Cobalt ultrathin film catalyzed ethanol chemical vapor deposition of single-walled carbon nanotubes

We report a simple and efficient chemical vapor deposition (CVD) process that can grow oriented and long single-walled carbon nanotubes (SWNTs) using a cobalt ultrathin film ( approximately 1 nm) as the catalyst and ethanol as carbon feedstock. In the process, millimeter- to centimeter-long, oriented and high-quality SWNTs can grow horizontally on various flat substrate surfaces, traverse slits as large as hundreds of micrometers wide, or grow over vertical barriers as high as 20 microm. Such observations demonstrate that the carbon nanotubes are suspended in the gas flow during the growth. The trace amount of self-contained water (0.2-5 wt %) in ethanol may act as a mild oxidizer to clean the nanotubes and to elongate the lifetime of the catalysts, but no yield improvement was observed at the CVD temperature of 850 degrees C. We found that tilting the substrates supporting the Co ultrathin film catalysts can grow more, longer carbon nanotubes. A mechanism is discussed for the growth of long SWNTs.     

Hydrogenation and hydrocarbonation and etching of single-walled carbon nanotubes

We present a systematic experimental investigation of the reactions between hydrogen plasma and single-walled carbon nanotubes (SWNTs) at various temperatures. Microscopy, infrared (IR) and Raman spectroscopy, and electrical transport measurements are carried out to investigate the properties of SWNTs after hydrogenation. Structural deformations, drastically reduced electrical conductance, and an increased semiconducting nature of SWNTs upon sidewall hydrogenation are observed. These changes are reversible upon thermal annealing at 500 degrees C via dehydrogenation. Harsh plasma or high temperature reactions lead to etching of nanotubes likely via hydrocarbonation. Smaller SWNTs are markedly less stable against hydrocarbonation than larger tubes. The results are fundamental and may have implications to basic and practical applications including hydrogen storage, sensing, band gap engineering for novel electronics, and new methods of manipulation, functionalization, and etching of nanotubes.     

Distribution patterns and controllable transport of water inside and outside charged single-walled carbon nanotubes

The density distribution patterns of water inside and outside neutral and charged single-walled carbon nanotubes (SWNTs) soaked in water have been studied using molecular dynamics simulations based on TIP3P potential and Lennard-Jones parameters of CHARMM force field, in conjunction with ab initio calculations to provide the electron density distributions of the systems. Water molecules show different electropism near positively and negatively charged SWNTs. Different density distribution patterns of water, depending on the diameter and chirality of the SWNTs, are observed inside and outside the tube wall. These special distribution patterns formed can be explained in terms of the van der Waals and electrostatic interactions between the water molecules and the carbon atoms on the hexagonal network of carbon nanotubes. The electric field produced by the highly charged SWNTs leads to high filling speed of water molecules, while it prevents them from flowing out of the nanotube. Water molecules enter the neutral SWNTs slowly and can flow out of the nanotube in a fluctuating manner. It indicates that by adjusting the electric charge on the SWNTs, one can control the adsorption and transport behavior of polar molecules in SWNTs to be used as stable storage medium with template effect or transport channels. The transport rate can be tailored by changing the charge on the SWNTs.     

Antibacterial effects of carbon nanotubes: size does matter!

We provide the first evidence that the size (diameter) of carbon nanotubes (CNTs) is a key factor governing their antibacterial effects and that the likely main CNT-cytotoxicity mechanism is cell membrane damage by direct contact with CNTs. Experiments with well-characterized single-walled carbon nanotubes (SWNTs) and multiwalled carbon nanotubes (MWNTs) demonstrate that SWNTs are much more toxic to bacteria than MWNTs. Gene expression data show that in the presence of both MWNTs and SWNTs, Escherichia coli expresses high levels of stress-related gene products, with the quantity and magnitude of expression being much higher in the presence of SWNTs.     

Metal-enhanced fluorescence of carbon nanotubes

The photoluminescence (PL) quantum yield of single-walled carbon nanotubes (SWNTs) is relatively low, with various quenching effects by metallic species reported in the literature. Here, we report the first case of metal enhanced fluorescence (MEF) of surfactant-coated carbon nanotubes on nanostructured gold substrates. The photoluminescence quantum yield of SWNTs is observed to be enhanced more than 10-fold. The dependence of fluorescence enhancement on metal-nanotube distance and on the surface plasmon resonance (SPR) of the gold substrate for various SWNT chiralities is measured to reveal the mechanism of enhancement. Surfactant-coated SWNTs in direct contact with metal exhibit strong MEF without quenching, suggesting a small quenching distance for SWNTs on the order of the van der Waals distance, beyond which the intrinsically fast nonradiative decay rate in nanotubes is little enhanced by metal. The metal enhanced fluorescence of SWNTs is attributed to radiative lifetime shortening through resonance coupling of SWNT emission to the reradiating dipolar plasmonic modes in the metal.     

Cobalt-filled apoferritin for suspended single-walled carbon nanotube growth with narrow diameter distribution

Cobalt-filled apoferritin (Co-ferritin) was, for the first time, used as a wet catalyst for the synthesis of single-walled carbon nanotubes (SWNTs) with narrow diameter distribution. Co-ferritins were spin-coated and converted to cobalt nanoparticles by calcination. Using chemical vapor deposition, suspended networks of SWNTs were formed on pillar-structured substrates. The suspended SWNTs show narrow tube diameter distribution with a relatively good graphite structure. By virtue of the low diffusion coefficient of cobalt, Co-ferritin might be more useful for narrow diameter SWNTs growth than ferritins, which encase iron particles.     

Entrapping of exohedral metallofullerenes in carbon nanotubes: (CsC60)n@SWNT nano-peapods

Exohedral C60-based metallofullerenes, CsC60, have been synthesized and successfully encapsulated into single-wall carbon nanotubes (SWNTs) in high yield by reducing C60 molecules into anions. High-resolution transmission electron microscopy (HRTEM) images and in situ electron energy loss spectroscopy (EELS) indicate that Cs atoms and C60 molecules align within SWNTs as CsC60 exohedral metallofullerenes, and that the formal charge state of encaged CsC60 is expressed as Cs+1C60-1. The present peapods with the exohedral metallofullerenes provide a new insight and the possibility to fine-tune the electronic and transport properties of carbon nanotubes.     

Improving the effectiveness of interfacial trapping in removing single-walled carbon nanotube bundles

Single-walled carbon nanotube (SWNT) bundles are selectively removed from an aqueous dispersion containing individually suspended carbon nanotubes coated with gum Arabic via interfacial trapping. The suspensions are characterized with absorbance, fluorescence, and Raman spectroscopy as well as atomic force microscopy (AFM) and rheology. The resulting aqueous suspensions have better dispersion quality after interfacial trapping and can be further improved by altering the processing conditions. A two-step extraction process offers a simple and fast approach to preparing high-quality dispersions of individual SWNTs comparable to ultracentrifugation. Partitioning of SWNTs to the liquid-liquid interface is described by free energy changes. SWNT bundles prefer to reside at the interface over individually suspended SWNTs because of greater free energy changes.     

Probing the Selectivity of Azomethine Imine Cycloaddition to Single‐Walled Carbon Nanotubes by Resonance Raman Spectroscopy

Selective covalent surface modification of single‐walled carbon nanotubes (SWNTs) is of great importance to various carbon nanotube‐based applications as it might offer an alternative method for enriching metallic and semiconducting nanotubes. Herein, we report on the surface modification of SWNTs through 1,3‐dipolar cycloaddition of 3‐phenyl‐phthalazinium‐1‐olate, which is a stable and reactive azomethine imine. For this reaction, microwave heating was found to be more efficient than conventional and solvent‐free heating. The sensitivity of cycloaddition to the molecular structure of SWNTs was probed using resonance Raman spectroscopy with three different laser excitations. Based on the obtained results, azomethine imine addition to the surface of nanotubes is selective for metallic and large‐diameter semiconducting SWNTs. Thermogravimetric analysis coupled with mass spectrometry showed that fragments released at high temperatures corresponded to the phenylphthalazine group, thus confirming the covalent surface functionalization. Modified SWNTs were further characterized by X‐ray photoelectron and UV/Vis‐NIR spectroscopies.     

ZnO纳米线基MWNTs/PVDF复合热电材料的制备及特性研究

将不同比例的多壁碳管(MWNTs)与聚偏二氟乙烯(PVDF)聚合物混合后,喷涂于n型ZnO半导体纳米线阵列上,制备了一种新型ZnO纳米线基MWNTs/PVDF热电复合材料.与以往采用价格昂贵的p型与n型单壁碳纳米管(SWNTs)与聚合物混合制备的复合热电材料特性相比,这种新型热电复合材料在降低制造成本的同时,利用分散于聚合物中MWNTs的一维电子传输特性及形成的大量界面势垒,加上ZnO半导体纳米线具有的较高载流子密度与迁移率,提高了复合热电材料中电子的输运特性,增加了材料对声子的散射强度.测试发现,在一定的温度梯度下,随着MWNTs添加质量百分比的增加,热电材料的温差电动势和电导率也随之增加,但其Seebeck系数变化量不大.研究表明,这种热电材料有望替代采用p型与n型SWNTs构建的SWNTs/PVDF复合热电材料.研究结果对开发超轻、无毒、廉价、可应用于各种微纳电子领域的新型电源具有重要的参考价值.     

High-yield synthesis of single-wall carbon nanotubes on MCM41 using catalytic chemical vapor deposition of acetylene

High-quality single-wall carbon nanotubes (SWNTs) with narrow diameter distribution have been grown on Fe/Co-loaded MCM41 by using acetylene as the carbon source within a short reaction period, typically 10 min or less. The optimum temperature for SWNTs synthesis is 850 degrees C. Longer reaction time (i.e., 30 min) favors the formation of multiwall carbon nanotubes (MWNTs) and graphitic carbon. When the reaction time is reduced to less than 10 min, formation of MWNTs and graphitic carbon is greatly suppressed, and high-quality SWNTs dominates the yield. The surface of the as-grown SWNTs is found to be free from amorphous carbon, as observed from high-resolution transmission electron microscope (HRTEM) analysis. Raman spectral data show a G/D ratio above 10, indicating that the as-grown SWNTs have very few defects. Furthermore, radial breathing mode (RBM) analysis reveals that the diameter distribution of the current SWNTs is narrow and ranges from 0.64 to 1.36 nm.     

The adsorption kinetics of cadmium by three different types of carbon nanotubes

Oxidized nitrogen-doped multiwall carbon nanotubes (ox-N-MWCNTs), oxidized multiwall carbon nanotubes (ox-MWCNTs), and oxidized single-wall carbon nanotubes (ox-SWCNTs) were evaluated via batch adsorption kinetic experiments to determine the effect of nanotube morphology on the adsorption rate of cadmium. The nanotubes were characterized by HRTEM, XRD and Raman spectroscopy. Cadmium adsorption isotherms were determined at pH 6. Analyses of the kinetic data with an external mass transport model and an intraparticle diffusion model considered two cases: (1) single nanotubes suspended in aqueous solution and (2) agglomerates of nanotubes suspended in aqueous solution. The intraparticle diffusion model produced the best fit to the experimental data. However, only the diffusivity coefficients for single nanotubes suspended in solution were similar to literature values: about 4×10(-9), 1×10(-9) and 2.4×10(-11) cm(2)/s for ox-N-MWCNTs, ox-MWCNTs and ox-SWCNTs, respectively. The morphology of the various carbon nanotubes might determine cadmium diffusivity. The high amount of sidewall pores observed in the single-walled carbon nanotubes could limit cadmium diffusion and account for the slow diffusion rate of 180 min. Conversely, the short length, small surface area and bamboo-type morphology observed with nitrogen-doped multiwall carbon nanotubes may account for the relatively fast adsorption rate of 15 min as this morphology prevents cadmium diffusion through the internal tubular space of these nanotubes.     

Remarkable support effect of SWNTs in Pt catalyst for methanol electrooxidation

Carbon nanotubes have been proposed as advanced metal catalyst support for electrocatalysis. In this work, different carbon support materials including single-walled carbon nanotubes (SWNTs), multi-walled carbon nanotubes (MWNTs) and XC-72 carbon black, were compared in terms of their electrochemical properties using cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). The SWNTs is found to exhibit the highest accessible surface area in electrochemical reactions and the lowest charge transfer resistance at the SWNTs/electrolytes. These carbon materials are then loaded with varying amount of Pt by the electrodeposition technique to prepare carbon supported Pt catalysts. Electrochemical measurements of methanol oxidation reveal that the SWNTs supported Pt catalyst exhibits the highest mass activity (mA/mg-Pt). In comparison with Pt-XC-72 and Pt-MWNTs, the remarkably enhanced electrocatalytic activity of the Pt-SWNTs maybe attributed to a higher dispersion and utilization of the Pt particles, which are directly related to the electrochemical characteristics of SWNTs. The high concentration of oxygen-containing functional groups, high accessible surface area, low charge transfer resistance at the carbon/electrolyte interfaces can be important for the Pt dispersing and strong metal-support interaction in the Pt-SWNTs catalyst.     

Dispersion of single-walled carbon nanotubes in alcohol-cholic acid mixtures

A procedure for dispersing single-walled carbon nanotubes (SWNTs) for the preparation of suspensions with high concentrations of individual nanotubes in various solvents was described. The most stable suspensions were obtained from a mixture of ethanol with cholic acid at an acid concentration of 0.018 mol/kg.     

Surfactant‐Dependent Charge Transfer between Polyoxometalates and Single‐Walled Carbon Nanotubes: A Fluorescence Spectroscopic Study

Hybridizations of redox‐active polyoxometalates (POMs) with single‐walled carbon nanotubes (SWNTs) have been widely investigated for their diverse applications. For the purpose of constructing high‐quality electronic devices, controlling charge transfer within POM/SWNT hybrids is an inevitable issue. As determined by means of fluorescence spectroscopy, electron transfer between SWNTs and a common POM dopant, phosphomolybdic acid (PMo₁₂), can be tuned simply by an alteration of nanotube surfactant type from anionic to nonionic. The mechanism is attributed to the influence of surfactant type on the stabilization of the electron donor–acceptor hybrid and effect of surfactant–nanotube interactions. These results will be important to control charge‐transport behavior in nanohybrids consisting of carbon nanotubes.     

Single electron emission from the closed-tips of single-walled carbon nanotubes

The single electron emission behaviors and characteristics from the well-defined quantized energy levels, corresponding to localized electronic states at the dome-structure tips, in single-walled carbon nanotubes (SWNTs) are investigated and illuminated by use of the energy level emission model in combination with the first-principles calculations on the electronic structures. Under the external electric field, the confined electrons are emitted simultaneously from each quantized energy level by virtue of the resonant tunneling effects. With increasing applied voltage, the emission current increases monotonically and exponentially up to the first peak value, and then steps into the increasing and decreasing "sawtoothlike" variations in sequence. The negative differential resistance or conductivity and the maximum current for SWNTs are simulated. The influences of localized electronic states and curvatures of the different closed tips on the single electron emission behaviors of SWNTs are evaluated and discussed. Also a few issues and applications relevant to electron emission of carbon nanotubes are addressed.     

Application of centrifugation to the large-scale purification of electric arc-produced single-walled carbon nanotubes

We report a further advance in the bulk purification of nitric acid-treated single-walled carbon nanotubes (SWNTs) by use of high-speed centrifugation. We have already shown that low-speed centrifugation is effective in removing amorphous carbon (AC). In these earlier experiments, the AC preferentially suspends in aqueous dispersions on low-speed centrifugation (2000g), leaving the SWNTs in the sediment. In a surprising reversal, we now show that high-speed centrifugation (20000g) of well-dispersed preparations is effective in sedimenting carbon nanoparticles (CNP), while leaving the SWNTs suspended in aqueous media. Taken together, these two techniques allow the bulk scale (10 g) purification of SWNTs by efficiently separating the two main contaminants, in an industrially viable process. We show that the mechanism of these separations is based on the differential charging (zeta-potential) of the AC, CNPs, and SWNTs that comes about during the chemical processing. Due to their more robust structure, nitric acid oxidation leaves the CNPs with a surface charge density lower than that of the SWNTs, and thus the CNPs do not form stable dispersions in aqueous media during high-speed centrifugation. The efficiency of the process was confirmed by the high purification recovery factor (PRF = 90%), which is a measure of the fractional quantity of the product recovered after the purification. We demonstrate that the purity of SWNTs significantly affects their mechanical and electrical properties.     

Controlled growth of single-walled carbon nanotubes by catalytic decomposition of CH4 over Mo/Co/MgO catalysts

It was found that the addition of molybdenum to Co/MgO catalysts could remarkably increase the yield and also improve the quality of single-walled carbon nanotubes (SWNTs) from catalytic decomposition of methane. The generation rate of SWNTs was raised at least 10 times and the formation of amorphous carbon was suppressed. But there is an optimum content of Mo and Co, beyond which multi-walled carbon nanotubes (MWNTs) were formed. In other words, the relative amount of SWNTs and MWNTs could be controlled by the composition of catalysts. The obtained SWNTs showed a very high BET surface area. The promotion role of molybdenum was discussed.     

Azafullerene encapsulated single-walled carbon nanotubes with n-type electrical transport property

Electrical transport properties of C60 and C59N encapsulated single-walled carbon nanotubes (SWNTs) are investigated by fabricating them as the channels of field effect transistor (FET) devices at room temperature. Their measurements indicate that C60@SWNTs exhibit the enhanced p-type characteristics compared with the case of pristine SWNTs, whereas C59N@SWNTs show the n-type behavior. The novel transport properties of peapods can be explained by the charge-transfer effect, which can modify the electronic structure of SWNTs.