitting diodes (LED) and solar cells have been studied. The transport mechanism of the diode has been investigated from the current–voltage characteristics measured at different temperatures (296–380 K). A model based on multi-step tunneling of carriers at reverse and low forward bias (<1 V) and on field tunneling across a narrow barrier at higher forward bias (>1.5 V) is proposed for the LED. In the case of the solar cells the porous silicon is formed in between the fingers of the front grid contact. Application of porous silicon in solar cells results in an increase of the short-circuit current and efficiency of the cells by about 30%.     

Enhanced etching of silicon didioxide guided by carbon nanotubes in HF solution

This paper describes a new method to create nanoscale SiO₂ pits or channels using single-walled carbon nanotubes (SWNTs) in an HF solution at room temperature within a few seconds. Using aligned SWNT arrays, a pattern of nanoscale SiO₂ channels can be prepared. The nanoscale SiO₂ patterns can also be created on the surface of three-dimensional (3D) SiO₂ substrate and even the nanoscale trenches can be constructed with arbitrary shapes. A possible mechanism for this enhanced etching of SiO₂ has been qualitatively analysed using defects in SWNTs, combined with H₃O⁺ electric double layers around SWNTs in an HF solution.     

Structural, optical and electrical properties of amorphous silicon thin films prepared by sputtering with different targets

Amorphous silicon (a-Si) films were prepared by sputtering method with polycrystalline and monocrystalline silicon targets. Structural, optical and electrical properties of the a-Si films have been systematically studied. The deposition power is from 100 to 200 W. Compared with the a-Si films deposited by using monocrystalline silicon target, the a-Si films prepared with polycrystalline silicon target exhibit better growth property, similar optical band gap, and own the highest mobility of 1.658 cm²/Vs, which make a good match with the optimal window of optical band gap for a-Si solar cells. The results indicated that the polycrystalline silicon target is superior to the monocrystalline silicon target when used to prepare a-Si films as the intrinsic layer in a-Si solar cells.